WO2025219172A1 - Procédé de production d'une vitre composite avec une partie d'insert fonctionnel - Google Patents

Procédé de production d'une vitre composite avec une partie d'insert fonctionnel

Info

Publication number
WO2025219172A1
WO2025219172A1 PCT/EP2025/059692 EP2025059692W WO2025219172A1 WO 2025219172 A1 WO2025219172 A1 WO 2025219172A1 EP 2025059692 W EP2025059692 W EP 2025059692W WO 2025219172 A1 WO2025219172 A1 WO 2025219172A1
Authority
WO
WIPO (PCT)
Prior art keywords
film
transition temperature
phase transition
pane
phase
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
PCT/EP2025/059692
Other languages
German (de)
English (en)
Inventor
Viktor SEIBEL
Muhammed Nasuh ALTIN
Michael Müller
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Saint Gobain Sekurit France
Original Assignee
Saint Gobain Sekurit France
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Saint Gobain Sekurit France filed Critical Saint Gobain Sekurit France
Publication of WO2025219172A1 publication Critical patent/WO2025219172A1/fr
Pending legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

L'invention concerne un procédé de production d'une vitre composite (100) avec une partie d'insert fonctionnel (6), comprenant les étapes suivantes consistant à : a) produire un empilement de couches (15) contenant - une première vitre (1) avec une première surface (I) et une deuxième surface (II) et une seconde vitre (3) avec une troisième surface (III) et une quatrième surface (IV), lesdites deuxième surface (II) et troisième surface (III) se faisant face, - au moins un premier film de liaison (2), au moins un second film de liaison (4), et au moins un film de cadre (5) qui sont disposés entre la première vitre (1) et la seconde vitre (3), ledit au moins un film de cadre (5) étant disposé entre l'au moins un premier film de liaison (2) et l'au moins un second film de liaison (4) de manière à entrer directement en contact avec celui-ci et ayant une découpe (8) telle qu'un espace de réception (13) est formé par la découpe (8), lesdits au moins un premier film de liaison (2), au moins un second film de liaison (4), et au moins un film de cadre (5) étant constitués d'un ou de plusieurs matériaux thermoplastiques, ledit matériau thermoplastique ayant une première température de transition de phase ou ladite pluralité de matériaux thermoplastiques ayant une première température de transition de phase maximale, une transition du ou des matériaux thermoplastiques d'un état solide à un état plastique ayant lieu à ou au-dessus de ladite première température de transition de phase, - une partie d'insert fonctionnel (6) qui a une forme plane et qui a une première surface principale (9), une seconde surface principale (10), et une surface de bord (11) s'étendant entre celles-ci, ladite partie d'insert fonctionnel (6) étant positionnée dans l'espace de réception (13) de telle sorte qu'une surface principale (9, 10) de la partie d'insert fonctionnel repose directement contre l'au moins un premier film de liaison (13) ou contre l'au moins un second film de liaison (14), - une couche de changement de phase (7) qui est disposée dans l'espace de réception (13) de telle sorte que la couche de changement de phase repose directement contre l'autre surface principale respective (9, 10) de la partie d'insert fonctionnel (6), ladite couche de changement de phase (7) n'ayant pas de contact direct avec l'au moins un film de cadre (5) de telle sorte qu'un espace de compensation (14) soit formé entre la couche de changement de phase (7) et l'au moins un film de cadre (5), ladite couche de changement de phase (7) étant constituée d'un matériau qui présente une transition du matériau de la couche de changement de phase d'un état solide ou de type gel à un état plastique ou liquide ayant lieu à ou au-dessus de ladite seconde température de transition de phase, ladite seconde température de transition de phase étant supérieure à la première température de transition de phase, b) mettre en œuvre un premier processus de stratification de l'empilement de couches (15) par évacuation et chauffage d'au moins des régions de l'empilement de couches (15) dans la région du film de cadre (5) à une température égale ou supérieure à la première température de transition de phase et inférieure à la seconde température de transition de phase, et c) mettre en œuvre un second processus de stratification de l'empilement de couches (15) par application d'une pression et chauffage de l'empilement de couches (15) à une température égale ou supérieure à la seconde température de transition de phase.
PCT/EP2025/059692 2024-04-15 2025-04-09 Procédé de production d'une vitre composite avec une partie d'insert fonctionnel Pending WO2025219172A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP24170366.9 2024-04-15
EP24170366 2024-04-15

Publications (1)

Publication Number Publication Date
WO2025219172A1 true WO2025219172A1 (fr) 2025-10-23

Family

ID=90735023

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2025/059692 Pending WO2025219172A1 (fr) 2024-04-15 2025-04-09 Procédé de production d'une vitre composite avec une partie d'insert fonctionnel

Country Status (1)

Country Link
WO (1) WO2025219172A1 (fr)

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0876608B1 (fr) 1995-11-27 2002-04-17 Fuhr, Günter Procede et dispositif de production de phenomenes de resonance dans des suspensions de particules
EP0847965B1 (fr) 1996-12-12 2004-10-20 Saint-Gobain Glass France Vitrage comprenant un substrat muni d'un empilement de couches minces pour la protection solaire et-ou l'isolation thermique
WO2007122428A1 (fr) 2006-04-20 2007-11-01 Pilkington Group Limited Vitrage
WO2007122429A1 (fr) 2006-04-20 2007-11-01 Pilkington Group Limited Vitrage
DE102008026339A1 (de) 2008-05-31 2009-12-03 Saint-Gobain Sekurit Deutschland Gmbh & Co. Kg Elektrisch schaltbares Sichtschutzfenster
WO2011033313A1 (fr) 2009-09-18 2011-03-24 Pilkington Group Limited Vitrage feuilleté
EP4242181A1 (fr) 2020-11-05 2023-09-13 Sekisui Chemical Co., Ltd. Structure de film intercouche pour panneau stratifié, et structure de panneau stratifié

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0876608B1 (fr) 1995-11-27 2002-04-17 Fuhr, Günter Procede et dispositif de production de phenomenes de resonance dans des suspensions de particules
EP0847965B1 (fr) 1996-12-12 2004-10-20 Saint-Gobain Glass France Vitrage comprenant un substrat muni d'un empilement de couches minces pour la protection solaire et-ou l'isolation thermique
WO2007122428A1 (fr) 2006-04-20 2007-11-01 Pilkington Group Limited Vitrage
WO2007122429A1 (fr) 2006-04-20 2007-11-01 Pilkington Group Limited Vitrage
DE102008026339A1 (de) 2008-05-31 2009-12-03 Saint-Gobain Sekurit Deutschland Gmbh & Co. Kg Elektrisch schaltbares Sichtschutzfenster
WO2011033313A1 (fr) 2009-09-18 2011-03-24 Pilkington Group Limited Vitrage feuilleté
EP4242181A1 (fr) 2020-11-05 2023-09-13 Sekisui Chemical Co., Ltd. Structure de film intercouche pour panneau stratifié, et structure de panneau stratifié

Similar Documents

Publication Publication Date Title
DE112019003296T5 (de) Laminierte verglasung mit einer umschaltbaren flüssigkristallschicht
EP2928686B1 (fr) Vitrage doté de propriétés optiques commutables électriquement
EP2882588B1 (fr) Agencement de vitrage feuillleté électriquement commutable
DE69938525T2 (de) Lichtdurchlässiger Schichtstoff für reflektive Anzeigevorrichtung
EP3774417B1 (fr) Impression optique améliorée d'un pare-brise de véhicules en pdlc au moyen d'une combinaison d'empilements intérieur et extérieur foncés
DE112018004359T5 (de) Laminat mit dünner einsatzsichtbehinderung aufweisend bessere festigkeit und optische qualität
EP3484705A1 (fr) Vitre feuilletée comprenant une couche composite multicouche et procédé pour sa fabrication
EP3060393B1 (fr) Vitre composite constituée d'une vitre en polymère et d'une vitre en verre
EP3154783A1 (fr) Feuille composite constituée d'une feuille de polymère et d'une feuille de verre
DE112020001086T5 (de) Laminiertes glas
DE112020002979T5 (de) Schaltbarer Film mit Randabdichtung
EP4164880B1 (fr) Procédé de laminage d'une vitre composite comprenant un élément fonctionnel à des propriétés optiques électriquement commutables
EP3826838A1 (fr) Vitre feuilletée comprenant un élément fonctionnel doté de propriétés optiques pouvant être commandées électriquement comprenant un scellement de bords amélioré
DE202023103995U1 (de) Verbundscheibe mit elektrischem Funktionselement
EP3720702A1 (fr) Procédé pour la fabrication d'un disque composite
EP4565424A1 (fr) Procédé de production d'une vitre composite
WO2024028113A1 (fr) Procédé de production d'une vitre composite, et vitre composite
WO2025219172A1 (fr) Procédé de production d'une vitre composite avec une partie d'insert fonctionnel
WO2021069354A1 (fr) Procédé de fabrication d'une vitre composite dotée d'un élément fonctionnel
EP3826836A1 (fr) Procédé de fabrication d'une vitre feuilletée comprenant un élément fonctionnel doté de propriétés optiques pouvant être commandées électriquement
EP4326550A1 (fr) Procédé de commande électrique d'un élément fonctionnel enfermé dans une unité de vitrage
WO2025219168A1 (fr) Procédé de production d'une vitre composite avec une partie d'insert fonctionnel
WO2025242469A1 (fr) Procédé de production d'une vitre composite
WO2024218224A1 (fr) Processus de post-traitement d'un panneau
DE202021100685U1 (de) Funktionselement mit elektrisch steuerbaren optischen Eigenschaften und einer aktiven Schicht umfassend Abstandhalter

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 25719311

Country of ref document: EP

Kind code of ref document: A1