WO2025005463A1 - Carte de circuit imprimé en céramique, son procédé de fabrication et module de puissance de type à refroidissement double face la comprenant - Google Patents

Carte de circuit imprimé en céramique, son procédé de fabrication et module de puissance de type à refroidissement double face la comprenant Download PDF

Info

Publication number
WO2025005463A1
WO2025005463A1 PCT/KR2024/006538 KR2024006538W WO2025005463A1 WO 2025005463 A1 WO2025005463 A1 WO 2025005463A1 KR 2024006538 W KR2024006538 W KR 2024006538W WO 2025005463 A1 WO2025005463 A1 WO 2025005463A1
Authority
WO
WIPO (PCT)
Prior art keywords
copper
layer
base
ceramic
copper layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
PCT/KR2024/006538
Other languages
English (en)
Korean (ko)
Inventor
김민수
배일석
서진원
김병길
육점국
이효종
문상환
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Rn2 Ceramics Co Ltd
Rn2 Technologies Co Ltd
Original Assignee
Rn2 Ceramics Co Ltd
Rn2 Technologies Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from KR1020240061410A external-priority patent/KR20250001884A/ko
Application filed by Rn2 Ceramics Co Ltd, Rn2 Technologies Co Ltd filed Critical Rn2 Ceramics Co Ltd
Publication of WO2025005463A1 publication Critical patent/WO2025005463A1/fr
Anticipated expiration legal-status Critical
Pending legal-status Critical Current

Abstract

La présente invention concerne une carte de circuit imprimé en céramique présentant d'excellentes performances de dissipation de chaleur du fait de l'inclusion de structures en cuivre, son procédé de fabrication, et un module de puissance de type à refroidissement double face la comprenant. La carte de circuit imprimé en céramique, selon un mode de réalisation de la présente invention, comprend : un substrat céramique comprenant une couche céramique, une première couche de cuivre de base disposée sur une première surface de la couche céramique, et une seconde couche de cuivre de base disposée sur une seconde surface de la couche céramique ; des premières structures de cuivre qui sont disposées sur des parties de la première couche de cuivre de base, qui sont formées par impression, compression et frittage d'une pâte contenant du cuivre, et qui présentent des porosités différentielles, la porosité étant inférieure sur la partie supérieure que sur la partie inférieure qui est plus proche de la première couche de cuivre de base ; et des structures de refroidissement qui sont formées par impression, compression et frittage d'une pâte contenant du cuivre et disposées sur des parties de la seconde couche de cuivre de base pour faire saillie à partir de celle-ci, formant un corps avec celle-ci.
PCT/KR2024/006538 2023-06-29 2024-05-14 Carte de circuit imprimé en céramique, son procédé de fabrication et module de puissance de type à refroidissement double face la comprenant Pending WO2025005463A1 (fr)

Applications Claiming Priority (10)

Application Number Priority Date Filing Date Title
KR20230084314 2023-06-29
KR10-2023-0084313 2023-06-29
KR20230084315 2023-06-29
KR10-2023-0084314 2023-06-29
KR10-2023-0084315 2023-06-29
KR20230084313 2023-06-29
KR10-2023-0114523 2023-08-30
KR20230114523 2023-08-30
KR10-2024-0061410 2024-05-09
KR1020240061410A KR20250001884A (ko) 2023-06-29 2024-05-09 세라믹 회로 기판, 그 제조방법, 및 이를 구비한 양면 냉각형 파워 모듈

Publications (1)

Publication Number Publication Date
WO2025005463A1 true WO2025005463A1 (fr) 2025-01-02

Family

ID=93938824

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2024/006538 Pending WO2025005463A1 (fr) 2023-06-29 2024-05-14 Carte de circuit imprimé en céramique, son procédé de fabrication et module de puissance de type à refroidissement double face la comprenant

Country Status (1)

Country Link
WO (1) WO2025005463A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR0179404B1 (ko) * 1993-02-02 1999-05-15 모리시타 요이찌 세라믹기판과 그 제조방법
JP2015086085A (ja) * 2013-10-28 2015-05-07 日本発條株式会社 積層体、絶縁性冷却板、パワーモジュールおよび積層体の製造方法
KR20210108221A (ko) * 2020-02-25 2021-09-02 현대자동차주식회사 양면 냉각형 파워모듈
KR20220109171A (ko) * 2021-01-28 2022-08-04 주식회사 알엔투세라믹스 냉각 핀을 구비한 양면 냉각형 파워 모듈용 세라믹 회로 기판, 그 제조방법 및 이를 구비한 양면 냉각형 파워 모듈
KR20220160248A (ko) * 2021-05-27 2022-12-06 주식회사 아모센스 인버터 파워모듈

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR0179404B1 (ko) * 1993-02-02 1999-05-15 모리시타 요이찌 세라믹기판과 그 제조방법
JP2015086085A (ja) * 2013-10-28 2015-05-07 日本発條株式会社 積層体、絶縁性冷却板、パワーモジュールおよび積層体の製造方法
KR20210108221A (ko) * 2020-02-25 2021-09-02 현대자동차주식회사 양면 냉각형 파워모듈
KR20220109171A (ko) * 2021-01-28 2022-08-04 주식회사 알엔투세라믹스 냉각 핀을 구비한 양면 냉각형 파워 모듈용 세라믹 회로 기판, 그 제조방법 및 이를 구비한 양면 냉각형 파워 모듈
KR20220160248A (ko) * 2021-05-27 2022-12-06 주식회사 아모센스 인버터 파워모듈

Similar Documents

Publication Publication Date Title
WO2018117361A1 (fr) Module à micro-led et son procédé de fabrication
WO2011021824A2 (fr) Dispositif de serrage électrostatique et procédé de fabrication dudit dispositif
WO2021221460A1 (fr) Film de transfert adhésif et procédé de fabrication d'un substrat de module de puissance en utilisant celui-ci
WO2016171530A1 (fr) Procédé de fabrication de substrat en céramique et substrat en céramique fabriqué par celui-ci
WO2019093609A1 (fr) Plaque de mandrin, structure de mandrin ayant une plaque de mandrin, et dispositif de soudure ayant une structure de mandrin
WO2022045694A1 (fr) Carte de circuit imprimé en céramique pour module de puissance de refroidissement double face, son procédé de préparation, et module de puissance de refroidissement double face la comprenant
EP2856502A1 (fr) Substrat de boîtier de semi-conducteurs, système de boîtier utilisant un tel substrat et son procédé de fabrication
WO2022158894A1 (fr) Procédé de fabrication de carte de circuit imprimé
WO2021251716A1 (fr) Composition de pâte d'ag et film de liaison produit à l'aide de celle-ci
WO2021235721A1 (fr) Procédé de fabrication de carte de circuit imprimé à base de céramique
WO2025005463A1 (fr) Carte de circuit imprimé en céramique, son procédé de fabrication et module de puissance de type à refroidissement double face la comprenant
WO2023113287A1 (fr) Dissipateur thermique revêtu ayant une structure maillée verticale et son procédé de fabrication
WO2022005183A1 (fr) Module d'alimentation
WO2018117484A1 (fr) Tige chauffante, module de chauffage comprenant celle-ci et dispositif de chauffage comprenant celle-ci
WO2025005462A1 (fr) Carte de circuit imprimé en céramique, son procédé de fabrication et module de puissance de type à refroidissement double face la comprenant
WO2025005458A1 (fr) Carte de circuit imprimé en céramique, son procédé de fabrication et module d'alimentation de type à refroidissement double face la comprenant
WO2023163439A1 (fr) Unité de substrat en céramique et son procédé de fabrication
WO2025005457A1 (fr) Carte de circuit imprimé en céramique, son procédé de fabrication et module d'alimentation de type à refroidissement double face la comprenant
WO2025005461A1 (fr) Module d'alimentation sans fil refroidi sur les deux surfaces et son procédé de fabrication
WO2014115929A1 (fr) Boîtier étanche d'une puce à semi-conducteurs et procédé de traitement associé
WO2025005460A1 (fr) Carte de circuit imprimé en céramique, son procédé de fabrication et module d'alimentation de type à refroidissement double face la comprenant
WO2025005459A1 (fr) Carte de circuit imprimé en céramique, son procédé de fabrication et module de puissance de type à refroidissement double face la comprenant
WO2021230623A1 (fr) Module d'alimentation
WO2021230615A1 (fr) Module d'alimentation et son procédé de fabrication
WO2022065651A1 (fr) Dispositif thermoélectrique

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 24832247

Country of ref document: EP

Kind code of ref document: A1