WO2023190759A1 - 撥水性ポリアクリロニトリル系人工毛髪繊維、その製造方法、及び頭飾製品 - Google Patents

撥水性ポリアクリロニトリル系人工毛髪繊維、その製造方法、及び頭飾製品 Download PDF

Info

Publication number
WO2023190759A1
WO2023190759A1 PCT/JP2023/012982 JP2023012982W WO2023190759A1 WO 2023190759 A1 WO2023190759 A1 WO 2023190759A1 JP 2023012982 W JP2023012982 W JP 2023012982W WO 2023190759 A1 WO2023190759 A1 WO 2023190759A1
Authority
WO
WIPO (PCT)
Prior art keywords
water
repellent
polyacrylonitrile
mass
amount
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2023/012982
Other languages
English (en)
French (fr)
Inventor
空明 小橋
伸崇 田岡
健 田中
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kaneka Corp
Original Assignee
Kaneka Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kaneka Corp filed Critical Kaneka Corp
Priority to JP2024512725A priority Critical patent/JPWO2023190759A1/ja
Publication of WO2023190759A1 publication Critical patent/WO2023190759A1/ja
Priority to US18/780,200 priority patent/US20240376665A1/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

撥水性に優れるとともに、触感にも優れるポリアクリロニトリル系人工毛髪繊維、当該繊維の製造方法、及び当該繊維を含む頭飾製品を提供する。　ポリアクリロニトリル系合成繊維（Ａ）を含む撥水性ポリアクリロニトリル系人工毛髪繊維であって、　撥水剤（Ｂ）が、前記ポリアクリロニトリル系合成繊維（Ａ）に付着しており、　前記撥水剤（Ｂ）が、フルオロ基を有しておらず、　前記撥水剤（Ｂ）が、デンドリマー系撥水剤（Ｂ―１）、アルキルウレタン系撥水剤（Ｂ―２）、及び縮合反応型ポリジメチルシロキサン（Ｂ―３）からなる群より選択される少なくとも１種を含み、　前記デンドリマー系撥水剤（Ｂ―１）が、エステル及び／又はウレタン結合を有しており、　前記アルキルウレタン系撥水剤（Ｂ―２）が、長鎖炭化水素側鎖を有しており、かつ、非デンドリマー型であり、　前記縮合反応型ポリジメチルシロキサン（Ｂ―３）が、両末端にヒドロキシ基、ヒドロキシ基を有する有機基、又はヒドロキシ基を生じうる有機基を有しており、　前記撥水剤（Ｂ）の付着量が、前記ポリアクリロニトリル系合成繊維（Ａ）の全質量に対して、０．０５質量％以上１．０質量％以下である、撥水性ポリアクリロニトリル系人工毛髪繊維を用いる。

Description

撥水性ポリアクリロニトリル系人工毛髪繊維、その製造方法、及び頭飾製品
　本発明は、撥水性ポリアクリロニトリル系人工毛髪繊維、その製造方法、及び頭飾製品に関する。
　従来、フッ素含有基を有するフッ素系撥水剤が知られており、かかるフッ素系撥水剤を繊維製品等に処理することにより、その表面に撥水性が付与された繊維製品が知られている。このようなフッ素系撥水剤は一般にフルオロアルキル基を有する単量体を重合、若しくは共重合させることにより製造される。フッ素系撥水剤で処理された繊維製品は優れた撥水性を発揮するものの、フルオロアルキル基を有する単量体は難分解性であるため環境への負荷が大きい。このような事情から、近年、フッ素を含まない非フッ素系撥水剤について研究が進められている。例えば、特許文献１には、ナイロン布やポリエステル布を特定の非フッ素系撥水剤で処理して得られる繊維製品が、十分な撥水性及び耐久撥水性を有することが記載されている。
特開２０１７－２１０７０４号公報
　ところで、ポリアクリロニトリル系合成繊維は人毛のような手触りを有するため人工毛髪繊維として使用されており、該ポリアクリロニトリル系人工毛髪繊維にも撥水性を付与することが求められている。そこで、かかる目的を達成するには前述の非フッ素系撥水剤で処理する方法が考えられる。しかしながら、非フッ素系撥水剤でポリアクリロニトリル系合成繊維を処理すると、撥水性は向上するものの、ポリアクリロニトリル系合成繊維が本来有する手触りが損なわれるという問題がある。
　本発明は、上記課題に鑑みてなされたものであり、撥水性に優れるとともに、触感にも優れるポリアクリロニトリル系人工毛髪繊維、当該繊維の製造方法、及び当該繊維を含む頭飾製品を提供することを目的とする。
　本発明者らは、特定の非フッ素系撥水剤を用いて、該非フッ素系撥水剤の付着量を鋭意検討することにより、上記課題を解決できることを見出し、本発明を完成するに至った。
　本発明の態様は、以下の撥水性ポリアクリロニトリル系人工毛髪繊維、当該繊維の製造方法、及び当該繊維を含む頭飾製品に関する。
［１］　ポリアクリロニトリル系合成繊維（Ａ）を含む撥水性ポリアクリロニトリル系人工毛髪繊維であって、
　撥水剤（Ｂ）が、前記ポリアクリロニトリル系合成繊維（Ａ）に付着しており、
　前記撥水剤（Ｂ）が、フルオロ基を有しておらず、
　前記撥水剤（Ｂ）が、デンドリマー系撥水剤（Ｂ－１）、アルキルウレタン系撥水剤（Ｂ－２）、及び縮合反応型ポリジメチルシロキサン（Ｂ－３）からなる群より選択される少なくとも１種を含み、
　前記デンドリマー系撥水剤（Ｂ－１）が、エステル及び／又はウレタン結合を有しており、
　前記アルキルウレタン系撥水剤（Ｂ－２）が、長鎖炭化水素側鎖を有しており、かつ、非デンドリマー型であり、
　前記縮合反応型ポリジメチルシロキサン（Ｂ－３）が、両末端にヒドロキシ基、ヒドロキシ基を有する有機基、又はヒドロキシ基を生じうる有機基を有しており、
　前記撥水剤（Ｂ）の付着量が、前記ポリアクリロニトリル系合成繊維（Ａ）の全質量に対して、０．０５質量％以上１．０質量％以下である、撥水性ポリアクリロニトリル系人工毛髪繊維。
［２］　さらに変性シリコーン（Ｃ）が前記ポリアクリロニトリル系合成繊維（Ａ）に付着しており、
　前記変性シリコーン（Ｃ）が、エポキシ基及び／又はアミノ基で置換されたジメチルシロキサン重合体であり、
　前記変性シリコーン（Ｃ）の付着量が、前記ポリアクリロニトリル系合成繊維（Ａ）の全質量に対して、０．０１質量％以上０．５質量％以下である、［１］に記載の撥水性ポリアクリロニトリル系人工毛髪繊維。
［３］　前記デンドリマー系撥水剤（Ｂ－１）が、疎水性末端残基を有する、［１］又は［２］に記載の撥水性ポリアクリロニトリル系人工毛髪繊維。
［４］　前記アルキルウレタン系撥水剤（Ｂ－２）が、ソルビタンに由来する骨格を有する、［１］～［３］のいずれかに記載の撥水性ポリアクリロニトリル系人工毛髪繊維。
［５］　さらに帯電防止剤（Ｄ）として、イオン性帯電防止剤（Ｄ１）及び／又は非イオン性帯電防止剤（Ｄ２）が、前記ポリアクリロニトリル系合成繊維（Ａ）に付着しており、
　前記帯電防止剤（Ｄ）の付着量が、前記ポリアクリロニトリル系合成繊維（Ａ）の全質量に対して、０．０５質量％以上０．３質量％以下である、［１］～［４］のいずれかに記載の撥水性ポリアクリロニトリル系人工毛髪繊維。
［６］　前記デンドリマー系撥水剤（Ｂ－１）の付着量と、前記変性シリコーン（Ｃ）の付着量との質量比率が、（Ｂ－１）：（Ｃ）＝１：０．０３以上０．３以下である、［１］～［５］のいずれかに記載の撥水性ポリアクリロニトリル系人工毛髪繊維。
［７］　前記アルキルウレタン系撥水剤（Ｂ－２）の付着量と、前記変性シリコーン（Ｃ）の付着量との質量比率が、（Ｂ－２）：（Ｃ）＝１：０．０３以上０．５以下である、［１］～［６］のいずれかに記載の撥水性ポリアクリロニトリル系人工毛髪繊維。
［８］　前記撥水剤（Ｂ）の付着量と、前記帯電防止剤（Ｄ）の付着量との質量比率が、（Ｂ）：（Ｄ）＝１：０．１５以上０．７以下である、［５］に記載の撥水性ポリアクリロニトリル系人工毛髪繊維。
［９］　前記デンドリマー系撥水剤（Ｂ－１）の付着量と、前記変性シリコーン（Ｃ）の付着量との質量比率が、（Ｂ－１）：（Ｃ）＝１：０．０３以上０．３以下であり、
　前記デンドリマー系撥水剤（Ｂ－１）の付着量と、前記帯電防止剤（Ｄ）の付着量との質量比率が、（Ｂ－１）：（Ｄ）＝１：０．１５以上０．７以下である、［５］に記載の撥水性ポリアクリロニトリル系人工毛髪繊維。
［１０］　前記アルキルウレタン系撥水剤（Ｂ―２）の付着量と、前記変性シリコーン（Ｃ）の付着量との質量比率が、（Ｂ―２）：（Ｃ）＝１：０．０３以上０．５以下であり、
　前記アルキルウレタン系撥水剤（Ｂ－２）の付着量と、前記帯電防止剤（Ｄ）の付着量との質量比率が、（Ｂ―２）：（Ｄ）＝１：０．１５以上０．７以下である、［５］に記載の撥水性ポリアクリロニトリル系人工毛髪繊維。
［１１］　単繊維繊度が１ｄｔｅｘ以上１００ｄｔｅｘ以下である、［１］～［１０］のいずれかに記載の撥水性ポリアクリロニトリル系人工毛髪繊維。
［１２］　［１］～［１１］のいずれかに記載の撥水性ポリアクリロニトリル系人工毛髪繊維の製造方法であって、
　アクリロニトリル系重合体を含む紡糸液を湿式紡糸することにより凝固糸条を得ることと、乾燥させる前の被処理糸条を、前記撥水剤（Ｂ）を含む油剤と接触させることとを含む、製造方法。
［１３］　［１］～［１１］のいずれかに記載の撥水性ポリアクリロニトリル系人工毛髪繊維の製造方法であって、
　乾燥されたポリアクリロニトリル系合成繊維（Ａ）を、前記撥水剤（Ｂ）を含む油剤と接触させることと、該接触処理後の糸状を乾燥させることとを含む、製造方法。
［１４］　［１］～［１１］のいずれかに記載の撥水性ポリアクリロニトリル系人工毛髪繊維を含む、頭飾製品。
［１５］　前記頭飾製品が、ヘアーウィッグ、かつら、ウィービング、ヘアーエクステンション、ブレードヘアー、ヘアーアクセサリー、及びドールヘアーからなる群より選ばれる少なくとも１種である、［１４］に記載の頭飾製品。
　本発明によれば、撥水性に優れるとともに、触感にも優れるポリアクリロニトリル系人工毛髪繊維、当該繊維の製造方法、及び当該繊維を含む頭飾製品を提供することができる。
≪撥水性ポリアクリロニトリル系人工毛髪繊維≫
　撥水性ポリアクリロニトリル系人工毛髪繊維は、ポリアクリロニトリル系合成繊維（Ａ）を含む。
　撥水性ポリアクリロニトリル系人工毛髪繊維は、後述する撥水剤（Ｂ）が、上記ポリアクリロニトリル系合成繊維（Ａ）に付着しており、
　上記撥水剤（Ｂ）の付着量が、上記ポリアクリロニトリル系合成繊維（Ａ）の全質量に対して、０．０５質量％以上１．０質量％以下である。
　より具体的には、撥水性ポリアクリロニトリル系人工毛髪繊維において、上記撥水剤（Ｂ）は、ポリアクリロニトリル系合成繊維（Ａ）の表面に付着して被膜を形成している。
　撥水性ポリアクリロニトリル系人工毛髪繊維は、上記撥水剤（Ｂ）がポリアクリロニトリル系合成繊維（Ａ）に特定の付着量で付着していることにより、後述する変性シリコーン（Ｃ）がポリアクリロニトリル系合成繊維（Ａ）に付着していない場合でも、撥水性に優れるとともに、触感にも優れるという効果を奏する。
　以下、撥水性ポリアクリロニトリル系人工毛髪繊維に含まれる、必須、又は任意の成分について説明する。
（ポリアクリロニトリル系合成繊維（Ａ））
　ポリアクリロニトリル系合成繊維（Ａ）を構成するアクリロニトリル系重合体は、アクリロニトリルに由来する構成単位を２５質量％以上含むものであれば、特に限定されず、例えば、アクリロニトリルに由来する構成単位を２５～１００質量％含み、他の単量体に由来する構成単位を０～７５質量％含むアクリロニトリル系重合体を用いることができる。上記アクリロニトリル系重合体は、アクリロニトリルに由来する構成単位を９５質量％以下、他の単量体に由来する構成単位を５質量％以上含んでもよく、アクリロニトリルに由来する構成単位を９０質量％以下、他の単量体に由来する構成単位を１０質量％以上含んでもよく、アクリロニトリルに由来する構成単位を３０～８５質量％未満、他の単量体に由来する構成単位を１５質量％より多く７０質量％以下含んでもよい。
　他の単量体としては、アクリロニトリルと共重合可能なものであればよく、特に限定されず、例えば、アクリル酸やメタクリル酸等の不飽和カルボン酸類及びこれらの塩類、アクリル酸メチル等のアクリル酸エステル、メタクリル酸メチル等のメタクリル酸エステル、グリシジルメタクリレート等の不飽和カルボン酸のエステル類、酢酸ビニルや酪酸ビニル等のビニルエステル類、ハロゲン含有単量体、並びにスルホン酸基含有単量体等が挙げられる。これらは、１種を単独で用いてもよく、２種以上を組み合わせて用いてもよい。
　上記アクリロニトリル系重合体は、耐熱性、難燃性及び染色性の観点から、アクリロニトリルに由来する構成単位を３０～８０質量％、ハロゲン含有単量体に由来する構成単位を２０～７０質量％、及びスルホン酸基含有単量体に由来する構成単位を０～５質量％含むことが好ましい。上記アクリロニトリル系重合体は、アクリロニトリルに由来する構成単位を３５～７５質量％、ハロゲン含有単量体に由来する構成単位を２５～６５質量％、及びスルホン酸基含有単量体に由来する構成単位を０～５質量％含んでもよく、アクリロニトリルに由来する構成単位を３５～７５質量％、ハロゲン含有単量体に由来する構成単位を２４．５～６４．５質量％、及びスルホン酸基含有単量体に由来する構成単位を０．５～５質量％含んでもよい。
　上記ハロゲン含有単量体としては、例えば、塩化ビニル、臭化ビニル等のハロゲン含有ビニル単量体や、塩化ビニリデン、臭化ビニリデン等のハロゲン含有ビニリデン単量体等が挙げられる。前記ハロゲン含有単量体は、１種を単独で用いてもよく、２種以上を組み合わせて用いてもよい。前記ハロゲン含有単量体は、塩化ビニル及び塩化ビニリデンからなる群から選ばれる一つ以上を含むことが好ましく、触感の観点から、塩化ビニルを含むことが好ましい。
　上記スルホン酸基含有単量体としては、特に限定されないが、例えば、アリルスルホン酸、メタリルスルホン酸、スチレンスルホン酸、イソプレンスルホン酸、２－アクリルアミド－２－メチルプロパンスルホン酸並びにこれらのナトリウム塩等の金属塩類及びアミン塩類等を用いることができる。前記スルホン酸基含有単量体は、１種を単独で用いてもよく、２種以上を組み合わせて用いてもよい。
　ポリアクリロニトリル系合成繊維（Ａ）の単繊維繊度としては、特に限定されず、例えば、１ｄｔｅｘ以上１００ｄｔｅｘ以下であることが好ましく、人工毛髪として好適に用いる観点から、単繊維繊度が１０ｄｔｅｘ以上９０ｄｔｅｘ以下であることがより好ましく、２０ｄｔｅｘ以上８０ｄｔｅｘ以下であることがさらに好ましく、３０ｄｔｅｘ以上７０ｄｔｅｘ以下であることがさらにより好ましく、３５ｄｔｅｘ以上６５ｄｔｅｘ以下であることが特に好ましい。
　ポリアクリロニトリル系合成繊維（Ａ）の製造方法は、特に限定されず、例えば、湿式紡糸法により製造することができる。湿式紡糸法は、前述したアクリロニトリル系重合体からなる紡糸原液を紡糸ノズルから凝固浴の中に押し出して、その中で固めて糸状を形成する方法である。また、湿式紡糸法は、上記凝固工程以外に、水洗工程、乾燥工程、延伸工程及び熱緩和工程のいずれかを含んでもよい。
　ポリアクリロニトリル系合成繊維（Ａ）は、上記の方法で製造してもよいし、市販のポリアクリロニトリル系合成繊維を入手してもよい。ポリアクリロニトリル系合成繊維（Ａ）の市販品としては、例えば、カネカ社製の「ＡＦＲＥＬＬＥ」、「ＳＹＣ」等が挙げられる。
（撥水剤（Ｂ））
　撥水剤（Ｂ）は、デンドリマー系撥水剤（Ｂ－１）、アルキルウレタン系撥水剤（Ｂ－２）、及び縮合反応型ポリジメチルシロキサン（Ｂ－３）からなる群より選択される少なくとも１種を含む。撥水剤（Ｂ）は、非フッ素系撥水剤として用いられる。このため、撥水剤（Ｂ）は、フルオロ基を有していない。
〔デンドリマー系撥水剤（Ｂ―１）〕
　デンドリマー系撥水剤（Ｂ－１）は、放射状でかつ中心から規則的に分枝した構造を持つ樹状高分子化合物を含む。デンドリマー系撥水剤（Ｂ－１）は、上記分岐構造中に、エステル及び／又はウレタン結合を有する。
　デンドリマー系撥水剤（Ｂ－１）は、上記分岐構造中に、疎水性末端残基を有することが好ましい。該疎水性末端残基が、デンドリマー系撥水剤（Ｂ－１）に撥水性を付与しているものと推測される。疎水性末端残基としては、例えば、炭素数１２～２６のアルキル基が好ましい。
　デンドリマー系撥水剤（Ｂ－１）の分子量は、溶液中の安定性や合成の簡便さの観点から、１０００以上１０万以下であることが好ましく、１０００以上３万以下であることがより好ましい。
　デンドリマー系撥水剤（Ｂ－１）の市販品としては、例えば、ＲＵＤＯＬＦ　ＧｍｂＨ社製の「ＲＵＣＯ－ＤＲＹ　ＥＣＯ　ＰＳＳ」、「ＲＵＣＯ－ＤＲＹ　ＥＣＯ　ＰＬＵＳ」等が挙げられる。
〔アルキルウレタン系撥水剤（Ｂ－２）〕
　アルキルウレタン系撥水剤（Ｂ－２）は、分子中に、ポリオール誘導体とポリイソシアネートとの反応に由来するウレタン結合、及び長鎖炭化水素側鎖を有する重合体である。上記長鎖炭化水素側鎖は、ポリオール誘導体及び／又はポリイソシアネートを有する側鎖であってもよい。長鎖炭化水素側鎖としては、例えば、炭素数１２～２４の直鎖アルキル基であることが好ましく、炭素数１６～２２の直鎖アルキル基であることがより好ましい。
　ポリオール誘導体としては、公知の化合物であれば特に限定されず、例えば、上記長鎖炭化水素側鎖を１つ以上有していてもよい、ポリエーテルポリオール、低分子ポリオール、ポリエステルポリオール、ポリカーボネートポリオール、ポリブタジエングリコール、グリコール、アクリルポリオール等が挙げられる。これらは１種単独で用いてもよく、２種以上組み合わせて用いてもよい。これらのうち、ソルビタン誘導体が好ましい。
　ポリイソシアネートとしては、公知の化合物であれば特に限定されず、例えば、上記長鎖炭化水素側鎖を有していてもよい、脂肪族ポリイソシアネート、脂環族ポリイソシアネート、芳香脂肪族ポリイソシアネート、芳香族ポリイソシアネート、該ポリイソシアネートの誘導体等が挙げられる。これらは１種単独で用いてもよく、２種以上組み合わせて用いてもよい。
　また、アルキルウレタン系撥水剤（Ｂ－２）は、ソルビタンに由来する骨格を有することが好ましい。
　アルキルウレタン系撥水剤（Ｂ－２）は、非デンドリマー型である。
　アルキルウレタン系撥水剤（Ｂ－２）の市販品としては、例えば、ＨＵＮＴＳＭＡＮ社製の「ＺＥＬＡＮ　Ｒ３」等が挙げられる。
〔縮合反応型ポリジメチルシロキサン（Ｂ－３）〕
　縮合反応型ポリジメチルシロキサン（Ｂ－３）は、両末端にヒドロキシ基、ヒドロキシ基を有する有機基、又はヒドロキシ基を生じうる有機基を有する。
　ヒドロキシ基を有する有機基としては、例えば、カルビノール基等のアルカノール基（－ＲＯＨ）、ポリエーテルアルキル基（－Ｒ－Ｘ－ＯＨ）等が挙げられる。ここで、アルカノール基、ポリエーテルアルキル基のＲは、炭素数１～３のアルキル基を示し、Ｘは、ポリエチレンオキシド鎖、ポリプロピレンオキシド鎖等のポリアルキレンオキシド鎖を示す。
　ヒドロキシ基を生じうる有機基としては、例えば、メトキシ基、エトキシ基、プロピルオキシ基等のアルコキシ基が挙げられる。
　縮合反応型ポリジメチルシロキサン（Ｂ－３）の市販品としては、例えば、三木理研工業社製の「リケンパランＳＧ－５４」等が挙げられる。
　撥水剤（Ｂ）の付着量は、ポリアクリロニトリル系合成繊維（Ａ）の全質量に対して、０．０５質量％以上１．０質量％以下であり、０．０８質量％以上０．７５質量％以下であることが好ましく、０．１質量％以上０．４質量％以下であることがより好ましい。
　デンドリマー系撥水剤（Ｂ－１）の付着量は、ポリアクリロニトリル系人工毛髪繊維が撥水性に優れるとともに、触感にも優れる観点から、ポリアクリロニトリル系合成繊維（Ａ）の全質量に対して、０．０５質量％以上１．０質量％以下であり、０．０８質量％以上０．７５質量％以下であることが好ましく、０．１質量％以上０．４質量％以下であることがより好ましい。
　アルキルウレタン系撥水剤（Ｂ－２）、及び縮合反応型ポリジメチルシロキサン（Ｂ－３）の付着量は、ポリアクリロニトリル系人工毛髪繊維が撥水性に優れるとともに、触感にも優れる観点から、それぞれポリアクリロニトリル系合成繊維（Ａ）の全質量に対して、０．０５質量％以上１．０質量％以下であり、０．０８質量％以上０．７５質量％以下であることが好ましく、０．１質量％以上０．６質量％以下であることがより好ましい。
（他の成分）
　ポリアクリロニトリル系人工毛髪繊維は、本発明の効果を損なわない限り、ポリアクリロニトリル系合成繊維（Ａ）及び撥水剤（Ｂ）以外の成分（以下、「他の成分」ともいう）を含有してもよい。他の成分としては、例えば、変性シリコーン；帯電防止剤；光沢調整剤；有機顔料、無機顔料、及び染料等の着色剤；光安定剤；熱安定剤；繊維収束剤；消臭剤；芳香剤；防虫剤；抗菌剤；架橋剤等が挙げられる。
（変性シリコーン（Ｃ））
　変性シリコーン（Ｃ）とは、シリコーンのポリジアルキルシロキサン骨格、好ましくはポリジメチルシロキサン骨格（以下、総称して「ポリシロキサン」ともいう）のいずれかの部位を置換した置換基を有するシリコーンであり、直鎖又は分岐のポリシロキサンの片末端、両末端、又は側鎖を変性した変性シリコーン、更にはこれらを架橋した架橋型変性シリコーンを包含する。
　変性シリコーン（Ｃ）としては、特に限定されず、例えば、エポキシ変性シリコーン、アミノ変性シリコーン、メルカプト変性シリコーン、カルボキシル変性シリコーン、ハイドロジェン変性シリコーン、メタクリル変性シリコーン等が挙げられる。これらは１種単独で用いてもよく、２種以上組み合わせて用いてもよい。
　これらの中では、前述のデンドリマー系撥水剤（Ｂ－１）又はアルキルウレタン系撥水剤（Ｂ－２）と併用することにより、ポリアクリロニトリル系人工毛髪繊維が撥水性に優れるとともに、触感にも優れる観点から、エポキシ変性シリコーン、アミノ変性シリコーンが好ましい。
　エポキシ変性シリコーンの市販品としては、例えば、信越化学工業社製の「ＰＯＬＯＮ－ＭＦ－１８Ｔ」が挙げられる。アミノ変性シリコーンの市販品としては、例えば、信越化学工業社製の「ＰＯＬＯＮ－ＭＦ－６３」が挙げられる。
　変性シリコーン（Ｃ）の付着量は、ポリアクリロニトリル系人工毛髪繊維が撥水性に優れるとともに、触感にも優れる観点から、ポリアクリロニトリル系合成繊維（Ａ）の全質量に対して、０．０１質量％以上０．５質量％以下であることが好ましく、０．０１質量％以上０．３質量％以下であることがより好ましく、０．０２質量％以上０．２質量％以下であることが特に好ましい。
（帯電防止剤（Ｄ））
　帯電防止剤（Ｄ）としては、特に限定されず、例えば、イオン性帯電防止剤（Ｄ１）、非イオン性帯電防止剤（Ｄ２）等が挙げられる。
　イオン性帯電防止剤（Ｄ１）としては、例えば、高級脂肪酸塩、高級アルコール硫酸エステル塩、硫酸化油、スルホン酸塩等のアニオン性帯電防止剤；アルキルアミン塩、第四級アンモニウム塩、イミダゾリニウム塩、グアニジン塩等のカチオン性帯電防止剤；アミンオキシド型、ベタイン型等の両性帯電防止剤が挙げられる。
　非イオン性帯電防止剤（Ｄ２）としては、例えば、ポリオキシエチレンアルキルエーテル型、多価アルコール脂肪酸エステル型、ポリオキシエチレン多価アルコール脂肪酸エステル型、脂肪酸アルカノールアミド型、ポリオキシエチレンアルキルアミン型、ポリアルキレングリコール等の非イオン性帯電防止剤が挙げられる。
　帯電防止剤（Ｄ）は、１種を単独で用いてもよく、２種以上組み合わせて用いてもよい。
　これらのうち、ポリアクリロニトリル系人工毛髪繊維が撥水性に優れるとともに、触感にも優れる観点から、カチオン性帯電防止剤（Ｄ１）及び／又は非イオン性帯電防止剤（Ｄ２）が好ましい。
　帯電防止剤（Ｄ）の付着量は、本発明の目的を阻害しない範囲で適宜選択でき、静電気を抑制する観点から、ポリアクリロニトリル系合成繊維（Ａ）の全質量に対して、０．０５質量％以上０．３質量％以下であることが好ましく、０．１０質量％以上０．３質量％以下であることがより好ましい。
　デンドリマー系撥水剤（Ｂ－１）がポリアクリロニトリル系合成繊維（Ａ）に付着している場合、帯電防止剤（Ｄ）の付着量は、本発明の目的を阻害しない範囲で適宜選択でき、静電気を抑制する観点から、ポリアクリロニトリル系合成繊維（Ａ）の全質量に対して、０．０５質量％以上０．３質量％以下であることが好ましく、０．１０質量％以上０．３質量％以下であることがより好ましい。
　アルキルウレタン系撥水剤（Ｂ－２）又は縮合反応型ポリジメチルシロキサン（Ｂ－３）がポリアクリロニトリル系合成繊維（Ａ）に付着している場合、帯電防止剤（Ｄ）の付着量は、本発明の目的を阻害しない範囲で適宜選択でき、静電気を抑制する観点から、ポリアクリロニトリル系合成繊維（Ａ）の全質量に対して、０．０５質量％以上０．３質量％以下であることが好ましく、０．０５質量％以上０．２質量％以下であることがより好ましい。
　デンドリマー系撥水剤（Ｂ－１）の付着量と、変性シリコーン（Ｃ）の付着量との質量比率は、撥水性に優れるとともに、触感にも優れる観点から、（Ｂ－１）：（Ｃ）＝１：０．０３以上０．３以下であることが好ましく、１：０．０３以上０．２以下であることがより好ましく、１：０．０３以上０．１以下であることがさらに好ましい。
　アルキルウレタン系撥水剤（Ｂ－２）の付着量と、変性シリコーン（Ｃ）の付着量との質量比率は、撥水性に優れるとともに、触感にも優れる観点から、（Ｂ－２）：（Ｃ）＝１：０．０３以上０．５以下であることが好ましく、１：０．０３以上０．４以下であることがより好ましく、１：０．０４以上０．３以下であることがさらに好ましい。
　撥水剤（Ｂ）の付着量と、帯電防止剤（Ｄ）の付着量との質量比率は、撥水性に優れるとともに、静電気を抑制する観点から、（Ｂ）：（Ｄ）＝１：０．１５以上０．７以下であることが好ましく、１：０．１５以上０．６以下であることがより好ましく、１：０．２以上０．５以下であることがさらに好ましい。
　なお、静電気が強く発生する場合、紡糸工程や加工時にトラブルが生じやすくなる。
≪撥水性ポリアクリロニトリル系人工毛髪繊維の製造方法１≫
　前述した撥水性ポリアクリロニトリル系人工毛髪繊維の製造方法の第１の実施形態は、アクリロニトリル系重合体を含む紡糸液を湿式紡糸することにより凝固糸条を得ることと、乾燥させる前の被処理糸条を、上記撥水剤（Ｂ）を含む油剤と接触させることとを含む。
　本実施形態の製造方法によれば、前述したように、撥水性に優れるとともに、触感にも優れる撥水性ポリアクリロニトリル系人工毛髪繊維を製造することができる。
　以下、アクリロニトリル系重合体を含む紡糸液を湿式紡糸することにより凝固糸条を得る工程（以下、「凝固工程」とも称する）、乾燥させる前の被処理糸条を、上記撥水剤（Ｂ）を含む油剤と接触させる工程（以下、「接触工程」とも称する）、及び任意の工程について説明する。
＜凝固工程＞
（アクリロニトリル系重合体）
　アクリロニトリル系重合体は、ポリアクリロニトリル系合成繊維（Ａ）の糸条を製造するための原料である。アクリロニトリル系重合体は、前述した「（ポリアクリロニトリル系合成繊維（Ａ））」の項目に記載されたアクリロニトリル系重合体の実施態様と同じである。
（紡糸液）
　紡糸液は、上記アクリロニトリル系重合体と有機溶媒を含有する。有機溶媒は、特に限定されず、アクリロニトリル系重合体の良溶媒を使用することが好ましい。アクリロニトリル系重合体の良溶媒としては、例えば、ジメチルスルホキシド（ＤＭＳＯ）、Ｎ，Ｎ－ジメチルアセトアミド（ＤＭＡｃ）、Ｎ，Ｎ－ジメチルホルムアミド（ＤＭＦ）、アセトン等が挙げられる。これらの中では、汎用性の観点から、アセトンを用いてもよい。また、安全性が高い観点から、ジメチルスルホキシドを用いてもよい。紡糸液は、少量の水、例えば、１．５質量％以上４．８質量％以下の水を含んでいてもよい。これにより、ボイドの形成を抑制することができる。
（他の添加剤）
　紡糸液は、本発明の効果を阻害しない範囲内であれば、必要に応じて、繊維特性を改良するための他の添加剤を含んでもよい。他の添加剤としては、例えば、光沢調整剤、有機顔料、無機顔料、染料等の着色剤、耐光性や耐熱性向上のための安定剤等が挙げられる。
（凝固工程）
　凝固工程は、上記紡糸液を、紡糸ノズルを通して、凝固液（凝固浴）へ吐出して、凝固させることにより糸状（以下、このような糸条を「凝固糸条」とも称する）を形成する工程である。凝固工程の操作は、特に限定されず、例えば、常法に従い、原液タンク中の紡糸液を、直接凝固液へ吐出する湿式紡糸法でもよい。また、紡糸ノズルからいったん空気中に吐出してから凝固液中へ導く乾湿式紡糸法でもよい。
　紡糸液の温度は、原液タンク中で紡糸液が経時変化することなく安定して保てる温度であれば特に限定されず、例えば、通常、４０℃以上７０℃以下が好ましい。
　凝固液の組成は、特に限定されず、例えば、アセトン等の良溶媒の水溶液を用いることが好ましい。良溶媒の濃度は、特に限定されず、例えば、１０質量％以上７０質量％以下が好ましい。１０質量％未満では、凝固が速くなって凝固構造が粗になり、繊維内部にボイドが形成される傾向がある。
　凝固液の温度は、特に限定されず、例えば、５℃以上４０℃以下が好ましい。
　紡糸ノズルは、目的とする繊維断面に合わせて適宜用いることができる。繊維断面は、特に限定されず、円形、楕円形、異形等のいずれの断面でもよい。
　紡糸液の紡糸ノズルからの吐出量は、特に限定されず、例えば、単孔吐出量として、０．１ｇ／ｍｉｎ以上が好ましい。紡糸液の紡糸ノズルからの紡糸速度は、特に限定されず、工業生産性の観点から、２ｍ／ｍｉｎ以上１７ｍ／ｍｉｎ以下が好ましい。
　凝固液を通過した凝固糸条（繊維）は、常法に従い、例えば、送りローラを介して巻取りローラで巻取られ、これにより未延伸の糸条が得られる。また、巻き取らずに、連続的に他の工程へ進んでもよい。
（他の工程）
　湿式紡糸は、本発明の効果を損なわない限り、凝固工程以外の工程（以下、「他の工程」ともいう）を含んでもよい。他の工程としては、水洗工程、乾燥工程、延伸工程、熱緩和処理工程等が挙げられる。
　延伸工程としては、水洗工程の前、或いは水洗工程の後かつ乾燥工程の前に行う湿式延伸工程、乾燥工程の後に行う乾式延伸工程が挙げられる。
　各工程の順序は、特に限定されず、例えば、凝固工程の後に、順に、湿式延伸工程、水洗工程、乾燥工程、乾式延伸工程、熱緩和処理工程を行う方法、又は凝固工程の後に、順に、水洗工程、湿式延伸工程、乾燥工程、乾式延伸工程、熱緩和処理工程を行う方法が挙げられる。
（湿式延伸工程）
　湿式延伸工程は、凝固糸条を延伸浴中で延伸（以下、「一次延伸」とも称する）する工程である。延伸浴は、凝固浴よりアセトン等の良溶媒の濃度が低い水溶液を用いることが好ましい。延伸浴の温度は、３０℃以上が好ましく、４０℃以上がより好ましい。延伸倍率は、特に限定されず、繊維の強度及び生産性を高める観点から、１．５倍以上８倍以下であることが好ましい。なお、水浴を用いて一次延伸を行う場合は、後述する水洗工程後に湿式延伸工程を行ってもよく、一次延伸と水洗を同時に行ってもよい。
（水洗工程）
　水洗工程は、凝固工程又は湿式延伸工程を経た糸条に付着したアセトン等の良溶媒を除去する工程である。水洗工程では、良溶媒を除去しやすい観点から。例えば、７０℃以上の温水を用いることが好ましい。
（乾燥工程）
　乾燥工程は、糸条を乾燥させることにより、糸条を緻密化する工程である。乾燥温度は、特に限定されず、例えば、１１０℃以上１９０℃以下が好ましい。
（乾式延伸工程）
　乾式延伸工程は、糸条を加熱条件下で延伸（以下、「二次延伸」とも称する）する工程である。延伸温度は、特に限定されず、例えば、１１０℃以上１９０℃以下が好ましい。延伸比は、特に限定されず、例えば、１倍以上４倍以下が好ましく、１．５倍以上３．５倍以下がより好ましく、１．５倍以上３倍以下がさらに好ましい。
　なお、乾燥前の湿式延伸を含めた全延伸比は、２倍以上１０倍以下が好ましく、２倍以上８倍以下がより好ましく、２倍以上６倍以下がさらに好ましく、２倍以上４倍以下が特に好ましい。
（熱緩和処理工程）
　熱緩和処理工程は、乾式延伸後の糸条を高温雰囲気下で緩和する工程である。緩和率は、特に限定されず、例えば、５％以上が好ましく、８％以上２０％以下がより好ましい。熱緩和処理は、例えば１４０℃以上２００℃以下の乾熱雰囲気下又は過熱水蒸気雰囲気下で行うことができる。
＜接触工程＞
（乾燥させる前の被処理糸条）
　乾燥させる前の被処理糸条とは、乾燥されていないことにより、緻密化されていない糸条であって、後述する油剤と接触させる糸条である。上記被処理糸条としては、上記湿式紡糸により得られた凝固糸条以外に、該糸条に前述した乾燥工程、乾式延伸工程、熱緩和処理工程以外の処理が施された糸条も含まれる。上記被処理糸条としては、具体的には、湿式紡糸により得られた凝固糸条、湿式延伸した後の糸条、水洗した後の糸条が挙げられる。これらの中では、油剤への有機溶剤の混入を防ぐ観点から、水洗した後の糸条が好ましい。
（油剤）
　油剤は、前述した撥水剤（Ｂ）を含む。油剤は、上記撥水剤（Ｂ）を水に分散又は溶解させた混合液として用いることが好ましい。
　油剤は、本発明の効果を損なわない限り、撥水剤（Ｂ）及び水以外の成分（以下、「他の成分」ともいう）を含有してもよい。他の成分としては、例えば、変性シリコーン；帯電防止剤；光沢調整剤；有機顔料、無機顔料、及び染料等の着色剤；光安定剤；熱安定剤；繊維収束剤；消臭剤；芳香剤；防虫剤；抗菌剤；架橋剤等が挙げられる。
　これらの中で、変性シリコーン及び帯電防止剤は、それぞれ前述した「（変性シリコーン（Ｃ））」及び「（帯電防止剤（Ｄ））」の項目に記載された実施態様と同じである。
（接触方法）
　被処理糸条と油剤とを接触させる方法は、特に限定されず、浸漬させる法、スプレーで噴霧する方法、シャワーで散布する用いる法、塗布する方法等が挙げられる。これらの中では、油剤に含まれる各成分を均一に接触させる観点から、浸漬させる方法が好ましい。
　接触温度は、特に限定されず、被処理糸条の状態や、目的とする付着量に応じて、４０℃以上９０℃以下で適宜調整することができる。
　接触時間も、特に限定されず、被処理糸条の状態や、目的とする付着量に応じて、１秒以上１０分以内で適宜調整することができる。
　本実施形態では、上記接触処理後の糸状を乾燥し、次いで乾式延伸することが好ましい。このような工程を経ることで、撥水性に優れるとともに、触感にも優れる撥水性ポリアクリロニトリル系人工毛髪繊維を製造することができる。
≪撥水性ポリアクリロニトリル系人工毛髪繊維の製造方法２≫
　前述した撥水性ポリアクリロニトリル系人工毛髪繊維の製造方法の第２の実施形態は、乾燥されたポリアクリロニトリル系合成繊維（Ａ）を、上記撥水剤（Ｂ）を含む油剤と接触させることと、該接触処理後の糸状を乾燥させることとを含む。
　本実施形態の製造方法によれば、前述したように、撥水性に優れるとともに、触感にも優れる撥水性ポリアクリロニトリル系人工毛髪繊維を製造することができる。
　以下、乾燥されたポリアクリロニトリル系合成繊維（Ａ）を、上記撥水剤（Ｂ）を含む油剤と接触させる工程（以下、「接触工程」とも称する）、接触処理後の糸状を乾燥させる工程（以下、「乾燥工程」とも称する）、及び任意の工程について説明する。
＜接触工程＞
　ポリアクリロニトリル系合成繊維（Ａ）は、前述した「（ポリアクリロニトリル系合成繊維（Ａ））」の項目に記載された実施態様と同じである。
　乾燥されたポリアクリロニトリル系合成繊維（Ａ）は、ポリアクリロニトリル系合成繊維（Ａ）を、例えば、室温以上１９０℃以下で乾燥させることにより得られる。
　上記撥水剤（Ｂ）を含む油剤は、前述した「（油剤）」の項目に記載された実施態様と同じである。
　乾燥されたポリアクリロニトリル系合成繊維（Ａ）を、上記油剤と接触させる方法は、前述した「（接触方法）」の項目に記載された実施態様と同じである。
　ただし、本製造方法２では、乾燥されたポリアクリロニトリル系合成繊維（Ａ）を原料とするため、油剤に含まれる成分がポリアクリロニトリル系合成繊維（Ａ）に付着し難い。そのため、接触時間は、前述した≪ポリアクリロニトリル系人工毛髪繊維の製造方法１≫における接触時間よりも長く設定することが好ましい。
＜乾燥工程＞
　乾燥工程は、接触処理後のポリアクリロニトリル系合成繊維（Ａ）の糸状を乾燥させることにより、該糸条を緻密化する工程である。乾燥温度は、特に限定されず、例えば、１１０℃以上１９０℃以下が好ましい。
（他の工程）
　本製造方法２では、本発明の効果を損なわない限り、接触工程、乾燥工程以外の工程（以下、「他の工程」ともいう）を含んでもよい。他の工程としては、延伸工程、熱緩和処理工程等が挙げられる。延伸工程及び熱緩和処理工程は、前述した「（延伸工程）」、「（熱緩和処理工程）」の項目に記載された実施態様と同じである。
≪頭飾製品≫
　頭飾製品は、前述した撥水性ポリアクリロニトリル系人工毛髪繊維を含む。
　頭飾製品としては、特に限定されず、例えば、ヘアーウィッグ、かつら、ウィービング、ヘアーエクステンション、ブレードヘアー、ヘアーアクセサリー、ドールヘアー等が挙げられる。撥水性ポリアクリロニトリル系人工毛髪繊維を単独で人工毛髪として用い、頭飾製品を構成してもよい。或いは、上記撥水性ポリアクリロニトリル系人工毛髪繊維に加えて、他の人工毛髪繊維、並びに人毛及び獣毛等の天然繊維を組み合わせて頭飾製品を構成してもよい。他の人工毛髪繊維としては、特に限定されないが、例えば、ポリ塩化ビニル系繊維、ナイロン繊維、ポリエステル繊維、再生コラーゲン繊維等が挙げられる。
　以下、実施例及び比較例に基づいて本発明をより具体的に説明するが、本発明は以下の実施例に限定されない。
［実施例１－１～１２－１及び比較例１－１～２－１］
（油剤の作製）
　下記撥水剤（Ｂ）、下記変性シリコーン（Ｃ）、下記帯電防止剤（Ｄ）、及び水を下記表１－１に記載の含有量で混合して、油剤水溶液である油剤１－１～１２－１及び比較油剤１－１～２－１を調製した。
　なお、表１－１中、油剤１－１と２－１、油剤４－１と５－１、油剤９－１と１０－１とは、それぞれ同じ組成物であるが、後述するように、撥水性ポリアクリロニトリル系人工毛髪繊維を作製する時のポリアクリロニトリル系合成繊維（Ａ）に対する油剤の適用方法がそれぞれＡ及びＢと異なるため、便宜上異なる油剤番号を使用している。
　撥水剤（Ｂ）として、下記Ｂ１－１～Ｂ２－１を用いた。
Ｂ１－１：デンドリマー系撥水剤（ＲＵＤＯＬＦ　ＧｍｂＨ社製、「ＲＵＣＯ－ＤＲＹ　ＥＣＯ　ＰＳＳ」）
Ｂ２－１：デンドリマー系撥水剤（ＲＵＤＯＬＦ　ＧｍｂＨ社製、「ＲＵＣＯ－ＤＲＹ　ＥＣＯ　ＰＬＵＳ」）
　変性シリコーン（Ｃ）として、下記Ｃ１～Ｃ２を用いた。
Ｃ１：エポキシ変性シリコーン（信越化学工業社製、「ＰＯＬＯＮ－ＭＦ－１８Ｔ」）
Ｃ２：アミノ変性シリコーン（信越化学工業社製、「ＰＯＬＯＮ－ＭＦ－６３」）
　帯電防止剤（Ｄ）として、下記Ｄ１を用いた。
Ｄ１：第四級アンモニウム塩
Figure JPOXMLDOC01-appb-T000001
［作製例Ａ］（実施例１－１、４－１、９－１）
　４９質量％のアクリロニトリルと、５０．５質量％の塩化ビニルと、０．５質量％のスチレンスルホン酸ナトリウムを共重合して得られたアクリロニトリル系重合体をアセトンにて溶解し、樹脂濃度が２９．５質量％の樹脂溶液を作製した。次いで、該樹脂溶液に着色剤として黒系顔料（アセトン溶液、１０．５質量％）を、アクリロニトリル系重合体１００質量部に対して、１９．２質量部になるように添加し、紡糸原液を作製した。この紡糸原液を２５℃、２５質量％のアセトン水溶液の凝固浴中に、紡糸ノズル（孔径０．４ｍｍ、孔数１００個）を用いて押し出して紡糸速度３ｍ／ｍｉｎで湿式紡糸した後、５０℃、２０質量％のアセトン水溶液の延伸浴中で２．０倍に延伸した。続いて８０℃の温水にて１．１倍に延伸しながら水洗を実施し、上記表１－１に記載の各油剤が導入されている油剤槽（６０℃）に１～２秒間浸漬して、糸条に油剤を含浸させた後、ポリアクリロニトリル系合成繊維（Ａ）に対し油剤が２０質量％付着するようにニップロールで油剤を絞り落した。続いて、１３０℃で乾燥させてから２．１倍に延伸し、１５０℃で９０秒間の熱処理条件にて、８％緩和収縮を行い、単繊維繊度が約４６ｄｔｅｘの下記表２－１に記載の実施例１－１、４－１、９－１の撥水性ポリアクリロニトリル系人工毛髪繊維を作製した。
　上記作製例Ａは、前述した≪撥水性ポリアクリロニトリル系人工毛髪繊維の製造方法１≫に該当する。本実施例において、表１―１等において、「油剤の適用方法」欄に記載された「Ａ」は、上記製造方法１に該当する方法により、撥水性ポリアクリロニトリル系人工毛髪繊維が製造されたことを示す。
［作製例Ｂ］（実施例２－１～３－１、５－１～８－１、１０－１～１２－１、及び比較例１－１～２－１）
　頭飾製品であるモダクリル繊維（カネカ社製、「ＡＦＲＥＬＬＥ」、４６ｄｔｅｘ）　１００ｇを６０℃の温水で洗浄した後、室温で一日乾燥させた。次いで、乾燥後のポリアクリロニトリル系合成繊維（Ａ）を、上記表１―１に記載の各油剤が導入されている油剤槽（６０℃）に５分間浸漬して繊維毛束に撥水剤含有油剤組成物を含浸させた後、繊維毛束の質量に対して油剤が２０質量％となるように小型延伸脱水機で付着量を調整した。続いて、繊維毛束の両端を固定し１５０℃で４０分間熱し、乾燥と熱処理を行い、実施例２－１～３－１、５－１～８－１、１０－１～１２－１、及び比較例１－１～２－１の撥水性ポリアクリロニトリル系人工毛髪繊維を作製した。
　上記作製例Ｂは、前述した≪撥水性ポリアクリロニトリル系人工毛髪繊維の製造方法２≫に該当する。本実施例において、表１―１等において、「油剤の適用方法」欄に記載された「Ｂ」は、上記製造方法２に該当する方法により、撥水性ポリアクリロニトリル系人工毛髪繊維が製造されたことを示す。
　表２－１において、撥水剤（Ｂ）、変性シリコーン（Ｃ）、及び帯電防止剤（Ｄ）の付着量「％ｏｗｆ」は、ポリアクリロニトリル系合成繊維（Ａ）の全質量に対する撥水剤（Ｂ）、変性シリコーン（Ｃ）、又は帯電防止剤（Ｄ）の質量％を意味する。なお、撥水剤（Ｂ）、変性シリコーン（Ｃ）、及び帯電防止剤（Ｄ）の上記付着量は、撥水性ポリアクリロニトリル系人工毛髪繊維を作製した後に、該繊維から撥水剤（Ｂ）、変性シリコーン（Ｃ）、及び帯電防止剤（Ｄ）を抽出し、得られた各成分の抽出量から算出した。
＜評価＞
　得られた撥水性ポリアクリロニトリル系人工毛髪繊維について、以下の方法に従って、撥水性及び触感を評価した。結果を表２－１に示す。
（撥水性）
　総繊度１２４．２万ｄｔｅｘとなるように毛束を作製し、１０ｃｍに切り揃え片端から１ｃｍの部分を結束バンドで固定した。次いで、５００ｍｌの容器に蒸留水を淵まで加え、毛束の結束バンドで固定した方を上に向け毛束全体を水に浸漬させ、毛束が水面から出ないように容器上部を塞いだ。毛束が容器の底に沈降するまでの時間を計測した。撥水性が高い場合、毛束の中心部に水が染み込むのが遅く沈降するまでの時間が長くなる。沈降するまでの時間により撥水性を以下のように評価した。
　３０分以上：高い撥水性が認められる（○）
　３分以上、３０分未満：撥水性が認められる（△）
　３分未満：十分な撥水性が認められない（×）
（触感）
　かつらの美容評価に３年以上従事した者３名により、総繊度が１２０万～１３０万ｄｔｅｘの繊維束試料を用いて官能評価を行い、ＡＦＲＥＬＬＥ（モダクリル繊維、カネカ社製、４６ｄｔｅｘ）と比較して、下記の３段階の基準でソフト感やぬめり感、しっとり感等の触感を総合的に判定した。
　Ａ（非常に良好）：ＡＦＲＥＬＬＥより良い触感を有する。
　Ｂ（良好）：ＡＦＲＥＬＬＥと同等の触感を有する。
　Ｃ（不良）：ＡＦＲＥＬＬＥより悪い触感を有する。
Figure JPOXMLDOC01-appb-T000002
　表２－１から、実施例１－１～１２－１の撥水性ポリアクリロニトリル系人工毛髪繊維は、人工毛髪としての触感を兼ね備えつつ撥水性が高く、一方、比較例１－１～２－１に示されるように、撥水剤（Ｂ）の付着量が極端に少ない場合や１．０質量％を超える場合は、人工毛髪としての触感と、撥水性を両立することができないことが分かる。
［実施例１Ａ－１～１８Ａ－１及び比較例１Ａ－１～４Ａ－１］
（油剤の作製）
　実施例１－１～１２－１及び比較例１－１～２－１で使用した上記撥水剤（Ｂ）、上記変性シリコーン（Ｃ）、上記帯電防止剤（Ｄ）、及び水を、下記表３－１に記載の含有量で混合して、油剤水溶液である油剤１Ａ－１～１８Ａ－１及び比較油剤１Ａ－１～４Ａ－１を調製した。
　ただし、油剤１７Ａ－１及び１８Ａ－１では、帯電防止剤（Ｄ）として、それぞれ下記Ｄ２及びＤ３を用いた。
Ｄ２：グアニジン系カチオン性帯電防止剤（日華化学社製「ナイスポールＦＬ」）
Ｄ３：ポリオキシエチレンアルキルエーテル型非イオン性帯電防止剤（日油社製「ノニオンＫ－２３０」）
［作製例Ｂ］（実施例１Ａ－１～１８Ａ－１及び比較例１Ａ－１～４Ａ－１）
　前述の「［作製例Ｂ］（実施例２－１～３－１、５－１～８－１、１０－１～１２－１、及び比較例１－１～２－１）」において、表１－１に記載の各油剤の代わりに、下記表３－１に記載の各油剤を用いたこと以外は、上記作製例Ｂと同様の方法で、下記表４－１に記載の実施例１Ａ－１～１８Ａ－１及び比較例１Ａ－１～４Ａ－１の撥水性ポリアクリロニトリル系人工毛髪繊維を作製した。
＜評価＞
　得られた撥水性ポリアクリロニトリル系人工毛髪繊維について、前述した方法に従って、撥水性及び触感を評価した。また、実施例１４Ａ－１～１８Ａ－１では、下記方法に従って、静電気量を評価した。結果を表４－１に示す。
（静電気量）
　総繊度１２４．２万ｄｔｅｘとなるように毛束を作製し、３０ｃｍに切り揃え、片端から５ｃｍの部分を結束バンドで固定し、温度２３℃、湿度５０％ＲＨの恒温恒湿室に１時間静置させた。次いで、恒温恒湿室内で毛束の上部を持ち、プラスチック製のコームを毛束に３回通し、すぐに静電気測定器（ＳＴＡＴＩＲＯＮ　ＤＺ４、シシド静電気株式会社）を毛束に５ｃｍの距離まで近づけ、静電気量を測定した。静電気の値により以下のように評価した。
　－６ｋＶ以上、＋６ｋＶ以下：静電気が抑制されている（○）
　－６ｋＶ未満、又は＋６ｋＶを超える：静電気が強く発生している（×）
Figure JPOXMLDOC01-appb-T000003
Figure JPOXMLDOC01-appb-T000004
　表４－１から、デンドリマー系撥水剤（Ｂ－１）の付着量と、変性シリコーン（Ｃ）の付着量との質量比率が、（Ｂ－１）：（Ｃ）＝１：０．０３以上０．３以下である場合、撥水性に優れるとともに、触感にも優れることが分かる。
　また、デンドリマー系撥水剤（Ｂ－１）の付着量と、帯電防止剤（Ｄ）の付着量との質量比率が、（Ｂ－１）：（Ｄ）＝１：０．１５以上０．７以下である場合、撥水性に優れるとともに、静電気の抑制効果にも優れることが分かる。
［実施例１－２～９－２及び比較例１－２～２－２］
（油剤の作製）
　下記撥水剤（Ｂ）、下記変性シリコーン（Ｃ）、下記帯電防止剤（Ｄ）、及び水を下記表１－２に記載の含有量で混合して、油剤水溶液である油剤１－２～９－２及び比較油剤１－２～２－２を調製した。
　なお、表１－２中、油剤１－２と２－２、油剤４－２と５－２とは、それぞれ同じ組成物であるが、後述するように、撥水性ポリアクリロニトリル系人工毛髪繊維を作製する時のポリアクリロニトリル系合成繊維（Ａ）に対する油剤の適用方法がそれぞれＡ及びＢと異なるため、便宜上異なる油剤番号を使用している。
　撥水剤（Ｂ）として、下記Ｂ１－２を用いた。
Ｂ１－２：アルキルウレタン系撥水剤（ＨＵＮＴＳＭＡＮ社製、「ＺＥＬＡＮ　Ｒ３」）
　変性シリコーン（Ｃ）として、下記Ｃ１～Ｃ２を用いた。
Ｃ１：エポキシ変性シリコーン（信越化学工業社製、「ＰＯＬＯＮ－ＭＦ－１８Ｔ」）
Ｃ２：アミノ変性シリコーン（信越化学工業社製、「ＰＯＬＯＮ－ＭＦ－６３」）
　帯電防止剤（Ｄ）として、下記Ｄ１を用いた。
Ｄ１：カチオン系帯電防止剤
Figure JPOXMLDOC01-appb-T000005
［作製例Ａ］（実施例１－２、４－２）
　前述の「［作製例Ａ］（実施例１－１、４－１、９－１）」において、表１－１に記載の各油剤の代わりに、上記表１－２に記載の各油剤を用いたこと以外は、上記作製例Ａと同様の方法で、下記表２－２に記載の実施例１－２、４－２の撥水性ポリアクリロニトリル系人工毛髪繊維を作製した。
［作製例Ｂ］（実施例２－２～３－２、５－２～９－２、及び比較例１－２～２－２）
　前述の「［作製例Ｂ］（実施例２－１～３－１、５－１～８－１、１０－１～１２－１、及び比較例１－１～２－１）」において、表１－１に記載の各油剤の代わりに、上記表１－２に記載の各油剤を用いたこと以外は、上記作製例Ｂと同様の方法で、下記表２－２に記載の実施例２－２～３－２、５－２～９－２、及び比較例１－２～２－２の撥水性ポリアクリロニトリル系人工毛髪繊維を作製した。
　表２－２において、撥水剤（Ｂ）、変性シリコーン（Ｃ）、及び帯電防止剤（Ｄ）の付着量「％ｏｗｆ」は、ポリアクリロニトリル系合成繊維（Ａ）の全質量に対する撥水剤（Ｂ）、変性シリコーン（Ｃ）、又は帯電防止剤（Ｄ）の質量％を意味する。なお、撥水剤（Ｂ）、変性シリコーン（Ｃ）、及び帯電防止剤（Ｄ）の上記付着量は、撥水性ポリアクリロニトリル系人工毛髪繊維を作製した後に、該繊維から撥水剤（Ｂ）、変性シリコーン（Ｃ）、及び帯電防止剤（Ｄ）を抽出し、得られた各成分の抽出量から算出した。
＜評価＞
　得られた撥水性ポリアクリロニトリル系人工毛髪繊維について、前述した方法と同様に、撥水性及び触感を評価した。結果を表２－２に示す。
Figure JPOXMLDOC01-appb-T000006
　表２―２から、実施例１－２～９－２の撥水性ポリアクリロニトリル系人工毛髪繊維は、人工毛髪としての触感を兼ね備えつつ撥水性が高く、一方、比較例１－２～２－２に示されるように、撥水剤（Ｂ）の付着量が極端に少ない場合や１．０質量％を超える場合は、人工毛髪としての触感と、撥水性を両立することができないことが分かる。
［実施例１Ａ－２～１８Ａ－２及び比較例１Ａ－２～２Ａ－２］
（油剤の作製）
　実施例１－２～９－２及び比較例１－２～２－２で使用した上記撥水剤（Ｂ）、上記変性シリコーン（Ｃ）、上記帯電防止剤（Ｄ）、及び水を、下記表３－２に記載の含有量で混合して、油剤水溶液である油剤１Ａ－２～１８Ａ－２及び比較油剤１Ａ－２～２Ａ－２を調製した。
　ただし、油剤１７Ａ－２及び１８Ａ－２では、帯電防止剤（Ｄ）として、それぞれ下記Ｄ２及びＤ３を用いた。
Ｄ２：グアニジン系カチオン性帯電防止剤（日華化学社製「ナイスポールＦＬ」）
Ｄ３：ポリオキシエチレンアルキルエーテル型非イオン性帯電防止剤（日油社製「ノニオンＫ－２３０」）
［作製例Ｂ］（実施例１Ａ－２～１８Ａ－２及び比較例１Ａ－２～２Ａ－２）
　前述の「［作製例Ｂ］（実施例２－１～３－１、５－１～８－１、１０－１～１２－１、及び比較例１－１～２－１）」において、表１－１に記載の各油剤の代わりに、下記表３－２に記載の各油剤を用いたこと以外は、上記作製例Ｂと同様の方法で、下記表４－２に記載の実施例１Ａ－２～１８Ａ－２及び比較例１Ａ－２～２Ａ－２の撥水性ポリアクリロニトリル系人工毛髪繊維を作製した。
＜評価＞
　得られた撥水性ポリアクリロニトリル系人工毛髪繊維について、前述した方法に従って、撥水性及び触感を評価した。また、実施例１４Ａ－２～１８Ａ－２では、前述した方法に従って、静電気量を評価した。結果を表４－２に示す。
Figure JPOXMLDOC01-appb-T000007
Figure JPOXMLDOC01-appb-T000008
　表４－２から、アルキルウレタン系撥水剤（Ｂ－２）の付着量と、変性シリコーン（Ｃ）の付着量との質量比率が、（Ｂ－２）：（Ｃ）＝１：０．０３以上０．５以下である場合、撥水性に優れるとともに、触感にも優れることが分かる。
　また、アルキルウレタン系撥水剤（Ｂ－２）の付着量と、帯電防止剤（Ｄ）の付着量との質量比率が、（Ｂ－２）：（Ｄ）＝１：０．１５以上０．７以下である場合、撥水性に優れるとともに、静電気の抑制効果にも優れることが分かる。
［実施例１－３～５－３及び比較例１－３～４－３］
（油剤の作製）
　下記シリコーン（Ｂ）、下記帯電防止剤（Ｄ）、及び水を下記表１－３に記載の含有量で混合して、油剤水溶液である油剤１－３～５－３及び比較油剤１－３～４－３を調製した。
　なお、表１－３中、油剤３－３と４－３は、それぞれ同じ組成物であるが、後述するように、撥水性ポリアクリロニトリル系人工毛髪繊維を作製する時のポリアクリロニトリル系合成繊維（Ａ）に対する油剤の適用方法がそれぞれＡ及びＢと異なるため、便宜上異なる油剤番号を使用している。
　シリコーン（Ｂ）として、下記Ｂ１－３～Ｂ３－３を用いた。
Ｂ１－３：縮合反応型ポリジメチルシロキサン系撥水剤（三木理研工業社製、「リケンパランＳＧ－５４」）
Ｂ２－３：エポキシ変性シリコーン（信越化学工業社製、「ＰＯＬＯＮ－ＭＦ－１８Ｔ」）
Ｂ３－３：シリコーン系化合物（日華化学社製、「ネオシードＮＲ－８０００」）
　帯電防止剤（Ｄ）として、下記Ｄ１を用いた。
Ｄ１：カチオン系帯電防止剤
Figure JPOXMLDOC01-appb-T000009
［作製例Ａ］（実施例３－３）
　前述の「［作製例Ａ］（実施例１－１、４－１、９－１）」において、表１－１に記載の各油剤の代わりに、上記表１－３に記載の各油剤を用いたこと以外は、上記作製例Ａと同様の方法で、下記表２－３に記載の実施例３－３の撥水性ポリアクリロニトリル系人工毛髪繊維を作製した。
［作製例Ｂ］（実施例１－３～２－３、４－３～５－３、及び比較例１－３～４－３）
　前述の「［作製例Ｂ］（実施例２－１～３－１、５－１～８－１、１０－１～１２－１、及び比較例１－１～２－１）」において、表１－１に記載の各油剤の代わりに、上記表１－３に記載の各油剤を用いたこと以外は、上記作製例Ｂと同様の方法で、下記表２－３に記載の実施例１－３～２－３、４－３～５－３、及び比較例１－３～４－３の撥水性ポリアクリロニトリル系人工毛髪繊維を作製した。
　表２－３において、シリコーン（Ｂ）及び帯電防止剤（Ｄ）の付着量「％ｏｗｆ」は、ポリアクリロニトリル系合成繊維（Ａ）の全質量に対するシリコーン（Ｂ）及び帯電防止剤（Ｄ）の質量％を意味する。なお、シリコーン（Ｂ）及び帯電防止剤（Ｃ）の上記付着量は、撥水性ポリアクリロニトリル系人工毛髪繊維を作製した後に、該繊維からシリコーン（Ｂ）及び帯電防止剤（Ｄ）を抽出し、得られた各成分の抽出量から算出した。
＜評価＞
　得られた撥水性ポリアクリロニトリル系人工毛髪繊維について、前述した方法と同様に、撥水性及び触感を評価した。結果を表２－３に示す。
Figure JPOXMLDOC01-appb-T000010
　表２－３から、シリコーン（Ｂ）として、Ｂ２－３又はＢ３－３が付着した比較例３－３～４－３の撥水性ポリアクリロニトリル系人工毛髪繊維は、人工毛髪としての撥水性及び触感を両立することができなかった。一方、実施例１－３～４－３及び比較例１－３～２－３の対比結果から、シリコーン（Ｂ）としてＢ１－３が０．０５質量％～１．０質量％付着した場合に、人工毛髪としての触感を兼ね備えつつ撥水性が高くなることが分かる。
［実施例１Ａ－３～６Ａ－３］
（油剤の作製）
　実施例１－３～５－３及び比較例１－３～４－３で使用した上記シリコーン（Ｂ）、上記帯電防止剤（Ｄ）、及び水を、下記表３－３に記載の含有量で混合して、油剤水溶液である油剤１Ａ－３～６Ａ－３を調製した。
　ただし、油剤５Ａ－３及び６Ａ－３では、帯電防止剤（Ｄ）として、それぞれ下記Ｄ２及びＤ３を用いた。
Ｄ２：グアニジン系カチオン性帯電防止剤（日華化学社製「ナイスポールＦＬ」）
Ｄ３：ポリオキシエチレンアルキルエーテル型非イオン性帯電防止剤（日油社製「ノニオンＫ－２３０」）
［作製例Ｂ］（実施例１Ａ－３～６Ａ－３）
　前述の「［作製例Ｂ］（実施例２－１～３－１、５－１～８－１、１０－１～１２－１、及び比較例１－１～２－１）」において、表１－１に記載の各油剤の代わりに、下記表３－３に記載の各油剤を用いたこと以外は、上記作製例Ｂと同様の方法で、下記表４－３に記載の実施例実施例１Ａ－３～６Ａ－３の撥水性ポリアクリロニトリル系人工毛髪繊維を作製した。
＜評価＞
　得られた撥水性ポリアクリロニトリル系人工毛髪繊維について、前述した方法に従って、撥水性及び触感を評価した。また、実施例１Ａ－３～６Ａ－３では、前述した方法に従って、静電気量を評価した。結果を表４－３に示す。
Figure JPOXMLDOC01-appb-T000011
Figure JPOXMLDOC01-appb-T000012
　表４－３から、縮合反応型ポリジメチルシロキサン（Ｂ－３）の付着量と、帯電防止剤（Ｄ）の付着量との質量比率が、（Ｂ－３）：（Ｄ）＝１：０．１５以上０．７以下である場合、撥水性に優れるとともに、静電気の抑制効果にも優れることが分かる。

Claims (15)

  1. 　ポリアクリロニトリル系合成繊維（Ａ）を含む撥水性ポリアクリロニトリル系人工毛髪繊維であって、
    　撥水剤（Ｂ）が、前記ポリアクリロニトリル系合成繊維（Ａ）に付着しており、
    　前記撥水剤（Ｂ）が、フルオロ基を有しておらず、
    　前記撥水剤（Ｂ）が、デンドリマー系撥水剤（Ｂ－１）、アルキルウレタン系撥水剤（Ｂ－２）、及び縮合反応型ポリジメチルシロキサン（Ｂ－３）からなる群より選択される少なくとも１種を含み、
    　前記デンドリマー系撥水剤（Ｂ－１）が、エステル及び／又はウレタン結合を有しており、
    　前記アルキルウレタン系撥水剤（Ｂ－２）が、長鎖炭化水素側鎖を有しており、かつ、非デンドリマー型であり、
    　前記縮合反応型ポリジメチルシロキサン（Ｂ－３）が、両末端にヒドロキシ基、ヒドロキシ基を有する有機基、又はヒドロキシ基を生じうる有機基を有しており、
    　前記撥水剤（Ｂ）の付着量が、前記ポリアクリロニトリル系合成繊維（Ａ）の全質量に対して、０．０５質量％以上１．０質量％以下である、撥水性ポリアクリロニトリル系人工毛髪繊維。
  2. 　さらに変性シリコーン（Ｃ）が前記ポリアクリロニトリル系合成繊維（Ａ）に付着しており、
    　前記変性シリコーン（Ｃ）が、エポキシ基及び／又はアミノ基で置換されたジメチルシロキサン重合体であり、
    　前記変性シリコーン（Ｃ）の付着量が、前記ポリアクリロニトリル系合成繊維（Ａ）の全質量に対して、０．０１質量％以上０．５質量％以下である、請求項１に記載の撥水性ポリアクリロニトリル系人工毛髪繊維。
  3. 　前記デンドリマー系撥水剤（Ｂ－１）が、疎水性末端残基を有する、請求項１又は２に記載の撥水性ポリアクリロニトリル系人工毛髪繊維。
  4. 　前記アルキルウレタン系撥水剤（Ｂ－２）が、ソルビタンに由来する骨格を有する、請求項１又は２に記載の撥水性ポリアクリロニトリル系人工毛髪繊維。
  5. 　さらに帯電防止剤（Ｄ）として、イオン性帯電防止剤（Ｄ１）及び／又は非イオン性帯電防止剤（Ｄ２）が、前記ポリアクリロニトリル系合成繊維（Ａ）に付着しており、
    　前記帯電防止剤（Ｄ）の付着量が、前記ポリアクリロニトリル系合成繊維（Ａ）の全質量に対して、０．０５質量％以上０．３質量％以下である、請求項１又は２に記載の撥水性ポリアクリロニトリル系人工毛髪繊維。
  6. 　前記デンドリマー系撥水剤（Ｂ－１）の付着量と、前記変性シリコーン（Ｃ）の付着量との質量比率が、（Ｂ－１）：（Ｃ）＝１：０．０３以上０．３以下である、請求項１又は２に記載の撥水性ポリアクリロニトリル系人工毛髪繊維。
  7. 　前記アルキルウレタン系撥水剤（Ｂ－２）の付着量と、前記変性シリコーン（Ｃ）の付着量との質量比率が、（Ｂ－２）：（Ｃ）＝１：０．０３以上０．５以下である、請求項１又は２に記載の撥水性ポリアクリロニトリル系人工毛髪繊維。
  8. 　前記撥水剤（Ｂ）の付着量と、前記帯電防止剤（Ｄ）の付着量との質量比率が、（Ｂ）：（Ｄ）＝１：０．１５以上０．７以下である、請求項５に記載の撥水性ポリアクリロニトリル系人工毛髪繊維。
  9. 　前記デンドリマー系撥水剤（Ｂ－１）の付着量と、前記変性シリコーン（Ｃ）の付着量との質量比率が、（Ｂ－１）：（Ｃ）＝１：０．０３以上０．３以下であり、
    　前記デンドリマー系撥水剤（Ｂ－１）の付着量と、前記帯電防止剤（Ｄ）の付着量との質量比率が、（Ｂ－１）：（Ｄ）＝１：０．１５以上０．７以下である、請求項５に記載の撥水性ポリアクリロニトリル系人工毛髪繊維。
  10. 　前記アルキルウレタン系撥水剤（Ｂ－２）の付着量と、前記変性シリコーン（Ｃ）の付着量との質量比率が、（Ｂ―２）：（Ｃ）＝１：０．０３以上０．５以下であり、
    　前記アルキルウレタン系撥水剤（Ｂ―２）の付着量と、前記帯電防止剤（Ｄ）の付着量との質量比率が、（Ｂ―２）：（Ｄ）＝１：０．１５以上０．７以下である、請求項５に記載の撥水性ポリアクリロニトリル系人工毛髪繊維。
  11. 　単繊維繊度が１ｄｔｅｘ以上１００ｄｔｅｘ以下である、請求項１又は２に記載の撥水性ポリアクリロニトリル系人工毛髪繊維。
  12. 　請求項１又は２に記載の撥水性ポリアクリロニトリル系人工毛髪繊維の製造方法であって、
    　アクリロニトリル系重合体を含む紡糸液を湿式紡糸することにより凝固糸条を得ることと、乾燥させる前の被処理糸条を、前記撥水剤（Ｂ）を含む油剤と接触させることとを含む、製造方法。
  13. 　請求項１又は２に記載の撥水性ポリアクリロニトリル系人工毛髪繊維の製造方法であって、
    　乾燥されたポリアクリロニトリル系合成繊維（Ａ）を、前記撥水剤（Ｂ）を含む油剤と接触させることと、該接触処理後の糸状を乾燥させることとを含む、製造方法。
  14. 　請求項１又は２に記載の撥水性ポリアクリロニトリル系人工毛髪繊維を含む、頭飾製品。
  15. 　前記頭飾製品が、ヘアーウィッグ、かつら、ウィービング、ヘアーエクステンション、ブレードヘアー、ヘアーアクセサリー、及びドールヘアーからなる群より選ばれる少なくとも１種である、請求項１４に記載の頭飾製品。
PCT/JP2023/012982 2022-03-30 2023-03-29 撥水性ポリアクリロニトリル系人工毛髪繊維、その製造方法、及び頭飾製品 Ceased WO2023190759A1 (ja)