WO2018025837A1 - Accumulateur au plomb - Google Patents

Accumulateur au plomb Download PDF

Info

Publication number
WO2018025837A1
WO2018025837A1 PCT/JP2017/027816 JP2017027816W WO2018025837A1 WO 2018025837 A1 WO2018025837 A1 WO 2018025837A1 JP 2017027816 W JP2017027816 W JP 2017027816W WO 2018025837 A1 WO2018025837 A1 WO 2018025837A1
Authority
WO
WIPO (PCT)
Prior art keywords
negative electrode
positive electrode
mass
electrode material
lead
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2017/027816
Other languages
English (en)
Japanese (ja)
Inventor
賢 稲垣
真観 京
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GS Yuasa International Ltd
Original Assignee
GS Yuasa International Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GS Yuasa International Ltd filed Critical GS Yuasa International Ltd
Priority to CN201780047806.8A priority Critical patent/CN109565040B/zh
Priority to JP2018531906A priority patent/JP6844622B2/ja
Publication of WO2018025837A1 publication Critical patent/WO2018025837A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un accumulateur au plomb, caractérisé en ce qu'il est pourvu d'une plaque d'électrode positive, d'une plaque d'électrode négative et d'une solution électrolytique ; un matériau d'électrode négative de la plaque d'électrode négative contient du graphite ou de la fibre de carbone et un élément de baryum, à raison de 1,1 % en masse ou plus sous forme de sulfate de baryum ; et un matériau d'électrode positive de la plaque d'électrode positive contient un élément d'étain.
PCT/JP2017/027816 2016-08-05 2017-08-01 Accumulateur au plomb Ceased WO2018025837A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN201780047806.8A CN109565040B (zh) 2016-08-05 2017-08-01 铅蓄电池
JP2018531906A JP6844622B2 (ja) 2016-08-05 2017-08-01 鉛蓄電池

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2016-154919 2016-08-05
JP2016154919 2016-08-05

Publications (1)

Publication Number Publication Date
WO2018025837A1 true WO2018025837A1 (fr) 2018-02-08

Family

ID=61073456

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/027816 Ceased WO2018025837A1 (fr) 2016-08-05 2017-08-01 Accumulateur au plomb

Country Status (3)

Country Link
JP (1) JP6844622B2 (fr)
CN (1) CN109565040B (fr)
WO (1) WO2018025837A1 (fr)

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0414758A (ja) * 1990-05-02 1992-01-20 Matsushita Electric Ind Co Ltd 液入充済鉛蓄電池
JPH04155767A (ja) * 1990-10-19 1992-05-28 Nippon Telegr & Teleph Corp <Ntt> 磁気光学的記録再生装置
JP2001155723A (ja) * 1999-11-26 2001-06-08 Shin Kobe Electric Mach Co Ltd 密閉形鉛蓄電池及びその製造方法
WO2011090113A1 (fr) * 2010-01-21 2011-07-28 株式会社Ｇｓユアサ Plaque cathodique pour batterie au plomb, procédé de production correspondant, et batterie au plomb
WO2012043556A1 (fr) * 2010-09-29 2012-04-05 株式会社Ｇｓユアサ Batterie d'accumulateurs au plomb et véhicule à arrêt au ralenti l'utilisant
JP2013140677A (ja) * 2011-12-28 2013-07-18 Gs Yuasa Corp 液式鉛蓄電池とこれを用いた電池システム
JP2016152131A (ja) * 2015-02-17 2016-08-22 株式会社Ｇｓユアサ 鉛蓄電池

Family Cites Families (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005317332A (ja) * 2004-04-28 2005-11-10 Furukawa Battery Co Ltd:The 鉛蓄電池
AU2005336806B2 (en) * 2005-09-27 2010-09-09 The Furukawa Battery Co., Ltd. Lead storage battery and process for producing the same
CN101123139B (zh) * 2007-09-29 2010-11-03 李中奇 一种超级蓄电池用双性极板
KR20120132491A (ko) * 2010-03-01 2012-12-05 신코베덴키 가부시키가이샤 납 축전지
CN103035957B (zh) * 2011-09-30 2014-10-29 松下蓄电池(沈阳)有限公司 储能用铅蓄电池
CN103035923B (zh) * 2012-12-18 2014-10-22 超威电源有限公司 一种耐低温蓄电池内化成铅膏
CN103066295B (zh) * 2012-12-18 2014-11-12 超威电源有限公司 一种适用于高温地区的蓄电池内化成铅膏
JP5769096B2 (ja) * 2014-09-05 2015-08-26 株式会社Ｇｓユアサ 鉛蓄電池
EP3035433B1 (fr) * 2014-12-18 2020-02-19 GS Yuasa International Ltd. Batterie au plomb
JP6070684B2 (ja) * 2014-12-24 2017-02-01 株式会社Ｇｓユアサ 制御弁式鉛蓄電池

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0414758A (ja) * 1990-05-02 1992-01-20 Matsushita Electric Ind Co Ltd 液入充済鉛蓄電池
JPH04155767A (ja) * 1990-10-19 1992-05-28 Nippon Telegr & Teleph Corp <Ntt> 磁気光学的記録再生装置
JP2001155723A (ja) * 1999-11-26 2001-06-08 Shin Kobe Electric Mach Co Ltd 密閉形鉛蓄電池及びその製造方法
WO2011090113A1 (fr) * 2010-01-21 2011-07-28 株式会社Ｇｓユアサ Plaque cathodique pour batterie au plomb, procédé de production correspondant, et batterie au plomb
WO2012043556A1 (fr) * 2010-09-29 2012-04-05 株式会社Ｇｓユアサ Batterie d'accumulateurs au plomb et véhicule à arrêt au ralenti l'utilisant
JP2013140677A (ja) * 2011-12-28 2013-07-18 Gs Yuasa Corp 液式鉛蓄電池とこれを用いた電池システム
JP2016152131A (ja) * 2015-02-17 2016-08-22 株式会社Ｇｓユアサ 鉛蓄電池

Also Published As

Publication number Publication date
CN109565040A (zh) 2019-04-02
JPWO2018025837A1 (ja) 2019-06-27
JP6844622B2 (ja) 2021-03-17
CN109565040B (zh) 2022-03-01

Similar Documents

Publication Publication Date Title
JP6635346B2 (ja) 鉛蓄電池
JP6202477B1 (ja) 鉛蓄電池
JP5857962B2 (ja) 鉛蓄電池
JP6115796B2 (ja) 鉛蓄電池
EP2544292A1 (fr) Accumulateur au plomb
WO2012086008A1 (fr) Batterie d&#39;accumulateurs au plomb
US10003069B2 (en) Lead-acid battery
JP6311799B2 (ja) 鉛蓄電池
JP6660072B2 (ja) 鉛蓄電池用正極板及び該正極板を用いた鉛蓄電池及び該鉛蓄電池用正極板の製造方法
JP6458829B2 (ja) 鉛蓄電池
US20160240857A1 (en) Lead-acid battery
JP6388094B1 (ja) 鉛蓄電池
JP6136079B2 (ja) 鉛蓄電池
JP5545975B2 (ja) 鉛蓄電池用正極活物質及びそれを充填して成る鉛蓄電池用正極板
JP6339030B2 (ja) 鉛蓄電池
JP6628070B2 (ja) 制御弁式鉛蓄電池用の正極板の製造法
JP6582636B2 (ja) 鉛蓄電池
JP6844622B2 (ja) 鉛蓄電池
JP2017174821A (ja) 鉛蓄電池
KR20200057465A (ko) 납축전지의 극판용 음극 활물질 페이스트 조성물, 및 이의 제조 방법
JPWO2018100639A1 (ja) 鉛蓄電池及びその製造方法
JP2018170303A (ja) 鉛蓄電池
JP2022138753A (ja) 鉛蓄電池
JP2008034286A (ja) 密閉式鉛蓄電池

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17836941

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2018531906

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase