WO2012017846A1 - Composition de revêtement monocomposant, photocatalyseur l'utilisant, film de revêtement composé de celle-ci, et procédé de fabrication associé - Google Patents

Composition de revêtement monocomposant, photocatalyseur l'utilisant, film de revêtement composé de celle-ci, et procédé de fabrication associé Download PDF

Info

Publication number
WO2012017846A1
WO2012017846A1 PCT/JP2011/066806 JP2011066806W WO2012017846A1 WO 2012017846 A1 WO2012017846 A1 WO 2012017846A1 JP 2011066806 W JP2011066806 W JP 2011066806W WO 2012017846 A1 WO2012017846 A1 WO 2012017846A1
Authority
WO
WIPO (PCT)
Prior art keywords
silica
powder
polymer
coating film
composite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2011/066806
Other languages
English (en)
Japanese (ja)
Inventor
裕仁 長田
金　仁華
培新 諸
建軍 袁
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kawamura Institute of Chemical Research
DIC Corp
Original Assignee
Kawamura Institute of Chemical Research
DIC Corp
Dainippon Ink and Chemicals Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kawamura Institute of Chemical Research, DIC Corp, Dainippon Ink and Chemicals Co Ltd filed Critical Kawamura Institute of Chemical Research
Priority to JP2012502039A priority Critical patent/JP5087184B2/ja
Publication of WO2012017846A1 publication Critical patent/WO2012017846A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne une poudre ayant une fonction photocatalytique suffisante même sous lumière visible, et une composition de revêtement monocomposant la contenant, la composition étant conçue pour un revêtement direct sur un substrat. La poudre comprend un composite dans lequel des particules d'oxyde de titane/d'oxyde de tungstène ayant des diamètres de particule de l'ordre du nanomètre sont fixées par cuisson sur une structure de l'ordre du nanomètre ayant de la silice comme composant principal. La poudre a une fonction photocatalytique supérieure à celle obtenue lorsque les particules d'oxyde de titane/d'oxyde de tungstène seules sont utilisées comme matière de départ. Une composition de revêtement monocomposant est obtenue par mélange de ces poudres avec une résine ayant un squelette de polysiloxane. L'application de la composition de revêtement sur une variété de substrats, le séchage de la composition, et l'irradiation de la composition avec une lumière spécifique permet l'exposition des particules d'oxyde de titane et d'oxyde de tungstène sur la surface du film de revêtement. Un film de revêtement ainsi obtenu présente une fonction photocatalytique sous lumière visible et présente une surface ultra-hydrophile.
PCT/JP2011/066806 2010-08-06 2011-07-25 Composition de revêtement monocomposant, photocatalyseur l'utilisant, film de revêtement composé de celle-ci, et procédé de fabrication associé Ceased WO2012017846A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2012502039A JP5087184B2 (ja) 2010-08-06 2011-07-25 １液型塗料組成物とこれに用いる光触媒、その塗膜、及びそれらの製造方法

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2010177352 2010-08-06
JP2010-177352 2010-08-06
JP2010-276892 2010-12-13
JP2010276892 2010-12-13

Publications (1)

Publication Number Publication Date
WO2012017846A1 true WO2012017846A1 (fr) 2012-02-09

Family

ID=45559349

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2011/066806 Ceased WO2012017846A1 (fr) 2010-08-06 2011-07-25 Composition de revêtement monocomposant, photocatalyseur l'utilisant, film de revêtement composé de celle-ci, et procédé de fabrication associé

Country Status (3)

Country Link
JP (1) JP5087184B2 (fr)
TW (1) TW201229161A (fr)
WO (1) WO2012017846A1 (fr)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2012245481A (ja) * 2011-05-30 2012-12-13 Dic Corp 可視光応答型光触媒及びその製造方法
WO2014080606A1 (fr) * 2012-11-22 2014-05-30 パナソニック株式会社 Composition de résine dispersée dans un semi-conducteur optique, son procédé de production et élément antibactérien
JP2015072159A (ja) * 2013-10-02 2015-04-16 岩宮　陽子 放射線遮蔽シート用コーティング組成物、放射線遮蔽シートの製造方法、および放射線遮蔽シート
JP2015134918A (ja) * 2013-12-20 2015-07-27 旭化成ケミカルズ株式会社 塗膜、水性組成物、及び塗装製品
WO2016157841A1 (fr) * 2015-03-31 2016-10-06 日本曹達株式会社 Structure supportée par un photocatalyseur et composition destinée à former une couche adhésive
WO2018170435A1 (fr) * 2017-03-17 2018-09-20 Nitto Denko Corporation Compositions superhydrophobes en vrac
JP2019056070A (ja) * 2017-09-22 2019-04-11 シャープ株式会社 水系光触媒塗料および浄化方法
KR20200020167A (ko) * 2018-08-16 2020-02-26 공주대학교 산학협력단 가시광선 광촉매 반응을 위해 신호등을 코팅하는 방법
WO2021261261A1 (fr) * 2020-06-25 2021-12-30 Dic株式会社 Agent de revêtement pour substrats en papier ou substrats en matière plastique, ainsi que substrats en papier, substrats en matière plastique, récipients, et matériau d'emballage qui ont une couche de revêtement constituée dudit agent de revêtement

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2998374A4 (fr) * 2013-05-13 2016-06-15 Panasonic Ip Man Co Ltd Composition d'agent de revêtement et élément antimicrobien/antiviral
TWI523919B (zh) 2014-12-04 2016-03-01 財團法人工業技術研究院 具有防霧與隔熱功能之塗料組成物、其製法及薄膜

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0226878A (ja) * 1988-07-14 1990-01-29 Natl Inst For Res In Inorg Mater チタニアーシリカ複合酸化物の繊維構造体の製造法
JPH10277400A (ja) * 1997-04-03 1998-10-20 Agency Of Ind Science & Technol 酸化チタンを担持したシリカ三次元網状構造光触媒およびその製造方法
JP2005325253A (ja) * 2004-05-14 2005-11-24 Shin Etsu Chem Co Ltd 機能性無機フィラー含有コーティング用エマルジョン組成物
JP2006213888A (ja) * 2005-02-07 2006-08-17 Kawamura Inst Of Chem Res 有機無機複合材料及びその製造方法
JP2008043848A (ja) * 2006-08-11 2008-02-28 Kansai Paint Co Ltd 光半導体微粒子
WO2009031489A1 (fr) * 2007-09-03 2009-03-12 Kawamura Institute Of Chemical Research Procédé de fabrication d'une structure recouverte d'un composite de nanostructure, structure recouverte d'un composite de nanostructure et réacteur utilisant la structure recouverte d'un composite de nanostructure
JP2010022963A (ja) * 2008-07-22 2010-02-04 Shinetsu Quartz Prod Co Ltd 繊維状光触媒体及びその製造方法並びに浄化装置

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2580537B2 (ja) * 1994-06-27 1997-02-12 工業技術院長 シリカ球状粒子からなる三次元網状構造体
DE19847630A1 (de) * 1998-10-15 2000-04-20 Basf Ag Siliciumdioxid mit Meso- und Mikroporen
JP3910322B2 (ja) * 1999-09-24 2007-04-25 三ツ星ベルト株式会社 超微粒子担持物の製造方法
JP2008284411A (ja) * 2007-05-15 2008-11-27 Osaka Univ 中空状多孔質シェル層に包含される光触媒及びその作製方法
TW201129616A (en) * 2009-11-30 2011-09-01 Dainippon Ink & Chemicals Silica nanofiber/metallic oxide nanocrystalline complex, method for producing the same and luminophor

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0226878A (ja) * 1988-07-14 1990-01-29 Natl Inst For Res In Inorg Mater チタニアーシリカ複合酸化物の繊維構造体の製造法
JPH10277400A (ja) * 1997-04-03 1998-10-20 Agency Of Ind Science & Technol 酸化チタンを担持したシリカ三次元網状構造光触媒およびその製造方法
JP2005325253A (ja) * 2004-05-14 2005-11-24 Shin Etsu Chem Co Ltd 機能性無機フィラー含有コーティング用エマルジョン組成物
JP2006213888A (ja) * 2005-02-07 2006-08-17 Kawamura Inst Of Chem Res 有機無機複合材料及びその製造方法
JP2008043848A (ja) * 2006-08-11 2008-02-28 Kansai Paint Co Ltd 光半導体微粒子
WO2009031489A1 (fr) * 2007-09-03 2009-03-12 Kawamura Institute Of Chemical Research Procédé de fabrication d'une structure recouverte d'un composite de nanostructure, structure recouverte d'un composite de nanostructure et réacteur utilisant la structure recouverte d'un composite de nanostructure
JP2010022963A (ja) * 2008-07-22 2010-02-04 Shinetsu Quartz Prod Co Ltd 繊維状光触媒体及びその製造方法並びに浄化装置

Cited By (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2012245481A (ja) * 2011-05-30 2012-12-13 Dic Corp 可視光応答型光触媒及びその製造方法
WO2014080606A1 (fr) * 2012-11-22 2014-05-30 パナソニック株式会社 Composition de résine dispersée dans un semi-conducteur optique, son procédé de production et élément antibactérien
CN104603208A (zh) * 2012-11-22 2015-05-06 松下知识产权经营株式会社 光半导体分散树脂组合物及其制造方法以及抗菌性部件
CN104603208B (zh) * 2012-11-22 2016-10-19 松下知识产权经营株式会社 光半导体分散树脂组合物及其制造方法以及抗菌性部件
JPWO2014080606A1 (ja) * 2012-11-22 2017-01-05 パナソニックＩｐマネジメント株式会社 光半導体分散樹脂組成物及びその製造方法、並びに抗菌性部材
JP2015072159A (ja) * 2013-10-02 2015-04-16 岩宮　陽子 放射線遮蔽シート用コーティング組成物、放射線遮蔽シートの製造方法、および放射線遮蔽シート
JP2017141474A (ja) * 2013-12-20 2017-08-17 旭化成株式会社 塗膜、水性組成物、及び塗装製品
JP2015134918A (ja) * 2013-12-20 2015-07-27 旭化成ケミカルズ株式会社 塗膜、水性組成物、及び塗装製品
JP2017125218A (ja) * 2013-12-20 2017-07-20 旭化成株式会社 塗膜、水性組成物、及び塗装製品
JPWO2016157841A1 (ja) * 2015-03-31 2018-01-11 日本曹達株式会社 光触媒担持構造体及び接着層形成用組成物
WO2016157841A1 (fr) * 2015-03-31 2016-10-06 日本曹達株式会社 Structure supportée par un photocatalyseur et composition destinée à former une couche adhésive
WO2018170435A1 (fr) * 2017-03-17 2018-09-20 Nitto Denko Corporation Compositions superhydrophobes en vrac
JP2020512445A (ja) * 2017-03-17 2020-04-23 日東電工株式会社 バルク超撥水性組成物
JP7018068B2 (ja) 2017-03-17 2022-02-09 日東電工株式会社 バルク超撥水性組成物
JP2019056070A (ja) * 2017-09-22 2019-04-11 シャープ株式会社 水系光触媒塗料および浄化方法
JP7034644B2 (ja) 2017-09-22 2022-03-14 シャープ株式会社 水系光触媒塗料および浄化方法
KR20200020167A (ko) * 2018-08-16 2020-02-26 공주대학교 산학협력단 가시광선 광촉매 반응을 위해 신호등을 코팅하는 방법
KR102124251B1 (ko) * 2018-08-16 2020-06-17 공주대학교 산학협력단 폴리카보네이트 재질의 신호등에 텅스텐 옥사이드를 코팅하는 방법 및 텅스텐 옥사이드가 코팅된 폴리카보네이트 재질의 신호등
WO2021261261A1 (fr) * 2020-06-25 2021-12-30 Dic株式会社 Agent de revêtement pour substrats en papier ou substrats en matière plastique, ainsi que substrats en papier, substrats en matière plastique, récipients, et matériau d'emballage qui ont une couche de revêtement constituée dudit agent de revêtement
JPWO2021261261A1 (fr) * 2020-06-25 2021-12-30
JP7131722B2 (ja) 2020-06-25 2022-09-06 Dic株式会社 紙基材用又はプラスチック基材用コーティング剤、並びに該コーティング剤のコーティング層を有する紙基材、プラスチック基材、容器及び包装材

Also Published As

Publication number Publication date
TW201229161A (en) 2012-07-16
JPWO2012017846A1 (ja) 2013-10-03
JP5087184B2 (ja) 2012-11-28

Similar Documents

Publication Publication Date Title
JP5087184B2 (ja) １液型塗料組成物とこれに用いる光触媒、その塗膜、及びそれらの製造方法
TW473400B (en) Modified photocatalyst sol
CN1152927C (zh) 光催化剂涂层剂组合物及载有光催化剂的构造体
JPWO2000030747A1 (ja) 変性光触媒ゾル
CN1756599A (zh) 光催化材料
CN102167954A (zh) 涂料组合物及其用途
JP2009019072A (ja) 水系有機・無機複合組成物
JP2017160117A (ja) シリカ粒子及びその製造方法、光触媒形成用組成物、光触媒、並びに、構造体
JP4738367B2 (ja) 水系有機・無機複合組成物
JP2019048758A (ja) シリカチタニア複合エアロゲル粒子、シリカチタニア複合エアロゲル粒子の製造方法、光触媒形成用組成物、光触媒、及び構造体
JP5368720B2 (ja) 光触媒塗膜及び光触媒組成物
JP5692892B2 (ja) 塗膜及び水系有機無機複合組成物
JP4635185B2 (ja) ポリエステル繊維の光触媒コーティング方法
JP5269453B2 (ja) 機能付与釉薬
JP2009101287A (ja) 変性光触媒ゾル及びその製造方法
JP2013139386A (ja) ハイブリッドチタニア粉末の製造方法、ハイブリッドチタニア粉末、機能付与液及び製品
JP5245150B2 (ja) ポリエステル成形体の光触媒コーティング方法
JP6953932B2 (ja) シリカチタニア複合エアロゲル粒子、シリカチタニア複合エアロゲル粒子の製造方法、光触媒形成用組成物、光触媒、及び構造体
JP2006136758A (ja) 光触媒組成物、および光触媒部材
JP2006136782A (ja) 光触媒アルミニウム部材
JP6969240B2 (ja) 酸化チタンエアロゲル粒子、酸化チタンエアロゲル粒子の製造方法、光触媒形成用組成物、光触媒、及び構造体
JP3806998B2 (ja) 光触媒組成物とその形成剤および光触媒組成物付き基体
JP7020007B2 (ja) シリカチタニア複合エアロゲル粒子、シリカチタニア複合エアロゲル粒子の製造方法、光触媒形成用組成物、光触媒、及び構造体
JP2019048757A (ja) シリカチタニア複合エアロゲル粒子、シリカチタニア複合エアロゲル粒子の製造方法、光触媒形成用組成物、光触媒、及び構造体
JP7077550B2 (ja) 酸化チタンエアロゲル粒子、酸化チタンエアロゲル粒子の製造方法、光触媒形成用組成物、光触媒、及び構造体

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 2012502039

Country of ref document: JP

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 11814476

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 11814476

Country of ref document: EP

Kind code of ref document: A1