WO1997030204A1 - Procede permettant d'affaiblir la tendance de tissu lyocellulaire a une fibrillation primaire - Google Patents

Procede permettant d'affaiblir la tendance de tissu lyocellulaire a une fibrillation primaire Download PDF

Info

Publication number
WO1997030204A1
WO1997030204A1 PCT/GB1997/000397 GB9700397W WO9730204A1 WO 1997030204 A1 WO1997030204 A1 WO 1997030204A1 GB 9700397 W GB9700397 W GB 9700397W WO 9730204 A1 WO9730204 A1 WO 9730204A1
Authority
WO
WIPO (PCT)
Prior art keywords
fabric
hypochlorite
dyeing
solution
washing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/GB1997/000397
Other languages
English (en)
Inventor
Karen Jane Cooper
James Martin Taylor
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Courtaulds Fibres Holdings Ltd
Original Assignee
Courtaulds Fibres Holdings Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Courtaulds Fibres Holdings Ltd filed Critical Courtaulds Fibres Holdings Ltd
Priority to AU18006/97A priority Critical patent/AU1800697A/en
Priority to EP97903449A priority patent/EP0888475A1/fr
Publication of WO1997030204A1 publication Critical patent/WO1997030204A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Il est possible d'affaiblir la tendance d'un tissu lyocellulaire à une fibrillation primaire après teinture et lavage en le mettant en contact, avant teinture, à haute température, avec une solution aqueuse d'un agent oxydant tel que de l'hypochlorite ou du peroxyde d'hydrogène. Selon la nature et la concentration de l'agent oxydant, le tissu obtenu ne connaîtra quasiment pas de fibrillation à la suite de teinture et de lavage ultérieurs ou sera susceptible d'avoir, après une teinture et un lavage ultérieurs, un toucher de peau de pêche.
PCT/GB1997/000397 1996-02-14 1997-02-13 Procede permettant d'affaiblir la tendance de tissu lyocellulaire a une fibrillation primaire Ceased WO1997030204A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
AU18006/97A AU1800697A (en) 1996-02-14 1997-02-13 Method of reducing the tendency of a lyocell fabric to primary fibrillation
EP97903449A EP0888475A1 (fr) 1996-02-14 1997-02-13 Procede permettant d'affaiblir la tendance de tissu lyocellulaire a une fibrillation primaire

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
GBGB9602991.3A GB9602991D0 (en) 1996-02-14 1996-02-14 Lyocell fabric treatment to reduce fibrillation tendency
GB9602991.3 1996-02-14

Publications (1)

Publication Number Publication Date
WO1997030204A1 true WO1997030204A1 (fr) 1997-08-21

Family

ID=10788673

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/GB1997/000397 Ceased WO1997030204A1 (fr) 1996-02-14 1997-02-13 Procede permettant d'affaiblir la tendance de tissu lyocellulaire a une fibrillation primaire

Country Status (6)

Country Link
EP (1) EP0888475A1 (fr)
KR (1) KR19990082009A (fr)
AU (1) AU1800697A (fr)
GB (1) GB9602991D0 (fr)
TW (1) TW336965B (fr)
WO (1) WO1997030204A1 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1999002767A1 (fr) * 1997-07-07 1999-01-21 Novo Nordisk A/S Procede de pre-fibrillation de fibres lyocellulaires
WO2002103104A3 (fr) * 2001-06-15 2003-11-27 Tencel Ltd Teinture et finissage de fibres lyocell
WO2021180817A1 (fr) 2020-03-12 2021-09-16 Lenzing Aktiengesellschaft Procédé pour la réduction du comportement de boulochage d'un tissu contenant des fibres cellulosiques artificielles ou constitué de celles-ci
CN114990904A (zh) * 2022-06-21 2022-09-02 青岛大学 一种莱赛尔针织物节能、环保染色工艺
CN115627632A (zh) * 2022-10-12 2023-01-20 中国纺织科学研究院有限公司 一种莱赛尔短纤维的制备方法及莱赛尔短纤维
WO2024218257A1 (fr) 2023-04-21 2024-10-24 Lenzing Aktiengesellschaft Traitement à l'ozone de tissus en fibres synthétiques cellulosiques

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH01298273A (ja) * 1988-05-25 1989-12-01 Toyobo Co Ltd 再生セルロース系繊維織編物の加工方法
WO1992007124A1 (fr) * 1990-10-12 1992-04-30 Courtaulds Plc Traitement de fibres
WO1994020656A1 (fr) * 1993-03-10 1994-09-15 Courtaulds Fibres (Holdings) Limited Traitement de fibres
WO1995030043A1 (fr) * 1994-05-03 1995-11-09 Courtaulds Fibres (Holdings) Limited Traitement d'une etoffe en fibre lyocell (fibre de cellulose tissee dans un solvant), destine a reduire la tendance de cette fibre a la fibrillation
WO1995035399A1 (fr) * 1994-06-22 1995-12-28 Courtaulds Fibres (Holdings) Limited Fibre de cellulose filee avec solvant et son procede de production

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH01298273A (ja) * 1988-05-25 1989-12-01 Toyobo Co Ltd 再生セルロース系繊維織編物の加工方法
WO1992007124A1 (fr) * 1990-10-12 1992-04-30 Courtaulds Plc Traitement de fibres
WO1994020656A1 (fr) * 1993-03-10 1994-09-15 Courtaulds Fibres (Holdings) Limited Traitement de fibres
WO1995030043A1 (fr) * 1994-05-03 1995-11-09 Courtaulds Fibres (Holdings) Limited Traitement d'une etoffe en fibre lyocell (fibre de cellulose tissee dans un solvant), destine a reduire la tendance de cette fibre a la fibrillation
WO1995035399A1 (fr) * 1994-06-22 1995-12-28 Courtaulds Fibres (Holdings) Limited Fibre de cellulose filee avec solvant et son procede de production

Non-Patent Citations (5)

* Cited by examiner, † Cited by third party
Title
BREIER, RUDI: "Die Veredelung von Lyocellfasern - Ein Erfahrungsbericht", LENZINGER BERICHTE, vol. 94, no. 9, September 1994 (1994-09-01), pages 99 - 101, XP002032693 *
CHEMICAL ABSTRACTS, vol. 105, no. 18, 3 November 1986, Columbus, Ohio, US; abstract no. 154531x, page 72; column 1; XP002032694 *
DATABASE WPI Section Ch Week 9003, Derwent World Patents Index; Class A11, AN 90-018791, XP002032695 *
MING G ET AL: "TREATING FABRIC THROUGH ALKALINE OXIDATION FOR A SILK-LIKE EFFECT", AMERICAN DYESTUFF REPORTER, vol. 85, no. 7, July 1996 (1996-07-01), pages 20, 22 - 24, 26, XP000598049 *
SHENAI, V. A.; NAIK, V. G.: "Hypochlorite oxidation of cellulose in presence of lead oxide", TEXT. DYER PRINTER, vol. 19, no. 16, 1986, pages 17 - 22 *

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1999002767A1 (fr) * 1997-07-07 1999-01-21 Novo Nordisk A/S Procede de pre-fibrillation de fibres lyocellulaires
WO2002103104A3 (fr) * 2001-06-15 2003-11-27 Tencel Ltd Teinture et finissage de fibres lyocell
WO2021180817A1 (fr) 2020-03-12 2021-09-16 Lenzing Aktiengesellschaft Procédé pour la réduction du comportement de boulochage d'un tissu contenant des fibres cellulosiques artificielles ou constitué de celles-ci
CN114990904A (zh) * 2022-06-21 2022-09-02 青岛大学 一种莱赛尔针织物节能、环保染色工艺
CN115627632A (zh) * 2022-10-12 2023-01-20 中国纺织科学研究院有限公司 一种莱赛尔短纤维的制备方法及莱赛尔短纤维
WO2024218257A1 (fr) 2023-04-21 2024-10-24 Lenzing Aktiengesellschaft Traitement à l'ozone de tissus en fibres synthétiques cellulosiques

Also Published As

Publication number Publication date
EP0888475A1 (fr) 1999-01-07
GB9602991D0 (en) 1996-04-10
KR19990082009A (ko) 1999-11-15
TW336965B (en) 1998-07-21
AU1800697A (en) 1997-09-02

Similar Documents

Publication Publication Date Title
US5759210A (en) Lyocell fabric treatment to reduce fibrillation tendency
JP3336012B2 (ja) 繊維の処理
US5709716A (en) Fibre treatment
EP0705358B1 (fr) Traitement pour tissus
JPWO1997008370A1 (ja) セルロースマルチフィラメント糸及びそれからなる布帛
EP0888475A1 (fr) Procede permettant d'affaiblir la tendance de tissu lyocellulaire a une fibrillation primaire
EP1599630B1 (fr) Procede de production d'un tissu de fibre lyocell teint et apprete
CN1272499C (zh) 莱赛尔织物的染色和整理
GB2314568A (en) Fibre finishing treatment
KR100963697B1 (ko) 모드 직물의 염색 및 마무리 가공방법
JPH11502267A (ja) 繊維の処理
WO2024218257A1 (fr) Traitement à l'ozone de tissus en fibres synthétiques cellulosiques
WO1998005815A1 (fr) Traitement d'etoffes
CN109371608A (zh) 天丝与纤维素纤维混纺面料的丝光工艺
GB2403956A (en) Treatment of lyocell-containing fibres or fabrics with solution of a multifunctional carboxylic acid and solution of a Lewis acid, followed by heat treatment

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AL AM AT AU AZ BA BB BG BR BY CA CH CN CU CZ DE DK EE ES FI GB GE HU IL IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK TJ TM TR TT UA UG US UZ VN YU AM AZ BY KG KZ MD RU TJ TM

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): KE LS MW SD SZ UG AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 1019980705728

Country of ref document: KR

WWE Wipo information: entry into national phase

Ref document number: 1997903449

Country of ref document: EP

NENP Non-entry into the national phase

Ref country code: JP

Ref document number: 97529092

Format of ref document f/p: F

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

WWP Wipo information: published in national office

Ref document number: 1997903449

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 1019980705728

Country of ref document: KR

WWW Wipo information: withdrawn in national office

Ref document number: 1997903449

Country of ref document: EP

WWW Wipo information: withdrawn in national office

Ref document number: 1019980705728

Country of ref document: KR