WO1997001591A1 - Composition de resine epoxy pour cartes a circuits imprimes et plaque feuilletee produite avec cette resine - Google Patents

Composition de resine epoxy pour cartes a circuits imprimes et plaque feuilletee produite avec cette resine Download PDF

Info

Publication number
WO1997001591A1
WO1997001591A1 PCT/JP1996/001707 JP9601707W WO9701591A1 WO 1997001591 A1 WO1997001591 A1 WO 1997001591A1 JP 9601707 W JP9601707 W JP 9601707W WO 9701591 A1 WO9701591 A1 WO 9701591A1
Authority
WO
WIPO (PCT)
Prior art keywords
epoxy resin
printed wiring
resin composition
bisphenol
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP1996/001707
Other languages
English (en)
French (fr)
Inventor
Michitoshi Arata
Shigeo Sase
Nozomu Takano
Tomio Fukuda
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Resonac Corp
Original Assignee
Hitachi Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hitachi Chemical Co Ltd filed Critical Hitachi Chemical Co Ltd
Priority to HK98111083.8A priority Critical patent/HK1015388B/xx
Priority to KR1019970709418A priority patent/KR100271050B1/ko
Priority to EP96918862A priority patent/EP0835892B1/en
Priority to DE69610771T priority patent/DE69610771T2/de
Publication of WO1997001591A1 publication Critical patent/WO1997001591A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Description

明 細 書 印刷配線板用エポキシ樹脂組成物及びそれを用 t、た積層板 技術分野
本発明は、 印刷配線板などの製造に用いられる印刷配線板用ェポキシ樹脂組成 物及びそれを用いた印刷配線板用積層板に関する。 背景技術
電子機器の小型化、 高性能化に伴い、 その中に搭載される印刷配線板は、 高多 層化、 薄物化、 スルーホールの小径化及び穴間隔の減少などによる高密度化が進 行している。 さらに近年では、 半導体チップを印刷配線板上に直接搭載し樹脂封 止した、 プラスチックビングリ ツ ドアレイやプラスチックボールグリ ッ ドアレイ 等の半導体パッケージに、 印刷配線板が用いられるようになつている。 半導体パ ッケージに用いられる場合、 印刷配線板はその製造工程において 1 7 5 °C以上の 高温でワイヤボンディングゃ樹脂封止といった工程を経ることになる。 その際に 印刷配線板の強度や弾性率が不足するとボンディ ングワイヤの接続不良や樹脂封 止後のそり、 ねじれ等の問題が発生する。 1 7 5 °C以上の高温域での強度や弾性 率等の高温特性を向上させるためには、 印刷配線板は従来以上の高い T g (ガラ ス転移温度） を有していることが必要である。 半導体パッケージ用の印刷配線板 はこれまで以上の高密度配線が要求されており、 絶縁信頼性が重要である。 これらの要求に対して、 印刷配線板の絶縁材料としてはエポキシ樹脂の高 T g 化が進んでいる。 高 T gの手法としては、 特開昭 6 0 - 1 5 5 4 5 3号公報に見 られるように、 多官能エポキシ樹脂をジシアンジアミ ドで硬化させる系が広く検 討されている。 し力、しな力 ら、 ジシアンジアミ ド硬化系では吸湿性が高くなる欠 点があり、 今後の印刷配線板の更なる高密度ィヒに伴う高い絶縁信頼性を満足する ことは困難となっており、 特に絶縁特性の中でも、 絶縁材料上又は絶縁材料内の 配線や回路パターンあるいは電極などを構成する金属が、 高湿度環境下、 電位差 の作用によって絶縁材料上又は絶縁材料内を移行する金属マイグレーシヨン （電 食） の発生は非常に大きな問題となってきた。
これに対して、 多官能性フヱノール類を硬化剤に用いた印刷配線板は、 吸水率 が低く耐電食性が良好となる。 ただし、 このような多官能性フヱノール類を用い た印刷配線板は、 多官能性フヱノール類の種類によっては加熱処理時に変色する 問題が生じる場合がある。 特公昭 6 2 - 2 8 1 6 8号公報には、 この加熱変色性 を向上させる目的で、 硬化剤にフヱノール又はビスフヱノール Aを主原料とする ハイオルソフェノール ·ホルムアルデヒ ド樹脂を配合した系が提案されている が、 1 7 5 °C以上の高温での使用に耐える T gを有する印刷配線板は得られてい ない。
本発明は、 かかる状況に鑑みなされたもので、 印刷配線板の製造に用いた場合 に吸湿性が低く、 優れた耐熱性と高温特性、 耐電食性、 耐加熱変色性を有し、 か つ高い T gを有する印刷配線板を製造することができるエポキシ樹脂組成物を提 供することを目的とする。
本発明はまた、 上記エポキシ樹脂組成物を用いた優れた耐熱性と高温特性、 耐 電食性、 耐加熱変色性を有し、 かつ高い T gを有する印刷配線板用積層板を提供 することを目的とする。 発明の開示
すなわち、 本発明は、 （a ) フヱノール類とヒドロキシベンズアルデヒドとの 縮合物をエポキシ化して得られるエポキシ樹脂及び （b ) ビスフエノール Aとホ ルムアルデヒドの縮合物、 ( c ) 難燃剤、 （d ) 硬化促進剤を必須成分として配 合してなる印刷配線板用エポキシ樹脂組成物を提供するものである。
また、 本発明は、 上記の印刷配線板用エポキシ樹脂組成物からなる樹脂ワニス を基材に含浸、 乾燥させて得られたプリプレ.グを重ね合わせ、 その片面若しくは 両面に金属箔を張り合せ、 加熱加圧成形して得られる印刷配線板用積層板を提供 するものである。 発明を実施するための最良の形態
以下、 本発明を詳細に説明する。 ( a ) のエポキシ樹脂はフエノール類とヒ ドロキシベンズアルデヒ ドとの縮合 物をエポキシ化して得られる。 フエノール類としては、 フエノール、 クレゾ一 ル、 プロピル基、 t e r t —ブチル基などのアルキル基を有する一価フエノール 類等が好ましく用いられ、 フヱノールが特に好ましく用いられる。 ヒ ドロキシべ ンズアルデヒ ドとしては、 サリチルアルデヒ ド、 m—ヒ ドロキシベンズアルデヒ ド、 p —ヒ ドロキシベンズアルデヒ ド、 バニリン、 シリンガアルデヒ ド、 β—レ ゾルシルアルデヒ ド、 プロ トカテチュアルデヒ ド等が好ましく用いられ、 サリチ ルアルデヒ ドが特に好ましく用いられる。
フエノール類とヒ ドロキシベンズアルデヒ ドとの縮合反応は特に限定されない が酸触媒下においてフエノール類 1モルに対してヒ ドロキシベンズアルデヒ ド 0. 1〜3 . 0モル、 好ましくは 0. 3〜1 . 5モルを反応させることが好まし い。
得られた縮合物をェピクロルヒ ドリンなどのエポキシ化剤によりエポキシ化す ると （a ) のエポキシ樹脂が得られる。
( a ) のエポキシ樹脂の原料として用いられるフエノール類、 ヒ ドロキシベン ズアルデヒ ド、 エポキシ化剤の種類については特に限定するものではなく、 縮合 及びエポキシ化の方法についても特に限定するものではないが、 好ましい （a ) のエポキシ樹脂としては、 フエノール 1モルに対し、 サリチルアルデヒ ド 0 . 1 〜 3 . 0モルを塩酸等の酸触媒の存在下で 8 0〜2 5 0 で1〜6時間反応させ て得られた縮合物の水酸基に対しェピクロルヒ ドリ ンを少なくとも 3当 ftS応さ せて得られたエポキシ樹脂が挙げられ、 そ'の重量平均分子量は 7 0 0〜5 , 0 0 0、 軟化温度は 4 0〜： I 4 0 °C、 エポキシ当量は 1 3 0〜2 8 0のものが好 ましい。
また、 本発明においては、 （a ) のエポキシ樹脂以外のエポキシ樹脂を併用し てもよい。 例えば、 ビスフエノール A型エポキシ樹脂、 ビスフヱノール F型ェポ キシ樹脂、 ビスフヱノール S型エポキシ樹脂、 ビフヱノール型エポキシ樹脂、 フ エノールノボラック型エポキシ樹脂、 クレゾ一ルノボラック型エポキシ樹脂、 ビ スフェノール Aノボラック型エポキシ樹脂、 ビスフエノール Fノボラック型ェポ キシ樹脂、 脂環式エポキシ樹脂、 脂肪族鎖状エポキシ樹脂、 グリシジルエステル 型ェポキシ樹脂、 グリシジルァミン型ェポキシ樹脂、 ヒダントイン型ェポキシ樹 脂、 イソシァヌレート型エポキシ樹脂、 その他、 二官能フユノール類のグリシジ ルエーテル化物、 二官能アルコールのグリシジルエーテル化物、 及びそれらの水 素添加物などがある。 これらのエポキシ樹脂は何種類かを併用することができ な
( a ) のエポキシ樹脂以外のエポキシ樹脂.の配合割合は、 （a ) のエポキシ樹 脂 1 0 0重量部に対し、 0〜2 0 0重量部とすることが好ましい。 更に好ましく は 1 0〜： I 0 0重量部である。
( b ) のビスフエノール Aとホルムアルデヒドの縮合物の分子量については制 限はないが、 重量平均分子量で 2 5 0〜2 0 , 0 0 0のものが好ましい。 縮合物 中にはビスフヱノール Aモノマーが含まれていても良い。 縮合反応は酸触媒の存 在下でビスフエノール A 1モルに対しホルムアルデヒ ド 0 . 1〜6 . 0モルを 8 0〜2 5 0 °Cで反応させることが好ましい。
ビスフヱノール Aとホルムアルデヒドの縮合物の好ましい例として、 水酸基当 量 1 0 0〜 1 3 0のビスフエノール Aノボラック樹脂が挙げられる。
このビスフヱノール Aとホルムアルデヒ ドの縮合物は硬化剤として配合される ものであるが、 その配合量は、 （a ) のエポキシ樹脂のエポキシ基に対する ( b ) の縮合物のフエノール性水酸基の当量が 0. 5 ~ 1 . 5当量の範囲となる ように配合することが好ましい。 さらに好ましくは 0 . 9〜1 . 1当量の範囲と する。
また、 ビスフヱノール Aとホルムアルデヒドの縮合物以外の硬化剤を併用して もよく、 例えば、 ビスフヱノール F、 ポリビニルフエノール、 又はフヱノール、 クレゾ一ル、 アルキルフエノール、 カテコール、 ビスフエノール Fなどから得ら れたノボラック樹脂などが用いられる。 これらの化合物の分子量も特に制限はな く、 これらの化合物を何種類かを併用することができる。 これらの化合物の配合 割合は （b ) のビスフエノール Aとホルムアルデヒ ドの縮合物 1 0 0重量部に対 し、 0〜 1 0 0重量部とすることが好ましい。
( c ) の難燃剤は一般に難燃剤と称されるものであればどのようなものでもよ く、 例えば、 ビスフエノール A型エポキシ樹脂、 ビスフエノール F型エポキシ樹 月旨、 ビスフエノール S型エポキシ樹脂、 フエノールノボラック型エポキシ樹脂、 クレゾ一ルノボラック型エポキシ樹脂、 ビスフエノール Aノボラック型エポキシ 樹脂、 ビスフヱノール Fノボラック型ェポキ 'シ樹脂、 脂環式エポキシ樹脂、 脂肪 族鎮状ェポキシ樹脂、 グリシジルエステル型ェポキシ樹脂、 グリシジルァミン型 エポキシ樹脂、 ヒダントイン型エポキシ樹脂、 イソシァヌレート型エポキシ樹 S旨、 その他、 二官能フヱノール類のグリシジルェ一テル化物、 二官能アルコール のグリシジルエーテル化物などのハロゲン化物、 ビスフエノール A、 ビスフエ ノール F、 ポリビニルフヱノール、 又はフヱノール、 クレゾール、 アルキルフエ ノール、 カテコール、 ビスフエノール Fなどのノボラック樹脂などのハロゲン化 物、 三酸化アンチモン、 トリフエニルフォスフェートなどがある。 この中で、 テ トラブロモビスフエノ一ル八、 テトラブロモビスフエノール Aのグリシジルエー テル化物、 フヱノールとホルムアルデヒドの縮合物のグリシジルエーテル化物の 臭素化物が、 特に好ましい。
( c ) の難燃剤の配合割合は （a ) のエポキシ樹脂 1 0 0重量部に対し、 好ま しくは、 2 0〜5 0 0重量部、 さらに好ましくは 3 0〜2 0 0重量部である。
( d ) の硬化促進剤としては、 エポキシ基とフヱノール性水酸基のエーテル化 反応を促進させるような触媒機能を持つ化合物であればどのようなものでも良く 例えば、 アルカリ金属化合物、 アルカリ土類金属化合物、 イミダゾール化合物、 有機りん化合物、 第二級ァミン、 第三級ァミン、 第四級アンモニゥム塩などがあ る。
好ましくは、 イミダゾール化合物が用いられる。 ィミノ基がァクリロニトリ ル、 イソシァネート、 メラミンァクリレートなどでマスク化されたイミダゾール 化合物を用いると、 従来の 2倍以上の保存安定性を有するプリプレダを得ること ができる。
ここで用いられるイミダゾ一ル化合物としては、 ィミダゾール環を有する化合 物はもちろんイミダゾリン環を有する化合物 |>含むこととし、 例えば、 イミダ ゾ一ル、 2—ェチルイミダゾ一ル、 2—ェチルー 4ーメチルイミダゾール、 2— フエ二ルイミダゾール、 2—ゥンデシルイミダゾール、 1一べンジルー 2—メチ ルイ ミダゾール、 2 —ヘプタデシルイミダゾール、 4 , 5 —ジフエ二ルイミダ ゾール、 2—メチルイ ミダゾリン、 2—フヱニルイ ミダゾリン、 2—ゥンデシル イ ミダゾリ ン、 2—へプタデシルイ ミダゾリ ン、 2—イソプロピルイ ミダゾー ル、 2 , 4—ジメチルイ ミダゾ一ル、 2—フヱニル— 4ーメチルイ ミダゾール、 2ーェチルイミダゾリン、 2—ィソプロピルイミダゾリン、 2， 4一ジメチルイ ミダゾリン、 2—フエ二ルー 4—メチルイ ミダゾリンなどがあり、 ィ ミノ基のマ スクイ匕剤としては、 アクリロニトリル、 フエ二レンジイソシァネート、 トルイジ ンイソシァネート、 ナフタレンジイソシァネート、 メチレンビスフエ二ルイソシ ァネート、 メラミ ンァクリ レートなどがある。
これらの硬化促進剤は何種類かを併用してもよく、 配合量はエポキシ樹脂 1 0 0重量部に対して 0 . 0 1〜5重量部が好ましい。 さらに好ましくは 0 . 0 5〜2重量部である。 0 . 0 1重量部より少ないと促進効果が小さく、 5重量 部より多いと保存安定性が悪くなる。
本発明に係るエポキシ樹脂組成物は、 各種の形態で利用されるが基材に塗布、 含浸する際にはしばしば溶剤が用いられる。 それらの溶剤としては、 アセトン、 メチルェチルケトン、 トルエン、 キシレン、 メチルイソブチルケトン、 酸ェチ ル、 エチレングリコールモノメチルエーテル、 N， N—ジメチルァセトアミ ド、 メタノール、 エタノールなどがありこれらは何種類かを混合しても良 t、。
本発明に係る、 エポキシ樹脂組成物には、 無機充填剤として、 結晶シリカ、 溶 融シリカ、 アルミナ、 ジルコン、 珪酸カルシウム、 炭酸カルシウム、 炭化珪素、 窒化珪素、 窒化ホウ素、 ベリ リア、 マグネシア、 ジルコニァ、 フォーステライ ト、 ステアライ ト、 スピネル、 ムライ ト、 チタニアなどの粉体及びチタン酸カリ ゥム、 炭化珪素、 窒化珪素、 アルミナなどの単結晶繊維、 ガラス繊維などを 1種 類以上配合することができる。
無機充填剤の配合割合は （a ) 、 （b ) 、 ( c ) の合計 1 0 0重量部に対して 好ましくは 6 5 0重量部以下、 さらに好ましくは 2 0 0重量部以下である。 配合 する場合は 2〜6 5 0重量部である。
前記の各成分を配合して得たワニスを、 ガラス布、 ガラス不織布又は紙、 ガラ ス以外を成分とする布などの基材に含浸させ、 乾燥炉内で 8 0 - 2 0 0 °Cの範囲 で乾燥させることにより、 印刷配線板用プリプレグを得る。 このプリプレグを所 定枚数重ね合わせ、 必要に応じその片面若しくは両面に銅箔等の金属箔を重ね、
1 5 0〜1 9 0。C、 2 0〜 8 0 k g f ノ c m2の範囲で加熱加圧することにより印 刷配線板用積層板を製造することができる。
またこのプリプレダを用いて印刷配線板を接着することにより多層の印刷配線 板を得ることができる。
なお、 プリプレグの製造における乾燥とは、 溶剤を使用した場合には溶剤を除 去すること、 溶剤を使用しない場合には室温で流動性がなくなるようにすること をいう。
本発明では、 フヱノール類とヒドロキシベンズアルデヒドとの縮合物をェポキ シ化して得られるエポキシ樹脂及びビスフエノール Aとホルムアルデヒドの縮合 物、 難燃剤、 硬化促進剤を用いることにより、 従来のエポキシ樹脂組成物に比べ グリシジルエーテル基とフヱノ一ル性水酸基の反応率が高く、 硬化物の架橋密度 が高くなるため、 印刷配線板とした場合に吸湿性が低く、 優れた耐熱性と高温特 性、 耐電食性、 耐加熱変色性を有し、 かつ高い T gを与えるエポキシ樹脂組成物 を得ることができる。
実施例
以下、 本発明を実施例に基づいて詳細に説明するが、 本発明はこれに限定され るものではない。
実施例 1
フエノールサリチルアルデヒ ドノボラック型エポキシ樹脂 （エポキシ当量 1 7 0 ) 1 0 0重量部とビスフヱノール Aノボラック樹脂 （水酸基当量 1 1 4 ) 4 6重量部及びテトラブロモビスフヱノール A (臭素含有率 5 8重量％、 水酸基 当量 2 7 2 ) 5 1重量部をメチルェチルケ トンで溶解した。 硬化促進剤として、 1 一シァノエチル— 2—ェチルー 4ーメチルイ ミダゾール 0 . 3重量部を配合 し、 不揮発分 6 5重量％のワニスを作製した。
実施例 2
フエノールサリチルアルデヒドノボラック型エポキシ樹脂 5 4重量部と臭素化 ビスフヱノール A型エポキシ樹脂 （臭素含有率 4 9重量％、 エポキシ当量 4 0 0 ) 4 6重量部及びビスフエノール Aノ.ボラック樹脂 5 0重量部をメチルェ チルケトンで溶解した。 硬化促進剤として、 1ーシァノエチルー 2—ェチル一4 ーメチルイミダゾ一ル 0 . 3重量部を配合し、 不揮発分 6 5重量％のワニスを作 製した。
実施例 3
フエノールサリチルアルデヒドノポラック型エポキシ樹脂 3 6重量部と臭素化 フエノールノボラック型エポキシ樹脂 （臭素含有率 3 5 . 3重量％、 エポキシ当 量 2 8 4 ) 6 4重量部及びビスフエノール Aノボラック樹脂 5 0重量部をメチル ェチルケトンで溶解した。 硬化促進剤として、 1—シァノエチルー 2—ェチルー 4—メチルイミグゾール 0. 3重量部を配合し、 不揮発分 6 5重量％のワニスを 作製した。
実施例 4
1ーシァノエチルー 2—ェチルー 4—メチルイミダゾールに代えて、 へキサメ チレンジィソシァネー 卜でマスクした 2—ェチルー 4ーメチルイ ミダゾールを 0. 5重量部配合した以外は実施例 1と同様の配合でワニスを作製した。
比較例 1
実施例 1において、 フエノールサリチルアルデヒドノポラック型エポキシ樹脂 に代えて、 o—クレゾ一ルノボラック型エポキシ樹脂 （エポキシ当量 1 9 5 ) 1 0 0重量部とビスフエノール Aノボラック樹脂 3 8重量部及びテトラブロモビ スフヱノール A 4 8重量部とした以外は実施例 1と同様の配合でワニスを作製し た。
比較例 2
実施例 1において、 ビスフヱノール Aノボラック樹脂に代えてフヱノールノボ ラック樹脂 （水酸基当量 1 0 6 ) 4 3重量部及びテトラブロモビスフヱノール A 5 0重量部とした以外は実施例 1と同様の配合でワニスを作製した。
比較例 3
低臭素化エポキシ樹脂 （臭素含有率 2 1重量％、 エポキシ当量 4 8 5 ) 8 0重 量部とフヱノールサリチルアルデヒドノポラック型ェポキシ樹脂 2 0重量部に、 あらかじめエチレングリコールモノメチルエーテルに溶解したジシアンジァミ ド 1重量部を配合した。 硬化促進剤として 1ーシァノエチル一 2—ェチル一4ーメ チルイミダゾ一ル 0. 2重量部を配合し、 不揮発分 65重量％のワニスを作製し た。
比較例 4
比較例 3において、 フエノールサリチルアルデヒドノポラック型エポキシ樹脂 に代えて o—クレゾ一ルノボラック型ェポキシ樹脂とした以外は、 比較例 3と同 様の配合でワニスを作製した。
各実施例及び比較例 1〜 4の主な配合を表 1に示した。 表 1中の配合量の単位 は、 重量部である。 また、 各実施例及び比較例 1〜4で得られたワニスを、 厚み が 0. 2 mmのガラス布に含浸し、 160°Cで 2〜 5分加熱してプリフレダを得 た。 得られたプリプレダについて、 製造直後及び 25°C、 50%RHで 60日保 存した後のゲルタイムを測定することにより保存安定性を評価した。 また、 得ら れたプリプレダ 4枚を重ね、 その両側に 18 /zmの銅箔を重ね、 175°C、 90 分、 2. 5 MP aのプレス条件で両面銅張積層板を作製した。 得られた両面銅張 積層板について、 Tg、 はんだ耐熱性、 吸水率、 耐電食性、 加熱変色性並びに常 温及び 200°Cでの曲げ強さ、 曲げ弾性率を調べた。 これらの結果を表 2及び表 .3に示す。 なお、 これらの両面銅張積層板は、 全て11 ー94 V0相当の耐燃 性を有することを確認した。
表 1
Figure imgf000012_0001
表 2
実施例 1 2 3 4 製造直後 122 121 120 125 プリプレダのゲルタイム （秒)
60日後 100 103 101 121
Tg 205 200 195 210 はんだ耐熱性 OK OK OK OK 吸水率 （重量％) 0.56 0.45 0.48 0.59 導通破壊までの日数 > 250 > 250 > 250 > 250 加熱変色性 〇 〇 〇 〇
告 曰 620 638 660 600 曲げ強さ
200 °C 82 84 78 86 吊' i 22.6 23.1 23.3 22.5 曲げ弾性率
200 °C 13.3 13.1 13.1 13.4 表 3
Figure imgf000013_0001
試験方法は以下の通りである。
Tg ：銅箔をエッチングし、 TMA (熱機械分析） により測定。 単位：。 C はんだ耐熱性：銅箔をエッチングし、 プレッシャークッカーテスター中に 2時間 保持した後、 260°Cのはんだに 20秒間浸漬して、 外観を目視で調べた。 表中 NGとは、 ミーズリング、 ふくれ発生を意味し、 OKとは、 ミーズリング、 ふく れ発生がないことを意味する。
吸水率：銅箔をエッチングし、 プレツジャークッカーテスタ一中に 4時間保持し た前後の重量の差から算出した。 単位：重量％
加熱変色性：銅箔をエッチングし、 気中において 1 60°Cで 5時間処理した後、 目視により評価した。 変色のないものを〇、 ¾^変色したものを△、 変色したも のを Xとした。
耐電食性試験： スルーホール穴壁間隔を 350 zmとしたテストパターンを用い て、 各試料について 400穴の絶縁抵抗を経時的に測定した。 試験条件は、 85 、 90%RH雰囲気中 1 00V印加して行い、 導通破壌が発生するまでの時間 を測定した。
曲げ試験： J I S C 6481に従い、 常温及び 200°Cで測定した。 単位： 曲げ強さ （GP a) 、 曲げ弾性率 (MP a) 以上の結果から、 次のことが分る。
エポキシ樹脂に、 フ Xノ一ルサリチルアルデヒドノボラック型エポキシを用い た実施例 1〜4は、 1 9 5 °C以上の高い T gを有し、 はんだ耐熱性、 耐電食性も 良好である。 また、 常温における曲げ強さ、 曲げ弾性率に対する 2 0 0 °Cにおけ る曲げ強さ、 曲げ弾性率の低下が小さい。 また、 硬化促進剤にイソシァネ一トマ スクイミダゾ一ルを用いた実施例 4は、 プリプレダの保存安定性が良好である。 さらに、 ビスフヱノール Aノボラック樹脂を用いた実施例 1〜 4及び比較例 1 は加熱変色性が良好である。
これに対して、 ェポキシ樹脂に 0—クレゾールノボラック型ェポキシ樹脂を用 いた比較例 1及び、 ビスフエノール Aノボラック樹脂に代えてフエノールノボラ ック樹脂を用いた比較例 2は、 T gが低く、 2 0 0 °Cにおける曲げ強さ、 曲げ弾 性率とも低い。 硬化剤にフヱノールノボラッ'クを用いた比較例 2は加熱変色性が 悪く、 また、 ジシアンジアミ ドを用いた比較例 3及び 4は吸水率が大きく、 耐電 食性に劣る。 産業上の利用可能性
本発明の印刷配線板用エポキシ樹脂組成物を用いて印刷配線板を製造すると、 吸湿性が低く、 優れた耐熱性と高温特性、 耐電食性、 耐加熱変色性を有し、 かつ 高い T gを有する印刷配線板を得ることができる。

Claims

請 求 の 範 囲
1. (a) フヱノール類とヒドロキシベンズアルデヒドとの縮合物をエポキシ化 して得られるエポキシ樹脂及び （b) ビスフエノール Aとホルムアルデヒドの縮 合物、 （c) 難燃剤、 （d) 硬化促進剤を必須成分として配合してなる印刷配線 板用エポキシ樹脂組成物。
2. (a) のエポキシ樹脂がフエノールとサリチルアルデヒドとの縮合物をェポ キシ化して得られる樹脂である請求の範囲 1記載の印刷配線板用ェポキシ樹脂組 成物。
3. (b) のビスフエノール Aとホルムアルデヒ ドの縮合物がビスフエノール A ノボラック樹脂である請求の範囲 1記載の印刷配線板用エポキシ樹脂組成物。
4. (a) のエポキシ樹脂のエポキシ基に対する （b) の縮合物のフヱノール性 7j酸基の当量が 0. 5〜： 1. 5当量の範囲となるよう配合した請求の範囲 1記載 の印刷配線板用エポキシ樹脂組成物。
5. (c) の難燃剤がテトラブロモビスフヱノール Aである請求の範囲 1記載の 印刷配線板用エポキシ樹脂組成物。
6. (c) の難燃剤がテトラブロモビスフヱノール Aのグリシジルエーテル化物 である請求の範囲 1記載の印刷配線板用エポキシ樹脂組成物。
7. ( c ) の難燃剤がフエノールとホルムアルデヒ ドの縮合物のグリシジルェ一 テル化物の臭素化物である請求の範囲 1記載の印刷配線板用エポキシ樹脂組成 物。
8. (d) の硬化促進剤がィソシァネートマスクイ ミダゾールである請求の範囲 1記載の印刷配線板用エポキシ樹脂組成物。
9 . 請求の範囲 1記載の印刷配線板用エポキシ樹脂組成物からなる樹脂ワニスを 基材に含浸、 乾燥させて得られたプリプレダを重ね合わせ、 その片面若しくは両 面に金属箔を重ね加熱加圧することにより得られた印刷配線板用積層板。
PCT/JP1996/001707 1995-06-27 1996-06-20 Composition de resine epoxy pour cartes a circuits imprimes et plaque feuilletee produite avec cette resine Ceased WO1997001591A1 (fr)