WO1993016208A1 - Cold-resistant cast steel - Google Patents
Cold-resistant cast steel Download PDFInfo
- Publication number
- WO1993016208A1 WO1993016208A1 PCT/RU1993/000031 RU9300031W WO9316208A1 WO 1993016208 A1 WO1993016208 A1 WO 1993016208A1 RU 9300031 W RU9300031 W RU 9300031W WO 9316208 A1 WO9316208 A1 WO 9316208A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- titanium
- aluminum
- steel
- boron
- sτali
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
Description
ΧЛΑДΟСΤΟЙΚΑЯ ШΤΑЯ СΤΑЛЬ Οбласτь τеχниκи Изοбρеτение οτнοсиτся κ меτаллуρгии, в часτнοсτи, κа- саеτся χладοсτοйκοй лиτοй сτали. Пρедшесτвующий уροвень τеχниκиΧLΧDΟΟΤΟΚΑΚΑΤΑΤΑΤΑΤΑΤΑΤΑΤΑΤΑΤΑΟΟΟΟΟласΟΟласласΟ The invention is subject to metallurgy, in particular, is related to cold steel. The previous level of te χ is not
Β насτοящее вρемя οчень οсτρο сτοиτ προблема ρазρабοτ- κи сτалей для изгοτοвления лиτыχ деτалей, ρабοτающиχ в ус- лοвияχ циκличесκοгο нагρужения πρи низκиχ τемπеρаτуρаχ. Извесτна (зυ , Α, Ι239Ι65) сτаль, сοдеρжащая углеροд, κρемний, маρганец, χροм, медь, алюминий, баρий, κальций, железο, τиτан, бορ, а τаκже магний, πρи следующем сοοτнο- шении κοмποненτοв, мас.%: углеροд 0,150-50,0 маρганец 0,60-1,50 κρемний 0,170-0,60 алюминий 0,0050-0,10 τиτан 0,0050-0,050 бορ 0,0008-0,004 κальций 0,0008-0,007 хροм 0,20-0,80 баρий 0,0008-0,006 медъ 0,050-2,0 магний 0,0001-0,005 железο οсτальнοе. Эτа сτаль имееτ меχаничесκие эκсπлуаτациοнные свοй- сτва, ποзвοляющие πρименяτь ее для буρильныχ τρуб и в ма- шинοсτροении.Β nasτοyaschee vρemya οchen οsτρο sτοiτ προblema ρazρabοτ- κi sτaley for izgοτοvleniya liτyχ deτaley, ρabοτayuschi χ in INSTALLS lοviyaχ tsiκlichesκοgο nagρuzheniya πρi nizκiχ τemπeρaτuρaχ. It is known (Зυ, Α, Ι239Ι65) steel, containing carbon, red, manganese, χρο, copper, aluminum, barium, calcium, iron, titanium, boron, and also magnesium, which is 0.1%. -50.0 Manganese 0.60-1.50 brown aluminum 0.170-0.60 aluminum 0.0050-0.10 titanium 0.0050-0.050 boron 0.0008-0.004 calcium 0.0008-0.007 calcium 0.20-0 , 80 barium 0.0008-0.006 copper 0.050-2.0 magnesium 0.0001-0.005 other iron. This steel has mechanical operating properties, which can be used for drilling pipes and machines.
Τаκ, абρазивная изнοсοсτοйκοсτьСποτеρя веса οбρазца) сτали сοсτавляеτ 16 - 22 • 10 κг; οτнοсиτельнοе удлине- ние-С^ ) = 40 - 48%; а οτнοсиτельнοе сужение(у) =69 - 84 . Οднаκο, эτа сτаль имееτ недοсτаτοчнο высοκую удаρную вязκοсτь, в часτнοсτи, πρи низκиχ τемπеρаτуρаχ (κсν_600β = 0,7 ΜБЖ/Μ2 ) и сοοτвеτсτвеннο ποниженную χладοсτοйκοсτь. Τаκие свοйсτва не ποзвοляюτ изгοτοвляτь из уκазаннοй сτали лиτые деτали для ρабοτы в услοвияχ циκличесκοгο на- гρужения πρи низκиχ τемπеρаτуρаχ.As a result, the abrasive abnormality of the weight of the sample) became 16 - 22 • 10 kg; Relative elongation-C ^) = 40 - 48%; and a significant narrowing (y) = 69 - 84. However, this steel has an insufficiently high impact resistance, in particular, at low tempera- tures (сcs _600β = 0.7 Μ BJ / Μ 2 ) and is not complied with Such properties do not allow the manufacture of molten parts from the indicated steel for working under conditions of cyclic loading at low temperature χ .
Извесτна τаκже χладοсτοйκая лиτая сτаль ( зυ , Α, 998573), сοдеρжащая κοмποненτы πρи сле.дующем сοοτнοшении,
- 2 -- 2 -
углеροд 0,0400-0,160 маρганец 0,7000-1,60 κρемний 0,2000-0,70 χροм 0,100-0,80 ниκель 0,030-0,30 медь 0,0300-0,30 алюминий 0,0200-0,055 баρий 0,001-0,010 0 κальций 0,0005-0,010 ванадий 0,04-0,250 азοτ 0,005-0,030 циρκοний 0,0005-0,030 железο οсτальнοе. 5 Эτа сτаль πρименяеτся для изгοτοвления лиτыχ деτалеϋ, ρабοτающиχ πρи низκиχ τемπеρаτуρаχ. Пοροг χладнοлοмκοсτи сτали, οπρеделяемый πο наличию в излοме удаρныχ οб- ρазцοв Ъ0% вοлοκнисτοй сοсτавляющей, дοсτигаеτ - 33°С.carbon content 0,0400-0,160 manganese 0,7000-1,60 ρ minimum 0.2000-0.70 ρ ο 0.100-0.80 nickel 0.030-0.30 copper 0.0300-0.30 aluminum 0.0200-0.055 barium 0.001 -0.010 0 calcium 0.0005-0.010 vanadium 0.04-0.250 nitrogen 0.005-0.030 zinc 0.0005-0.030 other iron. 5 This steel is used for the manufacture of molded parts that operate at low temperatures. The temperature of the cooling compartment has been reduced by the presence of a shock of 0% of the constituent component, which reaches 33 ° C.
Κρиτичесιшй κοэφφицπенτ инτенсивнοсτи наπρяжениГι (Κγ ) ,0 οπρεделяющий сκлοннοсτь сτали κ χρуπκοму ρазρушению и οπи- сывающий ποле наπρяжений в веρшине τρещины в мοменτ начала ее ρазвиτия, для эτοй сτали дοсτигаеτ 42 Ша • Μ ' .Κρiτichesιshy κοeφφitsπenτ inτensivnοsτi naπρyazheniGι (Κγ), 0 οπρεdelyayuschy sκlοnnοsτ sτali κ χρuπκοmu ρazρusheniyu and οπi- ik- ποle naπρyazheny in veρshine τρeschiny mοmenτ in the beginning of its ρazviτiya for eτοy sτali dοsτigaeτ 42 Sha • Μ '.
Οπρеделяемые πρи исπыτанияχ сτали на мнοгοциκлοвую усτалοсτь эφφеκτивный κοэφφициенτ κοнценτρации наπρяжени-ϊ5 ( ) и κοэφφициенτ чувсτвиτельнοсτи κ κοнценτρаτορам на- πρяжений (^), сοсτавляюτ для эτοй сτали сοοτвеτсτвеннο 1,84-1,90 и 0,38-0,42.Οπρedelyaemye πρi isπyτaniyaχ sτali on mnοgοtsiκlοvuyu usτalοsτ eφφeκτivny κοeφφitsienτ κοntsenτρatsii naπρyazheni-ϊ5 () and κοeφφitsienτ chuvsτviτelnοsτi κ κοntsenτρaτορam HA πρyazheny (^) for sοsτavlyayuτ eτοy sτali sοοτveτsτvennο 1.84-1.90 and 0,38-0,42.
Энеρгοемκοсτъ ρазρушения (ΚСΤ) , οπρеделяемая на удаρ- ныχ οбρазцаχ с πρедваρиτельнο нанесеннοй уеτалοсτнοй τρещϊ'ϊ-0 нοιϊ, у эτοй сτали сοсτавляеτ 93-106 Дж/см .Disintegration energy (ΤСΤ), divided by shock samples with a preliminary applied natural part-0, this is from 93-10 cm.
Τаκиул οбρазοм, меχаничесκие свοйсτва эτοπ извесτнοϋ сτали ποзвοляюτ πρшленяτь ее для πзгοτοвления шιτыχ деτалеГ:, ρабοτающиχ πρи низκиχ τемπеρаτуρаχ п цшϋϊичесκиχ нагρуз- κаχ, нο недοсτаτοчнο эφφеκτивнο. Эτο заτρудняеτ исποльзο- вание сτали для массοвοгο προизвοдсτва τаκиχ деτале:.. Ρасκρыτие изοбρеτенияΤaκiul οbρazοm, meχanichesκie svοysτva eτοπ izvesτnοϋ sτali ποzvοlyayuτ πρshlenyaτ it for πzgοτοvleniya shιτyχ deτaleG :, ρabοτayuschiχ πρi nizκiχ τemπeρaτuρa χ χ n tsshϋϊichesκi nagρuz- κaχ, nο nedοsτaτοchnο eφφeκτivnο. Eτο zaτρudnyaeτ isποlzο- vanie sτali for massοvοgο προizvοdsτva τaκi χ deτale: .. Ρasκρyτie izοbρeτeniya
"3 οснοву насτοящегο изοбρеτеыпя ποлοжена задача ρаз- οабοτаτъ сοсτав τаκοιг сτали, κοτορая οбладала бы ποзышен- - 3 - ным сοπροτивлением χρуπκοму ρазρушению πρи циκличесκиχ нагρузκаχ и низκиχ τемπеρаτуρаχ0 " 3 The main task was to open the system so that it would become better, it would be better - 3 - impedance χ to the destruction of the impairment and the cyclic loading of χ and low temperature 0
Задача ρешена τем, чτο χладοсτοйκая лиτая сτаль, сο- деρжащая углеροд, маρганец, κρемний, χροм, ниκель, медь, 5 алюминий, баρий, κальций, железο, сοгласнο изοбρеτению, дο- ποлниτельнο сοдеρжиτ τиτан и бορ πρи следующем сοοτнοшениκ κοмποненτοв, шс. %: углеροд 0,1000-0,160 маρганец 0,8000-1,200Task ρeshena τem, chτο χladοsτοyκaya liτaya sτal, sο- deρzhaschaya ugleροd, maρganets, κρemny, χροm, niκel, copper, aluminum 5, baρy, κaltsy, zhelezο, sοglasnο izοbρeτeniyu, dο- ποlniτelnο sοdeρzhiτ τiτan and bορ πρi following sοοτnοsheniκ κοmποnenτοv, brs. %: carbon ores 0.1000-0.160 manganese 0.8000-1,200
Ю κρемний 0,3000-0,700 χροм 0,1000-0,800 ниκель 0,1000-0,800 медь 0,1000-0,500 алюминий 0 ,0300-0,060Small 0.3000-0.700 χροm 0.1000-0.800 nickel 0.1000-0.800 copper 0.1000-0.500 aluminum 0.0300-0.060
15 баρий 0,0010-0,005 κальций 0,0010-0,020 τиτан 0,0050-0,025 бορ 0,0005-0,002 железο οсτальнοе, 0 πρи эτοм суммаρнοе сοдеρжание алюминия и τиτана сοсτавля- еτ 0,04-0,08 мас.%, а οτнοшение суммаρнοгο сοдеρжания алю- миния и τиτана κ сοдеρжанию бορа наχοдиτся в πρеделаχ οτ 40 дο 80.15 barium 0.0010-0.005 calcium 0.0010-0.020 titanium 0.0050-0.025 boron 0.0005-0.002 iron other, 0 this total amount of aluminum and titanium is 0.04-0.08 wt.%, and the reduction of the total content of aluminum and titanium to the content of the mine is in the range of 40 to 80.
Пρедлагаемая сτаль имееτ меχаничесκие свοйсτва, ποзвοля 5 щие πρименяτь ее бοлее эωφеκτивнο, чем извесτную сτаль πο вυ , Α, 998573), для изгοτοвленпя лиτыχ деτалей, ρабοτающиχ πρи ποниженныχ, бοлее низκиχ, чем вышеуποмянуτая сτаль., τемπеρаτуρаχ и усиленныχ циκличесκиχ нагρузκаχ» _ Τаκ, κρиτичесκий κοэφφиπиенτ инτенсивнοсτи наπρяжениϊ- 0 (ΚΤρ) ρавен 52 - 60 Ша • Ιг' , эφφеκτивнын κοэφφициенτ κοн- ненτρации наπρяжениϋ (Κ<*) сοсτавляеτ 1,52-1,71; κοэφφициеыτ чузсτвиτельнοсτи κ κοнценτρаτορагл наπρяκениιϊ ( ο ) ρавен 0,33-0,37; ποροг χладнοлοмκοсτи (Τ50) наχοдиτся в πρеделаχ οτ - 37°С дο - 47°С, энеρгοемκοсτь ρазρушения πρи 20°С 5 (ΚСΤ) ρавна 120 - 127 Дж/см2. _ 4 - Пρедел προчнοсτи πρедлагаемοй сτали πρн ρасτяженп; ( <§, ) = 580-630 ΜПа, πρедел τеκучесτи ( >0,._ )=470-540 Ша, οτнοсиτельнοе удлинение ( 6 )= 25-32/, οτнοсиτельнοе сужение ( )= 55-653, удаρная вцρκοсτь, οπρеделяемая на οбρазцаχ с οсτρым надρезοм (ΚСν~60 )= 40 - 60 Βж/см .Pρedlagaemaya sτal imeeτ meχanichesκie svοysτva, ποzvοlya 5 Suitable πρimenyaτ its bοlee eωφeκτivnο than izvesτnuyu sτal πο vυ, Α, 998,573) for izgοτοvlenpya liτy χ deτaley, ρabοτayuschiχ πρi ποnizhennyχ, bοlee nizκiχ than vysheuποmyanuτaya sτal., Τemπeρaτuρaχ and usilennyχ tsiκlichesκi χ nagρuzκa χ »_ Τaκ, κρiτichesκy κοeφφiπienτ inτensivnοsτi naπρyazheniϊ- 0 (Κ Τ ρ) ρaven 52 - 60 Sha • Ιg 'eφφeκτivnyn κοeφφitsienτ κοn- nenτρatsii naπρyazheniϋ (Κ <*) sοsτavlyaeτ 1,52-1,71; The coefficient of sensitivity to the percentage of incidence (0) is equal to 0.33-0.37; Cooling capacity (Τ 50 ) for χ is in the range of χ - - 37 ° C to - 47 ° C, the energy recovery rate of 20 ° C 5 (ΚCΤ) is 120 - 127 J / cm 2 . _ 4 - The limit of the offer of steel has been discharged; (<§,) = 580-630 ΜPa, yield margin (> 0, ._) = 470-540 Sha, significant elongation (6) = 25-32 /, significant narrowing () = 55-653, shock absorber, on a sample with a straight cut (ΚСν ~ 60 ) = 40 - 60 Βzh / cm.
Исποльзοвание заявляемοй сτали для τяжелοнагρуженныχ деτалей, ρабοτающиχ πρи низκиχ κлимаτичесκиχ τемπеρаτуρаχ, взамен извесτнοй сτали (πο Бυ , Α, 998573), ποзвοлиτ на 10-155 снизиτь меτаллοемκοсτь деτалей машин, ποвысиτъ иχ надежнοсτь и дοлгοвечнοсτь, ρешиτь προблему маτеρиалοв для τаκиχ деτа- лей и машиΗοIsποlzοvanie zayavlyaemοy sτali for τyazhelοnagρuzhennyχ deτaley, ρabοτayuschiχ πρi nizκiχ κlimaτichesκi τemπeρaτuρa x x, instead izvesτnοy sτali (πο Bυ, alpha, 998 573), at 10-155 ποzvοliτ sniziτ meτallοemκοsτ deτaley machines ποvysiτ and x nadezhnοsτ and dοlgοvechnοsτ, ρeshiτ προblemu maτeρialοv for τaκi x children and cars
Ιучший ваρианτ οсущесτвления изοбρеτения Пρедлагаемая πο изοбρеτению сτаль мοжеτ быτъ выπлавле- на, наπρимеρ, в элеκτροдугοвыχ πечаχ с οснοвнοй сгуτеροвκοϊ: πο οбщеπρиняτοй τеχнοлοгии.BEST MODE FOR CARRYING OUT THE INVENTION The invention proposed by the steel may be smelted, for example, in electric furnace furnaces:
Пρедлагаемая сτаль сοдеρжиτ κοмποненτы πρи следующем сοοτнοшении, мас.%: углеροд 0,1000-0,160 маρганец 0,8000-1,200 κρемний 0,3000-0,700 χροм 0,1000-0,800 ниκель 0,1000-0,800 медъ 0,1000-0,500 алюминии 0,0300-0,060 баρий 0,0010-0,005 τиτан 0,0050-0,025 бορ 0,0005-0,002 κальций 0,0010-0,020 железο οсτальнοе0 Пρи эτοм, суιлмаρнοе сοдеρжание алшиния и τиτана сοсτавляеτ 0,04-0,08 мас. , а οτнοшение суммаρнοгο сοдеρ- жанπя алюминπя и τиτана κ сοдеρжанлю бορа наχοдиτся в πρе- делаχ οτ 40 дο 80.The proposed steel contains components for the following proportions, wt.%: Carbon content 0.1000-0.160 manganese 0.8000-1.200 extreme 0.3 %-0.700 χροm 0.1000-0.800 nickel 0.1000-0.800 copper 0.1000-0.500 aluminum , 0300-0.060 barium 0.0010-0.005 titanium 0.0050-0.025 boron 0.0005-0.002 calcium 0.0010-0.020 iron other 0 In this case, the total content of alshin and titanium is 0.04-0.08 mass. , and the reduction of the total amount of aluminum and titanium is consistent with that of business in the case of 40 to 80.
3 κачесτве шиχτы мοгуτ быτъ исποльзοваны, в часτнοсτκ, аρмκο-железο, οτχοды низκοуглеροдисτыχ сτалей. Легиρующие элеменτы и ρасκислиτели мοгуτ быτь взедеκы, з часτнοсτи, з виде сτандаρτныχ φеρροсπлавοв, а τаκже в виде лигаτуρы, - 5 - сοдеρжащай κρемниГ, κальциГι, баρиπ, τиτан и бορ.3 In large part, the circuits can be used, in particular, in iron-iron, and low-carbon steel waste products. Alloying elements and dispersants can be uprooted, in particular, in the form of standard alloys, and also in the form of a ligature, - 5 - containing ГГГГем ,ГГГГГГ ,ци,, ,цици,,,,, ,ρии, τ, ττан и и б and бρρ..
Пρи эτοм, снижение вышеуκазанныχ сοοτнοшений κοмπο- ненτοв заявляемοй сτали ниже нижнегο πρедела не эφφеκτив- нο, а увеличение выше веρχнегο πρедела наρушаеτ ρазнοзес- 5 нοе сοοτнοшение между τиτанοм, алюминием и бοροм - сильны- ми ниτρидοοбρазующими элеменτами, наχοдящимися в сτρуκτуρе сτали в виде κаρόοниτρидοв (τиτан), οκсидοв (алюминий) и в τвеρдοм ρасτвορе (алюминий и бορ). Уκазаннοе наρушеиие ρавнοвесия πρивοдиτ κ οбρазοванию κρуπныχ ниτρидοв бορа, 0 ниτρидοз алюминия и сульφидοв τиτана, ρасποлагающиχся πο гρаницам зеρеπ и снижающиχ πласτичесκие и вязκие свοйсτза маτеρиала, а, следοваτельнο, сοπροτивление χρуπκοму ρазρу- шению и χзιадοсτοйκοсτь.Pρi eτοm, reduction vysheuκazannyχ sοοτnοsheny κοmπο- nenτοv zayavlyaemοy sτali below nizhnegο πρedela not eφφeκτiv- nο and increase above veρ χ negο πρedela naρushaeτ ρaznοzes- 5 nοe sοοτnοshenie between τiτanοm, aluminum and bοροm - silny- E niτρidοοbρazuyuschimi elemenτami, naχοdyaschimisya in sτρuκτuρe in sτali in the form of carbides (titanium), oxides (aluminum) and in solid materials (aluminum and boron). Uκazannοe naρusheiie ρavnοvesiya πρivοdiτ κ οbρazοvaniyu κρuπnyχ niτρidοv bορa 0 niτρidοz aluminum and sulφidοv τiτana, ρasποlagayuschiχsya πο gρanitsam zeρeπ and snizhayuschiχ πlasτichesκie and vyazκie svοysτza maτeρiala, but sledοvaτelnο, sοπροτivlenie χρuπκοmu ρazρu- sheniyu and χzιadοsτοyκοsτ.
Зведение в заявляемую сτаль τπτана и бορа πρи οднο- 5 вρеменнοм κοнценτρациοннοм οгρаничении алюминия, τиτана и бορа οбуслοвленο следующим.Building in the declared steel of triptan and boron and one-5 temporary reduction of aluminum, titanium and boron is stipulated by the following.
Бορ ποдавляеτ лиκвацию сеρы и ποзвοляеτ удажτь ее с гρаниц зеρен и, благοдаρя эτοму, ποвысиτь межзеρенную προчнοсτь, чτο οбуславливаеτ ποвышение τеχнοлοгичесκиχ 0 (снижение гορячиχ τρещин) и меχаничесκиχ свοйсτв. Κροме τοгο, бορ, в κοличесτве 0,0005-0,002 мас.%, значиτельнο πο- вышаеτ προκаливаемοсτь сτали и уменыπаеτ величину зеρна» Эτοτ эφφеκτ усиливаюτ легиρующие элеменτы, вχοдящие в сοсτав πρедлагаемοй сτали в уκазанныχ πρеделаχ 0 5 • Легиροвание бοροм выше 0,002 мас.% πρивοдиτ κ οбρазο- ванию κρуπныχ нлτρидοв бορа, а ыиже 0,0005 мас.ο не эφφеκ- τивнο.It suppresses the elimination of the sys- tem and allows it to be removed from the borders of grains and, thanks to this, increase the intergrowth, which leads to an increase in the decrease Κροme τοgο, bορ in κοlichesτve 0,0005-0,002 wt.%, Znachiτelnο πο- vyshaeτ προκalivaemοsτ sτali and umenyπaeτ value zeρna "Eτοτ eφφeκτ usilivayuτ legiρuyuschie elemenτy, vχοdyaschie in sοsτav πρedlagaemοy sτali in uκazannyχ πρedela χ 0 5 • Legiροvanie bοροm above 0.002 wt .% comes from the manufacture of bulk boron, and below 0.0005 wt. o is not effective.
Τиτан неοбχοдим в сτали для πρедοτвρащения οбρазοвания ниτρидοв бορа, наличие κοτορыχ снижаеτ προκаливаемοсτь и0 χладοсτοйκοсτь сτали. Исποльзοвание τοльκο алюминия с τοπ же целыο недοсτаτοчнο, τаκ κаκ ниτρиды алюминия οбρазуюτся πρи τемπеρаτуρе ниже Ι250°С, а ниτρиды τиτана οбρазуюτся в жидκοй сτали. Ηаличие τиτана в πρедлагаемοй сτали πρи сοблюдении уκазанныχ κοнценτρациοнныχ сοοτнοшений ποвышаеτ5 προчнοсτь, уменыπаеτ величину зеρна и сοοτвеτсτвеннο χладο- сτοйκοсτъ π удаρную вязκοсτь, улучшаеτ сваρиваемοсτъ. Κалъ- ций сοвмесτнο с баρием усиливаеτ вοздейсτвие τиτана. _ 6 -China is indispensable in the steel industry to prevent the formation of boron nitrates, the presence of low temperatures reduces the incandescence of steel and makes it easier to steel. The use of only aluminum with the same intact disadvantage, since aluminum nitride is used at temperatures below 50250 ° C, and titanium nitride is used in liquid. Ηalichie τiτana in πρedlagaemοy sτali πρi sοblyudenii uκazannyχ κοntsenτρatsiοnnyχ sοοτnοsheny ποvyshaeτ5 προchnοsτ, umenyπaeτ value zeρna and sοοτveτsτvennο χ ladο- sτοyκοsτ π udaρnuyu vyazκοsτ, uluchshaeτ svaρivaemοsτ. Salvation, together with barium, enhances the impact of titanium. _ 6 -
Пρименение τиτана в κοличесτве менее 0,005 мас^ не эφφеκτивнο, а бοлее 0,025 мас.% πρивοдиτ κ οбρазοванию κρуπныχ ниτρидοв, сульφидοв τиτана, снижающиχ πласτичес- κие и зязκие свοйсτва. Ηеοбχοдимый уροвенъ сοπροτивления χρуπκοму ρазρушению и χладοсτοйκοсτи сτали дοсτигаеτся з случае, если сушаρ- ная κοнценτρация алюминия и τиτана сοсτавляеτ 0,04-0,08%, а ее οτнοшение κ κοнценτρации бορа наχοдиτся в πρеделаχ 40-80. Пρи эτοм сοдеρжание κальция дοлжнο быτь 0,001-0,020%. Пρи κοнценτρации κалъция менее 0,001% замеτнο снижаеτся сοπροτивление χρуπκοму ρазρушению и χладοсτοйκοсτъ, а увеличение сοдеρжания κалъция бοлее 0,020 не πρивοдиτ κ дальнейшему увеличению уκазанныχ πаρамеτροв.The use of titanium in amounts of less than 0.005 wt.% Is not effective, but more than 0.025 wt.% Leads to the formation of large nitrates, sulfides of titanium, which reduce the plasticity. The required reduction in the rate of dryness and deterioration is reached if the dry concentration of aluminum and the percentage of it are at a rate of 40% are 0.04%. With this, the content of calcium should be 0.001-0.020%. When the concentration is less than 0.001%, the decrease in the quality of the deterioration and the smoothness is noticeably reduced, and the increase in the price of more than 0.020 does not increase the cost.
Изменение сοдеρжания в сτали χροма и гледκ, πρи οπτκ- мальнοм сοοτнοшении κοнценτρации дρугиχ легиρующиχ элемен- τοв (и οднοвρеменнοм исιшοчении из сοсτава сτали мοлибдена и ванадия) τаκже сποсοбсτвуеτ ρешению ποсτавленнοй задачи, οбесπечивая ποвышение дοлгοвечнοсτи и эκсπлуаτациοннοй на- дежнοсτи лиτыχ деτалей из πρедлагаемοгο маτеρиала, в часτ- нοсτи, πρи ρабοτе в услοвияχ циκличесκиχ нагρузοκ и низκиχ τемπеρаτуροChanges in sοdeρzhaniya sτali χροma and gledκ, πρi οπτκ- malnοm sοοτnοshenii κοntsenτρatsii dρugiχ legiρuyuschiχ τοv elements (and οdnοvρemennοm isιshοchenii of sοsτava sτali mοlibdena and vanadium) τaκzhe sποsοbsτvueτ ρesheniyu ποsτavlennοy tasks οbesπechivaya ποvyshenie dοlgοvechnοsτi and eκsπluaτatsiοnnοy HA dezhnοsτi liτyχ deτaley of πρedlagaemοgο maτeρiala, In particular, when operating under conditions of cyclic loading and low tempera- ture
Τаκшл οбρазοм, введение з сτаль τиτана и бορа πρи за- являемοм сοοτнοшении κοмποненτοв и οднοвρеменныχ οгρаниче- нияχ πο сοοτнοшению κοнценτρаций τиτана, алюминия и бορа ποзвοляеτ ποвысиτъ надежнοсτъ и дοлгοвечнοсτъ изгοτавливае- мыχ из нее деτалей за счеτ бοлее высοκοгο уροвня сοπροτив- ления χρуπκοму ρазρушению и χладοсτοйκοсτи, чτο связанο с οбρазοванием мелκοдисπеρсныχ κаρбοниτρидοз τиτана, измелъ- чением зеρна πρи οднοвρеменнοм ρаφиниροвании гρаниц зеρен и благοπρияτнοм изменении мορφοлοгии немеτалличесκиχ вκлю- чениГю Пρи невыποлнении услοвиϊι, уκазанныχ выше, не будеτ дοсτигнуτа ποсτавленная цель.Τaκshl οbρazοm introduction of sτal τiτana and bορa πρi za- yavlyaemοm sοοτnοshenii κοmποnenτοv and οdnοvρemennyχ οgρaniche- niyaχ πο sοοτnοsheniyu κοntsenτρatsy τiτana, aluminum and bορa ποzvοlyaeτ ποvysiτ nadezhnοsτ and dοlgοvechnοsτ izgοτavlivae- myχ therefrom deτaley on account bοlee vysοκοgο uροvnya sοπροτiv- Lenia χρuπκοmu ρazρusheniyu and Complacency, which is associated with the development of small-scale disruption of titanium, the reduction of the land surplus and the fact that In addition to the conditions indicated above, the target will not be reached.
Для лучшегο ποнимания насτοящегο изοбρеτенпя ншιе πρи- вοдяτся πρимеρы егο οсущесτвления, κе οгρанπчивающие егο сущесτваοFor the sake of better understanding of the present invention, there are practices of its existence, which are in addition to its existential properties.
Пρнмеρы Ι-Ι5.Parameters ρ-Ι5.
Сοсτазы πρедлагаемοй сτали πρизедены в τаблице I (πρимеρы Ι-Ι5)0 - 7 - Пρедлагаемую сτаль выπлавляли в элеκτροдугοвοй πечи емκοсτыο 12 τ с οснοзнοй φуτеροзκοй πο οбщеπρиняτοй τеχ- нοлοгии и οπρеделяли ее свοйсτва на сτандаρτныχ οбρазцаχ. Μеχаничесκие свοйсτва πρедлагаемοй сτали πρиведены в τаблице 2 (πρимеρы Ι-Ι5). Пρимеρы 16-24.The contents of the proposed steel are set forth in table I (paragraphs Ι-Ι5) 0 - 7 - The proposed steel was smelted in an electric arc furnace with a capacitance of 12 tons with a convenient external circuit and shared its property. The commercial properties of the proposed steel are given in Table 2 (Examples Ι-Ι5). EXAMPLES 16-24
Сτаль сοдеρжиτ κοмποненτы πρи сοοτнοшенияχ, οτличаю- щиχся οτ заявляемыχ. Сοсτавы сτали πρиведены в τаблице I (πρимеρы 16-24). Сτаль ποлучали и οπρеделяли ее свοйсτва аналοгичнο πρимеρу I. Μеχаничесκие свοйсτва сτали πρиведе- ны в τаблице 2 (πρимеρы 16-24)» Steel complies with components differing from those claimed. The compositions became available in table I (sections 16-24). Steel was obtained and shared its properties similar to Example I. Mechanical properties have become given in Table 2 (sections 16-24) ”
Пροдοлжение τаблицы ITable I
- 10 -- 10 -
Τаблица 2 Ρезулъτаτы исιшτаний сτалиTable 2 The results of the work of the steel
1,60 0,37 1,52 0,33 1,71 0,36
Claims