[go: up one dir, main page]

US20130130055A1 - Coated steel sheet, method for producing the same, and resin-coated steel sheet obtained using the same - Google Patents

Coated steel sheet, method for producing the same, and resin-coated steel sheet obtained using the same Download PDF

Info

Publication number
US20130130055A1
US20130130055A1 US13/636,858 US201113636858A US2013130055A1 US 20130130055 A1 US20130130055 A1 US 20130130055A1 US 201113636858 A US201113636858 A US 201113636858A US 2013130055 A1 US2013130055 A1 US 2013130055A1
Authority
US
United States
Prior art keywords
steel sheet
coating
coated steel
layer
resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US13/636,858
Other languages
English (en)
Inventor
Yuka Miyamoto
Takeshi Suzuki
Hiroki Iwasa
Norihiko Nakamura
Masao Inose
Hisato Noro
Yoichi Tobiyama
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JFE Steel Corp
Original Assignee
JFE Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JFE Steel Corp filed Critical JFE Steel Corp
Assigned to JFE STEEL CORPORATION reassignment JFE STEEL CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: TOBIYAMA, YOICHI, NAKAMURA, NORIHIKO, SUZUKI, TAKESHI, INOSE, MASAO, MIYAMOTO, YUKA, NORO, HISATO, IWASA, HIROKI
Publication of US20130130055A1 publication Critical patent/US20130130055A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/02—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material
    • C23C28/021—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material including at least one metal alloy layer
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/04—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material
    • B32B15/08—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material of synthetic resin
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B37/00—Methods or apparatus for laminating, e.g. by curing or by ultrasonic bonding
    • B32B37/02—Methods or apparatus for laminating, e.g. by curing or by ultrasonic bonding characterised by a sequence of laminating steps, e.g. by adding new layers at consecutive laminating stations
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B38/00—Ancillary operations in connection with laminating processes
    • B32B38/0008—Electrical discharge treatment, e.g. corona, plasma treatment; wave energy or particle radiation
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0278—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
    • C23C22/06—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6
    • C23C22/48—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 not containing phosphates, hexavalent chromium compounds, fluorides or complex fluorides, molybdates, tungstates, vanadates or oxalates
    • C23C22/50—Treatment of iron or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23G—CLEANING OR DE-GREASING OF METALLIC MATERIAL BY CHEMICAL METHODS OTHER THAN ELECTROLYSIS
    • C23G1/00—Cleaning or pickling metallic material with solutions or molten salts
    • C23G1/02—Cleaning or pickling metallic material with solutions or molten salts with acid solutions
    • C23G1/08—Iron or steel
    • C23G1/081—Iron or steel solutions containing H2SO4
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D3/00—Electroplating: Baths therefor
    • C25D3/02—Electroplating: Baths therefor from solutions
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D3/00—Electroplating: Baths therefor
    • C25D3/02—Electroplating: Baths therefor from solutions
    • C25D3/12—Electroplating: Baths therefor from solutions of nickel or cobalt
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D3/00—Electroplating: Baths therefor
    • C25D3/02—Electroplating: Baths therefor from solutions
    • C25D3/20—Electroplating: Baths therefor from solutions of iron
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D3/00—Electroplating: Baths therefor
    • C25D3/02—Electroplating: Baths therefor from solutions
    • C25D3/22—Electroplating: Baths therefor from solutions of zinc
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D3/00—Electroplating: Baths therefor
    • C25D3/02—Electroplating: Baths therefor from solutions
    • C25D3/38—Electroplating: Baths therefor from solutions of copper
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D3/00—Electroplating: Baths therefor
    • C25D3/02—Electroplating: Baths therefor from solutions
    • C25D3/54—Electroplating: Baths therefor from solutions of metals not provided for in groups C25D3/04 - C25D3/50
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of workpieces
    • C25D5/10—Electroplating with more than one layer of the same or of different metals
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of workpieces
    • C25D5/10—Electroplating with more than one layer of the same or of different metals
    • C25D5/12—Electroplating with more than one layer of the same or of different metals at least one layer being of nickel or chromium
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of workpieces
    • C25D5/34—Pretreatment of metallic surfaces to be electroplated
    • C25D5/36—Pretreatment of metallic surfaces to be electroplated of iron or steel
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of workpieces
    • C25D5/60—Electroplating characterised by the structure or texture of the layers
    • C25D5/605—Surface topography of the layers, e.g. rough, dendritic or nodular layers
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D7/00—Electroplating characterised by the article coated
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D9/00—Electrolytic coating other than with metals
    • C25D9/04—Electrolytic coating other than with metals with inorganic materials
    • C25D9/08—Electrolytic coating other than with metals with inorganic materials by cathodic processes
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D9/00—Electrolytic coating other than with metals
    • C25D9/04—Electrolytic coating other than with metals with inorganic materials
    • C25D9/08—Electrolytic coating other than with metals with inorganic materials by cathodic processes
    • C25D9/10—Electrolytic coating other than with metals with inorganic materials by cathodic processes on iron or steel
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25F—PROCESSES FOR THE ELECTROLYTIC REMOVAL OF MATERIALS FROM OBJECTS; APPARATUS THEREFOR
    • C25F1/00—Electrolytic cleaning, degreasing, pickling or descaling
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/70—Other properties
    • B32B2307/714—Inert, i.e. inert to chemical degradation, corrosion
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D3/00—Electroplating: Baths therefor
    • C25D3/02—Electroplating: Baths therefor from solutions
    • C25D3/30—Electroplating: Baths therefor from solutions of tin
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of workpieces
    • C25D5/48—After-treatment of electroplated surfaces
    • C25D5/50—After-treatment of electroplated surfaces by heat-treatment
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of workpieces
    • C25D5/48—After-treatment of electroplated surfaces
    • C25D5/50—After-treatment of electroplated surfaces by heat-treatment
    • C25D5/505—After-treatment of electroplated surfaces by heat-treatment of electroplated tin coatings, e.g. by melting
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12535—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.] with additional, spatially distinct nonmetal component
    • Y10T428/12556—Organic component
    • Y10T428/12569—Synthetic resin
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12806—Refractory [Group IVB, VB, or VIB] metal-base component

Definitions

  • the present invention relates to a coated steel sheet which is mainly used for containers, such as cans, after being further coated with a resin in such a manner that the surface of the coated steel sheet is laminated with a resin film or the like or a paint containing a resin is applied onto the surface of the coated steel sheet, and more particularly, relates to a coated steel sheet which has excellent adhesion to a resin coated thereon in a high-temperature, and humid environment (hereinafter, referred to as “humid resin adhesion”), and which exhibits excellent corrosion resistance even if the coated resin peels off.
  • the invention also relates to a method for producing the same, and to a resin-coated steel sheet obtained by further coating the coated steel sheet with a resin.
  • Metal sheets such as tin-plated steel sheets and electrolytic chromium coated steel sheets referred to as tin-free steel sheets, are used for various metal cans, such as beverage cans, food cans, pail cans, and 18-liter cans.
  • tin-free steel sheets are produced by subjecting steel sheets to electrolysis in a coating bath containing hexavalent Cr, and have excellent humid resin adhesion to a resin, such as a paint, coated thereon.
  • various metal cans have been conventionally manufactured in such a manner that metal sheets, such as tin-free steel sheets, are painted and then formed into can bodies.
  • metal sheets such as tin-free steel sheets
  • a method has come to be frequently used in which a resin-coated metal sheet that is not painted but is coated with a resin, such as a plastic film, and formed into a can body.
  • the resin needs to strongly adhere to the metal sheet.
  • resin-coated metal sheets used for beverage cans or food cans are required to have excellent humid resin adhesion such that the resin does not peel off even in a high-temperature and humid environment because the cans may be subjected to a retort process, in some cases, after contents have been packed therein, and are also required to have excellent corrosion resistance such that the cans are prevented from being corroded and pierced by the contents of the cans or the like even when the resin partially peels off owing to being scratched or the like.
  • Patent Literature 1 it is possible to produce a coated steel sheet having very excellent humid resin adhesion and excellent corrosion resistance, without using Cr, by depositing a corrosion-resistant coating composed of at least one layer selected from the group consisting of a Ni layer, a Sn layer, an Fe—Ni alloy layer, an Fe—Sn alloy layer, and an Fe—Ni—Sn alloy layer on at least one surface of steel sheet, and then depositing an adhesive coating to a resin to be coated thereon by performing cathodic electrolysis in an aqueous solution which includes ions containing Ti and further includes ions containing at least one metal element selected from the group consisting of Co, Fe, Ni, V, Cu, Mn, and Zn.
  • a corrosion-resistant coating composed of at least one layer selected from the group consisting of a Ni layer, a Sn layer, an Fe—Ni alloy layer, an Fe—Sn alloy layer, and an Fe—Ni—Sn alloy layer on at least one surface of steel sheet, and then depositing an adhesive coating to a resin to
  • the present invention provides, without using Cr, a coated steel sheet which has excellent humid resin adhesion and corrosion resistance and in which streaky surface defects do not occur, a method for producing the same, and a resin-coated steel sheet obtained using the coated steel sheet.
  • Patent Literature 1 an adhesive coating of Patent Literature 1 is deposited, it is effective to perform cathodic electrolysis in an aqueous solution which includes Zr instead of Ti and further includes at least one metal element selected from the group consisting of Co, Fe, Ni, V, Cu, Mn, and Zn.
  • the present invention has been made based on such a finding.
  • the present invention provides a coated steel sheet characterized by including a corrosion-resistant coating composed of at least one layer selected from the group consisting of a Ni layer, a Sn layer, an Fe—Ni alloy layer, an Fe—Sn alloy layer, and an Fe—Ni—Sn alloy layer disposed on at least one surface of steel sheet, and an adhesive coating disposed on the corrosion-resistant coating, the adhesive coating containing Zr and further containing at least one metal element selected from the group consisting of Co, Fe, Ni V, Cu, Mn, and Zn, in total, at a ratio by mass of 0.01 to 10 with respect to Zr.
  • the adhesive coating further contains P derived from a phosphoric acid and/or C derived from a phenolic resin, in total, at a ratio by mass of 0.01 to 10 with respect to Zr. Furthermore, preferably, the Zr coating weight of the adhesive coating is 3 to 200 mg/m 2 per one surface.
  • a coated steel sheet of the present invention can be produced by depositing a corrosion-resistant coating composed of at least one layer selected from the group consisting of a Ni layer, a Sn layer, an Fe—Ni alloy layer, an Fe—Sn alloy layer, and an Fe—Ni—Sn alloy layer on at least one surface of a steel sheet, and depositing an adhesive coating by performing cathodic electrolysis with an electric charge density of 1 to 20 C/dm 2 in an aqueous solution which includes Zr in an amount of 0.008 to 0.07 mol/l (1: liter) and further includes at least one metal element selected from the group consisting of Co, Fe, Ni, V, Cu, Mn, and Zn, in total, at a molar ratio of 0.01 to 10 with respect to Zr.
  • a coated steel sheet of the present invention can be produced by depositing a corrosion-resistant coating composed of at least one layer selected from the group consisting of a Ni layer, a Sn layer, an Fe—Ni alloy layer, an Fe—Sn alloy layer, and an Fe—Ni—Sn alloy layer on at least one surface of a steel sheet, and then depositing an adhesive coating by performing cathodic electrolysis in an aqueous solution which includes Zr in an amount of 0.008 to 0.07 mol/l and further includes at least one metal element selected from the group consisting of Co, Fe, Ni, V, Cu, Mn, and Zn, in total, at a molar ratio of 0.01 to 10 with respect to Zr, under the electrolysis conditions, using an electric current having a current density that changes with a cycle of 0.01 to 0.4 seconds between the current density at which Zr is deposited and the current density at which Zr is not deposited, and having a period of 0.005 to 0.2 seconds per cycle during which Zr is not deposited, in
  • the upper limit of the current density at which Zr is not deposited is a value that depends on the composition and pH of the aqueous solution used in the cathodic electrolysis.
  • the current density at which Zr is not deposited is set at 0 A/dm 2 .
  • the aqueous solution used in the cathodic electrolysis further includes a phosphoric acid and/or a phenolic resin, in total, at a molar ratio of 0.01 to 10 with respect to Zr.
  • the present invention also provides a resin-coated steel sheet in which the coated steel sheet of the present invention described above is coated with a resin.
  • the coated steel sheet of the present invention can be used without any problem as an alternative material to replace conventional tin-free steel sheets and can be used, without being coated with a resin, for containers which contain oil, organic solvents, paint, or the like. Furthermore, when the coated steel sheet is coated with a resin to obtain a resin-coated steel sheet and the resin-coated steel sheet is formed into cans or can lids, and even when the cans or can lids are exposed to a retort atmosphere, the resin does not peel off. In addition, at resin peel-off portions, such as scratches, the amount of dissolving out of Fe of a base steel sheet is markedly small, and very good corrosion resistance is exhibited.
  • FIG. 1 is a graph showing the relationship between the Zr coating weight and the current density in an aqueous solution, with pH4, containing 12.5 g/l of potassium hexafluorozirconate and 5 g/l of cobalt sulfate heptahydrate.
  • FIG. 2( a ), FIG. 2( b ), and FIG. 2( c ) are views illustrating a 180° peeling test.
  • a corrosion-resistant coating composed of at least one layer selected from the group consisting of a Ni layer, a Sn layer, an Fe—Ni alloy layer, an Fe—Sn alloy layer, and an Fe—Ni—Sn alloy layer is disposed on at least one surface of steel sheet, and an adhesive coating containing Zr and further containing at least one metal element selected from the group consisting of Co, Fe, Ni, V, Cu, Mn, and Zn is disposed thereon.
  • a low-carbon cold-rolled steel sheet commonly used for cans can be used as a base steel sheet.
  • the corrosion-resistant coating disposed on the surface of the base steel sheet needs to be a coating composed of a single layer selected from a Ni layer, a Sn layer, an Fe—Ni alloy layer, an Fe—Sn alloy layer, and an Fe—Ni—Sn alloy layer or a multi-layer including some of these layers so that it strongly bonds to the base steel sheet in order to impart excellent corrosion resistance to the steel sheet even when, after the coated steel sheet is coated with a resin, the resin partially peels off owing to being scratched or the like.
  • the Ni coating weight is preferably set at 200 mg/m 2 or more per one surface of steel sheet.
  • the Ni coating weight is preferably set at 60 mg/m 2 or more per one surface of the steel sheet.
  • the Sn coating weight is preferably set at 100 mg/m 2 or more per one surface of the steel sheet.
  • the Ni coating weight is set at 50 mg/m 2 or more and the Sn coating weight is set at 100 mg/m 2 or more per one surface of the steel sheet.
  • the coating weights of Ni and Sn can be determined by surface analysis using fluorescence X-rays.
  • Such a corrosion-resistant coating can be disposed by a known method appropriate to the metal element to be contained.
  • an adhesive coating containing Zr and further containing at least one metal element selected from the group consisting of Co, Fe, Ni, V, Cu, Mn, and Zn, in total, at a ratio by mass of 0.01 to 10, more preferably 0.01 to 2, with respect to Zr excellent humid resin adhesion can be obtained, and prevention of occurrence of streaky surface defects is ensured.
  • the adhesive coating further contains P derived from a phosphoric acid and/or C derived from a phenolic resin, in total, at a ratio by mass of 0.01 to 10 with respect to Zr.
  • P derived from a phosphoric acid and/or C derived from a phenolic resin in total, at a ratio by mass of 0.01 to 10 with respect to Zr.
  • hydroxyl groups present in the adhesive coating, hydroxyl groups of the phenolic resin or hydroxyl groups of the phosphoric acid, and hydroxyl groups present on the surface of the corrosion-resistant coating are crosslinked by dehydration condensation, resulting in covalent bonds between the corrosion-resistant coating and the adhesive coating through oxygen atoms.
  • the Zr coating weight is preferably 3 to 200 mg/m 2 per one surface of the steel sheet.
  • the reason for this is that at a Zr coating weight of 3 to 200 mg/m 2 , effects of improving humid resin adhesion and preventing occurrence of streaky surface defects can be sufficiently obtained, and at a Zr coating weight exceeding 200 mg/m 2 , the effects are saturated, resulting in an increase in cost.
  • the Zr coating weight is more preferably 20 to 100 mg/m 2 .
  • the total coating weight of at least one metal element selected from the group consisting of Co, Fe, Ni, V, Cu, Mn, and Zn is preferably 10 to 200 mg/m 2 per one surface of the steel sheet.
  • the total coating weight of these metal elements is 10 mg/m 2 or more and 200 mg/m 2 or less, it is possible to form a coating having excellent humid resin adhesion and having no streaky surface defects.
  • the adhesive coating further includes O.
  • O the coating becomes mainly composed of oxides of Zr, thus being more effective in improving humid resin adhesion and preventing occurrence of streaky surface defects.
  • the coating weight of Zr and the coating weights of Co, Fe, Ni, V, Cu, Mn, Zn, and P in the adhesive coating can be determined by surface analysis using fluorescence X-rays.
  • the C content in the adhesive coating can be obtained by subtracting the C content in the steel sheet as a background from the total C content measured by gas chromatography.
  • the O content is not particularly specified, the presence of O can be confirmed by surface analysis using XPS (X-ray photoelectron spectrometer).
  • the adhesive coating can be disposed by performing cathodic electrolysis with an electric charge density of 1 to 20 C/dm 2 in an aqueous solution which includes Zr in an amount of 0.008 to 0.07 mol/l, preferably 0.02 to 0.05 mol/l, and further includes at least one metal element selected from the group consisting of Co, Fe, Ni, V, Cu, Mn, and Zn, in total, at a molar ratio of 0.01 to 10, preferably 0.01 to 2.5, more preferably 0.01 to 2, with respect to Zr.
  • the Zr amount is less than 0.008 mol/l, it is not possible to disposing a coating having excellent humid resin adhesion and having no streaky surface defects.
  • the Zr amount exceeds 0.07 mol/l, it becomes difficult for Zr to be present in a stable state in the aqueous solution, and Zr oxides are formed.
  • the total amount, in terms of molar ratio, of at least one metal element selected from the group consisting of Co, Fe, Ni, V, Cu, Mn, and Zn is less than 0.01, it is difficult to dispose a coating having excellent humid resin adhesion and having no streaky surface defects.
  • the total amount exceeds 10 the effects are saturated, resulting in an increase in cost.
  • an aqueous solution containing Zr an aqueous solution containing fluorozirconate ions or an aqueous solution containing fluorozirconate ions and a fluoride salts is preferable.
  • a compound that produces fluorozirconate ions hexafluorozirconic acid, ammonium hexafluorozirconate, potassium hexafluorozirconate, or the like can be used.
  • a fluoride salt sodium fluoride, potassium fluoride, silver fluoride, tin fluoride, or the like can be used.
  • an aqueous solution containing potassium hexafluorozirconate or an aqueous solution containing potassium hexafluorozirconate and sodium fluoride can dispose a homogeneous coating efficiently, which is preferable.
  • cobalt sulfate cobalt chloride, iron sulfate, iron chloride, nickel sulfate, copper sulfate, vanadium oxide sulfate, zinc sulfate, manganese sulfate, and the like can be used.
  • these metal elements are added such that the total amount, in terms of molar ratio with respect to Zr, is 0.01 to 10, preferably 0.01 to 2.5, and more preferably 0.01 to 2.
  • the cathodic electrolysis may be performed with a current density of 5 to 20 A/dm 2 and at an electrolysis time of 1 to 5 sec.
  • the electric charge density is set at 3 to 15 C/dm 2 .
  • cathodic electrolysis under the electrolysis conditions, using an electric current having a current density that changes with a cycle of 0.01 to 0.4 seconds between the current density at which Zr is deposited and the current density at which Zr is not deposited, and having a period of 0.005 to 0.2 seconds per cycle during which Zr is not deposited, in which the number of cycles is 10 or more and the total electric charge density at the current density at which Zr is deposited is 3 to 20 C/dm 2 .
  • the upper limit of the current density at which Zr is not deposited depends on the composition and pH of the aqueous solution including Zr and at least one metal element selected from the group consisting of Co, Fe, Ni, V, Cu, Mn, and Zn.
  • FIG. 1 shows the relationship between the Zr coating weight and the current density in an aqueous solution, with pH4, containing 12.5 g/l of potassium hexafluorozirconate and 5 g/l of cobalt sulfate heptahydrate.
  • an alternating current that changes cyclically in a manner similar to a sine curve, or a pulsed current that changes in a binary manner between the current density at which Zr is deposited and the current density at which Zr is not deposited can be used. It is also possible to use a current obtained by superposing an alternating current or a pulsed current on a direct current.
  • the current density at which Zr is not deposited is set at 0 A/dm 2 because it eliminates the need to predetermine the upper limit of the current density depending on the aqueous solution to be used.
  • the cathodic electrolysis is performed in the aqueous solution which further includes a phosphoric acid and/or a phenolic resin, in total, at a molar ratio of 0.01 to 10 with respect to Zr.
  • the reason for this is that, by performing the cathodic electrolysis in the aqueous solution including phosphoric acid and/or phenolic resin, it is possible to dispose an adhesive coating containing P derived from a phosphoric acid and/or C derived from a phenolic resin, resulting in further improvement in coatability of the adhesive coating and improvement in corrosion resistance.
  • a compound that produces a phosphoric acid orthophosphoric acid or a phosphate compound of the metal element added simultaneously may be used, or nickel phosphate, iron phosphate, cobalt phosphate, zirconium phosphate, or the like can be used.
  • a phenolic resin a phenolic resin having a weight-average molecular weight of about 3,000 to 20,000 is preferable, and a phenolic resin having a weight-average molecular weight of about 5,000 is more preferable.
  • the phenolic resin may be provided with water solubility by being amino/alcohol denatured.
  • a resin-coated steel sheet can be obtained by coating the coated steel sheet of the present invention with a resin. As described above, since the coated steel sheet of the present invention has excellent humid resin adhesion, the resin-coated steel sheet has excellent corrosion resistance and formability.
  • the resin used to coat the coated steel sheet of the present invention is not particularly limited.
  • any of various thermoplastic resins and thermosetting resins may be used.
  • the resin that can be used include olefin resin films, such as polyethylene, polypropylene, ethylene-propylene copolymers, ethylene-vinyl acetate copolymers, ethylene-acrylic ester copolymers, and ionomers; polyester films, such as polybutylene terephthalate; polyamide films, such as nylon 6, nylon 6,6, nylon 11, and nylon 12; and thermoplastic resin films, such as polyvinyl chloride films and polyvinylidene chloride films. These films may be unoriented or biaxially oriented.
  • a urethane adhesive, epoxy adhesive, acid-modified olefin resin adhesive, copolyamide adhesive, copolyester adhesive, or the like is preferable.
  • a thermosetting paint may be applied onto the coated steel sheet or the film with a thickness in the range of 0.05 to 2 ⁇ m and used as an adhesive.
  • thermoplastic or thermosetting paints such as modified epoxy paints (e.g., phenol epoxy and amino-epoxy paints), vinyl chloride-vinyl acetate copolymers, saponified vinyl chloride-vinyl acetate copolymers, vinyl chloride-vinyl acetate-maleic anhydride copolymers, epoxy-modified-, epoxy amino-modified, or epoxy phenol-modified vinyl paints, or modified vinyl paints, acrylic paints, and synthetic rubber paints (e.g., styrene-butadiene copolymers), may be used alone or in combination of two or more.
  • modified epoxy paints e.g., phenol epoxy and amino-epoxy paints
  • vinyl chloride-vinyl acetate copolymers saponified vinyl chloride-vinyl acetate copolymers
  • vinyl chloride-vinyl acetate-maleic anhydride copolymers vinyl chloride-vinyl acetate-maleic anhydride copoly
  • the thickness of the resin coating layer is preferably in the range of 3 to 50 ⁇ m, and more preferably 5 to 40 ⁇ m. When the thickness falls below the range described above, corrosion resistance becomes insufficient. When the thickness exceeds the range described above, a problem in terms of formability is likely to occur.
  • the resin coating layer can be disposed on the coated steel sheet by any method.
  • an extrusion coating method for example, an extrusion coating method, a cast film heat bonding method, a biaxially oriented film heat bonding method, or the like can be used.
  • the coated steel sheet may be extrusion-coated with a resin in a molten state, and the resin is heat-bonded to the coated steel sheet. That is, the resin is melted and kneaded in an extruder and then extruded into a thin film from a T-die.
  • the extruded molten resin film, together with the coated steel sheet, is passed between a pair of lamination rolls, and the thin film and the coated steel sheet are integrated under pressure in a cooling environment, followed by quenching.
  • a multi-layered resin coating layer is disposed by extrusion coating
  • a method in which a plurality of extruders for corresponding layers are used resin flows from the individual extruders are joined together in a multilayer die, and then extrusion coating is performed in the same manner as that for a single-layer resin.
  • the resin-coated steel sheet can be used for three-piece cans with side seams and seamless cans (two-piece cans).
  • the resin-coated steel sheet can also be used for lids of stay-on-tab easy open cans and lids of full open easy open cans.
  • Corrosion-resistant coatings are disposed on both surfaces of cold-rolled steel sheet (thickness: 0.2 mm), which is made as cold-rolled low-carbon steel used to produce a tin-free steel sheet (TFS), using coating bath a or b shown in Table 1, by one of the methods A to D described below.
  • a cold-rolled steel sheet is annealed in an atmosphere of 10 vol % H 2 +90 vol % N 2 at about 700° C., subjected to temper rolling at an elongation percentage of 1.5%, degreased by alkali electrolysis, pickled with sulfuric acid, and then coated with Ni using the coating bath a to thereby dispose corrosion-resistant coatings made of Ni layers.
  • a cold-rolled steel sheet is degreased by alkali electrolysis, coated with Ni using the coating bath a, annealed in an atmosphere of 10 vol % H 2 +90 vol % N 2 at about 700° C. to perform diffusion coating of Ni, and then subjected to temper rolling at an elongation percentage of 1.5% to thereby dispose corrosion-resistant coatings made of Fe—Ni alloy layers.
  • a cold-rolled steel sheet is degreased by alkali electrolysis, coated with Ni using the coating bath a, annealed in an atmosphere of 10 vol % H 2 +90 vol % N 2 at about 700° C. to perform diffusion coating of Ni, subjected to temper rolling at an elongation percentage of 1.5%, followed by degreasing and acid pickling, coated with Sn using the coating bath b, and subjected to melting by heating the steel sheet at a temperature equal to or higher than the melting point of Sn.
  • a corrosion-resistant coating including an Fe—Ni—Sn alloy layer and a Sn layer thereon is disposed.
  • a cold-rolled steel sheet is degreased by alkali electrolysis, annealed under the same conditions as the conditions A, subjected to temper rolling, coated with Sn using the coating bath b, and subjected to melting by heating the steel sheet at a temperature equal to or higher than the melting point of Sn.
  • a corrosion-resistant coating including an Fe—Sn alloy layer and a Sn layer thereon is disposed.
  • Sn coating is partially alloyed by the melting treatment.
  • the net coating weight of remaining Sn which remains without being alloyed is shown in Tables 3 to 5.
  • coated steel sheets Nos. 1 to 33 are produced.
  • coated steel sheet Nos. 1, 16, 19, 22, and 29 are comparative examples, in which the adhesive coating does not contain any of Co, Fe, Ni, V, Cu, Mn, and Zn.
  • Nos. 30 and 31 are comparative examples, in which corrosion-resistant coatings are not disposed.
  • Nos. 32 and 33 are comparative examples, in which adhesive coatings containing Ti and further containing V or Mn are disposed on corrosion-resistant coatings.
  • the Zr coating weight and Ti coating weight in each adhesive coating are determined by X-ray fluorescence analysis in comparison with a calibration sheet in which the content of each metal is determined by chemical analysis in advance. Furthermore, regarding Co, Fe, Ni, V, Cu, Mn, and Zn, the coating weights contained are determined by a method appropriately selected from X-ray fluorescence analysis, the same technique as that used for Zr and Ti, chemical analysis, Auger electron spectroscopy analysis, and secondary ion mass spectrometry, and the mass ratio of Co, Fe, Ni, V, Cu, Mn, and Zn to Zr or Ti is evaluated. Furthermore, the presence of O can be confirmed by XPS surface analysis in each of Nos. 1 to 33.
  • both surfaces of each of the coated steel sheet Nos. 1 to 33 are laminated with isophthalic acid copolymerized polyethylene terephthalate films (draw ratio: 3.1 ⁇ 3.1, thickness: 25 copolymerization ratio: 12 mol %, melting point: 224° C.) under the laminating conditions such that the degree of biaxial orientation (BO value) of the films is 150, i.e., with a steel sheet feed rate of 40 m/min, a nip length of rubber roll of 17 mm, a period of time from pressure bonding to water cooling of 1 second.
  • laminated steel sheet Nos. 1 to 33 are produced.
  • the term “nip length” means the length of a contact portion of a rubber roll with each steel sheet in the feed direction.
  • humid resin adhesion, corrosion resistance, and streaky surface defects are evaluated.
  • Humid resin adhesion is evaluated by a 180° peeling test in a retort atmosphere having a temperature of 130° C. and a relative humidity of 100%.
  • a peel length 5 shown in FIG. 2( c ) is measured and evaluated.
  • the test piece is considered to have better humid resin adhesion.
  • the test piece is evaluated to have excellent humid resin adhesion targeted in the present invention.
  • Corrosion resistance A laminate surface of each laminated steel sheet is cut in a crossing manner with a cutter knife such that the cut depth reaches the base steel sheet, the laminated steel sheet is immersed in 80 ml of a test liquid prepared by mixing equivalent amounts of 1.5% by mass NaCl aqueous solution and 1.5% by mass citric acid aqueous solution, and left to stand at 55° C. for 9 days.
  • Streaky surface defects Degree of occurrence of streaky patterns is visually observed and evaluated as follows:
  • ⁇ No streaky patterns are observed.
  • x Streaky patterns are observed.
  • Coating bath Bath composition a Ni coating Nickel sulfate: 250 g/l, nickel chloride: 45 g/l, boric acid: bath) 30 g/l b (Sn coating Stunnous sulfate: 55 g/l, phenolsulfonic acid(65% by mass): bath) 35 g/l, brightener: appropriate amount
  • Example 24 0 700 300 100 Co 1.80
  • Example 25 0 500 70 20 Co 1.80
  • Example 26 0 500 70 60 Fe 0.80
  • Example 27 0 500 70 60 Ni 0.05
  • Example 28 0 1500 900 60 Fe 0.80
  • Example 29 0 700 300 60 — 0 Comparative example 30 — — — 60 Co 1.80 Comparative example 31 — — — 60 Fe 0.80 Comparative example
  • Corrosion-resistant coatings are formed on both surfaces of each cold-rolled steel sheet (thickness: 0.2 mm), which is made of cold-rolled low-carbon steel used to produce a tin-free steel sheet (TFS), using coating bath a or b shown in Table 1, by one of the methods A to D described above. In the methods C and D, Sn coating is partially alloyed by the melting treatment. The net amount of remaining Sn which remains without being alloyed is shown in Tables 7 to 9.
  • coated steel sheets Nos. 34 to 49 are produced.
  • the pH of the cathodic electrolysis bath is adjusted by an alkali solution, such as potassium hydroxide, or an acid solution, such as sulfuric acid.
  • a pulsed current is used, and the current density at which Zr is not deposited is set at 0 A/dm 2 .
  • coated steel sheets Nos. 46 and 47 a pulsed current is used, and on the basis of the results shown in FIG.
  • the Ni coating weight and Sn coating weight in each corrosion-resistant coating and the Zr coating weight and Ti coating weight in each adhesive coating are determined by X-ray fluorescence analysis in comparison with a calibration sample in which the content of each metal is determined by chemical analysis in advance. Furthermore, regarding Co, Fe, V, and Mn, the coating weights are determined by a method appropriately selected from X-ray fluorescence analysis, the same technique as that used for Zr and Ti, chemical analysis, Auger electron spectroscopy analysis, and secondary ion mass spectrometry. Furthermore, the presence of O can be confirmed by XPS surface analysis in each of Nos. 34 to 49.
  • Example 1 Both surfaces of each of the coated steel sheets Nos. 34 to 49 are laminated as in Example 1 to produce laminated steel sheet Nos. 34 to 49. Regarding the resulting laminated steel sheet Nos. 34 to 49, humid resin adhesion, corrosion resistance, and streaky surface defects are evaluated as in Example 1.
  • Corrosion-resistant coatings are formed on both surfaces of each cold-rolled steel sheet (thickness: 0.2 mm), which is made of cold-rolled low-carbon steel used to produce a tin-free steel sheet (TFS), using coating bath a or b shown in Table 1, by one of the methods A to D described above. In the methods C and D, Sn coating is partially alloyed by the heat melting treatment. The net coating weight of remaining Sn which remains without being alloyed is shown in Tables 11 and 12.
  • coated steel sheets Nos. 50 to 60 are produced.
  • the pH of the coating bath is adjusted by an alkali solution, such as potassium hydroxide, or an acid solution, such as sulfuric acid.
  • a pulsed current is used, and the current density at which Zr is not deposited is set at 0 A/dm 2 .
  • a phenolic resin in the coating bath a phenolic resin with a weight-average molecular weight of 5,000 is used.
  • the Ni coating weight and Sn coating weight in each corrosion-resistant coating and the Zr coating weight in each adhesive coating are determined by X-ray fluorescence analysis in comparison with a calibration sample in which the content of each metal is determined by chemical analysis in advance. Furthermore, regarding Co and P, the contents are determined by a method appropriately selected from X-ray fluorescence analysis, the same technique as that used for Zr, chemical analysis, Auger electron spectroscopy analysis, and secondary ion mass spectrometry, and the mass ratio of Co and P to Zr is evaluated. Furthermore, the presence of O can be confirmed by XPS surface analysis in each of Nos. 50 to 60. Furthermore, the C content in the adhesive coating is obtained by subtracting the C content in the steel sheet as a background from the total C content measured by gas chromatography.
  • Example 1 Both surfaces of each of the coated steel sheets Nos. 50 to 60 are laminated as in Example 1 to produce laminated steel sheet Nos. 50 to 60. Regarding the resulting laminated steel sheet Nos. 50 to 60, humid resin adhesion, corrosion resistance, and streaky surface defects are evaluated as in Example 1.
  • the present invention it is possible to produce, even without using Cr which is strictly environmentally regulated, a coated steel sheet which has excellent humid resin adhesion and corrosion resistance and in which streaky surface defects do not occur.
  • the coated steel sheet of the present invention can be used without any problem as an alternative material to replace conventional tin-free steel sheets and can be used, without being coated with a resin, for containers which contain oil, organic solvents, paint, or the like.
  • the coated steel sheet is coated with a resin to obtain a resin-coated steel sheet and the resin-coated steel sheet is formed into cans or can lids, and even when the cans or can lids are exposed to a retort atmosphere, the resin does not peel off.
  • resin peel-off portions, such as scratches the amount of dissolving out of Fe of a base steel sheet is markedly small, and very good corrosion resistance is exhibited. Therefore, the present invention can greatly contribute to the industry.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Electrochemistry (AREA)
  • Mechanical Engineering (AREA)
  • Thermal Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Inorganic Chemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Plasma & Fusion (AREA)
  • Laminated Bodies (AREA)
  • Other Surface Treatments For Metallic Materials (AREA)
  • Electroplating Methods And Accessories (AREA)
US13/636,858 2010-03-25 2011-03-24 Coated steel sheet, method for producing the same, and resin-coated steel sheet obtained using the same Abandoned US20130130055A1 (en)

Applications Claiming Priority (7)

Application Number Priority Date Filing Date Title
JP2010-069015 2010-03-25
JP2010069015 2010-03-25
JP2010183825 2010-08-19
JP2010-193825 2010-08-19
JP2010206515A JP5786296B2 (ja) 2010-03-25 2010-09-15 表面処理鋼板、その製造方法およびそれを用いた樹脂被覆鋼板
JP2010-206515 2010-09-15
PCT/JP2011/058154 WO2011118846A1 (fr) 2010-03-25 2011-03-24 Tôle d'acier traitée en surface, procédé de fabrication de cette dernière et tôle d'acier recouverte de résine utilisant cette dernière

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2011/058154 A-371-Of-International WO2011118846A1 (fr) 2010-03-25 2011-03-24 Tôle d'acier traitée en surface, procédé de fabrication de cette dernière et tôle d'acier recouverte de résine utilisant cette dernière

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US15/475,393 Division US10392709B2 (en) 2010-03-25 2017-03-31 Coated steel sheet, method for producing the same, and resin-coated steel sheet obtained using the same

Publications (1)

Publication Number Publication Date
US20130130055A1 true US20130130055A1 (en) 2013-05-23

Family

ID=44673381

Family Applications (2)

Application Number Title Priority Date Filing Date
US13/636,858 Abandoned US20130130055A1 (en) 2010-03-25 2011-03-24 Coated steel sheet, method for producing the same, and resin-coated steel sheet obtained using the same
US15/475,393 Expired - Fee Related US10392709B2 (en) 2010-03-25 2017-03-31 Coated steel sheet, method for producing the same, and resin-coated steel sheet obtained using the same

Family Applications After (1)

Application Number Title Priority Date Filing Date
US15/475,393 Expired - Fee Related US10392709B2 (en) 2010-03-25 2017-03-31 Coated steel sheet, method for producing the same, and resin-coated steel sheet obtained using the same

Country Status (6)

Country Link
US (2) US20130130055A1 (fr)
EP (1) EP2540867A4 (fr)
JP (1) JP5786296B2 (fr)
CN (2) CN102812156B (fr)
MY (1) MY168768A (fr)
WO (1) WO2011118846A1 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20140349135A1 (en) * 2013-05-27 2014-11-27 Thyssenkrupp Rasselstein Gmbh Method for coating a steel sheet with a metal layer
US20150111057A1 (en) * 2012-05-29 2015-04-23 Toyo Kohan Co., Ltd. Surface-Treated Steel Sheet for Container Having Excellent Processing Adhesion to Resin, Method For Manufacturing Same, and Can
US20160111182A1 (en) * 2013-05-23 2016-04-21 Jfe Steel Corporation Electrical steel sheet provided with insulating coating
US20170001415A1 (en) * 2014-08-27 2017-01-05 Schlumberger Technology Corporation Steel Armor Wire Coatings
US11859289B2 (en) 2019-12-19 2024-01-02 Nippon Steel Corporation Sn-based plated steel sheet
US11946121B2 (en) 2017-07-28 2024-04-02 Jfe Steel Corporation Steel sheet for battery outer tube cans, battery outer tube can and battery

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102339193B1 (ko) * 2017-07-28 2021-12-13 제이에프이 스틸 가부시키가이샤 전지 외통캔용 강판, 전지 외통캔 및 전지
EP4052834A4 (fr) * 2019-10-31 2023-01-04 JFE Steel Corporation Procédé de soudage mig
MX2022006167A (es) * 2019-11-22 2022-06-14 Ppg Ind Ohio Inc Metodos para depositar electrolicamente composiciones de pretratamiento.

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090032144A1 (en) * 2007-08-03 2009-02-05 Mcmillen Mark W Pretreatment compositions and methods for coating a metal substrate
US20100035055A1 (en) * 2006-12-13 2010-02-11 Kazuhisa Okai Surface-treated galvanized steel sheet with superior flat-portion corrosion resistance, blackening resistance, and appearance and corrosion resistance after press forming and aqueous surface-treatment liquid for galvanized steel sheet
US20130266819A1 (en) * 2010-12-07 2013-10-10 Henkel Ag & Co. Kgaa Metal pretreatment composition containing zirconium, copper, and metal chelating agents and related coatings on metal substrates

Family Cites Families (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3392008B2 (ja) * 1996-10-30 2003-03-31 日本表面化学株式会社 金属の保護皮膜形成処理剤と処理方法
AU1887601A (en) * 1999-12-13 2001-06-18 Toyo Kohan Co. Ltd. Method for producing surface treated steel sheet, surface treated steel sheet and surface treated steel sheet coated with resin
JP2001247977A (ja) * 2000-03-03 2001-09-14 Hitachi Ltd クロムフリー金属表面処理組成物
JP2004307923A (ja) * 2003-04-07 2004-11-04 Nippon Steel Corp 耐食性、塗装性及び加工性に優れる表面処理鋼板
JP2005023422A (ja) * 2003-06-09 2005-01-27 Nippon Paint Co Ltd 金属表面処理方法及び表面処理金属
JP2005048200A (ja) * 2003-07-29 2005-02-24 Jfe Steel Kk 耐食性および皮膜外観に優れる表面処理鋼板
JP5252925B2 (ja) 2005-11-22 2013-07-31 日本パーカライジング株式会社 表面化成処理液および化成処理金属板の製造方法
JP4470874B2 (ja) 2005-11-30 2010-06-02 Ｊｆｅスチール株式会社 表面処理亜鉛系めっき鋼板
JP5093797B2 (ja) 2006-03-24 2012-12-12 新日本製鐵株式会社 製缶加工性に優れた容器用鋼板
EP2006416B1 (fr) * 2006-03-29 2015-08-26 Nippon Steel & Sumitomo Metal Corporation Feuille en acier pour contenants
JP2008088552A (ja) * 2006-09-08 2008-04-17 Nippon Paint Co Ltd 金属基材の表面処理方法、当該表面処理方法により処理されてなる金属材料、及び当該金属材料の塗装方法。
CN101466872B (zh) * 2006-09-08 2011-05-18 新日本制铁株式会社 容器用钢板及其制造方法
JP4998707B2 (ja) * 2007-01-29 2012-08-15 Ｊｆｅスチール株式会社 表面処理金属板およびその製造方法、ならびに樹脂被覆金属板、金属缶および缶蓋
JP5467719B2 (ja) * 2007-12-25 2014-04-09 Ｊｆｅスチール株式会社 表面処理鋼板の製造方法
JP5251078B2 (ja) 2007-11-16 2013-07-31 新日鐵住金株式会社 容器用鋼板とその製造方法
JPWO2009081807A1 (ja) * 2007-12-21 2011-05-06 関西ペイント株式会社 表面処理された金属基材の製造方法及び該製造方法により得られた表面処理された金属基材、並びに金属基材処理方法及び該方法によって処理された金属基材
JP5123052B2 (ja) * 2008-05-26 2013-01-16 日本パーカライジング株式会社 表面化成処理液、化成処理金属板およびその製造方法、ならびに上層被覆金属板およびその製造方法
JP4886811B2 (ja) * 2008-06-05 2012-02-29 新日本製鐵株式会社 有機皮膜性能に優れた容器用鋼板およびその製造方法
JP5085439B2 (ja) * 2008-06-13 2012-11-28 新日本製鐵株式会社 金属（水）酸化物被覆金属材料

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20100035055A1 (en) * 2006-12-13 2010-02-11 Kazuhisa Okai Surface-treated galvanized steel sheet with superior flat-portion corrosion resistance, blackening resistance, and appearance and corrosion resistance after press forming and aqueous surface-treatment liquid for galvanized steel sheet
US20090032144A1 (en) * 2007-08-03 2009-02-05 Mcmillen Mark W Pretreatment compositions and methods for coating a metal substrate
US20130266819A1 (en) * 2010-12-07 2013-10-10 Henkel Ag & Co. Kgaa Metal pretreatment composition containing zirconium, copper, and metal chelating agents and related coatings on metal substrates

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
English Machine Translation of Yamaguchi JP 2004-307923, JPO, Accessed 12/29/2014. *

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20150111057A1 (en) * 2012-05-29 2015-04-23 Toyo Kohan Co., Ltd. Surface-Treated Steel Sheet for Container Having Excellent Processing Adhesion to Resin, Method For Manufacturing Same, and Can
US10526109B2 (en) * 2012-05-29 2020-01-07 Toyo Kohan Co., Ltd. Surface-treated steel sheet for container having excellent processing adhesion to resin, method for manufacturing same, and can
US20160111182A1 (en) * 2013-05-23 2016-04-21 Jfe Steel Corporation Electrical steel sheet provided with insulating coating
US20140349135A1 (en) * 2013-05-27 2014-11-27 Thyssenkrupp Rasselstein Gmbh Method for coating a steel sheet with a metal layer
US20170001415A1 (en) * 2014-08-27 2017-01-05 Schlumberger Technology Corporation Steel Armor Wire Coatings
US11946121B2 (en) 2017-07-28 2024-04-02 Jfe Steel Corporation Steel sheet for battery outer tube cans, battery outer tube can and battery
US11859289B2 (en) 2019-12-19 2024-01-02 Nippon Steel Corporation Sn-based plated steel sheet

Also Published As

Publication number Publication date
MY168768A (en) 2018-12-04
CN105667007B (zh) 2018-02-06
WO2011118846A1 (fr) 2011-09-29
JP5786296B2 (ja) 2015-09-30
US20170204521A1 (en) 2017-07-20
JP2012062509A (ja) 2012-03-29
CN105667007A (zh) 2016-06-15
CN102812156A (zh) 2012-12-05
CN102812156B (zh) 2016-12-07
US10392709B2 (en) 2019-08-27
EP2540867A1 (fr) 2013-01-02
EP2540867A4 (fr) 2014-01-22

Similar Documents

Publication Publication Date Title
US10392709B2 (en) Coated steel sheet, method for producing the same, and resin-coated steel sheet obtained using the same
JP5978576B2 (ja) 容器用鋼板およびその製造方法
JP5467719B2 (ja) 表面処理鋼板の製造方法
US8877348B2 (en) Surface-treated steel sheet and resin-coated steel sheet
CN103097582A (zh) 容器用钢板及其制造方法
US9580816B2 (en) Apparatus for continuous electrolytic treatment of steel sheet and method for producing surface-treated steel sheet using the same
JP5648522B2 (ja) 表面処理鋼板の製造方法
JP6168101B2 (ja) 表面処理鋼板、その製造方法およびそれを用いた樹脂被覆鋼板
JP5772845B2 (ja) 表面処理鋼板の製造方法
JP2010255065A (ja) 表面処理鋼板およびその製造方法
JP5742147B2 (ja) 表面処理鋼板、その製造方法およびそれを用いた樹脂被覆鋼板
JP5257192B2 (ja) 表面処理鋼板および樹脂被覆鋼板の製造方法
JP5151964B2 (ja) 表面処理鋼板、その製造方法および樹脂被覆鋼板
JP2012036424A (ja) 表面処理鋼板の製造方法および樹脂被覆鋼板の製造方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: JFE STEEL CORPORATION, JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:MIYAMOTO, YUKA;SUZUKI, TAKESHI;IWASA, HIROKI;AND OTHERS;SIGNING DATES FROM 20121101 TO 20121215;REEL/FRAME:029569/0570

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION