RU2005625C1

RU2005625C1 - Method of manufacturing multicore decorative panel

Info

Publication number: RU2005625C1
Authority: RU
Inventors: С.Б. Тертышный; В.С. Сахаров
Original assignee: Товарищество с ограниченной ответственностью - Фирма "Оникс"
Priority date: 1992-08-10
Filing date: 1992-08-10
Publication date: 1994-01-15

Abstract

FIELD: manufacturing of building materials. SUBSTANCE: glossy molding surface is coated by at least one layer of decorative mixture containing reinforcing and water- resistant additives and dyer and is then treated with water-containing solution and held till cracklings and formed. Then the base layer is applied and is subjected to effect of uniformly-distributed load capable of moving reciprocally in order to deform the cracks and fill them with the base material. The major components of the base material and decorative layer mixture is gypsum aggregate. EFFECT: improved decorative properties.

Description

Изобретение относится к производству декоративных строительных изделий, а именно, облицовочных панелей, применяемых для внутренней отделки помещения общественных, административных и других зданий. The invention relates to the production of decorative building products, namely, facing panels used for interior decoration of public, administrative and other buildings.

Известен способ формирования отделочного материала, имитирующего камень, заключающийся в раздельном приготовлении, по меньшей мере, двух композиций, нанесение смеси на подложку с последующим отверждением. A known method of forming a decorative material that simulates stone, which consists in the separate preparation of at least two compositions, applying the mixture to a substrate with subsequent curing.

Известный способ не обеспечивает качества лицевой поверхности, так как декоративный слой формируется последним, его лицевая сторона может иметь наплывы, неровности. На ее внешний вид существенно будут влиять качество поверхности подложки, на которой формируют декоративный слой, вязкость смеси композиций, способ нанесения смеси. The known method does not ensure the quality of the front surface, since the decorative layer is formed last, its front side may have influxes, bumps. Its appearance will be significantly affected by the quality of the surface of the substrate on which the decorative layer is formed, the viscosity of the mixture of compositions, the method of applying the mixture.

Наиболее близким к изобретению является способ изготовления декоративной пластины, включающий образование основы с рисунчатым слоем, нанесение прозрачной грунтовки, покрытие этого слоя водным раствором крахмального клея, высушивание его до образования небольших трещин, втирание в них красителя, удаление лишнего красителя; покрытие быстро затвердевающим пленкообразующим адгезивом. Closest to the invention is a method of manufacturing a decorative plate, including forming a base with a patterned layer, applying a transparent primer, coating this layer with an aqueous solution of starch glue, drying it to form small cracks, rubbing dye into them, removing excess dye; coating with rapidly hardening film-forming adhesive.

Недостатком известного способа является снижение качества лицевой поверхности, сложность процесса. Лицевой декоративный слой формируется не на формующей плоскости, а на основе посредством наложения слоев, поэтому на лицевой стороне изделия возможны неровности, наплывы, что, в свою очередь, снижает декоративное восприятие изделия. На качество этой поверхности существенное влияние будет оказывать шероховатость прилегающей поверхности основы, вязкость ингредиентов, накладываемых на основу слоев, их текучесть, способ нанесения. The disadvantage of this method is the decrease in the quality of the front surface, the complexity of the process. The front decorative layer is formed not on the forming plane, but on the basis of the application of layers, therefore, irregularities and sagging are possible on the front side of the product, which in turn reduces the decorative perception of the product. The quality of this surface will be significantly affected by the roughness of the adjacent surface of the base, the viscosity of the ingredients applied to the base of the layers, their fluidity, and the method of application.

Способ усложнен наличием таких операций, как нанесение грунтовки на рисунчатый слой, втирание красителя в трещины, удаление его остатков, покрытие пленкообразующим адгезивом. The method is complicated by the presence of operations such as applying a primer to the patterned layer, rubbing the dye into cracks, removing its residues, coating with a film-forming adhesive.

В изготовленном известным способом пластине декоративный эффект получается, в основном, за счет композиционного решения рисунчатого слоя, а мелкосетчатая структура поверхности, образованная трещинами с втертым в них красителем, не может имитировать плавные разводы, прожилки, вкрапления, свойственные природному камню, нашедшему широкое применение при производстве отделочных работ в строительстве. In a plate made by a known method, the decorative effect is obtained mainly due to the compositional solution of the patterned layer, and the fine-mesh surface structure formed by cracks with rubbed dye in them cannot imitate the smooth stains, streaks, inclusions characteristic of a natural stone, which has found wide application in finishing work in construction.

Цель изобретения - повышение качества лицевой поверхности, улучшение ее декоративного эффекта, а также упрощения процесса. Это достигается тем, что в способе изготовления многослойной декоративной панели, имитированной рисунком естественного камня, например, брекчиевидного мраморизированного известняка, включающем укладку на формующую поверхность, по меньшей мере, одного декоративного слоя, содержащего пигмент, нанесение на него раствора, содержащего воду, выдержку до образования трещин в декоративном слое, заполнение трещин путем механического воздействия в горизонтальной плоскости, нанесение слоя основы, отверждение и расформовку панели, в состав декоративного слоя дополнительно вводят упрочняющие и водостойкие добавки, наносят на глянцевую формующую поверхность, выдерживают, после чего увлажняют водой или водным раствором красителя, а заполнение трещин осуществляют после нанесения слоя основы путем наложения равномерно распределенной пригрузки и возвратно-поступательного ее перемещения с обеспечением деформирования трещин, при этом, в качестве основного ингредиента состава декоративного слоя и основы используют гипсовое вяжущее. The purpose of the invention is improving the quality of the front surface, improving its decorative effect, as well as simplifying the process. This is achieved by the fact that in the method of manufacturing a multilayer decorative panel imitated by a pattern of natural stone, for example, breccia-shaped marbled limestone, including laying on the forming surface of at least one decorative layer containing pigment, applying a solution containing water to it, holding it for up to the formation of cracks in the decorative layer, the filling of cracks by mechanical action in the horizontal plane, the application of a base layer, curing and molding of the panel, as part of the deco reinforcing and water-resistant additives are additionally introduced into the active layer, applied to the glossy forming surface, maintained, then moistened with water or an aqueous dye solution, and the cracks are filled after applying the base layer by applying a uniformly distributed load and its reciprocating movement to ensure crack deformation, at the same time, a gypsum binder is used as the main ingredient in the composition of the decorative layer and base.

Способ изготовления многослойной декоративной панели реализуется следующим образом. A method of manufacturing a multilayer decorative panel is implemented as follows.

Приготавливают в емкости раствор для образования декоративного слоя. Для этого берут 1 часть воды, в которой растворен краситель, составляющий 1-5% от массы гипсового вяжущего (в зависимости от тона окраски). После тщательного размешивания в нее вводят упрочняющие и гидрофобные добавки в количестве 0,5-2% от массы гипсового вяжущего и смесь снова перемешивают. Этой водой затворяют 3-4 мас. % гипсового вяжущего. A solution is prepared in the container to form a decorative layer. To do this, take 1 part of the water in which the dye is dissolved, comprising 1-5% by weight of the gypsum binder (depending on the color tone). After thorough mixing, hardening and hydrophobic additives are introduced into it in an amount of 0.5-2% by weight of the gypsum binder and the mixture is mixed again. 3–4 wt. % gypsum binder.

В качестве добавки используют лаки, клеевые водные растворы, раствор яичного белка и другие, а в качестве гипсового вяжущего используют строительный гипс, фосфогипс. As an additive, varnishes, glutinous aqueous solutions, egg white solution and others are used, and gypsum binder is used for building gypsum, phosphogypsum.

Подготовленную смесь любым из известных способов наносят слоем толщиной 1-3 мм на ровную горизонтально расположенную глянцевую поверхность, окаймленную по торцам, и дают выдержку до окончания химической реакции гипса с водой (до прекращения выделения (тепла). The prepared mixture by any of the known methods is applied with a layer of a thickness of 1-3 mm on a flat horizontally located glossy surface bordered at the ends, and give exposure to the end of the chemical reaction of gypsum with water (until the end of the release (heat).

После этого посредством пульверизатора декоративный слой увлажняют водой или водным раствором красителя, чем создают внутреннее напряжение в структуре декоративного слоя, поверхностная структура нарушается, и на ней проявляются линии разлома - трещины. Затем наносят слой основы, состоящий из затворенного гипсового вяжущего без красителя или с красителем, контрастным по цвету декоративному слою. После чего на поверхности основы равномерно размещают 5-7 пластмассовых пластин - пригрузочный инструмент, посредством которого в течение 1-2 с воздействуют на основу, придавая ему возвратно-поступательное движение в диапазоне 1-2 мм, при давлении 0,5-1 кг/см².After that, with the help of a spray gun, the decorative layer is moistened with water or an aqueous solution of the dye, which creates internal tension in the structure of the decorative layer, the surface structure is broken, and fault lines - cracks appear on it. Then, a base layer is applied, consisting of a shut gypsum binder without a dye or with a dye contrasting in color with the decorative layer. After that, 5-7 plastic plates are evenly placed on the surface of the base - a loading tool, through which they act on the base for 1-2 seconds, giving it a reciprocating movement in the range of 1-2 mm, at a pressure of 0.5-1 kg / cm ² .

При этом раствор материала основы, исходя из свойств гипсового вяжущего выделять тепло при отверждении, раздвигает декоративный слой по линиям разлома и затекает в образовавшиеся трещины, а механическое воздействие придает смеси большую подвижность, способствует расширению этих трещин до величины 0,5-1 мм и плотному заполнению их до плоскости формы материалом основы. In this case, the solution of the base material, based on the properties of the gypsum binder to generate heat during curing, pushes the decorative layer along the fault lines and flows into the formed cracks, and the mechanical effect gives the mixture greater mobility, contributes to the expansion of these cracks to 0.5-1 mm and dense filling them up to the plane of the mold with base material.

В случае нанесения на декоративный слой водного раствора красителя материал основы, затекающий в трещины, оттеняется цветом этого красителя. In the case of applying to the decorative layer an aqueous solution of the dye, the base material flowing into the cracks is tinted with the color of this dye.

Изделие выдерживают до отверждения основы, а затем расформовывают. The product is maintained until the base has cured, and then unformed.

В результате изготовленная декоративная панель имеет глянцевую лицевую поверхность с шероховатостью, соответствующей классу чистоты формовочной поверхности или ниже, но не более, чем на один класс. На фоне декоративного слоя этой поверхности видны прожилки, разводы, вкрапления контрастного цвета, это очень близко имитирует полированный камень естественных пород, например, брекчевидный мраморизированный известняк, мрамор месторождений в Тиллягуе, Каратау. (56) Заявка ЕПВ N 0368294, кл. В 44 F 9/04, 1990. As a result, the manufactured decorative panel has a glossy front surface with a roughness corresponding to the cleanliness class of the molding surface or lower, but not more than one class. Against the background of the decorative layer of this surface, streaks, stains, blots of contrasting color are visible, this very closely simulates polished stone of natural rocks, for example, brexpid marbled limestone, marble deposits in Tillagui, Karatau. (56) Application EPO N 0368294, cl. B 44 F 9/04, 1990.

Заявка Японии N 1-26880, кл. В 44 С 1/00, 1989. Japanese application N 1-26880, cl. B 44 C 1/00, 1989.

Claims

METHOD FOR PRODUCING A MULTI-LAYER DECORATIVE PANEL, imitated by a pattern of natural stone, for example, breccia-shaped marbled limestone, including laying at least one decorative layer containing pigment on the forming surface, applying a solution containing water on it, holding it to crack in the decorative layer, filling the cracks by mechanical action in a horizontal plane, applying a base layer, curing and forming of the panel, characterized in that the composition of the decorative hardening and water-resistant additives are additionally introduced, applied to the glossy forming surface, maintained, then moistened with water or an aqueous solution of the dye, and the cracks are filled after applying the base layer by applying a uniformly distributed load and its reciprocal movement to ensure crack deformation, at the same time, a gypsum binder is used as the main ingredient in the composition of the decorative layer and base.