WO2025161267A1 - Procédés de préparation de retardateur de flamme de ramollissement et de préparation de fil industriel en polyester retardateur de flamme flexible à haute résistance - Google Patents

Procédés de préparation de retardateur de flamme de ramollissement et de préparation de fil industriel en polyester retardateur de flamme flexible à haute résistance

Info

Publication number
WO2025161267A1
WO2025161267A1 PCT/CN2024/103754 CN2024103754W WO2025161267A1 WO 2025161267 A1 WO2025161267 A1 WO 2025161267A1 CN 2024103754 W CN2024103754 W CN 2024103754W WO 2025161267 A1 WO2025161267 A1 WO 2025161267A1
Authority
WO
WIPO (PCT)
Prior art keywords
flame
retardant
flexible
industrial yarn
polyester
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
PCT/CN2024/103754
Other languages
English (en)
Chinese (zh)
Inventor
赵金广
张玉梅
杨大矛
张玥
张烨
范瑞玲
汤方明
孙娜
杨勇
卫婷
王丽丽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Hengli Chemical Fiber Co Ltd
Original Assignee
Jiangsu Hengli Chemical Fiber Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Hengli Chemical Fiber Co Ltd filed Critical Jiangsu Hengli Chemical Fiber Co Ltd
Publication of WO2025161267A1 publication Critical patent/WO2025161267A1/fr
Pending legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

La présente invention appartient au domaine des filaments industriels en polyester, et concerne des procédés de préparation d'un retardateur de flamme de ramollissement et de préparation d'un fil industriel en polyester retardateur de flamme flexible à haute résistance. Le retardateur de flamme de ramollissement est du dioxyde de silicium qui est greffé en surface avec du polydiméthylsiloxane ; son procédé de préparation consiste à soumettre du dioxyde de silicium et du polydiméthylsiloxane à terminaison hydroxyle à une réaction de greffage pour obtenir le retardateur de flamme de ramollissement ; et son utilisation consiste à utiliser le retardateur de flamme de ramollissement et des copeaux de polyester à faible viscosité en tant que matières premières principales pour préparer un mélange maître de polyester retardateur de flamme de ramollissement, qui est ensuite soumis à un mélange à l'état fondu et à un filage conjointement avec des copeaux de polyester à viscosité élevée, de façon à préparer un fil industriel en polyester retardateur de flamme flexible à haute résistance, la viscosité intrinsèque des copeaux de polyester à faible viscosité étant de 0,65 à 0,68 dL/g, et la viscosité intrinsèque des copeaux de polyester à viscosité élevée étant de 1,05 à 1,20 dL/g. Les procédés de préparation selon la présente invention sont simples ; la flexibilité et l'ininflammabilité du fil industriel en polyester peuvent toutes deux être améliorées après l'ajout du retardateur de flamme de ramollissement préparé au fil industriel en polyester en tant qu'additif ; et le fil industriel en polyester retardateur de flamme flexible à haute résistance obtenu présente de bonnes performances.
PCT/CN2024/103754 2024-01-29 2024-07-05 Procédés de préparation de retardateur de flamme de ramollissement et de préparation de fil industriel en polyester retardateur de flamme flexible à haute résistance Pending WO2025161267A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN202410115842.5 2024-01-29
CN202410115842.5A CN117645728B (zh) 2024-01-29 2024-01-29 一种增柔阻燃剂及高强柔性阻燃聚酯工业丝的制备方法

Publications (1)

Publication Number Publication Date
WO2025161267A1 true WO2025161267A1 (fr) 2025-08-07

Family

ID=90046256

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2024/103754 Pending WO2025161267A1 (fr) 2024-01-29 2024-07-05 Procédés de préparation de retardateur de flamme de ramollissement et de préparation de fil industriel en polyester retardateur de flamme flexible à haute résistance

Country Status (2)

Country Link
CN (1) CN117645728B (fr)
WO (1) WO2025161267A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN120738788A (zh) * 2025-08-29 2025-10-03 武汉纺织大学 阻燃聚芳酯纳米纤维及其制备方法

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN117645728B (zh) * 2024-01-29 2024-06-18 江苏恒力化纤股份有限公司 一种增柔阻燃剂及高强柔性阻燃聚酯工业丝的制备方法
CN118272957B (zh) * 2024-06-03 2024-09-13 山东联欣环保科技有限公司 一种二氧化碳基聚碳酸酯纤维及其制备方法

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2009235314A (ja) * 2008-03-28 2009-10-15 Dow Corning Toray Co Ltd 熱可塑性樹脂用シリコーン系難燃剤、それを含んだ熱可塑性樹脂組成物およびそれを含んだ難燃性ポリエステル系繊維構造物の製造方法
CN110468464A (zh) * 2019-08-28 2019-11-19 无锡索力得科技发展有限公司 一种工业丝用高强阻燃聚酯切片及其制备方法
CN110528109A (zh) * 2019-08-28 2019-12-03 无锡索力得科技发展有限公司 一种高强阻燃涤纶工业丝及其制备方法
CN117210956A (zh) * 2023-09-04 2023-12-12 上海德福伦新材料科技有限公司 阻燃抑熔滴聚酯纤维的制备方法
CN117306014A (zh) * 2023-10-13 2023-12-29 南京市永信合智能科技有限公司 一种阻燃聚酯纤维及其制备方法
CN117645728A (zh) * 2024-01-29 2024-03-05 江苏恒力化纤股份有限公司 一种增柔阻燃剂及高强柔性阻燃聚酯工业丝的制备方法

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3019562B2 (ja) * 1991-12-10 2000-03-13 東レ株式会社 絹様の光学特性を有するポリエステル繊維
CN108129671B (zh) * 2017-12-18 2021-01-29 常州大学 一种基于硅橡胶微球制备具有超疏水性的微纳小球的方法
CN108252104B (zh) * 2017-12-23 2020-06-30 浙江凯洛琪服饰有限公司 一种纺织平滑剂的制备方法
WO2020079565A1 (fr) * 2018-10-16 2020-04-23 Sabic Global Technologies B.V. Préimprégné composite renforcé par des fibres continues formé d'un polyester ignifuge
CN110372904B (zh) * 2019-07-19 2021-07-30 常州大学 一种杂化材料改性聚酯薄膜的制备方法
CN112921446B (zh) * 2021-01-27 2022-02-22 合肥清华胜嘉服饰有限公司 一种耐磨性强的合成纤维及其制备方法
CN116925356A (zh) * 2022-03-29 2023-10-24 中国科学院化学研究所 一种羟基封端的二甲基二苯基聚硅氧烷的制备方法
CN115612061B (zh) * 2022-11-15 2024-06-21 福建永聚兴新材料科技有限公司 一种耐低温高强度热塑性弹性体复合材料
CN116476496B (zh) * 2023-05-18 2023-09-01 沧州兆阳纸塑包装有限公司 高阻隔抗皱pp隔离膜

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2009235314A (ja) * 2008-03-28 2009-10-15 Dow Corning Toray Co Ltd 熱可塑性樹脂用シリコーン系難燃剤、それを含んだ熱可塑性樹脂組成物およびそれを含んだ難燃性ポリエステル系繊維構造物の製造方法
CN110468464A (zh) * 2019-08-28 2019-11-19 无锡索力得科技发展有限公司 一种工业丝用高强阻燃聚酯切片及其制备方法
CN110528109A (zh) * 2019-08-28 2019-12-03 无锡索力得科技发展有限公司 一种高强阻燃涤纶工业丝及其制备方法
CN117210956A (zh) * 2023-09-04 2023-12-12 上海德福伦新材料科技有限公司 阻燃抑熔滴聚酯纤维的制备方法
CN117306014A (zh) * 2023-10-13 2023-12-29 南京市永信合智能科技有限公司 一种阻燃聚酯纤维及其制备方法
CN117645728A (zh) * 2024-01-29 2024-03-05 江苏恒力化纤股份有限公司 一种增柔阻燃剂及高强柔性阻燃聚酯工业丝的制备方法

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN120738788A (zh) * 2025-08-29 2025-10-03 武汉纺织大学 阻燃聚芳酯纳米纤维及其制备方法

Also Published As

Publication number Publication date
CN117645728A (zh) 2024-03-05
CN117645728B (zh) 2024-06-18

Similar Documents

Publication Publication Date Title
WO2025161267A1 (fr) Procédés de préparation de retardateur de flamme de ramollissement et de préparation de fil industriel en polyester retardateur de flamme flexible à haute résistance
CN102362021B (zh) 非晶性聚醚酰亚胺类纤维和耐热性布帛
JP3228977B2 (ja) カルボジイミド変性ポリエステル繊維およびその製造方法
CN111349325B (zh) 改性生物基聚合物纤维组合物和改性生物基聚合物纤维及其制备方法
EP2604730A1 (fr) Fibre amorphe de fusion thermique, corps de structure fibreuse et article moulé thermorésistant
TW200407471A (en) Poly (trimethylene terephthalate) bicomponent fibers
Ren et al. Enhancing flame retardancy and hydrolysis resistance of flame retardant copolyester fibers by reactive carbodiimide
CN115874307B (zh) 一种抗蠕变阻燃涤纶工业丝的制备方法
TW202122451A (zh) 具超高流動性和優異穩定性之聚酯及其熔噴纖維
JP2005299067A (ja) ポリ乳酸繊維
CN117488430B (zh) 一种抗收缩聚酯纤维的制备方法
Arık et al. Thermogravimetric, microscopic and mechanical analyses of PBT and pet yarns
JP3277704B2 (ja) 耐摩耗性の良好なポリエステル繊維とその製造方法
JP5463180B2 (ja) ポリカーボネート繊維
CN116575133B (zh) 一种基于熔体反应挤出的阻燃涤纶纤维的制备方法
JP2010229597A (ja) ポリカーボネート繊維およびその製造方法、ならびに繊維集合物
JP2005097819A (ja) ポリエステル系繊維構造物
CN108060465A (zh) 季戊四醇磷酸酯用于改善尼龙阻燃性和可纺性的用途
CN117624573B (zh) 一种均相分散二氧化硅的阻燃聚酯及其制备方法和应用
JP2011106060A (ja) ポリアリーレンスルフィド繊維
CN103556291B (zh) 一种抗蠕变抗水解聚酯fdy纤维及其制备方法
KR101037123B1 (ko) 난연성이 우수한 산업용 폴리에스테르 섬유 및 이의 제조방법
Xiaoxiang et al. Study on Flame Retardancy of Phosphate Reinforced Polyester Fiber
JP4720331B2 (ja) 難燃性繊維構造物
JP2009084754A (ja) ポリエステル繊維の製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 24921302

Country of ref document: EP

Kind code of ref document: A1