WO2025047007A1 - Élément de production d'énergie thermoélectrique transversal hybride et procédé de production d'énergie l'utilisant - Google Patents

Élément de production d'énergie thermoélectrique transversal hybride et procédé de production d'énergie l'utilisant Download PDF

Info

Publication number
WO2025047007A1
WO2025047007A1 PCT/JP2024/018449 JP2024018449W WO2025047007A1 WO 2025047007 A1 WO2025047007 A1 WO 2025047007A1 JP 2024018449 W JP2024018449 W JP 2024018449W WO 2025047007 A1 WO2025047007 A1 WO 2025047007A1
Authority
WO
WIPO (PCT)
Prior art keywords
thermoelectric
effect
layer
magnetic field
horizontal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
PCT/JP2024/018449
Other languages
English (en)
Japanese (ja)
Inventor
健一 内田
孝昌 平井
アミン ホセイン セペリ
康之 追川
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
National Institute for Materials Science
Original Assignee
National Institute for Materials Science
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by National Institute for Materials Science filed Critical National Institute for Materials Science
Publication of WO2025047007A1 publication Critical patent/WO2025047007A1/fr
Pending legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

L'invention concerne un élément de conversion thermoélectrique transversal ayant une performance de production d'énergie thermoélectrique comparable ou supérieure à celle de l'effet Seebeck. L'élément de conversion thermoélectrique transversal comprend : une première électrode et une seconde électrode qui sont opposées l'une à l'autre ; et un stratifié qui est pris en sandwich entre les première et seconde électrodes et qui est électriquement connecté à la fois aux première et seconde électrodes. Le stratifié a une structure dans laquelle des couches d'un premier matériau thermoélectrique et des couches d'un second matériau thermoélectrique sont stratifiées en alternance. Le premier matériau thermoélectrique et le second matériau thermoélectrique ont des valeurs différentes de coefficient Seebeck, de conductivité électrique et/ou de conductivité thermique. Au moins l'un des premier et second matériaux thermoélectriques présente un effet magnéto-thermoélectrique longitudinal ou un effet magnéto-thermoélectrique transversal. Des surfaces stratifiées des premières couches et des secondes couches sont inclinées par rapport à une direction dans laquelle la première électrode et la seconde électrode sont opposées l'une à l'autre. Une différence de potentiel est générée entre les première et seconde électrodes en raison d'une différence de température dans une direction perpendiculaire à la direction d'opposition dans l'élément de conversion thermoélectrique transversal et d'un champ magnétique appliqué dans une direction dans laquelle l'effet magnéto-thermoélectrique est généré.
PCT/JP2024/018449 2023-08-25 2024-05-20 Élément de production d'énergie thermoélectrique transversal hybride et procédé de production d'énergie l'utilisant Pending WO2025047007A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2023137279 2023-08-25
JP2023-137279 2023-08-25

Publications (1)

Publication Number Publication Date
WO2025047007A1 true WO2025047007A1 (fr) 2025-03-06

Family

ID=94818751

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2024/018449 Pending WO2025047007A1 (fr) 2023-08-25 2024-05-20 Élément de production d'énergie thermoélectrique transversal hybride et procédé de production d'énergie l'utilisant

Country Status (1)

Country Link
WO (1) WO2025047007A1 (fr)

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2010094964A (ja) * 2008-10-16 2010-04-30 Korea Electrotechnology Research Inst スライス積層プレス法による機能性材料の製造方法およびこれにより製造された機能性材料
JP2018078147A (ja) * 2016-11-07 2018-05-17 Tdk株式会社 磁気熱電素子および発電方法
WO2023054583A1 (fr) * 2021-09-30 2023-04-06 国立研究開発法人物質・材料研究機構 Corps thermoélectrique, élément de génération thermoélectrique, corps thermoélectrique multicouche, élément de génération thermoélectrique multicouche, générateur thermoélectrique et capteur de flux de chaleur

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2010094964A (ja) * 2008-10-16 2010-04-30 Korea Electrotechnology Research Inst スライス積層プレス法による機能性材料の製造方法およびこれにより製造された機能性材料
JP2018078147A (ja) * 2016-11-07 2018-05-17 Tdk株式会社 磁気熱電素子および発電方法
WO2023054583A1 (fr) * 2021-09-30 2023-04-06 国立研究開発法人物質・材料研究機構 Corps thermoélectrique, élément de génération thermoélectrique, corps thermoélectrique multicouche, élément de génération thermoélectrique multicouche, générateur thermoélectrique et capteur de flux de chaleur

Similar Documents

Publication Publication Date Title
JP6079995B2 (ja) 熱電発電デバイス
US11889762B2 (en) Vertical thermoelectric conversion element and device with thermoelectric power generation application or heat flow sensor using same
CN111052423B (zh) 热电装置
JP7669069B2 (ja) 熱電体、熱電発電素子、多層熱電体、多層熱電発電素子、熱電発電機、及び熱流センサ
US11011692B2 (en) Thermoelectric device utilizing non-zero berry curvature
Uchida et al. Hybrid Transverse Magneto‐Thermoelectric Cooling in Artificially Tilted Multilayers
Terasaki 1.09-Thermal Conductivity and Thermoelectric Power of Semiconductors
Zberecki et al. Enhanced thermoelectric efficiency in ferromagnetic silicene nanoribbons terminated with hydrogen atoms
Hirai et al. Hybridizing anomalous Nernst effect in artificially tilted multilayer based on magnetic topological material
Adachi et al. Fundamentals and Advances in Transverse Thermoelectrics
Ando et al. Multifunctional composite magnet realizing record-high transverse thermoelectric generation
Gomes et al. Flexible thermoelectric films based on interconnected magnetic nanowire networks
Park et al. High heat-flux sensitivity of the planar coil device based on the anomalous Nernst effect
JP6565689B2 (ja) 熱電変換素子、熱電変換素子モジュールおよび熱電変換素子の製造方法
WO2025047007A1 (fr) Élément de production d'énergie thermoélectrique transversal hybride et procédé de production d'énergie l'utilisant
JP7709717B2 (ja) 熱電素子及び熱電装置
WO2025047008A1 (fr) Élément de modulation de température thermoélectrique horizontal hybride et procédé de modulation de température l'utilisant
JP2020098860A (ja) 熱電変換装置、熱電変換方法
JP7505310B2 (ja) 熱電変換材料
Das et al. Thermopile based on anisotropic magneto-Peltier effect
JP2023120825A (ja) 熱電変換素子
JP2003060244A (ja) 冷却素子と熱電変換材料
Watzman et al. Utilizing magnetization and spin in thermoelectric applications: SJ Watzman et al.
WO2019124257A1 (fr) Élément de conversion thermoélectrique
Juarez-Acosta et al. On the interfacial thermal conductance of a ferromagnetic metal junction

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 24859056

Country of ref document: EP

Kind code of ref document: A1