WO2024203317A1 - Feuille d'acier inoxydable ferritique - Google Patents

Feuille d'acier inoxydable ferritique Download PDF

Info

Publication number
WO2024203317A1
WO2024203317A1 PCT/JP2024/009697 JP2024009697W WO2024203317A1 WO 2024203317 A1 WO2024203317 A1 WO 2024203317A1 JP 2024009697 W JP2024009697 W JP 2024009697W WO 2024203317 A1 WO2024203317 A1 WO 2024203317A1
Authority
WO
WIPO (PCT)
Prior art keywords
stainless steel
ferritic stainless
steel sheet
mass
value
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
PCT/JP2024/009697
Other languages
English (en)
Japanese (ja)
Inventor
拓哉 稲田
直樹 平川
一成 今川
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Steel Stainless Steel Corp
Original Assignee
Nippon Steel Stainless Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel Stainless Steel Corp filed Critical Nippon Steel Stainless Steel Corp
Priority to KR1020257026874A priority Critical patent/KR20250134664A/ko
Priority to CN202480011245.6A priority patent/CN120641591A/zh
Priority to JP2025510423A priority patent/JPWO2024203317A1/ja
Publication of WO2024203317A1 publication Critical patent/WO2024203317A1/fr
Anticipated expiration legal-status Critical
Pending legal-status Critical Current

Abstract

L'invention concerne une feuille d'acier inoxydable ferritique qui présente une faible limite d'élasticité conventionnelle et une faible résistance au striage, et réduit l'anisotropie dans le plan tout en présentant une valeur r élevée, ainsi que le procédé de production de celle-ci. La feuille d'acier inoxydable ferritique (1) présente une taille de grain cristallin comprise entre 15 et 40 µm inclus, et satisfait les relations I111 ≥ 10,0 et 0,2 ≤ (Ia/Ib) ≤ 4,0 lorsque la plus grande valeur parmi la résistance d'orientation de cristaux Ia [111]<110> et la résistance d'orientation de cristaux [111]<112> Ib dans une section transversale (13) parallèle à la surface de laminage dans le centre d'épaisseur de plaque est exprimée par I111.
PCT/JP2024/009697 2023-03-30 2024-03-13 Feuille d'acier inoxydable ferritique Pending WO2024203317A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
KR1020257026874A KR20250134664A (ko) 2023-03-30 2024-03-13 페라이트계 스테인리스 강판
CN202480011245.6A CN120641591A (zh) 2023-03-30 2024-03-13 铁素体系不锈钢板
JP2025510423A JPWO2024203317A1 (fr) 2023-03-30 2024-03-13

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2023-056652 2023-03-30
JP2023056652 2023-03-30

Publications (1)

Publication Number Publication Date
WO2024203317A1 true WO2024203317A1 (fr) 2024-10-03

Family

ID=92905786

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2024/009697 Pending WO2024203317A1 (fr) 2023-03-30 2024-03-13 Feuille d'acier inoxydable ferritique

Country Status (5)

Country Link
JP (1) JPWO2024203317A1 (fr)
KR (1) KR20250134664A (fr)
CN (1) CN120641591A (fr)
TW (1) TWI888069B (fr)
WO (1) WO2024203317A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN119506721A (zh) * 2024-11-01 2025-02-25 任丘市华凯通信设备有限公司 一种高强度抱箍及其制备方法

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016068139A1 (fr) * 2014-10-31 2016-05-06 新日鐵住金ステンレス株式会社 Plaque d'acier inoxydable à base de ferrite, tube d'acier et son procédé de production
JP2018184660A (ja) * 2017-04-25 2018-11-22 Ｊｆｅスチール株式会社 フェライト系ステンレス鋼板およびその製造方法
JP2019173149A (ja) * 2018-03-26 2019-10-10 日鉄ステンレス株式会社 フェライト系ステンレス鋼板、およびその製造方法ならびにフェライト系ステンレス部材
JP2022079072A (ja) * 2020-11-16 2022-05-26 日鉄ステンレス株式会社 フェライト系ステンレス鋼板及びその製造方法
WO2023089693A1 (fr) * 2021-11-17 2023-05-25 日鉄ステンレス株式会社 Feuille d'acier inoxydable ferritique
JP2023147504A (ja) * 2022-03-30 2023-10-13 日鉄ステンレス株式会社 フェライト系ステンレス鋼板およびその製造方法

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3788311B2 (ja) * 2001-10-31 2006-06-21 Ｊｆｅスチール株式会社 フェライト系ステンレス鋼板及びその製造方法
WO2021065738A1 (fr) * 2019-10-02 2021-04-08 日鉄ステンレス株式会社 Tôle en acier inoxydable ferritique, procédé pour la produire et élément d'acier inoxydable ferritique

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016068139A1 (fr) * 2014-10-31 2016-05-06 新日鐵住金ステンレス株式会社 Plaque d'acier inoxydable à base de ferrite, tube d'acier et son procédé de production
JP2018184660A (ja) * 2017-04-25 2018-11-22 Ｊｆｅスチール株式会社 フェライト系ステンレス鋼板およびその製造方法
JP2019173149A (ja) * 2018-03-26 2019-10-10 日鉄ステンレス株式会社 フェライト系ステンレス鋼板、およびその製造方法ならびにフェライト系ステンレス部材
JP2022079072A (ja) * 2020-11-16 2022-05-26 日鉄ステンレス株式会社 フェライト系ステンレス鋼板及びその製造方法
WO2023089693A1 (fr) * 2021-11-17 2023-05-25 日鉄ステンレス株式会社 Feuille d'acier inoxydable ferritique
JP2023147504A (ja) * 2022-03-30 2023-10-13 日鉄ステンレス株式会社 フェライト系ステンレス鋼板およびその製造方法

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN119506721A (zh) * 2024-11-01 2025-02-25 任丘市华凯通信设备有限公司 一种高强度抱箍及其制备方法

Also Published As

Publication number Publication date
JPWO2024203317A1 (fr) 2024-10-03
KR20250134664A (ko) 2025-09-11
CN120641591A (zh) 2025-09-12
TWI888069B (zh) 2025-06-21
TW202505044A (zh) 2025-02-01

Similar Documents

Publication Publication Date Title
CN104093871B (zh) 耐热铁素体系不锈钢冷轧钢板、冷轧基材用铁素体系不锈钢热轧钢板及其制造方法
CN104968823B (zh) 加工性优良的铁素体系不锈钢板及其制造方法
TWI404808B (zh) 淬火性優異之硼添加鋼板及製造方法
JP5043248B1 (ja) 高強度焼付硬化型冷延鋼板及びその製造方法
CN105658830B (zh) 拉伸加工性和渗碳热处理后的表面硬度优异的热轧钢板
JP6851269B2 (ja) フェライト系ステンレス鋼板、鋼管および排気系部品用フェライト系ステンレス部材ならびにフェライト系ステンレス鋼板の製造方法
JP5362582B2 (ja) 耐食性及び張出成形性に優れたフェライト系ステンレス鋼及びその製造方法
JP5219689B2 (ja) 加工肌荒れの小さいフェライト系ステンレス鋼板およびその製造方法
JP2016191150A (ja) 靭性に優れたステンレス鋼板およびその製造方法
CN111032898A (zh) 铁素体系不锈钢热轧退火钢板及其制造方法
JPWO2019189872A1 (ja) フェライト系ステンレス鋼板、およびその製造方法ならびにフェライト系ステンレス部材
JP4562280B2 (ja) 加工性に優れ面内異方性の小さいフェライト系ステンレス鋼及びその製造方法
WO2024203317A1 (fr) Feuille d&#39;acier inoxydable ferritique
JP7166878B2 (ja) フェライト系ステンレス鋼板、およびその製造方法ならびにフェライト系ステンレス部材
JP2001207244A (ja) 延性、加工性および耐リジング性に優れたフェライト系ステンレス冷延鋼板およびその製造方法
KR20190077672A (ko) 리징성이 우수한 페라이트계 스테인리스강
JP2023147504A (ja) フェライト系ステンレス鋼板およびその製造方法
TWI875541B (zh) 肥粒鐵系不鏽鋼鋼板
JP3950384B2 (ja) 加工性に優れた高強度鋼管及びその製造方法
JP7723888B2 (ja) フェライト系ステンレス熱延鋼板およびその製造方法
JP2018188687A (ja) 耐熱部材用フェライト系ステンレス鋼板
WO2023140239A1 (fr) Tôle d&#39;acier laminée à froid et son procédé de fabrication
WO2025204697A1 (fr) Tôle d&#39;acier inoxydable et son procédé de fabrication
JP2002249853A (ja) フレーム用フェライト系ステンレス鋼材およびその製造方法
JP2024144173A (ja) 二相ステンレス鋼板

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 24779446

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2025510423

Country of ref document: JP

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: 2025510423

Country of ref document: JP

WWE Wipo information: entry into national phase

Ref document number: 202480011245.6

Country of ref document: CN

ENP Entry into the national phase

Ref document number: 1020257026874

Country of ref document: KR

Free format text: ST27 STATUS EVENT CODE: A-0-1-A10-A15-NAP-PA0105 (AS PROVIDED BY THE NATIONAL OFFICE)

WWE Wipo information: entry into national phase

Ref document number: 1020257026874

Country of ref document: KR

WWE Wipo information: entry into national phase

Ref document number: 2501005373

Country of ref document: TH

WWP Wipo information: published in national office

Ref document number: 202480011245.6

Country of ref document: CN

NENP Non-entry into the national phase

Ref country code: DE