WO2022065053A1 - エラストマー組成物、シール材およびシール材の製造方法 - Google Patents

エラストマー組成物、シール材およびシール材の製造方法 Download PDF

Info

Publication number
WO2022065053A1
WO2022065053A1 PCT/JP2021/033156 JP2021033156W WO2022065053A1 WO 2022065053 A1 WO2022065053 A1 WO 2022065053A1 JP 2021033156 W JP2021033156 W JP 2021033156W WO 2022065053 A1 WO2022065053 A1 WO 2022065053A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
mass
sealing material
elastomer composition
compound
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2021/033156
Other languages
English (en)
French (fr)
Inventor
雅則 岡崎
直樹 大住
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Valqua Ltd
Original Assignee
Valqua Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Valqua Ltd filed Critical Valqua Ltd
Priority to US18/246,695 priority Critical patent/US20230365800A1/en
Priority to CN202180064242.5A priority patent/CN116323788A/zh
Priority to JP2022551865A priority patent/JPWO2022065053A1/ja
Priority to EP21872184.3A priority patent/EP4219611A4/en
Priority to KR1020237011594A priority patent/KR20230078693A/ko
Publication of WO2022065053A1 publication Critical patent/WO2022065053A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

本発明の一実施形態は、エラストマー組成物、シール材またはシール材の製造方法に関し、該エラストマー組成物は、フッ素含有量が６９質量％以上であるパーフルオロエラストマー以外の架橋性フルオロエラストマー（Ａ１）と、フッ素含有量が６６～６８質量％の範囲にあるパーフルオロエラストマー以外の架橋性フルオロエラストマー（Ａ２）とを含む。

Description

エラストマー組成物、シール材およびシール材の製造方法
　本発明の一実施形態は、エラストマー組成物、シール材またはシール材の製造方法に関する。
　従来より、シール材は、各種用途に幅広く使用されており、これらの用途の中でも、シール材に最も負荷のかかるシール材の用途の一例として、半導体製造装置等に使用されるシール材が挙げられる。
　このようなシール材としては、耐プラズマ性や耐ラジカル性に優れるシール材を得ることができることから、フルオロエラストマー（ＦＫＭ）や、パーフルオロエラストマー（ＦＦＫＭ）などの架橋性フルオロエラストマーが使用されている。
　例えば、特許文献１には、所定量のＦＦＫＭとＦＫＭとを含むことを特徴とするシール材が開示されている。
　前記のような架橋性フルオロエラストマー製のシール材は、通常、該架橋性フルオロエラストマーに、架橋剤や架橋助剤などの添加剤を配合して得られたエラストマー組成物を用い、このエラストマー組成物を成形、架橋することでシール材として使用されている。
特許第４６２８８１４号公報
　前述したように、架橋性フルオロエラストマーに添加剤を配合してエラストマー組成物とする際には、該エラストマー組成物から所望の物性を示すシール材を製造するために、該エラストマー組成物中の各成分は均一に混合している必要がある。
　しかしながら、従来の架橋性フルオロエラストマーを用いた場合、特に液状やオイル状の成分を用いる場合には、このような均一なエラストマー組成物を作製するのに長い時間を要しており、この点で改良の余地があった。
　また、作製されたエラストマー組成物から、生産性よくシール材を形成する際には、分出し工程により、エラストマー組成物をシート化することが通常行われている。この分出し工程は、通常、ロール間にエラストマー組成物を通して行われるが、従来のエラストマー組成物を用いた場合には、ロール間にエラストマー組成物が噛み込まなかったり、ロールにうまく巻き付かなかったりして、シート化することが容易ではなかった（分出し性が悪かった）。従って、従来のエラストマー組成物は、成形性の点で改良の余地があった。
　本発明の一実施形態は、短時間で均一なエラストマー組成物とすることができ、成形性に優れるエラストマー組成物を提供する。
　本発明者が、前記課題を解決すべく鋭意検討した結果、下記構成例によれば、前記課題を解決できることを見出し、本発明を完成した。
　本発明の構成例は以下の通りである。
　［１］　フッ素含有量が６９質量％以上であるパーフルオロエラストマー以外の架橋性フルオロエラストマー（Ａ１）と、
　フッ素含有量が６６～６８質量％の範囲にあるパーフルオロエラストマー以外の架橋性フルオロエラストマー（Ａ２）と
を含むエラストマー組成物。
　［２］　前記フルオロエラストマー（Ａ１）および（Ａ２）がパーオキサイド架橋可能なフルオロエラストマーである、［１］に記載のエラストマー組成物。
　［３］　エチレン性不飽和結合を有するパーフルオロ骨格の化合物、および、エチレン性不飽和結合を有するシロキサン骨格の化合物から選ばれる少なくとも１種のエチレン性不飽和結合含有化合物（Ｂ）を含む、［１］または［２］に記載のエラストマー組成物。
　［４］　架橋剤を含む、［１］～［３］のいずれかに記載のエラストマー組成物。
　［５］　充填材の含有量が、前記フルオロエラストマー（Ａ１）および（Ａ２）の合計１００質量部に対し、５質量部以下である、［１］～［４］のいずれかに記載のエラストマー組成物。
　［６］　［１］～［５］のいずれかに記載のエラストマー組成物から得られたシール材。
　［７］　［１］～［５］のいずれかに記載のエラストマー組成物に放射線を照射する工程を含む、シール材の製造方法。
　本発明の一実施形態によれば、短時間で均一なエラストマー組成物とすることができ、成形性、特に分出し性に優れるエラストマー組成物を提供することができる。
　また、本発明の一実施形態によれば、該エラストマー組成物を用いることで、硬度、引張強さ、切断時伸び、および、１００％伸びにおける引張応力（１００％Ｍｏ）にバランスよく優れるシール材を得ることができ、さらに、本発明の一実施形態によれば、耐プラズマ性（耐ラジカル性）、耐クラック性、圧縮永久歪等に優れるシール材を得ることができる。
≪エラストマー組成物≫
　本発明の一実施形態に係るエラストマー組成物（以下「本組成物」ともいう。）は、フッ素含有量が６９質量％以上であるパーフルオロエラストマー以外の架橋性フルオロエラストマー（Ａ１）と、フッ素含有量が６６～６８質量％の範囲にあるパーフルオロエラストマー以外の架橋性フルオロエラストマー（Ａ２）とを含む。
　なお、本発明において、「エラストマー」と「ゴム」は同義であり、これらに特に区別はない。
＜架橋性フルオロエラストマー（Ａ１）および架橋性フルオロエラストマー（Ａ２）＞
　架橋性フルオロエラストマー（Ａ１）は、フッ素含有量が６９質量％以上であるパーフルオロエラストマー以外の架橋性のフルオロエラストマーであれば特に制限されず、架橋性フルオロエラストマー（Ａ２）は、フッ素含有量が６６～６８質量％の範囲にあるパーフルオロエラストマー以外の架橋性のフルオロエラストマーであれば特に制限されない。
　架橋性フルオロエラストマー（Ａ１）と架橋性フルオロエラストマー（Ａ２）とはフッ素含有量が前記範囲にあれば、これらのエラストマーを構成する構成単位の種類は、同様でも、異なっていてもよい。
　本組成物に含まれるフルオロエラストマー（Ａ１）は、１種でもよく、２種以上でもよい。また、本組成物に含まれるフルオロエラストマー（Ａ２）も、１種でもよく、２種以上でもよい。
　以下、架橋性フルオロエラストマー（Ａ１）と架橋性フルオロエラストマー（Ａ２）とを総称して、架橋性フルオロエラストマー（Ａ）ともいう。
　架橋性フルオロエラストマー（Ａ）は、未加硫フッ素ゴムなどともいい、架橋タイプとしては、パーオキサイド架橋、ポリオール架橋、アミン架橋、放射線架橋タイプなどが挙げられる。これらの中でも、プラズマ雰囲気下等において、パーティクルの発生源となる受酸剤を用いる必要がなく、得られたシール材を使用中に、パーティクルを発生させる恐れがない等の点で、パーオキサイド架橋可能なフルオロエラストマーであることが好ましい。
　架橋性フルオロエラストマー（Ａ）の具体例としては、フルオロエラストマー（ＦＫＭ）、フッ素系熱可塑性エラストマー（例：少なくとも１種のエラストマー性ポリマー鎖セグメントおよび少なくとも１種の非エラストマー性ポリマー鎖セグメントを含み、これらのうちの少なくとも一方は含フッ素ポリマー鎖セグメントであるエラストマー）が挙げられる。
　架橋性フルオロエラストマー（Ａ）としては、各種半導体ドライプロセスで使用されるプラズマ（プラズマエッチング処理）に対する耐性を示すシール材を得ることができるようなエラストマーが好ましく、耐プラズマ性が比較的良好であり、シール性に優れるＦＫＭがより好ましい。また、ＦＫＭは、安価で汎用性のある等の点でも好ましい。
　架橋性フルオロエラストマー（Ａ）としては、従来公知の方法で合成したものを用いてもよく、市販品を用いてもよい。該市販品としては、ダイキン工業（株）製の「ダイエル」、ケマーズ社製の「バイトン」、３Ｍ社製の「ダイニオン」、ソルベイ社製の「テクノフロン」等が挙げられる。
　架橋性フルオロエラストマー（Ａ１）のフッ素含有量は、６９質量％以上であり、好ましくは７０質量％以上であり、好ましくは７３質量％以下、より好ましくは７１質量％以下であり、架橋性フルオロエラストマー（Ａ２）のフッ素含有量は、６６～６８質量％である。
　フッ素含有量が前記範囲にある架橋性フルオロエラストマーを少なくとも２種類用いることで、短時間で均一なエラストマー組成物とすることができ、成形性に優れるエラストマー組成物を容易に得ることができ、硬度、引張強さ、切断時伸びおよび１００％Ｍｏにバランスよく優れるシール材を容易に得ることができる。
　前記フッ素含有量は、19Ｆ－ＮＭＲや1Ｈ－ＮＭＲ等を用いたフッ素の元素分析または質量分析法（ＭＳスペクトル法）等により、測定・算出することができる。
　なお、本発明におけるフッ素含有量は、小数点以下を四捨五入した値である。
　架橋性フルオロエラストマー（Ａ）のムーニー粘度は、好ましくは１０以上、より好ましくは１５以上、さらに好ましくは２０以上であり、好ましくは１４０以下、より好ましくは１００以下、さらに好ましくは８０以下、特に好ましくは６０以下である。
　架橋性フルオロエラストマー（Ａ）のムーニー粘度が前記範囲にあると、成形性、特に分出し性に優れるエラストマー組成物を容易に得ることができる。
　なお、本明細書におけるムーニー粘度は、ＡＳＴＭ　Ｄ　１６４６に準拠して測定した１２１℃におけるムーニー粘度（ＭＬ１＋１０）のことをいう。
　架橋性フルオロエラストマー（Ａ１）の一態様としては、ムーニー粘度が、好ましくは４０～１４０、より好ましくは４０～１００、さらに好ましくは４０～６０の範囲にある、架橋性フルオロエラストマー（Ａ１－１）と、ムーニー粘度が、好ましくは１０以上４０未満、より好ましくは１０～３０の範囲にある、架橋性フルオロエラストマー（Ａ１－２）とを用いることが好ましい。
　架橋性フルオロエラストマー（Ａ１－１）および（Ａ１－２）を用いることで、硬度、引張強さ、切断時伸びおよび１００％Ｍｏ等の得られるシール材の常態物性と、成形性、特に分出し性等のエラストマー組成物の物性とに、よりバランスよく優れるため好ましい。
　架橋性フルオロエラストマー（Ａ１）として、架橋性フルオロエラストマー（Ａ１－１）および（Ａ１－２）を用いる場合、これらの合計１００質量％に対する、架橋性フルオロエラストマー（Ａ１－１）の含有量は、好ましくは２０～８０質量％である。
　架橋性フルオロエラストマー（Ａ１－１）の含有量が前記範囲にあると、硬度、引張強さ、切断時伸びおよび１００％Ｍｏ等の得られるシール材の常態物性と、成形性、特に分出し性等のエラストマー組成物の物性とに、よりバランスよく優れるため好ましい。
　本組成物の固形分中の架橋性フルオロエラストマー（Ａ１）の含有量は、好ましくは４０質量％以上、より好ましくは５０質量％以上であり、好ましくは９５質量％以下、より好ましくは８５質量％以下である。
　架橋性フルオロエラストマー（Ａ１）含有量が前記範囲にあると、耐プラズマ性、耐薬品性等の化学的耐性に優れるシール材を容易に得ることができる。
　なお、本明細書において、固形分とは、溶剤以外の成分のことをいう。
　本組成物の固形分中の架橋性フルオロエラストマー（Ａ２）の含有量は、好ましくは２質量％以上、より好ましくは５質量％以上であり、好ましくは５０質量％以下、より好ましくは４０質量％以下である。
　架橋性フルオロエラストマー（Ａ２）含有量が前記範囲にあると、成形性および化学的耐性にバランスよく優れるシール材を容易に得ることができる。
　本組成物中の架橋性フルオロエラストマー（Ａ１）および（Ａ２）の合計含有量に対する、架橋性フルオロエラストマー（Ａ１）の含有量は、好ましくは６０質量％以上、より好ましくは６５質量％以上であり、好ましくは９５質量％以下、より好ましくは９０質量％以下である。
　架橋性フルオロエラストマー（Ａ１）および（Ａ２）の含有量の質量比が前記範囲にあると、成形性および化学的耐性にバランスよく優れるシール材を容易に得ることができる。
［ＦＫＭ］
　ＦＫＭとしては特に制限されないが、ポリマー主鎖中に水素原子（炭素－水素結合）を含むポリマーが挙げられ、具体的には、フッ化ビニリデン由来の構成単位を含むことが好ましい。
　ＦＫＭとしては特に制限されないが、具体例としては、フッ化ビニリデン－ヘキサフルオロプロピレン系重合体；フッ化ビニリデン－ヘキサフルオロプロピレン－テトラフルオロエチレン系重合体；フッ化ビニリデン－プロピレン－テトラフルオロエチレン系重合体；エチレン－テトラフルオロエチレン－パーフルオロアルキルビニルエーテル系重合体；フッ化ビニリデン－テトラフルオロエチレン－パーフルオロアルキルビニルエーテル系重合体が挙げられる。
　前記パーフルオロアルキルビニルエーテルの好適例としては、パーフルオロメチルビニルエーテルが挙げられる。
　これらの中でも、耐プラズマ性、耐熱性、耐薬品性等に優れる等の点から、三元系ポリマーであることが好ましく、フッ化ビニリデン－ヘキサフルオロプロピレン－テトラフルオロエチレン系重合体がより好ましい。
　パーオキサイド架橋可能なフルオロエラストマーは、ヨウ素基、臭素基、シアノ基、ペルオキシ基、不飽和基等の官能性基を有することが好ましく、官能性基導入の容易性からヨウ素基、臭素基がより好ましい。
　ヨウ素基および／または臭素基を有するフルオロエラストマーは、例えば、該エラストマーを合成する際に、飽和または不飽和の含ヨウ素および／または含臭素化合物を１種以上用いることで得ることができる。
　前記含ヨウ素および／または含臭素化合物としては、例えば、下記式（１）または（２）で表される化合物が挙げられる。
　下記式（１）で表される化合物を用いることで、ヨウ素基および／または臭素基を側鎖に有するフルオロエラストマーを合成することができ、下記式（２）で表される化合物を用いることで、ヨウ素基および／または臭素基を末端に有するフルオロエラストマーを合成することができる。
　　ＣＹ1 2＝ＣＹ2ＲｆＸ　　（１）
［Ｙ1およびＹ2はそれぞれ独立に、フッ素原子、水素原子またはメチル基であり、Ｒｆは、水素原子の一部または全部がフッ素原子で置換された直鎖状または分岐状の含フッ素アルキレン基、または、該含フッ素アルキレン基の一部にエーテル結合を含む基であり、Ｘはヨウ素原子または臭素原子である。］
　前記式（１）で表される化合物の具体例としては、国際公開第２００９／１１９４０９号に記載の化合物が挙げられる。
　　ＩnＢｒmＲ　　（２）
［Ｒは炭素数１～１２のフルオロ炭化水素基であり、ｎおよびｍはそれぞれ独立に、０～２の整数であり、ｎ＋ｍは１または２である。］
　前記式（２）で表される化合物の具体例としては、特開２００２－９７３２９号公報や特開２００８－５６７３９号公報に記載の化合物が挙げられる。
＜エチレン性不飽和結合含有化合物（Ｂ）＞
　本組成物は、耐プラズマ性に優れ、非粘着であるシール材を容易に得ることができる等の点から、エチレン性不飽和結合含有化合物（Ｂ）を用いることが好ましい。
　化合物（Ｂ）は、エチレン性不飽和結合を有するパーフルオロ骨格の化合物（Ｂ１）、および、エチレン性不飽和結合を有するシロキサン骨格の化合物（Ｂ２）から選ばれる少なくとも１種の化合物である。これらの中でも、より耐プラズマ性に優れるシール材を容易に得ることができる等の点から、前記化合物（Ｂ）は、化合物（Ｂ１）を含むことが好ましい。
　前記エチレン性不飽和結合としては、例えば、ビニル基、メチルビニル基、アリル基、プロペニル基、イソプロペニル基、ブテニル基、ペンテニル基、ヘキセニル基、ヘプテニル基等の炭素数２～８のアルケニル基、ビニルフェニル基、（メタ）アクリロイル基、アリルオキシ基、スチリル基、プロパルギル基が挙げられる。これらの中でも、アルケニル基が好ましく、炭素数２～４のアルケニル基がより好ましく、ビニル基が特に好ましい。
　化合物（Ｂ）は、２種以上のエチレン性不飽和結合を有していてもよい。
　化合物（Ｂ）は、従来公知の方法で合成したものを用いてもよく、市販品を用いてもよい。該市販品としては、例えば、「ＳＩＦＥＬ」（信越化学工業（株）製）が挙げられる。
　なお、化合物（Ｂ）を含む市販品としては、１成分型の市販品と２成分型の市販品等があるが、これらのいずれを使用してもよい。また、化合物（Ｂ）を含む市販品としては、液状、ペースト状、オイル状、ミラブル状等があるが、これらのいずれを使用してもよい。
　化合物（Ｂ）として市販品を用いる場合、該市販品には、分子中に２個以上のヒドロシリル基を有する反応性有機珪素化合物（例：特開２００３－１８３４０２号公報、特開平１１－１１６６８４号公報等に記載の有機ケイ素化合物）、触媒（例：特開２００３－１８３４０２号公報、特開平１１－１１６６８４号公報等に記載の触媒）、充填材（例：シリカ）等の添加剤が含まれている場合があり、前記化合物（Ｂ）としては、これらの添加剤を含むものを用いてもよい。
　本組成物が化合物（Ｂ）を含有する場合、本組成物中の化合物（Ｂ）の含有量は、より短時間で均一なエラストマー組成物とすることができ、耐プラズマ性により優れるシール材を容易に得ることができる等の点から、架橋性フルオロエラストマー（Ａ）１００質量部に対して、好ましくは０．５質量部以上、より好ましくは１質量部以上であり、好ましくは５０質量部以下、より好ましくは２５質量部以下、さらに好ましくは１０質量部以下である。
　本組成物が、化合物（Ｂ）と下記架橋剤とを含む場合、耐プラズマ性により優れるシール材を容易に得ることができる等の点から、本組成物中の架橋剤の含有量に対する化合物（Ｂ）の含有量の質量比（化合物（Ｂ）の含有量／架橋剤の含有量）は、好ましくは１以上、より好ましくは２以上であり、好ましくは２０以下、より好ましくは１０以下である。
［化合物（Ｂ１）］
　前記化合物（Ｂ１）は、架橋性フルオロエラストマー（Ａ）以外の化合物である。
　前記化合物（Ｂ１）としては、例えば、エチレン性不飽和結合を有するパーフルオロポリエーテル構造の化合物、エチレン性不飽和結合を有するパーフルオロアルキレン構造の化合物が挙げられ、これらの中でも、エチレン性不飽和結合を有するパーフルオロポリエーテル構造の化合物（以下「化合物（Ｂ１－１）」ともいう。）が好ましい。
　本組成物が化合物（Ｂ１）を含む場合、本組成物に含まれる化合物（Ｂ１）は、１種でもよく、２種以上でもよい。
・化合物（Ｂ１－１）
　前記化合物（Ｂ１－１）としては、１分子中に２個以上のエチレン性不飽和結合を有するパーフルオロポリエーテルであることが好ましい。
　化合物（Ｂ１－１）の好適例としては、特開２００３－１８３４０２号公報、特開平１１－１１６６８４号公報、特開平１１－１１６６８５号公報、特開２０１５－６７７３７号公報に記載の化合物が挙げられる。
　化合物（Ｂ１－１）としては、例えば、下記式（１）で表される化合物が挙げられる。
　Ｚ1－（Ｘ）p－（Ｒｆ－Ｑ）a－Ｒｆ－（Ｘ）p－Ｚ2　・・・（１）
　Ｘは独立に－ＣＨ2－、－ＣＨ2Ｏ－、－ＣＨ2ＯＣＨ2－、＊－Ｓｉ(Ｒ2)2－Ｐｈ－（Ｐｈ：フェニレン基）、＊－Ｙ－ＮＲ1ＳＯ2－または＊－Ｙ－ＮＲ1－ＣＯ－（但し、Ｙは－ＣＨ2－または＊－Ｓｉ(Ｒ2)2－Ｐｈ－である。なお、前記＊部分が、Ｚ1またはＺ2に結合する。）である。
　Ｒｆは２価パーフルオロポリエーテル基（２価パーフルオロオキシアルキレン基）である。
　ｐは独立に０または１である。ａは０以上の整数であり、好ましくは０～１０の整数、より好ましくは０～６の整数である。
　Ｑは下記式（２）、（３）または（４）で表される基である。
　Ｒ2は、炭素数１～１０、特に炭素数１～８の置換または非置換の１価炭化水素基であり、例えば、メチル基、エチル基、プロピル基、イソプロピル基、ブチル基、イソブチル基、ｔ－ブチル基、ペンチル基、ヘキシル基、オクチル基、デシル基等のアルキル基、シクロペンチル基、シクロヘキシル基、シクロヘプチル基等のシクロアルキル基、ビニル基、アリル基、プロペニル基、イソプロペニル基、ブテニル基、ヘキセニル基等のアルケニル基、フェニル基、トリル基、キシリル基、ナフチル基等のアリール基、ベンジル基、フェニルエチル基、フェニルプロピル基等のアラルキル基、これらの基の水素原子の一部または全部をハロゲン原子等で置換した基（例：クロロメチル基、クロロプロピル基、ブロモエチル基、３，３，３－トリフルオロプロピル基、６，６，６，５，５，４，４，３，３－ノナフルオロヘキシル基等のフッ素置換アルキル基）が挙げられる。
　Ｒ1は、水素原子または前記Ｒ2として例示した基と同様の炭素数１～１０、特に炭素数１～８の置換または非置換の１価炭化水素基であり、水素原子またはＲ2と同様の基を挙げることができ、例えば、メチル基、エチル基、プロピル基、イソプロピル基等のアルキル基、シクロヘキシル基等のシクロアルキル基、ビニル基、アリル基等のアルケニル基、フェニル基、トリル基等のアリール基、これらの基の水素原子の一部をハロゲン原子等で置換した基（例：クロロメチル基、クロロプロピル基、３，３，３－トリフルオロプロピル基、６，６，６，５，５，４，４，３，３－ノナフルオロヘキシル基等のフッ素置換アルキル基）が挙げられる。
　Ｚ1およびＺ2はそれぞれ独立に、エチレン性不飽和結合含有基であり、－Ｓｉ（エチレン性不飽和結合含有基）（Ｒ’）2であってもよい。
　該エチレン性不飽和結合含有基としては、１価のアルケニル基が好ましく、炭素数２～４の１価のアルケニル基がより好ましく、１価のビニル基が特に好ましい。
　Ｒ’は独立に、置換または非置換の１価の炭化水素基であり、具体的には、例えば、メチル基、エチル基、ｎ－プロピル基、ｉ－プロピル基、ｎ－ブチル基、ｉ－ブチル基、ｔ－ブチル基、ペンチル基、ヘキシル基などのアルキル基；フェニル基、トリル基、キシリル基などのアリール基；３－クロロプロピル基、３，３，３－トリフルオロプロピル基などのハロゲン化アルキル基が挙げられ、これらの中でも、炭素数１～５のアルキル基が好ましい。
Figure JPOXMLDOC01-appb-C000001
　式（２）～（４）において、Ｘ、ｐおよびＲ1は前記式（１）中のＸ、ｐおよびＲ1と同義である。Ｒ3およびＲ4はそれぞれ独立に、結合途中に酸素原子、窒素原子、ケイ素原子および硫黄原子から選ばれる１種以上を介在させてもよい置換または非置換の２価炭化水素基であり、式（２）中のＲ3および式（３）中のＲ4はそれぞれ独立に、下記式（５）または（６）で表される基であってもよい。
Figure JPOXMLDOC01-appb-C000002
　式（５）、（６）において、Ｒ5は置換または非置換の１価炭化水素基であり、Ｒ6は炭素原子、酸素原子、窒素原子、ケイ素原子および硫黄原子から選ばれる１種以上を含む基である。
　Ｒ3およびＲ4としては、置換または非置換の２価炭化水素基であれば特に限定されないが、炭素数１～２０、特に２～１２の２価炭化水素基が好適であり、具体的にはメチレン基、エチレン基、プロピレン基、メチルエチレン基、ブチレン基、ヘキサメチレン基等のアルキレン基、シクロヘキシレン基等のシクロアルキレン基、フェニレン基、トリレン基、キシリレン基、ナフチレン基、ビフェニレン基等のアリーレン基、これらの基の水素原子の一部をハロゲン原子等で置換した基、これらの置換または非置換のアルキレン基、アリーレン基の組み合わせが例示される。
　－（Ｘ）p－（Ｒｆ－Ｑ）a－Ｒｆ－（Ｘ）p－は、－（Ｏ－Ｒ7）n－［Ｒ7はパーフルオロアルカンジイル基を示し、ｎは２以上の整数を示す。複数存在するＲ7は互いに同一でも異なっていてもよい。］であることが好ましい。
　Ｒ7で表されるパーフルオロアルカンジイル基としては、例えば、ＣmＦ2mで表される基（ｍは２以上の整数）が挙げられ、直鎖状でも分岐状であってもよい。パーフルオロアルカンジイル基の炭素数（すなわちｍ）は、例えば１～１０であり、好ましくは２～６、より好ましくは２～４、特に好ましくは２～３である。
　ｎは２以上であればよく、例えば１０以上、好ましくは４０以上、より好ましくは７０以上である。また、ｎは、例えば３００以下、好ましくは２００以下、より好ましくは１５０以下である。
　－（Ｏ－Ｒ7）n－は、下記Ｒｆと同様の基であってもよい。
　前記式（１）で表される化合物は、下記式（１－１）で表される化合物であることが好ましい。
　ＣＨ2＝ＣＨ－（Ｘ）p－（Ｒｆ－Ｑ）a－Ｒｆ－（Ｘ）p－ＣＨ＝ＣＨ2　・・・（１－１）
［式（１－１）中の各符号の定義は、式（１）中の各符号の定義と同様ある。］
　また、前記式（１－１）で表される化合物は、ａが０である化合物であることが好ましく、この場合、下記式（１－１－１）で表される。
　ＣＨ2＝ＣＨ－（Ｘ）p－Ｒｆ－（Ｘ）p－ＣＨ＝ＣＨ2　・・・（１－１－１）
［式（１－１－１）中の各符号の定義は、式（１）中の各符号の定義と同様ある。］
　前記Ｒｆの具体例としては、以下の基が挙げられる。
　－［ＣＦ（Ｚ）ＯＣＦ2］p－（ＣＦ2）r－［ＣＦ2ＯＣＦ（Ｚ）］q－
（Ｚは、フッ素原子または－ＣＦ3であり、ｐ、ｑおよびｒは、ｐ≧１、ｑ≧１、２≦ｐ＋ｑ≦２００、好ましくは２≦ｐ＋ｑ≦１１０、０≦ｒ≦６を満たす整数である。）、
　－ＣＦ2ＣＦ2ＯＣＦ2－（ＣＦ（ＣＦ3）ＯＣＦ2）s－（ＣＦ2）r－（ＣＦ2ＯＣＦ（ＣＦ3））t－ＣＦ2ＯＣＦ2ＣＦ2－
（ｒ、ｓおよびｔは、０≦ｒ≦６、ｓ≧０、ｔ≧０、０≦ｓ＋ｔ≦２００、好ましくは２≦ｓ＋ｔ≦１１０を満たす整数である。）、
　－ＣＦ（Ｚ）－（ＯＣＦ（Ｚ）ＣＦ2）u－（ＯＣＦ2）v－ＯＣＦ（Ｚ）－
（Ｚは、フッ素原子または－ＣＦ3であり、ｕおよびｖは、１≦ｕ≦１００、１≦ｖ≦５０を満たす整数である。）、
　－ＣＦ2ＣＦ2－［ＯＣＦ2ＣＦ2ＣＦ2］w－ＯＣＦ2ＣＦ2－
（ｗは、１≦ｗ≦１００を満たす整数である。）
［化合物（Ｂ２）］
　前記化合物（Ｂ２）としては、１分子中に２個以上のエチレン性不飽和結合を有するポリシロキサンであることが好ましく、１分子中に２個以上のエチレン性不飽和結合を有し、かつ、ケイ素原子に有機基が結合したオルガノポリシロキサンであることが好ましい。前記エチレン性不飽和結合の結合位置は特に制限されない。
　本組成物が化合物（Ｂ２）を含む場合、該本組成物に含まれる化合物（Ｂ２）は、１種でもよく、２種以上でもよい。
　ケイ素原子に結合した有機基としては、例えば、前記エチレン性不飽和結合、直鎖状アルキル基、分岐鎖状アルキル基、環状アルキル基、アリール基、アラルキル基、ハロゲン化アルキル基が挙げられる。
　直鎖状アルキル基としては、例えば、メチル基、エチル基、プロピル基、ヘキシル基、オクチル基、デシル基等の炭素数１～２０、好ましくは炭素数１～６の基が挙げられる。
　分岐鎖状アルキル基としては、例えば、イソプロピル基、イソブチル基、ｔ－ブチル基、２－エチルヘキシル基等の炭素数１～２０、好ましくは炭素数１～６の基が挙げられる。
　環状アルキル基としては、例えば、シクロペンチル基、シクロヘキシル基等の炭素数３～２０の基が挙げられる。
　アリール基としては、例えば、フェニル基、トリル基等の炭素数６～２０の基が挙げられる。
　アラルキル基としては、例えば、ベンジル基、２－フェニルエチル基、２－メチル－２－フェニルエチル基等の炭素数７～２０の基が挙げられる。
　ハロゲン化アルキル基としては、例えば、３，３，３－トリフルオロプロピル基、２－（ノナフルオロブチル）エチル基、２－（ヘプタデカフルオロオクチル）エチル基等の炭素数１～２０、好ましくは炭素数１～６の基が挙げられる。
　前記ケイ素原子に結合した有機基としては、直鎖状アルキル基、アルケニル基、アリール基が好ましく、炭素数１～６の直鎖状アルキル基、アルケニル基、アリール基がより好ましく、メチル基、ビニル基、フェニル基が特に好ましい。
　化合物（Ｂ２）の分子構造は特に限定されず、例えば、直鎖状、分岐鎖状、一部分岐を有する直鎖状、樹枝状（デンドリマー状）が挙げられ、好ましくは直鎖状、一部分岐を有する直鎖状である。化合物（Ｂ２）は、これらの分子構造を有する単一の重合体、これらの分子構造を有する共重合体、これらの重合体の２種以上の混合物であってもよい。
　化合物（Ｂ２）としては、例えば、分子鎖両末端ジメチルビニルシロキシ基封鎖ジメチルポリシロキサン、分子鎖両末端メチルフェニルビニルシロキシ基封鎖ジメチルポリシロキサン、分子鎖両末端ジメチルビニルシロキシ基封鎖ジメチルシロキサン・メチルフェニルシロキサン共重合体、分子鎖両末端ジメチルビニルシロキシ基封鎖ジメチルシロキサン・メチルビニルシロキサン共重合体、分子鎖両末端シラノール基封鎖ジメチルシロキサン・メチルビニルシロキサン共重合体、分子鎖両末端シラノール基封鎖ジメチルシロキサン・メチルビニルシロキサン・メチルフェニルシロキサン共重合体、分子鎖両末端トリメチルシロキシ基封鎖ジメチルシロキサン・メチルビニルシロキサン共重合体、分子鎖両末端ジメチルビニルシロキシ基封鎖メチル（３，３，３－トリフルオロプロピル）ポリシロキサン、式：（ＣＨ3）3ＳｉＯ1/2で表されるシロキサン単位と式：（ＣＨ3）2（ＣＨ2＝ＣＨ）ＳｉＯ1/2で表されるシロキサン単位と式：ＣＨ3ＳｉＯ3/2で表されるシロキサン単位と式：（ＣＨ3）2ＳｉＯ2/2で表されるシロキサン単位とからなるオルガノシロキサン共重合体、下記式（７）で表される化合物が挙げられる。
Figure JPOXMLDOC01-appb-C000003
 ［式（７）中、Ｒ1はそれぞれ独立に、非置換または置換の１価炭化水素基であり、Ｒ2は独立に、アルキル基、アルコキシアルキル基、アルケニル基またはアシル基であり、ｂは２～１００の整数であり、ａは１～３の整数である。但し、式（７）中のＲ1およびＲ2のうち少なくとも２つは、前記エチレン性不飽和結合を含む。］
　式（７）中、Ｒ1はそれぞれ独立に、非置換または置換の、好ましくは炭素数１～１０の１価炭化水素基であり、その例としては、前記ケイ素原子に結合した有機基として例示した基と同様の基が挙げられる。これらの中では、炭素数１～６の１価炭化水素基が好ましく、アルケニル基、アリール基、炭素数１～３のアルキル基がより好ましい。
　式（７）中のＲ2におけるアルキル基およびアルケニル基としては、例えば、前記ケイ素原子に結合した有機基として例示した基と同様の直鎖状アルキル基、分岐鎖状アルキル基、環状アルキル基、アルケニル基が挙げられる。
　式（７）中のＲ2におけるアルコキシアルキル基としては、例えば、メトキシエチル基、メトキシプロピル基等の炭素数２～１０の基が挙げられる。
　式（７）中のＲ2におけるアシル基としては、例えば、アセチル基、オクタノイル基等の炭素数２～１０の基が挙げられる。
　式（７）中のｂは、好ましくは１０～５０の整数であり、ａは、好ましくは３である。
＜架橋剤＞
　架橋性フルオロエラストマー（Ａ）は、架橋剤を用いなくても架橋させることはできるが、十分に架橋し、硬度、引張強さ、切断時伸び、および、１００％Ｍｏにバランスよく優れるシール材を容易に得ることができる等の点から、本組成物は、用いる架橋性フルオロエラストマー（Ａ）の種類に応じた架橋剤を含むことが好ましい。
　本組成物が架橋剤を含む場合、該本組成物に含まれる架橋剤は、１種でもよく、２種以上でもよい。
　前記架橋剤としては、従来より公知の架橋剤を特に制限なく使用することができ、用いる架橋性フルオロエラストマー（Ａ）の種類に応じて適宜選択すればよいが、例えば、ＦＫＭを用いる場合、パーオキサイド系架橋剤、ポリアミン系架橋剤、ポリオール系架橋剤、トリアジン系架橋剤等が挙げられる。
　これらの中でも、プラズマ雰囲気下等において、パーティクルの発生源となる、酸化マグネシウム、水酸化カルシウムなどの受酸剤を本組成物中に配合する必要がなく、得られたシール材を使用中に、パーティクルを発生させる恐れがない等の点でパーオキサイド系架橋剤が好ましい。
　パーオキサイド系架橋剤としては、例えば、２，５－ジメチル－２，５－ジ（ｔ－ブチルパーオキシ）ヘキサン、ジクミルパーオキサイド、２，４－ジクロロベンゾイルパーオキサイド、ジ－ｔ－ブチルパーオキサイド、ｔ－ブチルジクミルパーオキサイド、ベンゾイルパーオキサイド、２，５－ジメチル－２，５－（ｔ－ブチルパーオキシ）ヘキシン－３、２，５－ジメチル－２，５－ジ（ベンゾイルパーオキシ）ヘキサン、α，α’－ビス（ｔ－ブチルパーオキシ－ｍ－イソプロピル）ベンゼン、ｔ－ブチルパーオキシイソプロピルカーボネート、ジ－（４－ｔ－ブチルシクロヘキシル）パーオキシジカーボネート、ｐ－クロロベンゾイルパーオキサイド、ｔ－ブチルパーオキシ－２－エチルヘキサノエート、ｔ－ブチルパーオキシベンゾエート、１，１－ビス（ｔ－ブチルパーオキシ）－３，５，５－トリメチルシクロヘキサン、２，５－ジメチルヘキサン－２，５－ジヒドロパーオキサイド、α，α－ビス（ｔ－ブチルパーオキシ）－ｐ－ジイソプロピルベンゼン、ｔ－ブチルパーオキシベンゼン、ｔ－ブチルパーオキシマレイン酸が挙げられる。
　これらの中でも、２，５－ジメチル－２，５－ジ（ｔ－ブチルパーオキシ）ヘキサン、２，４－ジクロロベンゾイルパーオキサイド、ジクミルパーオキサイド、ベンゾイルパーオキサイド、α，α’－ビス（ｔ－ブチルペルオキシ－ｍ－イソプロピル）ベンゼンが好ましく、２，５－ジメチル－２，５－ジ（ｔ－ブチルパーオキシ）ヘキサンがより好ましい。
　本組成物が架橋剤を含有する場合、本組成物中の架橋剤の含有量は、架橋反応が十分に進行し、硬度、引張強さ、切断時伸び、および、１００％Ｍｏにバランスよく優れるシール材を容易に得ることができる等の点から、架橋性フルオロエラストマー（Ａ）１００質量部に対して、好ましくは０．２～４質量部、より好ましくは０．２～２．５質量部である。
＜架橋助剤＞
　本組成物では、前記架橋剤を単独で用いてもよいが、前記架橋剤を用いる場合、架橋助剤を用いることが好ましい。該架橋助剤としては、架橋剤の種類に応じて公知の架橋助剤を選択すればよい。
　本組成物が架橋助剤を含む場合、該本組成物に含まれる架橋助剤は、１種でもよく、２種以上でもよい。
　例えば、パーオキサイド系架橋剤を用いる場合に使用される架橋助剤の例としては、トリアリルイソシアヌレート；トリアリルシアヌレート；トリメタリルイソシアヌレート；トリアリルホルマール；トリアリルトリメリテート；Ｎ，Ｎ'－ｍ－フェニレンビスマレイミド；ジプロパギルテレフタレート；ジアリルフタレート；テトラアリルテレフタルアミド；エチレングリコール・ジ（メタ）アクリレート、トリメチロールプロパントリ（メタ）アクリレートなどの多官能性（メタ）アクリレート；等のラジカルによる共架橋が可能な化合物（多官能性モノマー）：高級カルボン酸の金属塩：多価アルコール（メタ）アクリレート：（メタ）アクリル酸金属塩が挙げられる。
　これらの中では、反応性に優れ、耐熱性に優れ、高硬度で高モジュラスのシール材を容易に得ることができる等の点から、トリアリルイソシアヌレートが好ましい。
　本組成物が架橋助剤を含有する場合、本組成物中の架橋助剤の含有量は、架橋反応が十分に進行し、硬度、引張強さ、切断時伸び、および、１００％Ｍｏにバランスよく優れるシール材を容易に得ることができる等の点から、架橋性フルオロエラストマー（Ａ）１００質量部に対して、好ましくは１質量部以上、より好ましくは２質量部以上、さらに好ましくは４質量部以上であり、好ましくは１０質量部以下、より好ましくは７質量部以下、さらに好ましくは６質量部以下である。
　特に、プラズマ雰囲気下等において、シール材に生じ得るクラックを抑制するために、放射線架橋したシール材（放射線処理物）が好ましいが、この場合、下記のような充填材を用いなくても、より高硬度で高モジュラスのシール材を容易に得ることができる等の点から、本組成物中の架橋助剤の含有量は、架橋性フルオロエラストマー（Ａ）１００質量部に対して、好ましくは２質量部以上、さらに好ましくは４質量部以上であり、好ましくは７質量部以下、さらに好ましくは６質量部以下である。
　本組成物中の架橋剤の含有量に対する架橋助剤の含有量の質量比（架橋助剤の含有量／架橋剤の含有量）は、架橋剤を過不足なく反応させ、所望の物性を示すシール材を容易に得ることができる、特に、下記のような充填材を用いなくても、より高硬度で高モジュラスのシール材を容易に得ることができる等の点から、好ましくは４以上、より好ましくは６以上であり、好ましくは３０以下、より好ましくは２０以下である。
＜その他の成分＞
　本組成物は、前記成分の他に、本発明の効果を損なわない範囲で、必要に応じて、シール材に配合されてきた従来公知のその他の成分を含んでいてもよい。該その他の成分としては、例えば、分子中に２個以上のヒドロシリル基を有する反応性有機珪素化合物；触媒；酸化マグネシウム、水酸化カルシウム等の受酸剤；アントラキノン系顔料、ペリレン系顔料、ジオキサジン系顔料等の有機顔料；可塑剤；加工助剤；加硫促進剤；老化防止剤；酸化防止剤；無機充填材；有機充填材が挙げられる。
　前記その他の成分はそれぞれ、１種のみを用いてもよいし、２種以上を用いてもよい。
　前記反応性有機珪素化合物としては、好適には、特開２００３－１８３４０２号公報、特開平１１－１１６６８４号公報等に記載の有機ケイ素化合物と同様の化合物等が挙げられる。
　前記触媒としては、好適には、特開２００３－１８３４０２号公報、特開平１１－１１６６８４号公報等に記載の触媒と同様の触媒等が挙げられる。
　前記有機顔料としては、好適には、国際公開第２０１６／０４３１００号、特許第４７２０５０１号公報、国際公開第２００４／０９４５２７号等に記載の有機顔料と同様の有機顔料等が挙げられる。
　前記無機充填材および有機充填材（以下これらを総称して、単に「充填材」ともいう。）は、前記化合物（Ｂ）、架橋剤および架橋助剤以外の粒子状（粉末状）の成分である。
　前記無機充填材としては、例えば、カーボンブラック、シリカ、硫酸バリウム、酸化チタン、酸化アルミニウムが挙げられる。
　前記有機充填材としては、例えば、ＰＴＦＥ、ＰＦＡ、ＦＥＰ、ＥＴＦＥ、ＰＶＤＦ等のフッ素樹脂、ポリエチレン樹脂、ポリイミド樹脂、シリコーン樹脂およびメラミン樹脂が挙げられる。
　本組成物を、プラズマ雰囲気下等の、パーティクルの発生が問題となるようなシール材の製造に用いる場合には、前記充填材の含有量は、架橋性フルオロエラストマー（Ａ）１００質量部に対し、好ましくは５質量部以下、より好ましくは３質量部以下、最も好ましくは０質量部である。
＜本組成物の製造方法＞
　本組成物は、架橋性フルオロエラストマー（Ａ１）と架橋性フルオロエラストマー（Ａ２）とを混合（混練）することで製造することができ、好ましくは、これらのエラストマー（Ａ１）および（Ａ２）と、化合物（Ｂ）と、架橋剤と、架橋助剤と、必要により前記その他の成分とを混合（混練）することで製造することができる。
　エラストマー（Ａ１）および（Ａ２）と、化合物（Ｂ）、架橋剤、架橋助剤、その他の成分等の添加剤との混合順は特に制限されず、任意の順番で順次混合（混練）してもよく、これらを一括混合（混練）してもよいが、各成分が均一になるように、順次混合（混練）することが好ましい。
　前記混合（混練）の際には、従来公知の混合（混練）機を用いることができ、例えば、オープンロール、バンバリーミキサー、二軸ロール、ニーダーが挙げられる。
　また、前記混合（混練）の際には、混合（混練）機に応じて、必要により、加熱下または冷却下で混合（混練）してもよい。
≪シール材≫
　本発明の一実施形態に係るシール材（以下「本シール材」ともいう。）は、前記本組成物から得られたシール材である。
　本シール材は、前記本組成物から得られるため、硬度、引張強さ、切断時伸び、および、１００％Ｍｏにバランスよく優れ、さらに、耐プラズマ性（耐ラジカル性）、耐クラック性、圧縮永久歪等に優れる。
　本シール材は、例えば、種々の部材のガスケットやパッキンとして使用することができ、特に前記効果を奏するため、半導体製造装置用や、プラズマ処理装置用、特に、プラズマ処理チャンバーユニットの開口部に使用されるゲートバルブをはじめとした駆動部用として好適に使用することができる。
　本シール材の形状等は、用いる用途に応じて適宜選択すればよい。
　本シール材は、前記充填材を含まないシール材でありながら、以下の物性を有するシール材とすることができる。
　本シール材のＪＩＳ　Ｋ　６２５３：２０１２に基づいて測定されたショアＡ硬度（タイプＡデュロメータ硬度）は、好ましくは６０以上である。
　本シール材のＪＩＳ　Ｋ　６２５１：２０１７に基づいて測定された引張強さは、好ましくは１０ＭＰａ以上である。
　本シール材のＪＩＳ　Ｋ　６２５１：２０１７に基づいて測定された切断時伸びは、好ましくは１３０％以上である。
　本シール材のＪＩＳ　Ｋ　６２５１：２０１７に基づいて測定された１００％モジュラスは、好ましくは３．５ＭＰａ以上である。
＜本シール材の製造方法＞
　本シール材は、具体的には、本組成物を成形することで製造することができるが、耐プラズマ性（耐ラジカル性）、耐クラック性、非粘着性等により優れるシール材を容易に得ることができる等の点から、本組成物を架橋処理する工程（架橋工程）を含む方法で得られた架橋処理物であることが好ましく、さらに、硬度、引張強さ、切断時伸び、および、１００％Ｍｏにバランスよく優れるシール材を容易に得ることができる等の点から、本組成物に放射線を照射する工程（放射線照射工程）を含む方法で得られた放射線処理物であることがより好ましい。
　本組成物からシール材を形成する際には、成形作業の効率を向上させるためや、不良率を低減するためなどの点から、分出し工程を行うことが好ましい。この分出し工程は、通常、ロールなどを使用して行われ、通常、本組成物をシート状に予備的に成形する工程でもある。
　前記分出し工程で得られたシートは、前記架橋工程や放射線照射工程の前に、所望のシール材の形状に予備成形することが好ましい。
　この予備成形は、分出し工程で得られたシートから直接所望のシール材形状を形成してもよく、分出し工程で得られたシートを、裁断や押出成形等により、ロープ状（リボン状、うどん状等も同義である。）等の形状にし、得られたロープ状物を所望のシール材形状にしてもよい。
　本シール材を製造する際には、前記放射線照射工程の前に、架橋工程を含むことが好ましく、該架橋工程は、一次架橋工程および二次架橋工程を含むことがより好ましい。
　前記架橋工程は、前記予備成形で得られた所望のシール材形状物を用いて行うことが好ましい。
　前記一次架橋工程としては、前記予備成形で得られた所望のシール材形状物を加熱加圧する工程であることが好ましく、具体的には、例えば予備成形された材料を金型に投入し、加熱プレス機等によって２～１５ＭＰａ程度の加圧下、例えば１５０～２００℃の温度で、例えば５～２０分間程度架橋する工程が挙げられる。
　前記二次架橋工程としては、前記一次架橋工程で得られた成形体を加熱する工程であることが好ましく、具体的には、常圧～減圧下で各種オーブン、好ましくは真空オーブンを用いて、例えば１５０～３００℃の温度で、１～２４時間、より好ましくは３～２４時間程度加熱する工程が挙げられる。
　この二次架橋工程により、架橋を促進させたり、前記一次架橋工程後に未反応成分が残存していたとしても、該未反応成分を分解揮散させることができ、より放出ガス発生の少ないシール材を得ることができる。
　前記放射線照射工程において照射する放射線としては、架橋性フルオロエラストマー（Ａ）を架橋できるものであれば特に制限されないが、例えば、Ｘ線、ガンマ線、電子線、陽子線、中性子線、重粒子線、アルファー線、ベータ線が挙げられ、これらの中でも、ガンマ線、電子線が好ましい。
　照射する放射線は、１種単独でもよく、２種以上でもよい。
　放射線を照射する際には、吸収線量が、好ましくは１～１２０ｋＧｙ、より好ましくは２０～１００ｋＧｙとなるように放射線を照射することが望ましい。このような量で放射線を照射すると、パーティクルや放出ガスとなり得る未反応成分を低減することができ、架橋性フルオロエラストマー（Ａ）を過度に低分子量化せず、耐プラズマ性、耐クラック性等に優れるシール材を容易に得ることができる。
　なお、前記放射線照射工程は、条件を変更して、２段階以上に分けて行ってもよい。
　放射線を照射する際には、空気中で照射してもよいが、放射線照射時に酸素が存在すると、架橋反応が阻害され、シール材の機械的強度の低下や、シール材の表面にベタツキが生じる恐れがある。このため、前記放射線照射工程は、窒素やアルゴンなどの不活性ガスの雰囲気下で行なうことが好ましい。
　次に、本発明について実施例を示してさらに詳細に説明するが、本発明はこれらによって限定されるものではない。
＜架橋性フルオロエラストマー＞
　下記実施例および比較例で用いた架橋性フルオロエラストマーは、以下の通りである。
・架橋性フルオロエラストマー（Ａ１－ａ）：テクノフロンＰ９５９（ソルベイ社製、フッ素含有量：７０質量％）
・架橋性フルオロエラストマー（Ａ１－ｂ）：テクノフロンＰ４５９（ソルベイ社製、フッ素含有量：７０質量％）
・架橋性フルオロエラストマー（Ａ１－ｃ）：ダイエルＧ９１２（ダイキン工業（株）製、フッ素含有量：７１質量％）
・架橋性フルオロエラストマー（Ａ１－ｄ）：ダイエルＧ９０２（ダイキン工業（株）製、フッ素含有量：７１質量％）
・架橋性フルオロエラストマー（Ａ２－ａ）：テクノフロンＰ７５７（ソルベイ社製、フッ素含有量：６７質量％）
・架橋性フルオロエラストマー（Ａ２－ｂ）：テクノフロンＰ４５７（ソルベイ社製、フッ素含有量：６７質量％）
・架橋性フルオロエラストマー（他）：テクノフロンＰＬ８５５（ソルベイ社製、フッ素含有量：６４質量％）
［実施例１］
　架橋性フルオロエラストマー（Ａ１－ａ）８０質量部および架橋性フルオロエラストマー（Ａ２－ａ）２０質量部、ＳＩＦＥＬ　８０７０Ａ（信越化学工業（株）製）１．０質量部、ＳＩＦＥＬ　８０７０Ｂ（信越化学工業（株）製）１．０質量部、ＴＡＩＣ（三菱ケミカル（株）製、トリアリルイソシアヌレート）６．０質量部、および、パーヘキサ２５Ｂ（日油（株）製）０．５質量部を順次ニーダーに入れ、電流値が安定するまで混練することで塊状のエラストマー組成物を得た。
　なお、ＳＩＦＥＬ　８０７０ＡおよびＳＩＦＥＬ　８０７０Ｂの少なくとも一方には、エチレン性不飽和結合を有するパーフルオロ骨格の化合物が含まれている。
　ニーダーに最初の成分を添加してから、最終の成分を添加した後、電流値が安定するまでの総時間をニーダー練り時間とした。結果を表１に示す。
　一般的に、ニーダーを用いて混練りを行う場合、添加した各成分が均一に混練されると電流値が安定するため、混練りの完了の目安として電流値が安定した時点をもって、均一な組成物が得られたと判断することが多い。
　得られた塊状のエラストマー組成物を、ロール（ロール間隔：８ｍｍ、温度：５０℃）を用いて、分出し工程（シート化工程）を行った。
　この際に、塊状のエラストマー組成物からシートを形成できた場合を、分出し性「ＯＫ」とし、ロール間にエラストマー組成物が噛み込まなかったり、ロールへの密着性が悪く、良好な分出しシートが得られなかった場合を、分出し性「ＮＧ」として、分出し性を評価した。結果を表１に示す。
　前記分出し工程で得られたシートを、圧縮真空プレス機を用い、５ＭＰａの加圧下、１７０℃で１０分間のプレス成形し（一次架橋）、次いで、プレス成形後のシートを、真空オーブン（真空度：５０Ｐａ）での減圧下、２００℃で１６時間加熱した（二次架橋）。その後、二次架橋されたシートに、吸収線量が８０ｋＧｙとなるように放射線を照射することで成形体を得た。
　得られた成形体について、下記常態物性を測定した。結果を表１に示す。
＜常態物性＞
　常態物性として、ＪＩＳ　Ｋ　６２５３：２０１２に準拠して、ショアＡ硬度を測定し、かつ、ＪＩＳ　Ｋ　６２５１：２０１７に準拠して、引張強さ、切断時伸び、１００％伸びにおける引張応力（１００％Ｍｏ）を測定した。
［実施例２～６および比較例１～２］
　実施例１において、表１に示す架橋性フルオロエラストマーを、表１に示す量で用いた以外は実施例１と同様にして、各種評価を行った。結果を表１に示す。
Figure JPOXMLDOC01-appb-T000004
　実施例１～６では、均一なエラストマー組成物を製造するのにかかる時間が短く、実施例１～６で得られたエラストマー組成物は、分出し性（シート成形性）に優れることが分かった。
　なお、比較例１および２では、均一なエラストマー組成物を製造するのに長い時間を要し、また、比較例１および２で得られたエラストマー組成物は分出し性が悪く、具体的には、ロール間にエラストマー組成物が噛み込まなかったり、ロールへうまく巻き付かなかったりして、良好なシートを形成することができなかった。
［実施例７～９および比較例３～５］
　実施例１において、表２に示す架橋性フルオロエラストマーを、表２に示す量で用いた以外は実施例１と同様にして、塊状のエラストマー組成物を得た。
　得られた塊状のエラストマー組成物を金型に充填し、圧縮真空プレス機を用い、５ＭＰａの加圧下、１７０℃で１０分間のプレス成形し（一次架橋）、次いで、プレス成形後のシートを、真空オーブン（真空度：５０Ｐａ）での減圧下、２００℃で１６時間加熱した（二次架橋）。その後、二次架橋されたシートに、吸収線量が８０ｋＧｙとなるように放射線を照射することで成形体を得た。
　得られた成形体について、前記常態物性および下記耐プラズマ性を測定した。結果を表２に示す。
＜耐プラズマ性＞
　得られた成形体について、耐プラズマ性（質量減少率）を測定した。具体的には以下の通り測定した。
　電極径；φ３００ｍｍ、電極間距離；５０ｍｍの平板プラズマ処理装置を用いて、ＲＦ；１０００Ｗ、Ｏ2ガスとＣＦ4ガスの流量比（Ｏ2：ＣＦ4）；１９０：１０、ガス流量２００ｓｃｃｍ、真空度１ｔｏｒｒの条件下で、得られた成形体にプラズマを３時間照射した。
　なお、得られた成形体は、プラズマ電極より６ｃｍ離れた場所に設置した。次いで、試験前後の成形体の質量を測定して、下記式により、質量減少率（％）を求めることで、耐プラズマ性を評価した。質量減少率が小さいほど耐プラズマ性に優れるといえる。
　質量減少率（％）＝［（試験前の成形体の質量－試験後の成形体の質量）／試験前の成形体の質量］×１００
Figure JPOXMLDOC01-appb-T000005
［実施例１０］
　架橋性フルオロエラストマー（Ａ１－ｃ）７０質量部および架橋性フルオロエラストマー（Ａ２－ａ）３０質量部、ＳＩＦＥＬ　３５９０－Ｎ（信越化学工業（株）製、エチレン性不飽和結合を有するパーフルオロ骨格の化合物含有、一液型液状タイプ）２質量部、ＴＡＩＣ　６質量部、および、パーヘキサ２５Ｂ　０．５質量部を順次ニーダーに入れ、電流値が安定するまで混練することで塊状のエラストマー組成物を得た。
　得られた塊状のエラストマー組成物を用いて、実施例７と同様にして成形体を得た。
　得られた成形体について、前記常態物性および耐プラズマ性を測定した。結果を表３に示す。
［実施例１１］
　架橋性フルオロエラストマー（Ａ１－ｃ）７０質量部および架橋性フルオロエラストマー（Ａ２－ａ）３０質量部、ＫＥ－１８３０（信越化学工業（株）製、エチレン性不飽和結合を有するシロキサン骨格の化合物含有、一液型液状タイプ）２質量部、ＴＡＩＣ　６質量部、および、パーヘキサ２５Ｂ　０．５質量部を順次ニーダーに入れ、電流値が安定するまで混練することで塊状のエラストマー組成物を得た。
　得られた塊状のエラストマー組成物を用いて、実施例７と同様にして成形体を得た。
　得られた成形体について、前記常態物性および耐プラズマ性を測定した。結果を表３に示す。
Figure JPOXMLDOC01-appb-T000006
　実施例１～１１で得られた成形体（シート）は、ショアＡ硬度、引張強さ、切断時伸び、および、１００％Ｍｏにバランスよく優れることが分かった。

Claims (7)

  1. 　フッ素含有量が６９質量％以上であるパーフルオロエラストマー以外の架橋性フルオロエラストマー（Ａ１）と、
    　フッ素含有量が６６～６８質量％の範囲にあるパーフルオロエラストマー以外の架橋性フルオロエラストマー（Ａ２）と
    を含むエラストマー組成物。
  2. 　前記フルオロエラストマー（Ａ１）および（Ａ２）がパーオキサイド架橋可能なフルオロエラストマーである、請求項１に記載のエラストマー組成物。
  3. 　エチレン性不飽和結合を有するパーフルオロ骨格の化合物、および、エチレン性不飽和結合を有するシロキサン骨格の化合物から選ばれる少なくとも１種のエチレン性不飽和結合含有化合物（Ｂ）を含む、請求項１または２に記載のエラストマー組成物。
  4. 　架橋剤を含む、請求項１～３のいずれか１項に記載のエラストマー組成物。
  5. 　充填材の含有量が、前記フルオロエラストマー（Ａ１）および（Ａ２）の合計１００質量部に対し、５質量部以下である、請求項１～４のいずれか１項に記載のエラストマー組成物。
  6. 　請求項１～５のいずれか１項に記載のエラストマー組成物から得られたシール材。
  7. 　請求項１～５のいずれか１項に記載のエラストマー組成物に放射線を照射する工程を含む、シール材の製造方法。
PCT/JP2021/033156 2020-09-28 2021-09-09 エラストマー組成物、シール材およびシール材の製造方法 Ceased WO2022065053A1 (ja)