WO2019027164A1 - 안료를 포함하는 화장료 조성물 및 그 제조방법 - Google Patents

안료를 포함하는 화장료 조성물 및 그 제조방법 Download PDF

Info

Publication number
WO2019027164A1
WO2019027164A1 PCT/KR2018/008215 KR2018008215W WO2019027164A1 WO 2019027164 A1 WO2019027164 A1 WO 2019027164A1 KR 2018008215 W KR2018008215 W KR 2018008215W WO 2019027164 A1 WO2019027164 A1 WO 2019027164A1
Authority
WO
WIPO (PCT)
Prior art keywords
pigment
cosmetic composition
coating layer
oil
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/KR2018/008215
Other languages
English (en)
French (fr)
Inventor
정하진
김경남
김준일
하주희
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Amorepacific Corp
Original Assignee
Amorepacific Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Amorepacific Corp filed Critical Amorepacific Corp
Priority to CN201880064138.4A priority Critical patent/CN111163748B/zh
Publication of WO2019027164A1 publication Critical patent/WO2019027164A1/ko
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

본 발명은 안료를 포함하는 화장료 조성물 및 그 제조방법에 관한 것으로서, 유상 및 수상을 포함하는 코팅층으로 코팅된 안료의 입도 분포를 균일화함으로써 화장료 조성물의 사용감과 기능성이 향상된, 안료를 포함하는 화장료 조성물 및 그 제조방법에 관한 것이다.

Description

안료를 포함하는 화장료 조성물 및 그 제조방법
본 출원은 2017년 7월 31일자 한국 특허출원 제10-2017-0097300호에 기초한 우선권의 이익을 주장하며, 해당 한국 특허 출원의 문헌에 개시된 모든 내용을 본 명세서의 일부로서 포함한다.
본 발명은 안료를 포함하는 화장료 조성물로서, 안료의 입도 분포 균일화를 통해 사용감과 기능성이 향상된 화장료 조성물 및 그 제조방법에 관한 것이다.
일반적으로 메이크업 화장료는 안료를 사용하여 피부의 결점을 은폐하고 아름다운 색상을 부여하며 자외선으로부터 피부보호 등을 위한 목적으로 사용되고 나아가 피부미화와 피부보호 기능에 의해 심리적으로 안정감을 주는 부수적인 목적으로 사용되고 있다.
상기 메이크업 화장료는 유화타입, 분산형타입, 파우더타입의 제형 형태에 따라 약간의 차이점이 있으나 색상부여와 피부결점을 커버하기 위한 대표적인 백색안료로서 이산화티탄(TiO2)을 가장 많이 사용하고 있다. 하지만 표면 개질되지 않은 이산화티탄의 경우 피부결점을 은폐시키는 기능이 우수할수록 재응집 현상이 발생하여 화장 후 뭉치는 현상을 야기하게 되고, 특히 상기 그 구조가 사면체이어서 피부에 도포시 피부를 손상시키며 전연성이 매우 나빠 사용성을 저하시키는 요인이 된다.
이러한 단점을 극복하기 위하여 안료의 표면을 다양한 기재로 코팅 또는 복합화하여 사용되는 방법이 사용되고 있다. 종래에는 실리콘, 불소, 아미노산, 키토산, 금속염 등으로 표면처리를 실시하여 밀착성과 지속성 등의 기능을 개선시킬 수 있다. 그러나, 제형 내에서의 퍼짐성과 재응집 방지성 및 사용시나 시간 경과 후 화장붕괴를 방지하는데는 아직도 만족스럽지 못한 실정이다.
예를 들어, 일본 등록특허 제5667330호는 다층 피복된 형태의 안료를 제시하며, 피복층은 고굴절성 피막(TiO2, 10-100nm 두께), 무색피막(20-100nm 두께) 및 고굴절성 피막(TiO2, 10-100nm 두께) 중 적어도 하나를 포함한다고 개시되어 있으나, 이와 같이 피막을 포함하는 안료의 입도 분포를 균일하게 하는 방법은 제시하지 못하여, 화장품에 적용시 사용감과 기능성을 확보하는데 어려움이 있을 수 있다.
또한, 미국공개특허 제2004-0258640호는 피부 결점 커버를 위한 화장품에 사용될 수 있는 interference pigment에 관한 것으로, 다층 피복된 형태의 안료가 개시되어 있으나 안료의 입도를 개선시킴으로서 화장품에 적용시 사용감과 기능성을 확보할 수 있는 기술에 대해서는 언급되어 있지 않다.
따라서, 안료를 보호할 수 있는 코팅층을 포함하면서도 입도 분포를 개선하여 피부에 적용시 사용감과 기능성을 동시에 향상시킬 수 있는 화장료 조성물 제조 기술 개발이 시급한 실정이다.
[선행기술문헌]
[특허문헌]
(특허문헌 1) 일본 등록특허 제5667330호, “은색 광택 안료”
(특허문헌 2) 미국공개특허 제2004-0258640호, “INTERFERENCE PIGMENT AND COMPOSITION INCLUDING SAME”
이에 본 발명자들은 상기 문제점을 해결하기 위해 다각적으로 연구를 수행한 결과, 유상층 및 수상층을 포함하는 이중 코팅층으로 코팅된 안료를 회전하는 분산기기를 이용하여 분산시킴으로써 입도 분포가 균일한 화장료 조성물을 제조할 수 있으며, 이렇게 제조된 화장료 조성물은 피부 도포시 얇게 밀착되어 피부에 윤기와 촉촉함을 부여하는 동시에 커버력과 시간 경과 후 들뜸과 뭉침이 방지되는 것을 확인하였다.
따라서, 본 발명의 목적은 안정성이 향상된 안료를 포함하는 화장료 조성물을 제공하는데 있다.
본 발명의 다른 목적은 입도 분포가 균일한 안료를 포함하는 화장료 조성물의 제조방법을 제공하는데 있다.
상기 목적을 달성하기 위해, 본 발명은 유상과 수상을 포함하는 코팅층으로 코팅된 안료 입자를 포함하는 화장료 조성물을 제공한다.
상기 안료의 입도는 0.1 ㎛ 내지 1 ㎛일 수 있다.
상기 안료는 산화티탄(titanium dioxide, TiO2), 마이크로 산화티탄(Micro TiO2), 산화아연(zinc oxide, ZnO), 마이크로 산화아연(Micro ZnO), 산화철, 산화알루미늄(alumina, Al2O3), 황산바륨(barium sulfate, BaSO3), 이산화규소(silica, SiO2), 탈크, 카올린, 세리사이트(sericite) 및 마이카로 이루어진 군에서 선택되는 1종 이상의 무기 안료일 수 있다.
상기 유상은 디메치콘류, 메치콘류, 하이드로겐 디메치콘류, 카플릴릭 실란류 및 불소계 실리콘류로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있다.
또한, 상기 수상은 레시틴류 및 실리카류로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있다.
또한, 상기 코팅층은 유상과 수상의 혼합물을 포함하는 단일 코팅층일 수 있다.
또한, 상기 코팅층은 유상층 및 수상층을 포함하는 이중 코팅층일 수 있다.
또한, 상기 화장료 조성물은 수분산, 유분산, W/O(water in oil) 또는 O/W(oil in water)의 형태로 제형화 될 수 있다.
또한, 상기 화장료 조성물은 리퀴드, 크림 또는 케익 형태의 파운데이션, 메이크업베이스 화장료 또는 자외선 차단용 화장료의 형태로 제형화될 수 있다.
본 발명은 또한, 안료와 유화제를 수상에 분산시키되, 회전하는 분산기기를 이용하여 분산시켜, 상기 안료의 표면에 유상과 수상을 포함하는 코팅층을 형성하는 단계를 포함하는 화장료 조성물의 제조방법을 제공한다.
상기 분산기기의 회전속도는 5 내지 50 m/s일 수 있다.
본 발명에 따른 화장료 조성물에 의하면, 상기 화장료 조성물 내에 포함된 안료 입자의 표면이 유상층 및 수상층을 포함하는 이중 코팅층으로 코팅되어 있어 피부에 도포시 얇고 균일한 화장막을 형성할 수 있고, 윤기와 보습감을 부여할 수 있다.
또한, 본 발명에 따른 화장료 조성물은 제조 공정 중 박막선회형 고속믹서를 이용함으로써 안료의 입도 분포를 균일화하면서도 점도를 적정 수준으로 유지할 수 있다.
이와 같이, 입도 분포가 균일하면서도 적정 수준의 점도를 가짐으로 인하여, 본 발명의 화장료 조성물을 쿠션, 팩트, 파운데이션과 같은 피부 베이스 화장품에 적용할 경우 커버력이 향상되고, 시간 경과 후 들뜸이나 뭉침과 같은 문제점을 개선시킬 수 있다.
도 1a 및 1b는 본 발명에 따른 안료를 포함하는 화장료 조성물의 모식도이다.
도 2는 본 발명의 화장료 조성물의 제조방법에 따라 박막선회형 고속믹서를 이용하여 안료 입자를 분산시키는 공정의 모식도를 나타낸 것이다.
도 3a 및 3b는 각각 실시예 1 및 비교예 1에서 각각 제조된 화장료 조성물의 현미경 사진이다.
도 4는 실시예 1,2 및 비교예 1,2의 화장료 조성물에 대한 점도 경시율 측정 결과를 나타낸 그래프이다.
도 5는 실시예 1,2 및 비교예 1,2에 따른 리퀴드 파운데이션 제형의 화장료 조성물에 대해 관능평가를 실시한 결과를 나타낸 그래프이다.
이하, 본 발명에 대한 이해를 돕기 위하여 본 발명을 더욱 상세하게 설명한다.
본 명세서 및 청구범위에서 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니 되며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.
안료를 포함하는 화장료 조성물
본 발명은 안료를 포함하는 화장료 조성물에 관한 것으로, 화장료 조성물에 포함된 안료 입자의 입도 분포가 균일한 화장료 조성물에 관한 것이다.
본 발명에 따른 화장료 조성물은 특히, 피부의 베이스 화장을 위한 화장료 조성물로 사용되어, 피부에 도포시 얇은 화장막을 형성할 수 있고, 피부에 윤기와 촉촉함을 부여할 뿐만 아니라, 커버력이 우수하며, 시간 경과 후 들뜸이나 뭉침을 방지할 수 있다.
본 발명에 따른 화장료 조성물은 유상과 수상을 포함하는 코팅층으로 코팅된 안료 입자를 포함할 수 있다.
본 발명에 따른 화장료 조성물에 포함된 안료는 입도가 0.1 ㎛ 내지 1 ㎛ 이고, 상기 화장료 조성물의 입도가 0.1 ㎛ 미만이면 입도분석기기의 신뢰구간에서 벗어나) 문제가 있고, 1 ㎛ 초과이면 재응집이 발생할 수 있다.
본 발명에 있어서, 상기 안료는 커버력, 은폐력, 지속성, 발유성, 발수성 및 사용성, 예컨대, 발림성 개선의 역할을 하는 것으로, 산화티탄(titanium dioxide, TiO2), 마이크로 산화티탄(Micro TiO2), 산화아연(zinc oxide, ZnO), 마이크로 산화아연(Micro ZnO), 산화철(Ⅱ)(FeO(Ⅱ)), 산화철, 산화알루미늄(alumina, Al2O3), 황산바륨(barium sulfate, BaSO3), 이산화규소(silica, SiO2), 탈크, 카올린, 세리사이트(sericite) 및 마이카로 이루어진 군에서 선택되는 1종 이상일 수 있으며, 특히, 산화티탄을 사용할 경우 커버력과 은폐력 측면에서 더욱 유리할 수 있다. 상기 산화철은 산화철(Ⅱ)(FeO(Ⅱ)), 산화철(Ⅲ)(FeO(Ⅲ)) 또는 산화철(Ⅳ)(FeO(Ⅳ))일 수 있다.
본 발명에 있어서, 상기 안료의 표면에 형성된 코팅층은 단일층 또는 이중층 형태일 수 있다.
도 1a 및 1b는 본 발명에 따른 안료를 포함하는 화장료 조성물의 모식도이다.
도 1a를 참조하면 본 발명에 따른 화장료 조성물에 포함된 유상과 수상을 포함하는 안료(1)는 안료 입자(10)의 표면에 단일 코팅층(20)이 형성된 형태로서, 단일 코팅층(20)은 유상과 수상의 혼합물을 포함할 수 있다.
또한, 도 1b를 참조하면 본 발명에 따른 화장료 조성물에 포함된 유상과 수상을 포함하는 안료(1)는 안료 입자(10)의 표면에 유상층(30a) 및 수상층(30b)를 포함하는 이중 코팅층(30)이 코팅된 형태일 수 있다.
이때, 상기 유상층과 수상층의 중량비는 1 : 0.1 내지 1, 바람직하게는 1: 0.3 내지 0.6일 수 있으며, 상기 유상에 대한 수상의 중량비가 0.1 미만이면 기능적인 측면에서 효능이 저하될 수 있고, 1 초과이면 분산성 측면에서 문제가 있을 수 있다.
본 발명에 있어서, 상기 유상층은 발수성 및 유상에서의 분산성을 향상시키는 역할을 하는 것으로, 디메치콘류, 메치콘류, 하이드로겐 디메치콘류, 카플릴릭 실란류 및 불소계 실리콘류로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있으며, 특히, 상기 유상층이 트리에톡시카프릴릴실란(TRIETHOXYCAPRYLYLSILANE)으로 이루어질 경우 커버력 및 분산성 측면에서 유리할 수 있다.
본 발명에 있어서, 상기 수상층은 발유성 및 수상에서의 분산성을 향상시키는 역할을 하는 것으로, 레시틴류 및 실리카류로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있으며, 특히, 상기 수상층이 하이드로제네이티드 레시틴(HYDROGENATED LECITHIN)으로 이루어질 경우 분산성 측면에서 유리할 수 있다.
본 발명에 있어서, 상기 안료의 함량은 상기 화장료 조성물 전체 중량을 기준으로 0.01 내지 40 중량%, 바람직하게는, 1 내지 10 중량%이다. 상기 안료의 함량의 상기 범위 미만이면 커버력과 은폐력이 좋지 않을 수 있고, 상기 범위 초과이면 안정화시키기 어려운 문제점이 있다.
본 발명의 화장료 조성물은 다양한 화장품, 특히, 쿠션, 에멀젼 파운데이션과같은 피부 베이스 화장품 뿐만 아니라, 고형 화장품, 예를 들어, 루스형 파우더, 파우더 파운데이션, 압축형 파운데이션, 볼터치, 아이섀도우, 아이브로우 케이크, 바디 파우더 및 기타 고체 형태의 화장품에 유용하다. 이때, “고형”이라는 것이 의미하는 것은 조성물이 25℃에서 고체이며 비유동성이라는 것이다.
본 발명의 화장료 조성물은 수분산, 유분산, W/O(water in oil) 또는 O/W(oil in water)의 형태로 제형화될 수 있다.
또한, 본 발명의 화장료 조성물은 리퀴드, 크림 또는 케익의 형태의 파운데이션, 메이크업베이스 화장료 또는 자외선 차단용 화장료의 형태로 제형화될 수 있다.
또한, 본 발명의 화장료 조성물은 당 업계에서 통상적으로 제조되는 어떠한 제형으로도 제조될 수 있으며, 예를 들어, 용액, 현탁액, 유탁액, 페이스트, 겔, 크림, 로션, 파우더, 비누, 계면활성제-함유 클렌징, 오일, 분말 파운데이션, 유탁액 파운데이션, 왁스 파운데이션 및 스프레이 등으로 제형화될 수 있으나, 이에 한정되는 것은 아니다. 보다 상세하게는, 유연 화장수, 영양 화장수, 영양 크림, 마사지 크림, 에센스, 아이 크림, 클렌징 크림, 클렌징 포옴, 클렌징 워터, 팩, 스프레이 또는 파우더의 제형으로 제조될 수 있다.
본 발명의 제형이 페이스트, 크림 또는 겔인 경우에는 담체 성분으로서 동물성유, 식물성유, 왁스, 파라핀, 전분, 트라칸트, 셀룰로오스 유도체, 폴리에틸렌 글리콜, 실리콘, 벤토나이트, 실리카, 탈크 또는 산화아연 등이 이용될 수 있다.
본 발명의 제형이 파우더 또는 스프레이인 경우에는 담체 성분으로서 락토스, 탈크, 실리카, 알루미늄 히드록시드, 칼슘 실리케이트 또는 폴리아미드 파우더가 이용될 수 있고, 특히 스프레이인 경우에는 추가적으로 클로로플루오로하이드로카본, 프로판/부탄 또는 디메틸 에테르와 같은 추진체를 포함할 수 있다.
본 발명의 제형이 용액 또는 유탁액인 경우에는 담체 성분으로서 용매, 용해화제 또는 유탁화제가 이용되고, 예컨대 물, 에탄올, 이소프로판올, 에틸 카보네이, 에틸 아세테이트, 글리세린, 카보머, 벤질 알코올, 벤질 벤조에이트, 프로필렌글리콜, 1,3-부틸글리콜 오일, 글리세롤 지방족 에스테르, 카프릴릭 카프릭 트리글리세라이드, 하이드로지네이티드 폴리데센, 세테아릴 글루코사이드, 소르비단 스테아레이트, 폴리에틸렌 글리콜, 세테아릴 알코올 등이 있다.
본 발명의 제형이 현탁액인 경우에는 담체 성분으로서 물, 에탄올 또는 프로필렌 글리콜과 같은 액상의 희석제, 에톡실화 이소스테아릴 알코올, 폴리옥시에틸렌 소르비톨 에스테르 및 폴리옥시에틸렌 소르비탄 에스테르와 같은 현탁제, 미소 결정성 셀룰로오스, 알루미늄 메타히드록시드, 벤토나이트, 아가 또는 트라칸트 등이 이용될 수 있다.
본 발명의 제형이 계면-활성제 함유 클린징인 경우에는 담체 성분으로서 지방족 알코올 설페이트, 지방족 알코올 에테르 설페이트, 설포숙신산 모노에스테르, 이세티오네이트, 이미다졸리늄 유도체, 메틸타우레이트, 사르코시네이트, 지방산아미드 에테르 설페이트, 알킬아미도베타인, 지방족 알코올, 지방산 글리세라이드, 지방산 디에탄올아미드, 식물성유, 라놀린 유도체 또는 에톡실화 글리세롤 지방산에스테르 등이 이용될 수 있다.
안료를 포함하는 화장료 조성물의 제조방법
본 발명은 또한, 안료와 유화제를 수상에 분산시키되, 회전하는 분산기기를 이용하여 분산시켜, 상기 안료의 표면에 유상과 수상을 포함하는 코팅층을 형성하는 단계를 포함하는 화장료 조성물의 제조방법에 관한 것이다.
도 2는 본 발명의 화장료 조성물의 제조방법에 따라 박막선회형 고속믹서를 이용하여 안료 입자를 분산시키는 공정의 모식도를 나타낸 것이다.
도 2를 참조하면, 처리액이 용기 내벽 따라 선회하여 생성되는 원심력으로 속도차가 발생하여 2차 응집을 풀고 재응집 방지 효과가 있어 안료의 입도 분포가 균일하게 될 수 있다.
상기 분산기기의 회전 속도는 5 m/s 내지 50 m/s 일 수 있으며, 상기 회전 속도가 5 m/s 미만이면 입도 분포가 개선되는 정도가 미미하고, 50 m/s 초과이면 안료입자의 형태가 변형될 수 있다.
또한, 상기 유화제는 안료가 수상에 잘 분산될 수 있도록 하기 위해 첨가하며, O/W(oil in water) 유화제로서 HLB(hydrophile-liphophile balance)가 높은 9~15 사이의 계면활성제를 사용하며 PEG-30 수소화된 캐스터 오일(Hydrogenated Castor Oil), 글리세릴 스테아레이트(glyceryl Stearate) 및 PEG-100 스테아레이트(Stearate), 폴리에틸렌 글리콜 모노이소스테아레이트(Polyethylene Glycol Monoisostearate), 세테아릴 올리베이트(Cetearyl Olivate)/소르비탄 올리베이트(Sorbitan Olivate), 수소화된 레시틴(Hydrogenated Lecithin), 아라치딜 알코올(Arachidyl Alcohol) 및 베헤닐 알코올(Behenyl Alcohol) 및 아라치딜 글루코시드(Arachidyl Glucoside), 세테아릴 알코올(Cetearyl Alcohol)/세테아릴 글루코시드(Cetearyl Glucoside), 폴리소르베이트(Polysorbate) 80 및 폴리소르베이트(Polysorbate) 60 로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있다.
상기 유화제는 화장료 조성물 총 중량에 대하여 0.1 내지 1.5 중량% 만큼 포함될 수 있으며, 유화제의 함량이 상기 범위에 포함될 경우 안료 입자의 분산성이 우수할 수 있다.
상술한 바와 같은 제조방법에 따라 제조된, 본 발명의 화장료 조성물은 입도 분포가 균일하고, 장시간이 경과하여도 점도 유지율이 높아 다양한 제형으로 제형화하기에 유리할 수 있다.
이하, 실시예를 통하여 본 발명을 더욱 구체적으로 설명하기로 하지만, 하기 실시예가 본 발명의 범위를 제한하는 것은 아니며, 이는 본 발명의 이해를 돕기 위한 것으로 해석되어야 할 것이다.
실시예 1
하기 표 1에 나타난 바와 같은 조성으로 W/O 형태의 리퀴드 파운데이션 제형을 가지는 화장료 조성물을 제조하였다.
입경이 0.3 ㎛ 내지 0.5 ㎛ 인 TiO2를 유화제인 POLYSORBATE 80 과 함께 수상인 하이드로제네이티드 레시틴(HYDROGENATED LECITHIN)에 첨가하여 박막선회형 고속믹서인 필믹서를 이용하여 30 m/s 의 회전속도로 분산시켜, 유상과 수상으로 코팅된 TiO2 안료 입자를 포함하는 리퀴드 파운데이션 제형의 화장료 조성물을 제조하였다.
이때, 상기 TiO2 안료 입자의 함량은 화장료 조성물 전체 중량을 기준으로 7 중량% 가 되도록 하였다.
성분 중량%
안료 입자(입경이 0.3 ㎛ 내지 0.5 ㎛ 인 TiO2) 7
유화제(POLYSORBATE 80) 1
수상(HYDROGENATED LECITHIN) 0.5
부틸렌 글라이콜 3
유화제(세틸 피이지/피피지-10/1 디메티콘) 3
안료입자(디메티콘으로 코팅된 산화철) 5.0
디메치콘(Dimethicone) 잔부
사이클로펜타실록산 및 PEG/PEG-19/19 디메치콘(Cyclopentasiloxane and PEG/PPG-19/19 Dimethicone) 5.0
디스테아르디모니움 헥토라이트 (Disteardimonium Hectorite) 1.0
방부제 적량
정제수 잔부
실시예 2
실시예 1과 동일하게 실시하되, 상기 TiO2 안료 입자의 함량은 화장료 조성물 전체 중량을 기준으로 10 중량% 가 되도록 하였다.
비교예 1
실시예 1과 동일하게 실시하되, 박막선회형 고속믹서 대신 링밀을 이용하여 유상과 수상으로 코팅된 TiO2 안료 입자를 포함하는 화장료 조성물을 제조하였다.
비교예 2
실시예 2와 동일하게 실시하되, 박막선회형 고속믹서 대신 링밀을 이용하여 유상과 수상으로 코팅된 TiO2 안료 입자를 포함하는 화장료 조성물을 제조하였다.
실험예 1: 입도 분포 측정
실시예 1 및 비교예 1에서 각각 제조된 리퀴드 파운데이션 제형의 화장료 조성물을 3D 레이저 현미경을 이용하여 관찰하였다.
도 3a 및 도 3b는 각각 실시예 1 및 비교예 1에서 각각 제조된 화장료 조성물의 현미경 사진이다.
도 3a를 참조하면 실시예 1은 크기가 큰 입자가 거의 관찰되지 않는 반면, 도 3b를 참조하면 비교예 1은 크기가 큰 입자가 다수 관찰되었다. 이로부터, 회전하는 분산기기의 원심력을 이용하여 안료 입자를 분산시키는 박막선회형 고속믹서를 사용하는 경우, 종래 링밀을 이용하는 경우에 비해 입도 분포를 균일하게 할 수 있음을 알 수 있다.
실험예 2: 장기 안정성 실험
실시예 1,2 및 비교예 1,2에서 각각 제조된 화장료 조성물에 대해서 점도 경시율을 측정하기 위하여, 점도 최초 측정 당일, 점도 최초 측정일로부터 1일째, 7일째 및 3달째 되던 날에 각 화장료 조성물의 점도를 측정하여, 3달 동안의 점도 경시율을 비교하였다.
도 4는 실시예 1,2 및 비교예 1,2의 화장료 조성물에 대한 점도 경시율 측정 결과를 나타낸 그래프이다.
도 4 및 하기 표 2를 참조하면, 실시예 1,2에서 각각 제조된 화장료 조성물은 3달 점도 경시율이 96% 정도이나, 비교예 2의 경우 3달 점도 경시율이 74% 정도이며 점도가 2만 cps 수준을 유지하므로 다양한 제형에 적용하기에 어려움이 있다.
단위:cps 당일 1일 7일 3달 점도 경시율
실시예 1 14450 cps 14000 cps 13800 cps 11200 cps 80%
실시예 2 14250 cps 13600 cps 13100 cps 13067 cps 96%
비교예 1 15050 cps 13550 cps 12650 cps 10133 cps 74%
비교예 2 21350 cps 20400 cps 20000 cps 16533 cps 81%
실험예 3: 입도분포
실시예 1,2 및 비교예 1,2에서 각각 제조된 화장료 조성물을 입도분포도를 측정하여 평균입도를 관찰하였다.
하기 표 3은 실시예 1,2 및 비교예 1,2에서 각각 제조된 화장료 조성물의 평균입도이다. 실시예 1,2는 안료의 함량이 늘어나도 기존 안료의 입도와 유사한 사이즈를 유지하나, 비교예 1,2는 안료의 함량이 늘어날수록 기존 안료보다 입자가 커진다. 이는 실시예의 기술을 적용 시 안료가 재응집이 되지 않고 기존 안료의 사이즈를 안정적으로 잘 유지하는 반면, 종래 기술인 비교예는 제형 내에서 안료들이 응집되면서 사이즈가 커진 것으로 추정된다.
안료 0.59 ㎛
실시예1 0.69 ㎛
실시예2 0.628 ㎛
비교예1 3.03 ㎛
비교예2 12.9 ㎛
실험예 4: 관능평가
실시예 1,2 및 비교예 1,2에서 각각 제조된 화장료 조성물에 대해서 관능평가를 실시하였다.
20~40세의 여성 30명을 대상으로 실시예 1,2 및 비교예 1,2에서 각각 제조된 화장료 조성물을 사용하게 하고, 하기와 같은 제1 특성 내지 제4 특성에 대해서 평가하여 그 결과를 도 5에 나타내었다.
- 제1 특성: 매끈함, 윤기, 촉촉함, 잔여감, 골끼임
- 제2 특성: 두께감, 끈적임, 커버력
- 제3 특성: 밀착감
- 제4 특성: 펴발림성
도 5는 실시예 1,2 및 비교예 1,2에 따른 화장료 조성물에 대해 관능평가를 실시한 결과를 나타낸 그래프이다.
도 5를 참조하면, 실시예 1,2의 경우 매끈함, 윤기, 촉촉함, 잔여감, 골끼임이 모두 우수하며, 특히, 실시예 2의 경우 실시예 1에 비해 안료의 함량이 높으며 이에 따라 커버력도 우수한 것을 알 수 있다.
이에, 촉촉함과 커버력을 동시에 구현할 수 있는 화장료 조성물을 개발할 수 있음을 확인하였다.
이하 본 발명의 또 다른 제형예를 설명하지만, 본 발명에 따른 유상과 수상을 포함하는 코팅층으로 코팅된 안료 입자를 포함하는 화장료 조성물의 제형이 이들 예로만 한정되는 것은 아니다.
제형예 1: 마사지 크림
하기 표 4의 조성에 따라 통상적인 방법으로 본 발명의 유상과 수상을 포함하는 코팅층으로 코팅된 안료를 포함하는 마사지 크림을 제조하였다.
성분 중량%
안료 입자(입경이 0.3 ㎛ 내지 0.5 ㎛ 인 TiO2) 0.5
유화제(POLYSORBATE 80) 1
수상(HYDROGENATED LECITHIN) 16.5
이카리시드 B2 0.5
밀납 10.0
폴리솔베이트 60 1.5
PEG 60 경화피마자유 2.0
솔비탄세스퀴올레이트 0.8
유동파라핀 40.0
스쿠알란 5.0
카프릴릭/카프릭트리글리세라이드 4.0
글리세린 5.0
부틸렌글리콜 3.0
프로필렌글리콜 3.0
트리에탄올아민 0.2
방부제,색소,향료 적량
정제수 잔부
제형예 2: 영양 화장수
하기 표 5의 조성에 따라 통상적인 방법으로 본 발명의 유상과 수상을 포함하는 코팅층으로 코팅된 안료를 포함하는 영양 화장수를 제조하였다.
성분 중량%
안료 입자(입경이 0.3 ㎛ 내지 0.5 ㎛ 인 TiO2) 0.1
유화제(POLYSORBATE 80) 1
수상(HYDROGENATED LECITHIN) 16.9
알파-케토글루타르산 1.0
나이아신아마이드 1.0
베타-1,3-글루칸 1.0
밀납 4.0
폴리솔베이트 1.5
솔비탄세스퀴올레이트 1.5
유동파라핀 0.5
카프릴릭/카프릭트리글리세라이드 5.0
글리세린 3.0
부틸렌글리콜 3.0
프로필렌글리콜 3.0
카르복시비닐폴리머 0.1
트리에탄올아민 0.2
방부제, 향료 0.1
정제수 잔부
제형예 3: 팩
하기 표 6의 조성에 따라 통상적인 방법으로 유상과 수상을 포함하는 코팅층으로 코팅된 안료를 포함하는 팩을 제조하였다.
성분 중량%
안료 입자(입경이 0.3 ㎛ 내지 0.5 ㎛ 인 TiO2) 2
유화제(POLYSORBATE 80) 1
수상(HYDROGENATED LECITHIN) 15
글리세린 4.0
폴리비닐알코올 15.0
히알루론산 추출물 5.0
베타글루칸 7.0
알란토인 0.1
노닐페닐에테르 0.4
폴리솔베이트 60 1.2
에탄올 6.0
정제수 잔부
제형예 4: 연고
하기 표 7의 조성에 따라 통상적인 방법으로 본 발명의 유상과 수상을 포함하는 코팅층으로 코팅된 안료를 포함하는 연고를 제조하였다.
성분 중량%
안료 입자(입경이 0.3 ㎛ 내지 0.5 ㎛ 인 TiO2) 2
유화제(POLYSORBATE 80) 1
수상(HYDROGENATED LECITHIN) 15
알파-케토글루타르산 1.0
나이아신아마이드 1.0
베타-1,3-글루칸 10.0
밀납 10.0
폴리솔베이트 5.0
피이지 60 경화피마자유 2.0
솔비탄세스퀴올레이트 0.5
바세린 5.0
유동파라핀 10.0
스쿠알란 5.0
쉐어버터 3.0
카프릴릭/카프릭트리글리세라이드 5.0
글리세린 10.0
프로필렌글리콜 10.2
트리에탄올아민 0.2
방부제, 향료 0.1
정제수 잔부
제형예 5: 겔
하기 표 8의 조성에 따라 통상적인 방법으로 유상과 수상을 포함하는 코팅층으로 코팅된 안료를 포함하는 겔을 제조하였다.
성분 중량%
안료 입자(입경이 0.3 ㎛ 내지 0.5 ㎛ 인 TiO2) 1
유화제(POLYSORBATE 80) 1
수상(HYDROGENATED LECITHIN) 16
판테놀 5.0
해송자 오일 0.01
알파-케토글루타르산 1.0
나이아신아마이드 1.0
베타-1,3-글루칸 0.1
에틸렌디아민초산나트륨 0.05
글리세린 5.0
카르복시비닐폴리머 0.3
에탄올 5.0
피이지 60 경화피마자유 0.5
트리에탄올아민 0.3
방부제, 향료 0.1
정제수 잔부
[부호의 설명]
1: 유상과 수상을 포함하는 코팅층을 포함하는 안료
10: 안료 입자
20: 단일 코팅층
30: 이중 코팅층
30a: 유상층
30b: 수상층

Claims (11)

  1. 유상과 수상을 포함하는 코팅층으로 코팅된 안료 입자를 포함하는 화장료 조성물.
  2. 제1항에 있어서,
    상기 안료의 입도는 0.1 ㎛ 내지 1 ㎛인, 화장료 조성물.
  3. 제1항에 있어서,
    상기 안료는 산화티탄(titanium dioxide, TiO2), 마이크로 산화티탄(Micro TiO2), 산화아연(zinc oxide, ZnO), 마이크로 산화아연(Micro ZnO), 산화철, 산화알루미늄(alumina, Al2O3), 황산바륨(barium sulfate, BaSO3), 이산화규소(silica, SiO2), 탈크, 카올린, 세리사이트(sericite) 및 마이카로 이루어진 군에서 선택되는 1종 이상의 무기 안료인, 화장료 조성물.
  4. 제1항에 있어서,
    상기 유상은 디메치콘류, 메치콘류, 하이드로겐 디메치콘류, 카플릴릭 실란류 및 불소계 실리콘류로 이루어진 군에서 선택되는 1종 이상을 포함하는, 화장료 조성물.
  5. 제1항에 있어서,
    상기 수상은 레시틴류 및 실리카류로 이루어진 군에서 선택되는 1종 이상을 포함하는, 화장료 조성물.
  6. 제1항에 있어서,
    상기 코팅층은 유상과 수상의 혼합물을 포함하는 단일 코팅층인, 화장료 조성물.
  7. 제1항에 있어서,
    상기 코팅층은 유상층 및 수상층을 포함하는 이중 코팅층인, 화장료 조성물.
  8. 제1항에 있어서,
    상기 화장료 조성물은 수분산, 유분산, W/O(water in oil) 또는 O/W(oil in water)의 형태로 제형화되는 것인, 화장료 조성물.
  9. 제1항에 있어서,
    상기 화장료 조성물은 리퀴드, 크림 또는 케익 형태의 파운데이션, 메이크업베이스 화장료 또는 자외선 차단용 화장료의 형태로 제형화되는 것인, 화장료 조성물.
  10. 안료와 유화제를 수상에 분산시키되, 박막선회형 고속믹서 분산기기를 이용하여 분산시켜, 상기 안료의 표면에 유상과 수상을 포함하는 코팅층을 형성하는 단계를 포함하는, 화장료 조성물의 제조방법.
  11. 제10항에 있어서,
    상기 분산기기의 회전속도는 5 내지 50 m/s인, 화장료 조성물의 제조방법.
PCT/KR2018/008215 2017-07-31 2018-07-20 안료를 포함하는 화장료 조성물 및 그 제조방법 Ceased WO2019027164A1 (ko)