WO2018137504A1 - Polymère covalent dynamique et son application - Google Patents

Polymère covalent dynamique et son application Download PDF

Info

Publication number
WO2018137504A1
WO2018137504A1 PCT/CN2018/072454 CN2018072454W WO2018137504A1 WO 2018137504 A1 WO2018137504 A1 WO 2018137504A1 CN 2018072454 W CN2018072454 W CN 2018072454W WO 2018137504 A1 WO2018137504 A1 WO 2018137504A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
dynamic covalent
polymer
dynamic
bond
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/CN2018/072454
Other languages
English (en)
Chinese (zh)
Inventor
郭琼玉
徐晖
张欢
梁愫
林淦
欧阳勇
翁文桂
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Weng Qiumei
Original Assignee
Weng Qiumei
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Weng Qiumei filed Critical Weng Qiumei
Publication of WO2018137504A1 publication Critical patent/WO2018137504A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un polymère covalent dynamique, ledit polymère comprenant une liaison ester inorganique covalente dynamique de borate de silicium, un groupe de liaison qui est relié à des atomes de silicium dans au moins deux liaisons ester inorganiques différentes de borate de silicium contenant un atome de carbone qui est sur la chaîne polymère covalente dynamique. Le polymère covalent dynamique présente une forte réversibilité dynamique et dissipation d'énergie du fait qu'il contient la liaison ester inorganique du borate de silicium, et fait preuve de propriétés fonctionnelles de réactivité aux stimuli, d'auto-réparation et similaires, présentant ainsi une large gamme de perspectives d'application dans les domaines de la thérapie athlétique, des revêtements fonctionnels, des matériaux biomimétiques et similaires.
PCT/CN2018/072454 2017-01-25 2018-01-12 Polymère covalent dynamique et son application Ceased WO2018137504A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN201710056037.X 2017-01-25
CN201710056037.XA CN108359100A (zh) 2017-01-25 2017-01-25 一种动态共价聚合物及其应用

Publications (1)

Publication Number Publication Date
WO2018137504A1 true WO2018137504A1 (fr) 2018-08-02

Family

ID=62978042

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2018/072454 Ceased WO2018137504A1 (fr) 2017-01-25 2018-01-12 Polymère covalent dynamique et son application

Country Status (2)

Country Link
CN (1) CN108359100A (fr)
WO (1) WO2018137504A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113622045A (zh) * 2021-08-18 2021-11-09 东华大学 一种类玻璃高分子纤维及其制备方法

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110607112B (zh) * 2019-08-26 2021-04-13 中国石油天然气集团公司 一种水性环氧重防腐涂料及其制备方法
CN112876753B (zh) * 2021-01-21 2021-11-16 中国石油大学(北京) 一种共价有机框架/丁苯橡胶复合材料及其制备方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5258437A (en) * 1991-06-27 1993-11-02 Shin-Etsu Chemical Co., Ltd. Silicone putty compositions
CN101343421A (zh) * 2008-08-28 2009-01-14 上海交通大学 pH调控释放的动态聚合物封装体系的制备方法
WO2013127989A1 (fr) * 2012-03-02 2013-09-06 Fundación Cidetec Matériau élastomère autorégénérant
CN105111470A (zh) * 2015-08-13 2015-12-02 四川大学 一种可逆共价交联聚硅氧烷弹性体及其制备方法与应用
CN105646872A (zh) * 2016-02-26 2016-06-08 翁秋梅 一种动态聚合物材料

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5258437A (en) * 1991-06-27 1993-11-02 Shin-Etsu Chemical Co., Ltd. Silicone putty compositions
CN101343421A (zh) * 2008-08-28 2009-01-14 上海交通大学 pH调控释放的动态聚合物封装体系的制备方法
WO2013127989A1 (fr) * 2012-03-02 2013-09-06 Fundación Cidetec Matériau élastomère autorégénérant
CN105111470A (zh) * 2015-08-13 2015-12-02 四川大学 一种可逆共价交联聚硅氧烷弹性体及其制备方法与应用
CN105646872A (zh) * 2016-02-26 2016-06-08 翁秋梅 一种动态聚合物材料

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113622045A (zh) * 2021-08-18 2021-11-09 东华大学 一种类玻璃高分子纤维及其制备方法

Also Published As

Publication number Publication date
CN108359100A (zh) 2018-08-03

Similar Documents

Publication Publication Date Title
CN108341951B (zh) 一种具有杂化交联结构的动态聚合物及其应用
WO2018137508A1 (fr) Polymère dynamique ayant une structure réticulée hybride, et application associée
CN107805308B (zh) 一种具有杂化交联网络的动态聚合物及其应用
CN107805311B (zh) 一种具有杂化交联网络的动态聚合物及其应用
WO2017206671A1 (fr) Polymère dynamique présentant une structure réticulée dynamique
CN109666167B (zh) 一种杂化动态聚合物组合物
CN108341960B (zh) 一种含有组合动态共价键的动态聚合物及其应用
CN109666121B (zh) 一种杂化动态交联聚合物及其应用
CN108610486A (zh) 一种基于组合杂化交联动态聚合物的吸能方法
WO2018137507A1 (fr) Polymère dynamique à phases séparées physiques et son utilisation
CN107129580A (zh) 一种动态聚合物材料及其应用
WO2018028365A1 (fr) Polymère dynamique à réseau réticulé hybride, et application associée
CN108342002A (zh) 一种具有杂化交联网络的动态聚合物及其应用
CN108341961B (zh) 一种含有组合动态共价键的动态聚合物制备及其应用
CN108342037A (zh) 一种基于杂化交联网络动态聚合物的吸能方法
CN108341948A (zh) 一种杂化交联动态聚合物及其应用
CN109666168A (zh) 一种自修复性固态杂化动态聚合物及其应用
CN109666156A (zh) 一种基于杂化动态聚合物组合物的吸能方法
WO2018137505A1 (fr) Polymère ou composition dynamique présentant une structure de liaison hybride, et application associée
CN108341944A (zh) 一种基于动态聚合物的吸能方法
CN108342013A (zh) 一种杂化交联动态聚合物及其应用
CN108341965A (zh) 一种交联动态聚合物及其应用
CN108341959A (zh) 一种动态聚合物及其应用
CN108341962A (zh) 一种动态聚合物及其应用
CN109666162A (zh) 一种基于动态交联聚合物的吸能方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18744418

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18744418

Country of ref document: EP

Kind code of ref document: A1