WO2017110565A1 - Composition de caoutchouc de silicone liquide formant une éponge et éponge en caoutchouc de silicone - Google Patents

Composition de caoutchouc de silicone liquide formant une éponge et éponge en caoutchouc de silicone Download PDF

Info

Publication number
WO2017110565A1
WO2017110565A1 PCT/JP2016/086943 JP2016086943W WO2017110565A1 WO 2017110565 A1 WO2017110565 A1 WO 2017110565A1 JP 2016086943 W JP2016086943 W JP 2016086943W WO 2017110565 A1 WO2017110565 A1 WO 2017110565A1
Authority
WO
WIPO (PCT)
Prior art keywords
component
silicone rubber
sponge
mass
group
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2016/086943
Other languages
English (en)
Japanese (ja)
Inventor
昭宏 中村
正和 入江
次雄 野副
遠藤　修司
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DuPont Toray Specialty Materials KK
Original Assignee
Dow Corning Toray Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dow Corning Toray Co Ltd filed Critical Dow Corning Toray Co Ltd
Priority to JP2017557888A priority Critical patent/JP6958984B2/ja
Publication of WO2017110565A1 publication Critical patent/WO2017110565A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne une composition de caoutchouc de silicone liquide formant une éponge qui forme une éponge de faible densité présentant une structure à alvéoles ouverts fins et uniformes, et qui est au moins composée de (A) un organopolysiloxane ayant au moins deux groupes alcényles dans chaque molécule, (B) un organopolysiloxane ayant au moins deux atomes d'hydrogène liés à un atome de silicium dans chaque molécule, (C) un mélange d'eau et d'un épaississant inorganique, (D) un tensioactif composé d'un tensioactif non ionique ayant une valeur HLB de 3 ou plus et d'un tensioactif non ionique ayant une valeur HLB inférieure à 3, (E) un catalyseur d'hydrosilylation et (F) un retardateur de vulcanisation.
PCT/JP2016/086943 2015-12-25 2016-12-12 Composition de caoutchouc de silicone liquide formant une éponge et éponge en caoutchouc de silicone Ceased WO2017110565A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2017557888A JP6958984B2 (ja) 2015-12-25 2016-12-12 スポンジ形成性液状シリコーンゴム組成物およびシリコーンゴムスポンジ

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2015-252782 2015-12-25
JP2015252782 2015-12-25

Publications (1)

Publication Number Publication Date
WO2017110565A1 true WO2017110565A1 (fr) 2017-06-29

Family

ID=59090162

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2016/086943 Ceased WO2017110565A1 (fr) 2015-12-25 2016-12-12 Composition de caoutchouc de silicone liquide formant une éponge et éponge en caoutchouc de silicone

Country Status (3)

Country Link
JP (1) JP6958984B2 (fr)
TW (1) TWI726025B (fr)
WO (1) WO2017110565A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019064711A1 (fr) * 2017-09-28 2019-04-04 日東電工株式会社 Feuille de fixation temporaire
WO2019150991A1 (fr) * 2018-02-01 2019-08-08 ダウ・東レ株式会社 Composition de caoutchouc silicone formant éponge, et éponge en caoutchouc silicone
WO2024063070A1 (fr) * 2022-09-21 2024-03-28 ダウ・東レ株式会社 Composition de caoutchouc de silicone multicomposants formant une éponge

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6933660B2 (ja) 2016-11-28 2021-09-08 ダウ・東レ株式会社 スポンジ形成性液状シリコーンゴム組成物およびシリコーンゴムスポンジ

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004143332A (ja) * 2002-10-25 2004-05-20 Shindo Seni Kogyo Kk シリコーンゴムスポンジ用エマルション組成物およびシリコーンゴムスポンジの製造方法
WO2005085357A1 (fr) * 2004-03-05 2005-09-15 Dow Corning Toray Co., Ltd. Composition d’émulsion pour une éponge en caoutchouc de silicone, procédé de fabrication de celle-ci, et procédé de fabrication de l’éponge en caoutchouc de silicone
JP2008214625A (ja) * 2007-02-07 2008-09-18 Dow Corning Toray Co Ltd スポンジ形成性液状シリコーンゴム組成物およびシリコーンゴムスポンジ
WO2010013847A1 (fr) * 2008-07-31 2010-02-04 東レ・ダウコーニング株式会社 Composition de caoutchouc de silicone liquide multicomposants formant une éponge et procédé de fabrication d'éponge de caoutchouc de silicone

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004143332A (ja) * 2002-10-25 2004-05-20 Shindo Seni Kogyo Kk シリコーンゴムスポンジ用エマルション組成物およびシリコーンゴムスポンジの製造方法
WO2005085357A1 (fr) * 2004-03-05 2005-09-15 Dow Corning Toray Co., Ltd. Composition d’émulsion pour une éponge en caoutchouc de silicone, procédé de fabrication de celle-ci, et procédé de fabrication de l’éponge en caoutchouc de silicone
JP2008214625A (ja) * 2007-02-07 2008-09-18 Dow Corning Toray Co Ltd スポンジ形成性液状シリコーンゴム組成物およびシリコーンゴムスポンジ
WO2010013847A1 (fr) * 2008-07-31 2010-02-04 東レ・ダウコーニング株式会社 Composition de caoutchouc de silicone liquide multicomposants formant une éponge et procédé de fabrication d'éponge de caoutchouc de silicone

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019064711A1 (fr) * 2017-09-28 2019-04-04 日東電工株式会社 Feuille de fixation temporaire
JP2019065079A (ja) * 2017-09-28 2019-04-25 日東電工株式会社 仮固定シート
TWI660850B (zh) * 2017-09-28 2019-06-01 日商日東電工股份有限公司 暫固定片
CN111148785A (zh) * 2017-09-28 2020-05-12 日东电工株式会社 临时固定片
WO2019150991A1 (fr) * 2018-02-01 2019-08-08 ダウ・東レ株式会社 Composition de caoutchouc silicone formant éponge, et éponge en caoutchouc silicone
KR20200118057A (ko) * 2018-02-01 2020-10-14 다우 도레이 캄파니 리미티드 스펀지 형성성 실리콘 고무 조성물 및 실리콘 고무 스펀지
JPWO2019150991A1 (ja) * 2018-02-01 2021-01-28 ダウ・東レ株式会社 スポンジ形成性シリコーンゴム組成物およびシリコーンゴムスポンジ
EP3747939A4 (fr) * 2018-02-01 2021-10-06 Dow Toray Co., Ltd. Composition de caoutchouc silicone formant éponge, et éponge en caoutchouc silicone
JP7164284B2 (ja) 2018-02-01 2022-11-01 ダウ・東レ株式会社 スポンジ形成性シリコーンゴム組成物およびシリコーンゴムスポンジ
US11981786B2 (en) 2018-02-01 2024-05-14 Dow Toray Co., Ltd. Sponge-forming silicone rubber composition and silicone rubber sponge
KR102679280B1 (ko) * 2018-02-01 2024-07-01 다우 도레이 캄파니 리미티드 스펀지 형성성 실리콘 고무 조성물 및 실리콘 고무 스펀지
WO2024063070A1 (fr) * 2022-09-21 2024-03-28 ダウ・東レ株式会社 Composition de caoutchouc de silicone multicomposants formant une éponge

Also Published As

Publication number Publication date
JPWO2017110565A1 (ja) 2018-10-11
JP6958984B2 (ja) 2021-11-02
TW201736517A (zh) 2017-10-16
TWI726025B (zh) 2021-05-01

Similar Documents

Publication Publication Date Title
JP5524451B2 (ja) スポンジ形成性液状シリコーンゴム組成物およびシリコーンゴムスポンジ
JP5577250B2 (ja) 多成分型スポンジ形成性液状シリコーンゴム組成物およびシリコーンゴムスポンジの製造方法
JP6047345B2 (ja) 導電性スポンジ形成性液状シリコーンゴム組成物の製造方法、導電性シリコーンゴムスポンジおよびその製造方法
EP3259307B1 (fr) Composition de caoutchouc de silicone apte à former une éponge et éponge en caoutchouc de silicone
JP5209049B2 (ja) シリコーンゴムスポンジ成形品の製造方法
WO2010073654A1 (fr) Composition d'emulsion de formation d'eponge de caoutchouc de silicone et procede de fabrication de cette eponge
EP3259308B1 (fr) Composition de caoutchouc de silicone apte à former une éponge et éponge en caoutchouc de silicone
JP6958984B2 (ja) スポンジ形成性液状シリコーンゴム組成物およびシリコーンゴムスポンジ
EP3747939B1 (fr) Composition de caoutchouc silicone formant éponge, et éponge en caoutchouc silicone
JP6933660B2 (ja) スポンジ形成性液状シリコーンゴム組成物およびシリコーンゴムスポンジ
JP2011168728A (ja) シリコーンゴムスポンジの製造方法
WO2024063070A1 (fr) Composition de caoutchouc de silicone multicomposants formant une éponge

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16878456

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2017557888

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16878456

Country of ref document: EP

Kind code of ref document: A1