WO2017002815A1 - Bloc d'éléments de batterie zinc-air et batterie l'utilisant - Google Patents

Bloc d'éléments de batterie zinc-air et batterie l'utilisant Download PDF

Info

Publication number
WO2017002815A1
WO2017002815A1 PCT/JP2016/069161 JP2016069161W WO2017002815A1 WO 2017002815 A1 WO2017002815 A1 WO 2017002815A1 JP 2016069161 W JP2016069161 W JP 2016069161W WO 2017002815 A1 WO2017002815 A1 WO 2017002815A1
Authority
WO
WIPO (PCT)
Prior art keywords
zinc
separator
air
battery cell
cell pack
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2016/069161
Other languages
English (en)
Japanese (ja)
Inventor
裕一 権田
鬼頭　賢信
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NGK Insulators Ltd
Original Assignee
NGK Insulators Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NGK Insulators Ltd filed Critical NGK Insulators Ltd
Priority to JP2017526376A priority Critical patent/JP7095991B2/ja
Publication of WO2017002815A1 publication Critical patent/WO2017002815A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne une forme d'un bloc d'éléments de batterie qui a d'excellentes propriétés de manipulation et qui est extrêmement avantageux dans l'assemblage d'une batterie, pour une batterie (un élément) unique d'une batterie zinc-air dans laquelle une électrode à air et une électrode négative ont été séparées de manière fiable avec un séparateur conducteur d'ions hydroxyde. Le bloc d'éléments de batterie zinc-air est équipé de : un corps de sac souple formé par un film souple et doté d'une ouverture ; une structure de séparation comprenant un séparateur qui ferme l'ouverture de manière étanche à l'air et à l'eau afin de former un espace fermé avec le corps de sac souple, et qui présente des propriétés de conduction des ions hydroxyde, mais pas des propriétés de perméabilité à l'eau et de respirabilité ; une électrode à air située sur un côté en regard de l'espace fermé du séparateur ; une électrode négative qui est logée dans l'espace fermé et est formée en comprenant du zinc, un alliage de zinc et/ou un composé de zinc ; et un électrolyte qui est logé dans l'espace fermé, possède l'électrode négative immergée en son sein, et est formé en comprenant une solution aqueuse d'hydroxyde de métal alcalin.
PCT/JP2016/069161 2015-07-01 2016-06-28 Bloc d'éléments de batterie zinc-air et batterie l'utilisant Ceased WO2017002815A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2017526376A JP7095991B2 (ja) 2015-07-01 2016-06-28 亜鉛空気電池セルパック及びそれを用いた組電池

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2015132861 2015-07-01
JP2015-132861 2015-07-01

Publications (1)

Publication Number Publication Date
WO2017002815A1 true WO2017002815A1 (fr) 2017-01-05

Family

ID=57608670

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2016/069161 Ceased WO2017002815A1 (fr) 2015-07-01 2016-06-28 Bloc d'éléments de batterie zinc-air et batterie l'utilisant

Country Status (2)

Country Link
JP (1) JP7095991B2 (fr)
WO (1) WO2017002815A1 (fr)

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017086278A1 (fr) * 2015-11-16 2017-05-26 日本碍子株式会社 Cartouche d'électrode et pile rechargeable au zinc l'utilisant
WO2019077953A1 (fr) * 2017-10-20 2019-04-25 日本碍子株式会社 Batterie secondaire au zinc
CN110313101A (zh) * 2017-02-03 2019-10-08 藤仓复合材料科技有限公司 金属空气电池及其使用方法
CN110534696A (zh) * 2019-07-29 2019-12-03 深圳大学 一种柔性电池及其制备方法
CN111326757A (zh) * 2018-12-14 2020-06-23 中国科学院大连化学物理研究所 一种金属海水燃料电池组
WO2020179645A1 (fr) * 2019-03-05 2020-09-10 シャープ株式会社 Électrode négative et batterie métal-air
JPWO2020246176A1 (fr) * 2019-06-05 2020-12-10
CN112585799A (zh) * 2018-08-22 2021-03-30 株式会社丰田自动织机 蓄电模块及蓄电模块的制造方法
CN112640197A (zh) * 2018-08-31 2021-04-09 夏普株式会社 金属空气电池模块
CN113707840A (zh) * 2021-08-19 2021-11-26 深圳德夏科技发展有限公司 柔性电池的制作方法、柔性电池及应用
CN114391198A (zh) * 2019-09-25 2022-04-22 日本碍子株式会社 空气极／隔板接合体及锌空气二次电池
CN115298856A (zh) * 2020-01-15 2022-11-04 三钛工业有限公司 具有多个电连接器的燃料电池
US11575181B2 (en) 2019-03-15 2023-02-07 Kabushiki Kaisha Toshiba Battery, battery pack, and stationary power supply

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004288571A (ja) * 2003-03-25 2004-10-14 Toshiba Battery Co Ltd 水系金属空気電池およびこれを用いた電子機器
JP2005515606A (ja) * 2001-12-31 2005-05-26 エビオニクス、インク． 折畳自在のカソードアセンブリを内蔵した充電式の金属空気型の電気化学セル
US20100255375A1 (en) * 2009-04-01 2010-10-07 United States Of America As Represented By Secretary Of The Army Molybdenum/air battery and cell design
JP2013037999A (ja) * 2011-08-10 2013-02-21 Toyota Motor Corp 金属空気電池
WO2013073292A1 (fr) * 2011-11-16 2013-05-23 日本碍子株式会社 Batterie rechargeable zinc-air
JP2013225443A (ja) * 2012-04-23 2013-10-31 Sharp Corp 金属空気電池およびエネルギーシステム
WO2014156578A1 (fr) * 2013-03-25 2014-10-02 日本碍子株式会社 Hydroxyde double lamellaire dense et son procédé de production
JP2014225344A (ja) * 2013-05-15 2014-12-04 日本碍子株式会社 金属空気二次電池の使用方法
WO2016076047A1 (fr) * 2014-11-13 2016-05-19 日本碍子株式会社 Corps de structure de séparateur destiné à être utilisé dans une batterie secondaire au zinc

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2012028062A (ja) * 2010-07-21 2012-02-09 Panasonic Corp リチウムイオン二次電池用負極及びその製造方法ならびにリチウムイオン二次電池

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005515606A (ja) * 2001-12-31 2005-05-26 エビオニクス、インク． 折畳自在のカソードアセンブリを内蔵した充電式の金属空気型の電気化学セル
JP2004288571A (ja) * 2003-03-25 2004-10-14 Toshiba Battery Co Ltd 水系金属空気電池およびこれを用いた電子機器
US20100255375A1 (en) * 2009-04-01 2010-10-07 United States Of America As Represented By Secretary Of The Army Molybdenum/air battery and cell design
JP2013037999A (ja) * 2011-08-10 2013-02-21 Toyota Motor Corp 金属空気電池
WO2013073292A1 (fr) * 2011-11-16 2013-05-23 日本碍子株式会社 Batterie rechargeable zinc-air
JP2013225443A (ja) * 2012-04-23 2013-10-31 Sharp Corp 金属空気電池およびエネルギーシステム
WO2014156578A1 (fr) * 2013-03-25 2014-10-02 日本碍子株式会社 Hydroxyde double lamellaire dense et son procédé de production
JP2014225344A (ja) * 2013-05-15 2014-12-04 日本碍子株式会社 金属空気二次電池の使用方法
WO2016076047A1 (fr) * 2014-11-13 2016-05-19 日本碍子株式会社 Corps de structure de séparateur destiné à être utilisé dans une batterie secondaire au zinc

Cited By (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10686177B2 (en) 2015-11-16 2020-06-16 Ngk Insulators, Ltd. Electrode cartridge and zinc secondary cell using same
WO2017086278A1 (fr) * 2015-11-16 2017-05-26 日本碍子株式会社 Cartouche d'électrode et pile rechargeable au zinc l'utilisant
CN110313101B (zh) * 2017-02-03 2023-04-04 藤仓复合材料科技株式会社 金属空气电池及其使用方法
CN110313101A (zh) * 2017-02-03 2019-10-08 藤仓复合材料科技有限公司 金属空气电池及其使用方法
US11342551B2 (en) 2017-10-20 2022-05-24 Ngk Insulators, Ltd. Zinc secondary battery
JPWO2019077953A1 (ja) * 2017-10-20 2020-05-28 日本碍子株式会社 亜鉛二次電池
WO2019077953A1 (fr) * 2017-10-20 2019-04-25 日本碍子株式会社 Batterie secondaire au zinc
CN112585799B (zh) * 2018-08-22 2024-02-02 株式会社丰田自动织机 蓄电模块及蓄电模块的制造方法
CN112585799A (zh) * 2018-08-22 2021-03-30 株式会社丰田自动织机 蓄电模块及蓄电模块的制造方法
US12034185B2 (en) 2018-08-31 2024-07-09 Sharp Kabushiki Kaisha Metal air battery module
CN112640197A (zh) * 2018-08-31 2021-04-09 夏普株式会社 金属空气电池模块
CN112640197B (zh) * 2018-08-31 2023-08-29 夏普株式会社 金属空气电池模块
CN111326757A (zh) * 2018-12-14 2020-06-23 中国科学院大连化学物理研究所 一种金属海水燃料电池组
WO2020179645A1 (fr) * 2019-03-05 2020-09-10 シャープ株式会社 Électrode négative et batterie métal-air
JPWO2020179645A1 (ja) * 2019-03-05 2021-12-23 シャープ株式会社 負極および金属空気電池
JP7223114B2 (ja) 2019-03-05 2023-02-15 シャープ株式会社 負極および金属空気電池
US11575181B2 (en) 2019-03-15 2023-02-07 Kabushiki Kaisha Toshiba Battery, battery pack, and stationary power supply
WO2020246176A1 (fr) * 2019-06-05 2020-12-10 日本碍子株式会社 Ensemble séparateur/électrode à air et batterie secondaire métal-air
JPWO2020246176A1 (fr) * 2019-06-05 2020-12-10
CN110534696A (zh) * 2019-07-29 2019-12-03 深圳大学 一种柔性电池及其制备方法
CN114391198A (zh) * 2019-09-25 2022-04-22 日本碍子株式会社 空气极／隔板接合体及锌空气二次电池
CN115298856A (zh) * 2020-01-15 2022-11-04 三钛工业有限公司 具有多个电连接器的燃料电池
CN113707840A (zh) * 2021-08-19 2021-11-26 深圳德夏科技发展有限公司 柔性电池的制作方法、柔性电池及应用

Also Published As

Publication number Publication date
JPWO2017002815A1 (ja) 2018-04-19
JP7095991B2 (ja) 2022-07-05

Similar Documents

Publication Publication Date Title
JP7095991B2 (ja) 亜鉛空気電池セルパック及びそれを用いた組電池
JP6067925B2 (ja) 亜鉛空気二次電池
KR101691338B1 (ko) 수산화물 이온 전도성 세라믹스 세퍼레이터를 이용한 이차 전지
JP6165998B2 (ja) ニッケル亜鉛電池セルパック及びそれを用いた組電池
JP6784694B2 (ja) 電極カートリッジ及びそれを用いた亜鉛二次電池
JP6723473B2 (ja) 亜鉛二次電池
JP5940237B1 (ja) 水酸化物イオン伝導性セラミックスセパレータを用いた二次電池
JP6180063B2 (ja) 電池及びその組み立て方法
JP6030780B2 (ja) 水酸化物イオン伝導性セラミックスセパレータを用いた二次電池
JPWO2016051934A1 (ja) 層状複水酸化物を用いた電池
JP6677860B2 (ja) 亜鉛二次電池用の負極構造体の製造方法
JP6313156B2 (ja) 亜鉛空気二次電池
JP6664195B2 (ja) 亜鉛二次電池
JP6580379B2 (ja) ニッケル亜鉛電池
JP2017016901A (ja) 亜鉛空気電池
JP6408878B2 (ja) 水酸化物イオン伝導性セラミックスセパレータを用いた二次電池
JP2019117780A (ja) 亜鉛二次電池用負極構造体
JP2016207631A (ja) 亜鉛空気電池及びその組み立て方法
WO2018078738A1 (fr) Batterie au nickel-zinc

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16817923

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2017526376

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16817923

Country of ref document: EP

Kind code of ref document: A1