WO2009038207A1 - Procédé pour produire une poudre de cuivre et poudre de cuivre - Google Patents

Procédé pour produire une poudre de cuivre et poudre de cuivre Download PDF

Info

Publication number
WO2009038207A1
WO2009038207A1 PCT/JP2008/067078 JP2008067078W WO2009038207A1 WO 2009038207 A1 WO2009038207 A1 WO 2009038207A1 JP 2008067078 W JP2008067078 W JP 2008067078W WO 2009038207 A1 WO2009038207 A1 WO 2009038207A1
Authority
WO
WIPO (PCT)
Prior art keywords
copper powder
slurry
oxide
copper
hydrazine
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2008/067078
Other languages
English (en)
Japanese (ja)
Inventor
Akira Aoki
Yoshinobu Nakamura
Takahiko Sakaue
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsui Kinzoku Co Ltd
Original Assignee
Mitsui Mining and Smelting Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsui Mining and Smelting Co Ltd filed Critical Mitsui Mining and Smelting Co Ltd
Priority to CN2008801074240A priority Critical patent/CN101801568B/zh
Priority to KR20107004861A priority patent/KR101510369B1/ko
Publication of WO2009038207A1 publication Critical patent/WO2009038207A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention porte sur un procédé pour produire une poudre de cuivre qui a une distribution de dimension de particules ayant une largeur extrêmement étroite et qui a une teneur en impuretés réduite ; et sur une poudre de cuivre qui est obtenue par le procédé, qui a une conductivité accrue, qui est homogène et qui a une qualité élevée. Le procédé pour la production de poudre de cuivre comprend les étapes consistant à : ajouter un agent de réduction à base d'hydrazine à une suspension de composé de sel de cuivre obtenue par addition d'une solution alcaline à une solution de sel de cuivre aqueuse pour obtenir une suspension d'oxyde de cuivre ; nettoyer la suspension d'oxyde de cuivre avec de l'eau et mettre à nouveau en suspension l'oxyde ; et ajouter un agent de réduction à base d'hydrazine à nouveau à la suspension résultante de l'oxyde de cuivre lavée. Dans ce procédé, un composé de phosphore est ajouté à la suspension de réaction avant achèvement de la réaction de réduction finale de façon à obtenir un rapport molaire phosphore/cuivre, P/Cu, se situant dans la plage de 0,0001-0,003.
PCT/JP2008/067078 2007-09-21 2008-09-22 Procédé pour produire une poudre de cuivre et poudre de cuivre Ceased WO2009038207A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN2008801074240A CN101801568B (zh) 2007-09-21 2008-09-22 铜粉的制造方法及铜粉
KR20107004861A KR101510369B1 (ko) 2007-09-21 2008-09-22 동분말의 제조 방법 및 동분말

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2007-246083 2007-09-21
JP2007246083A JP5392884B2 (ja) 2007-09-21 2007-09-21 銅粉の製造方法

Publications (1)

Publication Number Publication Date
WO2009038207A1 true WO2009038207A1 (fr) 2009-03-26

Family

ID=40468016

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2008/067078 Ceased WO2009038207A1 (fr) 2007-09-21 2008-09-22 Procédé pour produire une poudre de cuivre et poudre de cuivre

Country Status (5)

Country Link
JP (1) JP5392884B2 (fr)
KR (1) KR101510369B1 (fr)
CN (1) CN101801568B (fr)
TW (1) TWI455777B (fr)
WO (1) WO2009038207A1 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20140203222A1 (en) * 2011-05-18 2014-07-24 Toda Kogyo Corporation Copper particles, copper paste, process for producing conductive coating film, and conductive coating film
US20150266090A1 (en) * 2012-11-26 2015-09-24 Mitsui Mining & Smelting Co., Ltd. Copper powder and method for producing same
US9975110B1 (en) 2016-11-23 2018-05-22 Honda Motor Co., Ltd. Method for producing metal catalyst nanoparticles
CN110773177A (zh) * 2019-09-10 2020-02-11 安徽德诠新材料科技有限公司 一种高比表面积三元铜催化剂的制备方法
CN114786839A (zh) * 2019-11-22 2022-07-22 东邦钛株式会社 铜粉体及其制造方法
JPWO2023047990A1 (fr) * 2021-09-27 2023-03-30

Families Citing this family (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5476631B2 (ja) * 2010-03-05 2014-04-23 株式会社村田製作所 電子部品およびその製造方法
JP5531691B2 (ja) * 2010-03-16 2014-06-25 株式会社村田製作所 導電性ペーストおよびセラミック電子部品の製造方法
JP5759688B2 (ja) * 2010-08-17 2015-08-05 三井金属鉱業株式会社 扁平銅粒子
JP5820202B2 (ja) * 2010-09-30 2015-11-24 Ｄｏｗａエレクトロニクス株式会社 導電性ペースト用銅粉およびその製造方法
TWI487581B (zh) * 2010-11-12 2015-06-11 Mitsui Mining & Smelting Co Low carbon copper particles and methods for producing the same
KR101239391B1 (ko) * 2011-01-05 2013-03-05 한국지질자원연구원 입도 제어가 용이한 전자소재용 미세 구리 분말 제조 방법
JP5120477B2 (ja) * 2011-04-07 2013-01-16 日立化成工業株式会社 電極用ペースト組成物及び太陽電池
JP5785433B2 (ja) * 2011-04-28 2015-09-30 三井金属鉱業株式会社 低炭素銅粒子
JP6199430B2 (ja) * 2011-09-30 2017-09-20 Ｄｏｗａエレクトロニクス株式会社 亜酸化銅粉末およびその製造方法
JP5700864B2 (ja) * 2013-05-15 2015-04-15 石原ケミカル株式会社 銅微粒子分散液、導電膜形成方法及び回路基板
JP6303022B2 (ja) * 2014-10-03 2018-03-28 三井金属鉱業株式会社 銅粉
JP6698367B2 (ja) * 2015-03-31 2020-05-27 山陽特殊製鋼株式会社 球状粒子からなる金属粉末
US10384314B2 (en) * 2015-04-22 2019-08-20 Hitachi Metals, Ltd. Metal particle and method for producing the same, covered metal particle, and metal powder
US10773311B2 (en) * 2015-09-03 2020-09-15 Dowa Electronics Materials Co., Ltd. Phosphorus-containing copper powder and method for producing the same
JP2017179428A (ja) * 2016-03-29 2017-10-05 Ｄｏｗａエレクトロニクス株式会社 導電性材料、導電膜の形成方法、回路基板、半導体装置及び半導体装置の製造方法
CN108526490B (zh) * 2018-05-14 2021-05-25 六盘水中联工贸实业有限公司 一种用氯化铜或氯化亚铜生产金属铜粉的方法
CN112296345B (zh) * 2019-07-23 2022-02-18 富兰克科技（深圳）股份有限公司 具有长有机碳链可自分散纳米铜的制备方法、纳米铜制剂及其应用
JP7000621B1 (ja) * 2021-06-17 2022-01-19 古河ケミカルズ株式会社 銅微粒子の製造方法
CN116809921A (zh) * 2023-07-11 2023-09-29 嘉兴饶稷科技有限公司 一种纯铜光固化3d打印的高光敏活性浆料及其制备方法
WO2025070075A1 (fr) * 2023-09-28 2025-04-03 古河ケミカルズ株式会社 Poudre de cuivre et pâte conductrice
WO2025070074A1 (fr) * 2023-09-28 2025-04-03 古河ケミカルズ株式会社 Procédé de production de poudre de cuivre et procédé de production de pâte conductrice
CN117259780A (zh) * 2023-10-26 2023-12-22 有研纳微新材料(北京)有限公司 一种多面体亚微米铜粉的制备方法
CN118513560B (zh) * 2024-05-22 2025-02-18 厦门紫金新能源新材料科技有限公司 一种超细窄粒度高密度铜粉的制备方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6299406A (ja) * 1985-10-28 1987-05-08 Mitsui Mining & Smelting Co Ltd 銅粉末の製造法
JPH09256007A (ja) * 1996-03-22 1997-09-30 Murata Mfg Co Ltd 銅粉末の製造方法
JP2007169770A (ja) * 2005-12-26 2007-07-05 Mitsui Mining & Smelting Co Ltd 銅粒子並びに銅粉及びその銅粒子の製造方法

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1060108C (zh) * 1997-01-21 2001-01-03 北京化工大学 超细铜粉的制备方法
JP2911429B2 (ja) * 1997-06-04 1999-06-23 三井金属鉱業株式会社 銅微粉末の製造方法
JP3635451B2 (ja) * 1998-09-11 2005-04-06 株式会社村田製作所 金属粉末およびその製造方法ならびに導電性ペースト
KR100743844B1 (ko) * 1999-12-01 2007-08-02 도와 마이닝 가부시끼가이샤 구리 분말 및 구리 분말의 제조 방법
JP2002363618A (ja) * 2001-06-11 2002-12-18 Sumitomo Electric Ind Ltd 銅超微粒子とその製造方法
JP4868716B2 (ja) * 2004-04-28 2012-02-01 三井金属鉱業株式会社 フレーク銅粉及び導電性ペースト
JP4879473B2 (ja) * 2004-10-25 2012-02-22 三井金属鉱業株式会社 フレーク銅粉及びフレーク銅粉の製造方法並びにフレーク銅粉を含む導電性スラリー
JP4662760B2 (ja) * 2004-12-22 2011-03-30 三井金属鉱業株式会社 超微粒銅粉、超微粒銅粉スラリー及び超微粒銅粉スラリーの製造方法

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6299406A (ja) * 1985-10-28 1987-05-08 Mitsui Mining & Smelting Co Ltd 銅粉末の製造法
JPH09256007A (ja) * 1996-03-22 1997-09-30 Murata Mfg Co Ltd 銅粉末の製造方法
JP2007169770A (ja) * 2005-12-26 2007-07-05 Mitsui Mining & Smelting Co Ltd 銅粒子並びに銅粉及びその銅粒子の製造方法

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20140203222A1 (en) * 2011-05-18 2014-07-24 Toda Kogyo Corporation Copper particles, copper paste, process for producing conductive coating film, and conductive coating film
US9221979B2 (en) * 2011-05-18 2015-12-29 Toda Kogyo Corporation Copper particles, copper paste, process for producing conductive coating film, and conductive coating film
US20150266090A1 (en) * 2012-11-26 2015-09-24 Mitsui Mining & Smelting Co., Ltd. Copper powder and method for producing same
US10518323B2 (en) * 2012-11-26 2019-12-31 Mitsui Mining & Smelting Co., Ltd. Copper power and method for producing same
US9975110B1 (en) 2016-11-23 2018-05-22 Honda Motor Co., Ltd. Method for producing metal catalyst nanoparticles
CN110773177A (zh) * 2019-09-10 2020-02-11 安徽德诠新材料科技有限公司 一种高比表面积三元铜催化剂的制备方法
CN110773177B (zh) * 2019-09-10 2022-05-20 安徽德诠新材料科技有限公司 一种高比表面积三元铜催化剂的制备方法
CN114786839A (zh) * 2019-11-22 2022-07-22 东邦钛株式会社 铜粉体及其制造方法
CN114786839B (zh) * 2019-11-22 2024-03-26 东邦钛株式会社 铜粉体及其制造方法
JPWO2023047990A1 (fr) * 2021-09-27 2023-03-30
WO2023047990A1 (fr) * 2021-09-27 2023-03-30 宇部マテリアルズ株式会社 Poudre d'oxyde de magnésium, composition de vulcanisation pour caoutchouc, composition de caoutchouc, procédé de production de poudre d'oxyde de magnésium

Also Published As

Publication number Publication date
CN101801568B (zh) 2012-10-03
TWI455777B (zh) 2014-10-11
JP2009074152A (ja) 2009-04-09
KR101510369B1 (ko) 2015-04-06
KR20100071970A (ko) 2010-06-29
CN101801568A (zh) 2010-08-11
TW200932405A (en) 2009-08-01
JP5392884B2 (ja) 2014-01-22

Similar Documents

Publication Publication Date Title
WO2009038207A1 (fr) Procédé pour produire une poudre de cuivre et poudre de cuivre
TW200744954A (en) Process for production of copper powder and copper powder obtained by the process
JP2014149886A5 (fr)
CN103232055B (zh) 一种制备碱式碳酸铜的方法
CN102320644A (zh) 一种制备氧化铜粉的方法
CA2712608A1 (fr) Composition de boisson contenant une proteine soluble acide et procede pour sa production
WO2016052890A3 (fr) Procédé de préparation d'un composite de nanométal et d'un nanomatériau de carbone
CN105463203A (zh) 一种金矿低毒、高效选矿助剂及其制备方法
CN104972134B (zh) 一种用于生产超细铁粉的方法
CN103787977B (zh) 一种空气氧化制备3-氟代烷基-1-取代吡唑-4-羧酸的方法
CN106721058A (zh) 一种饲料用氨基酸微量元素螯合物
CN103737011B (zh) 高振实球形银粉的制备方法
WO2012165801A3 (fr) Complexe particulaire de cuivre destiné à l'électronique imprimée et pâte de cuivre
CN103657862B (zh) 一种胶磷矿反浮选捕收剂及其制备方法
CN104261455A (zh) 一种高纯度锡酸镧纳米粉体的制备方法
CN112371992B (zh) 核壳结构银粉的制备方法
CN102190327A (zh) 氧化亚铜的制备方法
CN103864146A (zh) 一种氧化铌纳米管的制备方法
CN100577559C (zh) 硒酸钡的生产方法
RO127465A8 (ro) Complecşi metalici ai clorhexidinei şi procedeu de obţinere a acestora
CN102603489A (zh) 一种使用炼钢废水处理过程产生的副产物硫代硫酸铵作为还原剂的用途及其使用方法
CN104071812A (zh) 一种氢氧化镁纳米粒子的制备方法
CN103739018A (zh) 一种生产四氧化三锰的方法
CN100341868C (zh) 由黄樟油合成的胡椒基丁醚的生产工艺
CN105315398A (zh) 造纸分散剂及其制备方法

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 200880107424.0

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 08832105

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 20107004861

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 08832105

Country of ref document: EP

Kind code of ref document: A1