WO2009078109A1 - Pan de verre hydrophobe, oléophobe et antisalissure, son procédé de fabrication et équipements de transport, de construction et d'optique l'utilisant - Google Patents

Pan de verre hydrophobe, oléophobe et antisalissure, son procédé de fabrication et équipements de transport, de construction et d'optique l'utilisant Download PDF

Info

Publication number
WO2009078109A1
WO2009078109A1 PCT/JP2007/074624 JP2007074624W WO2009078109A1 WO 2009078109 A1 WO2009078109 A1 WO 2009078109A1 JP 2007074624 W JP2007074624 W JP 2007074624W WO 2009078109 A1 WO2009078109 A1 WO 2009078109A1
Authority
WO
WIPO (PCT)
Prior art keywords
repellent
water
oil
soil
glass plate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2007/074624
Other languages
English (en)
Inventor
Kazufumi Ogawa
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to PCT/JP2007/074624 priority Critical patent/WO2009078109A1/fr
Publication of WO2009078109A1 publication Critical patent/WO2009078109A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne un pan de verre hydrophobe, oléophobe et antisalissure dont les propriétés hydrophobes, oléophobes et antisalissure sont améliorées, tout comme le sont ses propriétés en matière d'écoulement de l'eau (ou glissement de l'eau) et de durabilité, par exemple en termes de résistance à l'usure ou aux intempéries. L'invention concerne également son procédé de fabrication, ainsi que des équipements de transport, de construction et d'optique l'utilisant. Un pan de verre super-hydrophobe, oléophobe et antisalissure (10) est fabriqué, une de ses surfaces est revêtue de particules transparentes hydrophobes, oléophobes et antisalissure (9) fixées sur ladite surface par frittage. A cet effet, on prépare des particules transparentes (1) comportant un revêtement hydrophobe ou oléophobe (3), on les disperse dans une solution contenant de l'alcoxyde métallique, puis on applique et on laisse sécher la dispersion obtenue sur une surface d'un substrat en verre (5), suite à quoi on a recours à un traitement thermique, permettant l'obtention d'un revêtement hydrophobe, oléophobe et antisalissure (8) à la surface du substrat en verre (5), sur lequel les particules transparentes sont fixées par collage. Ce pan de verre super-hydrophobe, oléophobe et antisalissure (10) est utilisé pour des équipements de transport, de construction ou d'optique.
PCT/JP2007/074624 2007-12-17 2007-12-17 Pan de verre hydrophobe, oléophobe et antisalissure, son procédé de fabrication et équipements de transport, de construction et d'optique l'utilisant Ceased WO2009078109A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/JP2007/074624 WO2009078109A1 (fr) 2007-12-17 2007-12-17 Pan de verre hydrophobe, oléophobe et antisalissure, son procédé de fabrication et équipements de transport, de construction et d'optique l'utilisant

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/JP2007/074624 WO2009078109A1 (fr) 2007-12-17 2007-12-17 Pan de verre hydrophobe, oléophobe et antisalissure, son procédé de fabrication et équipements de transport, de construction et d'optique l'utilisant

Publications (1)

Publication Number Publication Date
WO2009078109A1 true WO2009078109A1 (fr) 2009-06-25

Family

ID=40795234

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2007/074624 Ceased WO2009078109A1 (fr) 2007-12-17 2007-12-17 Pan de verre hydrophobe, oléophobe et antisalissure, son procédé de fabrication et équipements de transport, de construction et d'optique l'utilisant

Country Status (1)

Country Link
WO (1) WO2009078109A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014058625A1 (fr) * 2012-10-12 2014-04-17 Empire Technology Development Llc Surfaces superhydrophobes et lipophobes

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH10203882A (ja) * 1997-01-21 1998-08-04 Saga Pref Gov 撥水性セラミックス
JPH1192175A (ja) * 1997-09-11 1999-04-06 Matsushita Electric Ind Co Ltd 撥水性ガラスコート膜及びその製造方法

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH10203882A (ja) * 1997-01-21 1998-08-04 Saga Pref Gov 撥水性セラミックス
JPH1192175A (ja) * 1997-09-11 1999-04-06 Matsushita Electric Ind Co Ltd 撥水性ガラスコート膜及びその製造方法

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014058625A1 (fr) * 2012-10-12 2014-04-17 Empire Technology Development Llc Surfaces superhydrophobes et lipophobes

Similar Documents

Publication Publication Date Title
JP5347124B2 (ja) 撥水撥油防汚性反射防止膜とその製造方法およびそれを形成したレンズやガラス板、ガラス、およびそれらを用いた光学装置および太陽エネルギー利用装置、ディスプレイ
JP4913844B2 (ja) 有機薄膜形成方法
JP5572803B2 (ja) 撥水撥油防汚性ガラスとその製造方法並びにそれらを用いたガラス窓、太陽エネルギー利用装置及び光学機器
KR20010034441A (ko) 반사 방지 표면용 얼룩 방지 코팅 및 이것의 제조 방법
JP5660500B2 (ja) 耐摩耗性超撥水撥油防汚性ガラスとその製造方法並びにそれらを用いたガラス窓、太陽エネルギー利用装置、光学機器および表示装置
WO2000034408A1 (fr) Article optique, procede de fabrication associe et compose organo-silicie
JP4670057B2 (ja) 撥水撥油防汚性ガラス板の製造方法
JP5347125B2 (ja) 撥水撥油防汚性反射防止膜およびその製造方法ならびにレンズ、ガラス板、ガラス、光学装置、太陽エネルギー利用装置およびディスプレイ
US9160053B2 (en) Icing and snow accretion preventive insulator, electric wire, and antenna, method for manufacturing them, and transmission line tower using them
JP5804548B2 (ja) 超撥水撥油防汚性透光性フィルムとその製造方法ならびにそれらを用いたガラス窓、太陽エネルギー利用装置、光学機器、および表示装置
JP5487418B2 (ja) 撥水撥油防汚性光反射板とその製造方法及びそれを用いたトンネル、道路標識、表示板、乗り物、建物。
JP4792575B2 (ja) 撥水性ガラス板とその製造方法及びそれを用いた乗り物またはガラス窓
JP5526393B2 (ja) 撥水撥油防汚性複合膜形成溶液とそれを用いた撥水撥油防汚性複合膜の製造方法とそれを用いた撥水撥油防汚性複合膜
US20080026163A1 (en) Treatment For Forming Waterdrop Slidable Films And Process For Forming Waterdrop Slidable Films
JP4654443B2 (ja) 太陽エネルギー利用装置の製造方法
WO2009078109A1 (fr) Pan de verre hydrophobe, oléophobe et antisalissure, son procédé de fabrication et équipements de transport, de construction et d'optique l'utilisant
US7160626B2 (en) Coated article, coating liquid composition, and method for producing coated article
JP5347123B2 (ja) 撥水撥油防汚性ガラス板およびその製造方法ならびにそれを用いた乗り物および建築物
JP5092130B2 (ja) 撥水撥油防汚性ガラス板とその製造方法及びそれを用いた自動車
US8658888B2 (en) Solar energy utilization device and method for manufacturing the same
JP5343226B2 (ja) 撥水性ガラス板、それを用いた乗り物および建築物の窓ガラス、ならびに撥水性ガラス板の製造方法
JP4929459B2 (ja) 撥水撥油防汚性ガラス板の製造方法
JP2012219003A (ja) 耐摩耗性超撥水撥油防汚性ガラスとその製造方法ならびにそれらを用いたガラス窓、太陽エネルギー利用装置、光学機器および表示装置
JP6031653B2 (ja) 撥水撥油性複合膜形成溶液とそれを用いた撥水撥油性複合膜の製造方法とその方法を用いて製造した撥水撥油性複合膜
WO2009084119A1 (fr) Appareil utilisant l'énergie solaire et son procédé de fabrication

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 07851030

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 07851030

Country of ref document: EP

Kind code of ref document: A1