WO2008116895A1 - Compositions de durcisseurs - Google Patents

Compositions de durcisseurs Download PDF

Info

Publication number
WO2008116895A1
WO2008116895A1 PCT/EP2008/053615 EP2008053615W WO2008116895A1 WO 2008116895 A1 WO2008116895 A1 WO 2008116895A1 EP 2008053615 W EP2008053615 W EP 2008053615W WO 2008116895 A1 WO2008116895 A1 WO 2008116895A1
Authority
WO
WIPO (PCT)
Prior art keywords
polyisocyanate
acid
optionally
isocyanate
compositions according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP2008/053615
Other languages
German (de)
English (en)
Inventor
Harald Schäfer
Carl Jokisch
Horst Binder
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BASF SE
Original Assignee
BASF SE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BASF SE filed Critical BASF SE
Publication of WO2008116895A1 publication Critical patent/WO2008116895A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne des compositions de durcisseurs stables au niveau de la couleur et destinées à des vernis polyuréthanne.
PCT/EP2008/053615 2007-03-27 2008-03-27 Compositions de durcisseurs Ceased WO2008116895A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP07104982.9 2007-03-27
EP07104982 2007-03-27

Publications (1)

Publication Number Publication Date
WO2008116895A1 true WO2008116895A1 (fr) 2008-10-02

Family

ID=39462042

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2008/053615 Ceased WO2008116895A1 (fr) 2007-03-27 2008-03-27 Compositions de durcisseurs

Country Status (1)

Country Link
WO (1) WO2008116895A1 (fr)

Cited By (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011061314A1 (fr) 2009-11-23 2011-05-26 Basf Se Catalyseurs pour des masses de revêtement à base de polyuréthane
US8373004B2 (en) 2007-03-27 2013-02-12 Basf Se Method for producing colorless isocyanurates of diisocyanates
WO2013060809A2 (fr) 2011-10-28 2013-05-02 Basf Se Procédé de production de polyisocyanates de diisocyanates (cyclo)aliphatiques résistants à la floculation dans les solvants
WO2013060614A1 (fr) 2011-10-28 2013-05-02 Basf Se Compositions de durcisseurs de couleur stable contenant des polyisocyanates de diisocyanates (cyclo)aliphatiques
US9617402B2 (en) 2011-10-28 2017-04-11 Basf Se Process for preparing polyisocyanates which are flocculation-stable in solvents from (cyclo)aliphatic diisocyanates
EP3305824A1 (fr) 2016-10-07 2018-04-11 Basf Se Compositions de durcisseur de couleur stable comprenant du polyisocyanate de diisocyanates (cyclo)aliphatiques
EP3305863A1 (fr) 2016-10-07 2018-04-11 Basf Se Procédé de production de polyisocyanates de diisocyanates (cyclo)aliphatiques résistants à la floculation dans les solvants
US9963538B2 (en) 2013-01-07 2018-05-08 Basf Se Catalysts for polyurethane coating compounds
EP3336118A1 (fr) 2017-09-20 2018-06-20 Basf Se Compositions d'agents de durcissement de couleur stable comprenant du polyisocyanate d'isocyanates (cyclo)aliphatiques
EP3336117A1 (fr) 2017-09-20 2018-06-20 Basf Se Procédé de fabrication de polyisocyanates de diisocyanates (cyclo)aliphatiques résistants à la floculation dans les solvants
EP3431521A1 (fr) 2017-07-20 2019-01-23 Basf Se Compositions d'agents de durcissement de couleur stable comprenant du polyisocyanate d'isocyanates (cyclo)aliphatiques
EP3286238B1 (fr) 2015-04-21 2019-03-20 Covestro Deutschland AG Mélange de polyisocyanates à base de 1,5-diisocyanatopentane
WO2021151774A1 (fr) 2020-01-30 2021-08-05 Basf Se Compositions d'agent de durcissement à couleur stable comprenant des polyisocyanates hydrodispersables
CN113396133A (zh) * 2019-02-12 2021-09-14 建筑研究和技术有限公司 用于制造聚氨酯/脲水泥混合体系的多组分组合物
CN114269805A (zh) * 2019-08-23 2022-04-01 韩华思路信(株) 制备聚异氰酸酯组合物的方法
WO2022128925A1 (fr) 2020-12-18 2022-06-23 Basf Se Compositions de durcisseur de couleur stable contenant des polyisocyanates de diisocyanates (cyclo)aliphatiques
CN114929791A (zh) * 2019-12-12 2022-08-19 米其林集团总公司 交联体系和包含所述交联体系的二烯橡胶组合物
WO2023280648A1 (fr) 2021-07-08 2023-01-12 Basf Se Formulations contenant un polyisocyanate
WO2023117989A1 (fr) 2021-12-21 2023-06-29 Basf Se Attributs environnementaux pour additifs de formulation

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3836555A (en) * 1973-04-20 1974-09-17 Goodrich Co B F Diisocyanate-organometallic catalyst solutions
US4565833A (en) * 1982-10-12 1986-01-21 Ciba-Geigy Ag Fire retardant composition
US5268393A (en) * 1992-07-17 1993-12-07 Blount David H Flame-retardant polyurethane foam produced without additional blowing agents
US5788915A (en) * 1996-09-30 1998-08-04 Blount; David H. Flame retardant compositions utilizing partially hydrolyzed amino condensation compounds

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3836555A (en) * 1973-04-20 1974-09-17 Goodrich Co B F Diisocyanate-organometallic catalyst solutions
US4565833A (en) * 1982-10-12 1986-01-21 Ciba-Geigy Ag Fire retardant composition
US5268393A (en) * 1992-07-17 1993-12-07 Blount David H Flame-retardant polyurethane foam produced without additional blowing agents
US5788915A (en) * 1996-09-30 1998-08-04 Blount; David H. Flame retardant compositions utilizing partially hydrolyzed amino condensation compounds

Cited By (38)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8373004B2 (en) 2007-03-27 2013-02-12 Basf Se Method for producing colorless isocyanurates of diisocyanates
US8709544B2 (en) 2009-11-23 2014-04-29 Basf Se Catalysts for polyurethane coating compounds
WO2011061314A1 (fr) 2009-11-23 2011-05-26 Basf Se Catalyseurs pour des masses de revêtement à base de polyuréthane
CN104024296B (zh) * 2011-10-28 2017-12-01 巴斯夫欧洲公司 包含(环)脂族二异氰酸酯的聚异氰酸酯的颜色稳定的固化组合物
CN104024296A (zh) * 2011-10-28 2014-09-03 巴斯夫欧洲公司 包含(环)脂族二异氰酸酯的聚异氰酸酯的颜色稳定的固化组合物
JP2014530944A (ja) * 2011-10-28 2014-11-20 ビーエーエスエフ ソシエタス・ヨーロピアＢａｓｆ Ｓｅ （環式）脂肪族ジイソシアナートのポリイソシアナートを含む色安定性の硬化剤組成物
US9617402B2 (en) 2011-10-28 2017-04-11 Basf Se Process for preparing polyisocyanates which are flocculation-stable in solvents from (cyclo)aliphatic diisocyanates
CN107815087A (zh) * 2011-10-28 2018-03-20 巴斯夫欧洲公司 包含(环)脂族二异氰酸酯的聚异氰酸酯的颜色稳定的固化组合物
WO2013060614A1 (fr) 2011-10-28 2013-05-02 Basf Se Compositions de durcisseurs de couleur stable contenant des polyisocyanates de diisocyanates (cyclo)aliphatiques
WO2013060809A2 (fr) 2011-10-28 2013-05-02 Basf Se Procédé de production de polyisocyanates de diisocyanates (cyclo)aliphatiques résistants à la floculation dans les solvants
CN107815087B (zh) * 2011-10-28 2023-02-28 巴斯夫欧洲公司 包含(环)脂族二异氰酸酯的聚异氰酸酯的颜色稳定的固化组合物
US9963538B2 (en) 2013-01-07 2018-05-08 Basf Se Catalysts for polyurethane coating compounds
EP3286238B1 (fr) 2015-04-21 2019-03-20 Covestro Deutschland AG Mélange de polyisocyanates à base de 1,5-diisocyanatopentane
EP3305824A1 (fr) 2016-10-07 2018-04-11 Basf Se Compositions de durcisseur de couleur stable comprenant du polyisocyanate de diisocyanates (cyclo)aliphatiques
WO2018065344A1 (fr) 2016-10-07 2018-04-12 Basf Se Compositions de durcisseurs de couleur stable contenant des polyisocyanates de diisocyanates (cyclo)aliphatiques
US11807709B2 (en) 2016-10-07 2023-11-07 Basf Se Method for producing polyisocyanates of (cyclo)aliphatic diisocyanates which are flocculation-stable in solvents
WO2018065343A1 (fr) 2016-10-07 2018-04-12 Basf Se Procédé de production de polyisocyanates de diisocyanates (cyclo)aliphatiques résistants à la floculation dans les solvants.
US11001730B2 (en) 2016-10-07 2021-05-11 Basf Se Colour-stable curing compositions containing polyisocyanates of (cyclo)aliphatic diisocyanates
EP3305863A1 (fr) 2016-10-07 2018-04-11 Basf Se Procédé de production de polyisocyanates de diisocyanates (cyclo)aliphatiques résistants à la floculation dans les solvants
WO2019016097A1 (fr) 2017-07-20 2019-01-24 Basf Se Compositions de durcisseurs de couleur stable contenant des polyisocyanates de diisocyanates (cyclo)aliphatiques
CN110914327A (zh) * 2017-07-20 2020-03-24 巴斯夫欧洲公司 包含脂(环)族二异氰酸酯的多异氰酸酯的颜色稳定的固化组合物
EP3431521A1 (fr) 2017-07-20 2019-01-23 Basf Se Compositions d'agents de durcissement de couleur stable comprenant du polyisocyanate d'isocyanates (cyclo)aliphatiques
CN110914327B (zh) * 2017-07-20 2023-08-22 巴斯夫欧洲公司 包含脂(环)族二异氰酸酯的多异氰酸酯的颜色稳定的固化组合物
US11624003B2 (en) 2017-09-20 2023-04-11 Basf Se Colour-stable curing compositions containing polyisocyanates of (cyclo)aliphatic diisocyanates
WO2019057539A1 (fr) 2017-09-20 2019-03-28 Basf Se Compositions de durcisseurs de couleur stable contenant des polyisocyanates de diisocyanates (cyclo)aliphatiques
EP3336118A1 (fr) 2017-09-20 2018-06-20 Basf Se Compositions d'agents de durcissement de couleur stable comprenant du polyisocyanate d'isocyanates (cyclo)aliphatiques
WO2019057540A1 (fr) 2017-09-20 2019-03-28 Basf Se Procédé de production de polyisocyanates de diisocyanates (cyclo)aliphatiques résistants à la floculation dans les solvants
US11542356B2 (en) 2017-09-20 2023-01-03 Basf Se Method for producing polyisocyanates of (cyclo)aliphatic diisocyanates which are flocculation-stable in solvents
EP3336117A1 (fr) 2017-09-20 2018-06-20 Basf Se Procédé de fabrication de polyisocyanates de diisocyanates (cyclo)aliphatiques résistants à la floculation dans les solvants
CN113396133A (zh) * 2019-02-12 2021-09-14 建筑研究和技术有限公司 用于制造聚氨酯/脲水泥混合体系的多组分组合物
CN113396133B (zh) * 2019-02-12 2023-09-22 Sika技术股份公司 用于制造聚氨酯/脲水泥混合体系的多组分组合物
CN114269805A (zh) * 2019-08-23 2022-04-01 韩华思路信(株) 制备聚异氰酸酯组合物的方法
CN114929791A (zh) * 2019-12-12 2022-08-19 米其林集团总公司 交联体系和包含所述交联体系的二烯橡胶组合物
CN114929791B (zh) * 2019-12-12 2023-11-24 米其林集团总公司 交联体系和包含所述交联体系的二烯橡胶组合物
WO2021151774A1 (fr) 2020-01-30 2021-08-05 Basf Se Compositions d'agent de durcissement à couleur stable comprenant des polyisocyanates hydrodispersables
WO2022128925A1 (fr) 2020-12-18 2022-06-23 Basf Se Compositions de durcisseur de couleur stable contenant des polyisocyanates de diisocyanates (cyclo)aliphatiques
WO2023280648A1 (fr) 2021-07-08 2023-01-12 Basf Se Formulations contenant un polyisocyanate
WO2023117989A1 (fr) 2021-12-21 2023-06-29 Basf Se Attributs environnementaux pour additifs de formulation

Similar Documents

Publication Publication Date Title
WO2008116895A1 (fr) Compositions de durcisseurs
EP2139939A1 (fr) Compositions de durcisseurs
WO2008116893A1 (fr) Compositions de durcisseurs
EP2771376B1 (fr) Compositions de durcisseurs de couleur stable contenant des polyisocyanates de diisocyanates (cyclo)aliphatiques
EP2773612B1 (fr) Procédé de production de polyisocyanates de diisocyanates (cyclo)aliphatiques résistants à la floculation dans les solvants
EP3523347B1 (fr) Compositions de durcisseur de couleur stable comprenant du polyisocyanate de diisocyanates (cyclo)aliphatiques
EP2941446B1 (fr) Catalyseurs pour matières de revêtement à base de polyuréthane
EP2220035B1 (fr) Polyisocyanates contenant des groupes allophanate
US20130109806A1 (en) Color-stable curing agent compositions comprising polyisocyanates of (cyclo)aliphatic diisocyanates
EP3431521A1 (fr) Compositions d'agents de durcissement de couleur stable comprenant du polyisocyanate d'isocyanates (cyclo)aliphatiques
DE102008054974A1 (de) Zweikomponentige Polyurethanbeschichtungsmassen
EP3684835B1 (fr) Compositions d'agents de durcissement de couleur stable comprenant du polyisocyanate d'isocyanates (cyclo)aliphatiques
EP3336117A1 (fr) Procédé de fabrication de polyisocyanates de diisocyanates (cyclo)aliphatiques résistants à la floculation dans les solvants
EP2205655A1 (fr) Polyisocyanates contenant des groupes uréthane
JP2023553750A (ja) （シクロ）脂肪族ジイソシアネートのポリイソシアネートを含む色安定性硬化剤組成物
EP3523387B1 (fr) Procédé de production de polyisocyanates de diisocyanates (cyclo)aliphatiques résistants à la floculation dans les solvants
JP2023513071A (ja) 水分散性ポリイソシアネートを含む色安定硬化剤組成物

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 08735506

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 08735506

Country of ref document: EP

Kind code of ref document: A1