WO2007133050A1 - Procédé de production de fonte liquide par l'injection d'un gaz hydrocarboné et appareil de production de fonte liquide associé - Google Patents

Procédé de production de fonte liquide par l'injection d'un gaz hydrocarboné et appareil de production de fonte liquide associé Download PDF

Info

Publication number
WO2007133050A1
WO2007133050A1 PCT/KR2007/002403 KR2007002403W WO2007133050A1 WO 2007133050 A1 WO2007133050 A1 WO 2007133050A1 KR 2007002403 W KR2007002403 W KR 2007002403W WO 2007133050 A1 WO2007133050 A1 WO 2007133050A1
Authority
WO
WIPO (PCT)
Prior art keywords
gas containing
melter
gasifier
gas
containing oxygen
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/KR2007/002403
Other languages
English (en)
Inventor
Eung-Soo Choi
Nam-Suk Hur
Jin-Chan Bae
Hoo-Geun Lee
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Posco Holdings Inc
Original Assignee
Posco Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Posco Co Ltd filed Critical Posco Co Ltd
Priority to CN2007800178286A priority Critical patent/CN101448962B/zh
Publication of WO2007133050A1 publication Critical patent/WO2007133050A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne un procédé de production de fonte liquide par l'injection d'un gaz contenant des hydrocarbures, et un appareil de production de fonte liquide faisant appel audit procédé. Le procédé de production de fonte liquide selon l'invention consiste : à réduire du minerai de fer dans un réacteur de réduction, et à convertir le minerai de fer en matières réduites; à charger les matières carbonées en morceaux dans un dispositif de fusion-gazéification relié au réacteur de réduction, et à former un lit fixe de charbon; à injecter un gaz contenant de l'oxygène dans le lit fixe de charbon et à former une canalisation; à procéder à la combustion des matières carbonées en morceaux dans la canalisation, et à générer un gaz réducteur; à injecter directement le gaz contenant des hydrocarbures dans la canalisation après avoir formé cette dernière puis à poursuivre la génération du gaz réducteur; à charger les matières réduites dans le dispositif de fusion-gazéification; à mettre les matières réduites en contact avec le gaz réducteur; et à fondre les matières réduites.
PCT/KR2007/002403 2006-05-17 2007-05-17 Procédé de production de fonte liquide par l'injection d'un gaz hydrocarboné et appareil de production de fonte liquide associé Ceased WO2007133050A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
CN2007800178286A CN101448962B (zh) 2006-05-17 2007-05-17 通过注入含烃气体制造铁水的方法和使用该方法制造铁水的设备

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
KR1020060044344A KR100972195B1 (ko) 2006-05-17 2006-05-17 탄화수소 함유가스 취입에 의한 용철제조방법 및 이를이용한 용철제조장치
KR10-2006-0044344 2006-05-17

Publications (1)

Publication Number Publication Date
WO2007133050A1 true WO2007133050A1 (fr) 2007-11-22

Family

ID=38694106

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2007/002403 Ceased WO2007133050A1 (fr) 2006-05-17 2007-05-17 Procédé de production de fonte liquide par l'injection d'un gaz hydrocarboné et appareil de production de fonte liquide associé

Country Status (3)

Country Link
KR (1) KR100972195B1 (fr)
CN (1) CN101448962B (fr)
WO (1) WO2007133050A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
LU91543B1 (en) * 2009-03-24 2010-09-27 Wurth Paul Sa Tuyere stock arrangement for a blast furnace and method for operating a blast furnace
CN102378818A (zh) * 2009-01-30 2012-03-14 西门子Vai金属科技有限责任公司 用于制造生铁或液态钢半成品的方法和设备
US8540931B2 (en) 2008-11-28 2013-09-24 Siemens Vai Metals Technologies Gmbh Nozzle for injecting gas containing oxygen into a pig iron device having an injector insertion pipe
US8911700B2 (en) 2009-02-20 2014-12-16 Siemens Vai Metals Technologies Gmbh Process and installation for producing substitute gas

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101431041B1 (ko) * 2013-08-12 2014-08-19 주식회사 포스코 천연가스 취입장치 및 천연가스 취입방법
DE102015008090A1 (de) * 2015-06-25 2016-12-29 Bogdan Vuletic Verfahren und Anlage zum Betreiben einer Corex - oder Finex-Anlage
KR102083539B1 (ko) * 2017-08-23 2020-04-23 주식회사 포스코 용선 제조 설비 및 용선 제조 방법
CN114134271B (zh) * 2021-12-03 2022-12-06 昌黎县兴国精密机件有限公司 一种高炉低碳冶炼的喷吹调控装置及方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5534046A (en) * 1992-10-22 1996-07-09 Voest-Alpine Industrieanlagenbau Gmbh Process for producing molten pig iron or molten steel pre-products
WO1998035064A1 (fr) * 1997-02-11 1998-08-13 Voest-Alpine Industrieanlagenbau Gmbh Procede de production de fonte brute liquide ou de produits de depart liquides en acier
KR19990077105A (ko) * 1996-11-08 1999-10-25 포항 아이런 앤드 스틸 씨오. 엘티디. 철함유 물질로부터 액체선철 즉 철강반제품을 생산하는 방법
KR20050089836A (ko) * 2002-12-23 2005-09-08 주식회사 포스코 유동환원로 조업을 개선한 용철제조장치 및 그용철제조방법

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5534046A (en) * 1992-10-22 1996-07-09 Voest-Alpine Industrieanlagenbau Gmbh Process for producing molten pig iron or molten steel pre-products
KR19990077105A (ko) * 1996-11-08 1999-10-25 포항 아이런 앤드 스틸 씨오. 엘티디. 철함유 물질로부터 액체선철 즉 철강반제품을 생산하는 방법
WO1998035064A1 (fr) * 1997-02-11 1998-08-13 Voest-Alpine Industrieanlagenbau Gmbh Procede de production de fonte brute liquide ou de produits de depart liquides en acier
KR20050089836A (ko) * 2002-12-23 2005-09-08 주식회사 포스코 유동환원로 조업을 개선한 용철제조장치 및 그용철제조방법

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8540931B2 (en) 2008-11-28 2013-09-24 Siemens Vai Metals Technologies Gmbh Nozzle for injecting gas containing oxygen into a pig iron device having an injector insertion pipe
CN102378818A (zh) * 2009-01-30 2012-03-14 西门子Vai金属科技有限责任公司 用于制造生铁或液态钢半成品的方法和设备
US8968441B2 (en) 2009-01-30 2015-03-03 Siemens Vai Metals Technologies Gmbh Method and system for producing pig iron or fluid steel pre-products
CN102378818B (zh) * 2009-01-30 2015-09-23 西门子Vai金属科技有限责任公司 用于制造生铁或液态钢半成品的方法和设备
US8911700B2 (en) 2009-02-20 2014-12-16 Siemens Vai Metals Technologies Gmbh Process and installation for producing substitute gas
LU91543B1 (en) * 2009-03-24 2010-09-27 Wurth Paul Sa Tuyere stock arrangement for a blast furnace and method for operating a blast furnace
WO2010108880A3 (fr) * 2009-03-24 2010-12-16 Paul Wurth S.A. Agencement de bras de tuyère pour haut fourneau, et procédé d'alimentation en gaz chauds dans un haut fourneau
CN102348813A (zh) * 2009-03-24 2012-02-08 保尔伍斯股份有限公司 用于鼓风炉的风口弯头装置以及将热鼓风供给至鼓风炉内的方法
JP2012521492A (ja) * 2009-03-24 2012-09-13 ポール ヴルス エス．エイ． 高炉に用いる羽口支持構造体装置、及び高炉への熱風送り込み方法
US8945463B2 (en) 2009-03-24 2015-02-03 Paul Wurth S.A. Tuyere stock arrangement for a blast furnace and method for feeding hot blast into a blast furnace
AU2010227583B2 (en) * 2009-03-24 2015-08-20 Paul Wurth S.A. Tuyere stock arrangement for a blast furnace and method for feeding hot blast into a blast furnace

Also Published As

Publication number Publication date
CN101448962A (zh) 2009-06-03
KR100972195B1 (ko) 2010-07-23
CN101448962B (zh) 2011-05-11
KR20070111230A (ko) 2007-11-21

Similar Documents

Publication Publication Date Title
LU500699B1 (en) Method for operating a shaft furnace plant
EP2350324B1 (fr) Procédé d exploitation d un haut-fourneau
CN102459654B (zh) 生产铁、半钢和还原气体的装置及方法
KR20230006894A (ko) 침탄된 해면철을 제조하는 방법
WO2007133050A1 (fr) Procédé de production de fonte liquide par l'injection d'un gaz hydrocarboné et appareil de production de fonte liquide associé
CN102037145B (zh) 通过加入碳氢化合物再循环高炉煤气而熔炼生铁的工艺
TWI864000B (zh) 用於操作高爐的方法
WO2015088092A1 (fr) Procédé et appareil de fabrication de fer en fusion
CN102586528A (zh) 一种天然气熔融还原炼铁新工艺
ES3033717T3 (en) Bleed-off gas recovery in a direct reduction process
KR101009031B1 (ko) 연료취입장치 및 이를 포함하는 용철제조장치
EP3868899B1 (fr) Appareil de fabrication de fer fondu avec émissions réduites de dioxyde de carbone et procédé de fabrication associé
US5558696A (en) Method of direct steel making from liquid iron
US20050151307A1 (en) Method and apparatus for producing molten iron
KR101481126B1 (ko) 용철 제조장치
KR101235252B1 (ko) 탄화수소 함유가스 취입에 의한 용철제조방법 및 이를이용한 용철제조장치
KR100803983B1 (ko) 용철제조장치 및 용철제조방법
KR20250161578A (ko) 고로의 조업 방법 및 부대 설비
JP2666396B2 (ja) 溶銑の製造方法
JP2025176150A (ja) 直接還元反応器を含むプラントの運転方法
WO2024209801A1 (fr) Procédé de fonctionnement de haut-fourneau et équipement auxiliaire
JPS58171514A (ja) 銑鉄の製造方法及びその装置
JPH0581641B2 (fr)
JPS59116308A (ja) 銑鉄の製造方法および装置

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 200780017828.6

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 07746551

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 2493/MUMNP/2008

Country of ref document: IN

122 Ep: pct application non-entry in european phase

Ref document number: 07746551

Country of ref document: EP

Kind code of ref document: A1