WO2007100673A2 - moule composite avec renfort de métal volatil - Google Patents

moule composite avec renfort de métal volatil Download PDF

Info

Publication number
WO2007100673A2
WO2007100673A2 PCT/US2007/004750 US2007004750W WO2007100673A2 WO 2007100673 A2 WO2007100673 A2 WO 2007100673A2 US 2007004750 W US2007004750 W US 2007004750W WO 2007100673 A2 WO2007100673 A2 WO 2007100673A2
Authority
WO
WIPO (PCT)
Prior art keywords
mold
region
mold region
alloy
backup
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2007/004750
Other languages
English (en)
Other versions
WO2007100673A3 (fr
Inventor
George W. Wolter
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Howmet Corp
Original Assignee
Howmet Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Howmet Corp filed Critical Howmet Corp
Publication of WO2007100673A2 publication Critical patent/WO2007100673A2/fr
Anticipated expiration legal-status Critical
Publication of WO2007100673A3 publication Critical patent/WO2007100673A3/fr
Ceased legal-status Critical Current

Abstract

L'invention concerne un moule composite pour une utilisation dans le coulage d'un métal ou d'un alliage comportant une région de moule interne englobant une cavité de moule et une région de moule de renfort externe métallique volatil résidant sur la région de moule interne, caractérisé en ce que le matériau métallique de la région de moule de renfort possède une température de fusion telle que la région de moule de renfort fond à partir de la région de moule interne après coulage du métal en fusion ou de l'alliage et solidification au moins partielle de celui-ci dans le moule. La région de moule interne peut comprendre un moule à coquille non métallique réfractaire ou céramique, tandis que la région de moule de renfort peut comprendre de l'étain ou tout autre métal ou alliage à point de fusion relativement bas.
PCT/US2007/004750 2006-02-27 2007-02-22 moule composite avec renfort de métal volatil Ceased WO2007100673A2 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US11/363,518 2006-02-27
US11/363,518 US20070199676A1 (en) 2006-02-27 2006-02-27 Composite mold with fugitive metal backup

Publications (2)

Publication Number Publication Date
WO2007100673A2 true WO2007100673A2 (fr) 2007-09-07
WO2007100673A3 WO2007100673A3 (fr) 2008-08-28

Family

ID=38442888

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2007/004750 Ceased WO2007100673A2 (fr) 2006-02-27 2007-02-22 moule composite avec renfort de métal volatil

Country Status (2)

Country Link
US (1) US20070199676A1 (fr)
WO (1) WO2007100673A2 (fr)

Families Citing this family (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
SG154346A1 (en) * 2008-01-10 2009-08-28 Turbine Overhaul Services Pte System and method for restoring metal components
US8858697B2 (en) 2011-10-28 2014-10-14 General Electric Company Mold compositions
US9011205B2 (en) 2012-02-15 2015-04-21 General Electric Company Titanium aluminide article with improved surface finish
US8932518B2 (en) 2012-02-29 2015-01-13 General Electric Company Mold and facecoat compositions
US8906292B2 (en) 2012-07-27 2014-12-09 General Electric Company Crucible and facecoat compositions
US8708033B2 (en) 2012-08-29 2014-04-29 General Electric Company Calcium titanate containing mold compositions and methods for casting titanium and titanium aluminide alloys
US8992824B2 (en) 2012-12-04 2015-03-31 General Electric Company Crucible and extrinsic facecoat compositions
US9592548B2 (en) 2013-01-29 2017-03-14 General Electric Company Calcium hexaluminate-containing mold and facecoat compositions and methods for casting titanium and titanium aluminide alloys
US9192983B2 (en) 2013-11-26 2015-11-24 General Electric Company Silicon carbide-containing mold and facecoat compositions and methods for casting titanium and titanium aluminide alloys
US9511417B2 (en) 2013-11-26 2016-12-06 General Electric Company Silicon carbide-containing mold and facecoat compositions and methods for casting titanium and titanium aluminide alloys
US10391547B2 (en) 2014-06-04 2019-08-27 General Electric Company Casting mold of grading with silicon carbide
US11007567B2 (en) * 2016-08-04 2021-05-18 Ube Machinery Corporation, Ltd. Die casting machine

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6766850B2 (en) * 2001-12-27 2004-07-27 Caterpillar Inc Pressure casting using a supported shell mold

Also Published As

Publication number Publication date
WO2007100673A3 (fr) 2008-08-28
US20070199676A1 (en) 2007-08-30

Similar Documents

Publication Publication Date Title
WO2007100673A2 (fr) moule composite avec renfort de métal volatil
EP1797978A2 (fr) Coulée sous pression dans un moule de précision
US9381569B2 (en) Vacuum or air casting using induction hot topping
US5335711A (en) Process and apparatus for metal casting
EP0748264B1 (fr) Moulage de fonte reactive en coquille
EP0897769B1 (fr) Four de coulée sur vide avec un chauffage de moule
EP1797977A2 (fr) Coulée sous pression dans un moule de précision
AU2021100090A4 (en) ICS- Counter Gravity Casting: Intelligent Centrifugal Counter Gravity Low- cost Casting System
US3635791A (en) Pressure pouring in a vacuum environment
EP0356624A2 (fr) Suspension active de véhicule automabile avec commande en fonction de l'angle de dérive pour améliorer la réponse de la direction
US6019158A (en) Investment casting using pour cup reservoir with inverted melt feed gate
EP0293960B1 (fr) Procédé et dispositif pour la coulée du métal
EP2450131B1 (fr) Unité de fonte pour système de moulage
WO2010078201A1 (fr) Moulage en sable basse pression d'éléments de moteur à cylindres en alliage d'aluminium
EP1082187B1 (fr) Moulage a modele perdu a l'aide d'un bouchon de pression
EP1101551B1 (fr) Moulage à modèle perdu avec bassin de coulée formant une boucle inversée
Lampman Permanent mold casting of aluminum alloys
US20020104639A1 (en) Investment casting with improved melt feeding
Mandal Near net shape casting through investment, die and centrifugal casting
RU2513672C2 (ru) Устройство для изготовления моделей поршня
Woycik et al. Low-Pressure Metal Casting
HK1196332A (en) Vacuum or air casting using induction hot topping
Turkselci METAL CASTING PROCESSES
Kim Development of a novel casting technique for the production of aluminium metal matrix composite (MMC) castings

Legal Events

Date Code Title Description
NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 07751506

Country of ref document: EP

Kind code of ref document: A2