WO2006067036A1 - Installation de laminage direct d'une bande metallique, procede de production d'une bande metallique et bande metallique - Google Patents

Installation de laminage direct d'une bande metallique, procede de production d'une bande metallique et bande metallique Download PDF

Info

Publication number
WO2006067036A1
WO2006067036A1 PCT/EP2005/056534 EP2005056534W WO2006067036A1 WO 2006067036 A1 WO2006067036 A1 WO 2006067036A1 EP 2005056534 W EP2005056534 W EP 2005056534W WO 2006067036 A1 WO2006067036 A1 WO 2006067036A1
Authority
WO
WIPO (PCT)
Prior art keywords
metal strip
casting
rolling
hot
cast
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP2005/056534
Other languages
German (de)
English (en)
Inventor
Hans-Herbert Welker
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Siemens AG
Siemens Corp
Original Assignee
Siemens AG
Siemens Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Siemens AG, Siemens Corp filed Critical Siemens AG
Priority to EP05819149A priority Critical patent/EP1827733A1/fr
Priority to US11/793,190 priority patent/US20080006387A1/en
Publication of WO2006067036A1 publication Critical patent/WO2006067036A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne une installation de laminage direct d'une bande métallique (7) et comprenant un dispositif de coulée (1), un dispositif de laminage à chaud (2) en aval de ce dernier et une section de refroidissement (3) en aval de cette dernière. Dans le dispositif de coulée (1), un métal liquide (6) est coulé en bande métallique (7) d'une épaisseur initiale (d1). Juste après la coulée à une épaisseur initiale (d1), la bande métallique (7) coulée est cédée au dispositif de laminage à chaud (2) où elle est laminée. La bande métallique (7) laminée à chaud est ensuite refroidie dans la section de refroidissement (3) avec un agent de refroidissement (8). L'installation de laminage direct présente un boîtier (4) qui entoure le dispositif de coulée (1), le dispositif de laminage à chaud (2) et la section de refroidissement (3) et peut être rempli d'un gaz protecteur. La bande métallique (7) peut ainsi être guidée au moins de la sortie du dispositif de coulée (1) jusqu'à la sortie de la section de refroidissement (3) dans un boîtier (4) rempli d'un gaz protecteur.
PCT/EP2005/056534 2004-12-22 2005-12-06 Installation de laminage direct d'une bande metallique, procede de production d'une bande metallique et bande metallique Ceased WO2006067036A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
EP05819149A EP1827733A1 (fr) 2004-12-22 2005-12-06 Installation de laminage direct d'une bande metallique, procede de production d'une bande metallique et bande metallique
US11/793,190 US20080006387A1 (en) 2004-12-22 2005-12-06 Continuous Casting and Rolling Plant for a Metal Strip, Production Method for a Metal Strip, and a Metal Strip Itself

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE102004061939.5 2004-12-22
DE102004061939A DE102004061939B3 (de) 2004-12-22 2004-12-22 Gießwalzanlage für ein Metallband, Erzeugungsverfahren für ein Metallband und Metallband selbst

Publications (1)

Publication Number Publication Date
WO2006067036A1 true WO2006067036A1 (fr) 2006-06-29

Family

ID=36027173

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2005/056534 Ceased WO2006067036A1 (fr) 2004-12-22 2005-12-06 Installation de laminage direct d'une bande metallique, procede de production d'une bande metallique et bande metallique

Country Status (7)

Country Link
US (1) US20080006387A1 (fr)
EP (1) EP1827733A1 (fr)
CN (1) CN101087667A (fr)
DE (1) DE102004061939B3 (fr)
RU (1) RU2368437C2 (fr)
UA (1) UA87175C2 (fr)
WO (1) WO2006067036A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019068444A1 (fr) * 2017-10-03 2019-04-11 Primetals Technologies Austria GmbH Procédé pour faire fonctionner une installation combinée de coulée et de laminage

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE102011090098A1 (de) 2011-12-29 2013-07-04 Sms Siemag Ag Verfahren und Vorrichtung zum Walzen von Walzgut sowie Verwendung eines Kühlschmierstoffes
EP2769779A1 (fr) 2013-02-22 2014-08-27 Siemens VAI Metals Technologies GmbH Installation et méthode de laminage d'une bande métallique
CN104722577A (zh) * 2013-12-23 2015-06-24 宝山钢铁股份有限公司 一种连续轧制生产工艺及工艺布置
CN107138528A (zh) * 2017-05-03 2017-09-08 广东金世纪高新材料有限公司 一种铝窄带的生产工艺
CN108356076A (zh) * 2018-01-18 2018-08-03 河钢股份有限公司承德分公司 一种连铸坯轧制方法
JP7040340B2 (ja) * 2018-07-26 2022-03-23 日本製鉄株式会社 連続鋳造設備及び圧延方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3506597A1 (de) * 1984-03-01 1985-09-05 Fujikura Ltd., Tokio/Tokyo Verfahren zur kontinuierlichen drahtherstellung
US4791979A (en) * 1986-07-18 1988-12-20 Allied-Signal Inc. Gas assisted nozzle for casting metallic strip directly from the melt
JPH01130802A (ja) * 1987-11-14 1989-05-23 Kobe Steel Ltd 難加工材の薄板連続製造法
US5043029A (en) * 1983-04-11 1991-08-27 Allied-Signal Inc. Casting in a exothermic reduction atmosphere
US5816311A (en) * 1995-12-22 1998-10-06 Ishikawajima-Harima Heavy Industries Company Limited Twin roll continuous caster

Family Cites Families (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4783314A (en) * 1987-02-26 1988-11-08 Nalco Chemical Company Fluorescent tracers - chemical treatment monitors
DE69032504T2 (de) * 1989-12-11 1999-01-14 Comalco Aluminium Ltd., Melbourne, Victoria Kontrolliertes vergiessen übereutektischer aluminium-silizium-legierungen
US5904204A (en) * 1995-04-14 1999-05-18 Nippon Steel Corporation Apparatus for producing strip of stainless steel
AUPQ436299A0 (en) * 1999-12-01 1999-12-23 Bhp Steel (Jla) Pty Limited Casting steel strip
US6517602B2 (en) * 2000-03-14 2003-02-11 Hitachi Metals, Ltd Solder ball and method for producing same
JP4542247B2 (ja) * 2000-08-08 2010-09-08 キャストリップ・リミテッド・ライアビリティ・カンパニー ストリップ連続鋳造装置及びその使用方法
DE10156034B4 (de) * 2001-11-15 2012-05-03 Techmag Ag Vorrichtung zur Herstellung von Profilen oder Blechformteilen aus Magnesium oder Magnesiumlegierungen
DE10310357A1 (de) * 2003-03-10 2004-09-30 Siemens Ag Gießwalzanlage zur Erzeugen eines Stahlbandes

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5043029A (en) * 1983-04-11 1991-08-27 Allied-Signal Inc. Casting in a exothermic reduction atmosphere
DE3506597A1 (de) * 1984-03-01 1985-09-05 Fujikura Ltd., Tokio/Tokyo Verfahren zur kontinuierlichen drahtherstellung
US4791979A (en) * 1986-07-18 1988-12-20 Allied-Signal Inc. Gas assisted nozzle for casting metallic strip directly from the melt
JPH01130802A (ja) * 1987-11-14 1989-05-23 Kobe Steel Ltd 難加工材の薄板連続製造法
US5816311A (en) * 1995-12-22 1998-10-06 Ishikawajima-Harima Heavy Industries Company Limited Twin roll continuous caster

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
PATENT ABSTRACTS OF JAPAN vol. 013, no. 376 (M - 862) 21 August 1989 (1989-08-21) *

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019068444A1 (fr) * 2017-10-03 2019-04-11 Primetals Technologies Austria GmbH Procédé pour faire fonctionner une installation combinée de coulée et de laminage
CN111148581A (zh) * 2017-10-03 2020-05-12 首要金属科技奥地利有限责任公司 用于运行铸轧复合设备的方法和铸轧复合设备
CN111148581B (zh) * 2017-10-03 2022-06-28 首要金属科技奥地利有限责任公司 用于运行铸轧复合设备的方法和铸轧复合设备

Also Published As

Publication number Publication date
EP1827733A1 (fr) 2007-09-05
US20080006387A1 (en) 2008-01-10
RU2007128051A (ru) 2009-01-27
CN101087667A (zh) 2007-12-12
RU2368437C2 (ru) 2009-09-27
DE102004061939B3 (de) 2006-08-03
UA87175C2 (ru) 2009-06-25

Similar Documents

Publication Publication Date Title
DE4402402B4 (de) Verfahren zur Herstellung von warmgewalztem Stahlband aus stranggegossenem Vormaterial und Anlage zur Durchführung des Verfahrens
DE69102280T2 (de) Verfahren und anlage zum herstellen von direkt einer warmwalzstrasse erzeugter stahlbandcoils mit kaltwalzeigenschaften.
EP2035587B1 (fr) Procédé et dispositif de production de matériau de laminage de feuillards à chaud en acier au silicium à base de brames fines
EP0804300B1 (fr) Procede et dispositif de production d'une feuille d'acier presentant les proprietes d'un produit lamine a froid
EP3504013B2 (fr) Procédé de fabrication d'une bande métallique dans une installation de laminage direct
EP2428288B1 (fr) Procédé de fabrication de bandes en acier par laminage continu ou semi-laminage continu
EP2603337B1 (fr) Procédé de production de laminés à l'aide d'une installation combinée de laminage direct, dispositif de commande et/ou de régulation pour une installation combinée de laminage direct, et installation combinée de laminage direct
EP0326190A2 (fr) Installation pour fabriquer un feuillard d'acier ayant une épaisseur située entre 2 et 25 mm
EP1519798B1 (fr) Procede et installation de laminage de coulee continue pour le laminage semi-continu ou continu par coulee d'une barre de metal, en particulier d'acier, separee transversalement selon le besoin apres solidification
EP1305122A1 (fr) Procede et installation de fabrication de produits plats minces
AT504782A4 (de) Verfahren zur herstellung eines warmgewalzten stahlbandes und kombinierte giess- und walzanlage zur durchführung des verfahrens
EP3558563B1 (fr) Procede de fabrication de bandes bobinees sans fin laminees a chaud dans une installation combinee de coulee et de laminage, et installation combinee de coulee et de laminage
EP4003623A1 (fr) Fabrication d'une bande d'acier pouvant être emboutie dans une installation combinée de coulée et de laminage
EP2651578B2 (fr) Train de laminoir pour la production d'acier tubulaire et de bandes minces
EP3341142B1 (fr) Procédé de fonctionnement d'une installation fonctionnant suivant le concept csp (compact strip production)
WO2006067036A1 (fr) Installation de laminage direct d'une bande metallique, procede de production d'une bande metallique et bande metallique
DE102013212951A1 (de) Gießwalzanlage und Verfahren zum Herstellen von metallischem Walzgut
WO2016165933A1 (fr) Installation de coulée et de laminage et procédé servant à faire fonctionner ladite installation
DE4009860C2 (de) Verfahren und Anlage zur Herstellung von warmgewalztem Stahlband, insbesondere für Edelstähle, aus bandförmig stranggegossenem Vormaterial
AT525563B1 (de) Trockengiessen in einer giess-walz-verbundanlage
DE102013214940A1 (de) Gießwalzanlage und Verfahren zum Herstellen von Brammen
AT525283B1 (de) Verfahren zur Herstellung eines Dualphasenstahlbands in einer Gieß-Walz-Verbundanlage, ein mit dem Verfahren hergestelltes Dualphasenstahlband und eine Gieß-Walz-Verbundanlage
DE102015223600A1 (de) Verfahren zum Herstellen eines metallischen Bandes durch Endloswalzen
EP1641573A2 (fr) Dispositif pour la production de feuillard d'acier lamine a chaud, en particulier a partir d'ebauche en bande coulee en continu
DE3401894A1 (de) Verfahren zum herstellen von walzband mit hoher bandprofil- und bandplanheitsguete

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KM KN KP KR KZ LC LK LR LS LT LU LV LY MA MD MG MK MN MW MX MZ NA NG NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SM SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IS IT LT LU LV MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 2005819149

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 11793190

Country of ref document: US

WWE Wipo information: entry into national phase

Ref document number: 200580044287.7

Country of ref document: CN

NENP Non-entry into the national phase

Ref country code: DE

WWE Wipo information: entry into national phase

Ref document number: 2007128051

Country of ref document: RU

WWP Wipo information: published in national office

Ref document number: 2005819149

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 11793190

Country of ref document: US