WO2002002870A2 - Procede de production d'une bande de papier - Google Patents

Procede de production d'une bande de papier Download PDF

Info

Publication number
WO2002002870A2
WO2002002870A2 PCT/US2001/019516 US0119516W WO0202870A2 WO 2002002870 A2 WO2002002870 A2 WO 2002002870A2 US 0119516 W US0119516 W US 0119516W WO 0202870 A2 WO0202870 A2 WO 0202870A2
Authority
WO
WIPO (PCT)
Prior art keywords
slurry
floccs
paper web
broke
filler
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2001/019516
Other languages
English (en)
Other versions
WO2002002870A3 (fr
Inventor
Richard D. Harvey
Stuart W. Mabee
James M. Crandall
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Grain Processing Corp
Original Assignee
Grain Processing Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Grain Processing Corp filed Critical Grain Processing Corp
Priority to AU2001268551A priority Critical patent/AU2001268551A1/en
Priority to JP2002507109A priority patent/JP2004502057A/ja
Publication of WO2002002870A2 publication Critical patent/WO2002002870A2/fr
Publication of WO2002002870A3 publication Critical patent/WO2002002870A3/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un procédé de production d'une bande de papier. La bande de papier est produite à partir d'une composition de qualité inférieure, qui contient des pâtes à papier de qualité inférieure, comme une pâte recyclée et/ou une pâte de bois, et qui dans un mode de réalisation préféré, est une pâte de papier journal. Selon le procédé de l'invention, une matière de remplissage préfloculée est ajoutée à la pâte à papier avant qu'une bande de papier soit formée à partir de la composition. La matière de remplissage est retenue dans la bande, et la rétention de composants non désirés de la composition dans la bande est réduite si l'on compare avec du papier journal dans lequel une matière de remplissage est incorporée par des procédés conventionnels. Selon un autre mode de réalisation, on incorpore une pâte liquide, préfloculée, de rejets imprégnés dans une pâte à papier, avant la formation de papier. La bande de papier formée par le procédé de l'invention présente des propriétés améliorées grâce à l'incorporation à la bande de la matière de remplissage préfloculée ou des rejets traités.
PCT/US2001/019516 2000-06-20 2001-06-19 Procede de production d'une bande de papier Ceased WO2002002870A2 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
AU2001268551A AU2001268551A1 (en) 2000-06-20 2001-06-19 Process for preparing a paper web
JP2002507109A JP2004502057A (ja) 2000-06-20 2001-06-19 紙ウェブの製造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US59747300A 2000-06-20 2000-06-20
US09/597,473 2000-06-20

Publications (2)

Publication Number Publication Date
WO2002002870A2 true WO2002002870A2 (fr) 2002-01-10
WO2002002870A3 WO2002002870A3 (fr) 2002-05-16

Family

ID=24391655

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2001/019516 Ceased WO2002002870A2 (fr) 2000-06-20 2001-06-19 Procede de production d'une bande de papier

Country Status (3)

Country Link
JP (1) JP2004502057A (fr)
AU (1) AU2001268551A1 (fr)
WO (1) WO2002002870A2 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN104053836A (zh) * 2012-01-16 2014-09-17 凯米罗总公司 制造纸张、纸板或类似物的方法与附聚物

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4809584B2 (ja) * 2004-01-23 2011-11-09 大王製紙株式会社 古紙パルプの製造方法

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4799964A (en) * 1985-07-29 1989-01-24 Grain Processing Corporation Preparation of filler compositions for paper
WO2000034581A1 (fr) * 1998-12-10 2000-06-15 CALGON CORPORATION a corporation of the State of Delaware Coagulant polyampholyte utilise pour la fabrication du papier

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN104053836A (zh) * 2012-01-16 2014-09-17 凯米罗总公司 制造纸张、纸板或类似物的方法与附聚物
CN104053836B (zh) * 2012-01-16 2016-10-26 凯米罗总公司 制造纸张或纸板的方法与附聚物

Also Published As

Publication number Publication date
JP2004502057A (ja) 2004-01-22
AU2001268551A1 (en) 2002-01-14
WO2002002870A3 (fr) 2002-05-16

Similar Documents

Publication Publication Date Title
US4225383A (en) Highly filled sheets and method of preparation thereof
US6835282B2 (en) Paper web with pre-flocculated filler incorporated therein
JP2017500454A (ja) ポリマー乳化剤によって乳化されたａｓａエマルションのサイズ効率を改善する方法
RU2415986C1 (ru) Суспензии обработанного латексом наполнителя для использования в бумажном производстве
AU2002247795B2 (en) Fibrous web and process for the preparation thereof
CN109983177B (zh) 聚合物在制造纸或纸板的过程中用于控制沉积物形成的用途
AU2002247795A1 (en) Fibrous web and process for the preparation thereof
WO2021001602A1 (fr) Procédé de fabrication de papier ou de carton et papier ou carton obtenu par le procédé, et utilisation d'un polymère d'émulsion cationique dans la fabrication de papier ou de carton
US6602389B2 (en) Process for treating a fibrous slurry of coated broke
EP0003481A2 (fr) Feuilles fortement chargées et procédé pour leur préparation
DE102004044379A1 (de) Verfahren zur Herstellung von Papier, Pappe und Karton
JP2002520505A (ja) 製紙工程における微粒子系
AU761303B2 (en) An acid colloid in a microparticle system used in papermaking
AU761790B2 (en) Silica-acid colloid blend in a microparticle system used in papermaking
US6719881B1 (en) Acid colloid in a microparticle system used in papermaking
WO2002002870A2 (fr) Procede de production d'une bande de papier
CN103097607A (zh) 酸性水在造纸中的用途
AU2003270990A1 (en) Process for preparing a paper web
WO2025006743A2 (fr) Utilisation de polymères en émulsion amphotères avec des résines résistantes en tant qu'auxiliaires de rétention et de drainage

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A2

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A2

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
AK Designated states

Kind code of ref document: A3

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A3

Designated state(s): GH GM KE LS MW MZ SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE TR BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase