WO1995007864A1 - Matieres premieres pour la production de materiaux en verre et en ceramique et leur procede de fabrication - Google Patents

Matieres premieres pour la production de materiaux en verre et en ceramique et leur procede de fabrication Download PDF

Info

Publication number
WO1995007864A1
WO1995007864A1 PCT/EP1994/003097 EP9403097W WO9507864A1 WO 1995007864 A1 WO1995007864 A1 WO 1995007864A1 EP 9403097 W EP9403097 W EP 9403097W WO 9507864 A1 WO9507864 A1 WO 9507864A1
Authority
WO
WIPO (PCT)
Prior art keywords
glass
raw materials
temperature
heated
range
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP1994/003097
Other languages
German (de)
English (en)
Inventor
Melania Savos
Ludbert GRAF ZU MÜNSTER
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to AU77825/94A priority Critical patent/AU7782594A/en
Publication of WO1995007864A1 publication Critical patent/WO1995007864A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention se rapporte à des matières premières pour la production de matériaux en verre et en céramique, pouvant être obtenues à partir de cendres, poussières de filtration et/ou boues électrochimiques métallifères provenant de l'industrie, ainsi qu'à leur procédé de fabrication.
PCT/EP1994/003097 1993-09-15 1994-09-15 Matieres premieres pour la production de materiaux en verre et en ceramique et leur procede de fabrication Ceased WO1995007864A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU77825/94A AU7782594A (en) 1993-09-15 1994-09-15 Raw materials for glass and ceramics manufacture as well as a process for producing them

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DEP4331352.3 1993-09-15
DE4331352A DE4331352A1 (de) 1993-09-15 1993-09-15 Rohstoffe zur Glas- und Keramikproduktion sowie Verfahren zu ihrer Herstellung

Publications (1)

Publication Number Publication Date
WO1995007864A1 true WO1995007864A1 (fr) 1995-03-23

Family

ID=6497791

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP1994/003097 Ceased WO1995007864A1 (fr) 1993-09-15 1994-09-15 Matieres premieres pour la production de materiaux en verre et en ceramique et leur procede de fabrication

Country Status (3)

Country Link
AU (1) AU7782594A (fr)
DE (1) DE4331352A1 (fr)
WO (1) WO1995007864A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
RU2136625C1 (ru) * 1998-07-27 1999-09-10 Чумаченко Наталья Генриховна Сырьевая смесь для изготовления керамических стеновых изделий
RU2151130C1 (ru) * 1998-07-14 2000-06-20 Технологический институт Саратовского государственного технического университета Масса для изготовления керамического фильтра-мембраны
RU2177924C1 (ru) * 2000-05-06 2002-01-10 Казанская государственная архитектурно-строительная академия Способ приготовления шихты для производства керамических стеновых изделий

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE4233334A1 (de) * 1992-10-05 1994-04-07 Hoelter Heinz Verfahren zur Herstellung schadgasfreier Baustoffe

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2344324A1 (de) * 1972-09-12 1974-04-25 John O Hopkins Verfahren zur behandlung schwefelhaltiger schlacke und nach diesem verfahren hergestelltes erzeugnis
FR2397858A1 (fr) * 1977-07-22 1979-02-16 Pelt & Hooykaas Procede de traitement de masses de filtration obtenues notamment lors de la purification d'acide phosphorique
EP0002536A1 (fr) * 1977-12-20 1979-06-27 Wessel-Werk GmbH Procédé de raffinage d'une scorie phosphorée et utilisation du matériau ainsi obtenu
EP0294362A2 (fr) * 1987-06-05 1988-12-07 Öko Wien Umweltschutzprojektentwicklungs- und managementgesellschaft m.b.H. Procédé et dispositif pour la préparation de granulés, corps et analogues, insolubles dans l'eau
JPH03137041A (ja) * 1989-10-20 1991-06-11 Mitsubishi Materials Corp フライアッシュの加熱処理方法及び低発熱・高耐久性セメント
US5220112A (en) * 1991-09-10 1993-06-15 Air Products And Chemicals, Inc. Fixation of heavy metals in municipal solid waste incinerator ash

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2344324A1 (de) * 1972-09-12 1974-04-25 John O Hopkins Verfahren zur behandlung schwefelhaltiger schlacke und nach diesem verfahren hergestelltes erzeugnis
FR2397858A1 (fr) * 1977-07-22 1979-02-16 Pelt & Hooykaas Procede de traitement de masses de filtration obtenues notamment lors de la purification d'acide phosphorique
EP0002536A1 (fr) * 1977-12-20 1979-06-27 Wessel-Werk GmbH Procédé de raffinage d'une scorie phosphorée et utilisation du matériau ainsi obtenu
EP0294362A2 (fr) * 1987-06-05 1988-12-07 Öko Wien Umweltschutzprojektentwicklungs- und managementgesellschaft m.b.H. Procédé et dispositif pour la préparation de granulés, corps et analogues, insolubles dans l'eau
JPH03137041A (ja) * 1989-10-20 1991-06-11 Mitsubishi Materials Corp フライアッシュの加熱処理方法及び低発熱・高耐久性セメント
US5220112A (en) * 1991-09-10 1993-06-15 Air Products And Chemicals, Inc. Fixation of heavy metals in municipal solid waste incinerator ash

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
CHEMICAL ABSTRACTS, vol. 115, no. 20, 18 November 1991, Columbus, Ohio, US; abstract no. 213701j, page 372; *

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
RU2151130C1 (ru) * 1998-07-14 2000-06-20 Технологический институт Саратовского государственного технического университета Масса для изготовления керамического фильтра-мембраны
RU2136625C1 (ru) * 1998-07-27 1999-09-10 Чумаченко Наталья Генриховна Сырьевая смесь для изготовления керамических стеновых изделий
RU2177924C1 (ru) * 2000-05-06 2002-01-10 Казанская государственная архитектурно-строительная академия Способ приготовления шихты для производства керамических стеновых изделий

Also Published As

Publication number Publication date
AU7782594A (en) 1995-04-03
DE4331352A1 (de) 1995-03-16

Similar Documents

Publication Publication Date Title
DE2245432C2 (fr)
DE69019757T2 (de) Aktivkohle.
DE3705787A1 (de) Verfahren zur entfernung von giftigen oxiden aus abfallstaub
KR0140871B1 (ko) 산화니오브 분말(Nb2O5) 및 이의 제조방법
EP2870107B1 (fr) Procédé de réduction de chrome hexavalent dans des matières solides oxydées
WO1995007864A1 (fr) Matieres premieres pour la production de materiaux en verre et en ceramique et leur procede de fabrication
DE69920925T2 (de) Verfahren zur erzeugung von reinstchrom
DE3826520C2 (fr)
EP0527309A1 (fr) Méthode de traitement des déchets de la distillation de chlorosilanes avec l'acide chlorhydrique, sans production d'eau résiduaire
WO2016074878A1 (fr) Procédé de réduction de chrome hexavalent dans des matières solides oxydiques
DE1278416B (de) Verfahren zur Herstellung von reinem hexagonalem Kadmiumsulfid
DE69902001T2 (de) Verfahren und anlage zur effizienten aufarbeitung von multi-element abfällen mittels pyrolyse und halogenierung
DE2305522C2 (de) Verfahren zur Gewinnung von Quecksilber aus SO2 -haltigen Röstgasen
EP2228146A1 (fr) Conditionnement thermique de cendres
DE2107844B2 (de) Verfahren zur großtechnischen Herstellung von Magnesiumoxyd hoher Reinheit
DE2512107A1 (de) Verfahren zur langsamentkarbonisierung von wasser
EP0266597B1 (fr) Procédé d'élimination de composés métalliques de poussières produites dans la production électrothermique de phosphore jaune
DE69407605T2 (de) Poröses körniges material aus waschwassern von wolle verfahren zur herstellung und verwendungen
DE480287C (de) Herstellung von Molybdaen- oder Wolframsaeure
DE1142159B (de) Verfahren und Vorrichtung zur Herstellung niederer Titanchloride
EP2640664B1 (fr) Procédé d'extraction de sulfate de potassium à partir de la production de biodiesel
EP4516733A1 (fr) Récupération de phosphore sous forme de ses chlorures à partir de cendres de boues d'épuration
DE102023125795A1 (de) Verfahren zur Gewinnung von Phosphor aus phosphorhaltigen organischen Abfallstoffen
EP0031408B1 (fr) Procédé pour séparer des métaux à partir de suie
EP0237702A2 (fr) Procédé pour la cokéfaction continue de poix et utilisation du coke obtenu

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AU CA FI JP KR NO PL US

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FR GB GR IE IT LU MC NL PT SE

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
NENP Non-entry into the national phase

Ref country code: CA

122 Ep: pct application non-entry in european phase