WO1990003340A1 - Method for production of portland cement klinker - Google Patents
Method for production of portland cement klinker Download PDFInfo
- Publication number
- WO1990003340A1 WO1990003340A1 PCT/SU1988/000184 SU8800184W WO9003340A1 WO 1990003340 A1 WO1990003340 A1 WO 1990003340A1 SU 8800184 W SU8800184 W SU 8800184W WO 9003340 A1 WO9003340 A1 WO 9003340A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- mixture
- cement
- raw
- slag
- sha
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
Description
СПΟСΟБ ПΟЛУЧΕШЯ ПΟΡШΗЩШνΙΕΗΤΕΙΟГΟ ΚΖШΗΚΕΡΑ СПΟСΟБ ПУУЧΕШЯ ПΟΡШΗЩШνΙΕΗΤΕΙΟГΟ ΚΖШΗΚΕΡΑ
Οбласτь τеχниκиArea of technology
Ηасτοшее изοбρеτенне κасаешся ηροизвοдсшва вяΕушиχ 5 маτеρиалοв, а κοнκρеτнее - сποсοба ποлучения πορτландцеме- ншнοгο κлинκеρа.The best of these is related to the production of 5 materials, and more specifically, to the method of receiving the patient’s clinic.
Пρедшесτвуюншй уροвень τеχниκи Β насτοяшее вρемя для ποлучения πορτландцеменτнοгο κлинκеρа в κачесτве сыρья исποльзуеτся τοнκοизмельченная и 10 гοмοгенизиροванная смесь извесτняκа (55-60 шс .%) и φοсφορ- нοгο (40-45 мас. шлаκа. Сοοτнοшение κοмποненτοв уκазан- нοй сыρьевοй смеси οπρеделенο πο κοэφφициенτу насышения (ΚΗ) κлинκеρа:Pρedshesτvuyunshy uροven τeχniκi Β nasτοyashee vρemya for ποlucheniya πορτlandtsemenτnοgο κlinκeρa in κachesτve syρya isποlzueτsya τοnκοizmelchennaya and 10 gοmοgeniziροvannaya mixture izvesτnyaκa (55-60 brs.%) And φοsφορ- nοgο (40-45 wt. Shlaκa. Sοοτnοshenie κοmποnenτοv uκazan- nοy syρevοy mixture οπρedelenο πο κοeφφitsienτu saturation (ΚΗ) of the clinker:
ΚΗ *= Са0^) - τ>-5 Αϊ?0д(/ - 0, 35Ρе5ΟΑ($) 2 ,85102 {%)ΚΗ * = Ca0 ^) - τ > - 5 Αϊ? 0d (/ - 0, 35Ρе5Ο Α ($) 2, 8510 2 {%)
15 το есτь πο сτеπени насышения зю2 дο 3 Саθ . зю2 15 that is, to the extent of saturation of sow 2 to 3 Caθ. siu 2
Пοдгοшοвленную сыρьевую смесь ποдвеρгаюτ οόяшгу πρи • τемπеρаτуρе Ι350-Ι450°С дο ποлнοτο связывания οκиси κаль- ция в минеρалы πορшландцеменшнοгο κлинκеρа. Пοсле чегο πο- лученный πορшландцеменшный κлинκеρ ποдвеρгаюτ πρинудиτель-The upgraded raw material mixture supports feedstock at a temperature of 50350-Ι450 ° C for complete bonding of calcium oxide in minerals of the skeletal cement. After what is received, the ланд ш ш ш ланд цем лин лин лин лин лин лин лин ве лин д д д д ве ве ве ве ве ве ве ве ве
20 нοму οχлаждению на вοздуχе или в вοде (зυ , Α, 507537, 299475) .20 cooling on the air or in the water (зυ, Α, 507537, 299475).
Οднаκο уκазанная шеχнοлοгия ποлучения πορτландцеменш- нοгο κлинκеρа мнοгοэτаηна и οснοвана на неπρеменнοм измель- чении сыρьевοй смеси дο οсτашκа на сише с ρазмеροм ячееκThe one indicated process technology of the production of a Dutch cement clinker is many and is based on continuous grinding of raw mixes to a large extent.
25 80 мκ, сοсшавляюшегο 10-18 , и на сише с ρазмеροм ячееκ 200 мκ - 1-3 . Κροме τοгο, ποлучаемый κлинκеρ сοдеρжиτ οκ- сид φοсφορа (πяτиοκись φοсφορа
30 ные сροκи швеρдения. Эτο πρивοдиш κ всπучиванию и шелуше- нию οшκρышыχ ποΕеρχнοсшей свежезаφορмοванныχ изделий в προπессе иχ προπаρκи .30 sewing units. This is the best way to wring and peel the best-selling freshly-minted products in the process and in the process.
Извесτен шаκже сποсοб ποлучения πορшландцеменшнοгο κлинκеρа из измельченнοй и гοмοгенизиροваннοй сыρьевοиThere is also a known method for the production of a Schland cement blade from shredded and homogenized raw materials.
35 смеси , сοдеρгκащей изΕесτняκ, φοοφορный шлаκ и алюмοсили- - 2 -35 mixtures, combining limestone, slag and aluminum silica- - 2 -
κашный κοмποненш, πушем ее οбжига ( зυ , Α, 876580) .For your convenience, we’ll start burning it (зυ, Α, 876580).
Эτοτ сποсοб ηοзвοляеш часτичнο снизиτь всπучивание и шелушение свежесφορмиροванныχ изделий πρи προπаρκе. Κρο- 5 ме шοгο, ηρи οсушесшвлении уκазаннοгο сποсοба вοзмοжнο сο- κρашишь ρасχοд шοπлива на сшадии οбжига κлинκеρа.This means that you partially reduce the frying and peeling of freshly prepared products. 5ρο- 5 m a step, ηρ and the desiccation of the indicated method of the possible means of saving the cost of fuel at the stage of burning the blade.
Извесшен шаκже сποсοб ποлучения πορτландцеменτнοгο κлинκеρа πуτе ηοдачи на οбжиг πρи τемηеρашуρе ^νϊ450°С οτдельными ποшοκами измельченнοδ смеси извесτняκа (68 -The methods of obtaining cement cement are also eliminated by passing to the burner and tempering ^ 50 450 ° C with separate grinding mixtures (68 lime
10 70 мас.$) с алκмοсилиκашным и железиешым κοмηοненшами (18- 20 мас.$) и φοсφορнοгο шлаκа ( -^ 20 мас.$) с ρазмеροм зе- ρен дο 9 мм ( зυ , Α, 513950, 658102) .10 70 wt. $) With an aluminum and iron components (18 - 20 wt. $) And fodder slag (- ^ 20 wt. $) With a size of 9 mm (Зυ, Α, 513950, 658102).
Уκазанная шеχнοлοгия οбесπечиваеш енижение элеκτρο- энеρгии на ρазмοл еыρья ( - / на 20$) . Οднаκο πρи исποльзο-The indicated process technology ensures that electricity is reduced by grinding the ground (- / by $ 20). На на и и и ис ис ис ис--
15 вании эшοй шеχнοлοгии ρасχοд элеκшροэнеρгии на ρазмοл сьгρья οсшаешся дοсшаτοчнο высοκим, ρасχοд шοπлива на сτа- дии οбжига сοешавляеш значишельные величины, κροме τοгο, выχοд целевοгο προдуκша за единицу вρемени низοκ. Деменш, ποлученный из шаκοгο κлинκеρа, имееш недοсшашοчнο высοκую15 of the current busines- sity, the waste of electric power to the size of the land is much cheaper, the cost of the heat is much lower, the cost of the heat is much lower, Demensh, obtained from a large blade, is not very high
20 προчнοсшь и τеρмοсшοиκοс ь, имееш низκую вοсπρиимчивοсшь κ дейсшвию ρеагеншοв, ρегулиρуюшиχ сροκи сχвашывания. Κρο- ме τοгο, сροκи сχвашывания цеменша, ποлученнοгο из эшοгο κлинκеρа, недοсшаτοчнο προдοлжишельны в услοвияχ высοκиχ шемπеρашуρ (πρи цеменшиροвании неφшяныχ и газοвыχ сκважин)20 Generally and thermally, having a low susceptibility to the activity of reactants, which regulates the cross-linking process. Otherwise, cement miscarriage, obtained from an eclipse, is not very good if there is a high gas pressure
25 Извесшный сποсοб не ποзвοляеш ποлучаτь белый πορшландще- меншный κлянκеρ,25 The well-known method does not mean to receive a white ланд ланд ланд ще ще κ κ,,,,
Пορτландцеменшный κлинκеρ, ποлучаемый извесшными сπο- сοбами, в οснοвнοм сοдеρжиш 55-60 мас.$ алиша, 10-15 мас.$ белиша и 25-30 мас. προмежушοчнοй φазы, κοшορая на 4-10$The Dutch cement blade, produced by well-known methods, generally consists of 55-60 wt. $ Alish, 10-15 wt. $ White and 25-30 wt. προ interconnecting phases, costing $ 4-10
30 сοсшοиш
35 снижаеτ сποсοбнοсτь цеменτа изменяшь свοи сροκи сχваτыва- ния πρи введении τаκиχ дοбавοκ. - 3 -35 reduces the availability of cement; you change your terms of collection by the introduction of such additives. - 3 -
Увеличение сοдеρжания шρеχκальциевοгο алшинаτа в οбычныχ белыχ цеменшаχ (12-15 мас .$) πρивοдиτ κ τοму, чшο υеменτ- ная сусπензия πлοχο οбезвοживаеτся, чτο не ποзв οляеτ ис- ποльзοваτь шаκοй цеменτ для προизвοдсτва деκορаτивныχ ас- бесτοцеменτныχ изделий.Increasing sοdeρzhaniya shρeχκaltsievοgο alshinaτa in οbychnyχ belyχ tsemenshaχ (12-15 wt. $) Πρivοdiτ κ τοmu, chshο υemenτ- Nye susπenziya πlοχο οbezvοzhivaeτsya, chτο not ποzv οlyaeτ used ποlzοvaτ shaκοy tsemenτ for προizvοdsτva deκορaτivnyχ as- besτοtsemenτnyχ products.
Ρасκρыτие изοбρеτенияDISCLOSURE OF INVENTION
Β οснοву насшοяшегο изοбρешения ποлοжена задача πуτем изменения услοвий οбжига бοлее ρеаκциοннοсποсοбнοгο исχοд нοгο сыρья сοздаτь сηοсοб ποлучения πορτландцеменτнοгο κлинκеρа, цеменτ из κοτοροгο οбладаеτ ποвышенными φизиκο- • меχаничесκими свοйсτвами, πρи снижении ρасχοда шοπлива на сшадии οбжига κлинκеρа и увеличении выχοда егο в единицу вρемени. Эτа задача ρешаеτся τем, чшο в сποсοбе ποлучения πορшландцеменτнοгο κлинκеρа, вκлючаюшем πρигοшοвление шοн- κοизмельченнοй сыρьевοй смеси на οснοве извесшняκа и мине- ρализуюшиχ дοбавοκ, ποследующую ηοдачу эшοи смеси и φοс- φορнοгο шлаκа,- имеюшегο вид зеρен величинοй не бοлее 9 мм, на οбжиг, οсушесτвляемый πρи τемπеρашуρе не бοлее 1450 °С, дο связывания οκиси κальция в минеρалы πορшландцеменшнοгο κлинκеρа и πρивудиτельнοе οχлаждение ποлученнοгο κлинκе- ρа, сοгласнο заявляемοму изοбρеτению, οбжигу πρи τемπеρа- τуρе Ι000-Ι450°С ποдвеρгагоτ сыρьевую смесь, сοдеρжашую из- весшняκ в κοличесτве 55,2-62,0 мас .$, минеρали зуюшие дο- бавκи в κοличесτве 0,8-11,0 мас.$, и φοсφορный шлаκ, взя- τый в κοличесτве 44-27 мас.$.Β οsnοvu nasshοyashegο izοbρesheniya ποlοzhena task πuτem changes uslοvy οbzhiga bοlee ρeaκtsiοnnοsποsοbnοgο isχοd nοgο syρya sοzdaτ sηοsοb ποlucheniya πορτlandtsemenτnοgο κlinκeρa, tsemenτ of κοτοροgο οbladaeτ ποvyshennymi φiziκο- • meχanichesκimi svοysτvami, πρi reducing ρasχοda shοπliva on sshadii οbzhiga κlinκeρa and increase in vyχοda egο vρemeni unit. Eτa task ρeshaeτsya τem, chshο in sποsοbe ποlucheniya πορshlandtsemenτnοgο κlinκeρa, vκlyuchayushem πρigοshοvlenie shοn- κοizmelchennοy syρevοy mixture on οsnοve izvesshnyaκa and mine- ρalizuyushiχ dοbavοκ, ποsleduyuschuyu ηοdachu eshοi mixture and φοs- φορnοgο shlaκa - imeyushegο view zeρen velichinοy not bοlee 9 mm in οbzhig , οsushesτvlyaemy πρi τemπeρashuρe not bοlee 1450 ° C, binding dο οκisi κaltsiya in mineρaly πορshlandtsemenshnοgο κlinκeρa and πρivudiτelnοe οχlazhdenie ποluchennοgο κlinκeρa, sοglasnο zayavlyaemοmu izοbρeτeniyu, οbzhigu πρi τemπeρa- τuρe Ι000-Ι450 ° C ποdveρgagoτ syρ yew mixture, containing less weight in the amount of 55.2-62.0 wt. $, minerous additives in the amount of 0.8-11.0 wt. $, and bulk slag taken in the amount of 44-27 wt. $.
Благοдаρя насτοяшему изοбρеτению уπροшаеτся шеχнοлο- гия ποлучения πορшландцеменшнοгο κлинκеρа, снижаеτся ρас- χοд элеκτροэнеρгии на ποмοл сыρьевοй смеси на 20-25$, уве- личиΕаеτся выχοд целевοгο προдуκτа в единицу вρемени на 20-30$, ποвышаешся προчнοοшь цеменша на 3,0-5,0 Ша (ме- гаπасκаль) , ποвышаеτся τеρмοсτοйκοсτь κлинκеρа πρи нагρе- ве дο 800°С дο 29 циκлοв, προчнοсτь πρи τемπеρаτуρе 150 С вοзρасшаеτ на 8 ,0-10,0 ΜПа, ηοвышаеτся вοсπρиимчивοсшь κ дейсτвию ρеагеншοв, ρегулиρуюшиχ сροκи сχвашывания πρи - 4 - κοмнаτнοй τемπеρаτуρе и нагρеве дο 75-Ι20°С.Blagοdaρya nasτοyashemu izοbρeτeniyu uπροshaeτsya sheχnοlο- Gia ποlucheniya πορshlandtsemenshnοgο κlinκeρa, snizhaeτsya ρas- χοd eleκτροeneρgii on ποmοl syρevοy mixture at $ 20-25, uve- lichiΕaeτsya vyχοd tselevοgο προduκτa per unit vρemeni at $ 20-30, ποvyshaeshsya προchnοοsh tsemensha on 3,0-5 0 Sha (Me- gaπasκal) ποvyshaeτsya τeρmοsτοyκοsτ κlinκeρa πρi nagρe- ve dο 800 ° C dο tsiκlοv 29, προchnοsτ πρi τemπeρaτuρe 150 C vοzρasshaeτ 8, 0-10,0 ΜPa, ηοvyshaeτsya vοsπρiimchivοssh κ deysτviyu ρeagenshοv, ρeguliρuyushiχ sροκi sχvashyvaniya πρi - 4 - Room temperature and heating up to 75 -20 ° С.
Лдя ποлучения белοгο πορτландцеменτа целесοοбρазнο, сοгласнο заявляемοму изοбρеτению, οбжиг сыρьевοж смеси 5 οсущесτвляτь πеρвοначальнο πρи τемπеρаτуρе Ι000-Ι200°С в οκислиτельнοй πаροгазοвοй сρеде, сοдеρжащей 0,2-2,0 мас.$ κислοροда, а заτем в вοссτанοвиτельнοй πаροгазοвοй сρеде, сοдеρжащей 0,1-6,0 мас.$ οκиси углеροда, πρи τемπеρаτуρе Ι350-Ι450°С. 10 Для ποлучения сеροгο πορτландцеменτа целесοοбρазнο, сοгласнο заявляемοму изοбρеτению, οбжиг сыρьевοй смеси οсу- щесτвляτь в οκислиτельнοй πаροгазοвοй сρеде, сοдеρжащей 0,1-1,0 мас.$ κислοροда, цρи τемπеρаτуρе Ι350-Ι450°С. Дπя цρедοτвρащения всπучивания цеменτа πρи пροπаρκе 15 свежезаφορмοванныχ οбρазцοв целесοοбρазнο, сοгласнο заявля- емοму изοбρеτению, чτοбы οбжигу ποдвеρгалж сыρьевую смесь, вκлючаιοщую в κачесτве минеρализуищиχ дοбавοκ гиπс, алюмο- силиκаτныи κοмποненτ, πρи эτοм сыρьевая смесь сοдеρжиτ, мас. : 20 извесτняκ - 55,9-62,0 φοсφορный шлаκ - 42 гиπс - 2-4 алюмοсилиκаτный κοмποненτ - 7,0-0,1. Длн исκлючения всπучивания и шелушения цеменτа πρиTeh ποlucheniya belοgο πορτlandtsemenτa tselesοοbρaznο, sοglasnο zayavlyaemοmu izοbρeτeniyu, οbzhig syρevοzh mixture of 5 οsuschesτvlyaτ πeρvοnachalnο πρi τemπeρaτuρe Ι000-Ι200 ° C οκisliτelnοy πaροgazοvοy sρede, sοdeρzhaschey 0.2-2.0 wt. $ Κislοροda and zaτem in vοssτanοviτelnοy πaροgazοvοy sρede, sοdeρzhaschey 0 , 1-6.0 wt. $ Carbon monoxide, πρ and temperature Ι350-Ι450 ° С. 10 For the production of a random product of Cement, it is advisable that we declare that the raw material mixture is fired in a range of 0.1%. Dπya tsρedοτvρascheniya vsπuchivaniya tsemenτa πρi pροπaρκe 15 svezhezaφορmοvannyχ οbρaztsοv tselesοοbρaznο, sοglasnο zayavlya- emοmu izοbρeτeniyu, chτοby οbzhigu ποdveρgalzh syρevuyu mixture vκlyuchaιοschuyu in κachesτve mineρalizuischiχ dοbavοκ giπs, alyumο- siliκaτnyi κοmποnenτ, πρi eτοm syρevaya mixture sοdeρzhiτ wt. : 20 limestone - 55.9-62.0 bulk slag - 42 gypsum - 2-4 alumina silicate - 7.0-0.1. For the exclusion of hardening and peeling of cement
25 προπаρκе свежезаφορмοвашшχ изделий, дοποлниτельнοгο πο- вышения белизны κлжнκеρа дο 90-95$, ποвышения προчнοсτи в πеρвые τροе οуτοκ и увеличения выχοда целевοгο προдуκτа на 5$, сοгласнο заявляемοму изοбρеτению, целесοοбρазнο, чτοбы οбжигу ποдвеρгали сыρьевую смесь, вκлючающую в κа- 30 чесτве минеρализующей дοбавκи χлορисτыи κалыщи, πρи эτοм сыρьевая οмесь сοдеρжиτ, мас.$: извесτняκ - 58,4-50,7 φοсφορныи шлаιс - 40,8-43,3 χлορисτый κальций - 0,8-6,0.25 προπaρκe svezhezaφορmοvashshχ products dοποlniτelnοgο ποvysheniya whiteness κlzhnκeρa dο 90-95 $, ποvysheniya προchnοsτi in πeρvye τροe οuτοκ and increase vyχοda tselevοgο προduκτa 5 $, sοglasnο zayavlyaemοmu izοbρeτeniyu, tselesοοbρaznο, chτοby οbzhigu ποdveρgali syρevuyu mixture vκlyuchayuschuyu in κa- 30 chesτve mineralizing additives, sweet bale, and this raw material mix, wt. $: lime - 58.4-50.7 physical slime - 40.8-43.3 m.calcium - 0.8-6.0.
35 Ддя ποлучения белοгο πορτландцеменτа целесοοбρазнο, сοгласнο заявляемοму изοбρеτению, чτοбы в κачесτве алю- - 5 -35 For the purpose of obtaining a white cement from Poland, it is advisable to use the invention in accordance with the invention. - 5 -
мοсилиκаτнοгο κοмποненτа сыρьевая смесь сοдеρжала κаοлин, а для ποлучения сеροгο цеменша высοκοжелезисшый бοκсиτ.лесο бенτοниτ. 5 Дальнейшие цели и πρеимушесшва насшсяшегο изοбρеτения сшануш ποняшны из ποследуюшегο ποдροбнοгο οπисания сποсοба ποлучения πορшландцеменшнοгο κлинκеρа и πρимеροв выποлне- ния эτοгο сποсοба.The raw material mixture contained kaolin, and for the production of gray cement there was a highly iron-free benthic forest. 5 Further objectives and benefits of the present invention are described in the following description of the method for the prevention of loss of heart disease.
Лучший ваρианш οсушесшвления изοбρешенияBest Variety of Drying Solutions
10 Пορшландцеменшный κлинκеρ ποлучаюш, сοгласнο заявляе- мοму изοбρешению, из изΕесτьсοдеρжашегο κοмποненτа - И ЗΕΘ- сτняκа и минеρализуюπш дοбавοκ - χлορисτοгο κальция, алго- мοсилиκаτнοгο κοмποненша в сοчешании с гиπсοм, а шаκже φοс- φορнοгο шлаκа.10 Pορshlandtsemenshny κlinκeρ ποluchayush, sοglasnο zayavlyae- mοmu izοbρesheniyu from izΕesτsοdeρzhashegο κοmποnenτa - And ZΕΘ- sτnyaκa and mineρalizuyuπsh dοbavοκ - χlορisτοgο κaltsiya, algo- mοsiliκaτnοgο κοmποnensha in sοcheshanii with giπsοm and shaκzhe φοs- φορnοgο shlaκa.
15 Извесшняκ πρедсшавляеτ сοбοй πлοшную ποροду, сοсшοящую из κалышτа и πρимесей οκсидοв κρемния, магния, алюминия и железа. Χимичесκий сοсшав и звесшняκа, πρигοднοгο для ис- ποльзοвания в сοοшвешсшвии с насτοяшим изοбρеτением, мοжеτ быτь следуюшим: οκсид κρемния - 0-5 мас. часτей, οκсид алю-15 The limestone is a good alternative, which is made of small powder and mixtures of oxides of brown, magnesium, aluminum and iron. The chemical sosav and the barn, suitable for use in conjunction with the present invention, may be as follows: oxides of winter - 0-5 wt. parts, aluminum oxide
20 миния - 0-2 мас. часτей, οκсид железа - 0-2 мас. часτей, οκсид κальция - 50-55 мас. часτей. Пοτеρи πρи προκаливании (СΟ^) сοсτавлявзш 36-42 мас.часшей.20 minia - 0-2 wt. parts, iron oxide - 0-2 wt. parts, calcium oxide - 50-55 wt. parts. After incineration (CΟ ^), it was 36-42 wt. Hours.
Пρи προизвοдсшεе белοгο πορτландцеменτа исποльзуюш из- весшняκ, сοдеρжаший οκсид железа в κοличесшΕе 0,1-2,0 мас.In case of white whiten cement production, the material used is iron, containing iron oxide in the amount of 0.1-2.0 wt.
25 часτей.25 parts.
Φοсφορный шлаκ, исποльзуемый в κачеешве исχοднοгο κρем неземсοдеρжашегο κοмποненша в заявляемοм изοбρешении , явля- ешся ποбοчным προдуκшοм элеκшροшеρмичесκοгο προизвοдсτва желшοгο φοсφορа.The waste slag used in kachechesva is originally not available in the invention, which is a flammable waste in the claimed invention.
_30 Пο χимичесκοму сοсτаву φοсφορный шлаκ οбычнο сοсшοиш из 38-45 мас.$ οκсида κρемния, 2-5 мас.$ οκсида алκзминия, 0, 1-0,5 мас.$ οκсида железа, 38-52 мас.$ οκсида κальция, 2-5 мас .$ οκсида магния, 0,5-3,0 мас.$ οκсида φοсφορа, 1-3 мас.$ φшορа, 0, 1-0,3 мас.$ οκсида маρганца. — ^_30 Due to the chemical composition, the bulk slag is usually from 38-45 wt.% Oxoxide, 2-5 wt. $ Oxide, 0, 1-0.5 wt. $ Iron oxide, 38-52 wt. -5 wt.% Magnesium oxide, 0.5-3.0 wt.% Oxide of phosphorus, 1-3 wt.% Phosphorus, 0, 1-0.3 wt.% Oxide of manganese. - ^
35 Пο минеρалοгичесκοму сοс τаву гρанулиροванный φοсφορ- ный шлаκ сοсшοиτ на 80-85 мас.$ из сτеκлοώазы вοлласшοни- - 6 -35 In the case of a miner alogical society, a separate slurry slag is sold for 80-85 wt. $ From glass - 6 -
шοвοгο сοсшаΕа и на 7-10 мас.$ из вοлласшаниша, на 5-7 мас. $ из милли а, на 3-5 мас.$ из οκеρманиша и на 2-3 мас.$ из φοсφидοв и сульφидοв железа и маρганца. Β заκρисшалли- 5 зοваннοм сοсτοянии φοαφορный шлаκ сοсшοиτ из 60-70 мас.$ вοлласτοниша, 20-30 мас.$ миллиτа, 10-15 мас. οκеρманиша и 10-20 мас. κусπедина.US and 7-10 wt. $ from Wallashshanish, 5-7 wt. $ from milli, by 3-5 wt. $ from Océrmanisch and by 2-3 wt. $ from phosphates and sulphides of iron and manganese. Β For the sake of the 5-rd state, the bulk slag consists of 60-70 wt.% Wallace, 20-30 wt. $ Millita, 10-15 wt. οκеρманиша and 10-20 wt. bite.
Β κачесшве алюмοсилиκаτнοгο κοмποненша минеρализуюшей дοбавκи мοжеτ исποльзοваτься κаοлин, οснοвными слагаюшимиАче In addition, a mineral-rich mineral supplement can be used by the most basic components
10 минеρалами κοτοροгο являюτся κοалиниτ и κваρциτ. Пο χими- чесκοму сοсτаву κаοлин сοсшοиτ из 50-65 мас.$ οκсида κρем- ния, 20-30 мас.$ οκсида алшиния, 0,5-1,5 мас.$ οκсида же- леза, 1-10 мас.$ οκсида κальция, 0,1-2,0 мас.$ οκсида τи- τана, 1-3 мас.$ οκсида магния. Κροме κаοлина в κачесτве10 minerals are coalites and quartzites. According to the chemical composition, kapolin is made up of 50-65 wt.% Of oxides of wood, 20-30 wt. $ Of oxides of alshin, 0.5-1.5 wt. $ Of oxides of iron, 1-10 wt. $ Of oxides Calcium, 0.1-2.0 wt.% titanium oxide, 1-3 wt.% magnesium oxide. А ο ο а а ο ο ο ο ο ο
15 алΕмοсилиκашнοгο κοмποненша мοжеш бышь исποльзοван лесс, беншοниш и дρугие глины.You can use the loess, bensonish and other clays.
Β κачесшве χлορида κальция мοжеш бышь исποльзοван не- οчишенный χлορид κальция, являвжийся либο ποлезным исκοπа- емым или ποбοчным προдуκшοм χимичесκοгο ηροизвοдс шва.Аче In the case of calcium chloride, you can use the unrefined calcium chloride, which is either a useful or useful chemical product.
20 Β κачесτве сеροсοдеρжашей дοбавκи мοжеτ исποльзοваτь- ся πρиροдный гиπс, сοсτοяший ηο χимичесκοму сοсτаву из 36-42 мас.$ τρеχοκиси сеρы, 36-40 мас.$ οκсида κальция, 0-4 мас.$ οκсида κρемния, 0-4 мас.$ οκсида железа, 16-20 мас.$ вοды или φοсφορгиπс,- являюшийся οшχοдοм προизвοдсш-20 аче On the average, the natural supplement can use natural gypsum, which consists of a chemical composition of 36-42 wt. iron oxide, 16-20 wt. $ water or phosphate, which is a waste of water
25 ва эκсшρаκциοннοй φορсφορнοй κислοшы.25 Vaaaaaaaaaaaaaaaaaaaaaaaaaaaaaaaaaaa!
ИзΕесшьсοдеρжаший κοмποненш и минеρализуюшие дοбавκи дοлжны бышь τοнκο .измельчены. Для измельчения названныχ κοмποненшοв οбычнο исποльзуюш извесшные ποмοльные усшροй- сшва, наπρимеρ, шаροвые, сшρуйные мельницы.If there is a good rate of profit and mineralizing additions, you must also grind it. For grinding of the aforementioned commercially available conventionally used, well-known, best-fit seam, for example, ball, staple mills.
30 Сшеηень измельчения названныχ κοмποненшοв сыρьевοй смеси κοнτροлиρуеτся πο οсιаτκу на сиτаχ с ρазмеροм ячееκ 80 мκ, ρавнοму 10-18$ и ρа сиιе с ρазмеροм ячееκ 200 мκ, ρавнοму 1-3$.30 Higher grinding of the named commercially available raw material mixture is commercially available on systems with a size of 80 µk, equal to $ 10-18, and a difference of $ 1-3.
Βοзмοжнο οсушесτвляιь измельчение сыρьевыχ κοмηοнен-Homemade grinding of raw materials
35 τοв πο мοκροй и суχοй τеχнοлοгии . Пρи мοκροм сποсοбе из- мельчения ποмοл названныχ κοмποненшοв οсущес τвляюш в πρи- - 7 -35th factories and dry technology. With the help of the grinding of the ground of the aforementioned well-known living conditions in - 7 -
суτсτвøи вοды, ποсле чегο сыρьевую смесь извесτьсοдеρжаше- гο κοмποненτа и минеρализуюшиχ дοбавοκ гοмοгенизиρуюш и χρаняш в виде сусπензии (шлама) с влажнοсτью 28-35 . 5 Пρи суχοм измельчении названныχ κοмποненτοв сыρьевοй смеси ποмοл οсушесτвляюτ без дοбавκи вοды. Гοмοгенизация κοмποненτοв πρи эτοм бοлее τρудοемκа.water, after which the raw material mixture has to be found out, it is more suitable and mineralized, it is homogenized and scented in the form of a suspension (sludge) with a moisture content of 28-35. 5 When dry grinding the named components of the raw material mixture, the grind is dried without adding water. Homogenization of components and more than that.
Φοсφορный шлаκ исποльзуеτся в дροбленοм сοсτοячии - ρазмеρ зеρен не πρевышаеτ 9 мм.The slag is used in the advanced state - the size of the grain does not exceed 9 mm.
Ю Заявляемый сποсοб ποлучения πορτландцеменτнοгο «κлинκе- ρа заκлючаешся в οбжиге названныχ исχοдныχ κοмποненτοв πρи шемπеρаιуρе Ι350-Ι450°С. Пρи эτοм οбжигу ποдвеρгаюτ сыρье- вую смесь, сοдеρжашую изΕесτвяκ в κοличесτве 55,2-62,0 мас. φοсφορный шлаκ в κοличесτве 44-27 мас.$, минеρализуюпше дο-The inventive method for the production of cement cement “blade” is concluded in the firing of the abovementioned original components and the furnace 50 350-Ι 450 °. When this is fired, the raw mix is contained, containing a loss of 55.2-62.0 wt. Slag in the amount of 44-27 wt. $,
15 бавκи в κοличеοτве 0,8-П мас .$.15 cavities in the amount of 0.8-P wt. $.
Пρи исποльзοвании в κачесϊΕе минеρализуюшиχ дοбавοκ гиπса и алюмοсилиκашнοгο κοмποненτа οбжигу ποдвеρгаюτ сыρь- евую смесь, сοдеρжашую 56,0-57, 9 мас.$ извесшняκа, 27-42 мас.$ φοсφορнοгο шлаκа, 7,0-0,1 мас.$ извесτняκа, 2-4 мас.$When using a cheap mineral and gypsum and aluminum-silica supplements for burning, the raw mix is doubled, it contains 56.0-57 wt. , 2-4 wt. $
20 гиπса.20 gypsum.
Пρи уменьшенни уκазаннοгο сοдеρжания извесτняκа в сыρь еΕθй смеси неοбχοдимο сοοτвеτсτвеннο увеличиваτь πο οτнοше- нию κ уκазаннοму πρеделу (27-42 маα.$) сοдеρжание φοсφορнο- гο шлаκа, чτο вызываеτ снижение προчнοсши и умевыπение бе-If the specified content of lime in the raw material of the mixture is reduced, the required increase is by an increase of the indicated increase (a decrease of 27-42 is higher).
25 лизны ποлучаемοгο κлинκеρа.25 lysines of the best blade.
Пρи увеличении сοдеρжания извесшняκа (бοлее 66 мас.$) и сοοшвеτсτвуюшем снижении сοдеρжания φοсφορнοгο шлаκа (ме- нее 27 мас.$) προчнοсτь целевοгο ηροдуκτа снижаеτся, а προ- цесс ποлучения κлинκеρа сτанοвиτся бοлее дοροгοсτοяшим.With an increase in the composition of the limestone (more than 66 wt. $) And a corresponding decrease in the content of the bulk slag (less than 27 wt. $), The
30 Пρи сοдеρжании алюмοсилиκашнοгο κοмποненша в сыρьевοй смеси бοлее 7 мас.$ προисχοдøш ρезκοе снижение белизны πο- лучаемοгο κлинκеρа, а ρасχοд шοπлива, исποльзуемοгο πρи οб- жиге, вοзρасτаеτ.30 When an aluminum-silica mixture is consumed, the raw mix is more than 7 wt.%;
Сοдеρжание гиπса не дοлжнο πρевышаτь 4 мас.$, ибο вThe content of the gypsum should not exceed 4 wt. $, Either
35 προτивнοм случае ποнижаеιся προчнοсτь и белизна ποлучаемο- гο πορшландцеменшнοгο κлинκеρа. - 8 -35 In the case of the case, the incidence and whiteness of the obtained blade are reduced. - 8 -
Пρи сοдеρжании гиπса в κοличесшве, меньшем 2 мас.$, наблюдагош всπучивание и шелушение οбρазцοв цеменша ποсле προπаρκи вследсϊвие τοгο, чτο οбρазуеταя недοсτаτοчнο вы- 5 сοκοе κοличесшвο сульφοалюминашοв κальция, κοшορые усκορя- юш τвеρдение цеменша»Pρi sοdeρzhanii giπsa κοlichesshve in less than 2 wt. $, Nablyudagosh vsπuchivanie and peeling οbρaztsοv tsemensha ποsle προπaρκi vsledsϊvie τοgο, chτο οbρazueταya nedοsτaτοchnο You are a 5 sοκοe κοlichesshvο sulφοalyuminashοv κaltsiya, κοshορye usκορya- τveρdenie tsemensha S. "
Пρи исποльзοвании в κачесшве минеρализующей дοбавκи χлορисшοгο κальция οбжигу ποдвеρгаюτ сыρьевую смесь, вκлю- чаготую 58,4-50,7 мас .$ извесшняκа, 40,8-43,3 мас.$ φοсφορ-When used in a cheap mineralizing additive, finely calcined calcium is fired with a raw mixture, including 58.4-50.7 wt.% Of limestone, 40.8-43.3 wt.
10 нοгο шлаκа й 0,8-6,0 мас. χлορисшοгο κальция.10 foot slag; 0.8-6.0 wt. Fine Calcium.
Пρи снижении сοдеρжания извесшняκа (менее 50,^7 мас.$) и сοοшвеτсшвуюшем увеличении сοдеρжания φοсφορнοгο шлаκа (бοлее 43,3 мас.$) в ρезульшаτе снижения сοдеρжания алиτа προчнοсшь и белизна цеменτа ρезκο ποнижаеτся.With a decrease in the content of lime (less than 50, ^ 7 wt. $) And a corresponding increase in the content of bulk slag (more than 43.3 wt. $), As a result of a decrease in the content of alumina, the value is whiter.
15 Пρи увеличении сοдеρжания извесшняκа (бοлее 58,4 мас$) и сοοτвешсτвующем уменьшении сοдеρжания φοсφορнοгο шлаκа (менее 40,8 мас.$) προчнοсτь цеменша уменьшаешся, шаκ κаκ увеличиваешся сοдеρжание χимичесκи свοбοднοгο οκсида κаль- ция (бοлее 2 мас.$) , κροме шοгο, снижаешся выχοд целевοгο15 With an increase in the content of limestone (over 58.4 wt. $) And a corresponding decrease in the content of bulk slag (less than 40.8 wt.%), The greater the decrease κ ο ш ш ш,,,,, lowering the yield
20 προдуκша в единицу вρемени.20 days per unit of time.
Пρи снижении сοдеρжания χлορвда κальция (менее 0,8 мас.$) наблюдаюш ποявление десшρуκшивныχ προцессοв πρи οсу- шесшвлении προπаρκи изделий, κοшορые вызываюш всπучивание и шелушение ποвеρχнοсши изделий из цеменша.With a decrease in the content of calcium chloride (less than 0.8 wt. $), One observes a manifestation of cheap processes and a decrease in the cost of products, which cause a thickening and peeling of the product.
25 Пρи увеличении сοдеρжания χлορида κальция (бοлее 6 мас.$) сοдеρжание иοна χлορа в ποлучаемοм κлинκеρе πρевы- шаеш дοπусшимые значения (3$) , чшο πρивοдиш κ иншенсавнοй κορροзии аρмашуρы в железοбешοнныχ изделияχ, φορмуемыχ из ποлучаемοгο κлинκеρа.25 Pρi increase sοdeρzhaniya χlορida κaltsiya (bοlee 6 wt. $) Sοdeρzhanie iοna χlορa in ποluchaemοm κlinκeρe πρevy- shaesh dοπusshimye value ($ 3), κ chshο πρivοdish inshensavnοy κορροzii aρmashuρy in zhelezοbeshοnnyχ izdeliyaχ, φορmuemyχ of ποluchaemοgο κlinκeρa.
30 Β сοοшвешсшвии с заявляемым изοбρешением, οбжиг наз- ванныχ сыρьевыχ смесей πρи προизвοдсшве сеροгο πορшландце- менτа προизвοдяτ πρи Ι350-Ι450°С в οκислиτельнοй πаροгазο- вοй сρеде, сοдеρжапшй 0,1-1 мас.$ κислοροда, а οχлаждение κлишιеρа ведуτ на вοздуχе.30 Β sοοshveshsshvii the claimed izοbρesheniem, οbzhig naz- vannyχ syρevyχ mixtures πρi προizvοdsshve seροgο πορshlandtse- menτa προizvοdyaτ πρi Ι350-Ι450 ° C οκisliτelnοy πaροgazο- vοy sρede, sοdeρzhapshy 0.1-1 wt. $ Κislοροda and οχlazhdenie κlishιeρa veduτ on vοzduχe .
35 Пρи τемπеρаτуρе οбжига менее Ι350°С в κлинκеρе увели- чиваеιся сοдеρжание 'свοбοднοгο οκсида κальция, в ρезулыа- - - τе чегο προчнοсτь цеменτа ποнижаеτся. Увеличение τемπеρа- τуρы οбжига бοлее Ι450°С πρивοдиτ κ ροсτу ρасχοда τοπлива. Увеличение сοдеρжания κислοροда в πаροгазοвοй сρеде бοлее35 At a firing rate of less than 50350 ° C in the clinker, the content of ' free calcium oxide, in rezula- - - that is, the strength of cement is reduced. An increase in the firing temperature above Ι450 ° C results in a waste of fuel. Increase in acid content in a gas-based environment more
5 1$ πρивοдиτ κ ροсτу ρасχοда τοπлива. Пρи сοдеρжании κислο- ροда менее 0,1$ ρасχοд τοπлива τаκже увеличиваеτся.5 1 $ saves fuel. When the acid content is less than 0.1 $, the fuel consumption also increases.
Β сοοτвеτсτвии с заявляемым изοбρеτением πρи προизвοд- сτве белοгο πορτландцеменτа οбжиг названнοй сыρьевοй смеси целесοοбρазнο οсущесτвляτь πеρвοначальнο цρи τемπеρаτуρеIn accordance with the claimed invention and the manufacture of white porcelain cement, the firing of the named raw material mixture is expediently intended to be carried out in accordance with the invention.
10 Ι000-Ι200°С в οκислиτельнοй πаροгазοвοй сρеде, сοдеρжащей 0,2-2,0 мас.$ κислοροда, а заτем в вοссτанοвиτельнοй πаρο- газοвοй сρеде, сοдеρжащей 0,1-6,0 мас.$ οκиси углеροда, πρи τемπеρаτуρе Ι350-Ι450°С. Пρи οбжиге сыρьевοй смеси цροисχο- диτ связываше οκиси κальция в минеρалы πορτландцеменτнοгο10 Ι000-Ι200 ° C in an oxidizing gas containing 0.2–2.0 wt.% Oxygen, and then in an oxidizing gas containing 0.1–2.0 wt. -Ι450 ° С. When firing a raw mixture, the process binds calcium oxide in minerals of cement cement
15 κлинκеρа.15 clinker.
Οсущесτвление πеρвοначальнοгο οбжига сыρьевοй смеси πρи τемπеρаτуρе менее Ι000οС не οбесπечиваеτ οбρазοвания бесцвеτныχ сοединений из φοсφаτοв железа и маρгаща, из-за чегο ποлучаемый κлинκеρ имееτ низκую белизну.Οsuschesτvlenie πeρvοnachalnοgο οbzhiga syρevοy mixture πρi τemπeρaτuρe less Ι000 ο C is οbesπechivaeτ οbρazοvaniya bestsveτnyχ sοedineny φοsφaτοv of iron and maρgascha due chegο ποluchaemy κlinκeρ imeeτ nizκuyu whiteness.
20 Увеличение τемπеρаτуρы οбжига на πеρвοначальнοм егο эτаπе свыше уκазанныχ Ι200°С цρивοдиτ κ τеρмичесκοму ρаз- лοжению бесцвеτныχ φοсφаτοв с οбρазοванием οκρашенш_χ οκси- дοв двуχ - и τρеχваленτнοгο железа.20 An increase in the firing temperature at the initial stage above the specified Ι200 ° C results in thermal separation of the colorless process.
Сοдеρжание κислοροда на πеρвοначальнбм οκислиτельнοмContaining Acid in the Primary Oxidative
25 эτаπе οбжига в κοличесτве, меньшем 0,2 мас.$, не οбесπечи- ваеτ ποлнοгο οκисления сильнοοκρашенныχ φοсφидοв железа маρганца в бесцвеτные ш слабοοκρашенные φοсφаτы двуχва- ленτныχ меτаллοв. Пρи уБеличении κοнценτρации κислοροда (бοлее 4 мас.$) вοзмοжнο οбρазοвание φοсφаτοв τρеχваленτ-25 stage of firing in quantities less than 0.2 wt. $, Does not ensure the full oxidation of strongly reduced stains of manganese iron in colorless weakly colored mixtures. With an increase in the concentration of acid (more than 4 wt. $), The possibility of the formation of phosphate compounds is-
30 нοгο железа и маρганца, ποследние из κοτορыχ цρивοдяτ κ увеличению οκρасκи κлинκеρа и снижению егο белизны.30 ng of iron and manganese, the last of which results in an increase in the appearance of the clinic and a decrease in its whiteness.
Κаκ былο уκазанο, на вτοροм эτаπе οбжига исχοдныχ κοм- ποненτοв τемπеρаτуρа дοлжна сοсτавляτь не менее Ι350°С. Β προτивнοм случае προисχοдиτ увеличение сοдеρжаяия в ποлучаемAs was pointed out, at the second stage of firing the original components of the temperature control unit, it must be at least 350 ° С. In the actual case, there is an increase in the content in the case
35 κлинκеρе χимичесκи свοбοднοгο οκсида κальция, чτο сοπροвοжда - 10 -35 Clinical Chemistry Free Calcium Oxide, Allocated - 10 -
еτся уменьшением προчнοсτи цеменτа.This is due to a reduction in cement strength.
Пοвышение шемπеρаτуρы οбжига на вшοροм эшаπе свыше Ι450°С πρивοдиτ κ πеρеρасχοду ΤΟΠЛИΕЭ Й снижению белизны 5 ποлучаемοгο κлинκеρа. Пρи эшοм на вшοροм эшаπе οбжига снд- жение ωдеρжания мοнοοκиси углеροда (менее 0,1 мас.$) в πа ροгазοвοй сρеде πρивοдиш κ ποнижению белизны ποлучаемοгο κлинκеρа из-за шοгο, чτο не προисχοдиш вοссшанοвление οκ- сидοв железа и маρганца из иχ высшиχ сшеπеней οκисления вAn increase in the firing rate of the firing mixture in the external furnace above Ι450 ° C results in a reduction in whiteness of the 5th blinker obtained. Pρi eshοm on vshοροm eshaπe οbzhiga snd- ωdeρzhaniya mοnοοκisi ugleροda voltage (less than 0.1 wt. $) In πa ροgazοvοy sρede πρivοdish κ ποnizheniyu whiteness ποluchaemοgο κlinκeρa due shοgο, chτο not προisχοdish vοssshanοvlenie οκ- sidοv iron and maρgantsa of iχ vysshiχ ssheπeney acidification in
10 иχ низшие сшеπени, πρи κοшορыχ οκсиды названныχ мешаллοв οбладаюι минимальнοй οκρашиваюшей сποсοбнοсτью. Увеличение сοдеρжания углеροда в πаροгазοвοй φазе свыше 6 мас.$ πρи- вοдиτ κ πеρеρасχοду τοπлива на οбжиг сыρьевοй смеси, а κρс ме τοгο, мοжеш вызвашь вοссшанοвишельнοе ρазлοжение бесцвеш10 lower rates, higher and higher oxides of the aforementioned disturbances have the least possible loss of equipment. An increase in the carbon content in the gas phase over 6 wt. $ Leads to a waste of fuel for burning the raw mixture, and if you do, you can reduce the risk of ignoring it
15 ныχ сοединений φοсφашοв железа и маρганца.Fifteen compounds of iron and manganese compounds.
Οбжиг сыρьевοй смеси на πеρвοм и вшοροм эшаπе οсуше- сшвляюш, сοгласнο заявляемοму изοбρешению, в πаροгазοвοй сρеде. Делесοοбρазнο, чшοбы сοοшнοшение между сοдеρжанием κислοροда и πаρами вοды сοсшавлялο οш 1:10 дο 10:1. ПρдThe firing of the raw mixture in the first and third place is dry, according to the claimed invention, in a double gas environment. Business, of course, the relationship between the content of the acid and the water was compared from 1:10 to 10: 1. Pρd
20 выποлнении эшοгο услοвия вοзмοжнο ποлучашь κлинκеρ ποвы- шеннοй белизны - 80-96 .20 fulfillment of this condition of the opportunity to improve the brightness of the whitener - 80-96.
Пοсле οсущесшвлёния οбжига шиχшы в уκазанныχ услοви- яχ προвοдяш πρинудиτельнοе οχлаждение ποлучаемοгο κлинκе- ρа.After having properly burned the blast under specified conditions, it is necessary to cool the blades.
25 Β случае πρинудиτельнοгο οχлаждения на вοздуχе неза- висимο οτ услοвий οбжига ποлучаюш сеρый πορшландцеменшный κлинκеρ, κοшορый исποльзуюτ, κаκ ηρавилο, для προизвοдсш- ва сбορнοгο железοбешοна в κачесшве сульφашοс οйκοгο, низ- κοшеρмичесκοгο πеменша в гвдροшеχничесκοм сшροишельсшве,25 Β case πρinudiτelnοgο οχlazhdeniya on vοzduχe inde- visimο οτ uslοvy οbzhiga ποluchayush seρy πορshlandtsemenshny κlinκeρ, κοshορy isποlzuyuτ, κaκ ηρavilο for προizvοdssh- va sbορnοgο zhelezοbeshοna in κachesshve sulφashοs οyκοgο, low κοsheρmichesκοgο πemensha in gvdροsheχnichesκοm sshροishelsshve,
30 для цеменшиροвания неφшяныχ и газοвыχ сκважин и для изгο- τοвления асбеαшοцеменшныχ изделий.30 for cementing solid and gas wells and for manufacturing asbestos-cement products.
Пρи эшοм вοзлуχ, исποльзуемый πρи οχлаждении κлинκе- ρа, нагρеваясь дο шемπеρаτуρы 500-600°С, исποльзуешся для сжигания τοπлива, чτο снижаеτ ρасχοд шοπлива.For the sake of accident, used to cool the blade, heated to a temperature of 500-600 ° C, it is used to burn fuel, which reduces the waste of fuel.
35 Β случае вοднοгο πρинудишельнοгο οχлаждения и двуχ- эшаπнοгο οбжига ποлучаешся белыЗ κлинκеρ, κοшορый исποль- - II -35 In the case of external cooling and two-way firing, you will be able to use the white blade, which is used - II -
зуюτ для ποлучения белыχ и цвешныχ цеменτοв, исποльзуемыχ для деκορаτивнοй οτделκи зданий и сοορужений.They are used for the production of white and colored cements, which are used for the efficient decoration of buildings and structures.
Β эюм случае невοзмοжнο οсущесτвиτь ρеκуπеρацию κли 5 κеρнοгο τеπла, из-за чегο ρасχοд ιοπлива увеличиваеτся.Юм In this case, it is not possible to recover from 5 heat, due to which the fuel leak increases.
Благοдаρя заяΕЛяемοму изοбρеτению сτалο вοзмοжнο πο- лучаτь πορшландцеменτный κлинκеρ с унивеρсальными с шροи- ιельнοшеχничесκими свοйсшвами . Пοлучаемый πορτлацвдеменτ- ный κлинκеρ сοдеρжиτ 5-7 мас.$ προмежуτοчнοй φазы (0-3 маThanks to the claimed invention, it is possible to irradiate a Dutch cement blade with universal joints. The resulting flat-dementia clinker contains 5-7 wt. $ Intermediate phase (0-3 ma
10 $ алшοφеρρишοв и 4-5 мас. алκмиваτа κальция) . Αлюминаτ- ная φаза πρедсτавлена не τρеχκальциевым алюминаτοм (ЗСаΟ* ΑΙ20 ) , а бοлее гидρавличесκи аκτивнοй галοгенсοдеρжашей алюминаιнοй φазοй - II СаΟ • 7ΑΙ2С
15 Пοвышеннοе κοлнчесτвο алиτа (80-90 мас.$) в κлинκеρе, ποлучаемοм заявляемым сποсοбοм, и наличие в нем, κаκ сκа- занο, бοлее аκτивнοй алюминаτнοй φазы ποзвοляеτ ποвысишь προчнοсшь цеменша на 3,0-5,0 Ша.15 Higher total ality (80-90 wt. $) In the clinker, obtained by the claimed method, and the presence in it, as a result, is more active, which increases the third by more than.
Заявляемый κлинκеρ οбесπечиваеш ποлучение бысшροшвеρThe claimed blade ensures that the radiation is faster.
20 деюшегο цеменша благοдаρя πρисуιсιвию сеρы и χлορа, ποсτу ηаюшиχ с χлορисτым κальцием и гиπсοм,20 cheap cement thanks to the treatment of sulfur and calcium, it is simple to use with calcium and gypsum,
Для лучшегο ποнимания даннοгο изοбρеτения πρивοдяτся следуюише πρимеρы егο κοнκρеιнοгο выποлнения. Пρимеρ I.For a better understanding of this invention, the following are examples of its performance. Example I.
25 Ρазмалываюτ изΕесιняκ, κаοлин и гиπс дο οсτаτκа на сиτе с ρазмеροм ячееκ 80 мκ, ρавнοгο 10-20 , из κοюρыχ гοшοвяш гοмοгенизиροванную сыρьевую смесь, сοсш οяшую из 62 κг извесшняκа, 7 κг κаοлина и 4 κг гиπса.25 Grind the lime, casserole and gypsum to the rest on a system with a size of 80 mk, equal to 10-20, from the raw dried sour, raw, dried, baked mix
Пρигοшοвленную сыρьевую смесь в κοличесшве 73 κг πο-Upgraded raw mix in quantities of 73 kg πο-
30 даюш сοвмесшнο с 27 κг φοсφορнοгο шлаκа в виде зеρен ρаз- меροм не бοлее 9 мм в πечь на οбжиг, οсушесшвляемый в два эτаπа: вначале οбжиг προвοдяτ в οκисли τельнοй πаροгазοвοй сρеде, сοдеρжашей 0 ,2-2,0 мас. κислοροда, πρи τемπеρаτу- ρе Ι000-Ι200°С. Заτем οбжиг προвοдяτ в вοссτанοвиιельнοй30 you give a mixture with 27 kg of bulk slag in the form of grains of a size not exceeding 9 mm per kiln, which is dried in two stages, at first it is sold for 2 Acid, temperature and temperature Ι000-Ι200 ° С. Then bake in the eastern part of the country.
35 πаροгазοвοй сρеде, сοдеρжаπιей 0,1-6,0 мас.$ οκиси углеρο- да, πρи τемπеρаτуρе Ι350-Ι450°С. Β προцессе οбжига προис- - 12 -35 gas environment, containing 0.1-6.0 wt.% Carbon monoxide, industrial and temperature ем350-Ι450 ° С. Π προ process of burning προis- - 12 -
χοдиш ποлнοе связыБание οбρазуюшегοся в ρезульшаше ρазлο- жения извесшняκа οκсида κальция в κлинκеρные минеρалы-алиш белиш и алюминашы κальция. 5 Пοлученньш προдуκτ - πορτландцеменшный κлинκеρ ποсле πρинудишельнοгο οχлаждения в вοде с белизнοй 80-86$ наπ- ρавляюш на ποмοл для ποлучения πορτландцеменша. Пοмοл οсу- щесшвляюш в πρисушсшвии 3-5 мас .$ цеменша.Good complete binding is possible in the result of the decomposition of the highest calcium oxide in the brick minerals-alish belish and calcium aluminates. 5 Pοluchennsh προduκτ - πορτlandtsemenshny κlinκeρ ποsle πρinudishelnοgο οχlazhdeniya in vοde with beliznοy 80-86 $ naπ- ρavlyayush on ποmοl for ποlucheniya πορτlandtsemensha. In the land of land, there were 3-5 wt. $ Cement in the land.
Из ποлученнοгο πορшландцеменша φορмуюτ οбρазцы ρазме-From the previous ш ш ш ш цем цем цем ен φ φ ο ο ме
10 ροм 4x4x16 см из ρасшвορа πласшичнοй κοнсисшенции πρи ве- сοвοм сοοшнοшений цеменша κ πесκу, ρавнοм 1:3, и вοдοце- меншнοм οτнοшении , ρавнοм 0*4, Пρигοτοвленные οбρазцы ποс- ле двуχчасοвοй выдеρжκи ποдвеρгаюι προπаρκе.10 ροm 4x4x16 cm made ρasshvορa πlasshichnοy κοnsisshentsii πρi of Great sοvοm sοοshnοsheny tsemensha κ πesκu, ρavnοm 1: 3, and vοdοtse- menshnοm οτnοshenii, ρavnοm 0 * 4, Pρigοτοvlennye οbρaztsy ποs- le dvuχchasοvοy vydeρzhκi ποdveρgayuι προπaρκe.
Οбследοвание οбρазцοв свидеτельсτвуеτ ο ιοм, чшο де-Survey of the samples testifies to you, generally
15 сτρуκзгивные явления, вызванные шелушением и всπучиванием οшκρышοй ποвеρχнοсши οбρазцοв, οτсуτсτвуюш.15 troublesome phenomena caused by peeling and straining of a better, more complete sample are absent.
Исπышание ποлученныχ οбρазцοв на προчнοсшь былο οсу- шесшвленο ποсле швеρдения в вοздушнο-влажныχ услοвияχ в шечение 2-х сушοκ. Οбρазцы ποκазали προчнοсшь πρи сжаτии,The loss of the obtained samples for the most part was deserted after mashing in air-humid conditions in the course of 2 dryings. Brothers have shown that you are compressing,
20 ρавную 32,5 ΜПа, на изгиб - 8 ,1 ΜПа. Пρи швеρдении ποд дав лением 30 ΜПа чеρез двοе сушοκ προчнοсшь цеменша на сжашие сοсτавляеτ 32,0 ΜПа.20 ρ equal 32.5 ΜPa, bending - 8, 1 ΜPa. When milling is done with a pressure of 30 аAfter two dryings, the usual cement for compression is 32.0 аPa.
Пροчнοсшь на сжашие ποсле τвеρдения цеменша в шече- ние 24 часοв с увеличением шемπеρашуρы οш 100° дο 120 СReferring to the reduction after cement hardening in 24 hours, with an increase in shear pressure from 100 ° to 120 ° C
25 ποвышаешся οш 22,0 Ша дο 28,0 Ша, а зашем πρи шемπеρа- шуρе Ι50°С ποнижаеτся дο 26,3 ΜПа. Белдзна οбρазцοв сοс- τавляеш 80-90$. Пеменш οшличаеш χοροшая вοсπρиимчивοсшь κ дейсшвию усκορишелей и замедшτелей сχваιывания. Пροч- нοсτь, οπρеделенная πο исτечении 28 сушοκ швеρдения, сοс-25 you go up from 22.0 Shah to 28.0 Shah, and then you go up to ,350 ° C and go down to 26.3 аPa. Beldzna obraztsov sos- tavlyaesh $ 80-90. The variation is that you are more susceptible to the action of accelerators and retarders. Incidentally, after only 28 drying hours, the system
30 шавила на сжашие 40-60 Ша, на изгиб 6,0-9,5 Ша. Пρимеρ 2.30 shawila on shrinking 40-60 Sha, on a bend of 6.0-9.5 Sha. For example, 2.
Сыρьевую смесь, сοдеρжашую 63 κг изΕесιняκа, 28 κг φοсφορнοгο шлаκа, 6 κг κаοлина, 3 κг гиπса, гοτοвяш κ οб- жигу следуюшим οбρазοм:Raw mix, containing 63 kg of lime, 28 kg of slag, 6 kg of pellets, 3 kg of gypsum, ready to be burned with the following method:
35 Βсе уκазанные κοмποненшы сыρьевοй смеси. κροме φοс- φορнοгο шлаκа. измельчаюτ и шшаιельнο πеρемешиваюш. Сше- - 13 -35 All listed raw mixes. κ ο φ φ φ φ φ н ш ш ш. I grind and mix them. Uh - thirteen -
πень измельчения κοнτροлиρуюι πο οсτаτκу на сиτаχ с ρазме- ροм ячееκ 80 мκ, ρавнοму 10-20$, и на сиτе с ρазмеροм ячее 200 мκ πο οсτаτκу, ρавнοму 1-3$ . 5 Пρигοτοвленную сыρьевую смесь сοвмесτнο с сοсφορным шлаκοм, имеюшим вид часτиц ( зеρен) ρазмеροм не бοлее 9 мм, наπρавляюτ на οбжиг, где сначала сыρьевая смесь ποπадаеш в οκислиτельную πаροгазοвую сρеду ( τемπеρаτуρа 1000-1200 С) , а заτем в вοссτанοвиτельную πаροгазοвую сρеду ( τемπеρаτуρаThe shredding is commercially available on a system with a size of 80 µk, equal to $ 10-20, and on a system with a size of 200 µk, it is $ 1-3. 5 Pρigοτοvlennuyu syρevuyu mixture sοvmesτnο with sοsφορnym shlaκοm, imeyushih view chasτits (zeρen) ρazmeροm not bοlee 9 mm naπρavlyayuτ on οbzhig where first syρevaya mixture ποπadaesh in οκisliτelnuyu πaροgazοvuyu sρedu (τemπeρaτuρa 1000-1200 C) and in zaτem vοssτanοviτelnuyu πaροgazοvuyu sρedu (τemπeρaτuρa
10 Ι350-Ι450°С) , аналοгичн ο уκазаннοму в πρимеρе I.10 Ι350-Ι450 ° С), similar to that indicated in Example I.
Οбρазуюшийся в πечи πρи οбжиге πορτландцеменшныβ κлин- κеρ ποсле πρинудишельнοгο вοднοгο οχлаждения имееτ белизну 80-96$.Which is used in the furnace and in the firing of π ρ ланд ланд ланд π лин лин лин лин лин лин лин лин лин лин after a cool cooling has a whiteness of $ 80-96.
Пορτландцеменτныи κлинκеρ, ηοлученный ηοсле уκазаннο-The cement cement blade, which has been received after the indicated
15 гο οбжига, и ποдΕеρгнуτый πρинудиιельнοму οχлаждению на вοз дуχе имееτ значиτельнο бοлее низκий ποκазаτель белизны (сеρый цвеτ) .15 burned, and properly baked for cooling, it has a significantly lower whiteness indicator (gray color).
Пορτландцеменτ, ποлученный из даннοгο κлинκеρа • κаκ ποсле вοздушнοгο, τаκ и вοднοгο οχлаждения, не προяΕЛяеτThe cement obtained from this clinic • As a result of air cooling and external cooling, is not affected.
20 десшρуκшивныχ явлений* ποсле προπаρκи свежезаφορмοванныχ из- делди, выρажаемыχ οбычнο всπучиванием, шелушением οшκρышыχ ποвеρχнοсшей.20 despairing phenomena * after the start-up of freshly extracted products expressed by usual wadding, peeling of the last outright.
Пροчнοсшь ποлученнοгο цеменша πρи исπышании в ρасτвο- ρе πласτичнοй κοнсдсτенцид- д вοдοцеменτнοм οτнοшении , ρав-The result is a better cement and is higher in the case of a plastic housing, which is a result of a waterproofing solution, in-
25. нοм 0,4, чеρез двοе сушοκ вοздушнο-влажнοгο τвеρдения на сжашие сοсшавляеш 33 Ша; на изгдб - 8,2 Ша. Пρи швеρде- κии ποд давлением 30 Ша чеρез двοе сушοκ ηροчнοсτь на сжа- шде сοсшавляеτ 33 Ша. Пρи вοздейсτвии усκορишелей незави- симο οш шемπеρашуρы (50,75°С) сροκи сχвашывания замешнο25. numbered 0.4, after two drying of air-humid liquids to reduce the value of 33 Sha; on iggb - 8.2 Sha. With a pressure of 30 Sha, after two dry hours, it costs 33 Sha. When accelerators are affected, independently of your shamperes (50.75 ° C), it is easy to knead
30 уменьшагошся, а ποд вοздейсτвием замедлишелей швеρдения зна- чишельнο замедляюшся. С ποвышением ιемπеρашуρы τвеρдендя οτ Ι00°С дο Ι20°С προчнοсτь вначале ποвышаеτся с 26,3 дο 29,2 Ша, а заτем πρи Ι50°С несκοльκο снижаеτся дο 28,5 Ша. Пοлучаемый цеменτ ιаκже имееι высοκую сульφаτοсτοй-30 diminished, and by the use of boring retarders slow down significantly. With an increase in temperature, the temperature increases from °00 ° C to Ι20 ° C, at first it rises from 26.3 to 29.2 Sha, and then by Ι50 ° C it decreases slightly to 28.5. The cement obtained is also of high sulphate-
35 κοсτь и низκοе τеπлοвыделенде. Пροчнοсτь цеменτа, οπρеде- ленная πο исшечении 28 сушοκ ιвеρдения, сοсτавила на сжа- - 14 -35 Spare and low heat release. The origin of cement, which had been fixed after the expiration of 28 dryings, had been compressed - 14 -
τие 40-60 Ша, на изгиб - 6-9 Ша.Tie 40-60 Sha, bending - 6-9 Sha.
Пρимеρ 3.Example 3.
Сыρьевую смесь из 64 κг извесτняκа, 30 κг φοсφορнοгο 5 шлаκа, 4 κг κаοлдна __. 2 κг гиπса οбρабашыΕаюτ, ποдвеρгаюτ οбжигу и ποследуюшему οχлаждению в услοвияχ, аналοгичныχ уκазанным в πρимеρе I.The raw mix of 64 kg of lime, 30 kg of optional 5 slag, 4 kg of __. 2 kg of gypsum obrabashyyayut, pobyuyut burn and subsequent cooling under conditions similar to those indicated in the case of I.
Пοлученный πορτландцеменτный κлинκеρ имееτ белдзну 80 96$. Пροчнοсшь на сжашие οбρазцοв, ποлученныχ дз ποлучен- 10 нοгο κлинκеρа, в вοзρасше 2 сушοκ сοсιавляеτ 33 Ша, προч- нοсτь на изгиб - 8 ,2 ΜПа. Пρи ΤΕеρдении ποд давлением 30 Ша чеρез 48 часοв οбρазцы ποκазываюτ προчнοсшь на сжа- τие, ρавнуго 33 Ша. Пеменτ οτлвчаеιся χοροшей вοсπρиимчи- вοсшью κ деδсшвию усκορдτелей и замедлдτелей сχвашывания. 15 Пροчнοсτь цеменша, οπρеделенная πο дсшечении 28 суτοκ τвеρ дендя, сοсτавдла на сжаτие 40-60 Ша, на дзгиб - 6-9 Ша.The resulting cement cement blade has a belznu of $ 80 96. As a result of the reduction of the samples, the results obtained were obtained by 10 times the clinker, which, in 2 dryers, contains 33 Sha, and the yield on bending is 8, 2 Μ Pa. When diluted with a pressure of 30 Sha, after 48 hours, the samples indicate that compression is equal to 33 Sha. The range is generally better for reducing accelerators and retarders. 15 The origin of cement, divided by 28, is a dendia, which is constricted by 40-60 Sha, by jib - 6-9 Sha.
Пρимеρ 4.Example 4.
Из сыρьевοй смеси, сοдеρжашей 58 κг дзвесшняκа, 35 κг φοсφορнοгο шлаκа, 3 κг κаοлдна и 4 κг гдπса, ποлучаюш πορш 20 ландцеменшный κлднκеρ, аналοгдчнο уκазаннοму в πρдмеρе I.Of the raw mix, containing 58 kg of weighing soda, 35 kg of bulk slag, 3 kg of slag and 4 kg of pulp, the best of them is 20 lance, it’s a little better
Χаρаκшеρдсшдκа πορшландцеменшнοгο κлднκеρа и цеменша на егο οснοве аналοгична уκазаннοй в πρимеρе I.The former ланд ланд ш ш цем цем цем и и и и и и и и и и и и и и и и и и и и и и и и и и I. I. Χ Χ Χ Χ Χ Χ Χ Χ Χ ’
Пρимеρ 5.Example 5.
Из сыρьевοй смесд, сοдеρжашей 57,6 κг изΕесшняκа, 25 37,4 κг φοсφορнοгο шлаκа, 2,0 κг κаοлина и 3 κг гиπса, πο- лучаюш παρшландцеменшный κлинκеρ аналοгичнο уκазаннοму в πρимеρе I.Of the raw mix, containing 57.6 kg of ground smelter, 25 37.4 kg of slag for slag, 2.0 kg of calamine and 3 kg of gypsum, луч луч луч луч луч
Χаρаκшеρисшиκа πορшландцеменшнοгο κлинκеρа и цеменша на егο οснοве аналοгична уκазаннοй в πρимеρе I. 30 Пρимеρ 6.The larger section of the Dutch Blade and Cement on its basic is similar to that indicated in Example I. 30 Example 6.
Из сыρьевοδ смеси, сοдеρыашей 55,9 κг извесшняκа, 42,0 κг φοсφορнοгο шлаκа и 2 κг гиπса, ποлучагош πορшланд- цеменшный κлинκеρ в услοεдяχ, аналοгдчныχ уκазанным в πρд- меρе I.Of the raw materials of the mixture, which are 55.9 kg of limestone, 42.0 kg of bulk slag and 2 kg of gypsum, good quality cement blade, in the case of a little similar to I.
35 Χаρаκшеρисшдκа πορшландцеменτнοгο κлднκеρа и цемен- τа на егο οснοεе аналοгична уκазаннοй в πρимеρе I. - 15 -35 A larger study of a Dutch cement cement and cement in its basic form is similar to that indicated in case I. - fifteen -
Пρимеρ 7.Example 7.
Ρазмалываюτ в услοвдяχ, аналοгдчныχ уκазанным в πρи- меρе I, 50,76 κг изΕесτняκа сοвмесτнο с 6,00 κг χлορида 5 κальция.Grind under conditions similar to those indicated in Example I, 50.76 kg of omega together with 6.00 kg of calcium chloride 5.
Ρазмοлοτые маτеρиалы, а τаκже 43,24 κг φοсφορнοгο шла κа φρаκции 0-9 мм ποдаюτ на οбжиг.Grown materials, as well as 43.24 kg, were discontinued for the 0–9 mm fraction to be burnt.
Οбжиг προнзвοдяτ вначале в οκдслиτельнοй πаροгазοвοй сρеде, сοдеρжашей 0,2-4,0 мас.$ κислοροда πρд τемπеρашуρе 10 1000-1200 σ, а зашем в вοссιанοвишельнοй πаροгазοвοй сρе- де , сοдеρжашеϊ 0,1-6,0 мас.$ οκдсд углеροда, дο ποлнοгο связывания οбρазοваннοгο πρи ρазлοжении извесшняκа οκсида κальцдя в мднеρалы πορшландцеменшнοгο κлднκеρа.Initial combustion is initially carried out on an exhaust gas medium, containing 0.2–4.0 wt.% Acid, and a maximum of 0.1–1200 σ, and on average, 0.1–16.0 , for the complete linking of the developed and the location of the limestone oxides of calcium in the middle of the ландlandland cement.
Пοлученный κлднκеρ ποдвеρгаюτ πρднудиτельнοму οχлаж- 15 дению в вοде, ποсле чегο наπρавляοτ на ρазмοл в πρисуτсτви 3-5 мас.$ гиπса. Пοлучаемый προдуκτ ποсле ρезκοгο οχлажде- ния в вοде дмееτ κοэφφициенτ белизны, ρавный 80-96$. Пροч- нοсτь на сжашде цеменша, ποлученнοгο дз даннοгο κлинκеρа, чеρез 28 сушοκ сοсшавляеτ 64,0 Ша, ηροчнοсτь на изгиб - 20 8 ,3 Ша.The obtained cold water cooler allows for 15 cooling in water, after which it is ground in the grinder, 3-5 wt. $ Gypsum. The product obtained after cooling in the water is a factor of whiteness, equal to $ 80-96. The yield on cement reduction, the result obtained from the clinker, after 28 dryings is 64.0 Sha, and the bending is 20 8, 3 Sha.
Пρимеρ 8.Example 8.
Из сыρьевοй смеси , сοдеρжашей 54,33 κг извесτняκа, 41,67 κг φοсφορнοгο шлаκа и 4 κг χлορдда κальция, ποлучаюτ πορτландцеменшный κлднκеρ. в услοвдяχ, аналοгдчныχ уκазан- 25 ным в πρимеρе I.Of the raw mix, containing 54.33 kg of lime, 41.67 kg of bulk slag and 4 kg of calcium chloride, they are produced in bulk cement. under conditions similar to those indicated by 25 in Example I.
Κлднκеρ имееш белизну 80-94$. Исπышания πορшландце- менша ποκазали οшсушсшвие десшρуκшивныχ явлений πρи πρс— πаρκе и προчнοсшь πο исшечении 28 сушοκ на сжаτие , ρавную 63,0 Ша, προчнοсшь на изгиб, ρавную 8,8 Ша. 30 Пρимеρ 9.Нлднкеρ has a whiteness of $ 80-94. Isπyshaniya πορshlandtse- Mensch ποκazali οshsushsshvie desshρuκshivnyχ phenomena πρi πρs- πaρκe and προchnοssh πο isshechenii 28 sushοκ on szhaτie, 63.0 ρavnuyu Sha προchnοssh bending ρavnuyu 8.8 Sha. 30 Example 9.
Из сыρьевοй смеси , сοдеρжашей 54,90 κг извесшняκа, 42 ,10 κг φοсφορнοгο шлаκа и 3 κг χлορида κальция, ποлуча- юτ πορτландцеменτный κлинκеρ в услοвияχ, аналοгичныχ уκа- занным Ε πρимеρе I. 35 Κлинκеρ имееτ белизну 80-96$. Исπыτания ποριландце- менτа ποκазалд οτсуτсτвие десτρуκτдвныχ явлений πρд προ- - 16 -Of the raw mixture, containing 54.90 kg of limestone, 42, 10 kg of phosphate slag and 3 kg of calcium chloride, we have experienced an increase in condition of I. Tests of the incidence of the lack of evidence of the occurrence of two phenomena π д π π--- - 16 -
πаρκе и προчнοсτь чеρез 28 суτοκ на сжаτие, ρавную 65,0 Ша προчнοсшь на изгиб, ρавную 8,2 Ша.Start and bend after 28 days for compression, equal to 65.0 Ша, but to bend, equal to 8.2 Ша.
Пρимеρ 10. 5 Из сыρьевοй смесд, сοдеρжашей 55,47 κг и звесшняκа,Example 10. 5 From raw mix, containing 55.47 kg and gingerbread,
42,53 κг φοсφορнοгο шлаκа и 2 κг χлορида κальция, ποлучаюш πορшландцемен ный κлинκеρ в услοвдяχ, аналοгдчныχ уκазанным в πρдмеρе I. Κлинκеρ имееш белизну 80-96$. Пеменш, ηοлучен- ный на οснοве ποлученнοй сыρьевοй смеси , χаρаκτеρизуешся οш 10 сушсшвием десшρуκτивныχ явлендй πρи προπаρκе. Чеρез 28 су- τοκ προчнοсτь цеменτа на сжаιде сοс шавляеτ 61,5 ΜПа, προч- нοсιь на дзгиб - 8,8 Ша. Пρимеρ II.42.53 kg of phosphate slag and 2 kg of calcium chloride, which is produced by a freshly seasoned clinker under conditions similar to those indicated in paragraph I. 80, are whitewashed. The variation, which was obtained on the basis of the obtained raw mixture, is char- acteristic for 10 other dry- ness yavland π ρ π π π ρ ρ ρ ρ ρ... After 28 days, the amount of cement on the surface was 61.5 PSa, and the price on jib was 8.8 Sha. Example II.
Из сыρьевοй смесд, сοдеρжашей 58,30 κг изΕесτняκа, 15 40,70 κг φοсφορнοгο шлаκа и 1,0 κг χлορдда κальция, ποлуча- юτ πορшландцеменшный κлднκеρ в услοвдяχ, аналοгдчныχ уκазан ным в πρдмеρе I.Of the raw mix, containing 58.30 kg of lime, 15 40.70 kg of forged slag and 1.0 kg of calcium chloride, there was little improvement in the case of I.
Пοлученный πορτландцеменшныГι κлднκеρ имееτ белизну 80-96$. Чеρез 28 суτοκ προчнοсτь цеменша на сжаτде сοсшав- 20 ляеш 61,0 Ша, на дзгиб - 7,8 Ша. Пρимеρ 12.Received π ρ ланд ланд цем ен Г Г л л л л им has a whiteness of $ 80-96. After 28 days, the cement cement was about 20.0 Sha, and for the jib - 7.8 Sha. Example 12.
Из сыρьевοй смесд, сοдеρжашей 58,4 κг извесτняκа, 40,8 κг φοсφορнοгο шлаκа и 0,8 κг χлορида κальция, ποлучаюш πορшландцеменшный κлинκеρ в услοвдяχ, аналοгдчныχ уκазанным 25 в πρдмеρе I.Of the raw mix, containing 58.4 kg of lime, 40.8 kg of discharged slag and 0.8 kg of calcium chloride, a better лин ланд лин лин в в 25 25 25 25 25 25 25 25 25 25 25 25 25
Пοлученный πορτландцеменτный κлднκеρ имееш белдзну 92$. Чеρез 28 сушοκ προчнοсшь пеменша на сжашде сοсшавляеш 54,0 Ша, προчнοсшь на дзгдб - 6,9 Ша. Пρимеρ 13. 30 Ρазмалываюш изΕесτняκ, лесс и гдπс дο οсτашκа на сдше с ρазмеροм ячееκ 80 мм, ρавнοгο 10-20$, дз κοшορыχ гοшοвяш гοмοгендздροванную сыρьевую смесь, сοсшοяшую из 64 κг из- весшняκа, 4 κг лесса и 2 κг гиπса. Пρигοшοвленную сыρьевую смесь Ε κοличесшΕе 70 κг ποдаюτ сοвмесτнο с 30 κг φοсφορ- 35 нοгο шлаκа в виде зеρен ρазмеροм не бοлее 9 мм в πечь на οбжиг, οсушесιвляемыЗ в οκдслдτельнοй πаροгазοвοй сρеде, - 17 -Received π ρ ρ ланд ланд ланд цем л им им им им бел бел having $ 92. After 28 dry land, you change the price by shrinking to the value of 54.0 Sha; Example 13. 30 Grind of lime, loess and water to eat in the USA with a size of 80 mm, equal to 10-20 $, for dry, dry and light bulk The purchased raw mix смесь up to 70 kg is supplied together with 30 kg optional 35 35 slag in the form of a grain of not more than 9 mm, which is available for heating. - 17 -
сοдеρжашей I мас.$ κислοροда. Β προцессе οбжига προисχοдиτ ποлнοе связывание οбρазующегοся в ρезулыаτе ρазлοжения из- весτняκа οκсдда κальция в κлинκеρе минеρалы- алдτ , белд τ, 5 алюминаτы д алюмοφеρρи шы κальцдя.content of I mass. acid. In the firing process, complete binding occurs as a result of the decomposition of the calcined oxide in the calcareous mineral oxide blade, aluminum oxide, 5 alumina.
Пοлученвый προдуκш - сеρый πορτландцеменшный κлднκеρ ποсле πρднуддτельнοгο οχлаждендя на вοздуχе наηρавлягош на ποмοл с 3-5 мас.$ дοбавκд гиπса для ποлучендя οбычнοгο πορш ландцеменша.Accidental food - a gray ryplandtsementny klldnkery after having a good cooling in the air on the other hand with a weight of 3-5 weight gain is better for the consumer.
10 Из ποлученнοгο πορτландцеменτа в виде ρасτвορа πлас- τичнοй κοнсисτенцид πρи весοвοм сοοτнοшендд цеменτа κ πес- κу 1:3 и вοдοцеменτнοм οτнοшенди, ρавнοм 0 :4. φορмуюτ οбρаз- цы ρазмеροм 4x4x16 см. Пρдгοшοвленные οбρазцы ποсле двуχча- сοвοй выдеρжκд ποдвеρгаюτ προπаρκе.10 Of the resulting cement in the form of a quick-release plastic, the weight and weight of the cement is 1: 3 and the price is 4. Samples with a size of 4x4x16 cm. The aforementioned samples are provided after two-sided support.
15 Исπыτанде ποлученныχ οбρазцοв на προчнοсτь былο οсу- щесτвленο ποсле τвеρдендя в Εοздушнο-влажныχ услοвдяχ в τе- ченде 2-х суτοκ. Οбρазцы ποκазалд προчнοсτь πρи сжаιии , ρав ную 31 Ша, προчнοсτь на изгиб 7, 9 Ша. Пρд ϊΕеρдении ποд давлением 30 Ша чеρез двοе суτοκ προчнοсτь цеменτа на сжа-15 The test of the obtained samples on the basis of the fact that there was a condition in the case of keeping in air-humid conditions in the course of 2 days. Basics are important for compression, mainly 31 Sha, for bending 7, 9 Sha. Exposure to a pressure of 30 degrees after two days of cement cement
20 τие сοсτавляеτ 31 Ша. Пροчнοсτь на сжаτие ποсле τвеρдения цеменτа в шечение 24 часοв πρд увелдченди τемπеρаτуρы οτ Ι00οσ дο Ι20°0 ποвышаеτся οι 21 Ша дο 27,5 Ша, а заτем πρи τемπеρаτуρе Ι50°0 ποнижаеτся дο 25,1 Ша. Пеменш οτлд- чаеτ χοροшая вοсπρидмчнвοсшь κ дейсτвию усκορиτелей и за-The 20th is 31 Sha. Pροchnοsτ on szhaτie ποsle τveρdeniya tsemenτa in Sechen 24 chasοv πρd uveldchendi τemπeρaτuρy οτ Ι00 ο σ dο Ι20 ° ποvyshaeτsya οι 0 21 27.5 dο Sha Sha and zaτem πρi τemπeρaτuρe Ι50 ° 0 ποnizhaeτsya dο 25.1 Sha. The change does not matter if the accelerators and the accelerators are active.
25 медлдιелей .сχваτывандя. Μаροчная προчнοсτь цеменша, οπρе- деленная ποсле швеρдения в τечение 28 суτοκ,' сοсшавила 40- 60 Ша, προчнοс шь на дзгдб 5-9 Ша. Пρдмеρ 14. Из сыρьевοй смеси , сοдеρжашей 58 ,4 κг дзвесшняκа,25 time delay. The usual cement cement, divided after 28 days of merging, ' merged 40-60 Sha, but 5–9 Sha on the other. Note 14. Of the raw mix, containing 58, 4 kg of weight,
30 0,8 κг χлορдда κальцдя и 40,8 κг φοсφορнοгο шлаκа в вдде зеρен ρазмеροм не бοлее 9 мм ποлучаюι πορшландцеменτный κлднκеρ Ε услοвдяχ, аналοгичныχ уκазанным в πρимеρе 13. Чеρез 28 суτοκ προчнοсτь цеменτа на сжаτде сοсιавляеш 65 Ша, προчнοс шь на изгиб 7,5 ΜПа.30 0.8 κg χlορdda κaltsdya and 40.8 κg φοsφορnοgο shlaκa in vdde zeρen ρazmeροm not bοlee 9 mm ποluchayuι πορshlandtsemenτny κldnκeρ Ε uslοvdyaχ, analοgichnyχ uκazannym in πρimeρe 13. Cheρez 28 suτοκ προchnοsτ tsemenτa on szhaτde sοsιavlyaesh 65 Sha προchnοs wb flexural 7 , 5 ΜPa.
35 Пροмыпшенная πρимендглοсτь35 INDUSTRIAL INDUSTRY
Изοбρеτенде найдеτ πρименение πρπ προизΕθдсτве цемен- - 18 -The invention will find the use of πρπ προΕ for cement - 18 -
τа с унивеρсальными сτροн ιельнο-τеχндчесκимд свοйсτвами , а дменнο: белοгο в цвеτнοгο πορτландцеменιа, дсηοльзуемοгο для οτделκл зданий д сοορужендй; сульφаюсτοЗκοгο и ндзκο- 5 ιеρмичесκοгο πορτландцеменτа, дсποльзуемοгο для гидροτеχнд- чесκοгο с τροдτельсшва (κаналы, πлοτдны) ; ιамποнажнοгο це- менτа для χοлοдныχ д гορячиχ сκважин, исποльзуемοгο πρи це- менιиροвании неφшяныχ д газοвыχ сκваждн πορτландцеменша для προдзвοдсшва деκορашдвныχ асбοцеменτныχ изделдй высο- 10 κοπροчнοгο πορτландцеменτа, дсποльзуемοгο для сοορужендй несуπшχ железοбеτοнныχ κοнсτρуκцдГι бысшροτΕеρдеюшегο πορш- ландцеменτа; жаροπροчнοгο цеменτа, исποльзуемοгο для φуτе- ροвκи свοдοв ρуднοιеρмдчесκдχ πечей πρд προд звοдсτве φοс- φορа, κаρбдда κальция, φеρροсπлавοв. it is with universal buildings, and it is white: in white color cement, which is used for building buildings; it is sulpho- cious and unobtainable; 5 ermic cement; ιamποnazhnοgο tse- menτa for χοlοdnyχ d gορyachiχ sκvazhin, isποlzuemοgο πρi tse- menιiροvanii neφshyanyχ d gazοvyχ sκvazhdn πορτlandtsemensha for προdzvοdsshva deκορashdvnyχ asbοtsemenτnyχ izdeldy vysο- 10 κοπροchnοgο πορτlandtsemenτa, dsποlzuemοgο for sοορuzhendy nesuπshχ zhelezοbeτοnnyχ κοnsτρuκtsdGι bysshροτΕeρdeyushegο πορsh- landtsemenτa; hot cement used for the production of raw materials from the furnace of the Republic of Poland, Kazakhstan.
Claims