Classifications

• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
  • C04B14/38—Fibrous materials; Whiskers
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B27—WORKING OR PRESERVING WOOD OR SIMILAR MATERIAL; NAILING OR STAPLING MACHINES IN GENERAL
  • B27N—MANUFACTURE BY DRY PROCESSES OF ARTICLES, WITH OR WITHOUT ORGANIC BINDING AGENTS, MADE FROM PARTICLES OR FIBRES CONSISTING OF WOOD OR OTHER LIGNOCELLULOSIC OR LIKE ORGANIC MATERIAL
  • B27N3/00—Manufacture of substantially flat articles, e.g. boards, from particles or fibres
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B27—WORKING OR PRESERVING WOOD OR SIMILAR MATERIAL; NAILING OR STAPLING MACHINES IN GENERAL
  • B27N—MANUFACTURE BY DRY PROCESSES OF ARTICLES, WITH OR WITHOUT ORGANIC BINDING AGENTS, MADE FROM PARTICLES OR FIBRES CONSISTING OF WOOD OR OTHER LIGNOCELLULOSIC OR LIKE ORGANIC MATERIAL
  • B27N3/00—Manufacture of substantially flat articles, e.g. boards, from particles or fibres
  • B27N3/002—Manufacture of substantially flat articles, e.g. boards, from particles or fibres characterised by the type of binder
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B13/00—Layered products comprising a a layer of water-setting substance, e.g. concrete, plaster, asbestos cement, or like builders' material
  • B32B13/02—Layered products comprising a a layer of water-setting substance, e.g. concrete, plaster, asbestos cement, or like builders' material with fibres or particles being present as additives in the layer
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B13/00—Layered products comprising a a layer of water-setting substance, e.g. concrete, plaster, asbestos cement, or like builders' material
  • B32B13/04—Layered products comprising a a layer of water-setting substance, e.g. concrete, plaster, asbestos cement, or like builders' material comprising such water setting substance as the main or only constituent of a layer, which is next to another layer of the same or of a different material
  • B32B13/08—Layered products comprising a a layer of water-setting substance, e.g. concrete, plaster, asbestos cement, or like builders' material comprising such water setting substance as the main or only constituent of a layer, which is next to another layer of the same or of a different material of paper or cardboard
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
  • B32B5/02—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by structural features of a fibrous or filamentary layer
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B14/00—Use of inorganic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of inorganic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
  • C04B14/38—Fibrous materials; Whiskers
  • C04B14/42—Glass
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B16/00—Use of organic materials as fillers, e.g. pigments, for mortars, concrete or artificial stone; Treatment of organic materials specially adapted to enhance their filling properties in mortars, concrete or artificial stone
  • C04B16/02—Cellulosic materials
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B18/00—Use of agglomerated or waste materials or refuse as fillers for mortars, concrete or artificial stone; Treatment of agglomerated or waste materials or refuse, specially adapted to enhance their filling properties in mortars, concrete or artificial stone
  • C04B18/04—Waste materials; Refuse
  • C04B18/18—Waste materials; Refuse organic
  • C04B18/24—Vegetable refuse, e.g. rice husks, maize-ear refuse; Cellulosic materials, e.g. paper, cork
  • C04B18/26—Wood, e.g. sawdust, wood shavings
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B20/00—Use of materials as fillers for mortars, concrete or artificial stone according to more than one of groups C04B14/00 - C04B18/00 and characterised by shape or grain distribution; Treatment of materials according to more than one of the groups C04B14/00 - C04B18/00 specially adapted to enhance their filling properties in mortars, concrete or artificial stone; Expanding or defibrillating materials
  • C04B20/0048—Fibrous materials
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B24/00—Use of organic materials as active ingredients for mortars, concrete or artificial stone, e.g. plasticisers
  • C04B24/24—Macromolecular compounds
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B24/00—Use of organic materials as active ingredients for mortars, concrete or artificial stone, e.g. plasticisers
  • C04B24/24—Macromolecular compounds
  • C04B24/26—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
  • C04B24/2623—Polyvinylalcohols; Polyvinylacetates
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B24/00—Use of organic materials as active ingredients for mortars, concrete or artificial stone, e.g. plasticisers
  • C04B24/24—Macromolecular compounds
  • C04B24/38—Polysaccharides or derivatives thereof
  • C04B24/383—Cellulose or derivatives thereof
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
  • C04B28/14—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing calcium sulfate cements
• • E—FIXED CONSTRUCTIONS
  • E04—BUILDING
  • E04C—STRUCTURAL ELEMENTS; BUILDING MATERIALS
  • E04C2/00—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels
  • E04C2/02—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by specified materials
  • E04C2/04—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by specified materials of concrete or other stone-like material; of asbestos cement; of cement and other mineral fibres
• • E—FIXED CONSTRUCTIONS
  • E04—BUILDING
  • E04C—STRUCTURAL ELEMENTS; BUILDING MATERIALS
  • E04C2/00—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels
  • E04C2/02—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by specified materials
  • E04C2/04—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by specified materials of concrete or other stone-like material; of asbestos cement; of cement and other mineral fibres
  • E04C2/043—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by specified materials of concrete or other stone-like material; of asbestos cement; of cement and other mineral fibres of plaster
• • E—FIXED CONSTRUCTIONS
  • E04—BUILDING
  • E04C—STRUCTURAL ELEMENTS; BUILDING MATERIALS
  • E04C2/00—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels
  • E04C2/02—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by specified materials
  • E04C2/26—Building elements of relatively thin form for the construction of parts of buildings, e.g. sheet materials, slabs, or panels characterised by specified materials composed of materials covered by two or more of groups E04C2/04, E04C2/08, E04C2/10 or of materials covered by one of these groups with a material not specified in one of the groups
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B13/00—Layered products comprising a a layer of water-setting substance, e.g. concrete, plaster, asbestos cement, or like builders' material
  • B32B13/14—Layered products comprising a a layer of water-setting substance, e.g. concrete, plaster, asbestos cement, or like builders' material next to a fibrous or filamentary layer
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
  • B32B2262/10—Inorganic fibres
  • B32B2262/101—Glass fibres
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2264/00—Composition or properties of particles which form a particulate layer or are present as additives
  • B32B2264/02—Synthetic macromolecular particles
  • B32B2264/0214—Particles made of materials belonging to B32B27/00
  • B32B2264/0221—Thermoplastic elastomer particles
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2264/00—Composition or properties of particles which form a particulate layer or are present as additives
  • B32B2264/02—Synthetic macromolecular particles
  • B32B2264/0214—Particles made of materials belonging to B32B27/00
  • B32B2264/0228—Vinyl resin particles, e.g. polyvinyl acetate, polyvinyl alcohol polymers or ethylene-vinyl acetate copolymers
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2264/00—Composition or properties of particles which form a particulate layer or are present as additives
  • B32B2264/02—Synthetic macromolecular particles
  • B32B2264/0214—Particles made of materials belonging to B32B27/00
  • B32B2264/0228—Vinyl resin particles, e.g. polyvinyl acetate, polyvinyl alcohol polymers or ethylene-vinyl acetate copolymers
  • B32B2264/0235—Aromatic vinyl resin, e.g. styrenic (co)polymers
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2264/00—Composition or properties of particles which form a particulate layer or are present as additives
  • B32B2264/02—Synthetic macromolecular particles
  • B32B2264/0214—Particles made of materials belonging to B32B27/00
  • B32B2264/025—Acrylic resin particles, e.g. polymethyl methacrylate or ethylene-acrylate copolymers
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2264/00—Composition or properties of particles which form a particulate layer or are present as additives
  • B32B2264/02—Synthetic macromolecular particles
  • B32B2264/0214—Particles made of materials belonging to B32B27/00
  • B32B2264/0278—Polyester particles
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2264/00—Composition or properties of particles which form a particulate layer or are present as additives
  • B32B2264/04—Cellulosic particles, e.g. rayon
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2264/00—Composition or properties of particles which form a particulate layer or are present as additives
  • B32B2264/06—Vegetal particles
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2264/00—Composition or properties of particles which form a particulate layer or are present as additives
  • B32B2264/06—Vegetal particles
  • B32B2264/062—Cellulose particles, e.g. cotton
  • B32B2264/067—Wood particles
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2264/00—Composition or properties of particles which form a particulate layer or are present as additives
  • B32B2264/12—Mixture of at least two particles made of different materials
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2307/00—Properties of the layers or laminate
  • B32B2307/30—Properties of the layers or laminate having particular thermal properties
  • B32B2307/306—Resistant to heat
  • B32B2307/3065—Flame resistant or retardant, fire resistant or retardant
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2419/00—Buildings or parts thereof
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B2607/00—Walls, panels
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B29/00—Layered products comprising a layer of paper or cardboard
  • B32B29/002—Layered products comprising a layer of paper or cardboard as the main or only constituent of a layer, which is next to another layer of the same or of a different material
• • C—CHEMISTRY; METALLURGY
  • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
  • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
  • C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
  • C04B2111/00474—Uses not provided for elsewhere in C04B2111/00
  • C04B2111/00612—Uses not provided for elsewhere in C04B2111/00 as one or more layers of a layered structure
  • C04B2111/0062—Gypsum-paper board like materials
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
  • Y02W—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO WASTEWATER TREATMENT OR WASTE MANAGEMENT
  • Y02W30/00—Technologies for solid waste management
  • Y02W30/50—Reuse, recycling or recovery technologies
  • Y02W30/91—Use of waste materials as fillers for mortars or concrete

Definitions

• the present invention relates to panels for use in building construction.
• the present invention relates to panels for providing partitions to which items such as sinks, televisions, or radiators may be affixed.
• Light-weight panels such as plasterboard (e.g. gypsum plasterboard), polystyrene board and fibreboard are commonly used to provide partitions within buildings. Their advantages for this application include the fact that they are light and quick to install.
• such light-weight panels may have the drawback that they are not strong enough to support fixtures (e.g. sinks, televisions, radiators, fire extinguishers, shelves and any other item that requires attachment to the panel).
• the weight of the fixture may cause the fixing means (e.g. screws) to be pulled out of the panel, such that the fixture falls away from the partition.
• the backing lamina being e.g. PVC, HDPE, Nylon, polycarbonate, Bakelite, polypropylene, acetal, or fibreglass.
• the plasterboard may be provided with sufficient ability to retain fixing means that no backing lamina is required.
• the present invention may provide a plasterboard comprising a gypsum matrix having particles of agglomerated fibres embedded therein in an amount of at least 1 wt % relative to the gypsum, the gypsum matrix further comprising a polymeric additive, the polymeric additive being present in an amount of at least 1 wt % relative to the gypsum;
• the panel By omitting a backing lamina, it may be possible to provide a panel having adequate fixing strength at a relatively lower cost, due to reduced raw material costs and greater ease of manufacture. Additionally, the panel may be easier to recycle, since the requirement to separate the lamina from the plasterboard may be avoided.
• lamina is intended to cover polymer-based sheets having a thickness of at least 1 mm (for example 2 mm), comprising substantially PVC, HDPE, Nylon, polycarbonate, Bakelite, polypropylene, acetal, or fibreglass.
• laminate is used herein to refer to a sheet that is attached to a face of a plasterboard, e.g. by gluing, such that there is a defined interface between the plasterboard and the sheet.
• the term “lamina” is not intended to refer to objects that are partially or wholly embedded within the plasterboard.
• the plasterboard may have paper facings on one or both sides thereof.
• the plasterboard may have a mat partially or fully embedded at its surface, for example, a glass fibre mat.
• the particles are present in an amount of at least 2 wt % relative to the gypsum, preferably at least 2.5 wt %. Typically, the particles are present in an amount of less than 10 wt % relative to the gypsum, preferably less than 8 wt %.
• the particles may be, for example, wood particles (such as woodchip or fine sawdust particles) or paper particles.
• the particles are wood particles.
• the particles are irregular in shape.
• wood particles is not intended to refer to particles of wood-derived material (such as paper particles) that have been processed to the point where individual fibres are no longer bound by the natural binders present in wood.
• these particles have a length that is greater than 0.5 mm. In general, these particles have a length that is less than 25 mm, preferably less than 20 mm.
• these particles have a thickness than is less than 4 mm, preferably less than 3 mm. In the case that the particles are paper particles, their thickness is typically less than 0.5 mm.
• the particles may be wood particles and the plasterboard may further comprise glass fibres.
• the glass fibres are preferably present in an amount of at least 1 wt %.
• the polymeric additive is present in an amount of at least 2 wt % relative to the gypsum, preferably at least 4 wt %.
• the polymeric additive is selected from group comprising polyvinyl acetate, poly vinyl acetate-ethylene co-polymer, polyvinyl pyrrolidone crosslinked with polystyrene sulfonate, polyvinyl alcohol, methyl cellulose, hydroxyethyl methyl cellulose, styrene-butadiene copolymer latex, acrylic ester latex, acrylic copolymer latex, polyester resin, epoxy resin, polymethyl methacrylate, polyacrylic acid, cationic starch, ethylated starch, dextrin and mixtures thereof.
• the polymeric additive is one of polyvinyl acetate and starch.
• the starch may be a native starch (that is, an unmodified starch). In other cases, the starch may be a modified starch, for example, an acid-thinned starch.
• the polymeric additive is polyvinyl acetate.
• the present invention may provide a plasterboard comprising a gypsum matrix having wood particles embedded therein in an amount of at least 2 wt % relative to the gypsum, the gypsum matrix further comprising glass fibres in an amount of at least 1 wt % relative to the gypsum.
• no backing lamina is attached to either face of the plasterboard.
• lamina is intended to cover polymer-based sheets having a thickness of at least 1 mm (for example 2 mm), comprising substantially PVC, HDPE, Nylon, polycarbonate, Bakelite, polypropylene, acetal, or fibreglass.
• laminate is used herein to refer to a sheet that is attached to a face of a plasterboard, e.g. by gluing, such that there is a defined interface between the plasterboard and the sheet.
• the term “lamina” is not intended to refer to objects that are partially or wholly embedded within the plasterboard.
• the plasterboard may have paper facings on one or both sides thereof.
• the plasterboard may have a mat partially or fully embedded at its surface, for example, a glass fibre mat.
• the wood particles are irregular in shape.
• the wood particles have a length that is greater than 0.5 mm. In general, these particles have a length that is less than 25 mm, preferably less than 20 mm.
• the wood particles have a thickness than is less than 4 mm, preferably less than 3 mm.
• the plasterboard has paper facings. These paper facings may comprise both cellulose fibres and glass fibres, as this is thought to improve the fire resistance of the plasterboard. In other cases, the plasterboard may have a mat partially or fully embedded at its surface, for example, a glass mat.
• the gypsum matrix comprises a hydrophobic additive, such as silicone oil or wax.
• the gypsum matrix may contain a biocide.
• the gypsum matrix may contain an anti-shrinkage agent such as unexpanded vermiculite, microsilica, and/or clay, in order to improve the fire-resistance of the product.
• an anti-shrinkage agent such as unexpanded vermiculite, microsilica, and/or clay, in order to improve the fire-resistance of the product.
• Certain embodiments of the first or second aspects of the invention may include foam or lightweight aggregate such as perlite. Such additives are known in the art to produce lower-density boards having acceptable thickness.
• Gypsum plasterboards were prepared using the following general methodology: Stucco and other dry additives (including woodchips) were weighed into a bag and shaken to mix them. Water and wet additives were weighed into a bowl and mixed using an electric mixer for 60 s.
• the dry powdered additives were added to the wet additives in the bowl and mixed in with the electric mixer for 30 s.
• the resultant slurry was sandwiched between two sheets of paper liner and allowed to hydrate for 25 minutes measured from the time of mixing.
• the board was then dried in an oven for 1 hour at 160° C.
• the panels had a thickness of 12.5 mm.
• a gypsum plasterboard was prepared from a slurry containing the following ingredients:
• a gypsum plasterboard was prepared from a slurry containing the following ingredients:
• a gypsum plasterboard was prepared from a slurry containing the following ingredients:
• a gypsum plasterboard was prepared from a slurry containing the following ingredients:
• a gypsum plasterboard was prepared from a slurry containing the following ingredients:
• a gypsum plasterboard was prepared from a slurry containing the following ingredients:
• Screw pull-out tests were carried out on samples measuring 100 mm by 100 mm that had been conditioned at a temperature of 23° C. and a relative humidity of 50%.
• a 50 mm single thread wood screw was inserted into the sample, passing through a metal load transfer element positioned on the surface of the sample.
• the load transfer element has a first portion that is configured to lie between the screw head and the surface of the sample, and a second portion that is configured to engage with a testing machine so as to allow a load to be applied to the screw along the axis of the screw.
• the screw was tightened to a torque of 1 Nm.
• the specimen was then mounted in a Zwick Universal Testing Machine and a 10 N pre-load applied to the screw along the axis of the screw. Subsequently, the load was increased by setting a constant cross-head speed of 10 mm/minute until pull out was achieved.

Landscapes

• Engineering & Computer Science (AREA)
• Chemical & Material Sciences (AREA)
• Ceramic Engineering (AREA)
• Structural Engineering (AREA)
• Materials Engineering (AREA)
• Organic Chemistry (AREA)
• Architecture (AREA)
• Life Sciences & Earth Sciences (AREA)
• Civil Engineering (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Wood Science & Technology (AREA)
• Inorganic Chemistry (AREA)
• Manufacturing & Machinery (AREA)
• Forests & Forestry (AREA)
• Environmental & Geological Engineering (AREA)
• Curing Cements, Concrete, And Artificial Stone (AREA)
• Panels For Use In Building Construction (AREA)
• Laminated Bodies (AREA)
• Building Environments (AREA)
• Finishing Walls (AREA)
• Compositions Of Macromolecular Compounds (AREA)

Applications Claiming Priority (3)

Related Parent Applications (1)

Related Child Applications (1)

Publications (1)

Family

ID=52292297

Family Applications (3)

Family Applications After (2)

Country Status (23)

Cited By (4)

Families Citing this family (4)

Citations (9)

Family Cites Families (27)

• 2014
  • 2014-11-20 GB GBGB1420678.3A patent/GB201420678D0/en not_active Ceased
• 2015
  • 2015-11-19 CU CU2017000065A patent/CU24484B1/es unknown
  • 2015-11-19 US US15/527,128 patent/US20170334784A1/en not_active Abandoned
  • 2015-11-19 HU HUE15800916A patent/HUE071533T2/hu unknown
  • 2015-11-19 WO PCT/GB2015/053534 patent/WO2016079528A1/en not_active Ceased
  • 2015-11-19 AU AU2015348035A patent/AU2015348035B2/en not_active Ceased
  • 2015-11-19 RU RU2017113092A patent/RU2698749C2/ru not_active IP Right Cessation
  • 2015-11-19 BR BR112017010218A patent/BR112017010218A2/pt not_active Application Discontinuation
  • 2015-11-19 CA CA2967624A patent/CA2967624C/en active Active
  • 2015-11-19 PL PL15800916.7T patent/PL3221139T3/pl unknown
  • 2015-11-19 PE PE2017000874A patent/PE20171544A1/es unknown
  • 2015-11-19 CN CN201580062275.0A patent/CN107001143A/zh active Pending
  • 2015-11-19 CN CN202210121202.6A patent/CN114455928A/zh active Pending
  • 2015-11-19 KR KR1020177012213A patent/KR20170085495A/ko not_active Withdrawn
  • 2015-11-19 SG SG11201703431UA patent/SG11201703431UA/en unknown
  • 2015-11-19 JP JP2017522616A patent/JP2018503577A/ja active Pending
  • 2015-11-19 EP EP15800916.7A patent/EP3221139B1/en active Active
  • 2015-11-19 MY MYPI2017701343A patent/MY192776A/en unknown
  • 2015-11-19 EP EP25162592.7A patent/EP4541541A3/en active Pending
  • 2015-11-19 MX MX2017005625A patent/MX2017005625A/es unknown
  • 2015-11-19 CA CA3205506A patent/CA3205506C/en active Active
  • 2015-11-20 AR ARP150103789A patent/AR102729A1/es active IP Right Grant
  • 2015-11-20 TW TW104138444A patent/TW201623751A/zh unknown
• 2017
  • 2017-04-18 CL CL2017000967A patent/CL2017000967A1/es unknown
  • 2017-05-12 PH PH12017500888A patent/PH12017500888A1/en unknown
  • 2017-06-06 CO CONC2017/0005625A patent/CO2017005625A2/es unknown
• 2020
  • 2020-08-10 US US16/988,773 patent/US11505498B2/en active Active
• 2022
  • 2022-10-14 US US17/966,019 patent/US20230040864A1/en active Pending

Patent Citations (9)

Also Published As

Similar Documents

Legal Events