RU2317270C1 - Glaze - Google Patents

Glaze Download PDF

Info

Publication number
RU2317270C1
RU2317270C1 RU2006125603/03A RU2006125603A RU2317270C1 RU 2317270 C1 RU2317270 C1 RU 2317270C1 RU 2006125603/03 A RU2006125603/03 A RU 2006125603/03A RU 2006125603 A RU2006125603 A RU 2006125603A RU 2317270 C1 RU2317270 C1 RU 2317270C1
Authority
RU
Russia
Prior art keywords
glaze
cao
mgo
nio
pbo
Prior art date
Application number
RU2006125603/03A
Other languages
Russian (ru)
Inventor
Юлия Алексеевна Щепочкина
Original Assignee
Юлия Алексеевна Щепочкина
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Юлия Алексеевна Щепочкина filed Critical Юлия Алексеевна Щепочкина
Priority to RU2006125603/03A priority Critical patent/RU2317270C1/en
Application granted granted Critical
Publication of RU2317270C1 publication Critical patent/RU2317270C1/en

Abstract

FIELD: technology of silicates.
SUBSTANCE: invention relates to compositions of fritted glazes that can be used in production of facing tile. Proposed glaze comprises SiO2, Al2O3, CaO, MgO, K2O, B2O3 and, additionally, PbO and NiO in the following ratio of components, wt.-%: SiO2, 48.0-52.0; Al2O3, 7.0-9.0; CaO, 6.0-20.0; MgO, 2.0-6.0; K2O, 3.0-4.0; B2O3, 6.0-8.0; PbO, 5.0-8.0, and NiO, 2.0-4.0. Invention provides enhancing resistance of glaze to cold.
EFFECT: improved and valuable property of glaze.
1 tbl

Description

Изобретение относится к области технологии силикатов, а именно к составам фриттованных глазурей, которые могут быть использованы в производстве облицовочной плитки.The invention relates to the field of technology of silicates, and in particular to compositions of fritted glazes that can be used in the manufacture of facing tiles.

Известна глазурь, содержащая SiO2, Al2O3, CaO, MgO, K2O, B2O3 и другие компоненты /1/.Known glaze containing SiO 2 , Al 2 O 3 , CaO, MgO, K 2 O, B 2 O 3 and other components / 1 /.

Известна глазурь, содержащая, мас.%: SiO2 48,33-54,25; Al2O3 12,74-19,12; Fe2O3 2,08-2,16; CaO 12,5-22,87; MgO 0,6-0,89; Na2O 2,4-3,24; K2O 2,51-3,52; B2O3 4,4-8,39 /2/.Known glaze containing, in wt.%: SiO 2 48.33-54.25; Al 2 O 3 12.74-19.12; Fe 2 O 3 2.08-2.16; CaO 12.5-22.87; MgO 0.6-0.89; Na 2 O, 2.4-3.24; K 2 O 2.51-3.52; B 2 O 3 4,4-8,39 / 2 /.

Цель изобретения состоит в повышении морозостойкости глазури.The purpose of the invention is to increase the frost resistance of the glaze.

Цель достигается тем, что в состав глазури дополнительно вводят PbO и NiO, при следующем соотношении компонентов, мас.%: SiO2 48,0-52,0; Al2O3 7,0-9,0; CaO 16,0-20,0; MgO 2,0-6,0; K2O 3,0-4,0; B2O3 6,0-8,0; PbO 5,0-8,0; NiO 2,0-4,0.The goal is achieved by the fact that the composition of the glaze is additionally introduced with PbO and NiO, in the following ratio of components, wt.%: SiO 2 48.0-52.0; Al 2 O 3 7.0-9.0; CaO 16.0-20.0; MgO 2.0-6.0; K 2 O 3.0-4.0; B 2 O 3 6.0-8.0; PbO 5.0-8.0; NiO 2.0-4.0.

В таблице приведены составы глазури.The table shows the glaze compositions.

ТаблицаTable СоставStructure Компоненты, мас.%:Components, wt.%: Морозостойкость, циклыFrost resistance cycles SiO2 SiO 2 Al2O3 Al 2 O 3 CaOCao MgOMgO K2OK 2 O B2O3 B 2 O 3 PbOPbo NiONio 1one 48,048.0 9,09.0 20,020,0 2,02.0 3,03.0 8,08.0 8,08.0 2,02.0 ~200~ 200 22 50,050,0 8,08.0 18,018.0 4,04.0 3,53,5 7,07.0 6,56.5 3,03.0 ~200~ 200 33 52,052.0 7,07.0 16,016,0 6,06.0 4,04.0 6,06.0 5,05,0 4,04.0 ~200~ 200

Компоненты глазури сплавляют при 1200°С, гранулируют в воду. Фритту размалывают мокрым способом с добавкой 5-7% глины. Нанесенную на керамические изделия глазурную суспензию обжигают при 1000°С.Glaze components are fused at 1200 ° C, granulated into water. The frit is ground wet with the addition of 5-7% clay. The glaze suspension deposited on ceramic products is fired at 1000 ° C.

Источники информации:Information sources:

1. Авторское свидетельство СССР № 765223, С03С 9/00, 1980.1. USSR author's certificate No. 765223, С03С 9/00, 1980.

2. Авторское свидетельство СССР № 1057452, С03С 9/00, 1983.2. USSR author's certificate No. 1057452, С03С 9/00, 1983.

Claims (1)

Глазурь, содержащая SiO2, Al2О3, CaO, MgO, K2O, В2О3, отличающаяся тем, что дополнительно содержит PbO и NiO при следующем соотношении компонентов, мас %: SiO2 48,0-52,0; Al2О3 7,0-9,0; CaO 16,0-20,0; MgO 2,0-6,0; K2O 3,0-4,0; В2О3 6,0-8,0; PbO 5,0-8,0; NiO 2,0-4,0.Glaze containing SiO 2 , Al 2 O 3 , CaO, MgO, K 2 O, B 2 O 3 , characterized in that it additionally contains PbO and NiO in the following ratio of components, wt%: SiO 2 48.0-52.0 ; Al 2 O 3 7.0-9.0; CaO 16.0-20.0; MgO 2.0-6.0; K 2 O 3.0-4.0; B 2 O 3 6.0-8.0; PbO 5.0-8.0; NiO 2.0-4.0.
RU2006125603/03A 2006-07-17 2006-07-17 Glaze RU2317270C1 (en)