RU2198743C1 - Method of applying polymer coating based on siloxane or fluorine-containing elastomer to cloth base from aramide or mineral fibers - Google Patents
Method of applying polymer coating based on siloxane or fluorine-containing elastomer to cloth base from aramide or mineral fibers Download PDFInfo
- Publication number
- RU2198743C1 RU2198743C1 RU2002106199/12A RU2002106199A RU2198743C1 RU 2198743 C1 RU2198743 C1 RU 2198743C1 RU 2002106199/12 A RU2002106199/12 A RU 2002106199/12A RU 2002106199 A RU2002106199 A RU 2002106199A RU 2198743 C1 RU2198743 C1 RU 2198743C1
- Authority
- RU
- Russia
- Prior art keywords
- composition
- band
- tape
- temperature
- layer
- Prior art date
Abstract
Description
Изобретение относится к способам последовательного нанесения полимерных композиций на тканевые поверхности невращающимися элементами конструкций с предварительной обработкой поверхностей для увеличения адгезии, в особенности при отделке термостойких материалов для пошива специальной огнезащитной и маслобензостойкой одежды. The invention relates to methods for sequentially applying polymer compositions to fabric surfaces with non-rotating structural elements with surface pretreatment to increase adhesion, especially when finishing heat-resistant materials for sewing special fireproof and oil-resistant clothing.
Известен способ нанесения полимерной композиции для защиты поверхности от агрессивных сред, в котором для повышения адгезии покрытий может быть применено введение в наносимые полимеры адгезионноактивных соединений, например аминов, эпоксидных смол (авторское свидетельство СССР 537098, кл. C 08 L 71/02, опубл. 30.11.76). A known method of applying a polymer composition to protect the surface from aggressive media, in which to increase the adhesion of coatings can be applied to the applied polymers of adhesive active compounds, for example amines, epoxies (copyright certificate of the USSR 537098, class C 08 L 71/02, publ. 11/30/76).
Недостатком известного способа является то, что введение в полимеры указанных добавок хотя и способствует значительному увеличению адгезии, но ухудшает химическую стойкость получаемых покрытий, так как вводимые в достаточно больших количествах (5-10)% добавки не являются химически стойкими соединениями. В результате такие покрытия не могут эксплуатироваться при повышенных температурах и в особо агрессивных средах. The disadvantage of this method is that the introduction of these additives into polymers, although it contributes to a significant increase in adhesion, but worsens the chemical resistance of the resulting coatings, since the additives introduced in sufficiently large quantities (5-10)% are not chemically stable compounds. As a result, such coatings cannot be used at elevated temperatures and in particularly aggressive environments.
Наиболее близким к заявляемому по технической сущности и достигаемому результату является способ нанесения полимерной композиции, а именно композиции на основе фторкаучука, изготовленной по способу, описанному в патенте РФ 2176598, кл. В 32 В 23/08, 25/04, 27/08, опубл. 10.12.01, или композиции силоксановой, изготовленной по способу, описанному в патенте РФ 2164930, кл. С 09 К 21/00, В 32 В 25/04, опубл. 10.04.01, на тканевую основу, выполненную из арамидного материала или из ткани на основе минерального волокна, заключающийся в том, что композицию накладывают на тканевую основу в виде ленты, движущейся поступательно с помощью приводного шкива со скоростью 3-5 м/мин, распределяют композицию по ленте спомощью вертикального скребкового ножа, образующего поворотом вокруг горизонтальной оси, расположенной в поперечном направлении относительно ленты, зазор для прохода ленты с наложенной композицией, дозирующий количество композиции, идущей на слой покрытия, подают ленту с распределенной по ней композицией в сушильную камеру (патент РФ 2176598, кл. В 32 В 23/08, 25/08, 27/08, опубл. 10.12.01 - прототип). Closest to the claimed technical essence and the achieved result is a method of applying a polymer composition, namely a composition based on fluororubber, made by the method described in RF patent 2176598, cl. B 32 V 23/08, 25/04, 27/08, publ. 12/10/01, or a siloxane composition made by the method described in RF patent 2164930, class. S 09 K 21/00, 32 V 25/04, publ. 04/10/2011, on a fabric base made of aramid material or fabric based on mineral fiber, consisting in the fact that the composition is applied to the fabric base in the form of a tape moving translationally using a drive pulley at a speed of 3-5 m / min, distribute the composition on the tape with the help of a vertical scraper knife, forming by a rotation around a horizontal axis located in the transverse direction relative to the tape, a clearance for the passage of the tape with the composition applied, dosing the amount of composition going to oh coating tape is fed with distributed over it the composition in the drying chamber (RF Patent 2176598, cl V 32 V 23/08, 25/08, 27/08, publ 10.12.01 -.. prototype).
Недостатками известного способа являются
- невысокая производительность процесса из-за недостаточной скорости движения тканевой основы, определяемой большими затратами времени нахождения ленты с нанесенной в один слой композицией в сушильной камере, достаточно большой толщины для обеспечения водоупорности;
- неравномерность толщины покрытия из-за нанесения его в один слои;
- низкая адгезия наносимого покрытия к тканевой основе.The disadvantages of this method are
- low productivity of the process due to the insufficient speed of movement of the fabric base, determined by the large cost of the time spent by the tape with the composition applied in one layer in the drying chamber, of sufficiently large thickness to ensure water resistance;
- uneven coating thickness due to its application in one layer;
- low adhesion of the coating to the fabric base.
Технической задачей изобретения является создание нового способа нанесения полимерного покрытия на основе силоксановой или фторкаучуковой композиции на тканевую основу из арамидных или минеральных волокон, обладающего высокой производительностью, с получением равномерного по толщине покрытия, обладающего высокой степенью адгезии. An object of the invention is the creation of a new method of applying a polymer coating based on a siloxane or fluororubber composition to a fabric base of aramid or mineral fibers with high performance, with obtaining a uniform coating thickness with a high degree of adhesion.
Техническая задача решается в заявляемом способе нанесения полимерного покрытия на основе силоксановой или фторкаучуковой композиции на тканевую основу из арамидных или минеральных волокон путем наложения композиции на тканевую основу в виде ленты, движущейся поступательно с помощью приводного шкива, распределения композиции по ленте, движущейся поступательно с помощью приводного шкива, распределения композиции по ленте с помощью вертикального скребкового ножа, образующего поворотом вокруг горизонтальной оси, расположенной в поперечном направлении относительно ленты, фиксированный зазор для прохода ленты с наложенной композицией, дозирующий количество композиции, образующей слой покрытия, подачи ленты с распределенной по ней композицией в сушильную камеру, в котором согласно изобретению композицию наносят в два слоя, нанося второй слой на первый с помощью второго поворотного вертикального скребкового ножа, установленного за сушильной камерой, и распределяя ее по ленте, движущейся со скоростью 3-8 м/мин с равномерностью первого слоя 10-120 г/ м2, а второго - 10-80 г/м2, после нанесения второго слоя ленту сушат во второй камере с температурой, как и в первой камере, 130-200oС, обрабатывая ленту с композицией перед сушильными камерами снизу паром с температурой 100-120oС.The technical problem is solved in the present method of applying a polymer coating based on a siloxane or fluororubber composition to a fabric base of aramid or mineral fibers by applying the composition to the fabric base in the form of a tape moving translationally using a drive pulley, distributing the composition on a tape moving translationally using a drive pulley, distributing the composition along the tape using a vertical scraper knife, forming a rotation around the horizontal axis located in the pope river direction relative to the tape, a fixed clearance for the passage of the tape with the applied composition, dosing the amount of the composition forming the coating layer, feeding the tape with the composition distributed over it into the drying chamber, in which according to the invention the composition is applied in two layers, applying a second layer to the first with the second rotary vertical scraper knife installed behind the drying chamber, and distributing it along the belt moving at a speed of 3-8 m / min with a uniformity of the first layer of 10-120 g / m 2 and the second - 10-80 g / m 2 , after applying the second layer, the tape is dried in a second chamber with a temperature of 130-200 ° C, as in the first chamber, by treating the tape with the composition in front of the drying chambers from below with steam at a temperature of 100-120 o C.
При таком способе нанесения полимерного покрытия на основе силоксановой или фторкаучуковой композиции на тканевую основу из арамидных или минеральных волокон тканевую основу до нанесения первого слоя композиции подвергают обработке паром с температурой 100-120oС и сушке при 130-200oС для удаления замасливателей при скорости движения ленты 5-10 м/мин.With this method of applying a polymer coating based on a siloxane or fluororubber composition to a fabric base of aramid or mineral fibers, the fabric base is subjected to steam treatment at a temperature of 100-120 ° C and drying at 130-200 ° C to remove lubricants at a speed before applying the first layer of the composition belt movements 5-10 m / min.
Такой способ нанесения полимерного покрытия на основе силоксановой или фторкаучуковой композиции на тканевую основу из арамидных или минеральных волокон обеспечивает
- повышенную производительность процесса, так как толщина каждого слоя двухслойного покрытия, а следовательно, и время его пребывания в сушильной камере значительно меньше, чем при однослойном покрытии.This method of applying a polymer coating based on a siloxane or fluororubber composition on a fabric base of aramid or mineral fibers provides
- increased productivity of the process, since the thickness of each layer of a two-layer coating, and therefore its residence time in the drying chamber, is significantly less than with a single-layer coating.
Кроме этого, создание парового эффекта перед камерами сушки способствует быстрой вулканизации композиции в камерах сушки, все это позволяет увеличить скорость ленты до 8 м/мин и повысить производительность процесса;
- обеспечивает равномерность толщины покрытия, так как второй слой компенсирует все неровности первого слоя, возникающие при его нанесении;
- способствует хорошей адгезии наносимых слоев композиции, образующих покрытие не только к тканевой основе, но и друг к другу вследствие создания парового эффекта перед камерами сушки, что создает положительный эффект для вулканизации композиции в камерах сушки, повышая адгезию.In addition, the creation of a vapor effect in front of the drying chambers contributes to the rapid vulcanization of the composition in the drying chambers, all this allows you to increase the speed of the tape up to 8 m / min and increase the productivity of the process;
- ensures uniform coating thickness, since the second layer compensates for all the irregularities of the first layer that occur during its application;
- promotes good adhesion of the applied layers of the composition, forming a coating not only to the fabric base, but also to each other due to the creation of a steam effect in front of the drying chambers, which creates a positive effect for the vulcanization of the composition in the drying chambers, increasing adhesion.
Кроме этого, устранение замасливателей с тканевой основы их арамидных или минеральных волокон путем обработки ее паром и сушкой перед нанесением первого слоя покрытия также способствует повышению адгезии наносимого покрытия. In addition, the elimination of lubricants from the fabric basis of their aramid or mineral fibers by treating it with steam and drying before applying the first coating layer also helps to increase the adhesion of the applied coating.
Для достижения необходимой величины адгезии наносимого полимерного покрытия на основе силоксановой или фторкаучуковой композиции на тканевую основу из арамидных или минеральных волокон, определяемой величиной 15 Н/см, что превышает величину адгезии прототипа 10 Н/см, необходимо следующее соотношение параметров процесса заявляемого изобретения (см.таблицу). In order to achieve the required adhesion value of the applied polymer coating based on a siloxane or fluororubber composition on a fabric base of aramid or mineral fibers, determined by a value of 15 N / cm, which exceeds the prototype adhesion value of 10 N / cm, the following ratio of process parameters of the claimed invention is necessary (see table).
При возможной обработке паром тканевой основы до нанесения первого слоя композиции при температуре 100-120oС адгезия наносимой композиции может увеличиться на 10-12% из-за устранения замасливателей.With a possible steam treatment of the fabric base before applying the first layer of the composition at a temperature of 100-120 o With the adhesion of the applied composition may increase by 10-12% due to the elimination of lubricants.
Предлагаемый способ иллюстрируется чертежом, на котором представлена схема установки, на которой осуществляется способ нанесения полимерного покрытия на основе силоксановои или фторкаучуковой композиции на тканевую основу из арамидных или минеральных волокон. The proposed method is illustrated in the drawing, which shows the installation diagram, which implements a method of applying a polymer coating based on siloxane or fluororubber composition on a fabric base of aramid or mineral fibers.
Лента 1, выполненная из арамидных или минеральных волокон, имеет возможность поступательного движения с помощью приводного шкива 2. На движущуюся ленту накладывается композиция на основе силоксана или фторкаучука, которая распределяется по ленте с помощью вертикального скребкового ножа 3, образующего с помощью поворота вокруг горизонтальной оси 4, расположенной в поперечном направлении относительно ленты 1, зазор 5, величина которого соответствует количеству композиционного покрытия, приходящегося на единицу площади ленты 1. В месте нанесения композиции лента опирается на обрезиненный ролик 6. Лента с распределенной с помощью поворотного ножа 3 композицией, образующей первый слой с распределением 10-120 г/м2, обрабатывается снизу паром с температурой 100-120oС из паропровода 7, расположенного под лентой 1. После обработки лента со слоем композиции поступает в первую сушильную печь 8, где происходит ее сушка при температуре 130-200oС. После выхода из сушильной печи 8 на первый слой композиции, подвергшейся вулканизации, наносится с помощью второго вертикального скребкового ножа 9 второй слой той же композиции, распределяемый по первому слою в количестве 10-80 г/м2 с помощью второго зазора 10, создаваемого поворотом ножа 9 вокруг горизонтальной оси 11, расположенной в поперечном направлении относительно ленты 1 и вторым обрезиненным роликом 12. После этого лента 1 с нанесенным вторым слоем композиции подвергается снизу повторной обработке паром из паропровода 7 и затем поступает во вторую сушильную печь 13 с температурой сушки 130-200oС и после сушки - на намоточное устройство 14. Скорость движения ленты в течение всего процесса 3-8 м/мин и зависит от толщины слоя нанесенной композиции.The tape 1, made of aramid or mineral fibers, has the possibility of translational motion using the drive pulley 2. A composition based on siloxane or fluororubber is applied to the moving tape, which is distributed along the tape using a
Возможна обработка тканевой основы до нанесения первого слоя композиции паром с температурой 100-120oС и сушка при температуре 130-200oС для удаления замасливателя при скорости подачи ленты 5-10 м/мин.It is possible to treat the fabric base before applying the first layer of the composition with steam at a temperature of 100-120 o C and drying at a temperature of 130-200 o C to remove the sizing agent with a tape feed speed of 5-10 m / min.
Полученное полимерное покрытие на основе силоксановой или фторкаучуковой композиции на тканевую основу из арамидных или минеральных волокон обладает равномерностью по толщине и высокой степенью адгезии к тканевой основе, а сам процесс отличается высокой производительностью по сравнению с прототипом. The resulting polymer coating based on a siloxane or fluororubber composition on a fabric basis of aramid or mineral fibers has uniformity in thickness and a high degree of adhesion to the fabric base, and the process itself is characterized by high productivity compared to the prototype.
Сопоставительный анализ заявляемого способа нанесения полимерного покрытия на основе силоксановой или фторкаучуковой композиции на тканевую основу из арамидных или минеральных волокон и прототипа выявляет наличие отличительных признаков у заявляемого способа по сравнению с наиболее близким аналогом, что позволяет сделать вывод о соответствии заявляемого способа критерию изобретения "новизна". A comparative analysis of the proposed method for applying a polymer coating based on a siloxane or fluororubber composition to a fabric base of aramid or mineral fibers and a prototype reveals the distinctive features of the proposed method in comparison with the closest analogue, which allows us to conclude that the claimed method meets the criteria of the invention of "novelty" .
Наличие отличительных признаков дает возможность получить положительный эффект, заключающийся в создании нового способа нанесения полимерного покрытия на основе силоксановой или фторкаучуковой композиции на тканевую основу из арамидных или минеральных волокон, обладающего высокой производительностью с получением равномерного по толщине покрытия, обладающего высокой степенью адгезии. The presence of distinctive features makes it possible to obtain a positive effect, which consists in creating a new method of applying a polymer coating based on a siloxane or fluororubber composition to a fabric base of aramid or mineral fibers, which has high performance with obtaining a uniform coating thickness with a high degree of adhesion.
Поскольку при исследовании объекта изобретения по патентной и научно-технической литературе не выявлено решений, содержащих признаки заявляемого изобретения, отличные от прототипа, следует сделать вывод, что заявляемое изобретение соответствует критерию "существенные отличия". Since when examining the subject of the invention in patent and scientific literature, no solutions were found containing the features of the claimed invention other than the prototype, it should be concluded that the claimed invention meets the criterion of "significant differences".
Использование заявляемого изобретения при последовательном нанесении полимерных композиций на тканевые поверхности обеспечивает ему соответствие критерию "промышленная применимость". The use of the claimed invention for the sequential application of polymer compositions on tissue surfaces provides it with the criterion of "industrial applicability".
Claims (2)