DE20318173U1

DE20318173U1 - Protective glove, especially for protection against chemical weapons, contains barrier layer comprising water vapor permeable membrane between carrier and adsorption layers

Info

Publication number: DE20318173U1
Application number: DE20318173U
Authority: DE
Original assignee: Bluecher GmbH
Current assignee: Bluecher GmbH
Priority date: 2003-10-14
Filing date: 2003-11-24
Publication date: 2004-11-25
Anticipated expiration: 2013-11-25
Also published as: ATE463966T1; DE10354902B4; DE20316856U1; DE10354902C5; DE502004011052D1; ES2343412T3; DE10354902A1

Abstract

The glove (1) contains a barrier layer (4) comprising a membrane (6) which is substantially impermeable to water and air, permeable to water vapor and either substantially impermeable to chemical toxins or capable of delaying the passage of these toxins. The membrane is located between the carrier layer (3) and adsorption layer (5). The glove (1) contains a barrier layer (4) comprising a membrane (6) which is substantially impermeable to water and air, permeable to water vapor and either substantially impermeable to chemical toxins or capable of delaying the passage of these toxins. The membrane is located between the carrier layer (3) and adsorption layer (5). The glove is breathable and comprises a multi- layer material (2) with a preferably flat carrier layer and a barrier layer for the toxins located on the inside of the carrier layer. The adsorption layer comprises a material used to adsorb the toxins, preferably an active carbon- based material. Independent claims are also included for breathable protective gloves made from the above material in which either (i) the glove material and/or membrane has a barrier effect against chemical weapons (especially bis[2-chloroethyl]sulfide of no more than 4 mu g/cm 2>per 24 h for a membrane thickness of 50 microns, (ii) the glove has a water vapor permeability of at least 10 l/m 2>per 24 h at 25[deg]C for a membrane thickness of 50 microns, or (iii) the glove has a water vapor flow resistance under stationary conditions of no more than 30 (m 2>.Pa)/W at 35[deg]C for a membrane thickness of 50 microns.

Description

Die vorliegende Erfindung betrifft einen atmungsaktiven Schutzhandschuh mit Schutzfunktion gegenüber chemischen Giften, insbesondere chemischen Kampfstoffen, nach dem Oberbegriff des Anspruchs 1, insbesondere für den militärischen Einsatz oder für den ABC-Einsatz.The The present invention relates to a breathable protective glove with protective function against chemical poisons, especially chemical warfare agents, according to the Preamble of claim 1, in particular for military use or for ABC use.

Es gibt eine Reihe von Stoffen, die von der Haut aufgenommen werden und zu schweren körperlichen Schäden führen. Als Beispiel seien das blasenziehende Lost (Gelbkreuz) und das Nervengift Sarin erwähnt. Menschen, die mit solchen Giften in Kontakt kommen können, müssen eine geeignete Schutzausrüstung tragen bzw. durch geeignete Schutzmaterialien gegen diese Gifte geschützt werden.It are a number of substances that are absorbed by the skin and too severe physical damage to lead. Examples include the blistering mustard (yellow cross) and the nerve poison sarin mentioned. People who can come into contact with such poisons must have one suitable protective equipment wear or with suitable protective materials against these poisons protected become.

Zum Schutz des Körpers, insbesondere der Extremitäten und des Rumpfes, gibt es entsprechende Schutzanzüge. Zum Schutz des Kopfes, insbesondere des Gesichtes, sowie der Atemwege werden im allgemeinen Gasmasken (ABC-Schutzmasken), gegebenenfalls zusammen mit Kapuzen, getragen.To the Protection of the body, especially the extremities and the fuselage, there are appropriate protective suits. To protect the head, especially the face, as well as the respiratory tract in general Gas masks (ABC protective masks), possibly together with hoods, carried.

Des weiteren ist aber auch darauf zu achten, daß auch die Hände mit einem ausreichenden Schutz gegenüber solchen Giften ausgestattet werden, insbesondere durch das Tragen von Schutzhandschuhen. Insbesondere muß ein solch schützender Handschuh für den militärischen Einsatz oder den ABC-Einsatz geeignet sein.Of Another is also to make sure that the hands with adequate protection against such poisons are endowed, in particular by wearing them of protective gloves. In particular, such a protective Glove for the military Stake or the ABC stake be suitable.

Zu diesem Zweck werden gemäß dem Stand der Technik für den militärischen Einsatz bzw. den ABC-Einsatz luft- und wasserdichte Gummihandschuhe, insbesondere auf Butylgummibasis, eingesetzt, welche gegenüber chemischen Giften, insbesondere chemischen Kampfstoffen, undurchlässig sind. Nachteil dieser Schutzhandschuhe ist die mangelnde Atmungsaktivität und der folglich nur geringe Tragekomfort, was insbesondere bei längeren Einsätzen hinderlich ist.To for this purpose, according to the status of Technology for the military Use or the ABC use of air and waterproof rubber gloves, especially based on butyl rubber, which are used against chemical Poisons, especially chemical warfare agents, are impermeable. The disadvantage of these protective gloves is the lack of breathability and the consequently only low wearing comfort, which is a hindrance especially for longer uses is.

Die auf die Anmelderin selbst zurückgehende US 6 301 715 B1 bzw. die zu derselben Patentfamilie gehörende WO 01/82728 A1 und DE 201 21 518 U1 beschreiben einen Handschuh für Piloten mit erhöhter Taktilität und Schutzwirkung gegenüber chemischen Giften, der aus einem atmungsaktiven Außenmaterial, wie z. B. Leder oder einem Textilmaterial, besteht und mit einer aktivkohlebasierten Adsorptionsschicht zur Adsorption chemischer Kampfstoffe ausgerüstet sein kann. Dieser Handschuh bietet aufgrund der aktivkohlebasierten Adsorptionsschicht zwar eine exzellente Schutzfunktion gegenüber chemischen Giften, insbesondere Kampfstoffen, jedoch ist die Tragezeit dieses Handschuhs bei einem militärischen bzw. ABC-Einsatz aufgrund der begrenzten Adsorptionskapazität der Aktivkohle beschränkt. Des weiteren ist dieser Handschuh nicht ohne weiteres dekontaminierbar bzw. regenerierbar.The originating from the applicant US 6,301,715 B1 or WO 01/82728 A1 and belonging to the same patent family DE 201 21 518 U1 describe a glove for pilots with increased tactility and protective effect against chemical poisons, which is made of a breathable outer material, such as. B. leather or a textile material, and can be equipped with an activated carbon-based adsorption layer for the adsorption of chemical warfare agents. Because of the activated carbon-based adsorption layer, this glove offers an excellent protective function against chemical poisons, especially warfare agents, but the wearing time of this glove is limited in military or ABC use due to the limited adsorption capacity of the activated carbon. Furthermore, this glove cannot easily be decontaminated or regenerated.

Es ist daher die Aufgabe der vorliegenden Erfindung, einen Schutzhandschuh, insbesondere einen atmungsaktiven Schutzhandschuh, mit Schutzfunktion gegenüber chemischen Giften, insbesondere chemischen Kampfstoffen, bereitzustellen, welcher sich insbesondere für den militärischen Einsatz oder den ABC-Einsatz eignet und die zuvor geschilderten Nachteile des Standes der Technik zumindest teilweise vermeidet.It is therefore the object of the present invention, a protective glove, especially a breathable protective glove with protective function across from to provide chemical poisons, in particular chemical warfare agents, which is especially for the military Use or the ABC use is suitable and the previously described Disadvantages of the prior art at least partially avoided.

Eine weitere Aufgabe der vorliegenden Erfindung besteht darin, den in der US 6 301 715 B1 bzw. in den beiden vorgenannten parallelen Schutzrechtsanmeldungen WO 01/82728 A1 und DE 201 21 518 U1 beschriebenen Handschuh weiterzuentwickeln.A further object of the present invention is that in the US 6,301,715 B1 or in the two aforementioned parallel patent applications WO 01/82728 A1 and DE 201 21 518 U1 to further develop the described glove.

Zur Lösung der zuvor geschilderten Aufgabenstellung schlägt die vorliegende Erfindung einen Schutzhandschuh, insbesondere einen atmungsaktiven Schutzhandschuh (z. B. Militärschutzhandschuh oder ABC-Schutzhandschuh), gemäß Anspruch 1 vor. Weitere, vorteilhafte Ausgestaltungen des erfindungsgemäßen Schutzhandschuhs sind Gegenstand der Unter- und Nebenansprüche.to solution The present invention proposes the above-described task a protective glove, especially a breathable protective glove (e.g. military protective glove or ABC protective glove), according to claim 1 before. Further advantageous configurations of the protective glove according to the invention are the subject of subclaims and subsidiary claims.

Die grundlegende Idee der vorliegenden Erfindung besteht darin, einen atmungsaktiven Schutzhandschuh mit mehrschichtigem Schichtaufbau mit einer insbesondere flächigen, außenseitigen Trägerschicht und einer der Trägerschicht zugeordneten, den Durchtritt chemischer Gifte verhindernden oder zumindest verzögernden, innenseitigen (d. h. im Tragezustand der Hand zugewandten) Sperrschicht, welche eine Adsorptionsschicht auf Basis eines che mische Gifte adsorbierenden Adsorptionsmaterials (z. B. auf Basis von Aktivkohle) umfaßt, dadurch mit einer erhöhten bzw. verbesserten Schutzfunktion gegenüber chemischen Giften, insbesondere chemischen Kampfstoffen, auszurüsten, daß die Sperrschicht zusätzlich zu der Adsorptionsschicht mit einer zumindest im wesentlichen wasser- und luftundurchlässigen, aber wasserdampfdurchlässigen, den Durchtritt chemischer Gifte verzögernden oder gegenüber chemischen Giften zumindest im wesentlichen undurchlässigen Membran, welche zwischen der Trägerschicht und der Adsorptionsschicht angeordnet wird, ausgestattet wird.The basic idea of the present invention is one breathable protective glove with multi-layer construction with a particularly flat, outboard backing and one of the backing layers assigned to prevent the passage of chemical poisons or at least delaying, inside (i.e. facing the hand when worn) barrier layer, which an adsorption layer based on a chemical adsorbing poisons Adsorption material (z. B. based on activated carbon) comprises, thereby with an increased or improved protective function against chemical poisons, in particular chemical warfare agents to equip, that the Additional barrier layer to the adsorption layer with an at least essentially water- and airtight, but permeable to water vapor, delaying the passage of chemical poisons or compared to chemical ones Poisons at least essentially impermeable membrane, which between the backing and the adsorption layer is arranged.

Die vorgenannte Membran, welche zwischen der Trägerschicht und der Adsorptionsschicht angeordnet wird, bewirkt, daß gegebenenfalls durch die außenseitige Trägerschicht eingedrungene chemische Gifte, wie z. B. chemische Kampfstoffe, die Adsorptionsschicht nicht oder zumindest zu einem überwiegenden Teil gar nicht erst erreichen, so daß die Adsorptionskapazität der Adsorptionsschicht quasi unerschöpflich bleibt. Durch die Ausstattung des erfindungsgemäßen Schutzhandschuhs mit einer speziellen atmungsaktiven Membran, welche den Durchtritt chemischer Gifte verzögert bzw. gegenüber chemischen Giften zumindest im wesentlichen undurchlässig ist, wird gleichzeitig eine gute Dekontaminierbarkeit und Regenerierbarkeit des erfindungsgemäßen Schutzhandschuhs erreicht.The aforementioned membrane, which is arranged between the support layer and the adsorption layer, causes chemical poisons, such as, for example, penetrated through the outside support layer. B. chemical warfare agents, the adsorption layer does not reach, or at least for the most part, so that the Adsorption capacity of the adsorption layer remains virtually inexhaustible. By equipping the protective glove according to the invention with a special breathable membrane which delays the passage of chemical poisons or is at least substantially impermeable to chemical poisons, good decontamination and regenerability of the protective glove according to the invention is achieved at the same time.

Weitere Vorteile, Eigenschaften, Aspekte und Merkmale der vorliegenden Erfindung ergeben sich aus der folgenden Beschreibung eines in den Zeichnungen dargestellten, bevorzugten Ausführungsbeispiels. Es zeigt:Further Advantages, properties, aspects and features of the present invention result from the following description of one in the drawings illustrated, preferred embodiment. It shows:

1 Eine schematische Darstellung eines atmungsaktiven Schutzhandschuhs gemäß einem bevorzugten Ausführungsbeispiel der Erfindung; 1 A schematic representation of a breathable protective glove according to a preferred embodiment of the invention;

2A eine schematische Schnittdarstellung durch den Schichtaufbau eines atmungsaktiven Schutzhandschuhs gemäß einem bevorzugten Ausführungsbeispiel der Erfindung entsprechend einer Ausführungsform, bei der die Adsorptionsschicht mittels diskontinuierlichem Klebstoffauftrag an der Membran befestigt ist; 2A is a schematic sectional view through the layer structure of a breathable protective glove according to a preferred embodiment of the invention according to an embodiment in which the adsorption layer is attached to the membrane by means of discontinuous adhesive application;

2B eine schematische Schnittdarstellung durch den Schichtaufbau eines atmungsaktiven Schutzhandschuhs gemäß einem bevorzugten Ausführungsbeispiel der Erfindung entsprechend einer alternativen Ausführungsform, bei der die Adsorptionsschicht mittels kontinuierlichem Klebstoffauftrag an der Membran befestigt ist. 2 B is a schematic sectional view through the layer structure of a breathable protective glove according to a preferred embodiment of the invention according to an alternative embodiment, in which the adsorption layer is attached to the membrane by means of continuous adhesive application.

1 zeigt einen erfindungsgemäßen atmungsaktiven Schutzhandschuh 1 mit Schutzfunktion gegenüber chemischen Giften, insbesondere gegenüber chemischen Kampfstoffen. Der erfindungsgemäße Schutzhandschuh 1 weist einen mehrschichtigen Schichtaufbau 2 mit einer insbesondere flächigen, außenseitigen Trägerschicht 3 und einer der Trägerschicht 3 zugeordneten, innenseitigen (d. h. im Tragezustand der Hand zugewandten), den Durchtritt chemischer Gifte verhindernden oder zumindest verzögernden Sperrschicht 4 auf, welche eine Adsorptionsschicht 5 auf Basis eines chemische Gifte adsorbierenden Adsorptionsmaterials, insbesondere auf Basis von Aktivkohle, umfaßt. Zusätzlich zu der Adsorptionsschicht 5 weist die Sperrschicht 4 eine zumindest im wesentlichen wasser- und luftundurchlässige, aber wasserdampfdurchlässige (d. h. atmungsaktive), den Durchtritt chemischer Gifte verzögernde oder gegenüber chemischen Giften zumindest im wesentlichen undurchlässige Membran 6 auf, welche zwischen der Trägerschicht 3 und der Adsorptionsschicht 5 angeordnet ist. Erfindungsgemäß umfaßt die Sperrschicht 4 also sowohl eine Adsorptionsschicht 5 als auch eine Membran 6 mit den vorgenannten Eigenschaften. Durch die Kombination von Adsorptionsschicht 5 einerseits und Membran 6 andererseits entsprechend dem erfindungsgemäßen Schichtaufbau 2 wird ein effizienter Schutz gegenüber chemischen Giften, insbesondere chemischen Kampfstoffen, bei gleichzeitig hohem Tragekomfort, insbesondere Atmungsaktivität, gewährleistet. 1 shows a breathable protective glove according to the invention 1 with protective function against chemical poisons, in particular against chemical warfare agents. The protective glove according to the invention 1 has a multi-layer structure 2 with a particularly flat, outer carrier layer 3 and one of the backing layers 3 assigned, on the inside (ie facing the hand when the hand is in place), preventing the passage of chemical poisons or at least retarding barrier layer 4 on which is an adsorption layer 5 based on a chemical poisons adsorbing adsorption material, in particular based on activated carbon. In addition to the adsorption layer 5 exhibits the barrier layer 4 an at least substantially water and air impermeable, but water vapor permeable (ie breathable), retarding the passage of chemical poisons or at least substantially impermeable to chemical poisons 6 on which between the backing layer 3 and the adsorption layer 5 is arranged. According to the invention, the barrier layer comprises 4 so both an adsorption layer 5 as well as a membrane 6 with the aforementioned properties. By combining the adsorption layer 5 on the one hand and membrane 6 on the other hand according to the layer structure according to the invention 2 efficient protection against chemical poisons, in particular chemical warfare agents, while at the same time being extremely comfortable, in particular breathability, is guaranteed.

Wie aus den 1 sowie 2A und 2B ersichtlich, wird durch die erfindungsgemäße Anordnung der Membran 6 zwischen der Trägerschicht 3 und der Adsorptionsschicht 5 erreicht, daß gegebenenfalls durch die äußere Trägerschicht 3 des Schutzhandschuhs 1 eingedrungene Gifte bereits von der Membran 6 zurückgehalten werden und folglich die Adsorptionsschicht 5 gar nicht erst erreichen oder allenfalls in äußerst geringen Mengen; auf diese Weise wird zum einen die Adsorptionskapazität der Adsorptionsschicht quasi niemals er schöpft, und zum anderen wird durch die Anwesenheit der Membran 6 ein zusätzlicher Schutz für den Träger des Schutzhandschuhs 1 bereitgestellt, so daß ein Schutzhandschuh 1 mit sozusagen doppelter Schutzfunktion gegenüber chemischen Giften resultiert (nämlich einerseits durch die Sperrwirkung der Membran 6 und andererseits durch die Adsorptionswirkung der Adsorptionsschicht 5). Durch die Anwesenheit der speziellen Membran 6 wird zudem erreicht, daß der Schutzhandschuh 1 dekontaminierbar und regenerierbar wird; denn durch die Außenschicht 3 gegebenenfalls eingedrungene Gifte können durch entsprechende Behandlungsverfahren von der Membran 6 wieder entfernt werden (z. B. durch Herunterspülen), beispielsweise mit geeigneten Dekontaminationslösungen, welche dem Fachmann zu diesen Zwecken bestens bekannt sind.Like from the 1 such as 2A and 2 B can be seen from the arrangement of the membrane according to the invention 6 between the backing layer 3 and the adsorption layer 5 achieved that, if necessary, through the outer carrier layer 3 of the protective glove 1 toxins already penetrated from the membrane 6 are retained and consequently the adsorption layer 5 not at all or at most in extremely small quantities; in this way, on the one hand, the adsorption capacity of the adsorption layer is almost never exhausted, and on the other hand, the presence of the membrane 6 an additional protection for the wearer of the protective glove 1 provided so that a protective glove 1 with a double protective function against chemical poisons, so to speak (on the one hand due to the barrier effect of the membrane 6 and on the other hand by the adsorption effect of the adsorption layer 5 ). Due to the presence of the special membrane 6 is also achieved that the protective glove 1 becomes decontaminable and regenerable; because through the outer layer 3 Any poisons that have penetrated can be removed from the membrane by appropriate treatment methods 6 are removed again (for example by flushing them down), for example with suitable decontamination solutions, which are well known to the person skilled in the art for these purposes.

Wie aus den 1 sowie 2A und 2B ersichtlich, ist die Membran 6 bzw. die Sperrschicht 4 an ihrer im Tragezustand von der Hand abgewandten Seite unmittelbar oder mittelbar mit der Trägerschicht 3 verbunden. Die im Tragezustand der Hand zugewandte bzw. der Trägerschicht 3 abgewandte Seite (d. h also der Innenseite) der Membran 6 ist dagegen mit der Adsorptionsschicht 5 beaufschlagt; im allgemeinen ist die Adsorptionsschicht 5 mittels Klebstoffauftrag 7 an der Membran 6 befestigt. Wie die 2A und 2B zeigen, kann dabei der Klebstoffauftrag 7 grundsätzlich diskontinuierlich (2A) oder aber kontinuierlich bzw. vollflächig (2B) erfolgen. Bevorzugt ist jedoch ein diskontinuierlicher, insbesondere punktförmiger Klebstoffauftrag entsprechend 2A, weil dies den Tragekomfort des erfindungsgemäßen Schutzhandschuhs 1 erhöht, insbesondere eine zusätzliche Steifigkeit der Membran 6 verhindert, wie dies im Fall eines vollflächigen bzw. kontinuierlichen Klebstoffauftrags der Fall sein kann. Dennoch ist es grundsätzlich möglich, einen vollflächigen bzw. kontinuierlichen Klebstoffauftrag 7 zu Zwecken der Befestigung der Adsorptionsschicht 5 an der Membran 6 vorzusehen; in diesem Fall sollte aber darauf geachtet werden, daß der Klebstoff 7 atmungsaktive Eigenschaften aufweist, insbesondere wasserdampfdurchlässig ist, um den nötigen Tragekomfort zu gewährleisten.Like from the 1 such as 2A and 2 B the membrane is visible 6 or the barrier layer 4 on its side facing away from the hand, directly or indirectly with the carrier layer 3 connected. The layer facing the hand or the backing layer when worn 3 opposite side (i.e. the inside) of the membrane 6 is against the adsorption layer 5 applied; in general is the adsorption layer 5 by means of adhesive application 7 on the membrane 6 attached. As the 2A and 2 B can show the adhesive application 7 basically discontinuous ( 2A ) or continuously or over the entire area ( 2 B ) respectively. However, a discontinuous, in particular punctiform, application of adhesive is preferred 2A because this is the comfort of the protective glove according to the invention 1 increased, especially an additional stiffness of the membrane 6 prevents, as can be the case in the case of a full or continuous application of adhesive. Nevertheless, it is basically possible to apply a full or continuous adhesive 7 for the purpose of fastening the adsorption layer 5 on the membrane 6 provide; in this case, however, care should be taken that the adhesive 7 Has breathable properties, in particular is permeable to water vapor, to ensure the necessary comfort.

Des weiteren kann vorgesehen sein, daß zwischen der Membran 6 und der Trägerschicht 3 eine zusätzliche, vorzugsweise flächige Trägerschicht 8 angeordnet ist. Bei dieser Ausführungsform ist die Membran 6 nur mittelbar mit der Trägerschicht 3 verbunden, und zwar über die zusätzliche Trägerschicht B. Die zusätzliche Trägerschicht 8 dient insbesondere zur Stabilisierung und/oder Stützung der Membran 6, und zwar sowohl bei der Verarbeitung der Membran 6, insbesondere bei der Beaufschlagung mit Klebstoff 7 und der Adsorptionsschicht 5, als auch im Gebrauch bzw. beim Tragen des Schutzhandschuhs 1. Durch die zusätzliche Trägerschicht 8 kann die insbesondere Verschleißbeständigkeit, so z. B. die Reißfestigkeit, der Membran 6 gesteigert werden. Zu diesem Zweck kann die Membran 6 auf die zusätzliche Trägerschicht auflaminiert oder aufkaschiert sein, insbesondere mittels eines Klebstoffes (in den Zeichnungen nicht dargestellt), der vorteilhafterweise punktförmig aufgetragen wird, weil dies eine übermäßige Steifigkeit der Membran 6 verhindert und auf diese Weise der Tragekomfort erhöht wird. Die zusätzliche Trägerschicht 8, die zwischen der Membran 6 und der äußeren Trägerschicht 3 angeordnet ist, kann dann mit der Trägerschicht 3 verbunden werden, üblicherweise mittels eines vorzugsweise diskontinuierlich, insbesondere punktförmig aufgetragenen Klebstoffes. Als Materialien für die zusätzliche Trägerschicht 8 eignen sich beispielsweise Textilmaterialien, insbesondere textile Flächengebilde, wie z. B. Gewebe, Gewirke, Gestricke, Gelege oder Textilverbundstoffe (z. B. Vliesstoffe), die vorzugsweise luftdurchlässig ausgebildet sind. Vorteilhafterweise hat die zusätzliche Trägerschicht 8 ein geringeres Flächengewicht als die Trägerschicht 3. Im allgemeinen beträgt das Flächengewicht der zusätzlichen Trägerschicht 8 weniger als 60 g/m², insbesondere weniger als 50 g/m², vorzugsweise weniger als 40 g/m²; dies trägt zu einen erhöhten Tragekomfort bei, weil auf diese Weise die Biegsamkeit des Schichtaufbaus 2 insgesamt im wesentlichen nicht beeinträchtigt wird und ein guter Tragekomfort erzielt wird.Furthermore, it can be provided that between the membrane 6 and the backing 3 an additional, preferably flat carrier layer 8th is arranged. In this embodiment, the membrane 6 only indirectly with the backing layer 3 connected, specifically via the additional carrier layer B. The additional carrier layer 8th serves in particular to stabilize and / or support the membrane 6 , both when processing the membrane 6 , especially when applying adhesive 7 and the adsorption layer 5 , as well as in use or when wearing the protective glove 1 , Due to the additional carrier layer 8th can the particular wear resistance, such. B. the tensile strength, the membrane 6 be increased. For this purpose the membrane 6 be laminated or laminated onto the additional carrier layer, in particular by means of an adhesive (not shown in the drawings), which is advantageously applied in a punctiform manner, because this results in excessive rigidity of the membrane 6 prevented and in this way the comfort is increased. The additional backing layer 8th that between the membrane 6 and the outer support layer 3 is then arranged with the carrier layer 3 are connected, usually by means of an adhesive which is preferably applied discontinuously, in particular in a punctiform manner. As materials for the additional backing layer 8th are suitable for example textile materials, in particular textile fabrics, such as. B. fabrics, knitted fabrics, knitted fabrics, scrims or textile composites (z. B. nonwovens), which are preferably air-permeable. The additional carrier layer advantageously has 8th a lower basis weight than the carrier layer 3 , In general, the basis weight of the additional carrier layer is 8th less than 60 g / m ² , in particular less than 50 g / m ² , preferably less than 40 g / m ² ; this contributes to increased wearing comfort, because in this way the flexibility of the layer structure 2 overall is essentially not impaired and good wearing comfort is achieved.

Wie zuvor geschildert, ist die Membran 6 innenseitig (d. h. auf der im Tragezustand der Hand zugewandten Seite) mit einer Adsorptionsschicht 5 beaufschlagt. Die Adsorptionsschicht 5 wiederum kann auf ihrer im Tragezustand der Hand zugewandten, d. h. also der Membran 6 abgewandten Seite mit einer Abdeckschicht 9 versehen sein, die vorteilhafterweise an der Adsorptionsschicht 5 befestigt ist; zur Befestigung der Abdeckschicht 9 an der Adsorptionsschicht 5 eignen sich beispielsweise Klebstoffe, die zu diesen Zwecken vorzugsweise diskontinuierlich, insbesondere punktförmig, auf der Abdeckschicht 9 aufgetragen werden, oder aber sogenannte Schmelzklebergewebe ("Schmelzkleberwebs"), welche zwischen Abdeckschicht 9 und Adsorptionsschicht 5 angeordnet werden. Als Abdeckschicht 9 eignen sich vorzugsweise luftdurchlässige Textilmaterialien, insbesondere textile Flächengebilde, wie Gewebe, Gewirke, Gestricke, Gelege oder Textilverbundstoffe (z. B. Vliese, insbesondere Polyamid/Polyester-Vliese bzw. PA/PES-Vliese). Vorteilhafterweise ist das Abdeckmaterial 9 abriebfest ausgebildet bzw. besteht aus einem abriebfesten Textilmaterial. Vorteilhafterweise besitzt das Abdeckmaterial 9 ein Flächengewicht von 5 bis 150 g/m², insbesondere 10 bis 125 g/m², vorzugsweise 40 bis 100 g/m². Die Anwesenheit des Abdeckmaterials bzw. der Abdeckschicht 9 hat insbesondere den Vorteil, daß ein unmittelbarer Kontakt der Haut bzw. der Hand mit der Adsorptionsschicht 5 beim Tragen des Schutzhandschuhs 1 vermieden wird; dadurch wird einerseits bewirkt, daß die Adsorptionsschicht 5 nicht durch Hautschweiß verunreinigt wird, und zum anderen wird ein höherer Tragekomfort erzielt, weil die Abdeckschicht 9 im Rahmen des erfindungsgemäßen Schichtaufbaus 2 die Funktion eines textilen Innenhandschuhs einnimmt, welcher ein angenehmes Tragegefühl bewirkt. Zum anderen verhindert die Abdeckschicht 9 eine übermäßige mechanische Belastung des Adsorptionsmaterials der Adsorptionsschicht.As described before, the membrane is 6 on the inside (ie on the side facing the hand when worn) with an adsorption layer 5 applied. The adsorption layer 5 in turn it can be on the hand, ie the membrane, when it is in the wearing state 6 opposite side with a cover layer 9 be provided, which advantageously on the adsorption layer 5 is attached; for fastening the cover layer 9 on the adsorption layer 5 For example, adhesives are suitable which are discontinuous, in particular punctiform, on the cover layer for these purposes 9 be applied, or so-called hot-melt adhesive fabric ("hot-melt adhesive webs"), which between the cover layer 9 and adsorption layer 5 to be ordered. As a cover layer 9 Air-permeable textile materials, in particular textile fabrics, such as woven fabrics, knitted fabrics, knitted fabrics, scrims or textile composites (e.g. nonwovens, in particular polyamide / polyester nonwovens or PA / PES nonwovens) are preferably suitable. The cover material is advantageous 9 abrasion-resistant or made of an abrasion-resistant textile material. The covering material advantageously has 9 a weight per unit area of 5 to 150 g / m ² , in particular 10 to 125 g / m ² , preferably 40 to 100 g / m ² . The presence of the covering material or the covering layer 9 has the particular advantage that direct contact of the skin or hand with the adsorption layer 5 when wearing the protective glove 1 is avoided; on the one hand, this causes the adsorption layer 5 is not contaminated by sweat on the skin, and on the other hand a higher wearing comfort is achieved because the cover layer 9 in the context of the layer structure according to the invention 2 takes on the function of a textile inner glove, which makes it comfortable to wear. On the other hand, the cover layer prevents 9 excessive mechanical stress on the adsorbent material of the adsorbent layer.

Wie zuvor beschrieben, kann die Membran 6 außenseitig (d. h. auf der im Tragezustand der Hand abgewandten Seite) – je nach Ausgestaltung des erfindungsgemäßen Schichtaufbaus 2 – entweder mit der Trägerschicht 3 oder aber mit der zusätzlichen Trägerschicht 8 verbunden, beispielsweise verklebt, sein. Vorteilhafterweise erfolgt die Verklebung nur diskontinuierlich, insbesondere punktförmig, insbesondere in Form eines punktförmigen Rasters oder Musters, wobei der Klebstoff nur höchstens 30 %, insbesondere nur höchstens 25 %, vorzugsweise nur höchstens 20 %, besonders bevorzugt nur höchstens 10 % der im Tragezustand von der Hand abgewandten Seite der Membran 6 bedeckt.As previously described, the membrane 6 on the outside (ie on the side facing away from the hand when it is worn) - depending on the design of the layer structure according to the invention 2 - either with the carrier layer 3 or with the additional backing layer 8th connected, for example glued. Advantageously, the adhesive is only discontinuous, in particular punctiform, in particular in the form of a punctiform grid or pattern, the adhesive only at most 30%, in particular only at most 25%, preferably only at most 20%, particularly preferably only at most 10% of those in the wearing state of the Hand facing away from the membrane 6 covered.

Innenseitig (d. h. auf der im Tragezustand der Hand zugewandten Seite) ist auf die Membran 6 die Adsorptionsschicht 5 aufgebracht, insbesondere mittels eines Klebstoffs 7; der Auftrag des Klebstoffs 7 erfolgt – wie zuvor geschildert – vorteilhafterweise diskontinuierlich, insbesondere nur punktförmig, üblicherweise in Form eines punktförmigen Rasters, wobei zur Erzielung einer hohen Adsorptionsleistung mindestens 50 %, insbesondere mindestens 60 %, vorzugsweise mindestens 70 %, besonders bevorzugt mindestens 75 %, ganz besonders bevorzugt mindestens 80 % der im Tragezustand der Hand zugewandten, d. h. also der Trägerschicht 3 abgewandten Seite der Membran 6 mit dem Adsorptionsmaterial der Adsorptionsschicht 5 bedeckt bzw. beaufschlagt sein kann; entsprechend ist der Klebstoffauftrag 7 über diese Flächenbereiche der Membran 6 vorzusehen. Für den Fall, daß als Adsorptionsmaterial der Adsorptionsschicht 5 ein Flächengebilde (Gewebe, Gewirke, Gelege, Vlies etc.) aus Aktivkohlefasern verwendet wird, kann die im Tragezustand der Hand zugewandte, d. h. also der Trägerschicht 3 abgewandte Seite der Membran 6 vollständig, d. h. zu 100 %, mit dem Adsorptionsmaterial der Adsorptionsschicht 5 bedeckt bzw. beaufschlagt sein; das Aktivkohlefasergebilde kann beispielsweise durch nur punktförmigen Klebstoffauftrag an der Membran 6 fixiert sein.On the inside (ie on the side facing the hand when it is worn) is on the membrane 6 the adsorption layer 5 applied, in particular by means of an adhesive 7 ; the application of the adhesive 7 takes place - as described above - advantageously discontinuously, in particular only in a punctiform manner, usually in the form of a punctiform grid, with at least 50%, in particular at least 60%, preferably at least 70%, particularly preferably at least 75%, very particularly preferably at least, in order to achieve a high adsorption capacity 80% of those facing the hand when worn, ie the support layer 3 opposite side of the membrane 6 with the adsorption material al the adsorption layer 5 can be covered or acted upon; the adhesive application is corresponding 7 over these surface areas of the membrane 6 provided. In the event that the adsorption material of the adsorption layer 5 A flat structure (woven, knitted, laid, fleece, etc.) made of activated carbon fibers can be used, the one facing the hand when worn, that is, the backing layer 3 opposite side of the membrane 6 completely, ie 100%, with the adsorption material of the adsorption layer 5 be covered or acted upon; the activated carbon fiber structure can, for example, only be applied to the membrane by punctiform adhesive 6 be fixed.

Im allgemeinen sind die einzelnen Schichten 3, 4, 5, 6, 8 und 9 des Schichtaufbaus 2 jeweils miteinander verbunden; dies geschieht mit an sich für diese Zwecke bekannten Methoden (z. B. durch Verkleben, Verschweißen, Vernähen, Verheften etc.). Vorteilhafterweise erfolgt das Verbinden bzw. Fixieren der einzelnen Schichten 3, 4, 5, 6, 8 und 9 des Schichtaufbaus 2 jeweils miteinander nahtlos, vorzugsweise ohne Beschädigung der einzelnen Schichten 3, 4, 5, 6, 8 und 9 (z. B. durch Verkleben, Verschweißen etc.). Für den Fall, daß die Schichten 3, 4, 5, 6, 8 und 9 – zumindest teilweise – vernäht oder dergleichen werden, empfiehlt es sich, die Nahtstellen abzudichten (z. B. mit einem sogenannten Nahtversiegelungsband). Insbesondere bilden die einzelnen Schichten 3, 4, 5, 6, 8 und 9 des Schichtaufliaus 2 einen zusammenhängenden Verbund aus.In general, the individual layers 3 . 4 . 5 . 6 . 8th and 9 of the layer structure 2 connected to each other; this is done using methods known per se for these purposes (e.g. by gluing, welding, sewing, stapling, etc.). The individual layers are advantageously connected or fixed 3 . 4 . 5 . 6 . 8th and 9 of the layer structure 2 each seamless with each other, preferably without damaging the individual layers 3 . 4 . 5 . 6 . 8th and 9 (e.g. by gluing, welding, etc.). In the event that the layers 3 . 4 . 5 . 6 . 8th and 9 - at least partially - sewn or the like, it is advisable to seal the seams (e.g. with a so-called seam sealing tape). In particular, the individual layers form 3 . 4 . 5 . 6 . 8th and 9 of the layer layer 2 a coherent network.

Die einzelnen Schichten 3, 4, 5, 6, 8 und 9 bzw. der Schichtaufbau 2 können bzw. kann sich dabei über die gesamte Hand einschließlich des Handgelenks und eines Teils des unteren Unterarms erstrecken (1). Gemäß dieser Ausführungsform bilden die einzelnen Schichten 3, 4, 5, 6, 8 und 9 bzw. der Schichtaufbau 2 einen zusammenhängenden Handschuh in Form einer Hand mit fünf Fingern und einem Schaft, der sich über den Handknöchel hinweg erstreckt.The individual layers 3 . 4 . 5 . 6 . 8th and 9 or the layer structure 2 can or can extend over the entire hand including the wrist and part of the lower forearm ( 1 ). According to this embodiment, the individual layers form 3 . 4 . 5 . 6 . 8th and 9 or the layer structure 2 a continuous glove in the shape of a hand with five fingers and a shaft that extends over the knuckle.

Vorteilhafterweise ist der Schutzhandschuh 1 als Fingerhandschuh ausgebildet, weist also die Form einer Hand mit fünf Fingern auf; dies steigert nicht nur den Tragekomfort, sondern erleichtert auch den Einsatz für militärische bzw. ABC-Zwecke. Die Tatsache, daß der erfindungsgemäße Handschuh 1 sich vorteilhafterweise über den Handknöchel hinweg erstreckt (d. h. einen Handschuhschaft aufweist), ermöglicht eine abdichtende Verbindung mit einem gleichzeitig getragenen ABC-Schutzanzug; zu diesem Zweck können der Handschuh und/oder der ABC-Schutzanzug mit entsprechenden Abdichtelementen ausgestattet sein (z. B. Reißverschlüsse, Klettelemente, Dichtlippen etc.), um den Übergang von Schutzhandschuh 1 und ABC-Schutzanzug abzudichten bzw. abdichtend miteinander zu verbinden.The protective glove is advantageous 1 designed as a glove, it has the shape of a hand with five fingers; This not only increases comfort, but also makes it easier to use for military or ABC purposes. The fact that the glove of the invention 1 extends advantageously over the knuckle (ie has a glove shaft), enables a sealing connection with an ABC protective suit worn at the same time; For this purpose, the glove and / or the ABC protective suit can be equipped with appropriate sealing elements (e.g. zippers, Velcro elements, sealing lips, etc.) to prevent the transition from the protective glove 1 and to seal the ABC protective suit or to connect it in a sealing manner.

Insbesondere bilden die einzelnen Schichten 3, 4, 8 und 9 dabei jeweils die Form eines Handschuhs mit fünf Fingern aus: Die Abdeckschicht 9 bildet dabei sozusagen einen Innenhandschuh aus, während die Trägerschicht 3 sozusagen einen Außenhandschuh ausbildet. Die Sperrschicht 4 mit innenseitiger Adsorptionsschicht 5 und außenseitiger Membran 6 bildet zusammen mit der zusätzlichen Trägerschicht 8 einen zwischen Innenhandschuh und Außenhandschuh befindlichen Kernhandschuh aus, wobei alle drei Handschuhteile -Außen-, Innen- wie Kernhandschuh – miteinander verbunden sind und gemeinsam den erfindungsgemäßen Schutzhandschuh 1 bilden.In particular, the individual layers form 3 . 4 . 8th and 9 each with the shape of a glove with five fingers: the cover layer 9 it forms an inner glove, so to speak, while the backing layer 3 forms an outer glove, so to speak. The barrier layer 4 with inside adsorption layer 5 and outside membrane 6 forms together with the additional carrier layer 8th a core glove located between the inner glove and the outer glove, all three glove parts — outer, inner and core glove — being connected to one another and together the protective glove according to the invention 1 form.

Was das Material der Trägerschicht 3, die im allgemeinen die Außenschicht des Schutzhandschuhs 1 bildet, anbelangt, so können hier beliebige, insbesondere atmungsaktive Materialien verwendet werden, wie sie für Handschuhe im allgemeinen verwendet werden. Beispiele hierfür sind Textilmaterialien, vorzugsweise luftdurchlässige Textilmaterialien, insbesondere in Form textiler Flächengebilde, so z. B. Gewebe, Gewirke, Gestricke, Gelege oder Textilverbundstoffe. Beispielsweise kann der Textilverbundstoff ein Vlies sein. Alternativ kann die Trägerschicht 3 aber auch als ein Ledermaterial ausgebildet sein. Dabei ist es vorteilhaft, den Außenhandschuh bzw. die Trägerschicht 3 im Bereich der Fingerspitzen nahtlos auszubilden. Für weitere diesbezügliche Einzelheiten kann auf die vorgenannten Dokumente US 6 301 715 B1 bzw. WO 01/82728 A1 und DE 201 21 518 U1 verwiesen werden, deren jeweiliger Offenbarungsgehalt hiermit im vollen Umfang durch Bezugnahme eingeschlossen ist.As for the material of the backing layer 3 that generally the outer layer of the protective glove 1 forms, as far as any arbitrary, especially breathable materials can be used, such as those used for gloves in general. Examples of this are textile materials, preferably air-permeable textile materials, in particular in the form of textile fabrics, such as. B. fabrics, knitted fabrics, knitted fabrics, scrims or textile composites. For example, the textile composite can be a nonwoven. Alternatively, the backing layer 3 but also be formed as a leather material. It is advantageous to use the outer glove or the backing layer 3 to train seamlessly in the area of the fingertips. For further details in this regard, refer to the aforementioned documents US 6,301,715 B1 or WO 01/82728 A1 and DE 201 21 518 U1 are referred to, the respective disclosure content of which is hereby fully incorporated by reference.

Um ein Eindringen chemischer Gifte (z. B. konzentrierter Tropfen von Kampfstoffen) zu verhindern bzw. zu erschweren, empfiehlt sich eine Oleophobierung und/oder Hydrophobierung des Materials der äußeren Trägerschicht 3, insbesondere durch eine spezielle Imprägnierung.In order to prevent or make it more difficult for chemical poisons to penetrate (e.g. concentrated drops of warfare agents), it is advisable to oleophobicize and / or hydrophobize the material of the outer carrier layer 3 , especially through a special impregnation.

Das Material der Trägerschicht 3 bzw. des Außenhandschuhs besitzt im allgemeinen ein Flächengewicht von 50 bis 300 g/m², insbesondere 75 bis 250 g/m², vorzugsweise 75 bis 175 g/m². Insbesondere ist die Trägerschicht 3 als ein luftdurchlässiges, 75 bis 250 g/m², vorzugsweise 75 bis 175 g/m² schweres textiles Flächengebilde, welches oleophob und/oder hydrophob ausgerüstet sein kann, ausgebildet.The material of the backing 3 or the outer glove generally has a basis weight of 50 to 300 g / m ² , in particular 75 to 250 g / m ² , preferably 75 to 175 g / m ² . In particular, the carrier layer 3 as an air-permeable, 75 to 250 g / m ² , preferably 75 to 175 g / m ² heavy textile fabric, which can be made oleophobic and / or hydrophobic.

Was die Membran 6 anbelangt, so handelt es sich hierbei im allgemeinen um eine kontinuierliche, insbesondere geschlossene oder allenfalls mikroporöse Membran. Dabei beträgt die Dicke der Membran 6 im allgemeinen 1 bis 500 μm, insbesondere 1 bis 250 μm, vorzugsweise 1 bis 100 μm, bevorzugt 1 bis 50 μm, besonders bevorzugt von 2,5 bis 30 μm, ganz besonders bevorzugt 5 bis 25 μm. Zur Erhöhung des Tragekomforts, insbesondere der Atmungsaktivität, weist die Membran 6 bei 25 °C und bei einer Dicke von 50 μm eine hohe Wasserdampfdurchlässigkeit von mindestens 12,5 l/m² pro 24 h, insbesondere mindestens 17,5 l/m² pro 24 h, vorzugsweise mindestens 20 l/m² pro 24 h oder mehr, auf (gemessen nach der "Methode des umgekehrten Bechers" bzw. "inverted cup method" nach ASTM E 96 und bei 25 °C) (Zu weiteren Einzelheiten zur Messung der Wasserdampfdurchlässigkeit [water vapour transmission, WVT] vgl. auch McCullough et al. "A comparison of standard methods for measuring water vapour permeability of fabrics" in Meas. Sci. Technol. [Measurements Science and Technology] 14, 1402-1408, August 2003). Hierdurch wird ein besonders hoher Tragekomfort gewährleistet.As for the membrane 6 As far as this is concerned, this is generally a continuous, in particular closed or at most microporous membrane. The thickness of the membrane 6 is generally 1 to 500 μm, in particular 1 to 250 μm, preferably 1 to 100 μm, preferably 1 to 50 μm, particularly preferably from 2.5 to 30 μm particularly preferably 5 to 25 μm. The membrane has been designed to increase comfort, especially breathability 6 at 25 ° C. and with a thickness of 50 μm a high water vapor permeability of at least 12.5 l / m ² per 24 h, in particular at least 17.5 l / m ² per 24 h, preferably at least 20 l / m ² per 24 h or more, on (measured according to the "inverted cup method" according to ASTM E 96 and at 25 ° C.) (For further details on measuring the water vapor transmission [water vapor transmission, WVT], see also McCullough et al. "A comparison of standard methods for measuring water vapor permeability of fabrics" in Meas. Sci. Technol. [Measurements Science and Technology] 14, 1402-1408, August 2003). This ensures a particularly high level of comfort.

Aufgrund der Vielzahl von Schichten 3, 4, 5, 6, 8 und 9 des Schichtaufbaus 2 ist die Wasserdampfdurchlässigkeit des Schutzhandschuhs 1 insgesamt – im Vergleich zu der Membran 6 allein – geringfügig geringer; die Wasserdampfdurchlässigkeit des Schutzhandschuhs 1 insgesamt ist dennoch sehr hoch und beträgt mindestens 10 l/m² pro 24 h, insbesondere mindestens 15 l/m² pro 24 h, vorzugsweise mindestens 20 l/m² pro 24 h, bei einer Dicke der Membran 6 von 50 μm (bei 25 °C).Because of the multitude of layers 3 . 4 . 5 . 6 . 8th and 9 of the layer structure 2 is the water vapor permeability of the protective glove 1 overall - compared to the membrane 6 alone - slightly less; the water vapor permeability of the protective glove 1 overall, however, is very high and amounts to at least 10 l / m ² per 24 h, in particular at least 15 l / m ² per 24 h, preferably at least 20 l / m ² per 24 h, with a thickness of the membrane 6 of 50 μm (at 25 ° C).

Die Membran 6 sollte aus Gründen der Atmungsaktivität einen geringen Wasserdampfdurchgangswiderstand R_et unter stationären Bedingungen – gemessen nach DIN EN 31 092:1993 vom Februar 1994 ("Textilien – Physiologische Wirkungen, Messung des Wärme- und Wasserdampfdurchgangswiderstandes unter stationären Bedingungen [sweating guarded-hotplate test]") bzw. nach gleichlautender internationaler Norm ISO 11 092 – bei 35 °C von höchstens 30 (m² • Pascal)/Watt, insbesondere höchstens 25 (m²·Pascal)/Watt, vorzugsweise höchstens 20 (m²·Pascal)/Watt, bei einer Dicke der Membran 6 von 50 μm aufweisen. Aufgrund der Vielzahl von Schichten 3, 4, 5, 6, 8 und 9 des Schichtaufbaus 2 ist der Wasserdampfdurchgangswiderstand R_et des Schutzhandschuhs 1 insgesamt – im Vergleich zu der Membran 6 allein – geringfügig höher; im allgemeinen beträgt der Wasserdampfdurchgangswiderstand R_et des Handschuhs 1 insgesamt höchstens 30 (m²·Pascal)/Watt, insbesondere höchstens 25 (m²·Pascal)/Watt, vorzugsweise höchstens 20 (m²·Pascal)/Watt, bei einer Dicke der Membran 6 von 50 μm.The membrane 6 should have a low water vapor resistance R _et under stationary conditions - measured according to DIN EN 31 092: 1993 from February 1994 ("textiles - physiological effects, measurement of heat and water vapor resistance under stationary conditions [sweating guarded-hotplate test]") for reasons of breathability or according to the international standard ISO 11 092 - at 35 ° C of at most 30 (m ² · Pascal) / watt, in particular at most 25 (m ² · Pascal) / watt, preferably at most 20 (m ² · Pascal) / watt, with a thickness of the membrane 6 of 50 μm. Because of the multitude of layers 3 . 4 . 5 . 6 . 8th and 9 of the layer structure 2 is the water vapor resistance R _{et of} the protective glove 1 overall - compared to the membrane 6 alone - slightly higher; in general, the water vapor resistance R _{et of} the glove 1 a total of at most 30 (m ² · Pascal) / watt, in particular at most 25 (m ² · Pascal) / watt, preferably at most 20 (m ² · Pascal) / watt, with a thickness of the membrane 6 of 50 μm.

Die Membran 6 sollte im übrigen allenfalls nur geringfügig wasseraufnahmefähig bzw. quellfähig sein; eine geringfügige Wasseraufnahmefähigkeit bzw. Quellfähigkeit erhöht den Tragekomfort. Insbesondere sollte die Quellfähigkeit bzw. das Wasseraufnahmevermögen der Membran 6 höchstens 35 %, insbesondere höchstens 25 %, vorzugsweise höchstens 20 %, bezogen auf das Eigengewicht der Membran 6, betragen. Im übrigen sollte die Membran 6 gegenüber Flüssigkeiten, insbesondere Wasser, und/oder gegenüber Aerosolen zumindest im wesentlichen undurchlässig sein oder zumindest deren Durchtritt verzögern. Zur Erreichung einer allenfalls geringfügigen Quellfähigkeit sollte die Membran 6 keine oder im wesentlichen keine stark hydrophilen Gruppen, insbesondere keine Hydroxylgruppen, aufweisen. Zu Zwecken einer geringfügigen Quellung kann die Membran 6 aber schwach hydrophile Gruppen, beispielsweise Polyethergruppen, aufweisen.The membrane 6 Otherwise, it should only be slightly water-absorbent or swellable; a slight water absorption or swelling capacity increases comfort. In particular, the swellability or water absorption capacity of the membrane should 6 at most 35%, in particular at most 25%, preferably at most 20%, based on the weight of the membrane 6 , amount. Otherwise, the membrane 6 be at least essentially impermeable to liquids, in particular water, and / or aerosols or at least delay their passage. In order to achieve a slight swelling capacity, the membrane should 6 have no or essentially no strongly hydrophilic groups, in particular no hydroxyl groups. The membrane may be used for slight swelling 6 but have weakly hydrophilic groups, for example polyether groups.

Die Membran 6 kann aus einem Kunststoff oder einen Polymermaterial bestehen oder ein solches umfassen. Ein solcher Kunststoff bzw. ein solches Polymer kann geeigneterweise z. B. ausgewählt sein aus der Gruppe von Polyuethanen, Polyetheramiden, Polyesteramiden, Polytetrafluorethylenen und/oder Polymeren auf Cellulosebasis sowie Derivaten der vorgenannten Verbindungen. Beispielsweise kann die Membran 6 als Reaktionsprodukt aus der Reak tion eines Isocyanats, insbesondere eines maskierten oder blockierten Isocyanats, mit einem isocyanatreaktiven Vernetzer erhalten sein. So kann die Membran 6 beispielsweise eine polyurethanbasierte Membran sein. Gleichermaßen kann die Membran 6 auch eine expandierte, gegebenenfalls mikroporöse Membran auf Basis von Polytetrafluorethylen sein.The membrane 6 may consist of or comprise a plastic or a polymer material. Such a plastic or such a polymer can suitably z. B. can be selected from the group of polyethanes, polyether amides, polyester amides, polytetrafluoroethylene and / or cellulose-based polymers and derivatives of the aforementioned compounds. For example, the membrane 6 be obtained as a reaction product from the reaction of an isocyanate, in particular a masked or blocked isocyanate, with an isocyanate-reactive crosslinker. So the membrane 6 for example, a polyurethane-based membrane. Similarly, the membrane 6 can also be an expanded, optionally microporous membrane based on polytetrafluoroethylene.

Gemäß einer besonderen Ausführungsform kann die gegebenenfalls vorhandene Membran 6 als ein mehrschichtiges Membranlaminat bzw. als ein mehrschichtiger Membranverbund ausgebildet sein. Dieses Membranlaminat bzw. dieser Membranverbund kann aus mindestens zwei, vorzugsweise mindestens drei miteinander verbundenen Membranschichten oder -lagen bestehen. Beispielsweise kann dieses Membranlaminat bzw. dieser Membranverbund eine Kernschicht auf Basis eines Polymers auf Cellulosegrundlage und zwei mit der Kernschicht verbundene äußere Schichten, insbesondere auf Basis eines Polyurethans, eines Polyetheramids und/oder eines Polyesteramids, umfassen. Dabei kann die Kernschicht auf Basis eines Polymers auf Cellulosegrundlage als 1 bis 100 μm, insbesondere 5 bis 50 μm, vorzugsweise 10 bis 20 μm dicke Membran ausgebildet sein und können die zwei mit der Kernschicht verbundenen äußeren Schichten jeweils als 1 bis 100 μm, insbesondere 5 bis 50 μm, vorzugsweise 5 bis 10 μm dicke Membran ausgebildet sein. Diese besondere Ausgestaltung der Membran 6 ermöglicht es, verschiedene Membranmaterialien mit jeweils unterschiedlichen Eigenschaften, insbesondere unterschiedlichen Wasserdampfdurchlässigkeiten und/oder Barrierewirkungen gegenüber chemischen Giften, miteinander zu kombinieren und so eine Optimierung der Eigenschaften der Membran 6 zu erreichen. Beispielsweise sind Cellulose und Cellulosederivate ausgezeichnete Sperrschichtmaterialien, insbesondere gegenüber chemischen Schad- bzw. Giftstoffen, wie z. B. Kampfstoffen (Lost etc.), und werden von diesen Giften nicht angegriffen bzw. aufgelöst; zum anderen verhindern polyurethanbasierte Materialien eine Migration bzw. Diffusion der in der Celluloseschicht gegebenenfalls vorhandenen Weichmacher und dämpfen außerdem das durch die Cellulose bedingte, beim Tragen auftretende Knistern. Deswegen ist es gemäß dieser besonderen Ausführungsform bevorzugt, daß im Fall eines Membranlaminats oder -verbunds die Kernschicht auf Basis eines Polymers auf Cellulosegrundlage gebildet wird, während die beiden Außenschichten der Membran 6 durch Polyurethanschichten gebildet werden.According to a special embodiment, the membrane which may be present 6 be designed as a multilayer membrane laminate or as a multilayer membrane composite. This membrane laminate or membrane composite can consist of at least two, preferably at least three interconnected membrane layers or layers. For example, this membrane laminate or membrane composite can comprise a core layer based on a cellulose-based polymer and two outer layers connected to the core layer, in particular based on a polyurethane, a polyether amide and / or a polyester amide. The core layer can be based on a cellulose-based polymer as a 1 to 100 μm, in particular 5 to 50 μm, preferably 10 to 20 μm thick membrane and the two outer layers connected to the core layer can each be 1 to 100 μm, in particular 5 to 50 microns, preferably 5 to 10 microns thick membrane. This special design of the membrane 6 makes it possible to combine different membrane materials with different properties, in particular different water vapor permeability and / or barrier effects against chemical poisons, and thus an optimization of the properties of the membrane 6 to reach. For example, cellulose and cellulose derivatives are excellent barrier materials, especially against chemical pollutants or toxins, such as. B. warfare agents (lost etc.), and are not attacked or dissolved by these poisons; on the other hand, polyurethane-based materials prevent migration or diffusion of the plasticizers that may be present in the cellulose layer and also dampen the crackling caused by the cellulose when it is worn. It is therefore preferred according to this particular embodiment that in the case of a membrane laminate or composite, the core layer is formed on the basis of a cellulose-based polymer, while the two outer layers of the membrane 6 be formed by polyurethane layers.

Wie zuvor geschildert, kann – insbesondere um die Stabilität bzw. Verschließbeständigkeit, insbesondere die Reißfestigkeit, der Membran 6 im Herstellungsprozeß (z. B. beim Bedrucken der Membran 6 mit heißem Klebstoff 7) wie auch beim Tragen zu erhöhen – die Membran 6 auf einer zusätzlichen Trägerschicht 8 aufgebracht bzw. aufkaschiert sein. Diesbezüglich kann auf obige Ausführungen verwiesen werden.As described above, the membrane can - in particular about the stability or wear resistance, in particular the tear strength 6 in the manufacturing process (e.g. when printing on the membrane 6 with hot glue 7 ) as well as when wearing - the membrane 6 on an additional support layer 8th be applied or laminated. In this regard, reference can be made to the above statements.

Zur Erhöhung des Tragekomforts einerseits und zur Erzielung einer guten Verschleißbeständigkeit andererseits ist es vorteilhaft, wenn die Membran 6 eine gewisse Elastizität aufweist. Insbesondere ist es vorteilhaft, wenn die Membran 6 zu mindestens 10 %, insbesondere zu mindestens 20 %, vorzugsweise zu mindestens 30 % oder mehr, zumindest in eine Richtung gedehnt bzw. gestreckt werden kann (bezogen auf die Membran 6). Auch der Schichtaufbau 2 insgesamt sollte zu den vorgenannten Zwecken – neben einer guten Biegsamkeit – auch eine gewisse Elastizität aufweisen; verglichen mit der Membran 6, ist die Elastizität des Schichtaufbaus 2 als Ganzes jedoch etwas geringer, und im allgemeinen ist der Schichtaufbau 2 insgesamt zu mindestens 5 %, vorzugsweise zu mindestens 10 %, ganz besonders bevorzugt zu mindestens 15 % oder mehr, zumindest in eine Richtung dehnbar bzw. streckbar.To increase the comfort on the one hand and to achieve good wear resistance on the other hand, it is advantageous if the membrane 6 has a certain elasticity. In particular, it is advantageous if the membrane 6 can be stretched or stretched at least 10%, in particular at least 20%, preferably at least 30% or more, at least in one direction (based on the membrane 6 ). Also the layer structure 2 overall, for the aforementioned purposes, in addition to good flexibility, it should also have a certain elasticity; compared to the membrane 6 , is the elasticity of the layer structure 2 as a whole, however, somewhat less, and in general the layer structure is 2 Overall at least 5%, preferably at least 10%, very particularly preferably at least 15% or more, at least stretchable or stretchable in one direction.

Gemäß einer besonderen, in den Figuren nicht dargestellten Ausführungsform kann die Membran 6 gleichzeitig die Klebstoffschicht 7 zur Befestigung der Adsorptionsschicht 5 darstellen. In diesem Fall muß die Membran 6 selbstklebend, insbesondere hitzeklebrig, ausgebildet sein. Gemäß dieser besonderen Ausführungsform kommt es zu einer Einsparung von Gewicht, da auf eine zusätzliche Klebstoffschicht 7 gänzlich verzichtet werden kann.According to a special embodiment, not shown in the figures, the membrane can 6 at the same time the adhesive layer 7 for attaching the adsorption layer 5 represent. In this case, the membrane 6 be self-adhesive, in particular heat-tacky. According to this particular embodiment, there is a saving in weight because of an additional adhesive layer 7 can be dispensed with entirely.

Bei dem Aufbau bzw. der Konzeption des erfindungsgemäßen Schutzhandschuhs 1 geht man im allgemeinen derart vor, daß die Membran 6 des Schutzhandschuhs 1 aus zwei miteinander verbundenen, vorzugsweise abdichtend miteinander verbundenen, insbesondere miteinander verklebten und/oder verschweißten Materialstücken besteht. Dabei weisen beide Materialstücke jeweils die Form einer Hand mit fünf Fingern auf, wobei eines der beiden Materialstücke zur Abdeckung der Handvorderseite (Handinnenseite) und das andere Materialstück zur Bedeckung der Handrückseite (Handrücken) bestimmt ist und die beiden Materialstücke nur entlang ihrer jeweiligen äußeren Kontu ren, insbesondere entlang des Handumrisses, miteinander verbunden, vorzugsweise abdichtend miteinander verbunden, insbesondere miteinander verklebt und/oder verschweißt, sind.In the construction or design of the protective glove according to the invention 1 the procedure is generally such that the membrane 6 of the protective glove 1 consists of two interconnected, preferably sealingly interconnected, in particular glued and / or welded pieces of material. Both pieces of material each have the shape of a hand with five fingers, one of the two pieces of material for covering the front of the hand (inside of the hand) and the other piece of material for covering the back of the hand (back of the hand) is intended and the two pieces of material only along their respective outer contours , in particular along the outline of the hand, connected to one another, preferably connected to one another in a sealing manner, in particular glued and / or welded to one another.

Was die Adsorptionsschicht 5 des erfindungsgemäßen Schutzhandschuhs 1 anbelangt, so ist diese im allgemeinen diskontinuierlich ausgebildet, d. h. die Adsorptionsschicht 5 umfaßt im allgemeinen diskrete, chemische Gifte adsorbierende Adsorptionspartikel (z. B. auf Basis von Aktivkohle), die beispielsweise mittels eines Klebstoffs 7 auf der Membran 6 fixiert sein können. Das Adsorptionsmaterial der Adsorptionsschicht 5 ist insbesondere ein Aktivkohle enthaltendes oder hieraus bestehendes Adsorptionsmaterial, beispielsweise ein Material auf Basis von Aktivkohle in Form von Aktivkohleteilchen und/oder Aktivkohlefasern.As for the adsorption layer 5 of the protective glove according to the invention 1 As far as this is concerned, it is generally discontinuous, ie the adsorption layer 5 generally comprises discrete adsorbent particles (e.g. based on activated carbon) adsorbing chemical poisons, for example by means of an adhesive 7 on the membrane 6 can be fixed. The adsorption material of the adsorption layer 5 is in particular an adsorption material containing or consisting of activated carbon, for example a material based on activated carbon in the form of activated carbon particles and / or activated carbon fibers.

Denn, wenn als Adsorptionsmaterial für die Ausbildung der Adsorptionsschicht 5 aktivkohlehaltige Materialien verwendet werden, kann der ohnehin bestehende, hohe Tragekomfort noch weiter gesteigert werden, weil die Aktivkohle als intermediärer Feuchtigkeits- bzw. Wasserspeicher (z. B. für Schweiß) dient und Feuchtigkeit bzw. Wasser sozusagen "abpuffern" kann. Bei Verwendung beispielsweise von Aktivkohlekügelchen als Adsorptionsmaterial für die Adsorptionsschicht 5 sind Auflagen von bis zu ca. 250 g/m² oder mehr üblich, so daß z. B. bei einem Schweißausbruch etwa 40 g/m² Feuchtigkeit gespeichert werden können, die im Fall einer atmungsaktiven Träger- bzw. Außenschicht 3 dann wieder an die Umgebung abgegeben werden können.Because if as an adsorption material for the formation of the adsorption layer 5 activated carbon-containing materials can be used, the already existing high level of comfort can be increased even further, because the activated carbon serves as an intermediate moisture or water reservoir (e.g. for sweat) and can "buffer" moisture or water, so to speak. When using, for example, activated carbon beads as the adsorption material for the adsorption layer 5 are up to about 250 g / m ² or more, so that z. B. in the event of a sweat, about 40 g / m ^{2 of} moisture can be stored, which in the case of a breathable backing or outer layer 3 can then be released to the environment again.

Gemäß einer Ausführungsform der vorliegenden Erfindung umfaßt die Adsorptionsschicht 5 diskrete Aktivkohleteilchen, vorzugsweise in Kornform ("Kornkohle") oder ("Kugelkohle"). In diesem Fall beträgt der mittlere Durchmesser der Aktivkohleteilchen weniger als 1,0 mm, insbesondere weniger als 0,5 mm, vorzugsweise weniger als 0,4 mm, bevorzugt weniger als 0,35 mm; der mittlere Durchmesser der Aktivkohleteilchen beträgt jedoch mindestens 0,1 mm. Bei dieser Ausführungsform werden die Aktivkohleteilchen im allgemeinen in einer Menge von 5 bis 500 g/m², vorzugsweise 20 bis 300 g/m², bevorzugt 25 bis 250 g/m², besonders bevorzugt 50 bis 120 g/m², auf der Membran 6 aufgebracht. Geeignete Aktivkohleteilchen weisen innere Ober flächen (BET) von mindestens 800 m²/g, insbesondere von mindestens 900 m²/g, vorzugsweise von mindestens 1.000 m²/g, bevorzugt im Bereich von 800 bis 1.500 m²/g, auf. Kornkohle, insbesondere Kugelkohle, hat den entscheidenden Vorteil, daß sie enorm abriebfest und sehr hart ist, was in Bezug auf die Verschleißeigenschaften von großer Bedeutung ist. Bevorzugterweise beträgt der Berstdruck für ein einzelnes Aktivkohleteilchen, insbesondere Aktivkohlekörnchen Bzw. -kügelchen, im allgemeinen mindestens etwa 5 Newton, insbesondere mindestens etwa 10 Newton, und kann bis zu etwa 20 Newton erreichen.According to one embodiment of the present invention, the adsorption layer comprises 5 discrete activated carbon particles, preferably in grain form ("grain coal") or ("spherical coal"). In this case, the average diameter of the activated carbon particles is less than 1.0 mm, in particular less than 0.5 mm, preferably less than 0.4 mm, preferably less than 0.35 mm; however, the average diameter of the activated carbon particles is at least 0.1 mm. In this embodiment, the activated carbon particles are generally present in an amount of 5 to 500 g / m ² , preferably 20 to 300 g / m ² , preferably 25 to 250 g / m ² , particularly preferably 50 to 120 g / m ² membrane 6 applied. Suitable activated carbon particles have inner surfaces (BET) of at least 800 m ² / g, in particular of at least 900 m ² / g, preferably of at least 1,000 m ² / g, preferably in the range from 800 to 1,500 m ² / g. Granular coal, in particular spherical coal, has the decisive advantage that it is extremely abrasion-resistant and very hard, which is of great importance with regard to the wear properties. The bursting pressure for an individual activated carbon particle, in particular activated carbon granules or spheres, generally at least about 5 newtons, especially at least about 10 newtons, and can reach up to about 20 newtons.

Gemäß einer alternativen Ausführungsform kann die Adsorptionsschicht 5 als Adsorptionsmaterial Aktivkohlefasern, insbesondere in Form von Aktivkohlefaserflächengebilden, umfassen. Derartige Aktivkohlefaserflächengebilde können beispielsweise ein Flächengewicht von 20 bis 200 g/m², insbesondere 30 bis 150 g/m², vorzugsweise 15 bis 120 g/m², aufweisen. Bei diesen Aktivkohlefaserflächengebilden kann es sich beispielsweise um Aktivkohlefasergewebe, -gewirke, -gelege oder -verbundstoffe handeln (z. B auf Basis von carbonisierter und aktivierter Cellulose und/oder carbonisierten und aktivierten Acrylnitrilen).According to an alternative embodiment, the adsorption layer 5 Activated carbon fibers, in particular in the form of activated carbon fiber structures, comprise as adsorption material. Such activated carbon fiber fabrics can have, for example, a basis weight of 20 to 200 g / m ² , in particular 30 to 150 g / m ² , preferably 15 to 120 g / m ² . These activated carbon fiber fabrics can be, for example, activated carbon fiber fabrics, knitted fabrics, scrims or composite materials (e.g. based on carbonized and activated cellulose and / or carbonized and activated acrylonitriles).

Gleichermaßen ist es auch möglich, als Adsorptionsmaterial der Adsorptionsschicht 5 Aktivkohleteilchen und Aktivkohlefasern miteinander zu kombinieren. Aktivkohleteilchen haben den Vorteil einer höheren Adsorptionskapazität, während Aktivkohlefasern eine bessere Adsorptionskinetik aufweisen.Likewise, it is also possible to use the adsorption layer as the adsorption material 5 Combine activated carbon particles and activated carbon fibers. Activated carbon particles have the advantage of a higher adsorption capacity, while activated carbon fibers have better adsorption kinetics.

Zur Erhöhung der Adsorptionseffizienz bzw. Adsorptionsleistung besteht die Möglichkeit, das Adsorptionsmaterial der Adsorptionsschicht 5, insbesondere die Aktivkohleteilchen und/oder die Aktivkohlefasern, außerdem mit mindestens einem Katalysator zu imprägnieren. Erfindungsgemäß geeignete Katalysatoren sind beispielsweise Enzyme und/oder Metallionen, vorzugsweise Kupfer-, Silber-, Cadmium-, Platin-, Palladium-, Zink- und/oder Quecksilberionen. Die Menge an Katalysator kann in weiten Bereichen variieren; im allgemeinen beträgt sie 0,05 bis 12 Gew.-%, vorzugsweise 1 bis 10 Gew.-%, besonders bevorzugt 2 bis 8 Gew.-%, bezogen auf das Gewicht der Adsorptionsschicht 5.The adsorption material of the adsorption layer can be used to increase the adsorption efficiency or adsorption performance 5 , in particular the activated carbon particles and / or the activated carbon fibers, also to be impregnated with at least one catalyst. Suitable catalysts according to the invention are, for example, enzymes and / or metal ions, preferably copper, silver, cadmium, platinum, palladium, zinc and / or mercury ions. The amount of catalyst can vary within wide limits; in general it is 0.05 to 12% by weight, preferably 1 to 10% by weight, particularly preferably 2 to 8% by weight, based on the weight of the adsorption layer 5 ,

Für eine effiziente Adsorptionsleistung ist es bevorzugt, wenn mindestens 50 %, insbesondere mindestens 60 %, vorzugsweise mindestens 70 %, der Adsorptionsschicht 5 bzw. des Adsorptionsmaterials der Adsorptionsschicht 5 für die zu adsorbierenden Gifte bzw. Kampfstoffe frei zugänglich sind, d. h. nicht mit Klebstoff 7 bedeckt sind. Dies geschieht dadurch, daß die Menge und die Art, insbesondere die Viskosität, des Klebstoffs 7 derart ausgelegt sind, daß das Adsorptionsmaterial der Adsorptionsschicht 5 nicht vollständig in den Klebstoff 7 eingedrückt wird bzw. einsinkt.For efficient adsorption performance, it is preferred if at least 50%, in particular at least 60%, preferably at least 70%, of the adsorption layer 5 or the adsorption material of the adsorption layer 5 are freely accessible for the poisons or warfare agents to be adsorbed, ie not with glue 7 are covered. This happens because the amount and type, especially the viscosity, of the adhesive 7 are designed such that the adsorbent material of the adsorbent layer 5 not completely in the glue 7 is pushed in or sinks.

Ein typischer Schutzhandschuh 1 nach der vorliegenden Erfindung kann beispielsweise aus den folgenden Schichten bestehen: Die Trägerschicht 3 ("Außenhandschuh") kann beispielsweise aus einer robusten und gegebenenfalls schwer entflammbaren Faserart bestehen, bevorzugt in einer nahtlosen rundgestrickten Form ausgeführt. Die Abdeckschicht 9 ("Innenhandschuh") kann aus Materialien bestehen, die angenehm auf der Haut zu tragen sind (Co, Rayon, PA, PES, m-Aramid), gegebenenfalls in flammfester Ausführung, bevorzugt in einer nahtlosen, rundgestrickten Ausführung. Die Sperrschicht 4, die zwischen dem Innen- und dem Außenhandschuh angeordnet ist, kann neben der Membran 6 aktivierte Aktivkohlestoffkügelchen und/oder -fasern zur Ausbildung der Adsorptionsschicht 5 zu Zwecken der Adsorption der Schadstoffe enthalten.A typical protective glove 1 according to the present invention can consist, for example, of the following layers: the carrier layer 3 ("Outer glove") can consist, for example, of a robust and possibly flame-retardant type of fiber, preferably in a seamless circular knitted form. The cover layer 9 ("Inner glove") can consist of materials that are comfortable to wear on the skin (Co, Rayon, PA, PES, m-aramid), optionally in a flame-resistant version, preferably in a seamless, circular-knitted version. The barrier layer 4 , which is arranged between the inner and outer gloves, can be next to the membrane 6 activated carbon balls and / or fibers to form the adsorption layer 5 for the purpose of adsorbing the pollutants.

Der erfindungsgemäße Schutzhandschuh 1 bietet einen effizienten Schutz gegenüber chemischen Giften, insbesondere chemischen Kampfstoffen, bei gleichzeitig hohem Tragekomfort, insbesondere guter Atmungsaktivität. Der entscheidende Vorteil des erfindungsgemäßen Schutzhandschuhs 1 nach der vorliegenden Erfindung besteht darin, daß die Schutzfunktion gegenüber chemischen Giften in den Schutzhandschuh 1 selbst integriert ist und kein zusätzlicher Ausrüstungsgegenstand erforderlich ist. Dadurch wird nicht nur eine beträchtliche Gewichtseinsparung und ein erhöhter Tragekomfort erreicht, sondern es wird zudem die Möglichkeit einer effizienten abdichtenden Verbindung des Übergangs zu einem ABC-Schutzanzug eröffnet, so daß chemische Gifte, z. B. Kampfstoffe, den Übergang von Schutzhandschuh/Schutzanzug nicht bzw. nicht ohne weiteres passieren können. Aufgrund dieser Eigenschaften eignet sich der erfindungsgemäße Schutzhandschuh 1 nach der vorliegenden Erfindung insbesondere für den militärischen Einsatz bzw. den ABC-Einsatz (z. B. in der Form eines Militärschutzhandschuhs bzw. ABC-Schutzhandschuhs).The protective glove according to the invention 1 offers efficient protection against chemical poisons, especially chemical warfare agents, while at the same time being very comfortable, especially good breathability. The decisive advantage of the protective glove according to the invention 1 according to the present invention is that the protective function against chemical poisons in the protective glove 1 itself is integrated and no additional equipment is required. This not only achieves considerable weight savings and increased comfort, but it also opens up the possibility of an efficient sealing connection of the transition to an ABC protective suit, so that chemical poisons, e.g. B. warfare agents, the transition from protective gloves / protective suit can not or not easily pass. Because of these properties, the protective glove according to the invention is suitable 1 according to the present invention, in particular for military use or ABC use (for example in the form of a military protective glove or ABC protective glove).

Infolge der hohen Effizienz der Schutzfunktion der Adsorptionsschicht 5, welche durch die erfindungsgemäße Verwendung der Membran 6 erhöht wird, lassen sich auch atmungsaktive Handschuhaußenmaterialien, so z. B. Leder oder Textilien, einsetzen, so daß sich auf diese Weise der Tragekomfort erhöhen läßt, ohne daß der Träger des Schutzhandschuhs 1 einer erhöhten Gefährdung durch die Verwendung eines atmungsaktiven Handschuhaußenmaterials ausgesetzt ist.As a result of the high efficiency of the protective function of the adsorption layer 5 which by the use of the membrane according to the invention 6 is increased, breathable glove outer materials, such. B. leather or textiles, so that the wearing comfort can be increased in this way without the wearer of the protective glove 1 is exposed to an increased risk from the use of a breathable outer glove material.

Aufgrund der hohen Flexibilität bzw. guten Biegsamkeit der einzelnen Schichten 3, 4, 5, 6, 8 und 9 bzw. des Schichtaufbaus 2 insgesamt wird nicht nur ein guter Tragekomfort erreicht, sondern außerdem auch eine gute Verschleißbeständigkeit des erfindungsgemäßen Schutzhandschuhs 1 bei gleichzeitig guter Taktilität.Because of the high flexibility and good flexibility of the individual layers 3 . 4 . 5 . 6 . 8th and 9 or the layer structure 2 overall not only good wearing comfort is achieved, but also good wear resistance of the protective glove according to the invention 1 with good tactility at the same time.

Durch die erfindungsgemäße Ausgestaltung des Schutzhandschuhs 1 nach der vorliegenden Erfindung wird eine ausgezeichnete Barrierewirkung gegenüber chemischen Kampfstoffen erreicht. Die Barrierewirkung des Schutzhandschuhs 1 bzw. der Membran 6 gegenüber chemischen Kampfstoffen, insbesondere Bis-[2-chlorethyl]sulfid (synonym auch als Senfgas, Lost oder Gelbkreuz bezeichnet), gemessen nach CRDEC-SP-84010, Methode 2.2, beträgt höchstens 4 μg/cm² pro 24 h, insbesondere höchstens 3,5 μg/cm² pro 24 h, vorzugsweise höchstens 3,0 μg/cm² pro 24 h, besonders bevorzugt höchstens 2,5 μg/cm² pro 24 h, bei einer Dicke der Membran 6 von 50 μm.The inventive design of the protective glove 1 according to the present invention, an excellent barrier against chemical warfare agents is achieved. The barrier effect of the protective glove 1 or the membrane 6 compared to chemical warfare agents, in particular bis- [2-chloroethyl] sulfide (also known synonymously as mustard gas, mustard or yellow cross), measured according to CRDEC-SP-84010, method 2.2, is at most 4 μg / cm ² per 24 h, in particular at most 3 , 5 μg / cm ² per 24 h, preferably at most 3.0 μg / cm ² per 24 h, particularly preferably at most 2.5 μg / cm ² per 24 h, with a thickness of the membrane 6 of 50 μm.

Die Herstellung des erfindungsgemäßen Schutzhandschuhs 1 kann in an sich bekannter Weise erfolgen. Dies ist dem mit der Herstellung von Handschuhen befaßten Fachmann bestens bekannt.The production of the protective glove according to the invention 1 can be done in a manner known per se. This is well known to those skilled in the manufacture of gloves.

Beispielsweise kann bei der Herstellung eines erfindungsgemäßen Handschuhs wie folgt vorgegangen werden: Eine ca. 50 bis 100 μm dicke Membran 6 wird mittels eines punktförmig aufgetragenen Klebstoffs auf eine Trägerschicht 8, die der Verstärkung und Stabilisierung der Membran dient, auflaminiert bzw. aufkaschiert. Anschließend wird die Membran 6, bei der es sich beispielsweise um eine Polyurethanmembran handeln kann, auf der der Trägerschicht 8 abgewandten Seite mit einem wasserdampfdurchlässigen Klebstoff 7 in Form eines punktförmigen Rasters bedruckt, auf den anschließen im noch klebefähigen Zustand der Klebstoffs 7 Aktivkohlekügelchen zur Ausbildung der Adsorptionsschicht 5 aufgebracht werden. Dann wird der Klebstoff 7 gegebenenfalls getrocknet und/oder ausgehärtet. Anschließend werden zwei Materialstücke des so erhaltenen Materials in Form einer Hand mit fünf Fingern ausgeschnitten und entlang der Handumrisse – jeweils mit den Membranen 6 zur Innenseite – verklebt oder verschweißt, so daß eine erfindungsgemäße Sperrschicht 4 in der Form eines mit Aktivkohle beaufschlagten Membranhandschuhs resultiert. Die Adsorptionsschicht 5 wird innenseitig mit einem Abdeckmaterial 9 in der Form eines Innenhandschuhs beaufschlagt, beispielsweise durch Verkleben mit einem Schmelzkleberweb; dies kann beispielsweise dadurch geschehen, daß der Innenhandschuh über einen Metalldorn in der Form einer hand mit fünf Fingern gestülpt wird, anschließend z. B. mit dem Schmelzkleberweb beaufschlagt wird und hierauf dann der zuvor hergestellte Membranhandschuh gestülpt wird. Die Tragschicht 8 wird anschließend außenseitig mit einer Trägerschicht 3 in der Form eines Außenhandschuhs verbunden (z. B. mittels der zuvor beschriebenen Technik), so daß letztendlich ein erfindungsgemäßer Schutzhandschuh 1 mit einer Abdeckschicht 9 als Innenhandschuh, einer äußeren Trägerschicht 3 als Außenhandschuh sowie einer zwischen Innen- und Außenhandschuh angeordneten Sperrschicht 4 aus Adsorptionsschicht 5 und Membran 6, die zusammen mit der zusätzlichen Stabilisierungsschicht 8 für die Membran 6 sozusagen den einen Kern- bzw. Mittelhandschuh bildet, resultiert, wobei die einzelnen Schichten 3, 4 und 9 jeweils miteinander verbunden sind.For example, the manufacture of a glove according to the invention can be carried out as follows: an approximately 50 to 100 μm thick membrane 6 is applied to a carrier layer by means of a point-applied adhesive 8th , which serves to reinforce and stabilize the membrane, laminated or laminated. Then the membrane 6 , which can be, for example, a polyurethane membrane on which the carrier layer 8th opposite side with a water vapor permeable adhesive 7 printed in the form of a dot-shaped grid on which the adhesive is still adhesive 7 Activated carbon beads to form the adsorption layer 5 be applied. Then the glue 7 optionally dried and / or cured. Subsequently, two pieces of material of the material thus obtained are cut out in the form of a hand with five fingers and along the outline of the hand - each with the membranes 6 to the inside - glued or welded, so that a barrier layer according to the invention 4 in the form of a membrane glove loaded with activated carbon. The adsorption layer 5 comes with a covering material on the inside 9 applied in the form of an inner glove, for example by gluing with a hot melt adhesive web; This can be done, for example, by putting the inner glove over a metal mandrel in the shape of a hand with five fingers, then z. B. is applied with the hot-melt adhesive web and then the membrane glove previously made is put on. The base course 8th is then coated on the outside with a backing 3 connected in the form of an outer glove (z. B. by means of the technique described above), so that ultimately a protective glove according to the invention 1 with a cover layer 9 as an inner glove, an outer backing 3 as an outer glove and a barrier layer arranged between inner and outer glove 4 from adsorption layer 5 and membrane 6 that together with the additional stabilization layer 8th for the membrane 6 The core or middle glove, so to speak, results, with the individual layers 3 . 4 and 9 are connected to each other.

Gemäß einer typischen Ausführungsform kann ein dreilagiger Schutzhandschuh 1 nach der vorliegenden Erfindung wie folgt zusammengesetzt werden:

1. Die Trägerschicht 3 ("Außenhandschuh") kann beispielsweise aus einer robusten und gegebenenfalls schwer entflammbaren Faserart bestehen, bevorzugt in einer nahtlosen rundgestrickten Form ausgeführt.
2. Die Abdeckschicht 9 ("Innenhandschuh") kann aus Materialien bestehen, die angenehm auf der Haut zu tragen sind (Co, Rayon, PA, PES, m- Aramid), gegebenenfalls in flammfester Ausführung, bevorzugt in einer nahtlosen, rundgestrickten Ausführung.
3. Die Sperrschicht 4 ("Funktionsschicht"), die zwischen dem Innen- und dem Außenhandschuh angeordnet ist, kann neben der Membran 6 aktivierte Aktivkohlestoffkügelchen und/oder -fasern zur Ausbildung der Adsorptionsschicht 5 zu Zwecken der Adsorption der Schadstoffe enthalten, und zwar in unterschiedlichen alternativen Ausgestaltungen, wie im folgenden beschrieben: a) Auf eine atmungsaktive Membranschicht 6 (z. B. aus PU, PES, PA, PTFE, Cellulose etc.) werden aktivierte Aktivkohlekügelchen aufgebracht. Das Erzeugen der Schicht und das Auftragen der Kügelchen kann durch Tauchen oder durch übliche Beschichtungs- und Belegungsprozesse erfolgen. Falls als Zwischenschritt eine beschichtete Folie erzeugt wird, wird diese durch geeignete Verfahren (z. B. Verkleben, Nähen, Schweißen etc.) in eine zwei- oder dreidimensionale Handform gebracht. Die Funktionsschicht kann in der Beschichtung oder auch der den Aktivkohlekügelchen gegenüberliegenden Seite mittels eines Netzes oder Gewirkes aus thermoplastischen Fasern verstärkt sein. b) Die Funktionsschicht besteht aus einem handschuhförmigen Gestrick aus aktivierten Kohlenstoffasern, hergestellt durch Carbonisieren eines entsprechenden Handschuhs aus Rayon oder Polyacrylnitrilfasern und anschließender Aktivierung bzw. gestrickt aus den auf den entsprechenden Weg hergestellten aktivierten Kohlenstoffasern. c) Auf die atmungsaktive Membranschicht gemäß a) können anstatt der Kohlenstoffkügelchen oder zusätzlich zu diesen durch herkömmliche Beflockungstechniken auch aktivierte Kohlenstofflockfasern aufgebracht werden. d) Die Kohlenstoffkügelchen und/oder -fasern werden auf einen nahtlosen oder vernähten Innenhandschuh gemäß 2.) aufgebracht. e) Über die Funktionsschichten gemäß b) oder d) kann ein nahtloser oder verschweißter Membranhandschuh (z. B. lose oder verklebend) als Flüssigkeitsspene gelegt werden.

According to a typical embodiment, a three-layer protective glove 1 according to the present invention are composed as follows:

1. The backing layer 3 ("Outer glove") can consist, for example, of a robust and possibly flame-retardant type of fiber, preferably in a seamless circular knitted form.
2. The cover layer 9 ("Inner glove") can consist of materials that are comfortable to wear on the skin (Co, Rayon, PA, PES, m-aramid), optionally in a flame-resistant version, preferably in a seamless, circular-knitted version.
3. The barrier layer 4 ("Functional layer"), which is arranged between the inner and outer gloves, can be next to the membrane 6 activated carbon balls and / or fibers to form the adsorption layer 5 Contained for the purpose of adsorbing the pollutants, in different alternative configurations, as described below: a) On a breathable membrane layer 6 (e.g. made of PU, PES, PA, PTFE, cellulose etc.) activated carbon balls are applied. The layer can be produced and the beads applied by dipping or by customary coating and coating processes. If a coated film is produced as an intermediate step, it is brought into a two-dimensional or three-dimensional hand shape by suitable methods (e.g. gluing, sewing, welding, etc.). The functional layer can be reinforced in the coating or also on the side opposite the activated carbon beads by means of a mesh or knitted fabric made of thermoplastic fibers. b) The functional layer consists of a glove-shaped knitted fabric made of activated carbon fibers, produced by carbonizing a corresponding glove made of rayon or polyacrylonitrile fibers and subsequent activation or knitted from the activated carbon fibers produced in the corresponding way. c) Instead of the carbon spheres or in addition to these, activated carbon flock fibers can also be applied to the breathable membrane layer according to a) by conventional flocking techniques. d) The carbon balls and / or fibers are applied to a seamless or sewn inner glove according to 2.). e) A seamless or welded membrane glove (e.g. loose or adhesive) can be placed over the functional layers according to b) or d) as a liquid donor.

Die einzelnen vorgenannten Schichten (Innenhandschuh, Funktionsschicht und Außenhandschuh) werden – dem Aufbau entsprechend – zusammengesteckt und am Armabschluß z. B. durch eine Naht miteinander verbunden. Zusätzlich können die Schichten bei Bedarf auch an den Oberseiten der Finger und auf dem Handrücken durch Klebstoffe (wie z. B. durch Schmelzkleber, beispielsweise mit thermischer Aktivierung des Klebers), doppelseitige Klebebandstreifen oder Klettverschlüsse oder dergleichen fixiert werden.The individual layers mentioned above (inner glove, functional layer and outer glove) become - the Structure accordingly - put together and at the arm z. B. connected by a seam. In addition, the layers can be used if necessary also on the top of the fingers and on the back of the hand Adhesives (such as by hot melt adhesive, for example with thermal Activation of the adhesive), double-sided adhesive tape strips or Velcro fasteners or the like are fixed.

Weitere Ausgestaltungen, Abwandlungen und Variationen der vorliegenden Erfindung sind für den Fachmann beim Lesen der Beschreibung ohne weiteres erkennbar und realisierbar, ohne daß er dabei den Rahmen der vorliegenden Erfindung verläßt.Further Embodiments, modifications and variations of the present invention are for the Specialist easily recognizable when reading the description and realizable without him thereby leaving the scope of the present invention.

Claims

Breathable protective glove ( 1 ) with protective function against chemical poisons, in particular chemical warfare agents, with a multilayered structure ( 2 ), having a particularly flat support layer ( 3 ) and one of the carrier layers ( 3 ) assigned barrier layer facing the hand when it is worn, preventing or at least delaying the passage of chemical poisons ( 4 ) which has an adsorption layer ( 5 ) based on a chemical adsorbing adsorbent material, in particular based on activated carbon, characterized in that - the barrier layer ( 4 ) in addition to the adsorption layer ( 5 ) an at least substantially water and air impermeable, but water vapor permeable, retarding the passage of chemical poisons or at least substantially impermeable to chemical poisons ( 6 ) and - that the membrane ( 6 ) between the carrier layer ( 3 ) and the adsorption layer ( 5 ) is arranged.

Protective glove according to claim 1, characterized in that the membrane ( 6 ) on its side facing away from the hand when worn, directly or indirectly with the backing layer ( 3 ) is connected and / or that the membrane ( 6 ) on the carrier layer facing the hand when it is worn ( 3 ) opposite side with the adsorption layer ( 5 ) is acted upon, in particular with the adsorption layer ( 5 ) with adhesive ( 7 ) to the membrane ( 6 ) can be attached.

Protective glove according to one or more of the preceding claims, characterized in that between the membrane ( 6 ) and the carrier layer ( 3 ) an additional, preferably flat support layer ( 8th ) is arranged, in particular with the additional carrier layer ( 8th ) to stabilize and / or support the membrane ( 6 ) serves and / or in particular where the additional carrier layer ( 8th ) is designed as a preferably air-permeable textile material, in particular a textile fabric, such as a woven fabric, knitted fabric, knitted fabric, scrim or textile composite, and / or in particular wherein the additional carrier layer ( 8th ) a lower basis weight than the carrier layer ( 3 ) and / or in particular wherein the additional carrier layer ( 8th ) has a basis weight of less than 60 g / m ² , in particular less than 50 g / m ² , preferably less than 40 g / m ² , and / or in particular wherein the membrane ( 6 ) on the additional carrier layer ( 8th ) is laminated on or laminated on, in particular by means of an adhesive preferably applied in a punctiform manner, and / or in particular wherein the additional carrier layer ( 8th ) with the carrier layer ( 3 ) is connected, in particular by means of an adhesive which is preferably applied in a punctiform manner.

Protective glove according to one or more of the preceding claims, characterized in that on the membrane ( 6 ) opposite side of the adsorption layer ( 5 ) a cover layer ( 9 ) is applied, in particular with the cover layer ( 9 ) on the adsorption layer ( 5 ) is attached, in particular by means of an adhesive which is preferably discontinuous, preferably punctiform, on the cover layer ( 9 ) is applied, or by means of a hot-melt adhesive fabric ("hot-melt adhesive web"), and / or in particular wherein the cover layer ( 9 ) is a preferably air-permeable textile material, in particular a textile fabric, preferably a fabric, knitted fabric, knitted fabric, scrim or textile composite, such as a nonwoven, in particular a polyamide / polyester nonwoven (PA / PES nonwoven), and / or in particular with the cover layer ( 9 ) is designed to be abrasion-resistant and in particular consists of an abrasion-resistant textile material and / or in particular wherein the cover layer ( 9 ) has a weight per unit area of 5 to 150 g / m ² , in particular 10 to 125 g / m ² , preferably 40 to 100 g / m ² .

Protective glove according to one or more of the preceding claims, characterized in that the membrane ( 6 ) with the carrier layer ( 3 ) or with the additional backing layer ( 8th ) is glued, in particular where the gluing is only punctiform, in particular in the form of a punctiform grid, in particular with the adhesive only at most 30%, in particular only at most 25%, preferably only at most 20%, particularly preferably only at most 10% of those in the worn state side of the membrane facing away from the hand ran ( 6 ) covered, and / or that adsorption layer ( 5 ) using an adhesive ( 7 ) on the membrane ( 6 ) is applied, in particular where the bonding is only punctiform, in particular in the form of a punctiform grid, and / or in particular where at least 50%, in particular at least 60%, preferably at least 70%, particularly preferably at least 75%, very particularly preferably at least 80% the support layer facing the hand ( 3 ) opposite side of the membrane ( 6 ) with the adsorption material of the adsorption layer ( 5 ) is applied.

Protective glove according to one or more of the preceding claims, characterized in that the individual layers ( 3 . 4 . 5 . 6 . 8th . 9 ) of the layer structure ( 2 ) are connected to each other and / or that the individual layers ( 3 . 4 . 5 . 6 . 8th . 9 ) of the layer structure ( 2 ) form a network.

Protective glove according to one or more of the preceding claims, characterized in that the protective glove ( 1 ) is designed as a glove and / or that the protective glove ( 1 ) has the shape of a hand with five fingers.

Protective glove according to one or more of the preceding claims, characterized in that the carrier layer ( 3 ) is designed as a textile material, preferably an air-permeable textile material, in particular a flat textile structure, in particular where the textile material can be a woven, knitted fabric, knitted fabric, scrim or textile composite, in particular where the textile composite can be a nonwoven, and / or that the backing layer ( 3 ) is designed as a leather material.

Protective glove according to one or more of the preceding claims, characterized in that the carrier layer ( 3 ) is oleophobic and / or hydrophobic, in particular by means of a special impregnation, and / or that the material of the carrier layer ( 3 ) has a weight per unit area of 50 to 300 g / m ² , in particular 75 to 250 g / m ² , preferably 75 to 175 g / m ² , and / or that the backing layer ( 3 ) is designed as an air-permeable, 75 to 250 g / m ² , preferably 75 to 175 g / m ² heavy textile fabric, which can be made oleophobic and / or hydrophobic.

Protective glove according to one or more of the preceding claims, characterized in that the membrane ( 6 ) is a continuous, in particular closed or at most microporous membrane and / or that the thickness of the membrane ( 6 ) 1 to 500 μm, in particular 1 to 250 μm, preferably 1 to 100 μm, preferably 1 to 50 μm, particularly preferably from 2.5 to 30 μm, very particularly preferably from 5 to 25 μm, and / or that the membrane ( 6 ) at 25 ° C and with a thickness of 50 μm a water vapor permeability of at least 12.5 l / m ² per 24 h, in particular at least 17.5 l / m ² per 24 h, preferably at least 20 l / m ² per 24 h or more, and / or that the protective glove ( 1 ) at 25 ° C and with a thickness of the membrane ( 6 ) of 50 μm has a water vapor permeability of at least 10 l / m ² per 24 h, in particular at least 15 l / m ² per 24 h, preferably at least 20 l / m ² per 24 h.

Protective glove according to one or more of the preceding claims, characterized in that the membrane ( 6 ) a water vapor resistance R _et under stationary conditions, measured according to DIN EN 31 092: 1993 (February 1994) and international standard ISO 11 092, at 35 ° C of at most 25 (m ² • Pascal) / Watt, in particular at most 20 (m ² · pascal) / watt, preferably, not more than 13 (m ² · pascal) / watt, having a thickness of 50 microns at and / or in that the protective glove ( 1 ) a water vapor resistance R _et under stationary conditions, measured according to DIN EN 31 092: 1993 (February 1994) and international standard ISO 11 092, at 35 ° C of at most 30 (m ² · Pascal) / Watt, in particular at most 25 (m ² Pascal) / watt, preferably at most 20 (m ² Pascal) / watt, with a thickness of the membrane ( 6 ) of 50 μm.

Protective glove according to one or more of the preceding claims, characterized in that the membrane ( 6 ) is at most only slightly swellable and / or water-absorbent, in particular where the swellability and / or the water-absorbing capacity of the membrane ( 6 ) at most 35%, in particular at most 25%, preferably at most 20%, based on the weight of the membrane ( 6 ), and / or that the membrane ( 6 ) is at least essentially impermeable to liquids, in particular water, and / or aerosols or at least delays their passage.

Protective glove according to one or more of the preceding claims, characterized in that the membrane ( 6 ) has no or essentially no strongly hydrophilic groups, in particular no hydroxyl groups, and / or that the membrane ( 6 ) has weakly hydrophilic groups, especially polyether groups.

Protective glove according to one or more of the preceding claims, characterized in that the membrane ( 6 ) comprises a plastic and / or a polymer and / or consists thereof, in particular wherein the plastic and / or the polymer from the group of polyurethanes, Po lyetheramides, polyesteramides, polytetrafluoroethylenes and / or polymers based on cellulose and / or derivatives of the aforementioned compounds can be selected.

Protective glove according to one or more of the preceding claims, characterized in that the membrane ( 6 ) is obtained as a reaction product from the reaction of an isocyanate, in particular a masked or blocked isocyanate, with an isocyanate-reactive crosslinker.

Protective glove according to one or more of the preceding claims, characterized in that the membrane ( 6 ) is a polyurethane-based membrane and / or that the membrane ( 6 ) is an expanded, optionally microporous membrane based on polytetrafluoroethylene.

Protective glove according to one or more of the preceding claims, characterized in that the membrane ( 6 ) is designed as a multilayer membrane laminate and / or as a multilayer membrane composite, in particular wherein the membrane laminate and / or the membrane composite consists of at least two, preferably at least three interconnected layers or layers.

Protective glove according to claim 17, characterized in that this Membrane laminate or the membrane composite is a core layer based one cellulosic polymer and two with the core layer connected outer layers, in particular based on a polyurethane, a polyether amide and / or one Polyester amides, includes in particular wherein the core layer is based on a polymer Cellulose base as 1 to 100 μm, in particular 5 to 50 μm, preferably 10 to 20 μm thick membrane can be formed and / or in particular where the two outer layers connected to the core layer each as 1 to 100 μm, in particular 5 to 50 μm, preferably 5 to 10 μm thick membrane can be formed.

Protective glove according to claim 17, characterized in that this Membrane laminate or the membrane composite is a core layer based a polymer based on a polyurethane and two with the core layer connected outer layers based on a polyurethane.

Protective glove according to one or more of the preceding claims, characterized in that the membrane ( 6 ) consists of two interconnected, preferably sealingly interconnected, in particular glued and / or welded pieces of material, in particular where the two pieces of material each have the shape of a hand with five fingers, one of the two pieces of material covering a front of the hand (inside of the hand) and that another piece of material is intended to cover the back of a hand (back of the hand) and the two pieces of material are connected to one another only along their respective outer contours, in particular along the hand circumference, preferably connected to one another in a sealing manner, in particular glued and / or welded to one another.

Protective glove according to one or more of the preceding claims, characterized in that the membrane ( 6 ) is self-adhesive, in particular heat-tacky, and / or that the membrane ( 6 ) at the same time as an adhesive layer ( 7 ) for attaching the adsorption layer ( 5 ) serves.

Protective glove according to one or more of the preceding claims, characterized in that the adsorption layer ( 5 ) is discontinuous and / or that the adsorption layer ( 5 ) Discrete, chemical poisons adsorbing adsorption particles, in particular based on activated carbon, and / or that the adsorption material of the adsorption layer ( 5 ) is an adsorption material containing or consisting of activated carbon and / or that the adsorption material of the adsorption layer ( 5 ) is a material based on activated carbon, in particular in the form of activated carbon particles and / or activated carbon fibers.

Protective glove according to one or more of the preceding claims, characterized in that the adsorption layer ( 5 ) comprises discrete activated carbon particles, preferably in the form of granules ("granular carbon") or spherical ("spherical carbon"), in particular wherein the average diameter of the activated carbon particles is preferably <1.0 mm, in particular <0.5 mm, preferably <0.4 mm <0.35 mm, particularly preferably <0.3 mm, and / or the average diameter of the activated carbon particles is at least 0.1 mm and / or in particular wherein the activated carbon particles in an amount of 5 to 500 g / m ² , in particular 10 up to 400 g / m ² , preferably 20 to 300 g / m ² , preferably 25 to 250 g / m ² , particularly preferably 50 to 150 g / m ² , very particularly preferably 50 to 120 g / m ² , on the membrane ( 6 ) are applied and / or in particular wherein the activated carbon particles have an inner surface area (BET) of at least 800 m ² / g, in particular of at least 900 m ² / g, preferably of at least 1,000 m ² / g, preferably in the range from 800 to 1,500 m ² / g, and / or in particular wherein the activated carbon particles have a burst pressure per individual activated carbon particle, in particular activated carbon granules or spheres, of at least 5 newtons, in particular at least 10 newtons, and / or of up to 20 newtons.

Protective glove according to one or more of the preceding claims, characterized indicates that the adsorption layer ( 5 ) Activated carbon fibers, in particular in the form of an activated carbon sheet, comprises, in particular wherein the activated carbon sheet has a basis weight of 20 to 200 g / m ² , in particular 30 to 150 g / m ² , preferably 50 to 120 g / m ² , and / or in particular wherein the activated carbon sheet is an activated carbon fabric, knitted fabric, laid fabric or composite, in particular based on carbonized and activated cellulose and / or a carbonized and activated acrylonitrile.

Protective glove according to one or more of the preceding claims, characterized in that the adsorption layer ( 5 ) is also impregnated with at least one catalyst, in particular using enzymes and / or metal ions, preferably copper, silver, cadmium, platinum, palladium, zinc and / or mercury ions, and / or the amount of Catalyst 0.05 to 12% by weight, preferably 1 to 10% by weight, particularly preferably 2 to 8% by weight, based on the weight of the adsorption layer ( 5 ).

Protective glove according to one or more of the preceding claims, characterized in that the adsorption layer ( 5 ) at least 50%, in particular at least 60%, preferably at least 70%, is freely accessible to the poisons and warfare agents to be adsorbed.

Protective glove according to one or more of the preceding claims, characterized in that the protective glove ( 1 ) and / or the membrane ( 6 ) a barrier effect against chemical warfare agents, in particular bis [2-chloroethyl] sulfide (mustard gas, mustard, yellow cross), measured according to CRDEC-SP-84010, method 2.2 , of at most 4 μg / cm ² per 24 h, in particular at most 3.5 μg / cm ² per 24 h, preferably at most 3.0 μg / cm ² per 24 h, particularly preferably at most 2.5 μg / cm ² per 24 h, with a thickness of the membrane ( 6 ) of 50 μm.

Breathable protective glove ( 1 ) with protective function against chemical poisons, in particular chemical warfare agents, with a multilayered structure ( 2 ), having a particularly flat support layer ( 3 ) and one of the carrier layers ( 3 ) assigned barrier layer facing the hand when it is worn, preventing or at least delaying the passage of chemical poisons ( 4 ) which has an adsorption layer ( 5 ) based on a chemical adsorbing adsorbent material, especially based on activated carbon, and one between the carrier layer ( 3 ) and the adsorption layer ( 5 ) arranged, at least essentially water and air impermeable, but water vapor permeable, retarding the passage of chemical poisons or at least substantially impermeable to chemical poisons ( 6 ), the protective glove ( 1 ) and / or the membrane ( 6 ) a barrier effect against chemical warfare agents, in particular bis [2-chloroethyl] sulfide, of at most 4 μg / cm ² per 24 h with a thickness of the membrane ( 6 ) of 50 μm.

Breathable protective glove ( 1 ) with protective function against chemical poisons, in particular chemical warfare agents, with a multilayered structure ( 2 ), having a particularly flat support layer ( 3 ) and one of the carrier layers ( 3 ) assigned barrier layer facing the hand when it is worn, preventing or at least delaying the passage of chemical poisons ( 4 ) which has an adsorption layer ( 5 ) based on a chemical adsorbing adsorbent material, especially based on activated carbon, and one between the carrier layer ( 3 ) and the adsorption layer ( 5 ) arranged, at least essentially water and air impermeable, but water vapor permeable, retarding the passage of chemical poisons or at least substantially impermeable to chemical poisons ( 6 ), the protective glove ( 1 ) at 25 ° C and with a thickness of the membrane ( 6 ) of 50 μm has a water vapor permeability of at least 10 l / m ² per 24 h.

Breathable protective glove ( 1 ) with protective function against chemical poisons, in particular chemical warfare agents, with a multilayered structure ( 2 ), having a particularly flat support layer ( 3 ) and one of the carrier layers ( 3 ) assigned barrier layer facing the hand when it is worn, preventing or at least delaying the passage of chemical poisons ( 4 ) which has an adsorption layer ( 5 ) based on a chemical adsorbing adsorbent material, especially based on activated carbon, and one between the carrier layer ( 3 ) and the adsorption layer ( 5 ) arranged, at least essentially water and air impermeable, but water vapor permeable, retarding the passage of chemical poisons or at least substantially impermeable to chemical poisons ( 6 ), the protective glove ( 1 ) a water vapor resistance R _et under stationary conditions at 35 ° C of at most 30 (m ² · Pascal) / watt with a thickness of the membrane ( 6 ) of 50 μm.