WO2025101449A1 - Séparation d'anneau à bride et à fond conçu de contenants en verre renforcé par l'intermédiaire d'éléments géométriques - Google Patents

Séparation d'anneau à bride et à fond conçu de contenants en verre renforcé par l'intermédiaire d'éléments géométriques Download PDF

Info

Publication number
WO2025101449A1
WO2025101449A1 PCT/US2024/054369 US2024054369W WO2025101449A1 WO 2025101449 A1 WO2025101449 A1 WO 2025101449A1 US 2024054369 W US2024054369 W US 2024054369W WO 2025101449 A1 WO2025101449 A1 WO 2025101449A1
Authority
WO
WIPO (PCT)
Prior art keywords
glass container
thickness
strengthened glass
equal
ratio
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
PCT/US2024/054369
Other languages
English (en)
Inventor
William John Furnas
Konstantin Sergeevich Koreshkov
Jamie Lynne MORLEY
Ross Johnson STEWART
Vijay Subramanian
Jamie Todd Westbrook
David Inscho Wilcox
Jiahau YAN
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Corning Inc
Original Assignee
Corning Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Corning Inc filed Critical Corning Inc
Publication of WO2025101449A1 publication Critical patent/WO2025101449A1/fr
Pending legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

Un contenant en verre renforcé comprend : une partie corps cylindrique présentant une première extrémité et une seconde extrémité, la partie corps cylindrique comprenant un diamètre extérieur (D) et une paroi latérale présentant une épaisseur de paroi latérale (h) ; un talon incurvé s'étendant radialement vers l'intérieur à partir de la première extrémité de la partie corps cylindrique ; et un fond s'étendant à partir du talon incurvé et fermant la partie corps cylindrique au niveau de la première extrémité de la partie corps cylindrique, le fond présentant une épaisseur de fond de pic (hb,peak). Un rapport entre l'épaisseur de fond de pic (hb,peak) et l'épaisseur de paroi latérale (h) est supérieur ou égal à 1,3.
PCT/US2024/054369 2023-11-09 2024-11-04 Séparation d'anneau à bride et à fond conçu de contenants en verre renforcé par l'intermédiaire d'éléments géométriques Pending WO2025101449A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US202363547919P 2023-11-09 2023-11-09
US63/547,919 2023-11-09
US202363600949P 2023-11-20 2023-11-20
US63/600,949 2023-11-20

Publications (1)

Publication Number Publication Date
WO2025101449A1 true WO2025101449A1 (fr) 2025-05-15

Family

ID=93651440

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2024/054369 Pending WO2025101449A1 (fr) 2023-11-09 2024-11-04 Séparation d'anneau à bride et à fond conçu de contenants en verre renforcé par l'intermédiaire d'éléments géométriques

Country Status (1)

Country Link
WO (1) WO2025101449A1 (fr)

Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8312739B2 (en) 2008-07-29 2012-11-20 Corning Incorporated Dual stage ion exchange for chemical strengthening of glass
US8551898B2 (en) 2011-10-25 2013-10-08 Corning Incorporated Glass compositions with improved chemical and mechanical durability
US8561429B2 (en) 2008-07-11 2013-10-22 Corning Incorporated Glass with compressive surface for consumer applications
US20140120279A1 (en) * 2012-02-29 2014-05-01 Corning Incorporated Glass packaging ensuring container integrity
US8854623B2 (en) 2012-10-25 2014-10-07 Corning Incorporated Systems and methods for measuring a profile characteristic of a glass sample
US9145329B2 (en) 2011-10-25 2015-09-29 Corning Incorporated Alkaline earth alumino-silicate glass compositions with improved chemical and mechanical durability
US20210002016A1 (en) * 2019-07-04 2021-01-07 Schott Ag Vial with optimized neck for improved side compression performance
US20210395141A1 (en) 2020-06-23 2021-12-23 Corning Incorporated Frangible glass articles and methods of making the same
US20220008292A1 (en) * 2018-11-13 2022-01-13 Sio2 Medical Products, Inc. Polymer vials with substantially flat bottoms and injection stretch blow molding methods for making the same
US20220017412A1 (en) * 2020-07-20 2022-01-20 Corning Incorporated Stress features for crack redirection and protection in glass containers
US20220226191A1 (en) * 2019-05-03 2022-07-21 Janssen Biotech, Inc. Low temperature vials and vial assemblies
US20230105652A1 (en) * 2021-09-30 2023-04-06 Corning Incorporated Glass containers for storing pharmaceutical compositions
US11639310B2 (en) 2018-09-11 2023-05-02 Corning Incorporated Glass-based articles with improved fracture resistance

Patent Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8561429B2 (en) 2008-07-11 2013-10-22 Corning Incorporated Glass with compressive surface for consumer applications
US8312739B2 (en) 2008-07-29 2012-11-20 Corning Incorporated Dual stage ion exchange for chemical strengthening of glass
US8551898B2 (en) 2011-10-25 2013-10-08 Corning Incorporated Glass compositions with improved chemical and mechanical durability
US9145329B2 (en) 2011-10-25 2015-09-29 Corning Incorporated Alkaline earth alumino-silicate glass compositions with improved chemical and mechanical durability
US20140120279A1 (en) * 2012-02-29 2014-05-01 Corning Incorporated Glass packaging ensuring container integrity
US8854623B2 (en) 2012-10-25 2014-10-07 Corning Incorporated Systems and methods for measuring a profile characteristic of a glass sample
US11639310B2 (en) 2018-09-11 2023-05-02 Corning Incorporated Glass-based articles with improved fracture resistance
US20220008292A1 (en) * 2018-11-13 2022-01-13 Sio2 Medical Products, Inc. Polymer vials with substantially flat bottoms and injection stretch blow molding methods for making the same
US20220226191A1 (en) * 2019-05-03 2022-07-21 Janssen Biotech, Inc. Low temperature vials and vial assemblies
US20210002016A1 (en) * 2019-07-04 2021-01-07 Schott Ag Vial with optimized neck for improved side compression performance
US20210395141A1 (en) 2020-06-23 2021-12-23 Corning Incorporated Frangible glass articles and methods of making the same
US20220017412A1 (en) * 2020-07-20 2022-01-20 Corning Incorporated Stress features for crack redirection and protection in glass containers
US20230105652A1 (en) * 2021-09-30 2023-04-06 Corning Incorporated Glass containers for storing pharmaceutical compositions

Similar Documents

Publication Publication Date Title
AU2018222898B2 (en) Glass packaging ensuring container integrity
Varshneya Stronger glass products: lessons learned and yet to be learned
US11034134B2 (en) Laminated glass article with determined modulus contrast and method for forming the same
US9919949B2 (en) Strengthened glass, strengthened glass plate, strengthened glass container, and glass for strengthening
US12064395B2 (en) Glass packaging ensuring container integrity
US11168019B2 (en) Ion exchangeable borosilicate glass compositions and glass articles formed from the same
US20200071222A1 (en) Strengthened glass articles with separation features
US20240327278A1 (en) Strengthened glass articles with reduced delayed breakage and methods of making the same
WO2025101449A1 (fr) Séparation d'anneau à bride et à fond conçu de contenants en verre renforcé par l'intermédiaire d'éléments géométriques
US20200140328A1 (en) Container of glass and method for its manufacture

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application