WO2025037342A1 - Procédé de bioraffinage en boucle fermée intégrée pour valorisation multi-produit durable avec évacuation de liquide nulle - Google Patents

Procédé de bioraffinage en boucle fermée intégrée pour valorisation multi-produit durable avec évacuation de liquide nulle Download PDF

Info

Publication number
WO2025037342A1
WO2025037342A1 PCT/IN2024/051492 IN2024051492W WO2025037342A1 WO 2025037342 A1 WO2025037342 A1 WO 2025037342A1 IN 2024051492 W IN2024051492 W IN 2024051492W WO 2025037342 A1 WO2025037342 A1 WO 2025037342A1
Authority
WO
WIPO (PCT)
Prior art keywords
cellulose
biomass
suspension
temperature
produce
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
PCT/IN2024/051492
Other languages
English (en)
Inventor
Srinivasulu Reddy Venkata Mohan
Ranaprathap KATAKOJWALA
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Council of Scientific and Industrial Research CSIR
Original Assignee
Council of Scientific and Industrial Research CSIR
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Council of Scientific and Industrial Research CSIR filed Critical Council of Scientific and Industrial Research CSIR
Publication of WO2025037342A1 publication Critical patent/WO2025037342A1/fr
Pending legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

L'invention concerne un procédé de bioraffinage rentable qui a été développé pour produire de multiples produits, notamment un sirop de mono-saccharomate, un précurseur polyphénolique et des dérivés cellulosiques tels que (R)-cellulose, (µ)-cellulose et (n)-cellulose, à partir de résidus de culture excédentaires. Ce procédé comprend plusieurs étapes, y compris une récupération de saccharomate, une séparation solide-liquide, une extraction de poly-phénol, un blanchiment, une séparation par densité, une dépolymérisation et un séchage. En outre, les sous-produits produits à chaque étape du procédé de bioraffinage peuvent être utilisés pour augmenter la valeur du procédé global par incorporation d'une stratégie de récupération de ressources photosynthétiques. Les procédés utilisés pour l'extraction et le traitement varient en fonction de la composition et du type de matière première de biomasse.
PCT/IN2024/051492 2023-08-16 2024-08-13 Procédé de bioraffinage en boucle fermée intégrée pour valorisation multi-produit durable avec évacuation de liquide nulle Pending WO2025037342A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
IN202311050246 2023-08-16
IN202311050246 2023-08-16

Publications (1)

Publication Number Publication Date
WO2025037342A1 true WO2025037342A1 (fr) 2025-02-20

Family

ID=94632787

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IN2024/051492 Pending WO2025037342A1 (fr) 2023-08-16 2024-08-13 Procédé de bioraffinage en boucle fermée intégrée pour valorisation multi-produit durable avec évacuation de liquide nulle

Country Status (1)

Country Link
WO (1) WO2025037342A1 (fr)

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2336196A1 (fr) * 2009-12-17 2011-06-22 Shell Internationale Research Maatschappij B.V. Traitement d' aliments lignocellulosiques
WO2015009986A2 (fr) * 2013-07-19 2015-01-22 Washington State University Prétraitement par écoulement continu hydrothermique de biomasse lignocellulosique pour maximiser les rendements de sucre fermentescible et de lignine
BR102019026904A2 (pt) * 2019-12-17 2021-06-29 Indian Oil Corporation Limited Processo para recuperação de açúcar superior a partir da biomassa

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2336196A1 (fr) * 2009-12-17 2011-06-22 Shell Internationale Research Maatschappij B.V. Traitement d' aliments lignocellulosiques
WO2015009986A2 (fr) * 2013-07-19 2015-01-22 Washington State University Prétraitement par écoulement continu hydrothermique de biomasse lignocellulosique pour maximiser les rendements de sucre fermentescible et de lignine
BR102019026904A2 (pt) * 2019-12-17 2021-06-29 Indian Oil Corporation Limited Processo para recuperação de açúcar superior a partir da biomassa

Similar Documents

Publication Publication Date Title
Katakojwala et al. Multi-product biorefinery with sugarcane bagasse: Process development for nanocellulose, lignin and biohydrogen production and lifecycle analysis
AU2009223302B2 (en) Method and apparatus for lignocellulose pretreatment using a super-cellulose-solvent and highly volatile solvents
US9487549B2 (en) Preparation of lignin
JP5301237B2 (ja) 可溶化リグニン、糖類原料および単糖類原料の製造方法
CN101821320B (zh) 一种分级分离甘蔗渣成为高α-纤维素纸浆、木聚糖和木素的方法
CN102272318B (zh) 制造糖类的方法及乙醇制造方法
Bello et al. Optimization of lignin extraction from alkaline treated mango seed husk by high shear homogenization-assisted organosolv process using response surface methodology
US20160362353A1 (en) Integrated process for producing cellulosic pulp and polyols stream
Toma et al. Comparison between lignin extraction by alkaline and ultrasound-assisted alkaline treatment from oil palm empty fruit bunch
Meraj et al. Effect of natural deep eutectic solvents on properties of micro crystalline cellulose isolated from kenaf fibre
JP5720131B2 (ja) リグニンの製造方法及びその組成物
Jiang et al. Ethylene glycol inhibited oxalic acid non-derivatization pretreatment for enhanced wheat straw rapid saccharification and with high efficiency
Zhang et al. Sustainable production of fermentable sugars and antioxidant lignin from industrial xylose residue with facile deep eutectic solvents
WO2025037342A1 (fr) Procédé de bioraffinage en boucle fermée intégrée pour valorisation multi-produit durable avec évacuation de liquide nulle
Li et al. Organosolv fractionation of waste biomass for lignin production enhanced by oxygen
KR102847678B1 (ko) 바이오매스로부터 미세결정질 셀룰로오스(mcc)를 생산하기 위한 방법
Alam et al. Microwave-Assisted Extraction of Cellulose from Waste Olive Wood Powder Using Deep Eutectic Solvents
Manokhoon et al. EFFECTS OF COMBINED CHEMICAL AND HYDROTHERMAL PRETREATMENT ON PAPYRUS CELLULOSE STRUCTURE
WO2025030240A1 (fr) Utilisation d'un acide modifié dans une délignification de biomasse à double usage
FI127296B (en) Method for processing and fractionating biomass

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 24854019

Country of ref document: EP

Kind code of ref document: A1