WO2025091190A1 - Procédé de préparation de biocharbon par régulation de biomasse à l'aide de cycles de congélation-décongélation, et utilisation - Google Patents

Procédé de préparation de biocharbon par régulation de biomasse à l'aide de cycles de congélation-décongélation, et utilisation Download PDF

Info

Publication number
WO2025091190A1
WO2025091190A1 PCT/CN2023/128069 CN2023128069W WO2025091190A1 WO 2025091190 A1 WO2025091190 A1 WO 2025091190A1 CN 2023128069 W CN2023128069 W CN 2023128069W WO 2025091190 A1 WO2025091190 A1 WO 2025091190A1
Authority
WO
WIPO (PCT)
Prior art keywords
biochar
freeze
biomass
thaw cycles
thaw
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
PCT/CN2023/128069
Other languages
English (en)
Chinese (zh)
Inventor
孟凡彬
赵梓任
李飞跃
李孝良
谢越
汪建飞
涂德宝
李忠
吴文革
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Academy Of Agricultural Sciences Rice Institute
Anhui University of Science and Technology
Original Assignee
Anhui Academy Of Agricultural Sciences Rice Institute
Anhui University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Academy Of Agricultural Sciences Rice Institute, Anhui University of Science and Technology filed Critical Anhui Academy Of Agricultural Sciences Rice Institute
Priority to PCT/CN2023/128069 priority Critical patent/WO2025091190A1/fr
Publication of WO2025091190A1 publication Critical patent/WO2025091190A1/fr
Pending legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

L'invention concerne un procédé de préparation de biocharbon par régulation de biomasse à l'aide de cycles de congélation-décongélation, et une utilisation. Le procédé comprend les étapes suivantes consistant à : S1. broyer la biomasse, puis tamiser et sécher la biomasse broyée, ajouter de l'eau, agiter uniformément, puis tremper le mélange, effectuer un traitement par cycles de congélation-décongélation de -80 °C à -10 °C, et sécher pour obtenir un précurseur ; et S2. placer le précurseur dans un récipient pour pyrolyse à 300-700 °C, et après achèvement de la pyrolyse, refroidir le produit de pyrolyse à température ambiante, et effectuer un broyage et un tamisage pour obtenir le biocharbon. Les simples cycles de congélation-décongélation sont utilisés pour prétraiter la biomasse afin de réguler la structure des pores du biocharbon. Le prétraitement par cycles de congélation-décongélation ne nécessite que de l'eau en tant que milieu, présente les avantages d'un procédé simple, d'un faible coût, d'absence de pollution, d'une production en masse facile, etc., et est un procédé potentiel de régulation précise des micropores dans le charbon actif.
PCT/CN2023/128069 2023-10-31 2023-10-31 Procédé de préparation de biocharbon par régulation de biomasse à l'aide de cycles de congélation-décongélation, et utilisation Pending WO2025091190A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/CN2023/128069 WO2025091190A1 (fr) 2023-10-31 2023-10-31 Procédé de préparation de biocharbon par régulation de biomasse à l'aide de cycles de congélation-décongélation, et utilisation

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/CN2023/128069 WO2025091190A1 (fr) 2023-10-31 2023-10-31 Procédé de préparation de biocharbon par régulation de biomasse à l'aide de cycles de congélation-décongélation, et utilisation

Publications (1)

Publication Number Publication Date
WO2025091190A1 true WO2025091190A1 (fr) 2025-05-08

Family

ID=95583222

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2023/128069 Pending WO2025091190A1 (fr) 2023-10-31 2023-10-31 Procédé de préparation de biocharbon par régulation de biomasse à l'aide de cycles de congélation-décongélation, et utilisation

Country Status (1)

Country Link
WO (1) WO2025091190A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017208250A1 (fr) * 2016-06-01 2017-12-07 Council Of Scientific And Industrial Research Procédé de production de biocharbon enrichi en potasse à partir de biomasse résiduaire
CN112139234A (zh) * 2020-09-16 2020-12-29 东北大学 一种在土壤冻融过程中抑制重金属解吸的方法
CN113118200A (zh) * 2021-03-26 2021-07-16 中国科学院沈阳应用生态研究所 一种在土壤冻融过程中降低镉生物有效性的方法
WO2023111135A1 (fr) * 2021-12-17 2023-06-22 Plastic Energy Limited Procédé de production de béton
CN116371358A (zh) * 2023-03-06 2023-07-04 昆明理工大学 一种利用冻融循环老化增强对镉离子吸附能力的磁性生物炭及其制备方法与应用

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017208250A1 (fr) * 2016-06-01 2017-12-07 Council Of Scientific And Industrial Research Procédé de production de biocharbon enrichi en potasse à partir de biomasse résiduaire
CN112139234A (zh) * 2020-09-16 2020-12-29 东北大学 一种在土壤冻融过程中抑制重金属解吸的方法
CN113118200A (zh) * 2021-03-26 2021-07-16 中国科学院沈阳应用生态研究所 一种在土壤冻融过程中降低镉生物有效性的方法
WO2023111135A1 (fr) * 2021-12-17 2023-06-22 Plastic Energy Limited Procédé de production de béton
CN116371358A (zh) * 2023-03-06 2023-07-04 昆明理工大学 一种利用冻融循环老化增强对镉离子吸附能力的磁性生物炭及其制备方法与应用

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
YANG, XUECHEN ET AL.: "Effect of Freeze-thaw Cycles and Biochar Coupling on the Soil Water-soil Environment, Nitrogen Adsorption and N2O Emissions in Seasonally Frozen Regions", SCIENCE OF THE TOTAL ENVIRONMENT, vol. 893, 15 June 2023 (2023-06-15), XP087347653, ISSN: 0048-9697, DOI: 10.1016/j.scitotenv.2023.164845 *

Similar Documents

Publication Publication Date Title
Hu et al. Structural changes and electrochemical properties of lacquer wood activated carbon prepared by phosphoric acid-chemical activation for supercapacitor applications
Yagmur et al. A novel method for production of activated carbon from waste tea by chemical activation with microwave energy
Tan et al. Structure-dependent electrode properties of hollow carbon micro-fibers derived from Platanus fruit and willow catkins for high-performance supercapacitors
Khadiran et al. Textural and chemical properties of activated carbon prepared from tropical peat soil by chemical activation method
WO2023024365A1 (fr) Procédé de préparation de charbon actif en utilisant de la noix d'arec et une boue comme matériaux
Ao et al. Characterization and analysis of activated carbons prepared from furfural residues by microwave-assisted pyrolysis and activation
Kunusa et al. FTIR, SEM and XRD analysis of activated carbon from sago wastes using acid modification
Jiang et al. Synthesis of biomass-based porous graphitic carbon combining chemical treatment and hydrothermal carbonization as promising electrode materials for supercapacitors
CN111115629A (zh) 一种基于废弃烟杆的高比表面积碳材料及其制备方法与应用
TWI700249B (zh) 活性碳及其製造方法
CN108128773B (zh) 一种利用花生壳制备电化学电容器用电极碳材料的方法
CN118206115B (zh) 一种高性能沥青基多孔碳材料及其制备方法
Li et al. Porous carbons from Sargassum muticum prepared by H3PO4 and KOH activation for supercapacitors
CN112225216A (zh) 一种中-微孔木质素基活性炭及其制备方法
Sahu et al. Economical way of processing activated carbon from Calotropis gigantea and its suitability for application in Lithium/Sodium ion batteries
Gao et al. Bio-based sunflower carbon/polyethylene glycol shape-stabilized phase change materials for thermal energy storage
Lin et al. Structure regulation and application of bagasse-based porous carbon material based on H2O2-assisted hydrothermal treatment
CN113648966A (zh) 一种生物质多孔碳材料及其制备方法和应用
WO2025091190A1 (fr) Procédé de préparation de biocharbon par régulation de biomasse à l'aide de cycles de congélation-décongélation, et utilisation
CN111591987A (zh) 一种利用青稞秸秆制备的活性炭及其制备方法
CN117165317A (zh) 一种利用冻融循环调控生物质制备生物炭的方法和应用
Yan et al. Effects of dry and wet torrefaction pretreatment on the physicochemical structure of corn stover-derived porous carbon and its performance in supercapacitor applications
WO2024239580A1 (fr) Biocharbon mésoporeux, sa méthode de préparation et son utilisation
He et al. Preparation of High-performance Activated Carbons from Hemicellulose Pre-extracted Residues of Poplar and their Application in VOCs Removal.
Zhang et al. Preparation and Characterization of Cellulose-based Activated Carbon by Cesium Chloride Chemical Method.

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 23957070

Country of ref document: EP

Kind code of ref document: A1