WO2024203847A1 - Matériau d'isolation thermique pour chambre de combustion, chauffe-eau et chaudière - Google Patents

Matériau d'isolation thermique pour chambre de combustion, chauffe-eau et chaudière Download PDF

Info

Publication number
WO2024203847A1
WO2024203847A1 PCT/JP2024/011292 JP2024011292W WO2024203847A1 WO 2024203847 A1 WO2024203847 A1 WO 2024203847A1 JP 2024011292 W JP2024011292 W JP 2024011292W WO 2024203847 A1 WO2024203847 A1 WO 2024203847A1
Authority
WO
WIPO (PCT)
Prior art keywords
combustion chamber
main surface
bulk density
surface portion
plate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
PCT/JP2024/011292
Other languages
English (en)
Japanese (ja)
Inventor
隆彦 岡部
寛明 竹内
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ibiden Co Ltd
Original Assignee
Ibiden Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ibiden Co Ltd filed Critical Ibiden Co Ltd
Publication of WO2024203847A1 publication Critical patent/WO2024203847A1/fr
Anticipated expiration legal-status Critical
Pending legal-status Critical Current

Abstract

Ce matériau d'isolation thermique pour une chambre de combustion est une pièce moulée en forme de plaque comprenant des fibres inorganiques, le matériau d'isolation thermique étant caractérisé en ce que, lorsque les densités apparentes d'une première partie de surface principale, d'une seconde partie de surface principale et d'une partie centrale entre la première partie de surface principale et la seconde partie de surface principale dans la direction de l'épaisseur sont comparées, au moins la densité apparente de la première partie de surface principale est inférieure à la densité apparente de la partie centrale, et la première partie de surface principale est disposée vers la surface de paroi interne de la chambre de combustion.
PCT/JP2024/011292 2023-03-31 2024-03-22 Matériau d'isolation thermique pour chambre de combustion, chauffe-eau et chaudière Pending WO2024203847A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2023-058375 2023-03-31
JP2023058375A JP2024145841A (ja) 2023-03-31 2023-03-31 燃焼室用断熱材、給湯器及びボイラー

Publications (1)

Publication Number Publication Date
WO2024203847A1 true WO2024203847A1 (fr) 2024-10-03

Family

ID=92906366

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2024/011292 Pending WO2024203847A1 (fr) 2023-03-31 2024-03-22 Matériau d'isolation thermique pour chambre de combustion, chauffe-eau et chaudière

Country Status (2)

Country Link
JP (1) JP2024145841A (fr)
WO (1) WO2024203847A1 (fr)

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5986853A (ja) * 1982-11-09 1984-05-19 Matsushita Electric Ind Co Ltd 温水ボイラ
JPS6458987A (en) * 1987-08-31 1989-03-06 Sumitomo Electric Industries Heat-insulating method of high temperature furnace
JPH02227244A (ja) * 1989-03-01 1990-09-10 Osaka Gas Co Ltd 成形断熱材
JPH05318639A (ja) * 1992-05-25 1993-12-03 Nippon Steel Chem Co Ltd 断熱吸音材
JPH11302954A (ja) * 1998-04-20 1999-11-02 Toshiba Monofrax Co Ltd ３層構造の無機繊維成形品
JP2001072477A (ja) * 1999-09-01 2001-03-21 Toshiba Monofrax Co Ltd 密度差を有する無機繊維製品と炉
JP2002309470A (ja) * 2001-04-17 2002-10-23 Toshiba Monofrax Co Ltd 密度差のあるアルミナ繊維ブロック及びその製造方法
KR20120056545A (ko) * 2010-11-25 2012-06-04 주식회사 경동나비엔 급기공기를 이용한 연소실 냉각구조
WO2013035645A1 (fr) * 2011-09-07 2013-03-14 三菱樹脂株式会社 Objet moulé à base de fibres inorganiques et son procédé de fabrication
JP2017166610A (ja) * 2016-03-17 2017-09-21 イビデン株式会社 断熱保温部材

Patent Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5986853A (ja) * 1982-11-09 1984-05-19 Matsushita Electric Ind Co Ltd 温水ボイラ
JPS6458987A (en) * 1987-08-31 1989-03-06 Sumitomo Electric Industries Heat-insulating method of high temperature furnace
JPH02227244A (ja) * 1989-03-01 1990-09-10 Osaka Gas Co Ltd 成形断熱材
JPH05318639A (ja) * 1992-05-25 1993-12-03 Nippon Steel Chem Co Ltd 断熱吸音材
JPH11302954A (ja) * 1998-04-20 1999-11-02 Toshiba Monofrax Co Ltd ３層構造の無機繊維成形品
JP2001072477A (ja) * 1999-09-01 2001-03-21 Toshiba Monofrax Co Ltd 密度差を有する無機繊維製品と炉
JP2002309470A (ja) * 2001-04-17 2002-10-23 Toshiba Monofrax Co Ltd 密度差のあるアルミナ繊維ブロック及びその製造方法
KR20120056545A (ko) * 2010-11-25 2012-06-04 주식회사 경동나비엔 급기공기를 이용한 연소실 냉각구조
WO2013035645A1 (fr) * 2011-09-07 2013-03-14 三菱樹脂株式会社 Objet moulé à base de fibres inorganiques et son procédé de fabrication
JP2017166610A (ja) * 2016-03-17 2017-09-21 イビデン株式会社 断熱保温部材

Also Published As

Publication number Publication date
JP2024145841A (ja) 2024-10-15

Similar Documents

Publication Publication Date Title
US20230151963A1 (en) Plate-shaped heat insulator, combustion chamber, boiler and water heater
EP2350517B1 (fr) Produit isolant composite flexible
CN102584314B (zh) 高导热耐高温瓦楞状陶瓷基换热器芯体制备方法
CN107954742A (zh) 微孔轻质耐火砖及其制备方法
WO2024203847A1 (fr) Matériau d'isolation thermique pour chambre de combustion, chauffe-eau et chaudière
JP7243228B2 (ja) 無機繊維シート及び無機繊維シートの製造方法
JP2022091057A (ja) シート状耐熱材の製造方法および積層体
CN107954740A (zh) 耐腐蚀微孔高铝矾土轻质耐火砖及其制备方法
JP2025057963A (ja) 燃焼室用断熱材、給湯器及びボイラー
JP2025009415A (ja) 燃焼室用断熱材、給湯器及びボイラー
US20230151962A1 (en) Plate-shaped heat insulator, combustion chamber, boiler and water heater
JP7759239B2 (ja) 燃焼室、ボイラ及び給湯器
JP2022091056A (ja) シート状耐熱材および積層体
CN110925851A (zh) 一种间歇性饱和蒸汽长输供热系统
JP6055477B2 (ja) ディスクロール及びその基材
US9051200B2 (en) Disk roll and base material thereof
JPS62299694A (ja) 直交型熱交換器用伝熱ブロツク
JP2004182528A (ja) 燃料処理装置
TW202220946A (zh) 無機質成形體
JP7724670B2 (ja) 燃焼室用断熱材、給湯器及びボイラー
JPH0133631Y2 (fr)
RU100768U1 (ru) Изделие из теплоизолирующего материала (варианты)
JP2024136844A (ja) 燃焼室用断熱材、給湯器及びボイラー
CN206094127U (zh) 一种用于cfb烟气发生设备的出口烟道或分离器顶部与侧墙角接处结构
WO2025204998A1 (fr) Matériau d'isolation thermique pour bloc-batterie, et bloc-batterie

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 24779965

Country of ref document: EP

Kind code of ref document: A1