WO2024088848A1 - Formulation destinée à un système d'isolation, son utilisation et corps moulé - Google Patents

Formulation destinée à un système d'isolation, son utilisation et corps moulé Download PDF

Info

Publication number
WO2024088848A1
WO2024088848A1 PCT/EP2023/078988 EP2023078988W WO2024088848A1 WO 2024088848 A1 WO2024088848 A1 WO 2024088848A1 EP 2023078988 W EP2023078988 W EP 2023078988W WO 2024088848 A1 WO2024088848 A1 WO 2024088848A1
Authority
WO
WIPO (PCT)
Prior art keywords
component
formulation according
formulation
insulation
pfts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP2023/078988
Other languages
German (de)
English (en)
Inventor
Steffen Lang
Marek Maleika
Niels Müller
Florian Schemmel
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Siemens AG
Siemens Mobility GmbH
Siemens Corp
Original Assignee
Siemens AG
Siemens Mobility GmbH
Siemens Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from EP22206022.0A external-priority patent/EP4362048A1/fr
Application filed by Siemens AG, Siemens Mobility GmbH, Siemens Corp filed Critical Siemens AG
Priority to EP23797684.0A priority Critical patent/EP4588077A1/fr
Priority to CN202380075059.4A priority patent/CN120113015A/zh
Publication of WO2024088848A1 publication Critical patent/WO2024088848A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention se rapporte de manière générale au domaine de l'isolation, plus particulièrement à une formulation destinée à une isolation haute température à des températures de fonctionnement de 200 °C et plus. L'isolation est utilisée pour isoler des conducteurs électriques. L'invention se rapporte ainsi à un système d'isolation d'une machine électrique, plus particulièrement d'une machine électrique tournante comportant un stator, tel qu'un moteur électrique et/ou un générateur présentant une résistance à la température améliorée des composants de système d'isolation polymères et/ou un revêtement isolant pour des conducteurs fabriqués de manière générative ou des parties de ces derniers, des barres omnibus, des barres de connexion et/ou des boîtes à bornes. La présente invention divulgue pour la première fois un composé, un revêtement en poudre et/ou une formulation destinée à un revêtement humide, qui comprend des thermoplastiques à haute performance en tant que charges, pour lesquels il a été démontré que lesdites charges peuvent augmenter considérablement la résistance thermique et fournir même de meilleures propriétés thermomécaniques dans un système d'isolation produit à partir de ces dernières.
PCT/EP2023/078988 2022-10-24 2023-10-18 Formulation destinée à un système d'isolation, son utilisation et corps moulé Ceased WO2024088848A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
EP23797684.0A EP4588077A1 (fr) 2022-10-24 2023-10-18 Formulation destinée à un système d'isolation, son utilisation et corps moulé
CN202380075059.4A CN120113015A (zh) 2022-10-24 2023-10-18 用于绝缘系统的制剂、其用途和模制体

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
EP22203336.7 2022-10-24
EP22203336 2022-10-24
EP22206022.0A EP4362048A1 (fr) 2022-10-24 2022-11-08 Formulation pour un système d'isolation, son utilisation et corps moulé
EP22206022.0 2022-11-08

Publications (1)

Publication Number Publication Date
WO2024088848A1 true WO2024088848A1 (fr) 2024-05-02

Family

ID=88585016

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2023/078988 Ceased WO2024088848A1 (fr) 2022-10-24 2023-10-18 Formulation destinée à un système d'isolation, son utilisation et corps moulé

Country Status (3)

Country Link
EP (1) EP4588077A1 (fr)
CN (1) CN120113015A (fr)
WO (1) WO2024088848A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2012158292A1 (fr) * 2011-05-13 2012-11-22 Dow Global Technologies Llc Formulations d'isolant
US20170335069A1 (en) * 2014-12-29 2017-11-23 Soochow University Carbon nanotube/polyetherimide/thermosetting resin dielectric composite and preparation method therefor
WO2020095268A1 (fr) * 2018-11-08 2020-05-14 Sabic Global Technologies B.V. Composition thermoplastique, fil électrique et article comprenant le fil électrique
US20200362169A1 (en) * 2018-02-01 2020-11-19 Mitsui Mining & Smelting Co., Ltd. Resin composition, copper foil with resin, dielectric layer, copper-clad laminate, capacitor element, and printed wiring board with built-in capacitor
EP4047625A1 (fr) * 2021-02-22 2022-08-24 Siemens Aktiengesellschaft Système d'isolation pour machines rotatives électriques, utilisation d'un mélange de matières et machine rotative électrique

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2012158292A1 (fr) * 2011-05-13 2012-11-22 Dow Global Technologies Llc Formulations d'isolant
US20170335069A1 (en) * 2014-12-29 2017-11-23 Soochow University Carbon nanotube/polyetherimide/thermosetting resin dielectric composite and preparation method therefor
US20200362169A1 (en) * 2018-02-01 2020-11-19 Mitsui Mining & Smelting Co., Ltd. Resin composition, copper foil with resin, dielectric layer, copper-clad laminate, capacitor element, and printed wiring board with built-in capacitor
WO2020095268A1 (fr) * 2018-11-08 2020-05-14 Sabic Global Technologies B.V. Composition thermoplastique, fil électrique et article comprenant le fil électrique
EP4047625A1 (fr) * 2021-02-22 2022-08-24 Siemens Aktiengesellschaft Système d'isolation pour machines rotatives électriques, utilisation d'un mélange de matières et machine rotative électrique

Also Published As

Publication number Publication date
CN120113015A (zh) 2025-06-06
EP4588077A1 (fr) 2025-07-23

Similar Documents

Publication Publication Date Title
EP4362048A1 (fr) Formulation pour un système d'isolation, son utilisation et corps moulé
DE69707973T2 (de) Wärmehärtbare Harzmischung, elektrisch isolierte Wicklung, elektrische rotierende Maschine und deren Herstellungsverfahren
EP1118086B1 (fr) Bande anti-effluves
WO2013041363A1 (fr) Systèmes isolants à tenue améliorée aux décharges partielles et procédé de fabrication desdits systèmes isolants
DE102011083409A1 (de) Isoliersysteme mit verbesserter Teilentladungsbeständigkeit, Verfahren zur Herstellung dazu
EP1243064B1 (fr) Procede pour realiser une isolation de haute qualite de conducteurs electriques ou de faisceaux de conducteurs de machines electriques rotatives, par revetement en lit fluidise
DE602004001781T2 (de) Elektrische leitung beschichtet mit einer haftenden schicht und herstellungsprozess davon
EP4183028A1 (fr) Formulation de revêtement en poudre pour un système d'isolation d'une machine électrique, machine électrique présentant un système d'isolation de ce type et procédé de production d'un système d'isolation de ce type
WO2022175264A1 (fr) Système d'isolation d'encoche pour machine électrique tournante, procédé de fabrication d'un système d'isolation d'encoche
WO2022175284A1 (fr) Système d'isolation pour machines électriques tournantes, utilisation d'un mélange et machine électrique tournante
EP3460959A1 (fr) Matériau électriquement isolant et/ou résine d'imprégnation pour isolation à bande enroulée d'une machine à haute et/ou à moyenne tension ainsi que système d'isolation correspondant
WO2014147072A1 (fr) Masse de scellement, utilisation de la masse de scellement et composite durci par voie thermique obtenu à partir de la masse de scellement
EP3593361B1 (fr) Bande anti-effluves pour machine électrique haute tension
EP3844218A1 (fr) Équipement électrique doté d'un système d'isolation, ainsi que procédé pour la production du système d'isolation
WO2024088848A1 (fr) Formulation destinée à un système d'isolation, son utilisation et corps moulé
EP4474435A1 (fr) Formulation de peinture, isolation de celle-ci et utilisation de celle-ci
EP4046773A1 (fr) Système d'isolation pour machines rotatives électriques, procédé de fabrication, ainsi que revêtement de peinture pulverulente
EP3363030B1 (fr) Enroulement electrique pour un transformateur de type sec et procede de fabrication d'un enroulement electrique pour un transformateur de type sec
DE102022202880A1 (de) Pulverlackformulierung zur Isolation des Wickelkopfes einer elektrischen rotierenden Maschine
WO2015090935A1 (fr) Composition de résine coulable résistant aux décharges disruptives et au contournement
WO2023170112A1 (fr) Isolation de sous-conducteur et composite de sous-conducteur d'une machine tournante électrique
EP4447283A1 (fr) Système d'isolation
WO2022096429A1 (fr) Bande de protection anti-effluves d'une machine électrique tournante à haute tension, son utilisation, et machine électrique

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 23797684

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2023797684

Country of ref document: EP

ENP Entry into the national phase

Ref document number: 2023797684

Country of ref document: EP

Effective date: 20250415

WWE Wipo information: entry into national phase

Ref document number: 202380075059.4

Country of ref document: CN

NENP Non-entry into the national phase

Ref country code: DE

WWP Wipo information: published in national office

Ref document number: 202380075059.4

Country of ref document: CN

WWP Wipo information: published in national office

Ref document number: 2023797684

Country of ref document: EP