WO2023279142A1 - Récupération de vanadium à partir de résidus de lixiviation à l'aide d'un procédé hydrométallurgique et pyrométallurgique combiné - Google Patents

Récupération de vanadium à partir de résidus de lixiviation à l'aide d'un procédé hydrométallurgique et pyrométallurgique combiné Download PDF

Info

Publication number
WO2023279142A1
WO2023279142A1 PCT/AU2022/050676 AU2022050676W WO2023279142A1 WO 2023279142 A1 WO2023279142 A1 WO 2023279142A1 AU 2022050676 W AU2022050676 W AU 2022050676W WO 2023279142 A1 WO2023279142 A1 WO 2023279142A1
Authority
WO
WIPO (PCT)
Prior art keywords
leach
vanadium
solution
residue
calcine
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/AU2022/050676
Other languages
English (en)
Inventor
David Robinson
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Avanti Materials Ltd
Original Assignee
Avanti Materials Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from AU2021902085A external-priority patent/AU2021902085A0/en
Application filed by Avanti Materials Ltd filed Critical Avanti Materials Ltd
Publication of WO2023279142A1 publication Critical patent/WO2023279142A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne un procédé de récupération de vanadium à partir d'un résidu de lixiviation contenant du vanadium, le procédé comprenant les étapes consistant à : soumettre le résidu de lixiviation à une étape de calcination pour produire un résidu calciné ; soumettre le résidu calciné à une étape de lixiviation comprenant la mise en contact du résidu calciné avec une solution de lixiviation de carbonate alcalin pour former une bouillie de lixiviation ; faire passer la bouillie de lixiviation à une étape de séparation de liquide solide pour produire une solution de lixiviation de calcinat contenant du vanadium et un résidu de lixiviation secondaire ; et la récupération d'un produit de vanadium à partir de la solution de lixiviation de calcinat.
PCT/AU2022/050676 2021-07-08 2022-06-30 Récupération de vanadium à partir de résidus de lixiviation à l'aide d'un procédé hydrométallurgique et pyrométallurgique combiné Ceased WO2023279142A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
AU2021902085A AU2021902085A0 (en) 2021-07-08 Recovery of Vanadium from Leach Residues Using Combined Hydrometallurgical and Pyrometallurgical Process
AU2021902085 2021-07-08

Publications (1)

Publication Number Publication Date
WO2023279142A1 true WO2023279142A1 (fr) 2023-01-12

Family

ID=84800112

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/AU2022/050676 Ceased WO2023279142A1 (fr) 2021-07-08 2022-06-30 Récupération de vanadium à partir de résidus de lixiviation à l'aide d'un procédé hydrométallurgique et pyrométallurgique combiné

Country Status (1)

Country Link
WO (1) WO2023279142A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN117488061A (zh) * 2023-11-27 2024-02-02 攀钢集团攀枝花钢铁研究院有限公司 一种碳酸化浸出液除铁的方法

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102560086A (zh) * 2012-03-14 2012-07-11 重庆大学 一种碳酸铵浸出钒渣熟料提钒的方法
CN104357652A (zh) * 2014-11-20 2015-02-18 重庆大学 一种高钙钒渣直接焙烧-碱浸提钒的方法
CN111321311A (zh) * 2020-04-26 2020-06-23 攀钢集团钒钛资源股份有限公司 钒渣两次转化成盐提钒的方法
CN111363926A (zh) * 2020-04-26 2020-07-03 攀钢集团钒钛资源股份有限公司 钒渣浅氧化焙烧分离钒的方法

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102560086A (zh) * 2012-03-14 2012-07-11 重庆大学 一种碳酸铵浸出钒渣熟料提钒的方法
CN104357652A (zh) * 2014-11-20 2015-02-18 重庆大学 一种高钙钒渣直接焙烧-碱浸提钒的方法
CN111321311A (zh) * 2020-04-26 2020-06-23 攀钢集团钒钛资源股份有限公司 钒渣两次转化成盐提钒的方法
CN111363926A (zh) * 2020-04-26 2020-07-03 攀钢集团钒钛资源股份有限公司 钒渣浅氧化焙烧分离钒的方法

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN117488061A (zh) * 2023-11-27 2024-02-02 攀钢集团攀枝花钢铁研究院有限公司 一种碳酸化浸出液除铁的方法

Similar Documents

Publication Publication Date Title
EP3204528B1 (fr) Procédé de récupération
US20230227940A1 (en) Recovery of vanadium from alkaline slag materials
US7666372B2 (en) Process for the treatment of electric and other furnace dusts and residues containing zinc oxides and zinc ferrites
AU2021280402B2 (en) Process for recovering titanium dioxide
CN102828025B (zh) 从石煤钒矿中提取v2o5的方法
JP2015535886A (ja) 種々の材料のＨＣｌ浸出によるアルミナおよび塩化マグネシウムを調製するためのプロセス
CN103415631A (zh) 从矿石和精矿中溶解并回收Nb或Ta中的至少一种元素以及U或稀土元素中的至少另一种元素
WO2021119728A1 (fr) Récupération de vanadium à partir de matériaux de scories
WO2009146518A1 (fr) Récupération de magnésium et de soufre dans la lixiviation de minerais de nickel latéritique
KR20210105406A (ko) 다금속 단괴로부터 금속을 회수하는 방법
CA3165363A1 (fr) Extraction de vanadium a partir de minerais disparates de schiste
AU2018247569B2 (en) A method for preparing a leach feed material
WO2020237312A1 (fr) Récupération de produits à base de titane à partir de minerais de titanomagnétite
WO2023279142A1 (fr) Récupération de vanadium à partir de résidus de lixiviation à l'aide d'un procédé hydrométallurgique et pyrométallurgique combiné
AU2016101526B4 (en) Recovery Process
RU2070596C1 (ru) Способ получения скандиевых концентратов
US20240344176A1 (en) Recovery of vanadium from leach residues
WO2023279144A1 (fr) Récupération de vanadium à partir de scories alcalines
CN116209779B (en) Method for recovering titanium dioxide
EP4481065A2 (fr) Procédé d'obtention d'un concentré de minerai de nickel, procédé de traitement d'un concentré de minerai de nickel, et procédé de récupération de matériaux dérivés de minerai de nickel
GENERAL LEACHING WITH ACIDS

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22836383

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 22836383

Country of ref document: EP

Kind code of ref document: A1