WO2023166943A1 - 樹脂組成物ならびにその用途および成形方法 - Google Patents

樹脂組成物ならびにその用途および成形方法 Download PDF

Info

Publication number
WO2023166943A1
WO2023166943A1 PCT/JP2023/004472 JP2023004472W WO2023166943A1 WO 2023166943 A1 WO2023166943 A1 WO 2023166943A1 JP 2023004472 W JP2023004472 W JP 2023004472W WO 2023166943 A1 WO2023166943 A1 WO 2023166943A1
Authority
WO
WIPO (PCT)
Prior art keywords
sugar
resin composition
ester
mass
alkanoate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2023/004472
Other languages
English (en)
French (fr)
Inventor
真之 廣田
麻美 前田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Osaka Gas Chemicals Co Ltd
Original Assignee
Osaka Gas Chemicals Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Osaka Gas Chemicals Co Ltd filed Critical Osaka Gas Chemicals Co Ltd
Priority to KR1020247025095A priority Critical patent/KR20240157642A/ko
Priority to CN202380020003.9A priority patent/CN118647665A/zh
Priority to US18/841,492 priority patent/US20250163247A1/en
Publication of WO2023166943A1 publication Critical patent/WO2023166943A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

熱可塑性樹脂および糖エステルを含み、かつ溶融成形に供するための溶融成形用樹脂組成物を調製する。前記熱可塑性樹脂は、セルロースジアセテート（Ａ）である。前記糖エステルは、単糖、オリゴ糖および糖アルコールからなる群より選択された少なくとも一種とＣ２－６アルカン酸とのエステル化物である糖アルカン酸エステル（Ｂ）を含む。前記糖アルカン酸エステル（Ｂ）はスクロースオクタアセテートであってもよい。前記糖アルカン酸エステル（Ｂ）の割合は、前記セルロースジアセテート１００質量部に対して１０～６５質量部であってもよい。前記樹脂組成物は、射出成形に供するための樹脂組成物であってもよい。前記樹脂組成物は、溶融成形性、透明性および機械的特性に優れている。

Description

樹脂組成物ならびにその用途および成形方法
　本発明は、セルロースジアセテートを含む樹脂組成物ならびにその用途および成形方法に関する。
　セルロースアセテートは、透明性、耐熱性、機械的特性に優れる樹脂であるが、成形性が低いため、溶媒に溶解させてキャストすることにより成形する溶液流延法が汎用されている。例えば、特開２０１６－１６４６６９号公報（特許文献１）には、ポリエステルオリゴマーおよび糖エステル化合物を添加剤として溶液流延法で製造されたセルロースアセテートフィルムが開示されている。
　一方、溶媒に溶解させた溶液流延法では、成形体の形状が限定されるため、溶融成形による成形方法も知られている。しかし、セルロースアセテートは、樹脂単体では溶融成形が困難であるため、溶融成形に際しては可塑剤が使用される。
　特表２００３－５２６６９４号公報（特許文献２）には、スクロースアセテートイソブチレートなどの機能性添加剤を酸と混合し、水などの水性沈殿剤と接触させて共沈させるセルロースエステルと機能性添加剤とのブレンド方法が開示されている。
　特開２０２１－１０９９４２号公報（特許文献３）には、セルロースナノファイバーを含む酢酸セルロースと、酢酸エチル、乳酸ブチル、フタル酸ジオクチル、クエン酸トリエチル、クエン酸トリブチル、リン酸トリオクチルなどの可塑剤とを押出機で混練して製造された複合材料が開示されている。
　国際公開第２００８／０６２６１０号（特許文献４）には、セルロースアセテートプロピオネートやセルロースアセテートブチレートなどのセルロースエステルと、アクリルポリマーと、グルコースペンタアセテート、スクロースオクタアセテート、スクロースオクタプロピオネート、スクロースオクタイソブチレート、スクロースオクタベンゾエート、マルトースオクタアセテートなどの糖エステル化合物とを含有する組成物を溶融流延してセルロースエステルフィルムを製造する方法が開示されている。
　国際公開第２００９／０１１２２８号（特許文献５）には、セルロースアセテートプロピオネートなどのセルロースエステルと、スクロースヘキサアセテート、スクロースヘキサプロピオネート、スクロースヘプタプロピオネート、スクロースヘキサベンゾエート、スクロースヘプタベンゾエートなどの部分エステル化糖と、グルコースペンタアセテート、グルコースペンタブチレート、スクロースオクタアセテート、スクロースオクタプロピオネート、スクロースオクタベンゾエートなどの完全エステル化糖とを含有する組成物を溶融流延してセルロースエステルフィルムを製造する方法が開示されている。
特開２０１６－１６４６６９号公報 特表２００３－５２６６９４号公報 特開２０２１－１０９９４２号公報 国際公開第２００８／０６２６１０号 国際公開第２００９／０１１２２８号
　しかし、特許文献２～５の組成物では、透明性に優れた成形体が得られるものの、溶融流動性が低い。そのため、特許文献２～５の組成物では、流動性、特に、溶融流動性が低いため、溶融成形性が低く、射出成形体などの高い溶融流動性を要求される成形に利用するのは困難であった。さらに従来の技術では、セルロースアセテートに可塑剤を配合して軟化させると、機械的特性は低下するため、流動性と機械的特性とはトレードオフの関係にあり、両立が困難な特性であった。
　従って、本発明の目的は、溶融成形性、透明性および機械的特性に優れた樹脂組成物ならびにその用途および成形方法を提供することにある。
　本発明者らは、前記課題を達成するため鋭意検討した結果、セルロースジアセテート（Ａ）を含む熱可塑性樹脂［特に、セルロースジアセテート（Ａ）からなる熱可塑性樹脂］と、特定の糖アルカン酸エステル化物（Ｂ）を含む糖エステルとを組み合わせることにより、溶融成形性、透明性および機械的特性に優れた樹脂組成物を提供できることを見出し、本発明を完成した。
　すなわち、本発明の態様［１］としての樹脂組成物は、熱可塑性樹脂および糖エステルを含み、かつ溶融成形に供するための溶融成形用樹脂組成物であって、前記熱可塑性樹脂が、セルロースジアセテート（Ａ）であり、前記糖エステルが、単糖、オリゴ糖および糖アルコールからなる群より選択された少なくとも一種とＣ２－６アルカン酸とのエステル化物である糖アルカン酸エステル（Ｂ）を含む。
　本発明の態様［２］は、前記態様［１］において、前記糖アルカン酸エステル（Ｂ）が、単糖または二糖のＣ２－４アルカン酸エステルである態様である。
　本発明の態様［３］は、前記態様［１］または［２］において、前記糖アルカン酸エステル（Ｂ）が、二糖とＣ２－３アルカン酸との完全エステル化物である態様である。
　本発明の態様［４］は、前記態様［１］～［３］のいずれかの態様において、前記糖アルカン酸エステル（Ｂ）が、スクロースオクタアセテートである態様である。
　本発明の態様［５］は、前記態様［４］において、前記スクロースオクタアセテートの割合が、前記糖エステル中９０質量％以上である態様である。
　本発明の態様［６］は、前記態様［１］～［５］のいずれかの態様において、前記糖アルカン酸エステル（Ｂ）の割合が、前記セルロースジアセテート（Ａ）１００質量部に対して１０～６５質量部である態様である。
　本発明の態様［７］は、前記態様［１］～［６］のいずれかの態様の樹脂組成物が、射出成形に供するための樹脂組成物である態様である。
　本発明の態様［８］は、前記態様［１］～［７］のいずれかの態様の樹脂組成物が、セルローストリアセテート、（メタ）アクリル系樹脂およびポリエステルオリゴマーからなる群より選択された少なくとも一種を含まない態様である。
　本発明には、態様［９］として、前記態様［１］～［８］のいずれかの態様の樹脂組成物で形成された成形体も含まれる。
　本発明の態様［１０］は、前記態様［９］の成形体が、自動車部品、電気・電子部品、建築資材、土木資材、農業資材、包装資材、生活資材および光学部材から選択される部品または資材である態様である。
　本発明には、態様［１１］として、前記態様［１］～［８］のいずれかの態様の樹脂組成物を溶融成形して成形体を製造する方法も含まれる。
　本発明の態様［１２］は、前記態様［１１］の方法において、前記樹脂組成物を射出成形して成形体を製造する態様である。
　本発明には、態様［１３］として、セルロースジアセテート（Ａ）の強度を向上させるための強度向上剤であって、単糖、オリゴ糖および糖アルコールからなる群より選択された少なくとも一種とＣ２－６アルカン酸とのエステル化物である糖アルカン酸エステル（Ｂ）で構成されている強度向上剤も含まれる。
　本発明には、態様［１４］として、セルロースジアセテート（Ａ）の溶融流動性を向上させるための流動性向上剤であって、単糖、オリゴ糖および糖アルコールからなる群より選択された少なくとも一種とＣ２－６アルカン酸とのエステル化物である糖アルカン酸エステル（Ｂ）で構成されている流動性向上剤も含まれる。
　本発明には、態様［１５］として、セルロースジアセテート（Ａ）に単糖、オリゴ糖および糖アルコールからなる群より選択された少なくとも一種とＣ２－６アルカン酸とのエステル化物である糖アルカン酸エステル（Ｂ）を配合し、前記セルロースジアセテート（Ａ）の溶融流動性および／または強度を向上する方法も含まれる。
　なお、本明細書および請求の範囲において、置換基の炭素原子の数をＣ１、Ｃ６、Ｃ１０などで示すことがある。例えば、「Ｃ１アルキル基」は炭素数が１のアルキル基を意味し、「Ｃ６－１０アリール基」は炭素数が６～１０のアリール基を意味する。
　本発明では、セルロースジアセテート（Ａ）を含む熱可塑性樹脂［特に、セルロースジアセテート（Ａ）からなる熱可塑性樹脂］と、特定の糖アルカン酸エステル（Ｂ）を含む糖エステルとを組み合わせているため、樹脂組成物の溶融成形性、透明性および機械的特性を向上できる。特に、特定の糖アルカン酸エステル（Ｂ）を所定の割合で配合することにより、射出成形に必要な溶融成形性を維持しながら、透明性、曲げ強さ、曲げ弾性率および衝撃強度を向上できる。また、糖エステルとして、特定の糖アルカン酸エステル（Ｂ）を用いると、セルロースジアセテート（Ａ）との組み合わせにおいて、高い生分解性を実現できる。
　［熱可塑性樹脂］
　本発明の樹脂組成物は、熱可塑性樹脂を含み、溶融成形に供される樹脂組成物である。さらに、前記熱可塑性樹脂は、セルロースジアセテート（またはセルロースジアセテート樹脂）（Ａ）を含むため、透明性および機械的特性に優れている。
　セルロースジアセテート（Ａ）は、汎用のセルロースジアセテートを利用できる。セルロースジアセテート（Ａ）の酢化度は５２～５９％である。酢化度は、好ましくは５３～５８％、さらに好ましくは５４～５６％、より好ましくは５４．５～５５．５％である。セルロースジアセテート（Ａ）の平均置換度（アセチル基総置換度）は２．２～２．７である。平均置換度は、好ましくは２．３～２．６、さらに好ましくは２．３～２．５である。アセチル基の置換度が小さすぎると、分子間の水素結合が強くなるため、樹脂組成物の成形性が低下する虞があり、逆に大きすぎると、融点が上昇するため成形温度が高くなり、成形の際に熱分解が起こる虞がある。
　なお、本明細書および請求の範囲において、セルロースジアセテート（Ａ）の酢化度および平均置換度は、ＡＳＴＭ－Ｄ－８１７－９１（セルロースアセテート等の試験法）に準拠して測定できる。
　セルロースジアセテート（Ａ）の６％粘度（２５℃）は、例えば３０～２００ｍＰａ・ｓ、好ましくは４０～１５０ｍＰａ・ｓ、さらに好ましくは５０～１００ｍＰａ・ｓ、より好ましくは６０～８０ｍＰａ・ｓである。６％粘度が小さすぎると、成形体の機械的特性が低下する虞があり、逆に大きすぎると、樹脂組成物の成形性が低下する虞がある。
　なお、本明細書および請求の範囲において、セルロースジアセテート（Ａ）の６％粘度は、慣用の方法、例えば、セルロースジアセテートを９５％アセトン水溶液に濃度６％（質量／体積％）で溶解させ、オストワルド粘度計を用いて流下時間を測定する方法で求めることができる。
　熱可塑性樹脂は、セルロースジアセテート（Ａ）に加えて、他の熱可塑性樹脂をさらに含んでいてもよい。
　他の熱可塑性樹脂としては、例えば、ポリオレフィン系樹脂、スチレン系樹脂、（メタ）アクリル系樹脂、塩化ビニル系樹脂、ポリビニルアルコール系樹脂、ポリアセタール系樹脂、ポリエステル系樹脂、ポリカーボネート系樹脂、ポリアミド系樹脂、ポリイミド系樹脂、ポリウレタン系樹脂、ポリスルホン系樹脂、ポリフェニレンエーテル系樹脂、ポリフェニレンスルフィド系樹脂、フッ素樹脂、セルロースジアセテート（Ａ）以外のセルロース誘導体などが挙げられる。これら他の熱可塑性樹脂は、単独でまたは二種以上組み合わせて使用できる。
　これら他の熱可塑性樹脂のうち、セルロースジアセテート（Ａ）との相溶性に優れる点から、セルロース誘導体が好ましい。
　セルロース誘導体としては、例えば、メチルセルロース、エチルセルロース、エチルメチルセルロース、プロピルセルロース、イソプロピルセルロース、ブチルセルロースなどのアルキルセルロース；ベンジルセルロースなどのアラルキルセルロース；ヒドロキシエチルセルロース、ヒドロキシプロピルセルロースなどのヒドロキシアルキルセルロース；カルボキシメチルセルロースなどのカルボキシアルキルセルロース；セルロースプロピオネート、セルロースブチレートなどのセルロースＣ３－４アシレート；セルロースアセテートプロピオネート、セルロースアセテートブチレートなどのセルロースアセテートＣ３－４アシレート；ニトロセルロース、硫酸セルロース、リン酸セルロースなどのセルロース無機酸エステルなどが挙げられる。これらのうち、セルロースジアセテートとの相溶性に優れる点から、セルロースＣ２－４アシレートやセルロースアセテートＣ３－４アシレートなどのセルロースアシレートが好ましい。
　他の熱可塑性樹脂の割合は、セルロースジアセテート（Ａ）１００質量部に対して、１００質量部以下（例えば０．１～１００質量部）であってもよく、好ましくは５０質量部以下（例えば１～５０質量部）、さらに好ましくは１０質量部以下、より好ましくは５質量部以下、最も好ましくは１質量部以下である。他の熱可塑性樹脂の割合が多すぎると、後述する糖アルカン酸エステル（Ｂ）を配合する効果が低下することなどによって成形性や機械的特性が低下する虞がある。
　熱可塑性樹脂は、セルロースジアセテート（Ａ）を主成分として含むのが好ましい。セルロースジアセテート（Ａ）の割合は、熱可塑性樹脂中５０質量％以上であってもよいが、好ましくは８０質量％以上、さらに好ましくは９０質量％以上、より好ましくは９５質量％以上、最も好ましくは９９質量％以上である。熱可塑性樹脂は、実質的にセルロースジアセテート（Ａ）のみからなってもよく、セルロースジアセテート（Ａ）のみからなるのが特に好ましい。
　熱可塑性樹脂は、セルロースジアセテート（Ａ）を主成分として含むのが好ましいため、セルロースジアセテート以外のセルロースアセテートを実質的に含まないのが好ましく、セルロースジアセテート以外のセルロースアセテートを含まないのが特に好ましい。
　熱可塑性樹脂は、（メタ）アクリル系樹脂を実質的に含まないのが好ましく、（メタ）アクリル系樹脂を含まないのが特に好ましい。
　［糖エステル］
　本発明の樹脂組成物は、セルロースジアセテート（Ａ）を含む熱可塑性樹脂に加えて、糖エステルを含む。なお、本明細書および請求の範囲において、糖エステルは、エステル化糖、糖エステル化合物とも称される化合物であり、単糖、オリゴ糖および糖アルコールからなる群より選択された少なくとも一種（低分子糖）と、カルボン酸とのエステル化物を意味する。
　前記糖エステルは、単糖、オリゴ糖および糖アルコールからなる群より選択された少なくとも一種と、Ｃ２－６アルカン酸（脂肪族モノカルボン酸）とのエステル化物である糖アルカン酸エステル（Ｂ）を含むため、樹脂組成物の溶融成形性を向上できる。従来の可塑剤では、セルロースジアセテート（Ａ）の流動性を高度に向上させるのは困難であり、例えば、射出成形に必要な溶融流動性を実現するのは困難であった。これに対して、本発明では、糖アルカン酸エステル（Ｂ）を用いることにより、射出成形に必要な溶融流動性も実現できる。さらに、糖アルカン酸エステル（Ｂ）は溶融流動性を向上できるだけでなく、従来の可塑剤の配合では流動性に対してトレードオフの関係にあった機械的特性、特に、曲げ強度、曲げ弾性率、衝撃強度（特に、強度）も向上できる。さらに、セルロースジアセテート（Ａ）と糖アルカン酸エステル（Ｂ）との組み合わせは、溶融流動性が高く、混練性に優れるため、セルロースジアセテート（Ａ）の透明性も維持でき、樹脂組成物および成形体の透明性も向上できる。
　単糖としては、例えば、アラビノース、キシロース、リボース、デオキシリボースなどのペントース；ブドウ糖（グルコース）、果糖（フルクトース）、ガラクトース、マンノース、ソルボース、フコース、ラムノース、ガラクチュロン酸、グルクロン酸、マンヌロン酸、グルコサミンなどのヘキソースなどが挙げられる。
　オリゴ糖は、二糖と、三糖以上のオリゴ糖とに大別できる。二糖としては、例えば、スクロース（ショ糖）、パラチノースなどのヘテロ二糖；セロビオース、乳糖（ラクトース）、異性化乳糖（ラクチュロース）、麦芽糖（マルトース）、イソマルトース、ゲンチオビオース、コージビオース、ラミナリビオース、メリビオース、ソホロース、トレハロースなどのホモ二糖などが挙げられる。三糖以上のオリゴ糖としては、例えば、メレチトース、ラフィノース、スタキオーズ、シクロデキストリンなどが挙げられる。
　糖アルコールとしては、例えば、キシリトール、エリスリトール、ソルビトール、マンニトール、還元麦芽糖水飴（マルチトール）、還元澱粉糖化物、還元パラチノース、還元乳糖（ラクチトール）、ペンタエリスリトールなどが挙げられる。
　これらの低分子糖は、単独でまたは二種以上組み合わせて使用できる。これらの低分子糖のうち、単糖または二糖が好ましく、二糖がさらに好ましく、ヘテロ二糖がより好ましく、スクロースが最も好ましい。
　Ｃ２－６アルカン酸としては、例えば、酢酸、プロピオン酸、酪酸、イソ酪酸、吉草酸、カプロン酸などの脂肪族モノカルボン酸などが挙げられる。これらのＣ２－６アルカン酸は、単独でまたは二種以上組み合わせて使用できる。これらのＣ２－６アルカン酸のうち、Ｃ２－４アルカン酸が好ましく、Ｃ２－３アルカン酸がさらに好ましく、酢酸が最も好ましい。
　糖アルカン酸エステル（Ｂ）は、低分子糖の水酸基のうち、一部の水酸基がエステル化した部分エステル化物であってもよいが、エステル化度は高い方が好ましく、全ての水酸基がエステル化した完全エステル化物が特に好ましい。
　糖アルカン酸エステル（Ｂ）としては、単糖または二糖のＣ２－６アルカン酸エステル、特に、二糖のＣ２－６アルカン酸エステルが好ましい。
　単糖のＣ２－６アルカン酸エステルとしては、例えば、グルコースアセテート、グルコースプロピオネート、グルコースブチレート、グルコースイソブチレート、グルコースアセテートプロピオネート、グルコースアセテートイソブチレートなどが挙げられる。
　二糖のＣ２－６アルカン酸エステルとしては、例えば、スクロースアセテート、スクロースプロピオネート、スクロースブチレート、スクロースイソブチレート、スクロースアセテートプロピオネート、スクロースアセテートイソブチレートなどが挙げられる。
　なかでも、糖アルカン酸エステル（Ｂ）としては、二糖のＣ２－４アルカン酸エステル、例えば、スクロースアセテート、スクロースプロピオネート、スクロースアセテートイソブチレートなどのヘテロ二糖とＣ２－４アルカン酸とのエステル化物が好ましく、スクローステトラアセテート、スクロースヘキサアセテート、スクロースオクタアセテートなどのスクローステトラないしオクタＣ２－４アルカン酸エステルがさらに好ましい。なかでも、スクロースとＣ２－３アルカン酸との完全エステル化物（オクタＣ２－３アルカン酸エステル）がより好ましく、スクロースオクタアセテートが最も好ましい。スクロースオクタアセテートなどの糖アルカン酸エステル（Ｂ）は、生分解性を有しているため、セルロースジアセテート（Ａ）との組み合わせにおいて、地球環境的に優れた材料を実現できる。
　糖エステルは、糖アルカン酸エステル（Ｂ）に加えて、他の糖エステルをさらに含んでいてもよい。
　他の糖エステルとしては、例えば、単糖、オリゴ糖および糖アルコールからなる群より選択された少なくとも一種と、Ｃ２－６アルカン酸以外の脂肪族カルボン酸、脂環族カルボン酸および芳香族カルボン酸からなる群より選択された少なくとも一種とのエステル化物などが挙げられる。単糖、オリゴ糖および糖アルコールとしては、前記糖アルカン酸エステル（Ｂ）を構成する低分子糖として例示された低分子糖などが挙げられる。脂肪族カルボン酸としては、例えば、ステアリン酸、オレイン酸、パルミチン酸などのＣ１２－２４アルカン酸などが挙げられる。脂環族カルボン酸としては、例えば、シクロヘキサンカルボン酸、テトラヒドロ安息香酸、ナフテン酸などが挙げられる。芳香族カルボン酸としては、安息香酸、メチル安息香酸などが挙げられる。
　これら他の糖エステルは、単独でまたは二種以上組み合わせて使用できる。これらのうち、ショ糖脂肪酸エステル（スクロースと、ステアリン酸、オレイン酸、パルミチン酸などのＣ１２－２４アルカン酸とのエステル）、スクロースベンゾエートなどのスクロースの芳香族カルボン酸エステルなどが汎用される。
　他の糖エステルの割合は、糖アルカン酸エステル（Ｂ）１００質量部に対して、１００質量部以下（例えば０．１～１００質量部）であってもよく、好ましくは５０質量部以下（例えば１～５０質量部）、さらに好ましくは１０質量部以下、より好ましくは５質量部以下、最も好ましくは１質量部以下である。他の糖エステルの割合が多すぎると、糖アルカン酸エステル（Ｂ）を配合する効果が低下することなどによって成形性や機械的特性が低下する虞がある。
　糖エステルは、糖アルカン酸エステル（Ｂ）を主成分として含むのが好ましい。糖アルカン酸エステル（Ｂ）の割合は、糖エステル中５０質量％以上であってもよいが、好ましくは８０質量％以上、さらに好ましくは９０質量％以上、より好ましくは９５質量％以上、最も好ましくは９９質量％以上である。糖エステルは、実質的に糖アルカン酸エステル（Ｂ）のみからなってもよく、糖アルカン酸エステル（Ｂ）のみからなるのが特に好ましい。
　糖エステルは、特に、スクロースオクタアセテートを主成分として含むのが好ましい。スクロースオクタアセテートの割合は、糖エステル中５０質量％以上であってもよいが、好ましくは８０質量％以上、さらに好ましくは９０質量％以上、より好ましくは９５質量％以上、最も好ましくは９９質量％以上である。糖エステルは、実質的にスクロースオクタアセテートのみからなってもよく、スクロースオクタアセテートのみからなるのが特に好ましい。
　糖エステルは、糖アルカン酸エステル（Ｂ）を主成分として含むのが好ましいため、他の糖エステルを実質的に含まないのが好ましく、他の糖エステルを含まないのが特に好ましい。
　糖エステル［特に、スクロースオクタアセテートなどの糖アルカン酸エステル（Ｂ）］の割合は、熱可塑性樹脂１００質量部に対して、例えば１～８０質量部、好ましくは５～６０質量部、さらに好ましくは１０～５０質量部である。糖エステルの割合が少なすぎると、成形性が低下する虞があり、逆に多すぎると、透明性および機械的特性が低下する虞がある。
　糖アルカン酸エステル（Ｂ）（特に、スクロースオクタアセテート）の割合は、セルロースジアセテート（Ａ）１００質量部に対して５～７０質量部程度の範囲から選択でき、例えば１０～６５質量部、好ましくは１５～６０質量部、さらに好ましくは２０～５０質量部、より好ましくは２５～４５質量部、最も好ましくは３０～３５質量部である。糖アルカン酸エステル（Ｂ）の割合が少なすぎると、溶融流動性および溶融成形性が低下する虞があり、逆に多すぎると、透明性および機械的特性（特に、衝撃強度）が低下する虞がある。
　糖アルカン酸エステル（Ｂ）（特に、スクロースオクタアセテート）は、セルロースジアセテート（Ａ）の溶融流動性（特に、射出成形に必要な溶融流動性）を向上できるため、セルロースジアセテート（Ａ）の流動性向上剤（特に、射出成形の溶融流動性を向上させるための流動性向上剤）としても利用できる。
　さらに、糖アルカン酸エステル（Ｂ）（特に、スクロースオクタアセテート）は、セルロースジアセテート（Ａ）の流動性を向上できるだけでなく、同時に樹脂組成物で形成された成形体の強度も向上できるため、強度向上剤としても作用する。そのため、糖アルカン酸エステル（Ｂ）は、セルロースジアセテート（Ａ）の強度向上剤としても利用できる。
　［可塑剤］
　本発明の樹脂組成物は、熱可塑性樹脂および糖エステルに加えて、可塑剤をさらに含んでいてもよい。可塑剤は、セルロースアセテートの可塑剤として汎用されている慣用の可塑剤であってもよい。
　慣用の可塑剤としては、例えば、クエン酸トリエチル、アセチルクエン酸トリエチル、アセチルクエン酸トリブチル、酒石酸ジブチルなどのヒドロキシ酸エステル；トリアセチン、トリプロピオニンなどのトリアシルグリセロール；２，２－ビス（４－ポリオキシエチレン－オキシフェニル）プロパンなどのポリエーテル；フタル酸ジメチル（ＤＭＰ）、フタル酸ジエチル（ＤＥＰ）、フタル酸ジブチル（ＤＢＰ）、フタル酸ジ－２－メトキシエチル、フタル酸ジアリル、ｏ－ベンゾイル安息香酸エチル、エチルフタリル・エチルグリコレート（ＥＰＥＧ）、メチルフタリル・エチルグリコレート（ＭＰＥＧ）などの芳香族カルボン酸エステル；ｐ－トルエンスルホン酸ｏ－クレジルなどの芳香族スルホン酸エステル；Ｎ－エチルトルエンスルホンアミドなどの芳香族スルホンアミド；リン酸トリエチル（ＴＥＰ）、リン酸トリフェニル（ＴＰＰ）などのリン酸エステル；ポリエステルオリゴマー、ポリアミドオリゴマーなどの樹脂オリゴマーなどが挙げられる。
　これら慣用の可塑剤は、単独でまたは二種以上組み合わせて使用できる。これらのうち、アセチルクエン酸トリブチルなどのヒドロキシ酸エステル、２，２－ビス（４－ポリオキシエチレン－オキシフェニル）プロパンなどのポリエーテルなどが汎用される。
　可塑剤の割合は、熱可塑性樹脂１００質量部に対して、５０質量部以下（例えば０．１～５０質量部）であってもよく、好ましくは３０質量部以下（例えば１～３０質量部）、さらに好ましくは１０質量部以下、より好ましくは５質量部以下、最も好ましくは１質量部以下である。可塑剤の割合が多すぎると、透明性および機械的特性が低下する虞がある。
　本発明の樹脂組成物は、前記糖エステルの配合によって溶融流動性を向上できるため、可塑剤を実質的に含まないのが好ましく、可塑剤を含まないのが最も好ましい。特に、本発明の樹脂組成物は、可塑剤の中でも、ポリエステルオリゴマーを実質的に含まないのが好ましく、ポリエステルオリゴマーを含まないのが特に好ましい。
　［他の成分］
　本発明の樹脂組成物は、熱可塑性樹脂および糖エステルに加えて、他の成分として、セルロースアセテートに配合される慣用の添加剤をさらに含んでいてもよい。慣用の添加剤としては、例えば、安定化剤（酸化防止剤、紫外線吸収剤、耐光安定剤、熱安定化剤など）、酸捕捉剤、導電剤、帯電防止剤、難燃剤（リン系難燃剤、ハロゲン系難燃剤、無機系難燃剤など）、難燃助剤、耐衝撃改良剤、流動性改良剤、レベリング剤、消泡剤、補強材（ガラス繊維、炭素繊維、セルロース繊維などの繊維状補強材、タルク、炭酸カルシウムなどの充填剤など）、着色剤、滑剤、離型剤、色相改良剤、分散剤、抗菌剤、防腐剤、低応力化剤、核剤などが挙げられる。これらの添加剤は、単独でまたは二種以上組み合わせて使用できる。
　他の成分の合計割合は、熱可塑性樹脂１００質量部に対して、例えば１００質量部以下（例えば０．１～１００質量部）であってもよく、好ましくは５０質量部以下（例えば１～５０質量部）、さらに好ましくは３０質量部以下、より好ましくは１０質量部以下、最も好ましくは５質量部以下である。
　［樹脂組成物の特性］
　本発明の樹脂組成物は、高い溶融流動性を有しており、メルトフローレートが２～１００ｇ／１０分である。メルトフローレートが小さすぎると、溶融成形性が低下し、逆に大きすぎると、機械的特性（特に、衝撃強度）が低下し、溶融成形性と機械的特性とを両立できない。樹脂組成物のメルトフローレートの好ましい範囲としては、以下段階的に、３～８０ｇ／１０分、５～５０ｇ／１０分、８～４０ｇ／１０分、１０～３５ｇ／１０分、１２～３０ｇ／１０分であり、最も好ましくは１５～２０ｇ／１０分である。
　なお、本明細書および請求の範囲において、樹脂組成物のメルトフローレート（ＭＦＲまたはメルトフローインデックスＭＦＩ）は、ＩＳＯ　１１３３に準じて、保持時間を５分として、温度２５０℃、荷重５ｋｇｆの条件で測定できる。
　本発明の樹脂組成物は、機械的特性にも優れている。本発明の樹脂組成物の曲げ強さは、例えば１００ＭＰａ以上であってもよく、例えば１００～１０００ＭＰａ、好ましくは１３０～５００ＭＰａ、さらに好ましくは１３５～３００ＭＰａ、より好ましくは１４０～２００ＭＰａ、最も好ましくは１４５～１６０ＭＰａである。
　本発明の樹脂組成物の曲げ弾性率は、１０００ＭＰａ以上であってもよく、例えば１０００～１００００ＭＰａ、好ましくは２０００～８０００ＭＰａ、さらに好ましくは３０００～６０００ＭＰａ、より好ましくは４０００～５０００ＭＰａである。
　なお、本明細書および請求の範囲において、樹脂組成物の曲げ強さおよび曲げ弾性率は、ＩＳＯ　１７８に準じて測定できる。
　本発明の樹脂組成物のアイゾット（ＩＺＯＤ）衝撃強度（ノッチ付き）は１ｋＪ／ｍ２以上であってもよく、例えば１～３０ｋＪ／ｍ２、好ましくは２～２０ｋＪ／ｍ２、さらに好ましくは３～１０ｋＪ／ｍ２、より好ましくは４～８ｋＪ／ｍ２、最も好ましくは４．５～６ｋＪ／ｍ２である。
　なお、本明細書および請求の範囲において、樹脂組成物のアイゾット衝撃強度は、ＩＳＯ　１８０に準じて測定できる。
　本発明の樹脂組成物は、熱可塑性樹脂と糖エステルと必要に応じて他の成分とを、乾式混合、溶融混練などの慣用の方法で混合することにより調製でき、樹脂組成物は、ペレットなどの形態であってもよい。溶融混練する場合、混練温度は、例えば２００～２８０℃、好ましくは２２０～２６０℃、さらに好ましくは２３０～２５０℃である。溶融混練の方法としては、慣用の方法を利用でき、例えば、二軸押出混練機を利用してもよい。
　［成形体］
　本発明の成形体は、前記樹脂組成物を慣用の成形法で成形することにより製造できる。慣用の成形法としては、圧縮成形法、射出成形法、射出圧縮成形法、押出成形法、トランスファー成形法、ブロー成形法、加圧成形法、キャスティング成形法などが挙げられる。本発明の樹脂組成物は、溶融流動性に優れるため、これらの成形方法のうち、高度な溶融流動性が要求される成形方法、例えば、射出成形法、射出圧縮成形法、押出成形法が好ましく、射出成形法が特に好ましい。
　射出成形法において、シリンダー温度は、例えば２３０～３００℃、好ましくは２４０～２８０℃、さらに好ましくは２４５～２７５℃、より好ましくは２５０～２７０℃、最も好ましくは２５５～２６５℃である。シリンダー温度が低すぎると、成形性が低下する虞があり、逆に高すぎると、成形体の機械的特性や透明性が低下する虞がある。
　射出圧力は、例えば１０～１００ＭＰａ、好ましくは２０～８０ＭＰａ、さらに好ましくは４０～６０ＭＰａである。
　金型温度は、例えば１００～２００℃、好ましくは１１０～１５０℃、さらに好ましくは１１５～１４５℃、より好ましくは１２０～１４０℃、最も好ましくは１２５～１３５℃である。金型温度が低すぎると、生産性が低下する虞があり、逆に高すぎると、成形体の機械的特性や透明性が低下する虞がある。
　本発明の成形体の形状は、特に限定されず、用途に応じて選択でき、線状または糸状などの一次元的構造体；フィルム状、シート状、板状などの二次元的構造体；ブロック状、棒状、管状またはチューブ状、中空状などの三次元的構造体などが挙げられる。特に、本発明の樹脂組成物は、射出成形によって高い生産性で成形体を製造できるため、従来のセルロースジアセテートでは成形が困難であった三次元的構造体であっても、高い生産性で製造できる。
　以下に、実施例に基づいて本発明をより詳細に説明するが、本発明はこれらの実施例によって限定されるものではない。また、各種評価方法および使用した原料の略号および詳細を下記に示す。
　［ＭＦＲ］
　ＩＳＯ　１１３３に準じて、保持時間を５分とし、温度２５０℃および試験荷重５ｋｇｆの条件で測定した。
　［曲げ強さおよび曲げ弾性率］
　ＩＳＯ　１７８に準じて測定した。
　［アイゾット（ＩＺＯＤ）衝撃強度（ノッチ付き）］
　ＩＳＯ　１８０に準じて測定した。
　［原料］
　（セルロースジアセテート）
　セルロースジアセテート（ＤＡＣ）：（株）ダイセル製「酢酸セルロース　Ｌ－３０」
　（エステル化糖類）
　スクロースオクタアセテート：東京化成工業（株）製
　（比較化合物）
　スクロース：東京化成工業（株）製
　スクロースベンゾエート：東京化成工業（株）製
　ショ糖脂肪酸エステル：東京化成工業（株）製（脂肪酸組成：パルミチン酸７５．０％以上）
　２，２－ビス（４－ポリオキシエチレン－オキシフェニル）プロパン（ＢＡ－１０）：日本乳化剤（株）製「ＢＡ－１０グリコール」
　アセチルクエン酸トリブチル（ＡＴＢＣ）：東京化成工業（株）製。
　（実施例１～５および比較例１～５）
　表１に示す質量割合の各成分を二軸押出機（サーモフィッシャーサイエンティフィック社製「Ｐｒｏｃｅｓｓ１１」）を用いて、温度２４０℃、スクリュー回転数２００ｒｐｍ、吐出量約５００ｇ／ｈで混練し、ペレット状の樹脂組成物を調製した。なお、混練物のストランド化とカットが安定的に実施できたものをペレット化「可」、熱劣化し実施できなかったものをペレット化「不可」とした。また、組成物が目視で透明であったものを「透明」、不透明であったものを「不透明」とした。得られた樹脂組成物を、ピストン式射出成形機（サーモフィッシャーサイエンティフィック社製「ＨＡＡＫＥ　ＭｉｎｉＪｅｔ　Ｐｒｏ」）を用いて、シリンダー温度：２６０℃、金型温度：１３０℃の条件で射出成形し、短冊状試験片を得た。また、得られた樹脂組成物にてＭＦＲを評価した。得られた試験片を用いて、曲げ強さ、曲げ弾性率、アイゾット衝撃強度を評価した。配合割合および評価結果を表１に示す。
Figure JPOXMLDOC01-appb-T000001
　表１の結果から明らかなように、実施例では、射出成形によって透明性および機械的特性に優れた成形体が得られた。
　本発明の樹脂組成物は、透明性、生分解性および機械的特性に優れるため、種々の分野の樹脂成形品［例えば、自動車部品、電気・電子部品、建築資材（壁材など）、土木資材、農業資材、包装資材（容器、緩衝材など）、生活資材（日用品など）など］に利用でき、特に、機械強度に優れるため、自動車部品、電気・電子部品の成形体として好適である。また、透明性に優れるため、包装資材（透明容器など）や光学用途の成形体（光学用成形体または光学部材）に好適に利用できる。

Claims (14)

  1. 　熱可塑性樹脂および糖エステルを含み、かつ溶融成形に供するための溶融成形用樹脂組成物であって、
    　前記熱可塑性樹脂が、セルロースジアセテート（Ａ）であり、
    　前記糖エステルが、単糖、オリゴ糖および糖アルコールからなる群より選択された少なくとも一種とＣ２－６アルカン酸とのエステル化物である糖アルカン酸エステル（Ｂ）を含む樹脂組成物。
  2. 　前記糖アルカン酸エステル（Ｂ）が、単糖または二糖のＣ２－４アルカン酸エステルである請求項１記載の樹脂組成物。
  3. 　前記糖アルカン酸エステル（Ｂ）が、二糖とＣ２－３アルカン酸との完全エステル化物である請求項１または２記載の樹脂組成物。
  4. 　前記糖アルカン酸エステル（Ｂ）がスクロースオクタアセテートである請求項１～３のいずれか一項に記載の樹脂組成物。
  5. 　前記スクロースオクタアセテートの割合が前記糖エステル中９０質量％以上である請求項４記載の樹脂組成物。
  6. 　前記糖アルカン酸エステル（Ｂ）の割合が、前記セルロースジアセテート（Ａ）１００質量部に対して１０～６５質量部である請求項１～５のいずれか一項に記載の樹脂組成物。
  7. 　射出成形に供するための樹脂組成物である請求項１～６のいずれか一項に記載の樹脂組成物。
  8. 　請求項１～７のいずれか一項に記載の樹脂組成物で形成された成形体。
  9. 　自動車部品、電気・電子部品、建築資材、土木資材、農業資材、包装資材、生活資材および光学部材から選択される部品または資材である請求項８記載の成形体。
  10. 　請求項１～７のいずれか一項に記載の樹脂組成物を溶融成形して成形体を製造する方法。
  11. 　前記樹脂組成物を射出成形して成形体を製造する請求項１０記載の方法。
  12. 　セルロースジアセテート（Ａ）の強度を向上させるための強度向上剤であって、単糖、オリゴ糖および糖アルコールからなる群より選択された少なくとも一種とＣ２－６アルカン酸とのエステル化物である糖アルカン酸エステル（Ｂ）で構成されている強度向上剤。
  13. 　セルロースジアセテート（Ａ）の溶融流動性を向上させるための流動性向上剤であって、単糖、オリゴ糖および糖アルコールからなる群より選択された少なくとも一種とＣ２－６アルカン酸とのエステル化物である糖アルカン酸エステル（Ｂ）で構成されている流動性向上剤。
  14. 　セルロースジアセテート（Ａ）に単糖、オリゴ糖および糖アルコールからなる群より選択された少なくとも一種とＣ２－６アルカン酸とのエステル化物である糖アルカン酸エステル（Ｂ）を配合し、前記セルロースジアセテート（Ａ）の溶融流動性および／または強度を向上する方法。
PCT/JP2023/004472 2022-03-02 2023-02-10 樹脂組成物ならびにその用途および成形方法 Ceased WO2023166943A1 (ja)