WO2023025534A1 - Composition de poly(sulfure d'arylène) - Google Patents

Composition de poly(sulfure d'arylène) Download PDF

Info

Publication number
WO2023025534A1
WO2023025534A1 PCT/EP2022/071621 EP2022071621W WO2023025534A1 WO 2023025534 A1 WO2023025534 A1 WO 2023025534A1 EP 2022071621 W EP2022071621 W EP 2022071621W WO 2023025534 A1 WO2023025534 A1 WO 2023025534A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
polymer composition
bisphenol
mol
epoxy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP2022/071621
Other languages
English (en)
Inventor
Kelly D. Branham
Benjamin TROTTER
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Solvay Specialty Polymers USA LLC
Original Assignee
Solvay Specialty Polymers USA LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Solvay Specialty Polymers USA LLC filed Critical Solvay Specialty Polymers USA LLC
Publication of WO2023025534A1 publication Critical patent/WO2023025534A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne des compositions de polymères, ainsi que des procédés de préparation de ces dernières. L'invention concerne également des compositions comprenant la composition de polymères et jusqu'à 60 % en poids d'au moins une charge, ainsi que des articles, des pièces et des matériaux composites comprenant la composition de polymères ou la composition. L'invention envisage également l'utilisation de la composition de polymères ou de la composition pour la fabrication d'objets 3D. Les compositions de polymères comprennent au moins un polymère poly(sulfure d'arylène) et au plus 5 % en poids d'au moins un macromère aromatique à fonctionnalité époxy (EFAM). Le macromère aromatique à fonctionnalité époxy a une masse moléculaire moyenne en nombre d'au plus 5 000 g/mol. L'allongement à la rupture des compositions de polymères selon l'invention est augmenté, et le module d'élasticité et la résistance à la traction des compositions de polymères selon l'invention sont sensiblement conservés, par rapport à ces mêmes propriétés d'une composition de polymères analogue ne comprenant pas le macromère aromatique à fonctionnalité époxy.
PCT/EP2022/071621 2021-08-24 2022-08-02 Composition de poly(sulfure d'arylène) Ceased WO2023025534A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US202163236510P 2021-08-24 2021-08-24
US63/236,510 2021-08-24

Publications (1)

Publication Number Publication Date
WO2023025534A1 true WO2023025534A1 (fr) 2023-03-02

Family

ID=83149190

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2022/071621 Ceased WO2023025534A1 (fr) 2021-08-24 2022-08-02 Composition de poly(sulfure d'arylène)

Country Status (1)

Country Link
WO (1) WO2023025534A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN119081406A (zh) * 2024-10-08 2024-12-06 江西聚真科技发展有限公司 一种电容器外壳用聚苯硫醚复合材料及其制备方法

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0104543A1 (fr) * 1982-09-17 1984-04-04 Dainippon Ink And Chemicals, Inc. Composition résineuse
EP0338544A2 (fr) * 1988-04-20 1989-10-25 Nippon Petrochemicals Company, Limited Composition de résine thermoplastique et procédé pour sa préparation
EP0360544A2 (fr) * 1988-09-20 1990-03-28 Ube Industries, Ltd. Composition de résines thermoplastiques
US20130079459A1 (en) * 2011-09-27 2013-03-28 Sabic Innovative Plastics Ip B.V. Blends of polyetherimide sulfone and poly(arylene sulfide) and methods of making
US20130079438A1 (en) * 2011-09-27 2013-03-28 Sabic Innovative Plastics Ip B.V. Blends of polyetherimide sulfone and poly(arylene sulfide)
WO2017161537A1 (fr) * 2016-03-24 2017-09-28 Ticona Llc Composition de sulfure de polyarylène à plus forte adhérence aux composants métalliques
WO2017161534A1 (fr) * 2016-03-24 2017-09-28 Ticona Llc Structure composite
WO2018100127A1 (fr) * 2016-12-02 2018-06-07 Solvay Specialty Polymers Usa, Llc Composition chargée contenant du sulfure de polyphénylène (pps) et du polyamide 6 (pa6)

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0104543A1 (fr) * 1982-09-17 1984-04-04 Dainippon Ink And Chemicals, Inc. Composition résineuse
EP0338544A2 (fr) * 1988-04-20 1989-10-25 Nippon Petrochemicals Company, Limited Composition de résine thermoplastique et procédé pour sa préparation
EP0360544A2 (fr) * 1988-09-20 1990-03-28 Ube Industries, Ltd. Composition de résines thermoplastiques
US20130079459A1 (en) * 2011-09-27 2013-03-28 Sabic Innovative Plastics Ip B.V. Blends of polyetherimide sulfone and poly(arylene sulfide) and methods of making
US20130079438A1 (en) * 2011-09-27 2013-03-28 Sabic Innovative Plastics Ip B.V. Blends of polyetherimide sulfone and poly(arylene sulfide)
WO2017161537A1 (fr) * 2016-03-24 2017-09-28 Ticona Llc Composition de sulfure de polyarylène à plus forte adhérence aux composants métalliques
WO2017161534A1 (fr) * 2016-03-24 2017-09-28 Ticona Llc Structure composite
WO2018100127A1 (fr) * 2016-12-02 2018-06-07 Solvay Specialty Polymers Usa, Llc Composition chargée contenant du sulfure de polyphénylène (pps) et du polyamide 6 (pa6)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN119081406A (zh) * 2024-10-08 2024-12-06 江西聚真科技发展有限公司 一种电容器外壳用聚苯硫醚复合材料及其制备方法

Similar Documents

Publication Publication Date Title
CN103154140B (zh) 热塑性树脂组合物的制造方法、热塑性树脂组合物和成型品
JP6885096B2 (ja) ポリフェニレンスルフィド樹脂組成物および成形品
JPWO2019208377A1 (ja) ポリアリーレンスルフィド樹脂組成物、成形品、複合成形品及びそれらの製造方法
JP5742377B2 (ja) ポリフェニレンスルフィド樹脂組成物および成形品
JP6809083B2 (ja) ポリアリーレンスルフィド樹脂組成物、成形品およびそれらの製造方法
KR20230161420A (ko) 폴리페닐렌 설파이드 수지 조성물 및 그것으로 이루어지는성형품
US20240317999A1 (en) Poly(arylene sulfide) composition
EP1416015B1 (fr) Composition resineuse
JP6701877B2 (ja) ポリフェニレンスルフィド樹脂組成物
WO2023025534A1 (fr) Composition de poly(sulfure d'arylène)
JP7238429B2 (ja) ポリフェニレンサルファイド樹脂組成物および成形品
JP2023068631A (ja) ポリフェニレンサルファイド樹脂組成物および成形品
JP7151086B2 (ja) ポリフェニレンスルフィド樹脂組成物
US12054591B2 (en) Poly(arylene sulfide) resin composition, molded article, composite molded article, and methods respectively for producing said products
EP4253481B1 (fr) Composition de résine de sulfure de polyphénylène et article moulé
JP7613099B2 (ja) 樹脂組成物、成形品および樹脂組成物の製造方法
JP7136372B2 (ja) ポリアリーレンスルフィド樹脂組成物、成形品およびそれらの製造方法
EP4146723A1 (fr) Copolymère de poly(sulfure d'arylène)
JP7311051B2 (ja) ポリアリーレンスルフィド樹脂組成物、成形品及びそれらの製造方法
JP2024162024A (ja) ブロック共重合体、組成物及び成形品並びにそれらの製造方法
WO2023218850A1 (fr) Composition de résine de sulfure de polyarylène, article moulé, et procédés de fabrication associés
JPWO2018056240A1 (ja) ポリアリーレンスルフィド樹脂組成物、成形品及び製造方法
JP2025079040A (ja) ポリアリーレンスルフィド樹脂組成物、成形品及びそれらの製造方法
JP6866609B2 (ja) ポリアリーレンスルフィド樹脂組成物、成形品およびそれらの製造方法
WO2025197579A1 (fr) Composition de résine de poly(sulfure d'arylène) et article moulé, et leurs procédés de production

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22761444

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 22761444

Country of ref document: EP

Kind code of ref document: A1