WO2022176519A1 - Composition pour formation d'électrode, élément de cellule solaire, et électrode stratifiée aluminium/argent - Google Patents

Composition pour formation d'électrode, élément de cellule solaire, et électrode stratifiée aluminium/argent Download PDF

Info

Publication number
WO2022176519A1
WO2022176519A1 PCT/JP2022/002478 JP2022002478W WO2022176519A1 WO 2022176519 A1 WO2022176519 A1 WO 2022176519A1 JP 2022002478 W JP2022002478 W JP 2022002478W WO 2022176519 A1 WO2022176519 A1 WO 2022176519A1
Authority
WO
WIPO (PCT)
Prior art keywords
electrode
particles
mass
aluminum
silver
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2022/002478
Other languages
English (en)
Japanese (ja)
Inventor
剛 早坂
剛 野尻
修一郎 足立
研耶 守谷
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Resonac Corp
Original Assignee
Showa Denko Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Showa Denko Materials Co Ltd filed Critical Showa Denko Materials Co Ltd
Priority to JP2023500664A priority Critical patent/JPWO2022176519A1/ja
Publication of WO2022176519A1 publication Critical patent/WO2022176519A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La composition pour formation d'électrode de l'invention contient des particules à teneur en argent, des particules à teneur en bismuth et des particules de verre. Lesdites particules de verre incluent des particules de verre comprenant un vanadium et un tellure.
PCT/JP2022/002478 2021-02-16 2022-01-24 Composition pour formation d'électrode, élément de cellule solaire, et électrode stratifiée aluminium/argent Ceased WO2022176519A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2023500664A JPWO2022176519A1 (fr) 2021-02-16 2022-01-24

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2021-022877 2021-02-16
JP2021022877 2021-02-16

Publications (1)

Publication Number Publication Date
WO2022176519A1 true WO2022176519A1 (fr) 2022-08-25

Family

ID=82931536

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2022/002478 Ceased WO2022176519A1 (fr) 2021-02-16 2022-01-24 Composition pour formation d'électrode, élément de cellule solaire, et électrode stratifiée aluminium/argent

Country Status (3)

Country Link
JP (1) JPWO2022176519A1 (fr)
TW (1) TW202244944A (fr)
WO (1) WO2022176519A1 (fr)

Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH04270140A (ja) * 1990-06-21 1992-09-25 Johnson Matthey Inc シーリングガラス組成物および導電性成分を含む同組成物
US5188990A (en) * 1991-11-21 1993-02-23 Vlsi Packaging Materials Low temperature sealing glass compositions
JP2009209032A (ja) * 2008-02-08 2009-09-17 Hitachi Powdered Metals Co Ltd ガラス組成物
JP2012218982A (ja) * 2011-04-11 2012-11-12 Hitachi Chemical Co Ltd 電子部品、それに適用されるアルミニウム電極用導電性ペースト、及びアルミニウム電極用ガラス組成物
JP2012226837A (ja) * 2011-04-14 2012-11-15 Hitachi Chem Co Ltd 電極用ペースト組成物、太陽電池素子及び太陽電池
JP2013074165A (ja) * 2011-09-28 2013-04-22 Yokohama Rubber Co Ltd:The 太陽電池集電電極形成用導電性組成物、太陽電池セル、および太陽電池モジュール
WO2013190981A1 (fr) * 2012-06-22 2013-12-27 株式会社 日立製作所 Récipient étanche, dispositif électronique et module de cellule solaire
WO2014014109A1 (fr) * 2012-07-19 2014-01-23 日立化成株式会社 Composition formant une couche de passivation, substrat semi-conducteur ayant une couche de passivation, procédé de fabrication d'un substrat semi-conducteur ayant une couche de passivation, élément de cellule solaire, procédé de fabrication d'un élément de cellule solaire, et cellule solaire
JP2014024730A (ja) * 2012-07-30 2014-02-06 Hitachi Chemical Co Ltd 電子部品及びその製法、並びにそれに用いる封止材料ペースト
WO2015030199A1 (fr) * 2013-08-30 2015-03-05 京セラ株式会社 Élément de cellule solaire et son procédé de fabrication
JP2016210681A (ja) * 2011-07-04 2016-12-15 株式会社日立製作所 ガラス組成物、該ガラス組成物を含むガラスフリット、および該ガラス組成物を含むガラスペースト
JP2017521826A (ja) * 2014-06-19 2017-08-03 イー・アイ・デュポン・ドウ・ヌムール・アンド・カンパニーＥ．Ｉ．Ｄｕ Ｐｏｎｔ Ｄｅ Ｎｅｍｏｕｒｓ Ａｎｄ Ｃｏｍｐａｎｙ 太陽電池用導体
KR20200031599A (ko) * 2018-02-23 2020-03-24 엘지전자 주식회사 무연계 저온 소성 글라스 프릿, 페이스트 및 이를 이용한 진공 유리 조립체

Patent Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH04270140A (ja) * 1990-06-21 1992-09-25 Johnson Matthey Inc シーリングガラス組成物および導電性成分を含む同組成物
US5188990A (en) * 1991-11-21 1993-02-23 Vlsi Packaging Materials Low temperature sealing glass compositions
JP2009209032A (ja) * 2008-02-08 2009-09-17 Hitachi Powdered Metals Co Ltd ガラス組成物
JP2012218982A (ja) * 2011-04-11 2012-11-12 Hitachi Chemical Co Ltd 電子部品、それに適用されるアルミニウム電極用導電性ペースト、及びアルミニウム電極用ガラス組成物
JP2012226837A (ja) * 2011-04-14 2012-11-15 Hitachi Chem Co Ltd 電極用ペースト組成物、太陽電池素子及び太陽電池
JP2016210681A (ja) * 2011-07-04 2016-12-15 株式会社日立製作所 ガラス組成物、該ガラス組成物を含むガラスフリット、および該ガラス組成物を含むガラスペースト
JP2013074165A (ja) * 2011-09-28 2013-04-22 Yokohama Rubber Co Ltd:The 太陽電池集電電極形成用導電性組成物、太陽電池セル、および太陽電池モジュール
WO2013190981A1 (fr) * 2012-06-22 2013-12-27 株式会社 日立製作所 Récipient étanche, dispositif électronique et module de cellule solaire
WO2014014109A1 (fr) * 2012-07-19 2014-01-23 日立化成株式会社 Composition formant une couche de passivation, substrat semi-conducteur ayant une couche de passivation, procédé de fabrication d'un substrat semi-conducteur ayant une couche de passivation, élément de cellule solaire, procédé de fabrication d'un élément de cellule solaire, et cellule solaire
JP2014024730A (ja) * 2012-07-30 2014-02-06 Hitachi Chemical Co Ltd 電子部品及びその製法、並びにそれに用いる封止材料ペースト
WO2015030199A1 (fr) * 2013-08-30 2015-03-05 京セラ株式会社 Élément de cellule solaire et son procédé de fabrication
JP2017521826A (ja) * 2014-06-19 2017-08-03 イー・アイ・デュポン・ドウ・ヌムール・アンド・カンパニーＥ．Ｉ．Ｄｕ Ｐｏｎｔ Ｄｅ Ｎｅｍｏｕｒｓ Ａｎｄ Ｃｏｍｐａｎｙ 太陽電池用導体
KR20200031599A (ko) * 2018-02-23 2020-03-24 엘지전자 주식회사 무연계 저온 소성 글라스 프릿, 페이스트 및 이를 이용한 진공 유리 조립체

Also Published As

Publication number Publication date
TW202244944A (zh) 2022-11-16
JPWO2022176519A1 (fr) 2022-08-25

Similar Documents

Publication Publication Date Title
CN103477395B (zh) 电极用糊剂组合物、太阳能电池元件以及太阳能电池
CN103503079B (zh) 电极用糊剂组合物、太阳能电池元件以及太阳能电池
CN104694778B (zh) 电极用糊剂组合物及太阳能电池
JP6206491B2 (ja) 電極形成用組成物、太陽電池素子及び太陽電池
CN103329214A (zh) 含锂导电糊料组合物和由其制成的制品
CN103262174A (zh) 含锂导电糊料组合物和由其制成的制品
WO2013073478A1 (fr) Composition de pâte pour électrode, élément de cellule solaire, cellule solaire
WO2015115565A1 (fr) Composition de formation d'électrode, électrode, élément de cellule solaire, leur procédé de fabrication, et cellule solaire
WO2022075456A1 (fr) Composition pour formation d'électrode, élément de cellule solaire, et électrode stratifiée aluminium/argent
JP2016189443A (ja) 電極形成用組成物、電極、太陽電池素子及びその製造方法、並びに太陽電池
JP2022143534A (ja) 電極形成用組成物及び太陽電池素子
WO2022176519A1 (fr) Composition pour formation d'électrode, élément de cellule solaire, et électrode stratifiée aluminium/argent
WO2022176520A1 (fr) Composition pour formation d'électrode, élément de cellule solaire, et électrode stratifiée aluminium/argent
WO2017033343A1 (fr) Composition pour formation d'électrode, électrode, élément de batterie solaire, batterie solaire, et procédé de fabrication d'élément de batterie solaire
WO2022181732A1 (fr) Élément de cellule solaire et cellule solaire
JP2016189310A (ja) 電極形成用組成物、電極、太陽電池素子及びその製造方法並びに太陽電池
WO2022181730A1 (fr) Élément de cellule solaire et cellule solaire
JP2022143533A (ja) 電極形成用組成物及び太陽電池素子
WO2022181731A1 (fr) Élément de cellule solaire et cellule solaire
WO2022138385A1 (fr) Composition pour former une électrode, élément de cellule solaire et électrode empilée d'aluminium/argent
WO2022075457A1 (fr) Composition pour formation d'électrode, élément de cellule solaire, et électrode stratifiée aluminium/argent
JP2016189447A (ja) 太陽電池素子及びその製造方法並びに太陽電池
JP6464669B2 (ja) 電極形成用組成物、電極、太陽電池素子並びに太陽電池及びその製造方法
JP2016189307A (ja) 電極形成用組成物、電極、太陽電池素子及びその製造方法並びに太陽電池
TW202506581A (zh) 導電性膏、導電性膏之用途、太陽電池及太陽電池之製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22755843

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2023500664

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 22755843

Country of ref document: EP

Kind code of ref document: A1