WO2022163552A1 - 新規なベンゾオキサジン化合物、それを含有する樹脂原料組成物、硬化性樹脂組成物及びその硬化物 - Google Patents

新規なベンゾオキサジン化合物、それを含有する樹脂原料組成物、硬化性樹脂組成物及びその硬化物 Download PDF

Info

Publication number
WO2022163552A1
WO2022163552A1 PCT/JP2022/002311 JP2022002311W WO2022163552A1 WO 2022163552 A1 WO2022163552 A1 WO 2022163552A1 JP 2022002311 W JP2022002311 W JP 2022002311W WO 2022163552 A1 WO2022163552 A1 WO 2022163552A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
general formula
benzoxazine compound
benzoxazine
compound
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2022/002311
Other languages
English (en)
French (fr)
Inventor
芳美 宇高
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Honshu Chemical Industry Co Ltd
Original Assignee
Honshu Chemical Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Honshu Chemical Industry Co Ltd filed Critical Honshu Chemical Industry Co Ltd
Priority to CN202280010108.1A priority Critical patent/CN116724027A/zh
Priority to US18/272,055 priority patent/US20240101523A1/en
Priority to JP2022578345A priority patent/JP7771488B2/ja
Priority to KR1020237023840A priority patent/KR20230141764A/ko
Publication of WO2022163552A1 publication Critical patent/WO2022163552A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

耐熱性に優れかつ、低い温度条件で硬化が可能な、新規なベンゾオキサジン化合物、それを含有する樹脂原料組成物、硬化性樹脂組成物及びその硬化物の提供を課題とする。解決手段として、一般式（１）で表されるベンゾオキサジン化合物を提供する。（式中、Ｒ１は水素原子又は炭素原子数１～６のアルキル基を示し、Ｒ２は炭素原子数１～６のアルキレン基を示す。）

Description

新規なベンゾオキサジン化合物、それを含有する樹脂原料組成物、硬化性樹脂組成物及びその硬化物
　本発明は、新規なベンゾオキサジン化合物、それを含有する樹脂原料組成物、硬化性樹脂組成物及びその硬化物に関する。詳しくは、メチレン基の両末端にベンゾオキサジン環を有し、さらにヒドロキシ基を有する新規なベンゾオキサジン化合物や、それを含有する樹脂原料組成物、硬化性樹脂組成物及びその硬化物に関する。
　ベンゾオキサジン化合物は、フェノール類、アミン類及びホルムアルデヒドを反応させることにより合成される化合物であり、加熱することにより揮発性の副生物を生ずることなく、ベンゾオキサジン環が開環重合して硬化する熱硬化性樹脂原料として知られており、絶縁基板用材料として利用可能な成形体、液晶配向剤、半導体封止用樹脂組成物などの原料として利用されている。かかる用途では、高温下での安定性や信頼性に優れた耐熱性が求められている。
　一方で、通常ベンゾオキサジン化合物の硬化温度は比較的高く、その重合温度を下げるために触媒、重合促進剤の他、高反応性ベンゾオキサジン化合物が近年開発されている。その高反応性ベンゾオキサジン化合物の中でも、比較的低温で短時間に環境に優しい方法で硬化が可能となるヒドロキシル官能基又は含窒素複素環を含有したベンゾオキサジン組成物が報告されている（特許文献１）。
特表２０１１－５３０５７０号公報
　熱硬化性樹脂の成型プロセスにおける温度を低下させ、加熱及び冷却の時間短縮や省エネルギー化による効率化や、重合時の高温にさらされることによる材料の熱劣化の抑制をするために、さらに低い温度条件で硬化が可能な優れた材料が要望されている。
　本発明は、耐熱性に優れかつ、低い温度条件で硬化が可能な、新規なベンゾオキサジン化合物、それを含有する樹脂原料組成物、硬化性樹脂組成物及びその硬化物を提供することを課題とする。
　本発明者は、上述の課題解決のために鋭意検討した結果、ビスフェノールＦを原料として用い、メチレン基の両末端にベンゾオキサジン環を有し、さらにヒドロキシ基を有する新規なベンゾオキサジン化合物が、耐熱性に優れかつ、低い温度条件で硬化が可能であることを見出し、本発明を完成した。
　本発明は以下のとおりである。
１．下記一般式（１）で表されるベンゾオキサジン化合物。
Figure JPOXMLDOC01-appb-C000002
 （式中、Ｒ１は水素原子又は炭素原子数１～６のアルキル基を示し、Ｒ２は炭素原子数１～６のアルキレン基を示す。）
２．１．に記載のベンゾオキサジン化合物を含む樹脂原料組成物。
３．１．に記載のベンゾオキサジン化合物又は２．に記載の樹脂原料組成物を含む、硬化性樹脂組成物。
４．１．に記載のベンゾオキサジン化合物又は２．に記載の樹脂原料組成物と、エポキシ樹脂、前記一般式（１）で表されるベンゾオキサジン化合物以外のベンゾオキサジン化合物、フェノール樹脂及びビスマレイミド化合物からなる群より選択される１種以上を含有する、３．に記載の硬化性樹脂組成物。
５．３．又は４．に記載の硬化性樹脂組成物を硬化させてなる硬化物。
　本発明化合物は、従来公知の下記化学構造を有する比較例化合物Ａに比べて、低温で硬化することができるため、熱硬化性樹脂の成型プロセスにおける温度を下げることができ、加熱及び冷却の時間短縮や省エネルギー化による効率化が可能であるほか、熱に弱い材料（基材）にも使用できるので非常に有用である。
Figure JPOXMLDOC01-appb-C000003
  　また、本発明化合物の硬化物は、従来公知の前記比較例化合物Ａの硬化物に比べて極めて優れた耐熱性を有するため、高温下での安定性や信頼性に優れる材料であり、非常に有用である。
　本発明における新規なベンゾオキサジン化合物、それを含有する樹脂原料組成物、硬化性樹脂組成物及びその硬化物は、各種基材に塗布可能なワニス、ワニスを含浸させたプリプレグ、プリント回路基板、電子部品の封止剤、電気・電子成型部品、自動車部品、積層材、塗料、レジストインク等の樹脂原料として好適に用いることができる。
＜本発明の新規なベンゾオキサジン化合物＞
　本発明の新規なベンゾオキサジン化合物は、下記一般式（１）で表される。
Figure JPOXMLDOC01-appb-C000004
 （式中、Ｒ１は水素原子又は炭素原子数１～６のアルキル基を示し、Ｒ２は炭素原子数１～６のアルキレン基を示す。）
　一般式（１）中のＲ１は、水素原子又は炭素原子数１～４のアルキル基であることが好ましく、水素原子又は炭素原子数１のアルキル基（メチル基）であることがより好ましく、水素原子であることが特に好ましい。Ｒ１が水素原子である場合の態様は、下記一般式（１’）で表される。
Figure JPOXMLDOC01-appb-C000005
  （式中、Ｒ２は一般式（１）と同じである。）
　一般式（１）中のベンゼン環に結合するＲ１がアルキル基である場合（Ｒ１’）、その結合位置としては、酸素原子の結合位置に対してオルソ位であることが好ましい。この時の態様は、下記一般式（１”）で表される。
Figure JPOXMLDOC01-appb-C000006
 （式中、Ｒ１’はアルキル基を示し、Ｒ２は一般式（１）と同じである。）
　一般式（１）中のＲ２は、炭素原子数１～４のアルキレン基であることが好ましく、炭素原子数１又は２のアルキレン基であることがより好ましく、炭素原子数２のアルキレン基（エチレン基）であることが特に好ましい。
　一般式（１）における中央のメチレン基と、２つのベンゾオキサジン環との結合位置は、酸素原子の結合位置に対してオルソ位又はパラ位であることが好ましい。
　本発明における、一般式（１）で表される新規なベンゾオキサジン化合物の具体例として、下記化学構造を有する化合物（ｐ－１）～（ｐ－３２）を示す。このうち、化合物（ｐ－１）～（ｐ－２０）が好ましく、化合物（ｐ－１）～（ｐ－１６）がより好ましく、化合物（ｐ－１）～（ｐ－１２）がさらに好ましく、化合物（ｐ－４）～（ｐ－６）が特に好ましい。
Figure JPOXMLDOC01-appb-C000007
Figure JPOXMLDOC01-appb-C000008
Figure JPOXMLDOC01-appb-C000009
Figure JPOXMLDOC01-appb-C000010
＜本発明化合物の製造方法＞
　本発明における、一般式（１）で表される新規なベンゾオキサジン化合物については、その製造における出発原料、製造方法について特に制限はない。例えば、下記反応式で例示するとおり、一般式（２）で表されるビスフェノール化合物、一般式（３）で表されるアミノアルコール化合物及びホルムアルデヒドを脱水縮合反応させて環化し、目的とする一般式（１）で表される新規なベンゾオキサジン化合物を得る製造方法が挙げられる。
Figure JPOXMLDOC01-appb-C000011
  （式中、Ｒ１とＲ２は一般式（１）と同じである。）
　上記製造方法において、出発原料として一般式（２）で表されるビスフェノール化合物、一般式（３）で表されるアミノアルコール化合物及びホルムアルデヒド類を使用する。
　一般式（２）で表されるビスフェノール化合物としては、具体的には、例えば、ビスフェノールＦ（ビス（２－ヒドロキシフェニル）メタン、２－ヒドロキシフェニル－４－ヒドロキシフェニルメタン、ビス（４－ヒドロキシフェニル）メタン）、ビス（４－ヒドロキシ－３－メチルフェニル）メタン、ビス（２－ヒドロキシ－５－メチルフェニル）メタン、ビス（４－ヒドロキシ－２－メチルフェニル）メタン、ビス（２－ヒドロキシ－６－メチルフェニル）メタン、２－ヒドロキシ－６－メチルフェニル－４－ヒドロキシ－２－メチル－フェニルメタン等が挙げられる。
　一般式（３）で表されるアミノアルコール化合物としては、具体的には、例えば、メタノールアミン、２－アミノエタノール、３－アミノ－１－プロパノール、１－アミノ－２－プロパノール、４－アミノ－１－ブタノール、２－アミノ－１－ブタノール、４－アミノ－２－ブタノール、５－アミノ－１－ペンタノール、６－アミノ－１－ヘキサノール、７－アミノ－１－ヘプタノール、バリノールが挙げられる。中でも、２－アミノエタノールが好ましい。
　ホルムアルデヒド類としては、具体的には、例えば、ホルムアルデヒド水溶液、１，３，５－トリオキサン、パラホルムアルデヒド等を挙げられる。
　上記製造方法において、ホルムアルデヒド類の使用量としては、一般式（２）で表されるビスフェノール化合物１モルに対して４．０～２０．０モルの範囲であることが好ましく、４．０～１６．０モルの範囲であることがより好ましく、４．０～１２．０モルの範囲であることがさらに好ましい。
　上記製造方法において、一般式（３）で表されるアミノアルコール化合物の使用量としては、一般式（２）で表されるビスフェノール化合物１モルに対して、２．０～１０．０モルの範囲であることが好ましく、２．０～８．０モルの範囲であることがより好ましく、２．０～６．０モルの範囲であることがさらに好ましい。
　反応を促進するための触媒は特に必要はないが、必要に応じて、酸触媒又は塩基触媒を使用することができる。この場合、使用できる酸触媒として、濃塩酸、塩酸ガス、トリフルオロ酢酸、メタンスルホン酸、ｐ－トルエンスルホン酸、安息香酸及びそれらの混合物等が挙げられ、使用できる塩基触媒としては、水酸化ナトリウム、炭酸ナトリウム、トリエチルアミン、トリエタノールアミン及びそれらの混合物等が挙げられるが、これらに限定されるものではない。
　反応は通常、溶媒の存在下に行われる。溶媒としては、反応を阻害しないものであれば特に制限はないが、トルエン、キシレン、酢酸エチル、酢酸ブチル、クロロホルム、ジクロロメタン、テトラヒドロフラン、ジオキサン等が好ましく挙げられる。これらの溶媒は単独又は組み合わせて用いることができる。また、溶媒の使用量は反応に支障なければ特に制限はないが、通常、一般式（２）で表されるビスフェノール化合物に対し０．５～５重量倍の範囲、好ましくは１～３重量倍の範囲で用いられる。
　反応温度は、通常１０～１５０℃の範囲で行い、１０～１２０℃の範囲が好ましく、１０～８０℃の範囲がより好ましく、２０～７０℃の範囲がさらに好ましく、２０～６０℃の範囲が特に好ましい。
　反応圧力は常圧条件下で行ってもよく、また、加圧下でも、或は減圧下で行ってもよい。
　別の態様として、原料に由来する水若しくは反応中に生成した水を系外に除去する手順を含むことができる。反応溶液から生成した水を除去する手順は特に制限されず、生成した水を反応溶液中の溶媒系と共沸的に蒸留することにより行うことができる。生成した水は、例えばコックを備えた等圧滴下漏斗、ジムロート冷却器、ディーンスターク装置等の使用により反応系外に除去することができる。
　得られた反応終了混合物は、反応終了後、公知の方法によりこの混合物から一般式（１）で表されるベンゾオキサジン化合物を得ることができる。例えば、反応後、反応混合物から残存原料や溶媒を留去することにより残液として目的物を得ることができる。また、残液を貧溶媒に添加して沈殿させた目的物を得ることや、反応混合物に溶媒を添加して晶析し、ろ過することにより粉体若しくは粒状の目的物を得ることも考えられる。上記方法により、取り出されたベンゾオキサジン化合物は、例えば、溶媒や水での洗浄や再結晶等の通常の精製手段により、高純度品とすることができる。
＜一般式（１）で表されるベンゾオキサジン化合物を含む樹脂原料組成物＞
　本発明の樹脂原料組成物は、一般式（１）で表されるベンゾオキサジン化合物を含むことを特徴としており、前述の反応混合物から残存原料や溶媒を留去することにより得ることができる。また、残液を貧溶媒に添加して沈殿させた目的物を得ることや、反応混合物に溶媒を添加して晶析し、ろ過することにより粉体若しくは粒状の本発明の樹脂原料組成物を得ることができる。例えば、溶媒や水での洗浄や再結晶等の通常の精製を行うことにより、前記一般式（１）で表されるベンゾオキサジン化合物の含有量が多い、本発明の樹脂原料組成物を得ることができる。
　本発明の樹脂原料組成物は、一般式（１）で表されるベンゾオキサジン化合物を製造する反応において、一般式（２）で表されるビスフェノール化合物における、ベンゼン環に結合するメチレン鎖の位置が異なる混合物を使用して製造してもよい。
　使用する一般式（２）で表されるビスフェノール化合物における、ベンゼン環に結合するメチレン鎖の位置が異なる化合物の比率には特に制限はない。
　具体例を挙げて説明をすると、ビスフェノールＦを使用する場合、その位置異性体すなわち、ビス（２－ヒドロキシフェニル）メタン、２－ヒドロキシフェニル－４－ヒドロキシフェニルメタン、ビス（４－ヒドロキシフェニル）メタンの混合物を使用することができ、その比率には特に制限はない。
　ビス（２－ヒドロキシフェニル）メタンの比率が大きいビスフェノールＦとしては、例えば、特開平０８－２４５４６４号公報の方法により得ることができ、ビス（４－ヒドロキシフェニル）メタンの比率が大きいビスフェノールＦとしては、例えば、特開平０６－３４０５６５号公報の方法により得ることができる。
　そのようなビスフェノールＦの位置異性体の混合物と一般式（３）で表されるアミノアルコール化合物として２－アミノエタノールを使用して、本発明の一般式（１）で表されるベンゾオキサジン化合物を上記製造方法により合成すると、化合物（ｐ－４）、（ｐ－５）、（ｐ－６）の混合物として得ることができる。
　使用する一般式（２）で表されるビスフェノール化合物において、ビスフェノール（２核体）の含有量としては、特に制限はないが、５０重量％以上であることが好ましく、７０重量％以上であることがより好ましく、８５重量％以上であることがさらに好ましく、８９重量％以上であることが特に好ましい。ビスフェノールの製造における副生物である多核体を含有していてもよい。
　本発明における樹脂原料組成物は、一般式（１）で表されるベンゾオキサジン化合物を製造する反応において副生する化合物を含有していてもよい。かかる副生物として、例えば、一般式（１）で表されるベンゾオキサジン化合物よりも高分子量の化合物が挙げられる。
　本発明の樹脂原料組成物において、一般式（１）で表されるベンゾオキサジン化合物の含有量については特に限定されないが、その含有量は、示差屈折計を検出器とするゲル浸透クロマトグラフィーにより分析することができ、通常、かかる分析で検出されるすべてのピークの面積に対して、１０～１００面積％であり、好ましくは２０～１００面積％であり、より好ましくは３０～１００面積％であり、特に好ましくは４０～１００面積％である。
＜一般式（１）で表されるベンゾオキサジン化合物又はそれを含む樹脂原料組成物を含む、硬化性樹脂組成物＞
　本発明の一般式（１）で表されるベンゾオキサジン化合物又はそれを含む樹脂原料組成物は、これを必須成分とする硬化性樹脂組成物として使用することができる。
　その一態様として、一般式（１）で表されるベンゾオキサジン化合物又はそれを含む樹脂原料組成物と、酸化珪素、酸化アルミニウム、酸化マグネシウム、窒化ホウ素、窒化アルミニウム、窒化珪素、炭化珪素があり、六方晶窒化ホウ素等の無機フィラーや、炭素繊維、ガラス繊維、有機繊維、ボロン繊維、スチール繊維、アラミド繊維等の強化繊維とを混合した硬化性樹脂組成物がある。
　その他の態様として、一般式（１）で表されるベンゾオキサジン化合物又はそれを含む樹脂原料組成物を必須成分として含有し、その他の高分子材料を含有する硬化性樹脂組成物がある。
　本発明の硬化性樹脂組成物を構成する高分子材料としては、特に制限はないが、エポキシ樹脂、フェノール樹脂、ビスマレイミド化合物、一般式（１）で表されるベンゾオキサジン化合物以外のベンゾオキサジン化合物、それぞれの原料を含有することができる。
　このエポキシ樹脂としては、例えば、オルソクレゾール型エポキシ樹脂、ビフェニル型エポキシ樹脂、ビフェニルアラルキル型エポキシ樹脂、ナフタレン型エポキシ樹脂、アントラセンジヒドリド型エポキシ樹脂、臭素化ノボラック型エポキシ樹脂等が挙げられる。
　このフェノール樹脂としては、例えば、フェノールノボラック樹脂、クレゾールノボラック樹脂、ナフトールノボラック樹脂、アミノトリアジンノボラック樹脂、トリスフェニルメタン型のフェノールノボラック樹脂等のノボラック型フェノール樹脂；テルペン変性フェノール樹脂、ジシクロペンタジエン変性フェノール樹脂等の変性フェノール樹脂；フェニレン骨格及び／又はビフェニレン骨格を有するフェノールアラルキル樹脂、フェニレン骨格及び／又はビフェニレン骨格を有するナフトールアラルキル樹脂等のアラルキル型樹脂；レゾール型フェノール樹脂等が挙げられる。
　このビスマレイミド化合物としては、例えば、下記構造を有するビスマレイミド化合物の原料等が挙げられる。
Figure JPOXMLDOC01-appb-C000012
　一般式（１）で表されるベンゾオキサジン化合物以外のベンゾオキサジン化合物としては、例えば、下記一般式（Ａ）～（Ｃ）で表される構造を有するベンゾオキサジン化合物等が挙げられる。
Figure JPOXMLDOC01-appb-C000013
  （式中、Ｒａは炭素原子数１～３０の２価の基を示し、Ｒｂは各々独立して置換基を有してもよい炭素原子数１～１０の１価の基を示し、ｎは０又は１を示す。）
Figure JPOXMLDOC01-appb-C000014
  （式中、Ｒｃは炭素原子数１～３０の２価の基、直接結合、酸素原子、硫黄原子、カルボニル基、又はスルホニル基を示し、Ｒｄは各々独立して炭素原子数１～１０の１価の基を示す。）
Figure JPOXMLDOC01-appb-C000015
  （式中、Ｒｅは各々独立して炭素原子数１～１０の１価の基を示し、ｍは０又は１を示す。）
　一般式（Ａ）で表される構造を有するベンゾオキサジン化合物におけるＲａは、炭素原子数１～３０の２価の基を示す。その具体例としては、１，２－エチレン、１，４－ブチレン、１，６－ヘキシレン等のアルキレン基、１，４－シクロヘキシレン、ジシクロペンタジエニレン、アダマンチレン等の環状構造を含むアルキレン基、１，４－フェニレン、４，４’－ビフェニレン、ジフェニルエーテル－４，４’－ジイル、ジフェニルエーテル－３，４’－ジイル、ジフェニルケトン－４，４’－ジイル、ジフェニルスルホン－４，４’－ジイル等のアリーレン基が挙げられる。
　一般式（Ａ）で表される構造を有するベンゾオキサジン化合物におけるＲｂは、各々独立して炭素原子数１～１０の１価の基を示す。その具体例としては、メチル基、エチル基、プロピル基、ブチル基等のアルキル基、ビニル基、アリル基等のアルケニル基、エチニル基、プロパルギル基等のアルキニル基、フェニル基、ナフチル基等のアリール基等が挙げられ、これらの基には更に、炭素原子数１～４のアルコキシ基、炭素原子数１～４のアシル基、ハロゲン原子、カルボキシル基、スルホ基、アリルオキシ基、ヒドロキシ基、チオール基等の置換基を有してもよい。
　一般式（Ａ）で表される構造を有するベンゾオキサジン化合物としては、例えば、四国化成社製Ｐ－ｄ型ベンゾオキサジン、ＪＦＥケミカル社製ＪＢＺ－ＯＰ１００Ｎ、ＪＢＺ－ＢＰ１００Ｎが挙げられる。
　一般式（Ｂ）で表される構造を有するベンゾオキサジン化合物におけるＲｃは、炭素原子数１～３０の２価の基、直接結合、酸素原子、硫黄原子、カルボニル基又はスルホニル基を示す。炭素原子数１～３０の２価の基としては、メチレン、１，２－エチレン、１，４－ブチレン、１，６－ヘキシレン等のアルキレン基、１，４－シクロヘキシレン、ジシクロペンタジエニレン、アダマンチレン等の環状構造を含むアルキレン基、エチリデン、プロピリデン、イソプロピリデン、ブチリデン、フェニルエチリデン、シクロペンチリデン、シクロヘキシリデン、シクロヘプチリデン、シクロドデシリデン、３，３，５－トリメチルシクロヘキシリデン、フルオレニリデン等のアルキリデン基等が挙げられる。
　一般式（Ｂ）で表される構造を有するベンゾオキサジン化合物におけるＲｄは、各々独立して炭素原子数１～１０の１価の基を示す。その具体例としては、メチル基、エチル基、プロピル基、ブチル基等のアルキル基、ビニル基、アリル基等のアルケニル基、エチニル基、プロパルギル基等のアルキニル基、フェニル基、ナフチル基等のアリール基が挙げられ、これらの置換基には更に、炭素原子数１～４のアルコキシ基、炭素原子数１～４のアシル基、ハロゲン原子、カルボキシル基、スルホ基、アリルオキシ基、ヒドロキシ基（但し、Ｒｃがメチレンである場合を除く）、チオール基等の置換基を有してもよい。
　一般式（Ｂ）で表される構造を有するベンゾオキサジン化合物としては、例えば、四国化成社製Ｆ－ａ型ベンゾオキサジン、小西化学工業社製ＢＳ－ＢＸＺが挙げられる。
　一般式（Ｃ）で表される構造を有するベンゾオキサジン化合物におけるＲｅは、各々独立して炭素原子数１～１０の１価の基を示す。その具体例としては、メチル基、エチル基、プロピル基、ブチル基等のアルキル基、ビニル基、アリル基等のアルケニル基、エチニル基、プロパルギル基等のアルキニル基、フェニル基、ナフチル基等のアリール基が挙げられ、これらの置換基には更に、炭素原子数１～４のアルコキシ基、炭素原子数１～４のアシル基、ハロゲン原子、カルボキシル基、スルホ基、アリルオキシ基、ヒドロキシ基、チオール基等の置換基を有してもよい。
　中でも、本発明の硬化性樹脂組成物は、一般式（１）で表されるベンゾオキサジン化合物又はそれを含む樹脂原料組成物と、エポキシ樹脂、一般式（１）で表されるベンゾオキサジン化合物以外のベンゾオキサジン化合物、フェノール樹脂、ビスマレイミド化合物からなる群より選択される１種以上を含有することが好ましい。
　本発明の硬化性樹脂組成物における、一般式（１）で表されるベンゾオキサジン化合物又はそれを含む樹脂原料組成物と、その他の高分子材料の混合量は、上記一般式（１）で表されるベンゾオキサジン化合物又はそれを含む樹脂原料組成物１重量部に対して、０．０１重量部～１００重量部の範囲である。
　本発明の硬化性樹脂組成物は、一般式（１）で表されるベンゾオキサジン化合物又はそれを含む樹脂原料組成物を、その他必要に応じて前記高分子材料に添加することによって得られるが、かかる添加方法は特に限定されず、従来公知の方法を採用することができる。例えば、高分子材料の合成や重合中に添加する方法、高分子材料からなる樹脂を例えば溶融押出工程等において溶融した溶融樹脂に添加する方法、高分子材料からなる樹脂製品等に含浸する方法等を挙げることができる。
　本発明の硬化性樹脂組成物は、組成物中に水や残存溶媒を含んでいると硬化時に気泡が発生してしまうので、これを防ぐために前処理として真空脱気処理を行うことが好ましい。この真空脱気処理の温度は、本発明の硬化性樹脂組成物が溶融状態となる温度であれば特に制限されないが、硬化が進行せず、かつ、脱気がしやすいとの理由により１５０℃を上限として行うのが好ましい。真空脱気処理の圧力は、特に制限はないが、低い（減圧度の高い）方がよく、空気中でも窒素置換雰囲気下中の何れで行ってもよい。この真空脱気処理は、気泡が目視で確認できなくなるまで行う。
　本発明の硬化性樹脂組成物は、用途の必要に応じて、酸化珪素、酸化アルミニウム、酸化マグネシウム、窒化ホウ素、窒化アルミニウム、窒化珪素、炭化珪素があり、六方晶窒化ホウ素等の無機フィラーや、炭素繊維、ガラス繊維、有機繊維、ボロン繊維、スチール繊維、アラミド繊維等の強化繊維と混合して使用することができる。
＜本発明の硬化性樹脂組成物を硬化させてなる硬化物＞
　続いて、本発明の硬化物について説明する。
　本発明の硬化物は、本発明の一般式（１）で表されるベンゾオキサジン化合物又はそれを含む樹脂原料組成物を必須成分とする、本発明の硬化性樹脂組成物を硬化させて得ることができる。
　本発明の硬化物の製造方法としては、例えば、所定の温度まで加熱して硬化させる方法、加熱融解させて金型等に注ぎ金型を更に加熱して硬化成型させる方法、溶融物を予め加熱された金型に注入して硬化させる方法等を挙げることができる。
　本発明の硬化物は、通常のベンゾオキサジンと同様の硬化条件にて、開環重合を行い硬化することができる。硬化温度は、通常１５０～３００℃の温度範囲であり、好ましくは１７０～２８０℃の温度範囲であり、より好ましくは１７０～２６０℃の温度範囲であるが、得られる硬化物の機械物性を良くするためには、特に１７０～２４０℃の温度範囲とすることが好ましい。このような温度範囲において硬化を行う場合には、反応時間は１～１０時間程度であればよい。
　硬化物の製造は、空気中でも窒素などの不活性ガス雰囲気下中の何れで行ってもよいが、不活性ガス雰囲気下中に行うことが、得られる硬化物の酸素による劣化を防止するために好ましい。
　本発明の樹脂組成物は、熱のみで硬化できるが、一般式（１）で表されるベンゾオキサジン化合物以外の成分やその含有量等によっては、硬化促進剤を用いた方が好ましい。使用できる硬化促進剤としては、特に限定されるものではなく、例えば、１，８－ジアザ－ビシクロ［５.４.０］ウンデセン－７、トリエチレンジアミン、トリス（２，４，６－ジメチルアミノメチル）フェノール等の第三級アミン類、２－エチル－４－メチルイミダゾール、２－メチルイミダゾール等のイミダゾール類、トリフェニルホスフィン、テトラフェニルホスホニウムブロマイド、テトラフェニルホスホニウムテトラフェニルボレート、テトラ－ｎ－ブチルホスホニウム－О，О－ジエチルホスホロジチオエート等のリン化合物、４級アンモニウム塩、有機金属塩類、及びこれらの誘導体等が挙げられる。これらは単独で使用してもよく、あるいは、併用してもよい。これら硬化促進剤の中では、第三級アミン類、イミダゾール類及びリン化合物を用いることが好ましい。
　本発明の一般式（１）で表されるベンゾオキサジン化合物は、従来公知の前記比較例化合物Ａと比べて硬化温度が低いことから、熱硬化性樹脂の成型プロセスにおける、加熱及び冷却の時間短縮や省エネルギー化による効率化が可能であるほか、熱に弱い材料（基材）にも使用できるため、非常に有用である。更に、その硬化物は、従来公知の前記比較例化合物Ａと比べて、極めて優れた耐熱性を有することから、高温下での安定性や信頼性に優れる材料であり、非常に有用である。
　以下、実施例により、本発明をさらに具体的に説明する。
＜分析方法＞
１．反応溶液組成及び純度分析（ゲル浸透クロマトグラフィー：ＧＰＣ）
　合成した各種ベンゾオキサジン化合物の純度は、本分析によるベンゾオキサジン化合物の面積百分率の数値とした。
装置　：ＨＬＣ－８３２０／東ソー（株）製
検出器：示差屈折計（ＲＩ）
［測定条件］
流量　：１ｍＬ／ｍｉｎ
溶出液：テトラヒドロフラン
温度　：４０℃
波長　：２５４ｎｍ
測定試料：ベンゾオキサジン化合物含有組成物１ｇをテトラヒドロフランで２００倍に希釈した。
２．硬化特性評価
　合成した各種ベンゾオキサジン化合物の硬化特性評価は、以下の操作条件の示差走査熱量測定（ＤＳＣ）により行った。発熱ピーク温度を硬化温度とした。
［測定条件］
　装置　　　　：ＤＳＣ７０２０／（株）日立ハイテクサイエンス製
　昇温速度　　：１０℃／ｍｉｎ
　測定温度範囲：３０～４００℃
　測定雰囲気　：窒素５０ｍＬ／ｍｉｎ
　測定試料　　：合成した各種ベンゾオキサジン化合物３ｍｇ
３．耐熱性評価（５％重量減少温度測定）
　合成した各種ベンゾオキサジン化合物の耐熱性評価は、２５０℃で硬化させ（硬化時間：１時間、昇温速度１０℃／ｍｉｎ）、室温まで冷却後（冷却速度１０℃／ｍｉｎ）、以下の操作条件の熱重量測定（以下ＴＧ）による５％重量減少温度で行った。
［測定条件］
装置：ＤＴＧ－６０Ａ／（株）島津製作所製
温度：３０→５００℃（昇温速度１０℃／ｍｉｎ）
測定雰囲気：開放、窒素５０ｍＬ／ｍｉｎ
測定試料：合成した各種ベンゾオキサジン化合物１０ｍｇ
４.ベンゾオキサジン化合物の硬化物の耐熱性評価
　合成した各種ベンゾオキサジン化合物の硬化物の耐熱性評価は、以下の操作条件の動的粘弾性測定によるガラス転移温度（Ｔｇ）測定により行った。
［測定条件］
装置　　　　：ＤＭＡ　Ｑ８００（ティー・エイ・インスツルメント・ジャパン株式会社製）
治具　　　　：デュアルカンチレバー
周波数　　　：１Ｈｚ
温度　　　　：３０→２５０℃（２℃／分）
測定試料　　：後述する方法により得た試験片
＜実施例１＞（下記化学式で表される本発明の化合物の合成）
Figure JPOXMLDOC01-appb-C000016
 　温度計、撹拌機、冷却管、滴下ロートを備えた１Ｌの４つ口フラスコにビスフェノールＦ（２核体含有率９０．１重量％、その内の異性体比率：ビス（２－ヒドロキシフェニル）メタン１８．８重量％、２－ヒドロキシフェニル－４－ヒドロキシフェニルメタン４９．３重量％、ビス（４－ヒドロキシフェニル）メタン３１．９重量％、多核体含有率９．９重量％）９７ｇ（０．４９モル）、９４％パラホルムアルデヒド６２ｇ、トルエン１２１ｇを仕込み、反応容器内を窒素置換した後、混合溶液の温度を７０℃とした。その後、２－アミノエタノール６０ｇを滴下ロートで４つ口フラスコに、温度を７０℃に保持しながら２時間かけて滴下した。滴下終了後、さらに７０℃で３時間撹拌した。上記分析方法によりＧＰＣで反応溶液の組成を分析した結果、反応溶液中に存在する目的化合物の割合は、５１面積％であった。
　反応終了後、トルエン及び水を、７０℃の条件下、減圧蒸留によって除去した。蒸留時の圧力は徐々に減圧し、最終的に４．８ｋＰａとした。目的化合物を含む組成物を抜き取り、冷却固化後、粉砕して、６０℃、１．５ｋＰａ条件下で乾燥して、１７３ｇの目的化合物（純度５３％、目的化合物より高分子量の化合物４７面積％）を得た。
　１Ｈ－ＮＭＲの分析結果から、上記構造の目的化合物が得られたことを確認した。
　１Ｈ－ＮＭＲ分析（４００ＭＨｚ、溶媒：ＣＤＣｌ３、基準物質：テトラメチルシラン）
　２．４３－２．７２（２Ｈ，ｂｒｍ），２．７１－３．１６（４Ｈ，ｍ），３．４１－４．０９（１２Ｈ，ｍ），４．６９－５．０１（４Ｈ，ｍ），６．４９－７．０７（６Ｈ，ｍ）．
＜比較合成例１＞（下記化学式で表される比較例化合物Ａの合成）
Figure JPOXMLDOC01-appb-C000017
 　温度計、撹拌機、冷却管、滴下ロートを備えた１Ｌの４つ口フラスコにビスフェノールＡ１００ｇ（０．４４モル）、９４％パラホルムアルデヒド５６ｇ、トルエン１８４ｇを仕込み、反応容器内を窒素置換した後、混合溶液の温度を７０℃とした。その後、２－アミノエタノール５３ｇを滴下ロートで４つ口フラスコに、温度を７０℃に保持しながら２時間かけて滴下した。滴下終了後、さらに７０℃で９．５時間撹拌した。上記分析方法によりＧＰＣで反応溶液の組成を分析した結果、反応溶液中に存在する目的とする化合物の割合は、５２面積％であった。
　反応終了後、トルエン及び水を、７０℃の条件下、減圧蒸留によって除去した。蒸留時の圧力は徐々に減圧し、最終的に２０ｋＰａとした。比較例化合物Ａを含む組成物を抜き取り、１８７ｇの比較例化合物Ａ含有組成物（純度：５４％、比較例化合物Ａより高分子量の化合物４６面積％）を得た。
　１Ｈ－ＮＭＲの分析結果から、上記化学構造の比較例化合物Ａのベンゾオキサジン化合物が得られたことを確認した。
　１Ｈ－ＮＭＲ分析（４００ＭＨｚ、溶媒：ＣＤＣｌ３、基準物質：テトラメチルシラン）
　１．１４－１．９６（６Ｈ，ｍ），２．４５－２．７７（２Ｈ，ｂｒｍ），２．７８－３．１８（４Ｈ，ｍ），３．２８－４．１９（１０Ｈ，ｍ），４．７０－５．１４（４Ｈ，ｍ），６．５６－７．１３（６Ｈ，ｍ）.
＜比較合成例２＞
　ベンゾオキサジン化合物として汎用される、下記構造で表されるＦａ型ベンゾオキサジン化合物（比較例化合物Ｂ）を以下のとおり合成した。
Figure JPOXMLDOC01-appb-C000018
 　温度計、撹拌機、冷却管、滴下ロートを備えた１Ｌの４つ口フラスコにビスフェノールＦ８３ｇ（０．４１モル）、アニリン７７ｇ、９４％パラホルムアルデヒド５６ｇ、トルエン１５３ｇを仕込み、反応容器内を窒素置換した後、混合溶液の温度を９０℃とした。その後、温度を９０℃に保持しながら２時間撹拌した。上記分析方法によりＧＰＣで反応溶液の組成を分析した結果、反応溶液中に存在する目的とする比較例化合物Ｂの割合は、７１面積％であった。
　反応終了後、トルエン及び水を、９０℃の条件下、減圧蒸留によって除去した。蒸留時の圧力は徐々に減圧し、最終的に２０ｋＰａとした。比較例化合物Ｂを含む組成物を抜き取り、１７８ｇの比較例化合物Ｂ含有組成物（純度：６９％、比較例化合物Ｂより高分子量の化合物３１面積％）を得た。
（実施例１化合物の硬化物の試験片の作成方法）
比較例化合物ＡをＤＭＡ測定用シリコーン注型板に充填した。その後、乾燥機内（ＤＰ３２、ヤマト科学株式会社製）にて、１７５℃で２時間加熱して、その後冷却した。得られた板状の樹脂硬化物をサンドペーパーで表面を研磨することにより硬化物の試験片を作製した。
＜硬化特性評価、耐熱性評価＞
　上記実施例１と、比較合成例１及び比較合成例２で得られたそれぞれのベンゾオキサジン化合物について、上記分析方法に従い硬化特性評価及び硬化物の耐熱性評価（５％重量減少温度測定及びガラス転移温度（Ｔｇ）測定）を行った。
　その結果を、下記表１にまとめて示す。なお、表中の「－」は未測定であることを示し、比較例化合物Ｂのガラス転移温度（Ｔｇ）は、エレクトロニクス実装学会誌、第１４巻、第３号、第２０４～２１１頁、２０１１年に記載された数値を示す。
Figure JPOXMLDOC01-appb-T000019
　表１に示すとおり、本発明化合物である実施例１化合物は、比較例化合物Ａ及び汎用されるＦａ型ベンゾオキサジン化合物（比較例化合物Ｂ）よりも、低い温度で硬化することが明らかとなった。この結果は、本発明の一般式（１）で表される新規のベンゾオキサジン化合物を使用することで、熱硬化性樹脂の成型プロセスにおける温度を低下させることができ、加熱及び冷却の時間短縮や省エネルギー化による効率化が可能であるほか、熱に弱い材料（基材）にも使用できるため、非常に有用であることを示すものである。
　また、表１に示すとおり、本発明化合物である実施例１化合物の硬化物は、５％重量減少温度を対比すると、比較例化合物Ａの硬化物よりも耐熱性においても優れていることが明らかとなった。比較例化合物Ｂの硬化物と比べると実施例化合物１の硬化物は５％重量減少温度においては若干劣るものの、ベンゾオキサジン化合物が使用される用途において十分な耐熱性有していること、並びにガラス転移温度（Ｔｇ）においては優れていることが明らかとなった。
 

Claims (5)

  1. 　下記一般式（１）で表されるベンゾオキサジン化合物。
    Figure JPOXMLDOC01-appb-C000001
     （式中、Ｒ１は水素原子又は炭素原子数１～６のアルキル基を示し、Ｒ２は炭素原子数１～６のアルキレン基を示す。）
  2. 　請求項１に記載のベンゾオキサジン化合物を含む樹脂原料組成物。
  3. 　請求項１に記載のベンゾオキサジン化合物又は請求項２に記載の樹脂原料組成物を含む、硬化性樹脂組成物。
  4. 　請求項１に記載のベンゾオキサジン化合物又は請求項２に記載の樹脂原料組成物と、エポキシ樹脂、前記一般式（１）で表されるベンゾオキサジン化合物以外のベンゾオキサジン化合物、フェノール樹脂及びビスマレイミド化合物からなる群より選択される１種以上を含有する、請求項３に記載の硬化性樹脂組成物。
  5. 　請求項３又は４に記載の硬化性樹脂組成物を硬化させてなる硬化物。
     
PCT/JP2022/002311 2021-01-29 2022-01-24 新規なベンゾオキサジン化合物、それを含有する樹脂原料組成物、硬化性樹脂組成物及びその硬化物 Ceased WO2022163552A1 (ja)