WO2022024181A1 - Composition de résine thermodurcissable, bobine de stator et machine électrique rotative - Google Patents

Composition de résine thermodurcissable, bobine de stator et machine électrique rotative Download PDF

Info

Publication number
WO2022024181A1
WO2022024181A1 PCT/JP2020/028714 JP2020028714W WO2022024181A1 WO 2022024181 A1 WO2022024181 A1 WO 2022024181A1 JP 2020028714 W JP2020028714 W JP 2020028714W WO 2022024181 A1 WO2022024181 A1 WO 2022024181A1
Authority
WO
WIPO (PCT)
Prior art keywords
insulating layer
thermosetting resin
microfiller
organic
inorganic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2020/028714
Other languages
English (en)
Japanese (ja)
Inventor
暁紅 殷
貴裕 馬渕
壮平 鮫島
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitsubishi Electric Corp
Original Assignee
Mitsubishi Electric Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsubishi Electric Corp filed Critical Mitsubishi Electric Corp
Priority to JP2022539802A priority Critical patent/JP7262677B2/ja
Priority to PCT/JP2020/028714 priority patent/WO2022024181A1/fr
Publication of WO2022024181A1 publication Critical patent/WO2022024181A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

Composition de résine thermodurcissable contenant : une résine thermodurcissable (4) ; une micro-charge organique (5) ; et une nano-charge inorganique (6). La composition de résine thermodurcissable est utilisée pour fabriquer une couche d'isolation (3) pour une bobine de stator d'une machine électrique rotative. La surface de la micro-charge organique (5) est revêtue d'une couche inorganique. La bobine de stator comprend : un fil conducteur ; et la couche d'isolation (3) qui couvre le fil conducteur. La couche d'isolation (3) contient : la résine thermodurcissable (4) ; la micro-charge organique (5) ; et la nano-charge inorganique (6).
PCT/JP2020/028714 2020-07-27 2020-07-27 Composition de résine thermodurcissable, bobine de stator et machine électrique rotative Ceased WO2022024181A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
JP2022539802A JP7262677B2 (ja) 2020-07-27 2020-07-27 熱硬化性樹脂組成物、固定子コイルおよび回転電機
PCT/JP2020/028714 WO2022024181A1 (fr) 2020-07-27 2020-07-27 Composition de résine thermodurcissable, bobine de stator et machine électrique rotative

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/JP2020/028714 WO2022024181A1 (fr) 2020-07-27 2020-07-27 Composition de résine thermodurcissable, bobine de stator et machine électrique rotative

Publications (1)

Publication Number Publication Date
WO2022024181A1 true WO2022024181A1 (fr) 2022-02-03

Family

ID=80037812

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2020/028714 Ceased WO2022024181A1 (fr) 2020-07-27 2020-07-27 Composition de résine thermodurcissable, bobine de stator et machine électrique rotative

Country Status (2)

Country Link
JP (1) JP7262677B2 (fr)
WO (1) WO2022024181A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2023158851A (ja) * 2022-04-19 2023-10-31 東芝三菱電機産業システム株式会社 レジン製造方法及び絶縁構造製造方法

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015059148A (ja) * 2013-09-18 2015-03-30 三菱日立パワーシステムズ株式会社 電気絶縁樹脂とそれを用いた高電圧機器
JP2015228781A (ja) * 2014-06-03 2015-12-17 三菱電機株式会社 絶縁シートおよびこれを用いた電気機械
JP2015231322A (ja) * 2014-06-06 2015-12-21 三菱電機株式会社 マイカテープ及び固定子コイル
WO2018011904A1 (fr) * 2016-07-13 2018-01-18 三菱電機株式会社 Composition de résine thermodurcissable, bobine de stator obtenue avec cette composition, et machine dynamo-électrique
JP2018115273A (ja) * 2017-01-19 2018-07-26 日立金属株式会社 ワニス、並びに、エナメル線及び当該エナメル線を備えるコイル及び電機部品
WO2019077793A1 (fr) * 2017-10-18 2019-04-25 三菱電機株式会社 Matériau de revêtement isolant pour bobines de stator et machine rotative l'utilisant
JP2020045417A (ja) * 2018-09-19 2020-03-26 株式会社日立産機システム 電機機器

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015059148A (ja) * 2013-09-18 2015-03-30 三菱日立パワーシステムズ株式会社 電気絶縁樹脂とそれを用いた高電圧機器
JP2015228781A (ja) * 2014-06-03 2015-12-17 三菱電機株式会社 絶縁シートおよびこれを用いた電気機械
JP2015231322A (ja) * 2014-06-06 2015-12-21 三菱電機株式会社 マイカテープ及び固定子コイル
WO2018011904A1 (fr) * 2016-07-13 2018-01-18 三菱電機株式会社 Composition de résine thermodurcissable, bobine de stator obtenue avec cette composition, et machine dynamo-électrique
JP2018115273A (ja) * 2017-01-19 2018-07-26 日立金属株式会社 ワニス、並びに、エナメル線及び当該エナメル線を備えるコイル及び電機部品
WO2019077793A1 (fr) * 2017-10-18 2019-04-25 三菱電機株式会社 Matériau de revêtement isolant pour bobines de stator et machine rotative l'utilisant
JP2020045417A (ja) * 2018-09-19 2020-03-26 株式会社日立産機システム 電機機器

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2023158851A (ja) * 2022-04-19 2023-10-31 東芝三菱電機産業システム株式会社 レジン製造方法及び絶縁構造製造方法
JP7702374B2 (ja) 2022-04-19 2025-07-03 株式会社Tmeic レジン製造方法及び絶縁構造製造方法

Also Published As

Publication number Publication date
JPWO2022024181A1 (fr) 2022-02-03
JP7262677B2 (ja) 2023-04-21

Similar Documents

Publication Publication Date Title
US4760296A (en) Corona-resistant insulation, electrical conductors covered therewith and dynamoelectric machines and transformers incorporating components of such insulated conductors
CN103814415B (zh) 具有改进的抗局部放电性的绝缘体系及其制备方法
KR102572152B1 (ko) 코로나 저항성 폴리이미드 절연체를 갖는 자석 와이어
US20130131218A1 (en) Insulation for rotating electrical machines
CN103797544A (zh) 具有改进的抗局部放电性的绝缘体系及其制备方法
WO2015114907A1 (fr) Ruban isolant et son procédé de production, enroulement de stator et son procédé de production, et machine tournante électrique
JPWO2016104141A1 (ja) 絶縁テープ及びその製造方法、並びに固定子コイル及びその製造方法、並びに発電機
WO2011138413A2 (fr) Matériau d'isolation électrique et bande d'isolation pour une isolation électrique d'une moyenne tension/haute tension
JP2018026249A (ja) 絶縁電線、回転電機及び絶縁電線の製造方法
CN109415554B (zh) 热固化性树脂组合物及使用其的定子线圈、以及旋转电机
US20230318384A1 (en) Powder Coating Formulation for an Insulation System of an Electric Machine
JP7262677B2 (ja) 熱硬化性樹脂組成物、固定子コイルおよび回転電機
CN104185876B (zh) 旋转机械用的绝缘材料
US12406779B2 (en) Insulating system comprising a solid insulating material and impregnating resin
JP3567334B2 (ja) エポキシワニス組成物とその使用方法
JP6275056B2 (ja) 絶縁樹脂組成物、絶縁部材、回転電機及び発電機
JPH0331738B2 (fr)
CN105102536A (zh) 用于高压旋转式机械的电绝缘体以及制造该电绝缘体的方法
JPWO2019077793A1 (ja) 固定子コイルの絶縁被覆材およびそれを用いた回転機
KR102518139B1 (ko) 고함량의 세라믹을 가지는 변성 pai 절연바니쉬가 다층 구조로 코팅된 각형 코일 및 이의 제조방법
US12417861B2 (en) Insulating system made of solid insulating material and impregnating resin
CA1168857A (fr) Compositions a base de resine s'opposant a l'effet de couronne
JP4499353B2 (ja) 回転電機のための超誘電耐高圧絶縁体
WO2018003044A1 (fr) Bobine pour machine électrique tournante, procédé de fabrication de bobine pour machine électrique tournante, bande de mica, produit durci de bande de mica, et matériau isolant
US11916448B2 (en) Small-fraction nanoparticle resin for electric machine insulation systems

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20947025

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2022539802

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20947025

Country of ref document: EP

Kind code of ref document: A1