WO2021005020A1 - Procédé de flottation d'un minerai de fer contenant du silicate avec un collecteur d'amidoamine - Google Patents

Procédé de flottation d'un minerai de fer contenant du silicate avec un collecteur d'amidoamine Download PDF

Info

Publication number
WO2021005020A1
WO2021005020A1 PCT/EP2020/069040 EP2020069040W WO2021005020A1 WO 2021005020 A1 WO2021005020 A1 WO 2021005020A1 EP 2020069040 W EP2020069040 W EP 2020069040W WO 2021005020 A1 WO2021005020 A1 WO 2021005020A1
Authority
WO
WIPO (PCT)
Prior art keywords
formula
compound
linear
flotation
ore
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP2020/069040
Other languages
English (en)
Inventor
Gabriela BUDEMBERG
Alexej Michailovski
Andre SOARES BRAGA
Gustavo RODRIGUES DOS SANTOS
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BASF SE
Original Assignee
BASF SE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BASF SE filed Critical BASF SE
Priority to BR112021024703A priority Critical patent/BR112021024703A2/pt
Publication of WO2021005020A1 publication Critical patent/WO2021005020A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne un procédé de fabrication d'un concentré enrichi en minerai de fer à partir d'un minerai, qui contient un minéral de fer et du silicate, par une flottation inverse, ledit procédé comprenant l'étape consistant à (c) ajouter un composé de formule (I) dans laquelle R1 représente un alcényle en C17, un alkyle en C17 linéaire ou un alkyle en C15 linéaire, ou un sel d'un composé protoné de formule (I) et un anion, à une pâte aqueuse préparée du minerai et éventuellement un ou plusieurs auxiliaires de flottation pour obtenir un mélange aqueux. Par exemple, un mélange de composés de formule (I) obtenus par réaction d'acides gras d'huile de soja avec N',N'-diméthylpropane-1,3-diamine est employé.
PCT/EP2020/069040 2019-07-11 2020-07-06 Procédé de flottation d'un minerai de fer contenant du silicate avec un collecteur d'amidoamine Ceased WO2021005020A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
BR112021024703A BR112021024703A2 (pt) 2019-07-11 2020-07-06 Método para fabricar um concentrado enriquecido em teor de mineral de ferro de um minério, e, uso de um composto

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP19185803 2019-07-11
EP19185803.4 2019-07-11

Publications (1)

Publication Number Publication Date
WO2021005020A1 true WO2021005020A1 (fr) 2021-01-14

Family

ID=67253791

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2020/069040 Ceased WO2021005020A1 (fr) 2019-07-11 2020-07-06 Procédé de flottation d'un minerai de fer contenant du silicate avec un collecteur d'amidoamine

Country Status (2)

Country Link
BR (1) BR112021024703A2 (fr)
WO (1) WO2021005020A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022144281A1 (fr) 2021-01-04 2022-07-07 Basf Se Procédé de flottation d'un minerai de fer contenant du silicate
WO2022152538A1 (fr) 2021-01-12 2022-07-21 Basf Se Procédé de flottation d'un minerai de fer contenant du silicate

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20140048454A1 (en) 2012-08-20 2014-02-20 Ceca S.A. Collectors for ore beneficiation
US20140048453A1 (en) 2012-08-20 2014-02-20 Ceca S.A. Collectors for ore beneficiation
US20140144290A1 (en) 2012-11-28 2014-05-29 Georgia-Pacific Chemicals Llc Mixed collector compositions
US20150096925A1 (en) 2013-10-09 2015-04-09 Georgia-Pacific Chemicals Llc Collector compositions and methods for making and using same

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20140048454A1 (en) 2012-08-20 2014-02-20 Ceca S.A. Collectors for ore beneficiation
US20140048453A1 (en) 2012-08-20 2014-02-20 Ceca S.A. Collectors for ore beneficiation
US20140144290A1 (en) 2012-11-28 2014-05-29 Georgia-Pacific Chemicals Llc Mixed collector compositions
US20150096925A1 (en) 2013-10-09 2015-04-09 Georgia-Pacific Chemicals Llc Collector compositions and methods for making and using same

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022144281A1 (fr) 2021-01-04 2022-07-07 Basf Se Procédé de flottation d'un minerai de fer contenant du silicate
WO2022152538A1 (fr) 2021-01-12 2022-07-21 Basf Se Procédé de flottation d'un minerai de fer contenant du silicate

Also Published As

Publication number Publication date
BR112021024703A2 (pt) 2022-02-08

Similar Documents

Publication Publication Date Title
US20250269387A1 (en) Method for flotation of a silicate-containing iron ore with a cationic collector
US20160114338A1 (en) Cationic collectors with mixed polyamidoamines and methods for making and using same
US20160114337A1 (en) Polyamidoamine cationic collectors and methods for making and using same
WO2021005020A1 (fr) Procédé de flottation d'un minerai de fer contenant du silicate avec un collecteur d'amidoamine
WO2012139986A2 (fr) Composés d'amine et de diamine et leur utilisation pour une flottation par moussage inverse de silicate à partir de minerai de fer
US4545898A (en) Process for froth flotation
CA3079763C (fr) Esterquats pour la flottation de mineraux et minerais non sulfures et procede de flottation
US4305815A (en) Conditioner for flotation of oxidized coal
US4276156A (en) Froth flotation process using condensates of hydroxyethylethylenediamines as collectors for siliceous material
EP4196281B1 (fr) Procédé de flottation d'un minerai de fer contenant du silicate
EP0016914B1 (fr) Condensé d'acide gras, d'alkanolamine comme conditionneur pour la flottation du charbon et un procédé de flottation utilisant ce condensé
CN114367383A (zh) 一种脂肪酸酯纳米悬浮液、其制备方法和应用
US4892649A (en) Calcium carbonate beneficiation
SE462371B (sv) Saett foer separation av mineral fraan gaangarter genom skumflotation
SE2450839A1 (en) Novel Cationic Collectors for Improving a Process for Froth Flotation of Silicates
AU2020265097B2 (en) Method for flotation of a silicate-containing iron ore with a cationic collector
CA3203534A1 (fr) Procede de flottation d'un minerai de fer contenant du silicate
BR112023013235B1 (pt) Método para fabricar um concentrado, uso de uma composição de coletor, e, composição de coletor
EA043320B1 (ru) Способ флотации силикатсодержащей железной руды с использованием катионного собирателя
GB2110958A (en) Froth floatation of coal
EP4026620A1 (fr) Procédé de flottation d'un minerai de fer contenant du silicate
US20230302464A1 (en) Novel Cationic Collectors for Improving a Process for Froth Flotation of Silicates
EA048737B1 (ru) Способ производства концентрата, обогащенного железосодержащим минералом, из руды с использованием аминов, применение аминов и их неклейкая композиция

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20735227

Country of ref document: EP

Kind code of ref document: A1

REG Reference to national code

Ref country code: BR

Ref legal event code: B01A

Ref document number: 112021024703

Country of ref document: BR

ENP Entry into the national phase

Ref document number: 112021024703

Country of ref document: BR

Kind code of ref document: A2

Effective date: 20211207

122 Ep: pct application non-entry in european phase

Ref document number: 20735227

Country of ref document: EP

Kind code of ref document: A1