WO2020123039A1 - Mousses de polysiloxane soufflé au gaz imprimées en trois dimensions - Google Patents

Mousses de polysiloxane soufflé au gaz imprimées en trois dimensions Download PDF

Info

Publication number
WO2020123039A1
WO2020123039A1 PCT/US2019/057488 US2019057488W WO2020123039A1 WO 2020123039 A1 WO2020123039 A1 WO 2020123039A1 US 2019057488 W US2019057488 W US 2019057488W WO 2020123039 A1 WO2020123039 A1 WO 2020123039A1
Authority
WO
WIPO (PCT)
Prior art keywords
ink
porosity
recited
polysiloxane
filament
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2019/057488
Other languages
English (en)
Inventor
Andrew Neil Mabe
Eric B. Duoss
Jeremy LENHARDT
Du Nguyen
Thomas S. Wilson
Alexandra Golobic
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lawrence Livermore National Security LLC
Original Assignee
Lawrence Livermore National Security LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lawrence Livermore National Security LLC filed Critical Lawrence Livermore National Security LLC
Publication of WO2020123039A1 publication Critical patent/WO2020123039A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne, selon un aspect, une formulation d'encre pour former un produit de polysiloxane soufflé au gaz comprend un polysiloxane comprenant au moins un groupe vinyle, un agent de réticulation à base de silane, un catalyseur, un agent de soufflage au gaz et un agent thixotrope. Selon un autre aspect de l'invention, un produit comprend une structure de polymère imprimé en trois dimensions formée à partir d'au moins un filament. La structure de polymère imprimé en trois dimensions comporte une pluralité de couches disposées selon un motif géométrique, les couches étant formées à partir du ou des filament(s), le ou les filament(s) comprenant un matériau polysiloxane comportant une pluralité de pores de cellule fermés formés à l'intérieur de ce dernier.
PCT/US2019/057488 2018-12-14 2019-10-22 Mousses de polysiloxane soufflé au gaz imprimées en trois dimensions Ceased WO2020123039A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US201862780070P 2018-12-14 2018-12-14
US62/780,070 2018-12-14
US16/659,025 2019-10-21
US16/659,025 US20200190345A1 (en) 2018-12-14 2019-10-21 Three dimensional printed gas blown polysiloxane foams

Publications (1)

Publication Number Publication Date
WO2020123039A1 true WO2020123039A1 (fr) 2020-06-18

Family

ID=71073326

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2019/057488 Ceased WO2020123039A1 (fr) 2018-12-14 2019-10-22 Mousses de polysiloxane soufflé au gaz imprimées en trois dimensions

Country Status (2)

Country Link
US (2) US20200190345A1 (fr)
WO (1) WO2020123039A1 (fr)

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019006029A1 (fr) 2017-06-27 2019-01-03 Lawrence Livermore National Security, Llc Composites polymères à mémoire de forme élastomère
US11787886B2 (en) * 2020-10-15 2023-10-17 Ahmed Ben Amor Tarfaoui Single step foamed polymeric material characterised by the presence of two or more cellular layers and aggregates that exhibit variation in cell size and cell density distribution
JP7658162B2 (ja) * 2021-05-17 2025-04-08 セイコーエプソン株式会社 可塑化装置、三次元造形装置、および射出成形装置

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3393260A (en) * 1965-04-27 1968-07-16 Baker Perkins Inc Process for preparing foam products
US4189545A (en) * 1978-03-13 1980-02-19 General Electric Company Silicone foam composition which has burn resistant properties
US4555529A (en) * 1985-03-25 1985-11-26 Dow Corning Corporation Foamable polyorganosiloxane compositions
US4576999A (en) * 1982-05-06 1986-03-18 General Electric Company Ultraviolet radiation-curable silicone release compositions with epoxy and/or acrylic functionality
US4833175A (en) * 1988-07-21 1989-05-23 Polyvoltac Canada Inc. Mixing process
US20140374905A1 (en) * 2013-06-19 2014-12-25 Shin-Etsu Chemical Co., Ltd. Formation of conductive circuit, conductive circuit, and conductive ink composition
US20170283655A1 (en) * 2014-09-17 2017-10-05 Dow Corning Corporation 3d printing method utilizing a photocurable silicone composition
WO2018183803A1 (fr) * 2017-03-30 2018-10-04 Dow Silicones Corporation Procédé de préparation d'un article en silicone poreux et utilisation de cet article en silicone

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2803606A (en) * 1954-03-12 1957-08-20 Dow Corning Powdered siloxane resin and process of preparing cellular resin therefrom
US4255527A (en) * 1979-07-19 1981-03-10 George F. Thagard, Jr. Novel blowing agent for polymeric foam process
US8900491B2 (en) * 2011-05-06 2014-12-02 International Business Machines Corporation Flame retardant filler
CN106751906B (zh) * 2016-12-28 2019-09-17 中国工程物理研究院化工材料研究所 具有可控多尺度孔结构硅橡胶泡沫的制备方法
EP3403806A1 (fr) * 2017-05-18 2018-11-21 Ecole Polytechnique Federale De Lausanne (Epfl) Structure poreuse hiérarchique
US20200317870A1 (en) * 2019-04-04 2020-10-08 Lawrence Livermore National Security, Llc Curable polymer resins for 3d-printable hierarchical nanoporous foams and aerogels
US11725112B2 (en) * 2020-02-28 2023-08-15 Lawrence Livermore National Security, Llc Three-dimensional printed porous silicone matrix using leachable porogen
US12195634B2 (en) * 2020-04-17 2025-01-14 Lawrence Livermore National Security, Llc Optically transparent 3D printed polysiloxane scintillators
US12331204B2 (en) * 2020-10-20 2025-06-17 Lawrence Livermore National Security, Llc Transparent 3D printed siloxane elastomers

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3393260A (en) * 1965-04-27 1968-07-16 Baker Perkins Inc Process for preparing foam products
US4189545A (en) * 1978-03-13 1980-02-19 General Electric Company Silicone foam composition which has burn resistant properties
US4576999A (en) * 1982-05-06 1986-03-18 General Electric Company Ultraviolet radiation-curable silicone release compositions with epoxy and/or acrylic functionality
US4555529A (en) * 1985-03-25 1985-11-26 Dow Corning Corporation Foamable polyorganosiloxane compositions
US4833175A (en) * 1988-07-21 1989-05-23 Polyvoltac Canada Inc. Mixing process
US20140374905A1 (en) * 2013-06-19 2014-12-25 Shin-Etsu Chemical Co., Ltd. Formation of conductive circuit, conductive circuit, and conductive ink composition
US20170283655A1 (en) * 2014-09-17 2017-10-05 Dow Corning Corporation 3d printing method utilizing a photocurable silicone composition
WO2018183803A1 (fr) * 2017-03-30 2018-10-04 Dow Silicones Corporation Procédé de préparation d'un article en silicone poreux et utilisation de cet article en silicone

Also Published As

Publication number Publication date
US20200190345A1 (en) 2020-06-18
US20230383131A1 (en) 2023-11-30

Similar Documents

Publication Publication Date Title
US20230383131A1 (en) Three-dimensional printed gas blown polysiloxane foams
CN104755542B (zh) 有机硅组合物及相关方法
JP6017433B2 (ja) 発泡材料の製造方法、その方法において使用されるエマルション状組成物、およびその方法から得ることができる発泡材料
RU2566502C2 (ru) Способ изготовления полиуретановой пены и получаемая при этом полиуретановая пена
RU2458078C2 (ru) Гибридный материал, содержащий вспененный полимер и неорганическое связующее, имеющий регулируемую плотность и морфологию, способ его получения и применение
CN104530712B (zh) 一种小孔径硅橡胶海绵及制备方法
US20200315975A1 (en) Three-dimensional printed structural siloxanes having controlled drug release
JP6565850B2 (ja) 高連泡シリコーンゴムスポンジの製造方法及び高連泡シリコーンゴムスポンジ用液状シリコーンゴム組成物並びにシリコーンゴムスポンジ
Wu et al. Large-scale and facile fabrication of phenyl-containing silicone foam materials with lightweight, wide-temperature flexibility and tunable pore structure for exceptional thermal insulation
Abshirini et al. Synthesis and characterization of hierarchical porous structure of polydimethylsiloxane (PDMS) sheets via two-step phase separation method
Métivier et al. New trends in cellular silicone: Innovations and applications
EP1423471B1 (fr) Composition de caoutchouc de silicone liquide presentant une gravite specifique basse et article moule
US20220064463A1 (en) Three dimensional porous siloxanes using leachable porogen particles
Cai et al. Preparation of open-cell rigid polyimide foam via nonaqueous high internal phase emulsion-templating technique
US20230250303A1 (en) Three-dimensional printed porous silicone matrix using leachable porogen
TW201915072A (zh) 氮化硼發泡體、其製造方法、及含氮化硼發泡體之製品
JP2019172953A (ja) 油水分離用スポンジ及び油水分離用スポンジ製造用組成物
KR20010098825A (ko) 실리콘 고무 스폰지 형성성 조성물, 실리콘 고무 스폰지및 실리콘 고무 스폰지의 제조방법
JP6338211B2 (ja) ポリスチレン・シリカコンポジット発泡体の製造方法およびそれを用いた断熱材料
Golobic et al. Controlled In Situ Foaming for Mechanical Responsiveness of Architected Foams
JP2024541193A (ja) 難燃性多層材料、その製造方法、及び使用
Strachota et al. Foaming of polysiloxane resins with ethanol: A new route to pyrolytic macrocellular SiOC foams
US20240279467A1 (en) Low density room temperature vulcanizable polysiloxane rubber composition compatible with high-resolution molding operations
Frankowski et al. Tunable microcellular morphologies from poly (ferrocenylsilane) ceramic precursors foamed in supercritical CO2
JP4987463B2 (ja) 発泡熱可塑性樹脂の製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19896152

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19896152

Country of ref document: EP

Kind code of ref document: A1