WO2020121745A1 - Copolymère, procédé de production de copolymère, composition de caoutchouc, pneu, composition de résine et produit résineux - Google Patents

Copolymère, procédé de production de copolymère, composition de caoutchouc, pneu, composition de résine et produit résineux Download PDF

Info

Publication number
WO2020121745A1
WO2020121745A1 PCT/JP2019/045163 JP2019045163W WO2020121745A1 WO 2020121745 A1 WO2020121745 A1 WO 2020121745A1 JP 2019045163 W JP2019045163 W JP 2019045163W WO 2020121745 A1 WO2020121745 A1 WO 2020121745A1
Authority
WO
WIPO (PCT)
Prior art keywords
copolymer
catalyst
compound
aromatic vinyl
group
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2019/045163
Other languages
English (en)
Japanese (ja)
Inventor
重永 高野
オリビエ タルディフ
文 堀田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bridgestone Corp
Original Assignee
Bridgestone Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bridgestone Corp filed Critical Bridgestone Corp
Priority to JP2020559881A priority Critical patent/JPWO2020121745A1/ja
Publication of WO2020121745A1 publication Critical patent/WO2020121745A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne : un copolymère de composé vinylique aromatique/composé de diène conjugué qui présente une faible température de transition vitreuse (Tg) tout en présentant une teneur en composé vinylique aromatique lié et une teneur en liaison vinylique qui sont sensiblement identiques à celles de copolymères classiques et qui satisfait à une relation donnée ; un procédé de production du copolymère ; une composition de caoutchouc et une composition de résine comprenant chacune le copolymère ; un pneu obtenu en faisant appel à la composition de caoutchouc ; et un produit résineux obtenu en faisant appel à la composition de résine.
PCT/JP2019/045163 2018-12-12 2019-11-19 Copolymère, procédé de production de copolymère, composition de caoutchouc, pneu, composition de résine et produit résineux Ceased WO2020121745A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2020559881A JPWO2020121745A1 (ja) 2018-12-12 2019-11-19 共重合体、共重合体の製造方法、ゴム組成物、タイヤ、樹脂組成物及び樹脂製品

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2018-232734 2018-12-12
JP2018232734 2018-12-12

Publications (1)

Publication Number Publication Date
WO2020121745A1 true WO2020121745A1 (fr) 2020-06-18

Family

ID=71076901

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2019/045163 Ceased WO2020121745A1 (fr) 2018-12-12 2019-11-19 Copolymère, procédé de production de copolymère, composition de caoutchouc, pneu, composition de résine et produit résineux

Country Status (2)

Country Link
JP (1) JPWO2020121745A1 (fr)
WO (1) WO2020121745A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20220220238A1 (en) * 2019-06-21 2022-07-14 Bridgestone Corporation Method for manufacturing copolymer

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2009148140A1 (fr) * 2008-06-04 2009-12-10 株式会社ブリヂストン Copolymère composé vinyle aromatique-composé diène conjugué, son procédé de fabrication, composition de caoutchouc et pneu
JP2016047889A (ja) * 2014-08-27 2016-04-07 横浜ゴム株式会社 タイヤ用ゴム組成物および空気入りタイヤ
WO2016060262A1 (fr) * 2014-10-17 2016-04-21 日本ゼオン株式会社 Composition de caoutchouc pour pneumatique
JP2017088864A (ja) * 2015-11-04 2017-05-25 住友ゴム工業株式会社 加硫ゴム組成物およびそれを用いたタイヤ
WO2017104423A1 (fr) * 2015-12-15 2017-06-22 株式会社ブリヂストン Composition de caoutchouc et pneu
JP2018532743A (ja) * 2015-10-21 2018-11-08 トリンゼオ ヨーロッパ ゲゼルシャフト ミット ベシュレンクテル ハフツング エラストマー系ポリマーの官能化に使用されるアミノシラン官能化ジエン

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2009148140A1 (fr) * 2008-06-04 2009-12-10 株式会社ブリヂストン Copolymère composé vinyle aromatique-composé diène conjugué, son procédé de fabrication, composition de caoutchouc et pneu
JP2016047889A (ja) * 2014-08-27 2016-04-07 横浜ゴム株式会社 タイヤ用ゴム組成物および空気入りタイヤ
WO2016060262A1 (fr) * 2014-10-17 2016-04-21 日本ゼオン株式会社 Composition de caoutchouc pour pneumatique
JP2018532743A (ja) * 2015-10-21 2018-11-08 トリンゼオ ヨーロッパ ゲゼルシャフト ミット ベシュレンクテル ハフツング エラストマー系ポリマーの官能化に使用されるアミノシラン官能化ジエン
JP2017088864A (ja) * 2015-11-04 2017-05-25 住友ゴム工業株式会社 加硫ゴム組成物およびそれを用いたタイヤ
WO2017104423A1 (fr) * 2015-12-15 2017-06-22 株式会社ブリヂストン Composition de caoutchouc et pneu

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20220220238A1 (en) * 2019-06-21 2022-07-14 Bridgestone Corporation Method for manufacturing copolymer
US12152096B2 (en) * 2019-06-21 2024-11-26 Bridgestone Corporation Method for manufacturing copolymer

Also Published As

Publication number Publication date
JPWO2020121745A1 (ja) 2021-10-28

Similar Documents

Publication Publication Date Title
EP3184554B1 (fr) Procédé de fabrication de polymère de diène conjugué à extrémité modifiée, polymère de diène conjugué à extrémité modifiée, composition de caoutchouc, et pneu
JP5941302B2 (ja) ゴム組成物、及び、前記ゴム組成物を有するタイヤ
JP6713759B2 (ja) 多元共重合体の製造方法及び多元共重合体
WO2019171679A1 (fr) Copolymère, procédé de production d'un copolymère, composition de caoutchouc et pneumatique
KR101781699B1 (ko) 공액 디엔의 중합용 촉매 조성물
JP6055827B2 (ja) ポリブタジエンの製造方法、ポリブタジエン、ゴム組成物及びタイヤ
JP5899011B2 (ja) 重合体、前記重合体を含むゴム組成物、及び、前記ゴム組成物を有するタイヤ
KR101796360B1 (ko) 공액 디엔계 중합체의 제조방법
JP2013185059A (ja) 重合体及びその製造方法、前記重合体を含むゴム組成物、並びに、前記ゴム組成物を有するタイヤ
EP3680265B1 (fr) Procédé de production d'un copolymère, copolymère, composition de caoutchouc, et pneumatique
WO2020121745A1 (fr) Copolymère, procédé de production de copolymère, composition de caoutchouc, pneu, composition de résine et produit résineux
JP7041585B2 (ja) 重合触媒、及び、共重合体の製造方法
CN108290972A (zh) 聚合催化剂组合物、和共轭二烯系聚合物的制造方法
JP7431817B2 (ja) 多元共重合体、ゴム組成物、樹脂組成物、タイヤ及び樹脂製品
JP2019151817A (ja) 共重合体、共重合体の製造方法、ゴム組成物及びタイヤ
JP5656686B2 (ja) ゴム組成物、架橋ゴム組成物、及びタイヤ
JP2016113496A (ja) ゴム組成物、及び該ゴム組成物を用いたタイヤ
JP7490442B2 (ja) グラフトポリマー、グラフトポリマーの製造方法、ゴム組成物及びタイヤ
JP7009307B2 (ja) 重合触媒、及び、共重合体の製造方法
JP7244432B2 (ja) 共重合体、共重合体の製造方法、ゴム組成物及びタイヤ
WO2022123993A1 (fr) Copolymère, composition de gomme et composition de résine
JP2022090555A (ja) 共重合体、ゴム組成物及び樹脂組成物
JP2013154618A (ja) ゴム製品の加硫用ブラダー
JP2021175771A (ja) グラフトポリマーの製造方法、グラフトポリマー、ゴム組成物及びタイヤ
JP2013159637A (ja) ゴム組成物及びタイヤ

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19894576

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2020559881

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19894576

Country of ref document: EP

Kind code of ref document: A1