WO2019101713A1 - Verre de sécurité feuilleté fonctionnalisé et son procédé de fabrication - Google Patents

Verre de sécurité feuilleté fonctionnalisé et son procédé de fabrication Download PDF

Info

Publication number
WO2019101713A1
WO2019101713A1 PCT/EP2018/081858 EP2018081858W WO2019101713A1 WO 2019101713 A1 WO2019101713 A1 WO 2019101713A1 EP 2018081858 W EP2018081858 W EP 2018081858W WO 2019101713 A1 WO2019101713 A1 WO 2019101713A1
Authority
WO
WIPO (PCT)
Prior art keywords
adhesive layer
thickness
glass
less
laminate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP2018/081858
Other languages
English (en)
Inventor
Florian MUMMY
Felix BIER
Robert Fuss
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kuraray Europe GmbH
Original Assignee
Kuraray Europe GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kuraray Europe GmbH filed Critical Kuraray Europe GmbH
Publication of WO2019101713A1 publication Critical patent/WO2019101713A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un stratifié comprenant des couches dans la séquence : une première feuille de verre présentant une épaisseur inférieure ou égale à 2,5 mm, de préférence inférieure ou égale à 2,1 mm ; une première couche adhésive ; une deuxième feuille de verre présentant une épaisseur inférieure ou égale à 2,5 mm, de préférence inférieure ou égale à 2,1 mm ou 1,8 mm ou 1,6 mm ; une couche fonctionnelle ; une deuxième couche adhésive ; une troisième feuille de verre présentant une épaisseur inférieure à 2,0 mm.
PCT/EP2018/081858 2017-11-27 2018-11-20 Verre de sécurité feuilleté fonctionnalisé et son procédé de fabrication Ceased WO2019101713A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE102016108685.1 2017-11-27
DE102016108685 2017-11-27

Publications (1)

Publication Number Publication Date
WO2019101713A1 true WO2019101713A1 (fr) 2019-05-31

Family

ID=64426921

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2018/081858 Ceased WO2019101713A1 (fr) 2017-11-27 2018-11-20 Verre de sécurité feuilleté fonctionnalisé et son procédé de fabrication

Country Status (1)

Country Link
WO (1) WO2019101713A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE102020206686A1 (de) 2020-05-28 2021-12-02 Volkswagen Aktiengesellschaft Verbundglasscheibe mit einer Scheibenheizung
US20220288895A1 (en) * 2019-08-30 2022-09-15 Central Glass Company, Limited Laminated glazing having holographic film laminated therein
WO2023155431A1 (fr) * 2022-09-21 2023-08-24 福耀玻璃工业集团股份有限公司 Verre feuilleté et véhicule

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20050002081A1 (en) * 2001-09-14 2005-01-06 Fabien Beteille Functional safety glazing unit
DE102006042538A1 (de) * 2006-09-11 2008-03-27 Futech Gmbh Verbundglas, Verglasungselement und Verfahren zu deren Herstellung
US20090311497A1 (en) * 2006-09-14 2009-12-17 Nippon Electric Glass Co., Ltd. Sheet glass laminate structure and mulitiple glass laminate structure
WO2017094884A1 (fr) * 2015-12-04 2017-06-08 旭硝子株式会社 Verre feuilleté pour véhicules

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20050002081A1 (en) * 2001-09-14 2005-01-06 Fabien Beteille Functional safety glazing unit
DE102006042538A1 (de) * 2006-09-11 2008-03-27 Futech Gmbh Verbundglas, Verglasungselement und Verfahren zu deren Herstellung
US20090311497A1 (en) * 2006-09-14 2009-12-17 Nippon Electric Glass Co., Ltd. Sheet glass laminate structure and mulitiple glass laminate structure
WO2017094884A1 (fr) * 2015-12-04 2017-06-08 旭硝子株式会社 Verre feuilleté pour véhicules
EP3385238A1 (fr) * 2015-12-04 2018-10-10 AGC Inc. Verre feuilleté pour véhicules

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20220288895A1 (en) * 2019-08-30 2022-09-15 Central Glass Company, Limited Laminated glazing having holographic film laminated therein
DE102020206686A1 (de) 2020-05-28 2021-12-02 Volkswagen Aktiengesellschaft Verbundglasscheibe mit einer Scheibenheizung
WO2023155431A1 (fr) * 2022-09-21 2023-08-24 福耀玻璃工业集团股份有限公司 Verre feuilleté et véhicule

Similar Documents

Publication Publication Date Title
US10946619B2 (en) Laminated glass comprising a functional film
CN100371166C (zh) 压花反射层压板
EP2097931B1 (fr) Cellules solaires comprenant l'utilisation de certaines couches d'encapsulation de poly(butyral de vinyle)/film bicouche ayant une faible tendance au blocage et procédé simplifié pour les produire
EP2118179B1 (fr) Compositions ionomères à indice de fluidité élevé
US10105932B2 (en) Process for producing laminated glass composites with embedded electrically conductive structures
US20210138767A1 (en) Laminated glazing with a switchable liquid crystal layer
KR101557172B1 (ko) 다층 필름 또는 시트, 및 그 필름 또는 시트를 포함하는 용품
JP6726151B2 (ja) 熱線遮蔽特性を有する合わせガラス積層体を製造する方法
JP6698427B2 (ja) 接着性が低減され、かつ可塑剤含分が低い中間フィルム層を用いて作製された、耐貫通性合わせガラス
MXPA02003874A (es) Metodo y pelicula para producir hojas de vidrio laminadas de seguridad.
JP2018052810A (ja) 可塑剤含有ポリビニルアセタールシートと、可塑剤の少ないポリビニルアセタールシートとを有する層体から、合わせガラス積層体を製造する方法
JP2011507278A (ja) ターイオノマーフィルムまたはシートおよびそれを含む太陽電池モジュール
JP2014518837A5 (fr)
WO2007029541A1 (fr) Procédé de production d’un verre stratifié constitué partiellement d'une plaque de plastique, et verre stratifié
CN107107570A (zh) 用于制备具有在载体箔上的红外反射涂层的复合玻璃板的方法
US8097114B2 (en) Glass laminate containing ionomer
JP2018052809A (ja) 可塑剤を含まないポリビニルアセタールからなる薄いシートをベースとする、熱線遮蔽特性を有する合わせガラス積層体
EP3535122B1 (fr) Procédé de fabrication d'un verre stratifié comprenant un film fonctionnel
WO2019101713A1 (fr) Verre de sécurité feuilleté fonctionnalisé et son procédé de fabrication
WO2018210900A1 (fr) Verre de sécurité feuilleté fonctionnalisé et son procédé de fabrication
WO2004009354A1 (fr) Lamine de verre
US11207868B2 (en) Method for producing a laminated pane
CN113165370B (zh) 用于制造具有功能元件的复合玻璃板的方法
CN112004785A (zh) 车辆用轻质夹层玻璃板的制造方法
JP2024135705A (ja) 合わせガラス用太陽電池モジュール及びその製造方法、並びに、合わせガラス及びその製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18807286

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18807286

Country of ref document: EP

Kind code of ref document: A1