WO2019175064A1 - Produit d'isolation et son procédé de fabrication - Google Patents

Produit d'isolation et son procédé de fabrication Download PDF

Info

Publication number
WO2019175064A1
WO2019175064A1 PCT/EP2019/055923 EP2019055923W WO2019175064A1 WO 2019175064 A1 WO2019175064 A1 WO 2019175064A1 EP 2019055923 W EP2019055923 W EP 2019055923W WO 2019175064 A1 WO2019175064 A1 WO 2019175064A1
Authority
WO
WIPO (PCT)
Prior art keywords
foam
envelope
insulation
mbar
insulation core
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/EP2019/055923
Other languages
English (en)
Inventor
Daniel Mack
Bahadir ÖZSOYLU
Ruud Zeggelaar
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kingspan Holdings IRL Ltd
Original Assignee
Kingspan Holdings IRL Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kingspan Holdings IRL Ltd filed Critical Kingspan Holdings IRL Ltd
Publication of WO2019175064A1 publication Critical patent/WO2019175064A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

La présente invention concerne un produit d'isolation comprenant un noyau d'isolation en mousse enveloppé dans une enveloppe étanche aux gaz ayant une atmosphère à pression réduite retenue à l'intérieur de cellules ouvertes du noyau d'isolation en mousse. L'invention concerne également des procédés de fabrication de ceux-ci.
PCT/EP2019/055923 2018-03-12 2019-03-08 Produit d'isolation et son procédé de fabrication Ceased WO2019175064A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
GB1803941.2 2018-03-12
GB1803941.2A GB2571940B (en) 2018-03-12 2018-03-12 An insulation product and method for manufacturing same

Publications (1)

Publication Number Publication Date
WO2019175064A1 true WO2019175064A1 (fr) 2019-09-19

Family

ID=61972751

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2019/055923 Ceased WO2019175064A1 (fr) 2018-03-12 2019-03-08 Produit d'isolation et son procédé de fabrication

Country Status (2)

Country Link
GB (1) GB2571940B (fr)
WO (1) WO2019175064A1 (fr)

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4444912A (en) 1981-07-10 1984-04-24 Koppers Company, Inc. Phenolic foam and composition and method for preparing the same
JP2002174485A (ja) * 2000-12-08 2002-06-21 Hitachi Ltd 冷蔵庫
WO2007029221A1 (fr) 2005-09-08 2007-03-15 Kingspan Holdings (Irl) Limited Mousse phenolique
WO2008118627A2 (fr) 2007-03-27 2008-10-02 Dow Global Technologies Inc. Agents d'expansion à base d'alcène fluoré pour mousse polymère de qualité
JP2011056882A (ja) * 2009-09-14 2011-03-24 Keisuke Kasahara ビーズ法ポリスチレン発泡体を用いた真空発泡断熱体及び芯材の製造方法とその方法による真空発泡断熱体
EP2752397A1 (fr) 2011-08-31 2014-07-09 LG Hausys, Ltd. Matériau d'isolation sous vide incluant un agent absorbant de composés

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0972488A (ja) * 1995-08-31 1997-03-18 Sekisui Plastics Co Ltd 真空断熱体及びその製造方法

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4444912A (en) 1981-07-10 1984-04-24 Koppers Company, Inc. Phenolic foam and composition and method for preparing the same
JP2002174485A (ja) * 2000-12-08 2002-06-21 Hitachi Ltd 冷蔵庫
WO2007029221A1 (fr) 2005-09-08 2007-03-15 Kingspan Holdings (Irl) Limited Mousse phenolique
WO2008118627A2 (fr) 2007-03-27 2008-10-02 Dow Global Technologies Inc. Agents d'expansion à base d'alcène fluoré pour mousse polymère de qualité
JP2011056882A (ja) * 2009-09-14 2011-03-24 Keisuke Kasahara ビーズ法ポリスチレン発泡体を用いた真空発泡断熱体及び芯材の製造方法とその方法による真空発泡断熱体
EP2752397A1 (fr) 2011-08-31 2014-07-09 LG Hausys, Ltd. Matériau d'isolation sous vide incluant un agent absorbant de composés

Non-Patent Citations (3)

* Cited by examiner, † Cited by third party
Title
DATABASE WPI Week 200305, Derwent World Patents Index; AN 2003-049121, XP002790967 *
DATABASE WPI Week 201125, Derwent World Patents Index; AN 2011-D14333, XP002790968 *
SAUNDERS; FRISCH: "Polyurethane Chemistry and Technology", vol. I, II, 1962, JOHN WILEY AND SONS

Also Published As

Publication number Publication date
GB2571940B (en) 2020-03-25
GB201803941D0 (en) 2018-04-25
GB2571940A (en) 2019-09-18

Similar Documents

Publication Publication Date Title
CN105849166B (zh) 酚醛树脂发泡体
JP6505644B2 (ja) フェノール樹脂発泡体及びその製造方法
RU2686935C2 (ru) Пенопласт на основе фенольной смолы и способ его получения
JP6550415B2 (ja) フェノール樹脂発泡体積層板及びその製造方法
CA2978851C (fr) Mousse en resine phenolique et son procede de production
GB2565331B (en) Phenolic foam and method of manufacture thereof
GB2575988A (en) Phenolic foam and method of manufacture thereof
EP1922356A1 (fr) Mousse phenolique
WO2021145417A1 (fr) Panneau stratifié en mousse de résine phénolique et panneau composite
JP2019089292A (ja) フェノール樹脂発泡体積層板及びその製造方法
GB2587601A (en) An insulation product and method for manufacturing same
WO2019175064A1 (fr) Produit d'isolation et son procédé de fabrication
JP7050579B2 (ja) フェノール樹脂発泡体積層板及びその製造方法
RU2791537C1 (ru) Ламинатная плита из вспененной фенольной смолы
RU2792103C1 (ru) Ламинированная плита и композитная плита из вспененной фенольной смолы
JP2019085525A (ja) フェノール樹脂発泡体及びその製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19709936

Country of ref document: EP

Kind code of ref document: A1

DPE1 Request for preliminary examination filed after expiration of 19th month from priority date (pct application filed from 20040101)
NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19709936

Country of ref document: EP

Kind code of ref document: A1