WO2019151124A1 - Acier inoxydable à base de ferrite - Google Patents

Acier inoxydable à base de ferrite Download PDF

Info

Publication number
WO2019151124A1
WO2019151124A1 PCT/JP2019/002412 JP2019002412W WO2019151124A1 WO 2019151124 A1 WO2019151124 A1 WO 2019151124A1 JP 2019002412 W JP2019002412 W JP 2019002412W WO 2019151124 A1 WO2019151124 A1 WO 2019151124A1
Authority
WO
WIPO (PCT)
Prior art keywords
content
less
steel
thermal fatigue
ferritic stainless
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2019/002412
Other languages
English (en)
Japanese (ja)
Inventor
徹之 中村
石川　伸
杉原　玲子
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JFE Steel Corp
Original Assignee
JFE Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JFE Steel Corp filed Critical JFE Steel Corp
Priority to JP2019524294A priority Critical patent/JP6624345B1/ja
Publication of WO2019151124A1 publication Critical patent/WO2019151124A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention fournit un acier inoxydable à base de ferrite qui se révèle excellent à la fois en termes de résistance à une oxydation répétée et de caractéristiques de fatigue thermique. Plus précisément, l'invention concerne un acier inoxydable à base de ferrite qui possède une composition comprenant, en % en masse, Ｃ：０,０２０％ ou moins, Ｓｉ：０,２５～１,０％, Ｍｎ：０, ０５～０,５０％, Ｐ：０,０５０％ ou moins, Ｓ：０,００８％ ou moins, Ｎｉ： ０,０２～０,６０％, Ａｌ：０,００１～０,０８％, Ｃｒ：１８,０～ ２０,０％, Ｎｂ：０,３０～０,８０％, Ｍｏ：１,８０～２,５０％, Ｎ：０,０１５％ ou moins, Ｚｒ：０,０１～０,４０％ et Ｃｏ：０,０１～０, ３０％, satisfaisant la formule (1), et dont le reste est constitué de Fe et des impuretés inévitables. Ｚｒ＋Ｃｏ：０,０３～０,５０％ ・・・（１） (Dans la formule (1), Zr et Co représentent la teneur de chaque élément (en % en masse).)
PCT/JP2019/002412 2018-01-31 2019-01-25 Acier inoxydable à base de ferrite Ceased WO2019151124A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2019524294A JP6624345B1 (ja) 2018-01-31 2019-01-25 フェライト系ステンレス鋼

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2018-015831 2018-01-31
JP2018015831 2018-01-31

Publications (1)

Publication Number Publication Date
WO2019151124A1 true WO2019151124A1 (fr) 2019-08-08

Family

ID=67479220

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2019/002412 Ceased WO2019151124A1 (fr) 2018-01-31 2019-01-25 Acier inoxydable à base de ferrite

Country Status (2)

Country Link
JP (1) JP6624345B1 (fr)
WO (1) WO2019151124A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115354239A (zh) * 2022-08-17 2022-11-18 常熟市港城不锈钢装饰有限责任公司 一种耐热合金钢材及其制备方法
JPWO2024157580A1 (fr) * 2023-01-23 2024-08-02

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH08218154A (ja) * 1995-02-14 1996-08-27 Nippon Steel Corp 耐金属間化合物析出脆化特性の優れた高強度フェライト系耐熱鋼
JP2004018921A (ja) * 2002-06-14 2004-01-22 Jfe Steel Kk 室温で軟質かつ耐高温酸化性に優れたフェライト系ステンレス鋼
WO2005064030A1 (fr) * 2003-12-26 2005-07-14 Jfe Steel Corporation Acier contenant du cr ferritique
JP2017179398A (ja) * 2016-03-28 2017-10-05 新日鐵住金ステンレス株式会社 排気マニホールド用フェライト系ステンレス鋼板および排気マニホールド

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10669982B2 (en) * 2016-07-28 2020-06-02 Bardex Corporation Wave energy converter with a depth adjustable paravane
EP3508597A4 (fr) * 2016-09-02 2019-09-04 JFE Steel Corporation Acier inoxydable ferritique

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH08218154A (ja) * 1995-02-14 1996-08-27 Nippon Steel Corp 耐金属間化合物析出脆化特性の優れた高強度フェライト系耐熱鋼
JP2004018921A (ja) * 2002-06-14 2004-01-22 Jfe Steel Kk 室温で軟質かつ耐高温酸化性に優れたフェライト系ステンレス鋼
WO2005064030A1 (fr) * 2003-12-26 2005-07-14 Jfe Steel Corporation Acier contenant du cr ferritique
JP2017179398A (ja) * 2016-03-28 2017-10-05 新日鐵住金ステンレス株式会社 排気マニホールド用フェライト系ステンレス鋼板および排気マニホールド

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115354239A (zh) * 2022-08-17 2022-11-18 常熟市港城不锈钢装饰有限责任公司 一种耐热合金钢材及其制备方法
JPWO2024157580A1 (fr) * 2023-01-23 2024-08-02
WO2024157580A1 (fr) * 2023-01-23 2024-08-02 Ｊｆｅスチール株式会社 Acier inoxydable ferritique et son procédé de production
JP7694815B2 (ja) 2023-01-23 2025-06-18 Ｊｆｅスチール株式会社 フェライト系ステンレス鋼およびフェライト系ステンレス冷延鋼板の製造方法

Also Published As

Publication number Publication date
JP6624345B1 (ja) 2019-12-25
JPWO2019151124A1 (ja) 2020-02-06

Similar Documents

Publication Publication Date Title
JP6075349B2 (ja) フェライト系ステンレス鋼
JP5700175B2 (ja) フェライト系ステンレス鋼
JP4702493B1 (ja) 耐熱性に優れるフェライト系ステンレス鋼
JP5234214B2 (ja) フェライト系ステンレス鋼
JP6123964B1 (ja) フェライト系ステンレス鋼
JP5904306B2 (ja) フェライト系ステンレス熱延焼鈍鋼板、その製造方法およびフェライト系ステンレス冷延焼鈍鋼板
JP6908179B2 (ja) フェライト系ステンレス鋼
WO2015174079A1 (fr) Acier inoxydable ferritique
JP6624345B1 (ja) フェライト系ステンレス鋼
JP6624347B1 (ja) フェライト系ステンレス鋼
JP7722299B2 (ja) フェライト系ステンレス冷延焼鈍鋼板、その素材となる冷延鋼板および前記冷延焼鈍鋼板の製造方法
JP6665936B2 (ja) フェライト系ステンレス鋼
JP7528894B2 (ja) フェライト系ステンレス鋼
JP2024129726A (ja) フェライト系ステンレス鋼およびその製造方法

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2019524294

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19747937

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19747937

Country of ref document: EP

Kind code of ref document: A1