WO2019080144A1 - Reworkable non-woven flame retardant tape - Google Patents
Reworkable non-woven flame retardant tapeInfo
- Publication number
- WO2019080144A1 WO2019080144A1 PCT/CN2017/108331 CN2017108331W WO2019080144A1 WO 2019080144 A1 WO2019080144 A1 WO 2019080144A1 CN 2017108331 W CN2017108331 W CN 2017108331W WO 2019080144 A1 WO2019080144 A1 WO 2019080144A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- sensitive adhesive
- reworkable
- flame retardant
- pressure
- substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
Description
本发明涉及粘接材料技术领域，具体地说，是一种用于消费电子，汽车领域的粘接材料，特别是具有可重工性，且具有低VOC的优点的阻燃胶带。The invention relates to the technical field of bonding materials, in particular to a bonding material used in the field of consumer electronics and automobiles, in particular to a flame-retardant tape which has reworkability and has the advantages of low VOC.
常规产品的无纺布单、双面胶带可重工性差，在制程过程中，会增加制造性企业的物料成本，尤其是良率不高的情况下更加明显。Conventional products of non-woven single-sided and double-sided tapes have poor reworkability, which increases the material cost of manufacturing enterprises during the manufacturing process, especially when the yield is not high.
聚酯薄膜类胶带，经过涂布胶水后拉伸，撕裂强度大，往往柔顺性变差，对于曲面等界面的追随性变差，难以结合两种材料的优点。The polyester film tape is stretched after being coated with glue, has a large tear strength, tends to be poor in flexibility, and has poor followability to an interface such as a curved surface, and it is difficult to combine the advantages of the two materials.
发明内容Summary of the invention
本发明的目的在于克服现有技术的缺陷，提供一种用于消费电子，汽车领域的粘接材料，特别是具有可重工性，且具有低VOC的优点的阻燃胶带，以适应市场及环保安全要求。The object of the present invention is to overcome the defects of the prior art and provide a flame-retardant adhesive tape for use in the field of consumer electronics and automobiles, in particular, having reworkability and low VOC, to adapt to the market and environmental protection. Safety requirements.
本发明的第一方面，提供一种可重工无纺布阻燃胶带，所述的可重工无纺布阻燃胶带依次包括第一离型层、第一压敏胶层、基材、第二压敏胶层和第二离型层；According to a first aspect of the present invention, a reworkable non-woven fabric flame retardant tape is provided, and the reworkable non-woven fabric flame retardant tape comprises a first release layer, a first pressure sensitive adhesive layer, a substrate, and a second a pressure sensitive adhesive layer and a second release layer;
其中，所述的基材可选绵纸无纺布基材，采用15～35g/m2的克重，厚度0.08～0.2mm，不同于常规的棉纸产品，此类产品的厚重比达到T:M＝2.5～5.5，由此产生独特的产品力学特性，高拉伸，撕裂强度；在产品粘接材料应用时，具有好的曲面粘接，追随性好，抗反翘优异。Wherein, the substrate is selected from a tissue nonwoven fabric substrate, and has a gram weight of 15 to 35 g/m 2 and a thickness of 0.08 to 0.2 mm. Unlike conventional cotton paper products, the weight ratio of such products reaches T: M=2.5～5.5, which produces unique product mechanical properties, high tensile strength and tear strength. It has good surface bonding, good followability and excellent anti-backlash when applied in product bonding materials.
在本发明的一个优选实施方式中，所述的基材采用绵纸无纺布基材，26g克重，厚度约0.09mm。In a preferred embodiment of the present invention, the substrate is a tissue nonwoven substrate having a weight of 26 g and a thickness of about 0.09 mm.
在本发明的另一个优选实施方式中，所述的基材采用高蓬松的无纺布，26g克重，厚度约0.11mm。In another preferred embodiment of the invention, the substrate is a high loft non-woven fabric having a weight of 26 g and a thickness of about 0.11 mm.
所述的基材还可以采用聚酯型无纺布基材，选用高蓬松比的聚酯型无纺布基材，厚重比T:M＝1.5～8.5。优选的，还可以添加阻燃填料，从而材料达到统一的阻燃效果。 The substrate may also be a polyester-type nonwoven fabric substrate, and a polyester-type nonwoven fabric substrate having a high loft ratio is used, and the weight ratio T:M=1.5 to 8.5. Preferably, a flame retardant filler may also be added to achieve a uniform flame retardant effect of the material.
在本发明的另一个优选实施方式中，所述的基材采用PET型熔喷无纺布，14g克重，厚度约0.04mm。In another preferred embodiment of the present invention, the substrate is a PET type meltblown nonwoven fabric having a weight of 14 g and a thickness of about 0.04 mm.
所述的第一压敏胶层和第二压敏胶层由基材上下表面分别涂布压敏胶水形成，所述的压敏胶水(PSA)选自具有压敏特性的水性压敏胶，热熔压敏胶，UV压敏胶，或有机气体挥发VOC低于0.5％的油性压敏胶。总体胶层厚度可在0.03～1.0mm；整体180°剥离力可在0.1～5.0kg/inch进行调节，粘接耐温性可控制在80～260℃，阻燃可达到0级(GBT 15903-1995压敏胶粘带耐燃性试验方法)。The first pressure-sensitive adhesive layer and the second pressure-sensitive adhesive layer are formed by coating a pressure sensitive adhesive on the upper and lower surfaces of the substrate, and the pressure sensitive adhesive (PSA) is selected from the group consisting of water pressure sensitive adhesives having pressure sensitive properties. Hot melt pressure sensitive adhesive, UV pressure sensitive adhesive, or oily pressure sensitive adhesive with organic gas volatilization VOC less than 0.5%. The overall thickness of the adhesive layer can be 0.03~1.0mm; the overall 180° peeling force can be adjusted at 0.1~5.0kg/inch, the bonding temperature resistance can be controlled at 80~260°C, and the flame retardant can reach 0 level (GBT 15903- 1995 Pressure-sensitive adhesive tape flame resistance test method).
在本发明的一个优选实施方式中，所述的压敏胶水采用水性丙烯酸树脂压敏胶SXL-90树脂(固含量45％)。In a preferred embodiment of the present invention, the pressure-sensitive adhesive is a water-based acrylic pressure-sensitive adhesive SXL-90 resin (solid content: 45%).
所述的压敏胶水中添加阻燃剂，添加量为压敏胶水质量百分比的10％～20％。所述的阻燃剂选自各类胶水用的溴系阻燃剂，磷系阻燃剂，氮系阻燃剂，无机阻燃剂中的一种或两种以上。The pressure sensitive adhesive water is added with a flame retardant in an amount of 10% to 20% by mass of the pressure sensitive adhesive. The flame retardant is selected from one or more of a bromine-based flame retardant, a phosphorus-based flame retardant, a nitrogen-based flame retardant, and an inorganic flame retardant for various types of glue.
在本发明的优选实施方式中，所述的阻燃剂为含量为99.5％环保性三氧化二锑、BASF阻燃剂Melapur 25、或氢氧化铝阻燃剂(如泰星化工阻燃剂HT-205)。In a preferred embodiment of the present invention, the flame retardant is a content of 99.5% environmentally friendly antimony trioxide, BASF flame retardant Melapur 25, or aluminum hydroxide flame retardant (such as Taixing chemical flame retardant HT -205).
所述的离型层为离型纸，离型膜，或者具有离型隔离作用的界面材料。The release layer is a release paper, a release film, or an interface material having a release barrier effect.
在本发明的优选实施方式中，所述的离型层为双硅离型纸、格拉幸离型纸或透明PET离型膜。In a preferred embodiment of the invention, the release layer is a double silicon release paper, a glazing release paper or a transparent PET release film.
优选的，所述的可重工无纺布阻燃胶带厚度在0.01～3.0mm之间。Preferably, the reworkable non-woven fabric flame retardant tape has a thickness of between 0.01 and 3.0 mm.
本发明的第二方面，提供一种上述的可重工无纺布阻燃胶带的制备方法，包括以下步骤：采用添加阻燃剂的压敏胶水，涂布在离型纸或离型膜上进行转移贴合，贴合无纺布基材，双面复合后完成胶带成品。According to a second aspect of the present invention, there is provided a method for preparing the above-mentioned reworkable non-woven fabric flame-retardant tape, comprising the steps of: applying a pressure-sensitive adhesive added with a flame retardant to a release paper or a release film; Transfer and fit, attach the non-woven substrate, and finish the tape after double-sided compounding.
本发明优点在于：The advantages of the invention are:
1、本发明产品对常规的无纺布双面胶带进行了结构与材料特性的优化，采用了特殊的无纺布结构涂布为胶带产品，使得其力学性能表现综合性能优异；1. The product of the invention optimizes the structure and material properties of the conventional non-woven double-sided tape, and adopts a special non-woven structure to be coated into a tape product, so that the mechanical properties and performance are excellent;
2、结合特殊的阻燃助剂，具有优良的自熄灭效果，无发烟，无滴落；2, combined with special flame retardant additives, has an excellent self-extinguishing effect, no smoke, no dripping;
3、采用环保的胶水体系，采用UV胶，水性胶，热熔胶压敏胶，产品无有机溶剂残留； 3, using environmentally friendly glue system, using UV glue, water-based glue, hot melt adhesive pressure sensitive adhesive, the product has no organic solvent residue;
4、本发明产品采用特种的无纺布，其具有高于常规无纺布绵纸，拉伸，撕裂强度，成品具有优于聚酯的柔顺性；仍采用阻燃的无纺布及胶水结合而成，且无卤素、有机溶剂残留，更加环保。4. The product of the invention adopts special non-woven fabric, which has higher than conventional non-woven tissue paper, tensile and tear strength, and the finished product has better flexibility than polyester; still uses flame retardant non-woven fabric and glue combination It is non-halogen, organic solvent residue and more environmentally friendly.
图1是本发明的可重工无纺布阻燃胶带的截面结构示意图。BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a schematic sectional view showing the structure of a reworkable nonwoven fabric flame-retardant tape of the present invention.
附图中涉及的附图标记和组成部分如下所示：The reference numerals and components referred to in the drawings are as follows:
1-基材； 2-第一压敏胶层；1-substrate; 2-first pressure sensitive adhesive layer;
3-第二压敏胶层； 4-第一离型层；3-second pressure sensitive adhesive layer; 4-first release layer;
5-第二离型层。5-second release layer.
下面结合实施例对本发明提供的具体实施方式作详细说明。The specific embodiments provided by the present invention will be described in detail below with reference to the embodiments.
实施例1：Example 1:
采用水性丙烯酸树脂压敏胶如SXL-90树脂(固含量45％)，阻燃剂为含量为99.5％环保性三氧化二锑，阻燃剂添加量为胶水的15％，经涂布在110g双硅离型纸上转移贴合，单层的干胶涂胶厚度0.065mm，贴合特种绵纸无纺布基材(26g克重，厚度约0.09mm)。Water-based acrylic resin pressure sensitive adhesive such as SXL-90 resin (solid content 45%), flame retardant content of 99.5% environmentally friendly antimony trioxide, flame retardant added amount of glue 15%, coated at 110g The transfer and bonding of the double-silicon release paper, the thickness of the single-layer dry glue coating is 0.065mm, and the special tissue paper non-woven substrate (26g gram weight, thickness about 0.09mm) is attached.
表1Table 1
实施例2：Example 2:
采用热熔性压敏胶，添加阻燃剂10％(如BASF阻燃剂Melapur 25)，涂布在90g的格拉幸离型纸上进行转移贴合，PET型熔喷无纺布(14g克重，厚度约0.04mm)，双面复合后完成胶带成品总厚度在0.1mm。Using hot melt pressure sensitive adhesive, adding 10% flame retardant (such as BASF flame retardant Melapur 25), coating on 90g Graham release paper for transfer bonding, PET meltblown non-woven fabric (14g g The weight is about 0.04mm), and the total thickness of the finished tape is 0.1mm after double-sided compounding.
表2Table 2
实施例3：Example 3:
采用UV型压敏胶，添加氢氧化铝阻燃剂20％(如泰星化工阻燃剂HT-205)，涂布在0.05mm透明PET离型膜上进行光聚合后转移贴合，采用高蓬松的无纺布(26g克重，厚度约0.11mm)，双面复合后完成胶带成品总厚度在0.17mm。UV type pressure sensitive adhesive, 20% aluminum hydroxide flame retardant (such as Taixing Chemical Flame Retardant HT-205), coated on 0.05mm transparent PET release film for photopolymerization, transfer and bonding, high The fluffy non-woven fabric (26g gram weight, thickness about 0.11mm), the total thickness of the completed tape finished product is 0.17mm after double-sided compounding.
表3table 3
以上已对本发明创造的较佳实施例进行了具体说明，但本发明创造并不限于所述实施例，熟悉本领域的技术人员在不违背本发明创造精神的前提下还可做出种种的等同的变型或替换，这些等同的变型或替换均包含在本申请权利要求所限定的范围内。 The preferred embodiments of the present invention have been specifically described above, but the present invention is not limited to the embodiments, and those skilled in the art can make various equivalents without departing from the inventive spirit of the present invention. Modifications or substitutions of the invention are intended to be included within the scope of the appended claims.
Claims (9)