WO2019078146A1 - Électrolyte liquide et cellule à flux redox - Google Patents

Électrolyte liquide et cellule à flux redox Download PDF

Info

Publication number
WO2019078146A1
WO2019078146A1 PCT/JP2018/038279 JP2018038279W WO2019078146A1 WO 2019078146 A1 WO2019078146 A1 WO 2019078146A1 JP 2018038279 W JP2018038279 W JP 2018038279W WO 2019078146 A1 WO2019078146 A1 WO 2019078146A1
Authority
WO
WIPO (PCT)
Prior art keywords
ion
electrolytic solution
concentration
vanadium
ions
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2018/038279
Other languages
English (en)
Japanese (ja)
Inventor
賢太郎 渡邉
ティンティン シュウ
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Resonac Holdings Corp
Original Assignee
Showa Denko KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Showa Denko KK filed Critical Showa Denko KK
Priority to JP2019549262A priority Critical patent/JPWO2019078146A1/ja
Publication of WO2019078146A1 publication Critical patent/WO2019078146A1/fr
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

L'invention concerne un électrolyte liquide comprenant une solution aqueuse qui comprend des ions tétrafluoroborate et des ions vanadium.
PCT/JP2018/038279 2017-10-17 2018-10-15 Électrolyte liquide et cellule à flux redox Ceased WO2019078146A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2019549262A JPWO2019078146A1 (ja) 2017-10-17 2018-10-15 電解液、およびレドックスフロー電池

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2017201097 2017-10-17
JP2017-201097 2017-10-17

Publications (1)

Publication Number Publication Date
WO2019078146A1 true WO2019078146A1 (fr) 2019-04-25

Family

ID=66173664

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/038279 Ceased WO2019078146A1 (fr) 2017-10-17 2018-10-15 Électrolyte liquide et cellule à flux redox

Country Status (2)

Country Link
JP (1) JPWO2019078146A1 (fr)
WO (1) WO2019078146A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022014195A1 (fr) * 2020-07-17 2022-01-20 住友電気工業株式会社 Solution électrolytique et pile redox
EP4322268A4 (fr) * 2021-04-07 2025-07-16 Soulbrain Co Ltd Procédé pour préparer un électrolyte au vanadium et batterie comprenant un électrolyte au vanadium

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6215770A (ja) * 1985-07-11 1987-01-24 Yamaguchi Univ レドックス二次電池
JPH11339835A (ja) * 1998-05-29 1999-12-10 Kashimakita Kyodo Hatsuden Kk レドックス電池
JP2010086935A (ja) * 2008-09-03 2010-04-15 Sharp Corp レドックスフロー電池
JP2013095918A (ja) * 2011-11-03 2013-05-20 Samsung Electronics Co Ltd イオン交換膜充電用組成物、イオン交換膜の製造方法、イオン交換膜及びレドックスフロー電池
JP2016162529A (ja) * 2015-02-27 2016-09-05 昭和電工株式会社 レドックスフロー電池用電解液およびレドックスフロー電池
US20160260994A1 (en) * 2013-10-28 2016-09-08 Hyundai Heavy Industries Co., Ltd. Ion exchange membrane and method for manufacturing same

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6215770A (ja) * 1985-07-11 1987-01-24 Yamaguchi Univ レドックス二次電池
JPH11339835A (ja) * 1998-05-29 1999-12-10 Kashimakita Kyodo Hatsuden Kk レドックス電池
JP2010086935A (ja) * 2008-09-03 2010-04-15 Sharp Corp レドックスフロー電池
JP2013095918A (ja) * 2011-11-03 2013-05-20 Samsung Electronics Co Ltd イオン交換膜充電用組成物、イオン交換膜の製造方法、イオン交換膜及びレドックスフロー電池
US20160260994A1 (en) * 2013-10-28 2016-09-08 Hyundai Heavy Industries Co., Ltd. Ion exchange membrane and method for manufacturing same
JP2016162529A (ja) * 2015-02-27 2016-09-05 昭和電工株式会社 レドックスフロー電池用電解液およびレドックスフロー電池

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022014195A1 (fr) * 2020-07-17 2022-01-20 住友電気工業株式会社 Solution électrolytique et pile redox
EP4322268A4 (fr) * 2021-04-07 2025-07-16 Soulbrain Co Ltd Procédé pour préparer un électrolyte au vanadium et batterie comprenant un électrolyte au vanadium

Also Published As

Publication number Publication date
JPWO2019078146A1 (ja) 2020-09-17

Similar Documents

Publication Publication Date Title
Mousavi et al. Decoupled low-cost ammonium-based electrolyte design for highly stable zinc–iodine redox flow batteries
JP6742337B2 (ja) 負電解液と正電解液を同時に改善するための、バイポーラ膜を有するフロー電池用バランシングセル
JP5007849B1 (ja) レドックスフロー電池、及びその運転方法
CN102341946B (zh) 氧化还原液流电池
AU2002328660B2 (en) Vanadium / polyhalide redox flow battery
US8916281B2 (en) Rebalancing electrolytes in redox flow battery systems
JP6742338B2 (ja) バイポーラ膜を有するフロー電池用バランシングセル及びその使用法
US20200259200A1 (en) All-vanadium sulfate acid redox flow battery system
US20120282509A1 (en) Redox flow battery
JP6621584B2 (ja) レドックスフロー電池用電解液およびレドックスフロー電池
WO2019246538A1 (fr) Batterie à flux entièrement en fer et systèmes
US20150357653A1 (en) Vanadium Solid-Salt Battery and Method for Producing Same
CN106030884A (zh) 氧化还原液流电池
WO2019078146A1 (fr) Électrolyte liquide et cellule à flux redox
WO2014030231A1 (fr) Batterie rechargeable
WO2019181983A1 (fr) Solution électrolytique et batterie redox
EP3565048A1 (fr) Batterie redox
WO2019124300A1 (fr) Solution d'électrolyte et batterie rédox
WO2020036107A1 (fr) Solution électrolytique pour batteries redox, batterie redox et son procédé de fonctionnement
JP2012204347A (ja) レドックスフロー電池、及びその運転方法
JPH04286871A (ja) レドックス型二次電池
WO2022014195A1 (fr) Solution électrolytique et pile redox
CN119542484A (zh) 一种液流电池用泥浆型锰正极电解液

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18867469

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2019549262

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18867469

Country of ref document: EP

Kind code of ref document: A1